CN101284973B - 胶合板胶粘剂专用填充剂 - Google Patents

胶合板胶粘剂专用填充剂 Download PDF

Info

Publication number
CN101284973B
CN101284973B CN2008100163893A CN200810016389A CN101284973B CN 101284973 B CN101284973 B CN 101284973B CN 2008100163893 A CN2008100163893 A CN 2008100163893A CN 200810016389 A CN200810016389 A CN 200810016389A CN 101284973 B CN101284973 B CN 101284973B
Authority
CN
China
Prior art keywords
agent
glued board
filling agent
board adhesive
filling
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN2008100163893A
Other languages
English (en)
Other versions
CN101284973A (zh
Inventor
魏孝新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANDONG XINGANG GROUP CO Ltd
Original Assignee
SHANDONG XINGANG GROUP CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANDONG XINGANG GROUP CO Ltd filed Critical SHANDONG XINGANG GROUP CO Ltd
Priority to CN2008100163893A priority Critical patent/CN101284973B/zh
Publication of CN101284973A publication Critical patent/CN101284973A/zh
Application granted granted Critical
Publication of CN101284973B publication Critical patent/CN101284973B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种胶合板胶粘剂专用填充剂，属于胶合板生产技术领域，其特征是，所述的填充剂由如下重量份的原料混合而成：高岭土40-60；玉米蛋白40-50；改性剂0～5。所述填充剂的加入量为胶粘剂总重量的20～30％。本发明能够有效降低胶合板胶粘剂的成本，且甲醛释放量低。

Description

胶合板胶粘剂专用填充剂
技术领域
本发明属于胶合板生产技术领域，具体涉及一种胶合板胶粘剂专用填充剂。
背景技术
木质人造板，是利用木材木质纤维、碎料和其他植物纤维为原料，加胶黏剂和其他添加剂制成材。由于木材生长缓慢，现有的森林资源远远不能满足我国建设事业发展的需要，而人造板则是替代木材的最佳材料，其产品主要是胶合板、纤维板及刨花板。胶合板、细木工板、中密度纤维板和刨花板等胶合板，目前主要使用的胶粘剂是脲醛树脂、酚醛树脂。为增加树脂的初粘度、提高柸板的预压效果、降低胶粘剂的成本，均要在树脂中添加填充剂，面粉是普遍采用的填充剂，面粉的加入量在20-30％。
其不足之处：1)面粉价格高，约2000元/吨，提高了胶合板的成本；2)胶粘剂脲醛树脂、酚醛树脂是产生甲醛的主要因素。
公开号为CN1821334的中国专利公开了一种用于胶合板的酚醛树脂胶及其调制方法，该方法采用以下步骤：在酚醛树脂中加入用量为酚醛树脂重量的0.02-0.8％的高吸水性树脂以及用量为酚醛树脂重量10-20％的面粉，然后将其加入调胶机中，搅拌至各组分混合均匀。不但有效防止了胶合板生产中涂胶单板的陈化过度，保证涂胶单板即使在风大、湿度低的情况下进行长时间的陈化，也不会出现板坯预压效果不好和在胶合板热压后出现开胶情况，而且基本不改变原有酚醛树脂的调胶工艺，简单易行，成本低。
公开号为CN1820914的中国专利公开了一种胶合板高效填充料，它是利用木粉、蛋白血粉等有机和无机矿物质混合而成的粉状物，用有机膨润土、无机膨润土和有机纤维素起增稠作用，用木粉起填充作用，用粘木粉、水玻璃和蛋白血粉起增加粘性作用，并且水玻璃和蛋白血粉还有吸收甲醛的作用。本发明配方进行了优化和改进，价格更加低廉，兼具环保功能，具有良好的市场前景。
发明内容
本发明针对现有技术中存在的问题，提供了一种胶合板胶粘剂专用填充剂，它通过采用价格较低的原料代替面粉，而且添加了吸收甲醛的组合物，解决了现有技术中的问题。采用本发明生产的胶合板甲醛释放量须≤0.2mg/L。
本发明具体采用如下技术方案：
一种胶合板胶粘剂专用填充剂，其特征是，所述的填充剂由如下重量份的原料混合而成：
高岭土    40-60
玉米蛋白  40-50
改性剂    0～5
所述填充剂的加入量为胶合板胶粘剂总重量的20～30％。
所述的改性剂是纳米SiO2、API胶中的一种或二者的混合物。
所述的改性剂是有机氨钙和API胶的混合物，其中：API胶占二者总重的90～95％。
所述的改性剂是有机氨钙和水玻璃的混合物，其中：水玻璃占二者总重的90～95％。
所述的改性剂是茶多酚和API胶或水玻璃的混合物，其中：API胶占二者总重的80～90％。
本发明的填充剂在使用时，按照以下步骤：先将填充剂混合均匀，在脲醛树脂或酚醛树脂胶粘剂高速搅拌的情况下加入填充剂，搅拌均匀即可。
本发明的有益效果如下：
1)本发明的填充剂成本低。现有技术中面粉的成本较高，大约2000元/T左右，本发明使用高岭土及玉米蛋白的混合物替代面粉，成本在800元/T左右，大大降低了人造板的制造成本，而人造板的物理力学性能均能达到或超过GB/T9846-2004规定的胶合板的性能指标.
2)本发明能够有效降低甲醛的释放量，根据试验，其释放量≤0.2mg/L，远远低于国家标准≤1.5mg/L。
使用本发明填充剂较低胶粘剂甲醛释放的原因是：1)使用API胶可以较少部分脲醛树脂或者酚醛树脂的用量；2)茶多酚、有机氨钙、水玻璃具有吸收甲醛的作用。
具体实施方式
实施例1
高岭土50～60Kg，玉米蛋白40～50Kg，均匀混合得本发明的填充剂。
实施例2
高岭土45～60Kg，玉米蛋白40～50Kg，纳米SiO2与API胶共重5Kg，其中，纳米SiO2与API胶任意配比。
实施例3
高岭土45～60Kg，玉米蛋白40～50Kg，有机氨钙与API胶共重5Kg，其中，  API胶为4.5～4.75Kg。
实施例4
高岭土45～60Kg，玉米蛋白40～50Kg，有机氨钙与水玻璃共重5Kg，其中，水玻璃为4.5～4.75Kg。
实施例5
高岭土45～60Kg，玉米蛋白40～50Kg，茶多酚与水玻璃(API胶)共重5Kg，其中，水玻璃为4.5～4Kg。

Claims (2)

1.一种胶合板胶粘剂专用填充剂，其特征是，所述的填充剂由如下重量份的原料混合而成：
高岭土       40-60
玉米蛋白     40-50
改性剂       0～5
所述填充剂的加入量为胶合板胶粘剂总重量的20～30％；
所述的改性剂是纳米SiO2、API胶中的一种或二者的混合物，或者
所述的改性剂是茶多酚和API胶或水玻璃的混合物，其中：API胶占二者总重的80～90％。
2.根据权利要求1中任一项所述的胶合板胶粘剂专用填充剂，其特征是，所述的胶粘剂是脲醛树脂或酚醛树脂中的一种。
CN2008100163893A 2008-05-28 2008-05-28 胶合板胶粘剂专用填充剂 Expired - Fee Related CN101284973B (zh)