CN100561614C - 一种铁氧体/铁基复合材料软磁粉芯的制备方法 - Google Patents

一种铁氧体/铁基复合材料软磁粉芯的制备方法 Download PDF

Info

Publication number
CN100561614C
CN100561614C CNB2006101249642A CN200610124964A CN100561614C CN 100561614 C CN100561614 C CN 100561614C CN B2006101249642 A CNB2006101249642 A CN B2006101249642A CN 200610124964 A CN200610124964 A CN 200610124964A CN 100561614 C CN100561614 C CN 100561614C
Authority
CN
China
Prior art keywords
powder
core
powder core
adhesive
ferrite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CNB2006101249642A
Other languages
English (en)
Other versions
CN1979698A (zh
Inventor
朱正吼
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHONGHENG COMPOSITE MATERIAL TECHNOLOGY CO., LTD.
Original Assignee
Nanchang University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nanchang University filed Critical Nanchang University
Priority to CNB2006101249642A priority Critical patent/CN100561614C/zh
Publication of CN1979698A publication Critical patent/CN1979698A/zh
Application granted granted Critical
Publication of CN100561614C publication Critical patent/CN100561614C/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种新型铁氧体/铁基复合材料软磁粉芯的制备方法，其粉芯是由下列重量百分比的原料组成：160目以下的粉体70～90%，胶粘剂1～30%；粉体材料由10～100%的铁粉和0～90%的锰锌铁氧体粉体构成，胶粘剂为水玻璃胶、硅酸乙酯胶，通过配料、成型、热处理、浸胶、浸漆包裹制得。本发明的优点是：(1)配方设计先进；(2)绝缘胶粘剂无毒、无味、收缩率极小，与粉体粘结率大，通过浸渍处理，粉芯的品质因数值大大提高；(3)提高了磁粉芯的综合性能指标参数，保证了产品性能参数的一致性，提高了质量合格率。

Description

一种铁氧体/铁基复合材料软磁粉芯的制备方法
技术领域
本发明涉及一种新型铁氧体/铁基复合材料软磁粉芯的制备方法。
背景技术
目前，国内外主要以纯铁粉体、铁硅铝合金粉体、铁镍合金粉体、铁氧体粉体来制备软磁粉芯。制备方法一般是将粉体与有机树脂混合后压制成型。对于铁氧体粉是在压制后高温烧结。对于金属粉体制备的粉芯，由于其内的有机树脂耐温度性能差，粉芯不能进行高温热处理，所以，制备的粉芯软磁性能不好，影响了粉芯的实际应用。
发明内容
本发明的目的是提供一种新型铁氧体/铁基复合材料软磁粉芯的制备方法。
本发明是这样来实现的，其原材料包括160目以上的粉体材料、胶粘剂、160目以上的填料，粉体材料由10～100％的铁粉和0～90％的锰锌铁氧体粉体构成，胶粘剂为水玻璃胶或硅酸乙酯胶，占粉体材料重量的1～30％，填料为碳酸钙粉或二氧化硅粉，占粉体材料重量的0～10％，其制备工艺步骤如下：1、配料：按配方将纯铁粉、铁氧体粉体、填料、胶称量混合，充分搅拌或研磨，使粉体表面被胶充分包覆，如果粉体表面不能被胶充分包裹则必须增加胶含量；2、成型：上述混合粉体造粒后直接在模具中压制成粉芯形状(如环形、E型、U型、T型等，规格根据所设计的铁芯要求而定)，粉芯的致密度与粉体大小、压制压力有关；3、热处理：在真空下或者在惰性气体保护下，粉芯进行热处理，温度200-1200℃，保温时间为0.5-3小时；4、浸胶：热处理后的粉芯在专用绝缘胶中浸渍0~5小时；5、浸漆包裹：绝缘胶固化后，可以通过浸漆或喷涂方法，在粉芯外层形成一层薄膜外壳，对粉芯进行包装。
本发明的优点是：(1)配方设计先进；(2)绝缘胶粘剂无毒、无味、收缩率极小，与粉体粘结率大，通过浸渍处理，粉芯的品质因数值大大提高；(3)提高了磁粉芯的综合性能指标参数，保证了产品性能参数的一致性，提高了质量合格率。
具体实施方式
实施例1：
采用“(纯度98％、200目)铁粉60％+锰锌铁氧体粉体(粒度200目)40％”混合，加入粉体重量5％的正硅酸乙酯胶，在容器内充分研磨，使粉体表面被胶充分包覆；上述混合粉体直接在模具中压制成环形粉芯形状，压制压力≥100Mpa；在氩气保护下，粉芯进行热处理，温度1200℃，保温时间为1小时；热处理后的粉芯在环氧树脂型绝缘胶中浸渍1小时；待绝缘胶固化后，采用刷涂方法，在粉芯外层刷上一层1mm左右厚度的环氧树脂胶，等胶完全固化后，对粉芯进行包装。
实施例2：
采用“(纯度98％、200目)铁粉60％+锰锌铁氧体粉体(粒度200目)40％”混合，加入粉体重量3％的水玻璃胶，在容器内充分研磨，使粉体表面被胶充分包覆；上述混合粉体直接在模具中压制成环形粉芯形状，压制压力≥100Mpa；在氩气保护下，粉芯进行热处理，温度1200℃，保温时间为1小时；热处理后的粉芯在环氧树脂型绝缘胶中浸渍1小时；待绝缘胶固化后，采用刷涂方法，在粉芯外层刷上一层1mm左右厚度的环氧树脂胶，等胶完全固化后，对粉芯进行包装。
实施例3：
采用“(纯度98％、200目)铁粉60％+锰锌铁氧体粉体(粒度200目)40％”混合，加入粉体重量5％的正硅酸乙酯胶，在容器内充分研磨，使粉体表面被胶充分包覆；上述混合粉体直接在模具中压制成环形粉芯形状，压制压力≥100Mpa；在氩气保护下，粉芯进行热处理，温度1000℃，保温时间为3小时；热处理后的粉芯在环氧树脂型绝缘胶中浸渍1小时；待绝缘胶固化后，采用刷涂方法，在粉芯外层刷上一层1mm左右厚度的环氧树脂胶，等胶完全固化后，对粉芯进行包装。
实施例4：
采用“(纯度98％、300目)铁粉80％+锰锌铁氧体粉体(粒度200目)20％”混合，加入粉体重量10％的正硅酸乙酯胶，在容器内充分研磨，使粉体表面被胶充分包覆；上述混合粉体直接在模具中压制成环形粉芯形状，压制压力≥100Mpa；在氩气保护下，粉芯进行热处理，温度1000℃，保温时间为3小时；热处理后的粉芯在环氧树脂型绝缘胶中浸渍1小时；待绝缘胶固化后，采用刷涂方法，在粉芯外层刷上一层1mm左右厚度的环氧树脂胶，等胶完全固化后，对粉芯进行包装。
实施例5：
采用“(纯度98％、300目)铁粉90％+锰锌铁氧体粉体(粒度200目)10％”混合，加入粉体重量10％的正硅酸乙酯胶，在容器内充分研磨，使粉体表面被胶充分包覆；上述混合粉体直接在模具中压制成环形粉芯形状，压制压力≥100Mpa；在氩气保护下，粉芯进行热处理，温度1100℃，保温时间为1小时；热处理后的粉芯在环氧树脂型绝缘胶中浸渍1小时；待绝缘胶固化后，采用刷涂方法，在粉芯外层刷上一层1mm左右厚度的环氧树脂胶，等胶完全固化后，对粉芯进行包装。
实施例6：
采用“(纯度98％、200目)铁粉40％+锰锌铁氧体粉体(粒度200目)50％+二氧化硅粉体(粒度300目)10％”混合，加入粉体重量10％的正硅酸乙酯胶，在容器内充分研磨，使粉体表面被胶充分包覆；上述混合粉体直接在模具中压制成环形粉芯形状，压制压力≥100Mpa；在氩气保护下，粉芯进行热处理，温度1200℃，保温时间为1小时；热处理后的粉芯在环氧树脂型绝缘胶中浸渍1小时；待绝缘胶固化后，采用刷涂方法，在粉芯外层刷上一层1mm左右厚度的环氧树脂胶，等胶完全固化后，对粉芯进行包装。
实施例7：
采用“(纯度98％、200目)铁粉40％+锰锌铁氧体粉体(粒度200目)50％+碳酸钙粉体(粒度200目)10％”混合，加入粉体重量10％的正硅酸乙酯胶，在容器内充分研磨，使粉体表面被胶充分包覆；上述混合粉体直接在模具中压制成环形粉芯形状，压制压力≥100Mpa；在氩气保护下，粉芯进行热处理，温度1200℃，保温时间为1小时；热处理后的粉芯在环氧树脂型绝缘胶中浸渍1小时；待绝缘胶固化后，采用刷涂方法，在粉芯外层刷上一层1mm左右厚度的环氧树脂胶，等胶完全固化后，对粉芯进行包装。

Claims (1)

1、一种铁氧体/铁基复合材料软磁粉芯的制备方法，其原材料包括160目以上的粉体材料、胶粘剂、160目以上的填料，粉体材料由10～90％的铁粉和10～90％的锰锌铁氧体粉体构成，胶粘剂为水玻璃胶或硅酸乙酯胶，占粉体材料重量的1～30％，填料为碳酸钙粉或二氧化硅粉，占粉体材料重量的0～10％，其特征在于制备工艺步骤如下：1、配料：按配方将纯铁粉、锰锌铁氧体粉体、填料、胶粘剂称量混合，充分搅拌或研磨，使粉体表面被胶粘剂充分包覆；2、成型：步骤1得到的混合粉体造粒后直接在模具中压制成粉芯形状；3、热处理：在真空下或者在惰性气体保护下，粉芯进行热处理，温度200-1200℃，保温时间为0.5-3小时；4、浸胶：热处理后的粉芯在环氧树脂型绝缘胶中浸渍1～5小时；5、浸漆包裹：环氧树脂型绝缘胶固化后，通过浸漆或喷涂方法，在粉芯外层形成一层薄膜外壳，对粉芯进行包装。
CNB2006101249642A 2006-11-06 2006-11-06 一种铁氧体/铁基复合材料软磁粉芯的制备方法 Active CN100561614C (zh)