BRPI1005150A8 - Processo para galvanização por imersão a quente - Google Patents
Processo para galvanização por imersão a quenteInfo
- Publication number
- BRPI1005150A8 BRPI1005150A8 BRPI1005150A BRPI1005150A BRPI1005150A8 BR PI1005150 A8 BRPI1005150 A8 BR PI1005150A8 BR PI1005150 A BRPI1005150 A BR PI1005150A BR PI1005150 A BRPI1005150 A BR PI1005150A BR PI1005150 A8 BRPI1005150 A8 BR PI1005150A8
- Authority
- BR
- Brazil
- Prior art keywords
- hot dip
- dip galvanizing
- galvanizing process
- weight
- flux
- Prior art date
Abstract
PROCESSO PARA GALVANIZAÇÃO POR IMERSÃO A QUENTE A presente invenção se relaciona geralmente a um fluxo para galvanização por imersão a quente compreendendo de 36% a 80 % em peso de cloreto de zinco (ZnC12) 6% a 62% em peso de cloreto de amônio (NH4Cl), 2% a 10% em peso de pelo menos um dos compostos NiCl2 e MnC12, ou uma mistura destes. A presente invenção ainda se relaciona a um banho de fluxagem, processo de galvanização por imersão a quente de artigos de ferro ou aço, e também ao uso do citado fluxo.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP09150777A EP2213758A1 (en) | 2009-01-16 | 2009-01-16 | Flux and fluxing bath for hot dip galvanization, process for the hot dip galvanization of an iron or steel article |
PCT/EP2010/050542 WO2010081905A1 (en) | 2009-01-16 | 2010-01-18 | Flux and fluxing bath for hot dip galvanization, process for the hot dip galvanization of an iron or steel article |
Publications (3)
Publication Number | Publication Date |
---|---|
BRPI1005150A2 BRPI1005150A2 (pt) | 2016-03-22 |
BRPI1005150A8 true BRPI1005150A8 (pt) | 2017-10-03 |
BRPI1005150B1 BRPI1005150B1 (pt) | 2020-04-22 |
Family
ID=40671105
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BRPI1005150A BRPI1005150B1 (pt) | 2009-01-16 | 2010-01-18 | processo para galvanização por imersão a quente |
Country Status (20)
Country | Link |
---|---|
US (1) | US8802198B2 (pt) |
EP (2) | EP2213758A1 (pt) |
JP (1) | JP5832902B2 (pt) |
KR (1) | KR101642305B1 (pt) |
CN (1) | CN102282285B (pt) |
AU (1) | AU2010205596B2 (pt) |
BR (1) | BRPI1005150B1 (pt) |
CA (1) | CA2748592C (pt) |
DK (1) | DK2391741T3 (pt) |
EA (1) | EA022105B1 (pt) |
ES (1) | ES2641788T3 (pt) |
HU (1) | HUE034193T2 (pt) |
MX (1) | MX340793B (pt) |
PL (1) | PL2391741T3 (pt) |
PT (1) | PT2391741T (pt) |
RS (1) | RS56389B1 (pt) |
TN (1) | TN2011000334A1 (pt) |
UA (1) | UA107340C2 (pt) |
WO (1) | WO2010081905A1 (pt) |
ZA (1) | ZA201104947B (pt) |
Families Citing this family (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
EP2650990B1 (en) | 2012-04-13 | 2014-11-19 | Vergokan | Weld-free assembly of galvanized steel parts |
JP2013227594A (ja) | 2012-04-24 | 2013-11-07 | Nippon Steel & Sumitomo Metal Corp | 溶融亜鉛めっき鋼管及び溶融亜鉛めっき鋼管の製造方法 |
AU2013332257A1 (en) * | 2012-10-17 | 2015-04-09 | Bluescope Steel Limited | Method of producing metal-coated steel strip |
US10616844B2 (en) | 2013-05-15 | 2020-04-07 | Huawei Technologies Co., Ltd. | Systems and methods for operation of wireless user devices with cellular and Wi-Fi interfaces |
JP5825295B2 (ja) * | 2013-05-16 | 2015-12-02 | 新日鐵住金株式会社 | 溶融亜鉛めっき鋼管及び溶融亜鉛めっき鋼管の製造方法 |
JP5979186B2 (ja) * | 2013-07-31 | 2016-08-24 | Jfeスチール株式会社 | 溶融亜鉛めっき用フラックスおよび溶融亜鉛めっき用フラックス浴ならびに溶融亜鉛めっき鋼材の製造方法 |
JP5871035B2 (ja) * | 2013-07-31 | 2016-03-01 | Jfeスチール株式会社 | 溶融亜鉛めっき用フラックスおよび溶融亜鉛めっき用フラックス浴ならびに溶融亜鉛めっき鋼材の製造方法 |
JP5884200B2 (ja) * | 2013-07-31 | 2016-03-15 | Jfeスチール株式会社 | 溶融亜鉛めっき用フラックスおよび溶融亜鉛めっき用フラックス浴ならびに溶融亜鉛めっき鋼材の製造方法 |
CN103938142B (zh) * | 2014-05-13 | 2016-08-24 | 国家电网公司 | 一种溶剂法热镀锌用镀层减薄无铵盐助镀剂 |
KR20170024023A (ko) * | 2014-07-31 | 2017-03-06 | 제이에프이 스틸 가부시키가이샤 | 용융 아연 도금 강재의 제조 방법 및 용융 아연 도금 강재 |
KR20170114608A (ko) * | 2016-04-05 | 2017-10-16 | 덕산갈바텍 주식회사 | 용융아연도금용 플럭스액 재생방법 |
RU2646303C2 (ru) * | 2016-07-12 | 2018-03-02 | Акционерное общество "Уралэлектромедь" | Флюс для горячего цинкования стальных изделий |
CN106567026B (zh) * | 2016-11-09 | 2019-02-19 | 陕西专壹知识产权运营有限公司 | 一种金属软管镀锌用助镀剂及其制备方法 |
CN110241369B (zh) * | 2019-05-24 | 2023-01-31 | 湖南创林新材料科技有限公司 | 一种热镀用锌铝镍钽合金及热镀锌的方法 |
CN111334733A (zh) * | 2020-04-30 | 2020-06-26 | 苏州鑫吴钢结构工程有限公司 | 构支架钢管的镀锌方法 |
CN113278905A (zh) * | 2021-05-19 | 2021-08-20 | 河北恒创环保科技有限公司 | 一种热浸镀锌助镀剂配方及其制作工艺 |
CN115011898A (zh) * | 2022-05-11 | 2022-09-06 | 徐州瑞马科宝金属制品有限公司 | 一种防漏的高铝热浸镀锌方法 |
BE1030796B1 (nl) | 2022-08-22 | 2024-03-18 | Balak Coatings Nv | Werkwijze voor het voorbehandelen van een te verzinken hekwerkpaneel en voorbehandeld hekwerkpaneel |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
LU75821A1 (pt) * | 1976-09-17 | 1977-05-04 | ||
JPH0517860A (ja) * | 1991-05-27 | 1993-01-26 | Sumitomo Metal Ind Ltd | 溶融亜鉛めつき方法 |
EP1209245A1 (en) * | 2000-11-23 | 2002-05-29 | Galvapower Group N.V. | Flux and its use in hot dip galvanization process |
WO2003057940A1 (en) * | 2002-01-10 | 2003-07-17 | Umicore | Preparation of steel surfaces for single-dip aluminium-rich zinc galvanising |
JP4564361B2 (ja) * | 2005-01-04 | 2010-10-20 | 新日本製鐵株式会社 | 溶融Zn−Al−Mg系合金めっき用フラックス組成物及びそれを用いた溶融Zn−Al−Mg系合金めっき鋼材の製造方法 |
EP2035594A4 (en) * | 2006-06-09 | 2010-12-08 | Teck Cominco Metals Ltd | HIGH ALUMINUM ALLOY FOR GENERAL GALVANIZATION |
-
2009
- 2009-01-16 EP EP09150777A patent/EP2213758A1/en not_active Withdrawn
-
2010
- 2010-01-18 HU HUE10700427A patent/HUE034193T2/en unknown
- 2010-01-18 RS RS20170939A patent/RS56389B1/sr unknown
- 2010-01-18 CA CA2748592A patent/CA2748592C/en not_active Expired - Fee Related
- 2010-01-18 MX MX2011007591A patent/MX340793B/es active IP Right Grant
- 2010-01-18 PL PL10700427T patent/PL2391741T3/pl unknown
- 2010-01-18 EA EA201101061A patent/EA022105B1/ru not_active IP Right Cessation
- 2010-01-18 US US13/144,309 patent/US8802198B2/en not_active Expired - Fee Related
- 2010-01-18 BR BRPI1005150A patent/BRPI1005150B1/pt not_active IP Right Cessation
- 2010-01-18 ES ES10700427.7T patent/ES2641788T3/es active Active
- 2010-01-18 CN CN201080004694.6A patent/CN102282285B/zh not_active Expired - Fee Related
- 2010-01-18 UA UAA201109943A patent/UA107340C2/ru unknown
- 2010-01-18 DK DK10700427.7T patent/DK2391741T3/en active
- 2010-01-18 AU AU2010205596A patent/AU2010205596B2/en not_active Ceased
- 2010-01-18 WO PCT/EP2010/050542 patent/WO2010081905A1/en active Application Filing
- 2010-01-18 JP JP2011545758A patent/JP5832902B2/ja not_active Expired - Fee Related
- 2010-01-18 EP EP10700427.7A patent/EP2391741B1/en active Active
- 2010-01-18 KR KR1020117019059A patent/KR101642305B1/ko active IP Right Grant
- 2010-01-18 PT PT107004277T patent/PT2391741T/pt unknown
-
2011
- 2011-05-05 ZA ZA2011/04947A patent/ZA201104947B/en unknown
- 2011-07-06 TN TN2011000334A patent/TN2011000334A1/fr unknown
Also Published As
Publication number | Publication date |
---|---|
CA2748592A1 (en) | 2010-07-22 |
AU2010205596B2 (en) | 2014-12-11 |
EA022105B1 (ru) | 2015-11-30 |
DK2391741T3 (en) | 2017-09-04 |
BRPI1005150B1 (pt) | 2020-04-22 |
MX2011007591A (es) | 2011-08-04 |
AU2010205596A2 (en) | 2011-10-13 |
EP2213758A1 (en) | 2010-08-04 |
RS56389B1 (sr) | 2017-12-29 |
KR20110107371A (ko) | 2011-09-30 |
CN102282285B (zh) | 2014-07-09 |
WO2010081905A1 (en) | 2010-07-22 |
CA2748592C (en) | 2016-09-27 |
EA201101061A1 (ru) | 2012-02-28 |
ZA201104947B (en) | 2012-03-28 |
AU2010205596A1 (en) | 2011-07-28 |
EP2391741A1 (en) | 2011-12-07 |
US8802198B2 (en) | 2014-08-12 |
KR101642305B1 (ko) | 2016-07-25 |
PT2391741T (pt) | 2017-08-29 |
PL2391741T3 (pl) | 2017-12-29 |
BRPI1005150A2 (pt) | 2016-03-22 |
CN102282285A (zh) | 2011-12-14 |
ES2641788T3 (es) | 2017-11-13 |
UA107340C2 (en) | 2014-12-25 |
MX340793B (es) | 2016-07-25 |
TN2011000334A1 (en) | 2013-03-27 |
JP5832902B2 (ja) | 2015-12-16 |
US20110293838A1 (en) | 2011-12-01 |
HUE034193T2 (en) | 2018-02-28 |
JP2012515268A (ja) | 2012-07-05 |
EP2391741B1 (en) | 2017-06-28 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BRPI1005150A8 (pt) | Processo para galvanização por imersão a quente | |
BR112012030800A2 (pt) | aços sinterizados nitrificados | |
MX2020010051A (es) | Articulo moldeado por estampado en caliente, lamina de acero enrollada en frio, y metodo para manufacturar el articulo moldeado por estampado en caliente. | |
BR112014007509A2 (pt) | folha de aço fornecida com camada galvanizada por imersão a quente excelente em umectabilidade de galvanização e adesão de galvanização e método de produção da mesma | |
BR112015001809A2 (pt) | chapa de aço galvanizada por imersão a quente e método de produção da mesma | |
MX366127B (es) | Composiciones de pretratamiento de zirconio que contienen molibdeno, metodos asociados para tratar sustratos metalicos, y sustratos metalicos revestidos relacionados. | |
MY166781A (en) | High-corrosion-resistance hot-dip galvanized steel sheet having excellent appearance uniformity and manufacturing method thereof | |
IN2014DN07662A (pt) | ||
WO2014104428A8 (ko) | 아연도금강판용 표면처리 조성물, 아연도금강판의 표면처리 방법 및 아연도금강판 | |
BR112017023814A2 (pt) | tira de aço de alta resistência galvanizada por imersão a quente | |
MX353363B (es) | El uso de complejos metalicos de ditioleno sustituido por arilo o heteroarilo en calidad de absorbedores de ir. | |
MY169256A (en) | Zirconium pretreatment compositions containing lithium, associated methods for treating metal substrates, and related coated metal substrates | |
EP2995698A4 (en) | HOT-DIP ZINC-COATED STEEL SHEET OR ALLOYED HOT-DIP ZINC-COATED STEEL SHEET HAVING SUPERIOR STRENGTH-BENDABILITY BALANCE WITH TENSILE STRENGTH OF 1180 MPa OR MORE | |
MX2016004415A (es) | Hoja de acero que tiene un revestimiento de znalmg y flexibilidad mejorada y metodo de produccion correspondiente. | |
UA112312C2 (uk) | Ванна розплавлених солей для азотування механічних деталей з сталі, спосіб азотування механічних деталей з сталі та механічна деталь з азотованої сталі | |
BR112013028712A2 (pt) | processo para a produção de partículas | |
IN2015DN00665A (pt) | ||
MX2015001322A (es) | Composicion resistente a calor elevado. | |
MY171863A (en) | Methods for treating a ferrous metal substrate | |
MX2018013233A (es) | Composicion para reducir la remocion corrosiva de material en el decapado de superficies metalicas que comprenden acero desnudo y galvanizado. | |
BR112013031898A2 (pt) | revestimento por autodeposição em único banho para combinação de substratos de metal e métodos para esse revestimento | |
MX2015014136A (es) | Aleacion para un miembro de cierre de cremallera y miembro de cierre de cremallera. | |
BR112016002541A2 (pt) | composições de pré-tratamento de metal que compreendem silanos e ácidos organofosforosos | |
BR112015022751A2 (pt) | agente quelante, e, métodos de fabricação do agente quelante e de desativação de um íon de metal | |
BR112015021017A2 (pt) | revestimento de conversão de temperatura alta em substratos de aço e ferro |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B25A | Requested transfer of rights approved |
Owner name: FONTAINE HOLDINGS NV (BE) |
|
B06F | Objections, documents and/or translations needed after an examination request according [chapter 6.6 patent gazette] | ||
B06T | Formal requirements before examination [chapter 6.20 patent gazette] | ||
B06A | Patent application procedure suspended [chapter 6.1 patent gazette] | ||
B09A | Decision: intention to grant [chapter 9.1 patent gazette] | ||
B16A | Patent or certificate of addition of invention granted [chapter 16.1 patent gazette] |
Free format text: PRAZO DE VALIDADE: 10 (DEZ) ANOS CONTADOS A PARTIR DE 22/04/2020, OBSERVADAS AS CONDICOES LEGAIS. |
|
B21F | Lapse acc. art. 78, item iv - on non-payment of the annual fees in time |
Free format text: REFERENTE A 12A ANUIDADE. |
|
B24J | Lapse because of non-payment of annual fees (definitively: art 78 iv lpi, resolution 113/2013 art. 12) |
Free format text: EM VIRTUDE DA EXTINCAO PUBLICADA NA RPI 2653 DE 09-11-2021 E CONSIDERANDO AUSENCIA DE MANIFESTACAO DENTRO DOS PRAZOS LEGAIS, INFORMO QUE CABE SER MANTIDA A EXTINCAO DA PATENTE E SEUS CERTIFICADOS, CONFORME O DISPOSTO NO ARTIGO 12, DA RESOLUCAO 113/2013. |