CN101041751B - 一种高动态抗开裂型弹性腻子 - Google Patents
一种高动态抗开裂型弹性腻子 Download PDFInfo
- Publication number
- CN101041751B CN101041751B CN200610146092A CN200610146092A CN101041751B CN 101041751 B CN101041751 B CN 101041751B CN 200610146092 A CN200610146092 A CN 200610146092A CN 200610146092 A CN200610146092 A CN 200610146092A CN 101041751 B CN101041751 B CN 101041751B
- Authority
- CN
- China
- Prior art keywords
- type elastic
- highly dynamic
- resistant type
- component
- cracking resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种高动态抗开裂型弹性腻子，它由按重量百分比计算的A、B组分组成。其中A组分是由水3-6％；1.5％纤维素醚溶液14-20％；分散剂0.4-0.6％；消泡剂0.3-0.5％；木质纤维素0.2-0.4％；聚丙烯纤维0.3-0.5％；滑石粉6-10％；石英砂40-46％；弹性乳液24-35％；B组分是由白水泥65-90％；重钙10-35％。施工时，A与B的配合比例为A∶B＝1.5∶1。该弹性腻子不仅具有高动态抗开裂性，还具有高效防水、抗渗等性能，能显著改善墙体的开裂性能等优点，防止涂膜表面出现病态。
Description
技术领域 本发明涉及一种涂料，特别涉及一种防止建筑物外墙表面开裂的弹性腻子，属于化工涂料技术领域。
背景技术 在建筑涂料的施工过程中，腻子质量的好坏对涂膜质量起着决定性的作用，涂膜表面出现的开裂、脱落等问题与底层腻子有直接的联系。而现在市场上的弹性腻子动态抗开裂效果都不是很理想，例如公开号CN1693329A名称为“一种柔性纤维抗裂腻子及其制备方法”的专利申请中涉及的腻子虽然具有一定的抗裂能力和防水抗渗性能，但动态抗开裂性指标还是达不到理想的标准。因此研究具有高动态抗开裂性、高效防水抗渗性能的弹性腻子意义重大。
发明内容 本发明的目的是提供一种弹性腻子，该弹性腻子不仅具有高动态抗开裂性，还具有高效防水、抗渗等性能，能显著改善墙体的开裂性能等优点，防止涂膜表面出现病态。
一种高动态抗开裂型弹性腻子按重量百分比计算A、B两个组份为：
A组分：水：3-6％；1.5％纤维素醚溶液：14-20％；分散剂：0.4-0.6％；消泡剂：0.3-0.5％；木质纤维素：0.2-0.4％；聚丙烯纤维：0.3-0.5％；滑石粉：6-10％；石英砂：40-46％；弹性乳液：24-35％；
B组分：白水泥：65-90％；重钙：10-35％；
A组分与B组分的重量配合比例为：A∶B＝1.5∶1。
本发明使用的弹性乳液为无增塑剂的阴离子型苯乙烯/丙烯酸酯共聚物，固体含量为56-58％，最低成膜温度在-7℃。可以改善水泥的柔软性，并具有优良的耐水，耐碱及低温弹性。
本发明使用的纤维素醚溶液为1.5％的羟丙基甲基纤维素溶液，分子量为55000。具有优异的保水性，良好的温度稳定性，改善腻子施工性，提高粘结强度。
本发明使用的木质纤维素长度为300-400μm，密度为0.8～1.3g/cm3。具有优异的和易性，抗流坠性能，提高材料表面强度和与基层的粘结强度，并能起到了很好的抗裂作用。
本发明使用的聚丙烯纤维为经过特殊的抽丝生产工艺及表面处理的100％聚丙烯，长度为3-4mm。能够提高与水泥材料的握裹力，使掺有纤维的腻子极限拉伸率提高，从而极大地提高腻子的抗开裂性能。此外，该纤维可以迅速容易的与腻子混合均匀，呈单丝状态均匀的分布在体系中，形成一个均匀的三维网状乱向支撑体系。从而产生一种有效地加强效果，达到抗裂、抗渗、抗冲击、抗冻的目的。
本发明使用的分散剂为低分子量聚丙烯酸钠盐分散剂，可以显著提高填料分散浆的浓度及其稳定性，通过这种分散剂，可以在填料颗粒表面包围一层电荷，使颗粒之间相互排斥，从而达到稳定浆料的效果。
本发明使用的滑石粉为325目，石英砂为200目，重钙为400目，白水泥的标号为425#。
本发明的生产工艺为：A组份：在低速搅拌下按配方的比例称量后按顺序加入各种物料，搅拌均匀即可；B组份：将白水泥、重钙按照配方的比例称量后加入干粉混合机混合均匀即可.
使用时，在施工现场将A和B按1.5∶1的比例混合搅拌均匀就可以进行刮涂。
具体实施方式 下面是本发明的一个实施例。
一种高动态抗开裂型弹性腻子，由A、B两种组份组成，其含量如下：
A组份：3份去离子水；18份1.5％羟丙基甲基纤维素溶液41070；0.5份分散剂602N；0.3份消泡剂F111；0.3份木质纤维素FD40；0.3份聚丙烯纤维EW-01；8份细度325目的滑石粉；43.6份细度200目的石英砂；26份弹性乳液601。
B组份：65份425#的白水泥，35份细度400目的重钙。
将A与B以1.5∶1的重量比例混合搅拌均匀施工即可。
依据本发明制作的弹性腻子其各项指标均达到JG/T157-2004关于外墙腻子所规定的要求，而且具有优异的动态抗开裂性，硬度好，附着力好，抗渗性能显著，能显著改善墙体的防水，抗裂性能。防止和覆盖建筑物上的小裂缝，可保证建筑物外墙表面能长久地保持清洁华丽的表面。客户反应效果良好。
Claims (5)
1.一种高动态抗开裂型弹性腻子，按重量百分比计算A、B两个组份为：
A组分：水：3-6％；1.5％纤维素醚溶液：14-20％；分散剂：0.4-0.6％；消泡剂：0.3-0.5％；木质纤维素：0.2-0.4％；聚丙烯纤维：0.3-0.5％；滑石粉：6-10％；石英砂：40-46％；弹性乳液：24-35％；
B组分：白水泥：65-90％；重钙：10-35％；
A组分与B组分的配合比例为：A∶B＝1.5∶1。
2.根据权利要求1所述的高动态抗开裂型弹性腻子，其特征是所说的乳液为无增塑剂的阴离子型苯乙烯/丙烯酸酯共聚物，固体含量为56-58％，最低成膜温度在-7℃。
3.根据权利要求1所述的高动态抗开裂型弹性腻子，其特征是所说的纤维素醚溶液为1.5％的羟丙基甲基纤维素溶液，分子量为55000。
4.根据权利要求1所述的高动态抗开裂型弹性腻子，其特征是所说的的木质纤维素长度为300-400μm，密度为0.8～1.3g/cm3。
5.根据权利要求1所述的高动态抗开裂型弹性腻子，其特征是所使用的滑石粉为325目，石英砂为200目，重钙为400目，白水泥的标号为425#。