CN104631722B - Construction method of special putty-based mixture for coating aerated block masonry - Google Patents
Construction method of special putty-based mixture for coating aerated block masonry Download PDFInfo
- Publication number
- CN104631722B CN104631722B CN201310548047.7A CN201310548047A CN104631722B CN 104631722 B CN104631722 B CN 104631722B CN 201310548047 A CN201310548047 A CN 201310548047A CN 104631722 B CN104631722 B CN 104631722B
- Authority
- CN
- China
- Prior art keywords
- special
- putty
- special putty
- based mixture
- base compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a construction method of a special putty-based mixture for coating an aerated block masonry. The construction method comprises the following steps: (1) a concave-convex part of a wall is physically treated, and is moisturized by water; (2) the special putty-based mixture is prepared; putty powder of 62.2-73.8%, cement of 4.8-6.5%, gypsum powder of 6.6-8.0%, cast stone powder of 1.5-2.3%, talcum powder of 4.2-5.5%, kieselguhr of 2.3-3.0%, water of 3.4-4.0%, flexible adhesive glue of 0.9-1.5% and crack resistant additive of 4.2-5.3% are added in a special barrel of 50 L in percentage by weight in sequence, are stirred for 3-5 minutes, and are subjected to still standing for 5-10 minutes; (3) a masonry mortar joint is filled by the special putty-based mixture; (4) a joint of the concrete and a masonry wall surface is filled by the special putty-based mixture, and is bonded with alkali-resisting glass fiber gridding cloth; (5) the special putty-based mixture of 4-6 mm is pressed into the alkali-resisting glass fiber gridding cloth; (6) the special putty-based mixture is used for leveling; and (7) general putty is coated once; and emulsion paint is brushed for two times. The special putty-based mixture is high in strength and great in adhesive force, and is directly combined with the aerated block masonry without being deformed and dropped.
Description
Art
The present invention is applied to building masonry wall and is particularly suited for the construction that aerated blocks masonry smears special putty base compound
Method.
Background technology
The wall plaster of traditional aerated blocks masonry, be first with the mortar that cement, yellow ground make carry out painting levelling after, then
Use common putty-painting, it is disadvantageous in that: putty material and body of wall are not direct joints, but clip one layer of mortar material
Material, because mortar is easily unrestrained, pollutes environment, waste of materials；And mortar rendering layer is easily cracking, hollowing, feed consumption of taking a lot of work；Plus
Common putty low intensity, adhesive force is smaller, easy to crack, in wet condition, easy to fall off.
Content of the invention
The invention aims to overcoming weak point and providing aerated blocks masonry to smear special putty base compound
Construction method, special putty base compound can directly be applied on aerated blocks masonry, saves the levelling of one mortar, it is to avoid
Because of the unrestrained pollution environment causing of mortar, waste of material, it also avoid the cracking because mortar rendering layer occurs, hollowing and make
The feed consumption of taking a lot of work becoming；More importantly special putty base compound intensity is high, and adhesive force is big, is directly combined with aerated blocks masonry,
Indeformable, even if in wet condition, also will not come off.
The technical solution adopted for the present invention to solve the technical problems is: aerated blocks masonry smears special putty base compound
Construction method: first step, metope is processed, and the excessive jog of physical treatment body of wall, but be not levelling with filler uses water
Moistening；Second step, prepares special putty base compound, prepares a special barrel, and volume is 50 liters.By weight percentage, exist
Powder of lacquer putty for use on 62.2 73.8%, cement 4.8-6.5%, Gypsum Fibrosum powder 6.6-8.0%, glass-cermic powder 1.5 is sequentially added in special barrel
2.3%th, Pulvis Talci 4.2-5.5%, kieselguhr 2.3 3.0%, water 3.4-4.0%, flexible adhesion agent glue 0.9 1.5%, anti-
Split additive 4.2-5.3%, stirred 35 minutes with portable electric blender, uniformly paste, stand 5 10 minutes, then
Stirring, you can use；Third step, fills and leads up masonry mortar joint with special putty base compound；Four steps, in concrete and masonry
Metope junction special putty base compound criticize flat, and paste alkali resistant glass fibre open weave cloth；5th step, batch 4-6 millimeters thick is special
Putty base compound, and it is pressed into alkali resistant glass fibre open weave cloth；6th step, floating with special putty base compound；7th step, batch
A time common putty, two times emulsion paints of brush.
The invention has effective effect that, the aerated blocks masonry of the application present invention smears the construction party of special putty base compound
Method, special putty base compound can directly be applied on aerated blocks masonry, save the levelling of one mortar, it is to avoid because of mortar
The unrestrained pollution environment causing of material, waste of material, it also avoid cracking because mortar rendering layer occurs, hollowing and the expense that causes
Work feed consumption；More importantly special putty base compound intensity is high, and adhesive force is big, is directly combined with aerated blocks masonry, indeformable,
Even if in wet condition, also will not come off.
Specific embodiment
Embodiment 1, aerated blocks masonry smears the construction method of special putty base compound: first step, and metope is processed, thing
Reason processes the excessive jog of body of wall, but is not levelling with filler, uses water-wet；Second step, prepares special putty base and mixes
Close material, prepare a special barrel, volume is 50 liters.By weight percentage, powder of lacquer putty for use on 67.8%, water are sequentially added in special barrel
Mud 5.8%, Gypsum Fibrosum powder 7.0%, glass-cermic powder 2.0%, Pulvis Talci 4.8%, kieselguhr 2.7%, water 3.9%, flexible adhesion agent glue
1.0%th, anti-crack additive 5.0%, is stirred 35 minutes with portable electric blender, uniformly paste, stands 8 minutes, then
Stirring, you can use；Third step, fills and leads up masonry mortar joint with special putty base compound；Four steps, in concrete and masonry
Metope junction special putty base compound criticize flat, and paste alkali resistant glass fibre open weave cloth；5th step, batch 4-6 millimeters thick is special
Putty base compound, and it is pressed into alkali resistant glass fibre open weave cloth；6th step, floating with special putty base compound；7th step, batch
A time common putty, two times emulsion paints of brush.
Embodiment 2, aerated blocks masonry smears the construction method of special putty base compound: first step, and metope is processed, thing
Reason processes the excessive jog of body of wall, but is not levelling with filler, uses water-wet；Second step, prepares special putty base and mixes
Close material, prepare a special barrel, volume is 50 liters.By weight percentage, powder of lacquer putty for use on 67.4%, water are sequentially added in special barrel
Mud 6.0%, Gypsum Fibrosum powder 7.6%, glass-cermic powder 1.9%, Pulvis Talci 4.9%, kieselguhr 2.5%, water 3.7%, flexible adhesion agent glue
1.2%th, anti-crack additive 4.8%, is stirred 5 minutes with portable electric blender, uniformly paste, stands 10 minutes, then stirs
Mix, you can use；Third step, fills and leads up masonry mortar joint with special putty base compound；Four steps, in concrete and masonry wall
Face junction special putty base compound criticize flat, and paste alkali resistant glass fibre open weave cloth；5th step, batch 4-6 millimeters thick is special greasy
Subbase compound, and it is pressed into alkali resistant glass fibre open weave cloth；6th step, floating with special putty base compound；7th step, criticizes one
All over common putty, two times emulsion paints of brush.
Claims (1)
1. aerated blocks block wall construction method it is characterised in that: first step, metope is processed, and physical treatment body of wall is excessive
Jog, but be not levelling with filler, use water-wet；Second step, prepares special putty base compound: prepare one specially
With bucket, volume is 50 liters, by weight percentage, sequentially adds powder of lacquer putty for use on 62.2-73.8%, cement 4.8- in special barrel
6.5%th, Gypsum Fibrosum powder 6.6-8.0%, glass-cermic powder 1.5-2.3%, Pulvis Talci 4.2-5.5%, kieselguhr 2.3-3.0%, water 3.4-
4.0%th, flexible adhesion agent glue 0.9-1.5%, anti-crack additive 4.2-5.3%, stirs 3-5 minute with portable electric blender,
Uniformly paste, stands 5-10 minute, is stirred for, you can use；Third step, fills and leads up masonry with special putty base compound
Mortar joint；Four steps, in concrete and block wall junction special putty base compound criticize flat, and pastes alkali-resisting glass fiber grid
Cloth；5th step, batch 4-6 millimeters thick special putty base compound, and it is pressed into alkali resistant glass fibre open weave cloth；6th step, with special
Putty base compound is floating；7th step, a batch common putty, two times emulsion paints of brush.