CN101215916A - Indoor wall surface putty construction process - Google Patents
Indoor wall surface putty construction process Download PDFInfo
- Publication number
- CN101215916A CN101215916A CNA2008100592812A CN200810059281A CN101215916A CN 101215916 A CN101215916 A CN 101215916A CN A2008100592812 A CNA2008100592812 A CN A2008100592812A CN 200810059281 A CN200810059281 A CN 200810059281A CN 101215916 A CN101215916 A CN 101215916A
- Authority
- CN
- China
- Prior art keywords
- scrape
- glue
- batch
- white cement
- drying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a construction technique of indoor wall surface lacquer putty and belongs to the technical field of building construction techniques, which comprises following steps: adopting white cement and talcum powder, mixing according to the weight percentage of 70%-90%:30%-10%, adding 801 glue water, stirring until even paste is formed, and then scrapping on the wall surface for three times, wherein the thickness for each scraping is better to be smaller than 0.3mm. The invention replaces traditional 107 glue water by the 801 glue water as adhesive, which effectively increases the cohesive force, and two main problems of bulges and fissures in construction work of indoor lacquer putty are overcome through adopting new proportion of 801 adhesive and materials and combining with a new scraping technique, and the indoor wall surface lacquer putty which is adopted by the invention has the qualified rate 97.3% according to inspection statistics and achieves significant effects.
Description
Technical field
The present invention relates to a kind of architectural construction technology, especially relate to a kind of indoor wall surface putty construction process.
Background technology
At present, the emulsion paint facing is almost all widely applied in each building decoration engineering, its construction technology and method be " constant " almost, but development along with society, the owner is also more and more higher to the quality requirement of emulsion paint, indivedual owners' (managements) employing light bounce techniques are the impression quality of the emulsion paint facing in the sensing chamber from the side, and the critical process that influences emulsion paint facing quality is the indoor wall surface putty quality, but not emulsion paint itself or its are smeared the lacquer finish procedures, therefore, indoor wall surface putty quality direct relation facing and impression quality.The indoor wall surface putty quality mainly reflects that by inspection data such as drum, verticality, levelness, crack, scratch and other impressions by statistics, indoor wall surface putty mass defect is as shown in table 1:
Table 1, indoor wall surface putty mass defect project statistical form
| Sequence number | Defective item | Frequency | Cumulative frequency | Cumulative percentage (%) |
| 1 | Play drum | 46 | 46 | 56.1 |
| 2 | The crack | 18 | 64 | 78 |
| 3 | Verticality | 6 | 70 | 85.4 |
| 4 | Planeness | 5 | 75 | 91.5 |
| 5 | Scratch | 3 | 78 | 95.1 |
| 6 | Other impression | 4 | 82 | 100 |
| Add up to | 82 | 82 | 100 |
By the indoor wall surface putty mass defect shown in the table 1 statistics and arrangement analysis as can be known, playing drum and these 2 defective items of crack and accounted for 78%, therefore, how to solve indoor wall surface putty and rise and rouse and crack problem, is the key of raising interior decoration engineering quality.
Summary of the invention
For solving the problems referred to above of prior art, the object of the present invention is to provide a kind of indoor wall surface putty construction process that can effectively solve drum and crack problem.
The technical scheme that the present invention is taked for achieving the above object is that a kind of indoor wall surface putty construction process comprises the steps:
1, now join wall surface putty coating: after white cement and French chalk 70%～90%: 30%～10% mixing by weight percentage, add 801 glue, be stirred to and form even paste, the slump is 8%～10%, is fit to criticize to scrape get final product.
2, criticize and scrape: with metope mend flat after, adopt above-mentioned coating to divide and on metope, batch scrape for three times.
Preferred employing 325
#White cement;
The preferred each batch of thickness of scraping is being good less than 0.3mm;
Preferably before each batch is scraped, adopt ventilation, drying step to reduce indoor wall humidity;
For obtaining best implementation result, can on metope, brush one time 801 glue earlier, carrying out first pass after waiting to do criticizes and scrapes, first pass is criticized spread coated paint and preferably is adopted as 90% white cement and 10% French chalk proportioning, polish off pick blade seratch after the drying, scrape with carrying out second time batch then, second time batch of spread coated paint preferably is adopted as 80% white cement and 20% French chalk proportioning, polish off pick blade seratch after the drying, carrying out the 3rd time batch at last scrapes, the 3rd time batch of spread coated paint preferably is adopted as 70% white cement and 30% French chalk proportioning, polishes smooth after waiting to do.
Principle of the present invention and beneficial effect: by indoor wall surface putty being played the analysis of drum and crack problem, its main cause is as follows: 1, the adhesion stress of cementing agent is not enough; 2, indoor wall humidity height; 3, proportioning control is bad; 4, disposable batch to scrape thickness excessive.The present invention has improved bonding force effectively by changing 107 traditional glue into 801 glue as cementing agent; And adopt 801 cementing agents and material proportioning again, scrape technology in conjunction with new criticizing, solved the problems referred to above effectively, adopted indoor wall surface putty of the present invention, on inspection statistics, check 150 of data points, do not conform to lattice point and have only 4 (playing 2 of drums, 2 of planeness), qualification rate 97.3% has obtained obvious effects, prescription of the present invention and technology are simple, overcome indoor putty effectively and play drum and two subject matters in crack in construction.
The specific embodiment
Embodiment 1
With metope mend flat after, keep room ventilation, drying, one time 801 glue of brushing on metope is earlier waited to do the back and is mixed 90% white cement, 10% French chalk with 801 glue and carry out first pass and criticize and scrape, and criticizes and scrapes thickness 0.1mm, polishes off pick blade seratch after the drying; Mix 80% white cement, 20% French chalk with 801 glue then and carry out second time batch and scrape, batch scrape thickness 0.1mm, polish off pick blade seratch after the drying; Mix 70% white cement, 30% French chalk with 801 glue at last and carry out the 3rd time batch and scrape, batch scrape thickness 0.2mm, polish smooth after waiting to do.
Embodiment 2
With metope mend flat after, keep room ventilation, drying, one time 801 glue of brushing on metope is earlier waited to do the back and is mixed 90% white cement, 10% French chalk with 801 glue and carry out first pass and criticize and scrape, and criticizes and scrapes thickness 0.1mm, polishes off pick blade seratch after the drying; Mix 80% white cement, 20% French chalk with 801 glue then and carry out second time batch and scrape, batch scrape thickness 0.2mm, polish off pick blade seratch after the drying; Mix 70% white cement, 30% French chalk with 801 glue at last and carry out the 3rd time batch and scrape, batch scrape thickness 0.2mm, polish smooth after waiting to do.
Embodiment 3
With metope mend flat after, keep room ventilation, drying, one time 801 glue of brushing on metope is earlier waited to do the back and is mixed 90% white cement, 10% French chalk with 801 glue and carry out first pass and criticize and scrape, and criticizes and scrapes thickness 0.1mm, polishes off pick blade seratch after the drying; Mix 75% white cement, 25% French chalk with 801 glue then and carry out second time batch and scrape, batch scrape thickness 0.1mm, polish off pick blade seratch after the drying; Mix 70% white cement, 30% French chalk with 801 glue at last and carry out the 3rd time batch and scrape, batch scrape thickness 0.2mm, polish smooth after waiting to do.
Embodiment 4
With metope mend flat after, keep room ventilation, drying, one time 801 glue of brushing on metope is earlier waited to do the back and is mixed 90% white cement, 10% French chalk with 801 glue and carry out first pass and criticize and scrape, and criticizes and scrapes thickness 0.1mm, polishes off pick blade seratch after the drying; Mix 75% white cement, 25% French chalk with 801 glue then and carry out second time batch and scrape, batch scrape thickness 0.2mm, polish off pick blade seratch after the drying; Mix 70% white cement, 30% French chalk with 801 glue at last and carry out the 3rd time batch and scrape, batch scrape thickness 0.25mm, polish smooth after waiting to do.
Claims (7)
1. indoor wall surface putty construction process, it is characterized in that: after white cement and French chalk 70%～90%: 30%～10% mixing by weight percentage, add 801 glue, be stirred to and form even paste, divide to criticize on metope for three times and scrape, the each batch of thickness of scraping is less than 0.3mm.
2. a kind of indoor wall surface putty construction process according to claim 1 is characterized in that: described white cement preferably adopts 325
#White cement.
3. a kind of indoor wall surface putty construction process according to claim 1 is characterized in that: preferably adopt ventilation, drying step to reduce indoor wall humidity before each batch is scraped.
4. a kind of indoor wall surface putty construction process according to claim 1, it is characterized in that: after the metope benefit is put down, keep room ventilation, drying, on metope, brush one time 801 glue earlier, waiting to do the back mixes 90% white cement, 10% French chalk with 801 glue and carries out first pass and criticize and scrape, criticize and scrape thickness 0.1mm, polish off pick blade seratch after the drying; Mix 80% white cement, 20% French chalk with 801 glue then and carry out second time batch and scrape, batch scrape thickness 0.1mm, polish off pick blade seratch after the drying; Mix 70% white cement, 30% French chalk with 801 glue at last and carry out the 3rd time batch and scrape, batch scrape thickness 0.2mm, polish smooth after waiting to do.
5. a kind of indoor wall surface putty construction process according to claim 1, it is characterized in that: after the metope benefit is put down, keep room ventilation, drying, on metope, brush one time 801 glue earlier, waiting to do the back mixes 90% white cement, 10% French chalk with 801 glue and carries out first pass and criticize and scrape, criticize and scrape thickness 0.1mm, polish off pick blade seratch after the drying; Mix 80% white cement, 20% French chalk with 801 glue then and carry out second time batch and scrape, batch scrape thickness 0.2mm, polish off pick blade seratch after the drying; Mix 70% white cement, 30% French chalk with 801 glue at last and carry out the 3rd time batch and scrape, batch scrape thickness 0.2mm, polish smooth after waiting to do.
6. a kind of indoor wall surface putty construction process according to claim 1, it is characterized in that: after the metope benefit is put down, keep room ventilation, drying, on metope, brush one time 801 glue earlier, waiting to do the back mixes 90% white cement, 10% French chalk with 801 glue and carries out first pass and criticize and scrape, criticize and scrape thickness 0.1mm, polish off pick blade seratch after the drying; Mix 75% white cement, 25% French chalk with 801 glue then and carry out second time batch and scrape, batch scrape thickness 0.1mm, polish off pick blade seratch after the drying; Mix 70% white cement, 30% French chalk with 801 glue at last and carry out the 3rd time batch and scrape, batch scrape thickness 0.2mm, polish smooth after waiting to do.
7. a kind of indoor wall surface putty construction process according to claim 1, it is characterized in that: after the metope benefit is put down, keep room ventilation, drying, on metope, brush one time 801 glue earlier, waiting to do the back mixes 90% white cement, 10% French chalk with 801 glue and carries out first pass and criticize and scrape, criticize and scrape thickness 0.1mm, polish off pick blade seratch after the drying; Mix 75% white cement, 25% French chalk with 801 glue then and carry out second time batch and scrape, batch scrape thickness 0.2mm, polish off pick blade seratch after the drying; Mix 70% white cement, 30% French chalk with 801 glue at last and carry out the 3rd time batch and scrape, batch scrape thickness 0.25mm, polish smooth after waiting to do.