CN101116896A - 低发气性高透气性水基铸铁树脂砂涂料 - Google Patents

低发气性高透气性水基铸铁树脂砂涂料 Download PDF

Info

Publication number
CN101116896A
CN101116896A CNA2007100279151A CN200710027915A CN101116896A CN 101116896 A CN101116896 A CN 101116896A CN A2007100279151 A CNA2007100279151 A CN A2007100279151A CN 200710027915 A CN200710027915 A CN 200710027915A CN 101116896 A CN101116896 A CN 101116896A
Authority
CN
China
Prior art keywords
weight percent
percent content
cast iron
forming property
low gas
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CNA2007100279151A
Other languages
English (en)
Inventor
陈和平
刘启平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
GUANGDONG SHAOZHU GROUP CO Ltd
Original Assignee
GUANGDONG SHAOZHU GROUP CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by GUANGDONG SHAOZHU GROUP CO Ltd filed Critical GUANGDONG SHAOZHU GROUP CO Ltd
Priority to CNA2007100279151A priority Critical patent/CN101116896A/zh
Publication of CN101116896A publication Critical patent/CN101116896A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种低发气性高透气性水基铸铁树脂砂涂料，包括骨料，该骨料采用土状石墨和磷片石墨，其中骨料中粒度为200目的成分的重量百分比含量大于80％，低于及高于200目的成分的重量百分比含量均小于10％。本发明的配方合理，制作成本低，具有发气性低、透气性高、适应性强的优点，能有效消除铸铁件气孔，提高产品质量，特别适合于对产品质量要求高的铸铁件的生产。

Description

低发气性高透气性水基铸铁树脂砂涂料
【技术领域】
本发明涉及一种涂料，尤其是涉及一种在铸造工艺中使用的低发气性高透气性水基铸铁树脂砂涂料。
【背景技术】
目前，市场上的各种铸造涂料一般用于防止铸件粘砂，虽然其适用性广泛，但对有特殊要求的铸件却不能适应。
例如：在铸造汽车缸盖铸铁件时，对涂料要求就非常高，常见的各种铸造涂料的缺点是：一是在高温(900℃)下，涂料的发气量太大(一般在20ml/g以上，有些甚至达到40ml/g)；二是涂料过细(一般在325目到425目之间)，从而直接导致涂料的透气性太低，使得涂料的透气性低于5cm4/g.min，使用上述高发气性或者低透气性的涂料铸造汽车缸盖铸铁件时，导致产品产生大量气孔废品，严重地影响了产品质量。
【发明内容】
为了克服现有技术的上述缺点，本发明提供一种能消除铸铁件气孔、提高产品质量的低发气性高透气性水基铸铁树脂砂涂料。
本发明解决其技术问题所采用的技术方案是：一种低发气性高透气性水基铸铁树脂砂涂料，包括骨料，该骨料采用土状石墨和磷片石墨，其中骨料中粒度为200目的成分的重量百分比含量大于80％，低于及高于200目的成分的重量百分比含量均小于10％。
所述土状石墨和磷片石墨的重量配比是1∶1。
所述低发气性高透气性水基铸铁树脂砂涂料中还添加有辅料，该辅料组分包括钠基膨润土、羟甲其纤维素、酚醛树脂、乳化剂和正辛醇
所述辅料中各组分的重量百分比含量分别是：钠基膨润土的重量百分比含量小于2.5％、羟甲其纤维素的重量百分比含量小于0.2％、酚醛树脂的重量百分比含量小于1％、乳化剂的重量百分比含量小于0.3％、正辛醇的重量百分比含量小于0.03％。
所述辅料的组分还有氢氧化钠，氢氧化钠的重量百分比含量为辅料中酚醛树脂的重量百分比含量的5％。
本发明的有益效果是：本发明的配方合理，制作成本低，具有发气性低、透气性高、适应性强的优点，能有效消除铸铁件气孔，提高产品质量，特别适合于对产品质量要求高的铸铁件的生产。
【具体实施方式】
下面结合实施例对本发明进一步说明。
一种低发气性高透气性水基铸铁树脂砂涂料，包括骨料，该骨料采用土状石墨和磷片石墨，所述土状石墨和磷片石墨的重量配比采用1∶1，其中骨料中粒度为200目的成分的重量百分比含量大于80％，低于及高于200目的成分的重量百分比含量均小于10％；在本发明所述低发气性高透气性水基铸铁树脂砂涂料中还添加有辅料，该辅料组分包括钠基膨润土、羟甲其纤维素、酚醛树脂、乳化剂和正辛醇，其中钠基膨润土的重量百分比含量小于2.5％、羟甲其纤维素的重量百分比含量小于0.2％、酚醛树脂的重量百分比含量小于1％、乳化剂的重量百分比含量小于0.3％、正辛醇的重量百分比含量小于0.03％；在辅料中添加有氢氧化钠，氢氧化钠的重量百分比含量为辅料中酚醛树脂的重量百分比含量的5％。
在配制本发明时，先将钠基膨润土、羟四基纤维素和酚醛树脂分别提前泡好，然后把泡好的钠基膨润土和羟甲基纤维在使用前用胶体磨研磨均匀，酚醛树脂溶解完后加入氢氧化钠进行乳化，然后再加入到搅拌机中，在搅拌机中加入水，然后加入钠基膨润土、羟甲基纤维素和乳化好的酚醛树脂溶液，进行搅拌，再加入石墨粉、乳化剂和正辛醇进行搅拌；最后进行静置、待用。本发明的实测性能是：发气量是13.5ml/g；透气性：16cm4/g.min，在本实施例中乳化剂采用烷基酚聚氧乙烯醚。采用本发明所铸造的产品气孔废品基本消除，同时铸件也不粘砂。

Claims (6)

1.一种低发气性高透气性水基铸铁树脂砂涂料，包括骨料，其特征是：该骨料采用土状石墨和磷片石墨，其中骨料中粒度为200目的成分的重量百分比含量大于80％，低于及高于200目的成分的重量百分比含量均小于10％。
2.如权利要求1所述的低发气性高透气性水基铸铁树脂砂涂料，其特征是：所述土状石墨和磷片石墨的重量配比是1∶1。
3.如权利要求1或2所述的低发气性高透气性水基铸铁树脂砂涂料，其特征是：所述低发气性高透气性水基铸铁树脂砂涂料中还添加有辅料，该辅料组分包括钠基膨润土、羟甲其纤维素、酚醛树脂、乳化剂和正辛醇。
4.如权利要求3所述的低发气性高透气性水基铸铁树脂砂涂料，其特征是：所述辅料中各组分的重量百分比含量分别是：钠基膨润土的重量百分比含量小于2.5％、羟甲其纤维素的重量百分比含量小于0.2％、酚醛树脂的重量百分比含量小于1％、乳化剂的重量百分比含量小于0.3％、正辛醇的重量百分比含量小于0.03％。
5.如权利要求3所述的低发气性高透气性水基铸铁树脂砂涂料，其特征是：所述辅料的组分还有氢氧化钠，氢氧化钠的重量百分比含量为辅料中酚醛树脂的重量百分比含量的5％。
6.如权利要求4所述的低发气性高透气性水基铸铁树脂砂涂料，其特征是：所述辅料的组分还有氢氧化钠，氢氧化钠的重量百分比含量为辅料中酚醛树脂的重量百分比含量的5％。
CNA2007100279151A 2007-04-30 2007-04-30 低发气性高透气性水基铸铁树脂砂涂料 Pending CN101116896A (zh)