CN103045040A - 一种天然岩片漆及制备方法 - Google Patents
一种天然岩片漆及制备方法 Download PDFInfo
- Publication number
- CN103045040A CN103045040A CN2013100046547A CN201310004654A CN103045040A CN 103045040 A CN103045040 A CN 103045040A CN 2013100046547 A CN2013100046547 A CN 2013100046547A CN 201310004654 A CN201310004654 A CN 201310004654A CN 103045040 A CN103045040 A CN 103045040A
- Authority
- CN
- China
- Prior art keywords
- natural
- paint
- agent
- sliver paint
- tackiness agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种天然岩片漆及制备方法,属于装饰漆技术领域。其特征在于由天然云母片和粘合剂按重量比1:1-3混合而成,所述粘合剂由下述重量配比的原料组合而成:硅丙乳液50%-60%,铝溶液15%-25%,硅烷偶联剂1%-3%,联接剂1%-3%,成膜助剂2%-4%,水10%-20%,余量为增稠剂。本发明采用上述技术方案所能达到的有益效果是:与目前市场上使用的人工合成的岩片漆相比,具有独特的装饰效果,添加的天然云母石更具良好的保温效果、其使用周期更长,颜色光亮度更鲜艳。
Description
技术领域
本发明属于装饰漆技术领域,具体涉及一种天然岩片漆及制备方法。
背景技术
目前,市场上的装饰涂料种类繁多,岩片漆是其中的一种,由于岩片漆具有良好的装饰效果,在市场上广泛受到关注,现有的岩片漆有两种大类,一类是采用天然岩石制作的岩片漆,另一类是采用人工合成的岩片制作的岩片漆。人工合成的岩片制作的岩片漆,只适合近看,远看则难以看出岩片和纹理的效果,没有真石的感觉,采用现有工艺制备仍然无法达到岩石的效果,其保温效果、耐久性及颜色的亮光度都无法和天然岩石相比;采用天然岩石制备岩片漆,可使建筑装饰更贴合自然,更具优雅、稳重、气派之效果,然后,在天然岩片漆的制备过程中,原料、配方、不用的加工工艺条件,都影响到天然岩片漆的使用效果,现有的天然岩片漆及制备工艺,存在施工难度大,易喷花的问题。
发明内容
针对现有技术中存在的问题,本发明的目的在于提供一种天然岩片漆及制备方法。
所述的一种天然岩片漆,其特征在于由天然云母片和粘合剂按重量比1:1-3混合而成,所述粘合剂由下述重量配比的原料组合而成:硅丙乳液50%-60%,铝溶液15%-25%,硅烷偶联剂1%-3%,联接剂1%-3%,成膜助剂2%-4%,水10%-20%,余量为增稠剂。
所述的一种天然岩片漆,其特征在于所述天然云母片和粘合剂的重量比为1:1-2。
所述的一种天然岩片漆,其特征在于所述的粘合剂由下述重量比的原料组合而成:硅丙乳液53%-58%,铝溶液18%-23%,硅烷偶联剂1.5%-2.5%,联接剂1.5%-2.5%,成膜助剂2%-3%,水13%-17%,余量为增稠剂。
所述的一种天然岩片漆,其特征在于所述成膜助剂包括2,2,4-三甲基-1,3-戊二醇单异丁酸酯或苯甲醇的一种或二种的组合。
所述的天然岩片漆的制备方法,其特征在于该方法步骤如下:
1)将硅丙乳液、铝溶液、硅烷偶联剂、联接剂、成膜助剂、水、增稠剂按配比依次加入高速搅拌机,边加入边搅拌,搅拌均匀后调PH值6-8后静止两小时,既得粘合剂。
2)按配比在步骤1)中制得的粘合剂中添加天然云母片,边加边用U型棒搅拌,搅拌均匀后即为天然岩片漆成品。
所述的天然岩片漆的制备方法,其特征在于所述步骤1)中的搅拌时间为2-2.5小时,搅拌速度为4000转/分钟。
所述的天然岩片漆的制备方法,其特征在于所述步骤2)中的搅拌时间为2小时,搅拌速率为30-60转/分钟。
本发明使用的硅丙乳液、铝溶液、硅烷偶联剂、联接剂、成膜助剂、增稠剂及天然云母片均可由市场上购买得到。
本发明采用上述技术方案所能达到的有益效果是:与目前市场上使用的人工合成的岩片漆相比,具有独特的装饰效果,添加的天然云母石更具良好的保温效果、其使用周期更长,颜色光亮度更鲜艳。
具体实施方式
本发明下面结合实施例予以进一步详述。
实施例1
一种天然岩片漆,由天然云母片和粘合剂按重量比1:1混合而成,粘合剂由下述重量配比的原料组合而成:硅丙乳液50%,铝溶液25%,硅烷偶联剂1%,联接剂3%,苯甲醇4%,水10%,增稠剂7%。
将硅丙乳液50%、铝溶液25%、硅烷偶联剂1%、联接剂3%、苯甲醇4%、水10%、增稠剂7%依次加入高速搅拌机中,边加入边搅拌,搅拌时间为2小时,搅拌速度为4000转/分钟,搅拌均匀后调PH值6-8即得粘合剂,静止两小时后在粘合剂中加入天然云母片,边加入边用U型棒搅拌,搅拌时间为2小时,搅拌速度为30-60转/分钟,即制得天然岩片漆成品,包装即可。
实施例2
一种天然岩片漆,由天然云母片和粘合剂按重量比1:2混合而成,粘合剂由下述重量配比的原料组合而成:硅丙乳液60%,铝溶液15%,硅烷偶联剂3%,联接剂1%,2,2,4-三甲基-1,3-戊二醇单异丁酸酯2%,水13%,增稠剂6%。
将硅丙乳液60%、铝溶液15%、硅烷偶联剂3%、联接剂1%、2,2,4-三甲基-1,3-戊二醇单异丁酸酯2%、水13%、增稠剂6%依次加入高速搅拌机中,边加入边搅拌,搅拌时间为2.5小时,搅拌速度为4000转/分钟,搅拌均匀后调PH值6-8即得粘合剂,静止两小时后在粘合剂中加入天然云母片,边加入边用U型棒搅拌,搅拌时间为2小时,搅拌速度为30-60转/分钟,即制得天然岩片漆成品,包装即可。
实施例3
一种天然岩片漆,由天然云母片和粘合剂按重量比1:3混合而成,粘合剂由下述重量配比的原料组合而成:硅丙乳液55%,铝溶液20%,硅烷偶联剂2%,联接剂2%,2,2,4-三甲基-1,3-戊二醇单异丁酸酯3%,水15%,增稠剂3%。
将硅丙乳液55%、铝溶液20%、硅烷偶联剂2%、联接剂2%、2,2,4-三甲基-1,3-戊二醇单异丁酸酯3%、水15%、增稠剂3%依次加入高速搅拌机中,边加入边搅拌,搅拌时间为2小时,搅拌速度为4000转/分钟,搅拌均匀后调PH值6-8即得粘合剂,静止两小时后在粘合剂中加入天然云母片,边加入边用U型棒搅拌,搅拌时间为2小时,搅拌速度为30-60转/分钟,即制得天然岩片漆成品,包装即可。
实施例4
一种天然岩片漆,由天然云母片和粘合剂按重量比1:3混合而成,粘合剂由下述重量配比的原料组合而成:硅丙乳液58%,铝溶液18%,硅烷偶联剂1.5%,联接剂2.5%,成膜助剂3%,水15%,增稠剂2%。成膜助剂采用2,2,4-三甲基-1,3-戊二醇单异丁酸酯和苯甲醇,二者按重量比2:1配制。
将硅丙乳液58%、铝溶液18%、硅烷偶联剂1.5%、联接剂2.5%、成膜助剂3%、水15%、增稠剂2%依次加入高速搅拌机中,边加入边搅拌,搅拌时间为2小时,搅拌速度为4000转/分钟,搅拌均匀后调PH值6-8即得粘合剂,静止两小时后在粘合剂中加入天然云母片,边加入边用U型棒搅拌,搅拌时间为2小时,搅拌速度为30-60转/分钟,即制得天然岩片漆成品,包装即可。
本发明施工时要求墙面平整,腻子刮平,高渗透专用底漆刷一遍,岩片漆喷涂一遍,罩面漆两遍。
Claims (7)
1.一种天然岩片漆,其特征在于由天然云母片和粘合剂按重量比1:1-3混合而成,所述粘合剂由下述重量配比的原料组合而成:硅丙乳液50%-60%,铝溶液15%-25%,硅烷偶联剂1%-3%,联接剂1%-3%,成膜助剂2%-4%,水10%-20%,余量为增稠剂。
2.如权利要求1所述的一种天然岩片漆,其特征在于所述天然云母片和粘合剂的重量比为1:1-2。
3.如权利要求1或2所述的一种天然岩片漆,其特征在于所述的粘合剂由下述重量比的原料组合而成:硅丙乳液53%-58%,铝溶液18%-23%,硅烷偶联剂1.5%-2.5%,联接剂1.5%-2.5%,成膜助剂2%-3%,水13%-17%,余量为增稠剂。
4.如权利要求1或2所述的一种天然岩片漆,其特征在于所述成膜助剂包括2,2,4-三甲基-1,3-戊二醇单异丁酸酯或苯甲醇的一种或二种的组合。
5.一种制备如权利要求1所述的天然岩片漆的方法,其特征在于该方法步骤如下:
1)将硅丙乳液、铝溶液、硅烷偶联剂、联接剂、成膜助剂、水、增稠剂按配比依次加入高速搅拌机,边加入边搅拌,搅拌均匀后调PH值6-8后静止两小时,既得粘合剂;
2)按配比在步骤1)中制得的粘合剂中添加天然云母片,边加边用U型棒搅拌,搅拌均匀后即为天然岩片漆成品。
6.根据权利要求5所述的天然岩片漆的制备方法,其特征在于所述步骤1)中的搅拌时间为2-2.5小时,搅拌速度为4000转/分钟。
7.根据权利要求5所述的天然岩片漆的制备方法,其特征在于所述步骤2)中的搅拌时间为2小时,搅拌速率为30-60转/分钟。