CN100443521C - 一种纸质高压装饰防火板用浸渍水性酚醛树脂及生产工艺 - Google Patents
一种纸质高压装饰防火板用浸渍水性酚醛树脂及生产工艺 Download PDFInfo
- Publication number
- CN100443521C CN100443521C CNB2005100502070A CN200510050207A CN100443521C CN 100443521 C CN100443521 C CN 100443521C CN B2005100502070 A CNB2005100502070 A CN B2005100502070A CN 200510050207 A CN200510050207 A CN 200510050207A CN 100443521 C CN100443521 C CN 100443521C
- Authority
- CN
- China
- Prior art keywords
- water
- add
- alkali
- phenol
- urea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种用于纸质高压装饰防火板的浸渍水性酚醛树脂及生产工艺。所要解决的技术问题是提供的水性酚醛树脂及生产工艺应具有可挥发的有机成分含量少、成本低、安全环保的特点,生产工艺具有流程简单、易于操作的特点。技术方案是:一种纸质高压装饰防火板用浸渍水性酚醛树脂,其配方中的各成分的重量份为:水370-390、碱55-65、苯酚210-240、甲醛270-300、尿素15-25。还可加入松香130-150重量份。生产工艺是:一、碱水加温;二、加苯酚;三、加甲醛、碱、水及尿素;四、放料,控制终点粘度8-10恩格拉。
Description
技术领域
本发明涉及一种水性酚醛树脂及生产工艺,尤其是用于纸质高压装饰防火板的浸渍水性酚醛树脂及生产工艺。
背景技术
现代人一天的时间,约80%是在室内度过的,因而室内环境对人类的身体的影响至关重要。国际上甚至把室内空气污染列为继“煤烟污染”和“光化学烟雾污染”之后,人们所经历的第三次污染时期。尤其近几年来,室内环境的日益恶化使人们的环境意识和健康意识更加增强,“健康、长寿、舒适”已成为现代人追求的共同目标和消费的热点,对室内装饰材料的卫生环保功能也提出了更高的要求。目前市场上用于生产室内防火板的醇溶性酚醛树脂组分中容易挥发的游离酚、游离醛含量较高(通常游离酚含量在3-5%、游离醛含量在3-4%),且醇溶性酚醛树脂需要使用大量的有机溶剂,不但在生产时造成环境污染严重,生产成本又高;而且由防火板中逸出的挥发性成分增加了室内空气的污染,对人们的身体健康造成不利影响。
发明内容
本发明所要解决的技术问题是提供一种水性酚醛树脂及生产工艺的改进,该产品应具有可挥发的有机成分含量少、成本低、安全环保的特点,生产工艺具有流程简单、易于操作的特点。
本发明提供的技术方案是:一种纸质高压装饰防火板用浸渍水性酚醛树脂,其配方中的各成分的重量份为:水370-390、碱55-65、苯酚210-240、甲醛270-300、尿素15-25。
还可加入松香130-150重量份。
所述的配方中的各成分的重量份为:水380、碱61、松香130、苯酚235、甲醛295、尿素19。
所述的纸质高压装饰防火板用浸渍水性酚醛树脂的生产工艺是:
一、碱水加温:将三分之一水放入反应釜中,开动搅拌,第一次加入由五分之二的碱与二倍重量的水所溶化后的碱液,开汽升温;
二、加苯酚:当冷却至75-80℃,加入苯酚,再升温至85-90℃,保温35-45分钟;
三、加甲醛、碱、水及尿素:加入甲醛、第二次加入由剩余的碱与二倍重量的水溶化而成的碱液、四分之一的水,缓慢升温到85-95℃保温35-45分钟,控制粘度到10-12恩格拉,然后加入尿素,反应6-12分钟;
四、放料:最后加入剩余的水,冷却至38-42℃放料,控制终点粘度8-10恩格拉。
上述工艺中可在加苯酚前按以下方式加入松香:当温度升到65-75℃时,将松香缓慢地加入反应锅内并继续升温到90-100℃,保温沸腾110-130分钟,然后自然冷却。
本发明提供的水性酚醛树脂在其组分中游离酚含量小于2.5%,游离醛含量小于0.3%,防火板甲醛释放量达到1.5mg以下,达到国家环保要求。用该树脂制造的纸质高压装饰防火板用于室内装饰后,对室内空气的污染大为降低,对人体健康的危害也显著减小,符合人们对装饰装潢材料的环保要求。且水性酚醛树脂与醇溶性酚醛树脂相比较,由于节约了大量高成本的有机溶剂,因而生产水性酚醛树脂的成本大幅降低。另外,该树脂的生产工艺的流程也简单,容易操作控制,可保证产品质量的稳定。
具体实施方式
本发明的生产工艺中所采用的反应釜是常规设备,无须另行改造。加温时一般采用蒸汽。
实施例1:各原料的重量份是:水370、碱55、松香130、苯酚210、甲醛300、尿素25。
生产工艺是:
一、碱水加温:将三分之一水放入反应釜中,开动搅拌,第一次加入由五分之二的碱与二倍重量的水所溶化后的碱液,开汽升温;
二、加松香:当温度升到65℃时,将松香缓慢地加入反应锅内并继续升温到100℃,保温沸腾1200分钟,然后自然冷却;
三、加苯酚:当冷却至78℃,加入苯酚,再升温至88℃,保温45分钟;
四、加甲醛、碱、水及尿素:加入甲醛、第二次加入由剩余的碱与二倍重量的水溶化而成的碱液、四分之一的水,缓慢升温到85℃保温45分钟,控制粘度到10恩格拉,然后加入尿素,反应6分钟;
五、放料:最后加入剩余的水,冷却至38℃放料,控制终点粘度8恩格拉。
实施例2:各原料的重量份是:水390、碱65、松香150、苯酚240、甲醛270、尿素15。
所述的纸质高压装饰防火板用浸渍水性酚醛树脂的生产工艺是:
一、碱水加温:将三分之一水放入反应釜中,开动搅拌,第一次加入由五分之二的碱与二倍重量的水所溶化后的碱液,开汽升温;
二、加松香:当温度升到75℃时,将松香缓慢地加入反应锅内并继续升温到90℃,保温沸腾110分钟,然后自然冷却;
三、加苯酚:当冷却至80℃,加入苯酚,再升温至85℃,保温35分钟;
四、加甲醛、碱、水及尿素:加入甲醛、第二次加入由剩余的碱与二倍重量的水溶化而成的碱液、四分之一的水,缓慢升温到95℃保温35分钟,控制粘度到12恩格拉,然后加入尿素,反应12分钟;
五、放料:最后加入剩余的水,冷却至42℃放料,控制终点粘度10恩格拉。
实施例3:各原料的重量份是:水380、碱61、苯酚235、甲醛295、尿素19。
所述的纸质高压装饰防火板用浸渍水性酚醛树脂的生产工艺是:
一、碱水加温:将三分之一水放入反应釜中,开动搅拌,第一次加入由五分之二的碱与二倍重量的水所溶化后的碱液,开汽升温;
二、加苯酚:当温度至75℃,加入的苯酚,再升温至90℃,保温40分钟;
三、加甲醛、碱、水及尿素:加入甲醛、第二次加入由剩余的碱与二倍重量的水溶化而成的碱液、四分之一的水,缓慢升温到88℃保温40分钟,控制粘度到11恩格拉,然后加入尿素,反应10分钟;
四、放料:最后加入剩余的水,冷却至40℃放料,控制终点粘度11恩格拉。实施例4:各原料的重量份是:水380、碱61、松香130、苯酚235、甲醛295、尿素19。
该实施例的生产工艺与实施例1相同。
Claims (1)
1、一种纸质高压装饰防火板用浸渍水性酚醛树脂的生产工艺,其特征在于配方中的各成分及其重量份为:水370-390、碱55-65、苯酚210-240、甲醛270-300、尿素15-25、松香130-150重量份;
该工艺依次按以下步骤操作:
1)碱水加温:将三分之一水放入反应釜中,开动搅拌,第一次加入由五分之二的碱与二倍重量的水所溶化后的碱液,开汽升温;
2)加松香:当温度升到65-75℃时,将松香缓慢地加入反应锅内并继续升温到90-100℃,保温沸腾110-130分钟,然后自然冷却;
3)加苯酚:当温度至75-80℃,加入苯酚,再升温至85-90℃,保温35-45分钟;
4)加甲醛、碱、水及尿素:加入甲醛、第二次加入由剩余的碱与二倍重量的水溶化而成的碱液、四分之一的水,缓慢升温到85-95℃保温35-45分钟,控制粘度到10-12恩格拉,然后加入尿素,反应6-12分钟;
5)放料:最后加入剩余的水,冷却至38-42℃放料,控制终点粘度8-10恩格拉。