CN101100780A - 低支无捻超柔软浴巾及其制造方法 - Google Patents
低支无捻超柔软浴巾及其制造方法 Download PDFInfo
- Publication number
- CN101100780A CN101100780A CNA2006100911715A CN200610091171A CN101100780A CN 101100780 A CN101100780 A CN 101100780A CN A2006100911715 A CNA2006100911715 A CN A2006100911715A CN 200610091171 A CN200610091171 A CN 200610091171A CN 101100780 A CN101100780 A CN 101100780A
- Authority
- CN
- China
- Prior art keywords
- water intaking
- content
- dissolves
- dyestuff
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明一种低支无捻超柔软浴巾及制造方法,提供了一种经过煮漂、中和、脱氧、染色、皂煮、酵洗、加软等步骤的制造低支无捻超柔软浴巾的方法,利用此方法,可以得到一种以纯棉为基本原料的,外观漂亮美观,手感柔软丰满,并且摆脱以往产品质地粗糙、坚硬的弊端,并且具有健康、安全、人性化等特点的新型低支无捻超柔软浴巾。
Description
技术领域
本发明涉及一种日常物品及其制造方法,特别是一种浴巾织物及其制造方法。
背景技术
浴巾是日常生活中必不可少的生活用品,现有浴巾其结构比较简单,制作工艺古老陈旧,所生产出的产品图案单一,档次不高,在市场上的竞争力明显不足。
现有浴巾产品,其质地相对粗糙,坚硬,产品原料参差不齐,并且功能单一,在安全功能(抗菌、阻燃、防静电、预测、报警等)、人性化功能(柔软、舒适、吸湿、透气、干爽、润滑等)、卫生功能(理疗、减肥、防褥疮、尿不湿、防螨虫、防蚊虫等)方面往往都没有涉及,不能满足现今消费者对浴巾及其同类产品的多种功能的需求。
特别是,对于前两年爆发的SARS,大大提高人们对健康的关注,更是使得现在的消费者对于浴巾及其同类产品的需求不进在于其使用舒适、美观好看,而且对其相应的附加功能也有相当的需求。
发明内容
本发明的目的在于:提供一种以纯棉为基本原料的,外观漂亮美观,手感柔软丰满,并且摆脱以往产品质地粗糙、坚硬的弊端,并且具有健康、安全、人性化等特点的新型低支无捻超柔软浴巾及其制造方法。
本发明所采用的技术方案为:
本发明的低支无捻超柔软浴巾,其中:
原料为100%优质环锭纺精梳纱线;
毛经为9S无捻纱,64.8rex:棉绒长度在33mm以上;地经为18.2×2tex纯棉纱,复合捻度为16捻/英寸,修正强力≥600CN;纬纱为OEC44.8tex纯棉纱和29.2×2tex丝光棉;
成品经密为220根/10cm;成品纬密为162根/10cm;
上机筘号:56齿/2英寸,上机密度:40根/英寸;
毛经1∶1,地经1∶1∶2入筘;
毛倍:6.2,毛圈长度:1.20cm。
本发明的低支无捻超柔软浴巾的制造方法,其中包括以下工序:
一、前处理工艺:
1)、将原料煮漂,整体过程30分钟,温度105摄氏度:
取水8l,溶入火碱,火碱含量为5ml/l,进行第一步煮漂;
取水5l,溶入稳定剂,稳定剂含量为3ml/l,进行第二步煮漂;
取水12l,溶入双氧水,双氧水含量为7.8ml/l,进行第三步煮漂。
2)、中和,整体过程10分钟:
取水1.5升,溶入醋酸,醋酸含量为1ml/l。
3)、脱氧,整体过程20分钟,温度40摄氏度:
取水0.18l,溶入脱氧酶,脱氧酶含量为0.12ml/l。
二、染色工艺,整体过程30分钟,温度60摄氏度:
1)、主料染色:
染料:100%RR红,取水58g,染料含量0.0400%;
染料:100%RR黄,取水251g,染料含量0.1650%;
染料:100%RR兰,取水102g,染料含量0.0680%。
2)、副料染色:
染料:元明粉,取水15kg,溶入元明粉,元明粉含量为10g/l;
染料:纯碱,取水11kg,溶入纯碱,纯碱含量为7g/l。
三、皂煮工艺,整体过程15分钟,温度90摄氏度:
取水200g,溶入洗净剂,洗净剂含量为0.13g/l。
四、酵洗工艺,整体过程30分钟,温度50摄氏度:
1)、取水0.67kg,溶入醋酸;
2)、取水1.6kg,溶入纤柔酶、
五、加软工艺,整体过程20分钟,温度40摄氏度:
取水4l,溶入柔软剂288,柔软剂288的含量为2.7ml/l。
采用上述的浴巾结构及制造方法,可以得到一种以纯棉为基本原料的,外观漂亮美观,手感柔软丰满,并且摆脱以往产品质地粗糙、坚硬的弊端,并且具有健康、安全、人性化等特点的新型低支无捻超柔软浴巾。
附图说明
图1是本发明的工艺流程图。
具体实施方式
为能使贵审查员清楚本发明的主要技术内容,以及实施方式,兹以实施例说明如下:
本发明的低支无捻超柔软浴巾,其主要技术参数如下:
1、原料:100%优质环锭纺精梳纱线(棉绒长度在33mm以上,用埃及棉和新疆棉)
2、纱支:
毛经为9S无捻纱(64.8rex):棉绒长度在33mm以上,用埃及棉和新疆棉;
地经为18.2×2tex纯棉纱,复合捻度为16捻/英寸,修正强力≥600CN;
纬纱为OEC44.8tex纯棉纱和29.2×2tex丝光棉。
3、成品经密:220根/10cm;
4、成品纬密:162根/10cm;
5、组织(三纬毛巾组织):
上机筘号:56齿/2英寸,上机密度:40根/英寸;
毛经1∶1,地经1∶1∶2入筘;
6、规格:70cm×140cm;
7、重量:610克/条;
8、毛倍:6.2,毛圈长度:1.20cm。
本发明的低支无捻超柔软浴巾的制造方法如下:
如图1所示,其制作流程基本为:
原棉→纺纱→合水溶丝→整经→织造→退水溶丝→漂煮→染色→烘干→整理→包装。
其具体制造方法举例如下,其原料物重145kg,共用水1500l:
一、前处理工艺:
1、将原料煮漂,整体过程30分钟,温度105摄氏度:
取水8l,溶入火碱,火碱含量为5ml/l,进行第一步煮漂;
取水5l,溶入稳定剂,稳定剂含量为3ml/l,进行第二步煮漂;
取水12l,溶入双氧水,双氧水含量为7.8ml/l,进行第三步煮漂。
2、中和,整体过程10分钟:
取水1.5升,溶入醋酸,醋酸含量为1ml/l。
3、脱氧,整体过程20分钟,温度40摄氏度:
取水0.18l,溶入脱氧酶,脱氧酶含量为0.12ml/l。
二、染色工艺,整体过程30分钟,温度60摄氏度:
1、主料染色:
染料:100%RR红,取水58g,染料含量0.0400%;
染料:100%RR黄,取水251g,染料含量0.1650%;
染料:100%RR兰,取水102g,染料含量0.0680%。
2、副料染色:
染料:元明粉,取水15kg,溶入元明粉,元明粉含量为10g/l;
染料:纯碱,取水11kg,溶入纯碱,纯碱含量为7g/l。
三、皂煮工艺,整体过程15分钟,温度90摄氏度:
取水200g,溶入洗净剂,洗净剂含量为0.13g/l。
四、酵洗工艺,整体过程30分钟,温度50摄氏度:
1、取水0.67kg,溶入醋酸;
2、取水1.6kg,溶入纤柔酶、
五、加软工艺,整体过程20分钟,温度40摄氏度:
取水4l,溶入柔软剂288,柔软剂288的含量为2.7ml/l。
完成上述工艺后,即可出布,脱水,烘干,得到所需产品。
Claims (2)
1、一种低支无捻超柔软浴巾,其特征在于:
原料为100%优质环锭纺精梳纱线;
毛经为9S无捻纱,64.8rex:棉绒长度在33mm以上;地经为18.2×2tex纯棉纱,复合捻度为16捻/英寸,修正强力≥600CN;纬纱为OEC44.8tex纯棉纱和29.2×2tex丝光棉;
成品经密为220根/10cm;成品纬密为162根/10cm;
上机筘号:56齿/2英寸,上机密度:40根/英寸;
毛经1∶1,地经1∶1∶2入筘;
毛倍:6.2,毛圈长度:1.20cm。
2、一种低支无捻超柔软浴巾的制造方法,其特征在于包括以下工序:
一、前处理工艺:
1)、将原料煮漂,整体过程30分钟,温度105摄氏度:
取水8l,溶入火碱,火碱含量为5ml/l,进行第一步煮漂;
取水5l,溶入稳定剂,稳定剂含量为3ml/l,进行第二步煮漂;
取水12l,溶入双氧水,双氧水含量为7.8ml/l,进行第三步煮漂;
2)、中和,整体过程10分钟:
取水1.5升,溶入醋酸,醋酸含量为1ml/l;
3)、脱氧,整体过程20分钟,温度40摄氏度:
取水0.18l,溶入脱氧酶,脱氧酶含量为0.12ml/l;
二、染色工艺,整体过程30分钟,温度60摄氏度:
1)、主料染色:
染料:100%RR红,取水58g,染料含量0.0400%;
染料:100%RR黄,取水251g,染料含量0.1650%;
染料:100%RR兰,取水102g,染料含量0.0680%;
2)、副料染色:
染料:元明粉,取水15kg,溶入元明粉,元明粉含量为10g/l;
染料:纯碱,取水11kg,溶入纯碱,纯碱含量为7g/l;
三、皂煮工艺,整体过程15分钟,温度90摄氏度:
取水200g,溶入洗净剂,洗净剂含量为0.13g/l;
四、酵洗工艺,整体过程30分钟,温度50摄氏度:
1)、取水0.67kg,溶入醋酸;
2)、取水1.6kg,溶入纤柔酶;
五、加软工艺,整体过程20分钟,温度40摄氏度:
取水4l,溶入柔软剂288,柔软剂288的含量为2.7ml/l。