CN101143986A - Terrace paint - Google Patents
Terrace paint Download PDFInfo
- Publication number
- CN101143986A CN101143986A CNA2007100093415A CN200710009341A CN101143986A CN 101143986 A CN101143986 A CN 101143986A CN A2007100093415 A CNA2007100093415 A CN A2007100093415A CN 200710009341 A CN200710009341 A CN 200710009341A CN 101143986 A CN101143986 A CN 101143986A
- Authority
- CN
- China
- Prior art keywords
- terrace
- lacquer
- aggregate
- prescription
- sizing material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a floor coating and a preparation method and application thereof, wherein the floor coating of the invention consists of rubber compound, aggregate, and overlay maintenance agent; the method for preparing the floor coating includes the following steps: (1) preparation of rubber compound and overlay maintenance agent: each component material is added into a stirred tank according to the mentioned certain proportion and stirred for about 10min followed by filter and qualification to discharge; (2) preparation of aggregate: each component of raw material is added into dry-powder mixing tank according a certain proportion, and stirred for 30min, followed by qualification to discharge. The application of the floor coating of the invention includes that: the sealed base layer is firstly coated on the cement base layer by rubber compound, then the middle paint layer is coated on the sealed base layer by aggregate, after that the cover-layer is coated on the middle paint layer by overlay maintenance agent. The floor coating of the invention is a product which has high cost-performance and very good market.
Description
Technical field
The present invention relates to terrace lacquer and its production and application.
Background technology
In recent years, in order to reach best decorative effect and desirable quality, the architect has gradually adopted marble, terrazzo, colored cement, floor tile, the sclerosis terrace, the pressing mold terrace, material and Handicraft decorative terraces such as plastics floor, also reached reasonable effect, but As time goes on, some disadvantages have also appearred gradually, as: concrete, colored cement, the sclerosis terrace, terrazzo floor, because of insufficient strength plays dirt easily, not wear-resisting, decorative effect is not strong, be difficult for repairing, the heavily contaminated of terrazzo terrace, characteristics such as resistance to acids and bases is poor, and is easy to change are withdrawn from the market now substantially; Marble, floor tile, because of frangible, resistance to acids and bases is poor, crushing resistance is poor, wet and slippery serious, characteristics such as cost is high, long in time limit, also substantially not teacher of being designed adopt.Now many have pressing mold terrace, plastics floor, self-leveling cement terrace are adopted in market, its texture is strong, moulding uniqueness etc., be subjected to people's favorable comment, but problems such as cost height, construction technology complexity, long in time limit, the complicated difficult accommodation of machine die also occurred, also limited to development space.
Summary of the invention
One of purpose of the present invention is the above-mentioned deficiency that will overcome prior art, and a kind of novel terrace lacquer is provided.
Terrace lacquer of the present invention is made up of sizing material, aggregate, cover curing agent; Its prescription is as follows respectively:
Aggregate (being to be coated with material in the terrace lacquer) each component components by weight percentage scope is: white cement or the high-alumina cement 30-45% of intensity more than 42.5R, high-modulus quartz sand or silica sand or silicon carbide 55-70%, water reducer 1.0-0.5%, dry powder defoamer 0.1-0.5%, polypropylene fibre or other high molecular polymerization fibres 0.1-0.3%, Mierocrystalline cellulose 0.1-0.3%, mildew-resistant algae-resistant agent 0.3-1.0%, iron oxide silicate-resistant class pigment 1.0-5.0%.
Liquid part each component components by weight percentage scope in sizing material (being terrace lacquer basecoat material) and the bicomponent material is: ethene one acetate emulsion or aqueous epoxy resins 30-50%, water 50-70%, algae agent 0.3-1.0% is prevented in mildew-resistant, frostproofer 1.0-3.0%, wetting agent 0.1-0.2%.
Cover curing agent (being that the terrace lacquer painting is coated with material) each component components by weight percentage scope is: extraordinary acrylic resin 25-35%, and toluene organic solvent 45-75%, algae agent 0.3-1% is prevented in mildew-resistant.
It more than is described terrace lacquer two-pack prescription.
Fill a prescription other each components and above-mentioned terrace lacquer two-pack of described terrace lacquer single component filled a prescription identically, and difference is to add by weight percentage to be furnished with in above-mentioned aggregate: latex powder 3.0-8.0%.
Two of purpose of the present invention is that above-mentioned terrace lacquer preparation method will be provided:
1, the preparation of sizing material (being the undercoat material), cover curing agent (being topcoat material): the each component material adds in the stirring tank in above-mentioned fixed weight percent ratio, stirs about 10 minutes, and it is qualified to filter, detect, and gets final product discharging.
2, the preparation of aggregate (being coated with material promptly): the each component raw and auxiliary material adds in the dry powder blend still in above-mentioned fixed weight percent ratio, after the stir about 30 minutes, qualified after testing after, get final product discharging.
Three of purpose of the present invention is application that above-mentioned terrace lacquer will be provided: it is to coat sealing basic unit with sizing material (being terrace lacquer basecoat material) at cement basic layer earlier that described terrace lacquer is used, secondly in sealing basic unit, add sizing material with aggregate (being to be coated with material during terrace coats with lacquer) and stir after coat inter coat, use cover curing agent (being that the terrace lacquer painting is coated with material) on inter coat, to coat finish coat then.
Terrace of the present invention coats with lacquer compared with the prior art, and advantage is: (1) can adapt to the concrete surface of different appearance, and basal plane is had very strong caking ability, can Proteanly satisfy client and Designers to requirement attractive in appearance, moulding.(2) processing property excellence, construction technology is simple, and the duration is short fast dry, suitable large-area construction, moderate cost is easy to large-scale popularization and uses.(3) have excellent weather, ageing-resistant, performances such as acid and alkali-resistance, freeze-thaw-; Ultimate compression strength (7 days) can reach more than the 60mpa, and ultimate compression strength (28 days) reaches more than the 70mpa.(4) color and luster changes for a short time in the use bright in luster, does not play dirt, flakes, nearly hundred kinds of assortment are selective, be suitable for family or commercial comprise around walkway, step, balcony, courtyard, ground, not load-carrying track, the swimming pool, place such as park.(5) anti-wet and slippery property is special, and its special basic unit's design in rainy season promotes security.(6) feature of environmental protection is outstanding, and production and construction process do not have useless row, satisfy environment requirement.
Embodiment
Below the present invention is further described.(but not being limitation of the present invention).
Terrace lacquer of the present invention is made up of sizing material, aggregate, cover curing agent; Its prescription is as follows respectively:
Aggregate (being to be coated with material in the terrace lacquer) each component components by weight percentage scope is: white cement or the high-alumina cement 30-45% of intensity more than 42.5R, high-modulus quartz sand or silica sand or silicon carbide 55-70%, water reducer 1.0-0.5%, dry powder defoamer 0.1-0.5%, polypropylene fibre or other high molecular polymerization fibres 0.1-0.3%, Mierocrystalline cellulose 0.1-0.3%, mildew-resistant algae-resistant agent 0.3-1.0%, iron oxide silicate-resistant class pigment 1.0-5.0%.
Sizing material (being terrace lacquer basecoat material) each component components by weight percentage scope is: ethene one acetate emulsion or aqueous epoxy resins 30-50%, and water 50-70%, algae agent 0.3-1.0%, frostproofer 1.0-3.0%, wetting agent 0.1-0.2% are prevented in mildew-resistant.
Cover curing agent (being that the terrace lacquer painting is coated with material) each component components by weight percentage scope is: extraordinary acrylic resin 25-35%, and toluene organic solvent 45-75%, algae agent 0.3-1% is prevented in mildew-resistant.
It more than is terrace lacquer two-pack prescription of the present invention.
Fill a prescription other each components and above-mentioned terrace lacquer two-pack of described terrace lacquer single component filled a prescription identically, and difference is to add by weight percentage to be furnished with in above-mentioned aggregate: latex powder 3.0-8.0%.
Sizing material is selected the organic water cure high molecular polymer of the modification of adhesive property excellence, functional agent for use.Aggregate is selected inorganic coagulation material (special high-strength silicic acid salt slurry) abrasive aggregates, acid and alkali-resistance pigment, activated macromolecular fibre for use, and multiple auxiliary agent is formed; When aggregate mixes with sizing material, under the interaction of the strong and ionic bond of chemical adsorption effect one hydrogen between organic polymer and the inorganic coagulation material, improved the absorption cohesive force of material; The adding of special activation macromolecular fibre, functional agent, adsorption moisture from high molecular polymer, and continuous aquation, simultaneously, the water retaining function of polymkeric substance, aquation factor when having guaranteed cement solidification, polymkeric substance solidifies gradually owing to dewater, and makes the hole of the terrace lacquer painting spatial skeleton of formation, by firm, cohesive strength is high, have necessarily with flexible organic polymer colloid network, rete gluing, have high strength thereby form, be coated with in the matrix material of high-wearing feature.Priming paint and sizing material adopt the nanotechnology polymer emulsion, its nano particle has infiltration closed concrete capillary function, special functional agent impels polymer beads to soften and produces crosslinking reaction with silicates alkali crystal, reacted particle water-swellable, block concrete pore, reaching the sealing effect, strengthen with in be coated with the cohesive force of material.The surface finishing curing agent adopts epoxide modified silicon resin copolymer resin, its permeation enhanced function is peculiar, functions such as the wear resistance of lifting terrace lacquer, cohesive strength, ultimate compression strength, UV resistant promote extraordinary washable chemically-resistant and the physical surface performance of waiting of self-cleaning function comprehensively comprehensively.
Above-mentioned terrace lacquer preparation method of the present invention is:
1, the preparation of sizing material (being the undercoat material), cover curing agent (being topcoat material): the each component material adds in the stirring tank in above-mentioned fixed weight percent ratio, stirs about 10 minutes, and it is qualified to filter, detect, and gets final product discharging.
2, the preparation of aggregate (being coated with material promptly): the each component raw and auxiliary material adds in the dry powder blend still in above-mentioned fixed weight percent ratio, after the stir about 30 minutes, qualified after testing after, get final product discharging.
It is to be that terrace lacquer basecoat material is coated sealing basic unit at cement basic layer with sizing material earlier that described terrace lacquer is used, secondly being coated with inter coat with being coated with material in the terrace lacquer in sealing basic unit, is that the terrace lacquer painting is coated with material coats finish coat on inter coat with the cover curing agent then.The construction technique of the application of described terrace lacquer is:
1. carry out base treatment earlier: reach flawless, smooth, firm.
2. carry out sealing bottom coating then:
A, brushing or spray one oyster white sealing sizing material, dry back forms layer of transparent back cover coating.
B or employing add the pigment of white pigment or other color in oyster white sealing sizing material, brush after the stirring or spray, and form the seal coat of one deck white or other color.
3. lay the moulding paper matrix: pattern modelling and corresponding size by design are carried out scene laying reworked paper matrix.
4. spray main material:
A. use single-component prescription terrace lacquer: aggregate is poured in the plastic tank, and the water of interpolation 18-19% adds toner after stirring with electric drill, and restir is even, can carry out spraying application.
B. use two-pack prescription terrace lacquer: sizing material is poured in the plastic tank, added after toner stirs, add aggregate, aggregate: the liquid material is about 5: 1, carries out spraying application after stirring into the cream pasty state.
5. polishing coarseparticulate, dedusting: after spraying application was finished 24 hours, thick thing removed in available sand papering, and removed dust with besom, loosening granular substance, and sweep off loosening granular substance with hard besom, and use air gun, blow away floating dust.
6. Lacquer finish: test before unshowy place carries out the spraying of small area earlier, and adjust the Lacquer finish spray gun, make it to reach spraying evenly, the glossiness unanimity is carried out large-area spraying application again.
Sealer coat mainly acts on: the hole in the dust of set road basal plane, floating sand, the obstruction concrete plays the water proof anti-seepage effect, plays basal plane and middle level abrasive aggregates and promotes cohesive action.
Inter coat: adopt high-strength special type cement and macromolecule polymer material as binding agent, use the mineral-type aggregate of high abrasion strong hardness, the various physical and chemical performances of coating are effectively ensured, used polymer cracking resistance strongthener, make the various materials of inter coat be linked to be integral body, thereby improve the over-all properties of whole coating system, added the functional agent that helps application property, make the execution of coating performance enough fully satisfy construction requirement.The special-purpose spray gun that adopts carries out coating decoration, and formed concavo-convex decorative pattern makes the anti-skid of terrace paint system more outstanding, and decorative effect more can embody.
Finish coat: having used acrylic resin is filmogen; the construction of employing spraying method can be mixed in the intermediate materials resin equably, has improved the relevant physicochemical property of middle layer material; and can protect the surface of terrace paint system, the wear resistance of terrace paint, weather resistance are improved.
The shortcoming of cement silicon carbide abrasion-proof terrace, paving tile terrace, marble terrace, pressing mold terrace, the existence of terrazzo terrace is at present: (1) cement silicon carbide abrasion-proof terrace shortcoming: need and the concrete initial set staged construction during construction, wayward quality, exist tone single, rainy day is easily sliding, the surface is abrasion easily, easily dusting, a dirt.(2) paving tile terrace shortcoming: operation is numerous and diverse, not resistant to pressure, fragile, fracture, fugitive color, easily loss of gloss, poor durability, production paving tile are seriously polluted etc.(3) marble terrace shortcoming: the transportation of materials power consumption is big, cost is high, rainy day is easily sliding, it is big to expend social resources, colour forming is single, easily produces the scrap stock contaminate environment, (4) pressing mold terrace shortcoming: cost height, construction technology complexity, long construction period, moulding mould is single, is not easy to be connected, changes, transports, uses mould that cost is increased when with a varied topography, needs the skilled labor to operate.(5) terrazzo terrace shortcoming: big, seriously polluted, the easy cunning of construction noise, dusting, a dirt, easily abrasion.Application of the present invention mainly is the cement silicon carbide abrasion-proof terrace that will substitute present widespread use, paving tile terrace, marble terrace, pressing mold terrace, terrazzo terrace etc.And the blade coating of terrace of the present invention lacquer, the requirement that spraying property all reaches workability, color artistic terrace lacquer system adopts the construction of combined type construction technology to form, if material master material is cellulosic polymer, acid and alkali-resistance pigment, the cracking resistance auxiliary agent of high-strength silicate cement, quartz sand, activated processing, and material such as various admixtures, in construction, mix high molecular polymer, inorganic, the organic compound floor material of a kind of collection that having construction back to adopt silicon curing agent modification cover to form, from face solved organic and inorganic can not the hybrid technology vicious circle.This terrace lacquer can adopt artificial and mechanical type construction technology, is not subjected to operating technique, and zone, climate change effect are not limited by facility, pattern, can satisfy decoration and the practicality of people to each color, various zones to greatest extent.Can under the situation of condition difference, construct, also can adopt the automatization spray painting equipment, satisfy old road renewal and reform, and passage large-area construction duration problem. terrace lacquer of the present invention has following function:
(1) antiskid function: adopt spraying method to form concavo-convex texture decorative pattern in substrate surface, strengthen the degree of roughness on coat surface, make it to have antiskid function, used various pattern paper matrix and be divided into the fritter separated from one another that varies in size through spraying afterwards and take off paper matrix formation, both play the effect that beautifies, played anti-skidding effect again.
(2) can tolerate the rideability of vehicle: mainly be the middle level material selection the hard abrasive aggregates of high-intensity special cement, high molecular polymer ethene one vinyl acetate between to for plastic glue is as organic binder bond, other relevant cement additire etc., make the high compressive strength of coating, high-wearing feature, the high breaking strength performance can access sufficient embodiment, ethene one vinyl acetate between to for plastic has good cement compatibility and gives full play to its inherent cohesiveness and snappiness in addition, make in the terrace paint system organic, the complementation of inorganic bond performance advantage reaches the effect of high compressive strength and high abrasion.
(3) good decorating effect: can be according to the environment of terrace periphery, owner individual's hobby, the construction requirement of engineering waits selects corresponding design and color collocation, the whole looks of end change terrace are built in the construction back, color, the pattern of terrace can be merged mutually with the environment of periphery, contrast finely with each other and just right, make the whole more apparent novelty of architectural environment, harmony attractive in appearance.
(4) construction technology is simple, does not need skilled operator and mould, only needs to brush or spray one seal coat or lines priming paint, is coated with material in the spraying together again, after the drying, sprays one solvent-borne type finishing paint again and gets final product, and construction environment is not had particular requirement.
(5) scope of application is extensive, and outdoor, indoor terrace all can use, as road, square, villa, school, hospital, swimming pool periphery, parking lot etc.Solved solely narrow shortcoming of many terrace paint ranges of application.
(6) superior durability: because of the present invention is a kind of high performance compound terrace paint, used the aggregate of high-strength special type cement and hard wear resistant, and the solvent-type acrylic resin of special use that has adopted high weather-proof, high abrasion is as covering material, and formed coating has superpower sticking power and persistent weather resistance.Having solved with the organic high molecular compound resin material is the terrace paint sticking power such as road graticule of base-material and the defective of poor durability.
(7) do not produce three waste discharge during feature of environmental protection production and construction, convenient transportation, promote easily.
(8) utilize the scrap stock fragmentation, screening of tool certain degree of hardness such as marble, glass, all can be used as stopping composition and replace quartz sand, silica sand to use, reach refuse reclamation.
Claims (3)
1. terrace lacquer is characterized in that described terrace lacquer is made up of sizing material, aggregate, cover curing agent; Its prescription is as follows respectively:
Aggregate each component components by weight percentage scope is: white cement or the high-alumina cement 30-45% of intensity more than 42.5R, high-modulus quartz sand or silica sand or silicon carbide 55-70%, water reducer 1.0-0.5%, dry powder defoamer 0.1-0.5%, polypropylene fibre or other high molecular polymerization fibres 0.1-0.3%, Mierocrystalline cellulose 0.1-0.3%, mildew-resistant algae-resistant agent 0.3-1.0%, iron oxide silicate-resistant class pigment 1.0-5.0%;
Sizing material each component components by weight percentage scope is: ethene one acetate emulsion or aqueous epoxy resins 30-50%, and water 50-70%, algae agent 0.3-1.0%, frostproofer 1.0-3.0%, wetting agent 0.1-0.2%, propylene glycol 1-3% are prevented in mildew-resistant;
Cover curing agent each component components by weight percentage scope is: extraordinary acrylic resin 25-35%, and toluene organic solvent 45-75%, algae agent 0.3-1% is prevented in mildew-resistant;
It more than is described terrace lacquer two-pack prescription;
Fill a prescription other each components and above-mentioned terrace lacquer two-pack of described terrace lacquer single component filled a prescription identically, and difference is to add by weight percentage to be furnished with in above-mentioned aggregate: latex powder 3.0-8.0%.
2. terrace lacquer preparation method according to claim 1 is characterized in that:
The preparation of described sizing material, cover curing agent: the each component material adds in the stirring tank in above-mentioned definite ratio, stirs about 10 minutes, and it is qualified to filter, detect, and gets final product discharging;
Described aggregate processing: the each component raw and auxiliary material adds in the dry powder blend still in proportion, after the stir about 30 minutes, qualified after testing after, get final product discharging.
3. the application of terrace lacquer according to claim 1 is characterized in that:
Earlier coating sealing basic unit with sizing material at cement basic layer, is to be coated with material during terrace coats with lacquer to coat inter coat with aggregate in sealing basic unit secondly, is that the terrace lacquer painting is coated with material coats finish coat on inter coat with the cover curing agent then; The construction technique of the application of described terrace lacquer is:
(1), carries out base treatment earlier: reach flawless, smooth, firm;
(2), carry out sealing bottom coating then:
A, brushing or spray the oyster white sizing material one, dry back forms layer of transparent back cover coating;
B, in the oyster white sizing material, add the pigment of white pigment or other color, brush after the stirring or spray, form the seal coat of one deck white or other color;
(3), lay the moulding paper matrix: pattern modelling and corresponding size by design are laid the reworked paper matrix;
(4), spray main material:
A, use single-component prescription terrace lacquer: aggregate is poured in the plastic tank, adding toner after the water of interpolation 18-19% stirs with electric drill, restir is even, can carry out spraying application;
B, use two-pack prescription terrace lacquer: sizing material is poured in the plastic tank, added after toner stirs, add aggregate, aggregate: the liquid material is about 5: 1, carries out spraying application after stirring into the cream pasty state;
(5), polishing coarseparticulate, dedusting: after spraying application was finished 24 hours, remove thick thing with sand papering, and remove dust with besom, loosening granular substance, and sweep off loosening granular substance with hard besom, and use air gun is blown away floating dust.
(6), Lacquer finish: carry out the preceding test of spraying of small area earlier, and adjust the Lacquer finish spray gun, make it to reach spraying evenly, the glossiness unanimity is carried out large-area spraying application again.