CN107476514A - A kind of wall surface putty construction process - Google Patents
A kind of wall surface putty construction process Download PDFInfo
- Publication number
- CN107476514A CN107476514A CN201610400107.4A CN201610400107A CN107476514A CN 107476514 A CN107476514 A CN 107476514A CN 201610400107 A CN201610400107 A CN 201610400107A CN 107476514 A CN107476514 A CN 107476514A
- Authority
- CN
- China
- Prior art keywords
- wall surface
- construction process
- puttying
- putty
- wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses it is a kind of can effectively solve to ftracture, wrinkle, the wall surface putty construction process of scaling and the problem that comes off, comprise the following steps：Base cleaning → spray latex water or varnish → filling chink part batch Puttying → filling cracks even up full wall after being stained with cloth and criticize Puttying → polishing scratch → latex water of spray second time or varnish → full wall Puttying → polishing scratch again.Construction technology of the present invention is simple, and the putty composition of raw materials of improvement, bonding force greatly enhances, and the problems such as effectively solving metope cracking, corrugation, scaling and come off, and can absorb pernicious gas, green.
Description
Technical field
The present invention relates to a kind of architectural construction technology, more particularly to a kind of wall surface putty is applied
Work technique.
Background technology
At present, inexpensive putty is not only applicable to the decoration of face wall in architectural engineering, and has come into ten million and used
In the family at family, its construction technology and method are almost unchanged, and batch scraping for usual putty is first with calcium hydroxide by after face wall criticize flat, then is criticized
By the putty that plaster of Paris is primary raw material, such way, although certain building decoration cost can be saved, safety has really been buried
Hidden danger, after the carbon dioxide reaction in calcium hydroxide and air in metope, volume can expand 20%~25%, easily cause metope
Ftracture and produce Seepage, and plaster of Paris class putty poor water resistance, think after brushing through corrugation, scaling often occur and coming off
As.
The content of the invention
To solve the above mentioned problem of prior art, can effectively solve to ftracture it is an object of the invention to provide one kind, wrinkle,
Scaling and the wall surface putty construction process for the problem that comes off.
The technical scheme that the present invention is taken to achieve the above object is a kind of wall surface putty construction process, including as follows
Step：
Base cleaning → spray latex water or varnish → filling chink part batch Puttying → filling cracks are evened up full after being stained with cloth
Wall batch Puttying → polishing scratch → latex water of spray second time or varnish → multiple Puttying → polishing scratch of full wall.
Preferably, the putty is by clear water, talcum powder and white cement by weight percentage 25%~15%：30%~35%：45%
After~50% is mixed, homogeneous paste is formed.
Preferably, the described batch of thickness scraped is 0.2~0.3mm.
Preferably, criticize to scrape every time and carried out in temperature >=15 DEG C, the environment of humidity≤60%.
Beneficial effects of the present invention：Construction technology of the present invention is simple, and the putty composition of raw materials of improvement, bonding force increases
By force, the problems such as effectively solving metope cracking, corrugation, scaling and coming off, and pernicious gas can be absorbed, it is green.
Embodiment
The present invention is described in further detail below in conjunction with specific embodiment.
Embodiment one：
After concrete in basic unit, greasy dirt, floating sand, dust are cleaned out, spray latex water or varnish carries out back cover, in environment
Temperature >=15 DEG C, under conditions of humidity≤60%, the putty of composition is mixed by wall with 25% clear water, 30% talcum powder and 45% white cement
Face gap, which is tamped, to be struck off, as metope have crack can first with glass grid Bradley it is straight after be bonded at crack, and expire wall and batch scrape thickness
0.2mm putty, polished smooth after putty is dry, spray second time latex water or varnish, completely wall batch scrapes the greasy of thick 0.2mm again
Son, polished smooth after putty is dry.
Embodiment two：
After concrete in basic unit, greasy dirt, floating sand, dust are cleaned out, spray latex water or varnish carries out back cover, in environment
Temperature >=15 DEG C, under conditions of humidity≤60%, the putty of composition is mixed by wall with 20% clear water, 33% talcum powder and 47% white cement
Face gap, which is tamped, to be struck off, as metope have crack can first with glass grid Bradley it is straight after be bonded at crack, and expire wall and batch scrape thickness
0.25mm putty, polished smooth after putty is dry, spray second time latex water or varnish, completely wall batch scrapes the greasy of thick 0.25mm again
Son, polished smooth after putty is dry.
Embodiment three：
After concrete in basic unit, greasy dirt, floating sand, dust are cleaned out, spray latex water or varnish carries out back cover, in environment
Temperature >=15 DEG C, under conditions of humidity≤60%, the putty of composition is mixed by wall with 15% clear water, 35% talcum powder and 50% white cement
Face gap, which is tamped, to be struck off, as metope have crack can first with glass grid Bradley it is straight after be bonded at crack, and expire wall and batch scrape thickness
0.3mm putty, polished smooth after putty is dry, spray second time latex water or varnish, completely wall batch scrapes the greasy of thick 0.3mm again
Son, polished smooth after putty is dry.
Claims (4)
1. a kind of wall surface putty construction process, it is characterised in that comprise the following steps：
Base cleaning → spray latex water or varnish → filling chink part batch Puttying → filling cracks are evened up full after being stained with cloth
Wall batch Puttying → polishing scratch → latex water of spray second time or varnish → multiple Puttying → polishing scratch of full wall.
A kind of 2. wall surface putty construction process according to claim 1, it is characterised in that：The putty is by clear water, talcum
Powder and white cement by weight percentage 25%~15%：30%~35%：After 45%~50% is mixed, homogeneous paste is formed.
A kind of 3. wall surface putty construction process according to claim 1, it is characterised in that：The described batch of thickness scraped is 0.2
~0.3mm.
A kind of 4. wall surface putty construction process according to claim 1, it is characterised in that：Criticize and scraped in temperature >=15 every time
DEG C, carried out in the environment of humidity≤60%.