CN105038455B - 一种红外保温隔热建筑薄层涂料及其制备方法 - Google Patents
一种红外保温隔热建筑薄层涂料及其制备方法 Download PDFInfo
- Publication number
- CN105038455B CN105038455B CN201510402940.8A CN201510402940A CN105038455B CN 105038455 B CN105038455 B CN 105038455B CN 201510402940 A CN201510402940 A CN 201510402940A CN 105038455 B CN105038455 B CN 105038455B
- Authority
- CN
- China
- Prior art keywords
- parts
- thermal insulation
- infrared thermal
- thin coatings
- ketone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种红外保温隔热建筑薄层涂料及其制备方法,该涂料包括以下重量份的原料:丙烯酸乳液16‑30份,填料10‑20份,硫酸钡20‑26份,高岭土1‑5份,钛白粉5‑18份,十二醇脂1‑4份,2‑甲基‑4‑异噻唑啉‑4‑酮0.1‑0.2份,2‑正辛基‑4‑异噻唑啉‑3‑酮0.1‑0.4份,巴斯夫A10 0.1‑0.4份,聚丙烯酸钠0.1‑0.5份,三聚磷酸钠8‑15份,水10‑20份。按重量份取样,取填料、硫酸钡、高岭土、钛白粉与水混合,加入三聚磷酸钠搅拌至均匀;加入丙烯酸乳液和十二醇脂搅拌至均匀;加入剩余原料,球磨即得。本发明具有保温隔热性能良好、成本低廉、涂层较薄的特点。
Description
技术领域
本发明涉及建筑材料技术领域,具体涉及一种红外保温隔热建筑薄层涂料,同时还涉及该红外保温隔热建筑薄层涂料涂料的制备方法。
背景技术
建筑物传统保温隔热通常采用外挂式有机或无机类保温板,但占地面积大、施工周期长且施工工艺复杂,同时还存在易燃、易起层、易脱落、易渗漏等安全隐患。
随着涂料技术的发展,建筑保温隔热涂料因具有经济、环保、使用方便和节能效果明显等优点已被用于建筑节能领域,涂刷保温隔热涂料代替外挂式外墙保温层已成为一种技术趋势。
由于各地区气候特点相差较大,不同地区建筑物对墙体结构热物性质要求不同。目前,市场上绝大多数建筑涂料主要基于阻隔反射原理,性能以夏季反射隔热为主,建筑物冬季保温效果不佳。反射隔热涂料的制备通常以空心玻璃微珠为隔热填料,该填料质量和结构对产品隔热性能影响较大,且与钛白粉混合使用时还易造成钛白粉反射功能受限,致使产品性能不稳定和质量下降。产品性能主要以夏季反射隔热为主、冬季保温效果不佳、成本高、涂层较厚。
发明内容
本发明的目的在于提供一种保温隔热性能良好、成本低廉、涂层较薄的红外保温隔热建筑薄层涂料。
本发明的另一目的在于提供该红外保温隔热建筑薄层涂料的制备方法。
本发明的一种红外保温隔热建筑薄层涂料,按重量份计,包括以下原料:
丙烯酸乳液16-30份,填料10-20份,硫酸钡20-26份,高岭土1-5份,钛白粉5-18份,十二醇脂1-4份,2-甲基-4-异噻唑啉-4-酮0.1-0.2份,2-正辛基-4-异噻唑啉-3-酮0.1-0.4份,巴斯夫A10 0.1-0.4份,聚丙烯酸钠0.1-0.5份,三聚磷酸钠8-15份,水10-20份。
上述的一种红外保温隔热建筑薄层涂料,其中:所述填料由10-30%钛酸钡粉体和90-70%托贝莫来石粉体混合均匀后球磨2-5h制得。
本发明的一种红外保温隔热建筑薄层涂料的制备方法,包括以下步骤:
(1)取10-20份填料、20-26份硫酸钡、1-5份高岭土、5-18份钛白粉与10-20份水混合,加入8-15份三聚磷酸钠搅拌至均匀;
(2)加入16-30份丙烯酸乳液和1-4份十二醇脂,搅拌至均匀;
(3)加入0.1-0.2份2-甲基-4-异噻唑啉-4-酮、0.1-0.4份2-正辛基-4-异噻唑啉-3-酮、0.1-0.4份巴斯夫A10和0.1-0.5份聚丙烯酸钠,球磨9-12h即得。
本发明与现有技术相比,具有明显有益效果,从以上技术方案可知:本发明是根据建筑物墙体热传递机制和太阳光能量分布特点,运用热传递理论和玻尔兹曼定律而提出的,所采用的填料具有红外高发射率,与钛白粉混合使用不会影响钛白粉的反射功能和质量。其利用各原料合理配比之后涂料所具有的独有结构性质对建筑物夏季环境可见光和红外光进行反射和对外红外发射,以达降温目的;对建筑物冬季环境屋内因空调、家用电器及暖气等产生的热能吸收后进行对内红外发射,且因发射红外波段在2.5-35μm范围,在达到保温目的的同时,还增大了建筑物环境内的人体舒适度。能克服现有以反射隔热为主的涂料产品性能单一、保温效果不佳、成本高、涂层较厚(本发明涂刷后涂层厚度仅为0.3-0.6mm)的不足。
具体实施方式
实施例1
一种红外保温隔热建筑薄层涂料,包括以下步骤:
(1)取10kg填料(由10%钛酸钡粉体和90%托贝莫来石粉体混合均匀后球磨2h制得)、20kg硫酸钡、1kg高岭土、5kg钛白粉与10kg水混合,加入8kg三聚磷酸钠搅拌至均匀;
(2)加入16kg丙烯酸乳液和1kg十二醇脂,搅拌至均匀;
(3)加入0.1kg2-甲基-4-异噻唑啉-4-酮、0.4kg 2-正辛基-4-异噻唑啉-3-酮、0.1kg巴斯夫A10和0.5kg聚丙烯酸钠,球磨9h即得。
依据JGJ/T 132-2009《居住建筑节能检测标准》,测得该配比涂料使用前后围护结构主体部位热阻值分别为0.59(m2·k)/W和1.12(m2·k)/W,使用该配比涂料后有效热阻提高约89%。
实施例2
一种红外保温隔热建筑薄层涂料,包括以下步骤:
(1)取20kg填料(由30%钛酸钡粉体和70%托贝莫来石粉体混合均匀后球磨5h制得)、26kg硫酸钡、5kg高岭土、18kg钛白粉与20kg水混合,加入15kg三聚磷酸钠搅拌至均匀;
(2)加入30kg丙烯酸乳液和4kg十二醇脂,搅拌至均匀;
(3)加入0.2kg2-甲基-4-异噻唑啉-4-酮、0.1kg 2-正辛基-4-异噻唑啉-3-酮、0.4kg巴斯夫A10和0.1kg聚丙烯酸钠,球磨12h即得。
依据JGJ/T 132-2009《居住建筑节能检测标准》,测得该配比涂料使用前后围护结构主体部位热阻值分别为0.59(m2·k)/W和1.14(m2·k)/W,使用该配比涂料后有效热阻提高约93%。
实施例3
一种红外保温隔热建筑薄层涂料,包括以下步骤:
(1)取15kg填料(由20%钛酸钡粉体和80%托贝莫来石粉体混合均匀后球磨3h制得)、23kg硫酸钡、3kg高岭土、11kg钛白粉与15kg水混合,加入12kg三聚磷酸钠搅拌至均匀;
(2)加入23kg丙烯酸乳液和2.5kg十二醇脂,搅拌至均匀;
(3)加入0.15kg2-甲基-4-异噻唑啉-4-酮、0.25kg2-正辛基-4-异噻唑啉-3-酮、0.25kg巴斯夫A10和0.3kg聚丙烯酸钠,球磨10h即得。
依据JGJ/T 132-2009《居住建筑节能检测标准》,测得该配比涂料使用前后围护结构主体部位热阻值分别为0.59(m2·k)/W和1.15(m2·k)/W,使用该配比涂料后有效热阻提高约95%。
以上所述,仅是本发明的较佳实施例而已,并非对本发明做任何形式上的限制,任何未脱离本发明技术方案内容,依据本发明的技术实质对以上实施例所做的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (2)
1.一种红外保温隔热建筑薄层涂料,按重量份计,包括以下原料:
丙烯酸乳液16-30份,填料10-20份,硫酸钡20-26份,高岭土1-5份,钛白粉5-18份,十二醇脂1-4份,2-甲基-4-异噻唑啉-4-酮0.1-0.2份,2-正辛基-4-异噻唑啉-3-酮0.1-0.4份,巴斯夫A10 0.1-0.4份,聚丙烯酸钠0.1-0.5份,三聚磷酸钠8-15份,水10-20份;所述填料由10-30%钛酸钡粉体和90-70%托贝莫来石粉体混合均匀后球磨2-5h制得;所述红外保温隔热建筑薄层涂料涂刷后的涂层厚度仅为0.3-0.6mm。
2.一种如权利要求1所述的红外保温隔热建筑薄层涂料的制备方法,包括以下步骤:
(1)取10-20份填料、20-26份硫酸钡、1-5份高岭土、5-18份钛白粉与10-20份水混合,加入8-15份三聚磷酸钠搅拌至均匀;
(2)加入16-30份丙烯酸乳液和1-4份十二醇脂,搅拌至均匀;
(3)加入0.1-0.2份2-甲基-4-异噻唑啉-4-酮、0.1-0.4份2-正辛基-4-异噻唑啉-3-酮、0.1-0.4份巴斯夫A10和0.1-0.5份聚丙烯酸钠,球磨9-12h即得。