CN100363304C - 一种尖晶石质低水泥功能耐火材料浇注料 - Google Patents

一种尖晶石质低水泥功能耐火材料浇注料 Download PDF

Info

Publication number
CN100363304C
CN100363304C CNB2005100409601A CN200510040960A CN100363304C CN 100363304 C CN100363304 C CN 100363304C CN B2005100409601 A CNB2005100409601 A CN B2005100409601A CN 200510040960 A CN200510040960 A CN 200510040960A CN 100363304 C CN100363304 C CN 100363304C
Authority
CN
China
Prior art keywords
cement
magnesium
spinel
functional refractory
low
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CNB2005100409601A
Other languages
English (en)
Other versions
CN1891670A (zh
Inventor
张雪松
刘步周
俞晓东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU SUJIA GROUP NEW MATERIAL CO Ltd
Original Assignee
JIANGSU SUJIA GROUP NEW MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU SUJIA GROUP NEW MATERIAL CO Ltd filed Critical JIANGSU SUJIA GROUP NEW MATERIAL CO Ltd
Priority to CNB2005100409601A priority Critical patent/CN100363304C/zh
Publication of CN1891670A publication Critical patent/CN1891670A/zh
Application granted granted Critical
Publication of CN100363304C publication Critical patent/CN100363304C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种尖晶石质低水泥功能耐火材料浇注料，属于一种耐火材料。按照本发明所提供的设计方案，这种材料含有镁铝尖晶石40-65%，白刚玉15-40%，活性氧化铝3-15%，镁锆共晶料0.5-8%，水泥2-5%，外加剂0.01～4.7%，水3-7%。这种浇注料不含Cr元素，避免了Cr对环境的污染问题。由于镁锆共晶材料的使用，使该浇注料又具有良好的抗热震性能。由于以镁铝尖晶石为主要成份之一，使该浇注料具有良好的抗渣侵蚀性能。

Description

一种尖晶石质低水泥功能耐火材料浇注料
技术领域
本发明属于一种耐火材料。
背景技术
耐火材料浇注料主要用于炼钢耐火材料部件的制造，例如钢包水口座砖、透气砖、透气塞、炼钢电炉底电极套砖等部位。目前使用的此类浇注料大多含有Cr2O3，由于Cr2O3中的Cr3+在升温过程中易变成Cr6+，而含有Cr6+的化合物有致癌作用，将损害操作工人的身体健康，污染环境。而不含Cr2O3的浇注料抗渣侵蚀性能和抗高温热震性较差，使用寿命短，不能满足工艺对材料的性能要求。
发明内容
本发明的目的在于寻求一种尖晶石质低水泥功能耐火材料浇注料，这种浇注料不含Cr元素，避免了Cr对环境的污染问题。由于镁锆共晶材料的使用，使该浇注料又具有良好的抗热震性能。由于以镁铝尖晶石为主要成份之一，使该浇注料具有良好的抗渣侵蚀性能。
按照本发明所提供的设计方案，这种材料含有镁铝尖晶石40-65％，白刚玉15-40％，活性氧化铝3-15％，镁锆共晶料0.5-8％，水泥2-5％，外加剂0.01～4.7％，水3-7％。
在镁锆共晶料中含二氧化锆5-35％。
所述外加剂包括以下材料中的一种或多种：减水剂0.1-1.5％；防爆纤维0.01-0.2％；耐热钢纤维0.2-2.0％。
使用镁锆共晶料的作用是：1、使用镁锆共晶料替代镁砂细粉，可防止镁砂细粉的水化反应，避免制品在升温时开裂。由于镁锆共晶料中ZrO2大多分布在MgO晶体周围，MgO和ZrO2之间的相互溶解，可以有效抑制MgO的活性。使MgO与H2O发生反应的趋势受到抑制。2、ZrO2的引入，使制品的抗热震稳定性提高。由于ZrO2在不同温度条件下会发生不同程度的晶形转变，在单斜晶系-四方晶系-立方晶系之间发生晶形转变，在制品内部产生微裂纹，当温度变化时，这些微裂纹会吸收膨胀，从而使制品的抗热震性能提高。3、ZrO2可以减少钢液、钢渣对制品的润湿，提高制品的抗渣渗透性能。
使用镁铝尖晶石可以提高制品的抗渣侵蚀性能，尤其是炼钢碱性渣的侵蚀。也可防止在Al2O3质浇注料中引入较多MgO而引起的恶性膨胀。
具体实施方式
实施一：
其水口座砖的配料组份如下：含有镁铝尖晶石42％，白刚玉33％，活性氧化铝15％，镁锆共晶料1％，水泥3％，耐热钢纤维1.8％，水4％，硼酸0.2％。用该浇注料浇注钢包水口座砖，使用寿命达到55次。
实施二：
使用该浇注料生产炼钢电炉底电极套砖。所生产产品化学成份如下：含有镁铝尖晶石49％，白刚玉23％，活性氧化铝11％，镁锆共晶料8％，水泥3％，减水剂0.3％(减水剂可以是三聚磷酸钠、六偏磷酸钠、硼酸、ADS、ADW、硅微粉、高分子有机减水剂中的一种或多种)，水5.7％。用该浇注料浇注的电炉底电极套砖使用寿命达到550次。其中的ADS、ADW是美铝公司的减水剂牌号。
实施例三
含有镁铝尖晶石46％，白刚玉33％，活性氧化铝3％，镁锆共晶料5.1％，水泥5％，减水剂ADS或ADW 1.5％，防爆纤维0.2％，耐热钢纤维1.2％，水5％。用该浇注料浇注钢包水口座砖，使用寿命达到55次。
实施例四
含有镁铝尖晶石65％，白刚玉15％，活性氧化铝9.49％，镁锆共晶料0.5％，水泥4％，防爆纤维0.01％，硅微粉0.5％，水5.5％。用该浇注料浇注钢包水口座砖，使用寿命达到55次。
实施例五
含有镁铝尖晶石40％，白刚玉40％，活性氧化铝5.3％，镁锆共晶料5％，水泥2％，减水剂0.5％，防爆纤维0.2％，耐热钢纤维2.0％，硅微粉1.0％，水4％。用该浇注料浇注钢包水口座砖，使用寿命达到55次。

Claims (4)

1.一种尖晶石质低水泥功能耐火材料浇注料，其特征是：含有镁铝尖晶石40-65％，白刚玉15-40％，活性氧化铝3-15％，镁锆共晶料0.5-8％，水泥2-5％，外加剂0.01～4.7％，水3-7％。
2.根据权利要求1所述尖晶石质低水泥功能耐火材料浇注料，其特征是：镁锆共晶料中含二氧化锆5-35％。
3.根据权利要求1所述尖晶石质低水泥功能耐火材料浇注料，其特征在于，外加剂包括以下材料中的一种或多种：
减水剂0.1-1.5％；
防爆纤维0.01-0.2％；
耐热钢纤维0.2-2.0％。
4.根据权利要求3所述尖晶石质低水泥功能耐火材料浇注料，其特征在于，减水剂为以下材料的一种或多种：柠檬酸三钠，三聚磷酸钠，六偏磷酸钠，硼酸，硅微粉，高分子有机减水剂。
CNB2005100409601A 2005-07-07 2005-07-07 一种尖晶石质低水泥功能耐火材料浇注料 Expired - Fee Related CN100363304C (zh)