CN101210150B - 烤漆组合物 - Google Patents

烤漆组合物 Download PDF

Info

Publication number
CN101210150B
CN101210150B CN2006101324499A CN200610132449A CN101210150B CN 101210150 B CN101210150 B CN 101210150B CN 2006101324499 A CN2006101324499 A CN 2006101324499A CN 200610132449 A CN200610132449 A CN 200610132449A CN 101210150 B CN101210150 B CN 101210150B
Authority
CN
China
Prior art keywords
nylon
varnish composition
baking varnish
silane coupling
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2006101324499A
Other languages
English (en)
Other versions
CN101210150A (zh
Inventor
彭亚培
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitac Precision Technology Shunde Ltd
Original Assignee
Mitac Precision Technology Shunde Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitac Precision Technology Shunde Ltd filed Critical Mitac Precision Technology Shunde Ltd
Priority to CN2006101324499A priority Critical patent/CN101210150B/zh
Publication of CN101210150A publication Critical patent/CN101210150A/zh
Application granted granted Critical
Publication of CN101210150B publication Critical patent/CN101210150B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种烤漆组合物，其主要成分以重量分数表示为：饱和聚酯树脂64-70；异丁醚化三聚氰胺甲醛树脂20-28；环氧树脂0-10；流平剂0-0.01；溶剂6-7.6；硅烷偶联剂0-1。上述配方是以饱和聚酯树脂配合异丁醚化三聚氰胺甲醛树脂加入少量环氧树脂和微量硅烷偶联剂在烘烤下发生交联反应成膜，具有极好的附着力及物化性。上述烤漆组合物，可直接涂装于尼龙和玻璃纤维表面，省去前处理步骤，其耐腐蚀性强，环保无毒害，涂装尼龙和玻璃纤维表面后所生成的油漆膜层附着力强。

Description

烤漆组合物
技术领域
本发明涉及到一种溶剂型烤漆组合物，特别是涉及到一种高附着溶剂型烤漆组合物。
背景技术
油漆是指涂到物体表面能干燥成膜，使物体美观并得到保护，或者在物体表面形成具有其它特殊功能膜的一类成膜物质。油漆在不同的环境中起保护作用，因此需要有力学强度、耐老化、耐腐蚀等特点。
尼龙和玻璃纤维素材上为防止被腐蚀通常也涂装一油漆层加以保护，但是尼龙和玻璃纤维素材上涂装十分困难，目前大多要经过前处理后再涂装双组分油漆，给施工带来麻烦。
发明内容
为解决上述问题，本发明提供了一种对产品外观保护性强的高附着烤漆组合物。
本发明的技术方案为：一种高附着溶剂型烤漆组合物，其主要成分以重量分数表示为：
饱和聚酯树脂               64-70；
异丁醚化三聚氰胺甲醛树脂   20-28；
环氧树脂                   0-10；
流平剂                     0-0.01；
溶剂                       6-7.6；
硅烷偶联剂                 0-1。
其中，上述配方是以饱和聚酯树脂配合异丁醚化三聚氰胺甲醛树脂加入少量环氧树脂和微量硅烷偶联剂在烘烤下发生交联反应成膜，具有极好的附着力及物化性。硅烷偶联剂用于尼龙和玻璃纤维的浸润处理，且由于其苯氧基有机官能基团的作用，同时在交联过程中，抗氧化能力显着增强。所述的溶剂为正丁醇、尼龙酸二甲酯，所述的流平剂为聚醚改性聚二甲基硅氧烷，以促进漆膜流平。
上述烤漆组合物，可直接涂装于尼龙和玻璃纤维表面，省去前处理步骤，其耐腐蚀性强，环保无毒害，涂装尼龙和玻璃纤维表面后所生成的油漆膜层附着力强。
本发明提供的用于涂装尼龙和玻璃纤维表面的烤漆其性能优越，友好环境，具有较好的社会和经济效益。
具体实施方式
实施例1
按照上述技术方案中的配方，各组分重量份数分别为：
饱和聚酯树脂                  70；
异丁醚化三聚氰胺甲醛树脂       28；
环氧树脂                      10；
聚醚改性聚二甲基硅氧烷        0.01；
正丁醇                        4.6；
尼龙酸二甲酯                  3；
硅烷偶联剂                    1。
将上述称取好的原料按常规方法混合均匀后制成油漆，然后将该油漆涂装于一尼龙和玻璃纤维(含玻璃纤维35％)素材表面，使用方法与其它油漆相同，接着按照烤漆流程，在150℃的温度下烘烤20分钟，然后检验该生成的油漆膜层，其附着力强，耐溶剂、耐化学品，性能优异，具有良好的效益；同时，可省去涂装于尼龙和玻璃纤维等产品时，需在涂装前对上述产品表面进行前处理的麻烦，给施工带来便利。
实施例2
按照上述技术方案中的配方，各组分重量份数分别为：
饱和聚酯树脂                69；
异丁醚化三聚氰胺甲醛树脂     25；
环氧树脂                    8；
聚醚改性聚二甲基硅氧烷      0.01；
正丁醇                      4；
尼龙酸二甲酯                2.5；
硅烷偶联剂                  0.5。
将上述称取好的原料按常规方法混合均匀后制成油漆，然后将该油漆涂装于一尼龙和玻璃纤维(含玻璃纤维35％)素材表面，使用方法与其它油漆相同，接着按照烤漆流程，在150℃的温度下烘烤20分钟，然后检验该生成的油漆膜层，其附着力强，耐溶剂、耐化学品，性能优异，具有良好的效益；同时，可省去涂装于尼龙和玻璃纤维等产品时，需在涂装前对上述产品表面进行前处理的麻烦，给施工带来便利。

Claims (1)

1.一种烤漆组合物，其特征在于：主要成分以重量分数表示为，
饱和聚酯树脂                    64-70；
异丁醚化三聚氰胺甲醛树脂        20-28；
环氧树脂                        8-10；
流平剂                          0-0.01；
溶剂                            6-7.6；
硅烷偶联剂                      0.5-1；
其中，所述的溶剂为正丁醇、尼龙酸二甲酯；所述的流平剂为聚醚改性聚二甲基硅氧烷。
CN2006101324499A 2006-12-29 2006-12-29 烤漆组合物 Expired - Fee Related CN101210150B (zh)