CN100493698C - 含锂的复合氧化物光催化剂及制备方法 - Google Patents
含锂的复合氧化物光催化剂及制备方法 Download PDFInfo
- Publication number
- CN100493698C CN100493698C CNB2007101625397A CN200710162539A CN100493698C CN 100493698 C CN100493698 C CN 100493698C CN B2007101625397 A CNB2007101625397 A CN B2007101625397A CN 200710162539 A CN200710162539 A CN 200710162539A CN 100493698 C CN100493698 C CN 100493698C
- Authority
- CN
- China
- Prior art keywords
- sub
- equal
- raw material
- preparation
- oxide photocatalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种含锂的复合氧化物光催化剂及制备方法。含锂的复合氧化物光催化剂的化学组成通式为LiBa4-xSrxNb3-yTayO12,式中0.00≤x≤4,0.00≤y≤3。其制备方法为:(1)以Li、Ba和/或Sr以及Ta和/或Nb的氧化物或相应的碳酸盐、硝酸盐为原料,按照LiBa4-xSrxNb3-yTayO12的化学计量比配料,其中0.00≤x≤4,0.00≤y≤3,把原料混合研磨均匀;(2)把混匀的原料于800℃-1300℃温度下,于空气气氛中煅烧1-13小时;(3)自然冷却至室温,充分研磨,即得含锂的复合氧化物光催化剂粉末。本发明制备方法简单、成本低,制备的光催化剂具有优良的催化性能,在紫外或可见光照射下具有分解有害化学物质、有机生物质和杀菌的作用。
Description
技术领域
本发明涉及一种含锂的复合氧化物光催化剂及其制备方法。
背景技术
环境污染是世界各国十分关注的问题,已经导致了人们生活的饮用水源、工业水源质量不断下降,导致大气污染不断加剧,造成生态环境的不断破坏,对人类的生存构成严重威胁。为了解决这些问题,人们通过各种方法控制和治理环境污染。
从20世纪70年代末期,国外开始应用光催化法治理环境污染。目前的研究大多局限在使用常规二氧化钛光催化剂,但是由于其量子效率较低,总反应速度慢,难以处理量大且浓度高的工业废气和废水,使得该技术的广泛应用受到制约。近来关于复合氧化物的光催化剂有不少报道,申请号为98111246、公开号为CN1201769的中国专利,申请公开了一种铁酸锌—一二氧化钛纳米复合光催化剂及其制备方法;日本专利申请延迟公开No.7-24329提出了表示通式为A3+B3+O3的LaFeO3和表示通式为A2+B3+Ox的SrMnOx光催化剂;日本专利申请延迟公开No.10-244164提出了层状类钙钛矿型ABCO4;日本专利申请延迟公开No.8-196912提出了以钙钛矿KLaCa2Nb3O10氧化物为基体,在其层间插入二氧化钛、二氧化锆等氧化物,从而制备出高比表面积及高催化活性的的光催化剂;日本专利申请延迟公开No.11-139826提出基于层状钙钛矿氧化物KLaCa2Nb3O10的光催化剂;申请号为02801196、公开号为CN1461237的中国专利公开了一种由烧绿石结构的氧化物半导体与锐钛矿氧化物半导体复合制备高活性催化剂;申请号为02801197、公开号为CN1461238的中国专利公开了一种由钙钛矿类型氧化物半导体与二氧化钛等复合而制备高活性的光催化剂;中请号为200410012729.7、公开号为CN1248780C的中国专利公开了一种铌钾复合氧化物光催化剂及制备方法;申请号为200510019175.8、公开号为CN1736593A的中国专利公开了一种掺铜的铌钾复合氧化物光催化剂及制备方法。
以上发明的光催化剂,虽然有的光催化效果较好,但大部分的光催化剂均存在制备工艺复杂或较为复杂,制备条件苛刻,从而给推广使用带来很多困难
发明内容
本发明的目的是提供一种制备方法简单,成本低的含锂的复合氧化物光催化剂及制备方法。
本发明涉及的含锂的复合氧化物光催化剂,其化学组成通式为LiBa4-xSrλNb3-yTayO12,其中0.00≤x≤4,0.00≤y≤3。
含锂的复合氧化物光催化剂的制备方法为:
(1)以Li、Ba和/或Sr以及Ta和/或Nb的氧化物或相应的碳酸盐、硝酸盐为原料,按照LiBa4-xSrxNb3-yTayO12的化学计量比配料,其中0.00≤x≤4,0.00≤y≤3,把原料混合研磨均匀;
(2)把混匀的原料于800℃-1300℃温度下,于空气气氛中煅烧1-13小时;
(3)自然冷却至室温,充分研磨,即得含锂的复合氧化物光催化剂粉末。
本发明制备方法简单、成本低,制备的光催化剂具有优良的催化性能,在紫外或可见光照射下具有分解有害化学物质、有机生物质和杀菌的作用。
具体实施方式
实施例1:
(1)采用纯度>99%的Li2CO3、BaCO3、Nb2O5为原料,按照LiBa4Nb3O12的化学计量比配料,把原料混合研磨均匀;
(2)把混匀的原料放于铂金坩埚中,置于800℃温度下,于空气气氛中煅烧10小时;
(3)自然冷却至室温,充分研磨,即得以LiBa4Nb3O12为主相的光催化剂粉末。
实施例2:
(1)采用纯度>99%的Li2CO3、BaCO3、Nb2O5、Ta2O5为原料,按照LiBa4Nb2TaO12的化学计量比配料,把原料混合研磨均匀;
(2)把混匀的原料放于铂金坩埚中,置于800℃温度下,于空气气氛中煅烧3小时,再将温度升至1250℃,于空气气氛中煅烧10小时;
(3)自然冷却至室温,充分研磨,即得以LiBa4Nb2TaO12为主相的光催化剂粉末。
实施例3:
(1)采用高纯(>99%)的Li2CO3、BaCO3、Nb2O3、Ta2O5为原料,按照LiBa4NbTa2O12的化学计量比配料,把原料混合研磨均匀;
(2)把混匀的原料放于铂金坩埚中,置于800℃温度下,于空气气氛中煅烧3小时,再将温度升至1200℃,于空气气氛中煅烧10小时;
(3)自然冷却至室温,充分研磨,即得以LiBa4NbTa2O12为主相的光催化剂粉末。
实施例4:
(1)采用纯度>99%的Li2CO3、BaCO3、SrCO3、Nb2O5、Ta2O5为原料,按照LiBa3SrNb3O12的化学计量比配料,把原料混合研磨均匀;
(2)把混匀的原料放于铂金坩埚中,置于800℃温度下,于空气气氛中煅烧3小时,再将温度升至1300℃,于空气气氛中煅烧10小时;
(3)自然冷却至室温,充分研磨,即得以LiBa3SrNb3O12为主相的光催化剂粉末。
实施例5:
(1)采用纯度>99%的Li2CO3、BaCO3、SrCO3、Nb2O5、Ta2O5为原料,按照LiBa2Sr2Nb3O12的化学计量比配料,把原料混合研磨均匀;
(2)把混匀的原料放于铂金坩埚中,置于800℃温度下,于空气气氛中煅烧3小时,再将温度升至1300℃,于空气气氛中煅烧10小时;
(3)自然冷却至室温,充分研磨,即得以LiBa2Sr2Nb3O12为主相的光催化剂粉末。
以上发明实施方案所制的光催化剂粉末可负载于多种基体表面上。基体可以是玻璃、陶瓷、活性炭、石英砂等,光催化剂可以以薄膜的形式负载于基体表面。
本发明决不限于以上实施方案。具有与Ba相似结构与化学性质的元素如Ca,Pb等也可以做出与本发明类似晶体结构与性能的光催化剂。
通过对酸性红G的光催化降解效果,对以上方案所得的光催化剂的光催化活性进行了评价。具体方法如下:
室温下(25℃左右),准确称取150毫克光催化剂于300毫升浓度为20毫克/升的酸性红G溶液中,在磁力搅拌和紫外灯(主波长253.7nm)的照射下,紫外灯的功率为20瓦,进行光催化降解实验。反应120min后,在波长为505nm处测试溶液的吸光度,计算酸性红G的降解率。试验结果为:无催化剂的情况下,样品的降解率为3%;使用本发明实施例1所得光催化剂,样品降解率为94%;使用本发明其它实施例所得光催化剂,样品的降解率均为100%。
Claims (1)
1、一种含锂的复合氧化物在光催化中的应用,其特征在于含锂的复合氧化物光催化剂的化学组成通式为LiBa4-xSrxNb3-yTayO12,式中0.00≤x≤4,0.00≤y≤3;所述的含锂的复合氧化物光催化剂的制备方法步骤为:
(1)以Ba、Sr、Li、Ta和Nb的氧化物或相应的碳酸盐、硝酸盐为原料,按照LiBa4-xSrxNb3-yTayO12的化学计量比配料,其中0.00≤x≤4,0.00≤y≤3,把原料混合研磨均匀;
(2)把混匀的原料于800℃-1300℃温度下,于空气气氛中煅烧1-13小时;
(3)自然冷却至室温,充分研磨,即得含锂的复合氧化物光催化剂粉末。