CN101112782A - 橡胶地砖制作方法 - Google Patents
橡胶地砖制作方法 Download PDFInfo
- Publication number
- CN101112782A CN101112782A CNA2006100149825A CN200610014982A CN101112782A CN 101112782 A CN101112782 A CN 101112782A CN A2006100149825 A CNA2006100149825 A CN A2006100149825A CN 200610014982 A CN200610014982 A CN 200610014982A CN 101112782 A CN101112782 A CN 101112782A
- Authority
- CN
- China
- Prior art keywords
- floor tile
- rubber
- mixture
- temperature
- roller mill
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
一种橡胶地砖制作方法，将废橡胶轮胎打碎、分离、滤取橡胶颗粒，将包括色母、粘合剂、硫磺、滑石粉及三氧化二锑在内的原料混合配制成初级混合物，将初级混合物放入轧辊机内混合搅拌成面团形状，将该面团状的初级混合物与上述橡胶颗粒混合，放入轧辊机内混合搅拌成面团形状二级混合物，将该面团状二级混合物放在轧辊机内加热，并压制成片材，将该片材裁剪，放入硫化机模具内，硫化成产品，去除毛边即制成地砖。本发明的优点：废橡胶轮胎再利用，耐磨、防滑、吸音、透气，质地柔软，具有弹性。
Description
技术领域
本发明涉及涉及一种橡胶地砖制作方法。
背景技术
传统的废橡胶制成的橡胶地砖，只能在黑色表面漆刷各种颜色，使用不久后，黑色就会显露出来，影响了美观。这种彩色橡胶地砖经合成压成型后，由于颗粒之间结合不好，制成的地砖缺乏硬度，缺乏柔软弹性、透气性、吸音和防滑性差。
发明内容
本发明的目的在于克服上述的缺陷，提供一种橡胶地砖制作方法。
本发明的技术方案是：一种橡胶地砖制作方法，其特征在于：将废橡胶打碎、分离并滤取合适的橡胶颗粒，将包括色母、粘合剂、硫磺、滑石粉及三氧化二锑的原料混合配制成初级混合物，将该初级混合物放入轧辊机内混合搅拌三小时以上，温度100℃，混合搅拌成面团形状，再将该面团状初级混合物与上述橡胶颗粒混合，放入轧辊机内混合搅拌三小时，温度100℃，混合搅拌成面团形状二级混合物，然后将该面团状二级混合物加热压成片材，最后将该片材裁剪成所需尺寸，放入硫化机的模具内，温度100℃，时间1小时，硫化成产品，再去除毛边制成地砖。
本发明具有以下优点：解决废橡胶轮胎再利用，具有多种颜色，耐磨、防滑、吸音、透气，质地柔软，具有弹性，其表面可制作成各种美观大方的花纹和图形。
具体实施方式
实施例：一种橡胶地砖制作方法，将废弃的橡胶轮胎打碎、分离、滤取适度的橡胶颗粒，再将包括色母、粘合剂、硫磺、滑石粉及三氧化二锑在内的原料按适当的比例混合配制成初级混合物，将初级混合物放入轧辊机内混合搅拌3小时以上，温度100℃，混合搅拌成面团形状，再将该面团状的初级混合物与上述橡胶颗粒混合，放入轧辊机内混合搅拌3小时，温度100℃，混合搅拌成面团形状二级混合物。然后将该面团状二级混合物放在轧辊机内加热，并压制成片材.最后将该片材根据需要裁剪成所需尺寸，放入硫化机模具内，温度100℃，时间1小时，硫化成产品，去除毛边即制成地砖。
Claims (1)
1.一种橡胶地砖制作方法，其特征在于：将废弃的橡胶轮胎打碎、分离、滤取适度的橡胶颗粒，再将包括色母、粘合剂、硫磺、滑石粉及三氧化二锑在内的原料按适当的比例混合配制成初级混合物，将初级混合物放入轧辊机内混合搅拌3小时以上，温度100℃，混合搅拌成面团形状，再将该面团状的初级混合物与上述橡胶颗粒混合，放入轧辊机内混合搅拌3小时，温度100℃，混合搅拌成面团形状二级混合物。然后将该面团状二级混合物放在轧辊机内加热，并压制成片材.最后将该片材根据需要裁剪成所需尺寸，放入硫化机模具内，温度100℃，时间1小时，硫化成产品，去除毛边即制成地砖。