CN100346901C - 高硬度铸造模具的制造方法 - Google Patents
高硬度铸造模具的制造方法 Download PDFInfo
- Publication number
- CN100346901C CN100346901C CNB200510016540XA CN200510016540A CN100346901C CN 100346901 C CN100346901 C CN 100346901C CN B200510016540X A CNB200510016540X A CN B200510016540XA CN 200510016540 A CN200510016540 A CN 200510016540A CN 100346901 C CN100346901 C CN 100346901C
- Authority
- CN
- China
- Prior art keywords
- grams per
- per liters
- mould
- plating
- core
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
工序号 | 工序名称 | 化学成分 | 浓度(g/l) | 处理时间(min) | 温度(℃) |
1 | 绘制芯模的图样 | ||||
2 | 快速制造芯模 | ||||
3 | 喷改性环氧树脂涂料 | ||||
4 | 干燥 | 24h |
5 | 除油 | 乙醇 | 95% | 5 | 常温 |
6 | 温水清洗 | 0.5 | 50 | ||
7 | 水洗 | 0.5 | 常温 | ||
8 | 敏化 | 氯化亚锡 | 5 | 10 | |
浓盐酸 | 20 | ||||
锡粒 | 少许 | ||||
9 | 水洗 | 0.5 | 常温 | ||
10 | 去离子水洗 | 去离子水 | 1 | 常温 | |
11 | 活化 | 硝酸银 | 5 | 10 | |
去离子水洗 | 去离子水 | 1 | 常温 | ||
1213 | 化学镀镍 | 硫酸镍 | 15.3~25.8 | 15 | 75 |
次磷酸钠 | 14.1~16.4 | ||||
醋酸钠 | 12.8~14.3 | ||||
14 | 水洗 | 0.5 | 常温 | ||
15 | 电铸 | 常规电铸镍 | |||
16 | 水洗 | 0.5 | 常温 | ||
17 | 烘干 | 60 | |||
18 | 热处理 | 2 | 280 | ||
19 | 溶解芯模 | 硫酸 | 20% | 溶完为止 | 常温 |
20 | 水洗 | 5 | 常温 | ||
21 | 喷砂 | ||||
22 | 背衬 | 环氧树脂 |
Claims (4)