CN100556581C - 一种制备非晶合金首饰的方法及喷管设备 - Google Patents

一种制备非晶合金首饰的方法及喷管设备 Download PDF

Info

Publication number
CN100556581C
CN100556581C CNB200710119047XA CN200710119047A CN100556581C CN 100556581 C CN100556581 C CN 100556581C CN B200710119047X A CNB200710119047X A CN B200710119047XA CN 200710119047 A CN200710119047 A CN 200710119047A CN 100556581 C CN100556581 C CN 100556581C
Authority
CN
China
Prior art keywords
jewellery
jet pipe
nozzle
gypsum mold
amorphous metal
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CNB200710119047XA
Other languages
English (en)
Other versions
CN101073824A (zh
Inventor
张涛
李岩
李然
逄淑杰
马朝利
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Beihang University
Original Assignee
Beihang University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Beihang University filed Critical Beihang University
Priority to CNB200710119047XA priority Critical patent/CN100556581C/zh
Publication of CN101073824A publication Critical patent/CN101073824A/zh
Application granted granted Critical
Publication of CN100556581C publication Critical patent/CN100556581C/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及首饰制备技术,具体为一种制备非晶合金首饰的方法及专用于制备非晶合金首饰方法的喷管设备。首先将母合金装入喷管中,加热至合金熔化并保温,将喷嘴与首饰石膏模具注入口贴合紧密,向喷管中吹入惰性气体,使熔融合金注入首饰石膏模具中;本发明所使用的喷管,喷管主体的桶型管体为圆桶型,喷管末端的喷嘴为圆台型,喷嘴锥度为5~75°,与首饰石膏模具注入口锥度正负相差不大于2°,喷嘴外表面为磨砂面。本发明采用廉价石膏模具制备非晶首饰,价格低廉,工艺简单,成品率高,产品表面质量高,适用于批量工业生产。

Description

一种制备非晶合金首饰的方法及喷管设备
技术领域
本发明涉及首饰制造方法,具体为一种非晶合金首饰的制造方法及专用于该方法的喷管设备。
背景技术
非晶合金是一种具有特殊结构的新型金属材料,具有已往晶态金属材料所不具备的许多出色的性能,其高耐磨性和抗腐蚀能力使之尤其适合作为饰品的制备材料。
目前块体非晶的制备方法有水淬法,铜模铸造法,高压铸造法等。其中水淬法是将熔融态合金淬水冷却后制得非晶合金,由于冷却介质原因,不能形成结构复杂件;铜模铸造法和高压铸造法均采用金属模具冷却,可以制备出棒状、板状和一些结构比较简单的非晶合金铸件。利用铜模铸造法和高压铸造法虽然也可以制备出一些非晶首饰,但由于其采用金属模具,开模难度大,成本高,并且不易制造出各种形状的结构复杂铸件。目前,还没有一种方法能够利用非晶合金制造出款式多样的非晶合金首饰。本发明采用首饰制造常用的石膏模具结合高非晶形成能力的非晶合金,提供了一种制造非晶合金首饰的新方法。
发明内容
本发明的目的之一在于提供一种制备非晶合金首饰的方法,该方法不但能制造出各种形状款式的非晶合金首饰,而且价格低廉、制造工艺简单、成品率高、产品表面质量高,同时适用于批量工业生产。
为了解决以上技术问题,本发明采取的技术方案是:
一种制备非晶合金首饰的方法,其特征在于其步骤如下:
1、把母合金装入喷管中,并将母合金加热熔化,保温;
2、把喷管末端的喷嘴与首饰石膏模具注入口对准后反复旋转使之贴合紧密;
3、由喷管上端开口处向喷管中充入适量惰性气体,使合金熔体受气体压力由喷管快速注入到首饰石膏模具中,分离喷管与石膏模具,熔体凝固即可得到非晶合金首饰。
本发明的另一个目的在于提供一种专用于制备非晶合金首饰方法的喷管设备。
喷管主体的桶型管体为圆桶型,喷管末端的喷嘴为圆台型,桶型管体上标有刻度,用于度量喷出合金的体积,喷嘴锥度为5~75°,与首饰石膏模具注入口锥度正负相差不大于2°,喷嘴外表面为磨砂处理,与首饰石膏模具注入口贴合时反复相对旋转,以保证二者紧密贴合并具有一定的密闭性,通过惰性气体的压力使熔融合金从喷管喷出,由于喷管与模具注入口之间具有一定的密闭性,可增大熔体进入模具型腔的压力,有利于对于模具细微部位完整充型:喷管内表面为光滑面,形状圆柱型或圆锥型,锥度小于30°。
本发明的优点是:
1、非晶合金首饰制备采用普通首饰石膏模具,价格低廉,花样繁多,工艺简单,产品表面质量高,可根据市场需求及时调整产品类型,适用于工业批量生产。
2、喷管圆台型喷嘴可与首饰石膏模具注入口形状相匹配,其外表面磨砂处理可使喷嘴与模具注入口紧密贴合,具备一定密闭性,可增大熔体进入模具型腔的压力,有利于对模具细微部位完整精确充型。
3、桶型管体标有刻度,可据此来度量喷铸合金体积,以避免合金注入量不足或过量合金注入,保证了饰品的完整充型并节约了合金。
附图说明
图1为本发明喷管示意图。
图2为图1喷管末端的喷嘴的局部放大图
图3为本发明具体实施方式中形成的非晶合金饰品实物图。
具体实施方式
下面结合具体实施例对本发明做详细说明,但不仅仅限于本实施例。
LaCeCoAl母合金粗破碎后装入石英喷管中,采用高频感应加热合金熔化后喷铸到首饰石膏模具中,具体步骤如下:
1、把LaCeCoAl母合金粗破碎后装入石英喷管中,将石英喷管放置于高频感应炉中,并将喷管上端连接惰性气体导管;
2、对合金进行高频感应加热至高于合金熔化温度50℃左右,保温;
3、调整石英喷管与石膏模具相对位置,使石英喷嘴插入石膏模具注入口中,相对转动使二者贴合紧密;
4、关闭高频感应电源,向石英喷管中充入氩气,使熔融合金受气体压力由喷管注入首饰石膏模具中,待合金完整充型后,快速分离石英喷管与石膏模具。

Claims (2)

1、一种制备非晶合金首饰的方法,其特征在于包括以下步骤:
(1)把母合金装入喷管中加热熔化并保温;
(2)把喷管末端的喷嘴与首饰石膏模具注入口贴合紧密;
(3)向喷管中充入惰性气体,使合金熔体注入到首饰石膏模具中,将喷管与石膏模具分离,熔体凝固得到非晶合金首饰。
2、一种专用于如权利要求1所述的制备非晶合金首饰方法的喷管设备,其特征在于:喷管主体的桶型管体为圆桶型,喷管末端的喷嘴为圆台型,喷嘴锥度为5~75°,与首饰石膏模具注入口锥度正负相差不大于2°,喷嘴外表面为磨砂处理。
CNB200710119047XA 2007-06-19 2007-06-19 一种制备非晶合金首饰的方法及喷管设备 Active CN100556581C (zh)