CN101077925A - 高表面硬度pc－abs树脂的改性配方 - Google Patents

高表面硬度pc－abs树脂的改性配方 Download PDF

Info

Publication number
CN101077925A
CN101077925A CN 200610035661 CN200610035661A CN101077925A CN 101077925 A CN101077925 A CN 101077925A CN 200610035661 CN200610035661 CN 200610035661 CN 200610035661 A CN200610035661 A CN 200610035661A CN 101077925 A CN101077925 A CN 101077925A
Authority
CN
China
Prior art keywords
parts
abs resin
surface hardness
abs
high surface
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610035661
Other languages
English (en)
Other versions
CN101077925B (zh
Inventor
汪克风
岳瑟
杨得志
刘济林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mitac Precision Technology Shunde Ltd
Original Assignee
Mitac Precision Technology Shunde Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitac Precision Technology Shunde Ltd filed Critical Mitac Precision Technology Shunde Ltd
Priority to CN2006100356613A priority Critical patent/CN101077925B/zh
Publication of CN101077925A publication Critical patent/CN101077925A/zh
Application granted granted Critical
Publication of CN101077925B publication Critical patent/CN101077925B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高表面硬度PC－ABS树脂的改性配方，由60～85份PC－ABS树脂原料、12～25份PMMA、1～5份CPE、1～5份接枝共聚物、1～7份增韧剂的组分组成。本发明提供的PC－ABS树脂改性配方在对PC－ABS树脂的力学性能改变不大的基础上提高了其表面硬度，扩大了其应用领域。该配方既降低了PC－ABS树脂加工工艺成本，又不会因传统工艺的喷漆处理而对环境造成额外的负担。

Description

高表面硬度PC-ABS树脂的改性配方
技术领域
本发明涉及高分子材料技术中热塑性树脂组合物领域，具体涉及一种高表面硬度PC(Polycarbonate，聚碳酸酯)-ABS树脂的改性配方。
背景技术
PC-ABS树脂是60年代发展起来的一种综合性能优越的工程塑料，它既具有PC的耐热性、机械强度和尺寸稳定性，又具有ABS树脂的易加工性和价廉等优点，综合性能好，性价比合理，广泛应用于汽车工业、家用电器、日用品等领域。由于PC-ABS树脂树脂广泛用于电子电器产品的面板制作中，为维持面板的形状长久及外观美感，对其有较高的表面硬度要求。在以往的工艺中，均采用表面喷漆的方法来提高PC-ABS树脂的表面硬度，但是表面喷漆工艺一方面对环境和人体带来不良影响，另一方面增加了加工工艺及提高了生产成本。为此，研究和开发一种对PC-ABS进行硬化改性的配方已经十分必要。
发明内容
本发明的目的在于提供一种高表面硬度PC-ABS树脂的改性配方，对PC-ABS树脂进行改性。
为达到上述目的，本发明提供的高表面硬度PC-ABS树脂的改性配方是在PC-ABS树脂中添加抗冲改性剂、增容剂等进行改性，从而提高PC-ABS的机械性能和表面硬度，使PC-ABS的应用更加广泛。
本发明提供的一种高表面硬度PC-ABS树脂的改性配方，由按质量份数计算的下列组分组成：
(a)PC-ABS树脂原料                    60～85份
(b)PMMA(聚甲基丙烯酸甲酯)            12～25份
(c)CPE(氯化聚乙烯)                   1～5份
(d)接枝共聚物                        1～5份
(e)增韧剂                            1～7份
上述配方中的接枝共聚物是马来酸酐接枝ABS、SEBS(饱和苯乙烯-丁二烯-苯乙烯嵌段共聚物)或PS共聚物(即ABS-g-MAH、SEBS-g-MAH或PS-g-MAH)。
上述配方中的增韧剂是MBS、MMB或ASA。
优选地，上述高表面硬度PC-ABS树脂的改性配方，由按质量份数计算的下列组分组成：
(a)PC-ABS树脂原料        63份
(b)PMMA                  24份
(c)CPE                   4份
(d)ABS-g-MAH             3份
(e)MBS                   6份
优选地，上述高表面硬度PC-ABS树脂的改性配方，由按质量份数计算的下列组分组成：
(a)PC-ABS树脂原料        73.6份
(b)PMMA                  18.4份
(c)CPE                   1份
(d)ABS-g-MAH             2份
(e)MBS                   5份
优选地，上述高表面硬度PC-ABS树脂的改性配方，由按质量份数计算的下列组分组成：
(a)PC-ABS树脂原料        80份
(b)PMMA                  13份
(c)CPE                   3份
(d)ABS-g-MAH             2份
(e)MBS                   2份
本发明提供的高表面硬度PC-ABS树脂的改性配方，在对PC-ABS树脂的力学性能改变不大的基础上提高了其表面硬度，扩大了其应用领域。该配方既降低了PC-ABS树脂加工工艺成本，又不会因传统工艺的喷漆处理而对环境造成额外的负担。
具体实施方式
实施例1
取PC-ABS树脂原料、PMMA、CPE、接枝共聚物、增韧剂等成分，按下述组成配方将所有原料进行共混：
(a)PC-ABS树脂原料        63份
(b)PMMA                  24份
(c)CPE                   4份
(d)ABS-g-MAH             3份
(e)MBS                   6份
再将该共混料通过挤出机中混炼造粒，所得混炼造粒经注射成型制成成品，最后按国家标准GB13525/T-92测试所得成品的机械性能及表面硬度，结果如表1所示。
表1：实施例1所得PC经ABS改性后的树脂性能
    项目     原料     改性料
    冲击强度(kJ/M2)     40     35.17
    拉伸强度(MPa)     64     62.96
    表面硬度     2B     HB
    M1(g/10min)     19     20.61
实施例2
取PC-ABS树脂原料、PMMA、CPE、接枝共聚物、增韧剂等成分，按下述组成配方将所有原料进行共混：
(a)PC-ABS树脂原料      73.6份
(b)PMMA                18.4份
(c)CPE                 1份
(d)ABS-g-MAH           2份
(e)MBS                 5份
再将该共混料通过挤出机中混炼造粒，所得混炼造粒经注射成型制成成品，最后按国家标准GB13525/T-92测试所得成品的机械性能及表面硬度，结果如表1所示。
表2：实施例2所得PC经ABS改性后的树脂性能
    项目     原料     改性料
    冲击强度(kJ/M2)     40     40.87
    拉伸强度(MPa)     64     66.12
    表面硬度     2B     HB
    M1(g/10min)     19     17.67
实施例3
取PC-ABS树脂原料、PMMA、CPE、接枝共聚物、增韧剂等成分，按下述组成配方将所有原料进行共混：
(a)PC-ABS树脂原料    73.6份
(b)PMMA              18.4份
(c)CPE               1份
(d)ABS-g-MAH         2份
(e)MBS               5份
再将该共混料通过挤出机中混炼造粒，所得混炼造粒经注射成型制成成品，最后按国家标准GB13525/T-92测试所得成品的机械性能及表面硬度，结果如表1所示。
表3：实施例3所得PC经ABS改性后的树脂性能
    项目     原料     改性料
    冲击强度(kJ/M2)     40     42.21
    拉伸强度(MPa)     64     70.27
    表面硬度     2B     HB
    M1(g/10min)     19     19.45
以上具体实施方式，是对本发明所作的详细说明。注意这些实施方式并非用以限定本发明，对于本领域的熟练技术人员，在不背离本发明精神的情况下所做出的改进和补充，应该视为在本发明的保护范围之内。

Claims (6)

1.一种高表面硬度PC-ABS树脂的改性配方，其特征在于，由按质量份数计算的下列组分组成：
(a)PC-ABS树脂原料               60～85份
(b)PMMA                         12～25份
(c)CPE                          1～5份
(d)接枝共聚物                   1～5份
(e)增韧剂                       1～7份。
2.根据权利要求1所述的高表面硬度PC-ABS树脂的改性配方，其特征在于，所述接枝共聚物是ABS-g-MAH、SEBS-g-MAH或PS-g-MAH。
3.根据权利要求1所述的高表面硬度PC-ABS树脂的改性配方，其特征在于，所述增韧剂是MBS、MMB或ASA。
4.根据权利要求1-3中任意一项所述的高表面硬度PC-ABS树脂的改性配方，其特征在于，由按质量份数计算的下列组分组成：
(a)PC-ABS树脂原料               63份
(b)PMMA                         24份
(c)CPE                          4份
(d)ABS-g-MAH                    3份
(e)MBS                          6份。
5.根据权利要求1-3中任意一项所述的高表面硬度PC-ABS树脂的改性配方，其特征在于，由按质量份数计算的下列组分组成：
(a)PC-ABS树脂原料               73.6份
(b)PMMA                         18.4份
(c)CPE                          1份
(d)ABS-g-MAH                    2份
(e)MBS                          5份。
6.根据权利要求1-3中任意一项所述的高表面硬度PC-ABS树脂的改性配方，其特征在于，由按质量份数计算的下列组分组成：
(a)PC-ABS树脂原料               80份
(b)PMMA                         13份
(c)CPE                             3份
(d)ABS-g-MAH                       2份
(e)MBS                             2份。
CN2006100356613A 2006-05-26 2006-05-26 高表面硬度pc-abs树脂的改性组合物 Expired - Fee Related CN101077925B (zh)