CN100368494C - 水性建筑保温涂料及其滚坛法制备工艺 - Google Patents

水性建筑保温涂料及其滚坛法制备工艺 Download PDF

Info

Publication number
CN100368494C
CN100368494C CNB2006100242538A CN200610024253A CN100368494C CN 100368494 C CN100368494 C CN 100368494C CN B2006100242538 A CNB2006100242538 A CN B2006100242538A CN 200610024253 A CN200610024253 A CN 200610024253A CN 100368494 C CN100368494 C CN 100368494C
Authority
CN
China
Prior art keywords
parts
agent
altar
water
stirring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2006100242538A
Other languages
English (en)
Other versions
CN1810900A (zh
Inventor
陆丕禾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CNB2006100242538A priority Critical patent/CN100368494C/zh
Publication of CN1810900A publication Critical patent/CN1810900A/zh
Application granted granted Critical
Publication of CN100368494C publication Critical patent/CN100368494C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种水性建筑保温涂料，它是以下述原料为主要成分、采用滚坛法经搅拌、滚磨、过滤而获得，其主要成分(按重量份计)为：纯丙烯酸乳液或醋酸丙烯酸乳液30-50份，去离子水15-25份，丙二醇1-2.5份，乙二醇0.5-1.5份，醇酯-120.5-1.5份，钛白粉10-20份，高岭土1-3份，氧化铝粉末15-25份，防霉剂0.1-1份，分散剂0.1-1份，甲基硅油0.1-1份，流平剂0.1-1份，增稠剂1-2份，润湿剂0.1-1份，氨水0.1-1份。本发明施工方法简单，不含有害物质，对环境无污染，2mm厚度就可反射约80-85%的阳光辐射，隔热效率达55%以上，保温效果好。

Description

水性建筑保温涂料及其滚坛法制备工艺
技术领域
本发明涉及建筑材料技术领域，具体地说是一种水性建筑保温涂料及其滚坛法制备工艺。
背景技术
整个社会都在重视建筑节能问题，并且采取了相应的技术手段，目前，国内外比较常用的墙面保温技术主要有以下几种：
①、外挂式外保温
外挂的保温材料有岩(矿)棉板、玻璃棉、毡、聚苯乙烯泡沫板(简称聚苯板、EPS、XPS)、陶粒混凝土复合聚苯仿石装饰保温板、钢丝网架夹芯墙板等。这种外挂式的外保温安装费时，施工难度大，且施工占用主导工期，对整体建筑的装饰影响很大，工程费用高。
②、聚苯板与墙体一次浇注成型
该技术是在混凝土框-剪体系中将聚苯板内置于建筑模板内，安装在即将浇注的墙体外侧，然后浇注混凝土，混凝土与聚苯板一次浇注成型为复合墙体。这种做法采用钢丝网架，造价高，且钢材是热导体，会降低墙体的保温效果。
③、聚苯颗粒保温料砂浆外墙保温
将聚苯乙烯塑料(简称EPS)加工破碎成为0.5-4mm的颗粒来配制保温砂浆。该施工技术保温层总体厚度有20-30mm，对建筑外观的影响很大，保温层和建筑外墙之间的黏结牢度问题比较严重，容易脱落。
以上各保温技术均是以“隔热”作为保温的手段，效果虽然不错，但对建筑本身承重、外装饰等的影响很大，工程施工成本也会增加很多。
发明内容
本发明的目的是针对现有技术的不足而提供的一种水性建筑保温涂料及其滚坛法制备工艺，该涂料对阳光具有高效的反射率及良好的抗紫外线性能，附着力强，保温效果好，抗污染，价格低廉，制备工艺简单。
实现本发明目的的具体技术方案是：
一种水性建筑保温涂料，它是以下述原料为主要成分、采用滚坛法经搅拌、滚磨、过滤而获得，其主要成分(按重量份计)为：纯丙烯酸乳液或醋酸丙烯酸乳液30-50份，去离子水15-25份，丙二醇1-2.5份，乙二醇0.5-1.5份，醇酯-120.5-1.5份，钛白粉10-20份，高岭土1-3份，氧化铝粉末15-25份，异噻唑酮0.1-1份，分散剂0.1-1份，甲基硅油0.1-1份，流平剂0.1-1份，增稠剂1-2份，润湿剂0.1-1份，氨水0.1-1份。
所述分散剂为聚羧酸盐类分散剂或缩合磷酸盐类分散剂。
所述防霉剂为异噻唑酮或3，3-二硫代二丙酸二甲酯。
所述流平剂为丙烯酸有机硅酯。
所述增稠剂为聚丙烯酸酯。
所述润湿剂为聚氧乙烯醚。
本发明包括以下工序：
a、搅拌
将纯丙烯酸乳液或醋酸丙烯酸乳液、增稠剂放入容器中搅拌，在搅拌过程中慢速加入去离子水，边搅拌边加入钛白粉、氧化铝粉末、高岭土，搅拌均匀后，依次加入丙二醇、乙二醇、醇酯-12、防霉剂、分散剂、甲基硅油、润湿剂、流平剂、氨水继续搅拌至稀浆状；
b、滚磨
在陶瓷坛内装入φ35-40mm、数量为坛容积50-60％的硬质陶瓷球，加入上述步骤所得的浆料，盖紧坛盖，上滚坛机滚坛18-22小时，在滚速为40-45转/分下对坛内浆料进行滚磨。
c、过滤
将滚磨后的浆料倒出，经80-100目锦纶滤网过滤，得水性建筑保温涂料。
本发明与现有技术相比，具有以下有益效果：
①、施工方法简单
本发明施工方法与普通建筑涂料施工方法一致。
②、环境友好
本发明不含大量的VOC等挥发性致癌物质及其它有害化合物，对环境无污染。
③、保温效果好
本发明阻隔太阳辐射的性能优异，隔热性能在相同厚度的情况下，大大优于其它材料。
④、应用厚度薄
本发明2mm厚度就可反射约80-85％的辐射，隔热效率可超过55％。
具体实施方式
实施例
取醋酸丙烯酸乳液40份，去离子水20份，丙二醇2份，乙二醇1份，醇酯-121.5份，钛白粉20份，高岭土3份，氧化铝粉末25份，异噻唑酮1份，聚羧酸钠1份，甲基硅油1份，丙烯酸有机硅酯0.5份，聚丙烯酸酯1.5份，聚氧乙烯醚0.5份，氨水0.5份。将醋酸丙烯酸乳液、聚丙烯酸酯放入容器中搅拌，在搅拌过程中慢速加入去离子水，边搅拌边加入钛白粉、氧化铝粉末、高岭土，搅拌均匀后，依次加入丙二醇、乙二醇、醇酯-12、异噻唑酮、聚羧酸钠、甲基硅油、聚氧乙烯醚、丙烯酸有机硅酯、氨水继续搅拌至稀浆状；在陶瓷坛内装入φ38mm、数量为坛容积50％的硬质陶瓷球，加入上述步骤所得的浆料，盖紧坛盖，上滚坛机滚坛20小时，在45转/分的转速下对坛内浆料进行滚磨；滚磨后的浆料倒出后，经滤网过滤，得本发明产品。

Claims (7)

1.一种水性建筑保温涂料，其特征在于它是以下述原料为主要成分、采用滚坛法经搅拌、滚磨、过滤而获得，其主要成分以重量份计：纯丙烯酸乳液或醋酸丙烯酸乳液30-50份，去离子水15-25份，丙二醇1-2.5份，乙二醇0.5-1.5份，醇酯-12 0.5-1.5份，钛白粉10-20份，高岭土1-3份，氧化铝粉末15-25份，防霉剂0.1-1份，分散剂0.1-1份，甲基硅油0.1-1份，流平剂0.1-1份，增稠剂1-2份，润湿剂0.1-1份，氨水0.1-1份。
2.根据权利要求1所述的涂料，其特征在于所述分散剂为聚羧酸盐类分散剂或缩合磷酸盐类分散剂。
3.根据权利要求1所述的涂料，其特征在于所述防霉剂为异噻唑酮或3，3-二硫代二丙酸二甲酯。
4.根据权利要求1所述的涂料，其特征在于所述流平剂为丙烯酸有机硅酯。
5.根据权利要求1所述的涂料，其特征在于所述增稠剂为聚丙烯酸酯。
6.根据权利要求1所述的涂料，其特征在于所述润湿剂为聚氧乙烯醚。
7.一种权利要求1所述涂料的滚坛法制备工艺，其特征在于它包括以下工序：
a、搅拌
将纯丙烯酸乳液或醋酸丙烯酸乳液、增稠剂放入容器中搅拌，在搅拌过程中慢速加入去离子水，边搅拌边加入钛白粉、氧化铝粉末、高岭土，搅拌均匀后，依次加入丙二醇、乙二醇、醇酯-12、防霉剂、分散剂、甲基硅油、润湿剂、流平剂、氨水继续搅拌至稀浆状；
b、滚磨
在陶瓷坛内装入φ35-40mm、数量为坛容积50-60％的硬质陶瓷球，加入上述步骤所得的浆料，盖紧坛盖，上滚坛机滚坛18-22小时，在滚速为40-45转/分下对坛内浆料进行滚磨；
c、过滤
将滚磨后的浆料倒出，经80-100目锦纶滤网过滤，得水性建筑保温涂料。
CNB2006100242538A 2006-03-01 2006-03-01 水性建筑保温涂料及其滚坛法制备工艺 Expired - Fee Related CN100368494C (zh)