BR112016013130B1 - folha de aço e método para fabricar uma folha de aço - Google Patents

folha de aço e método para fabricar uma folha de aço Download PDF

Info

Publication number
BR112016013130B1
BR112016013130B1 BR112016013130-4A BR112016013130A BR112016013130B1 BR 112016013130 B1 BR112016013130 B1 BR 112016013130B1 BR 112016013130 A BR112016013130 A BR 112016013130A BR 112016013130 B1 BR112016013130 B1 BR 112016013130B1
Authority
BR
Brazil
Prior art keywords
steel sheet
temperature
martensite
cold
equal
Prior art date
Application number
BR112016013130-4A
Other languages
English (en)
Portuguese (pt)
Other versions
BR112016013130A2 (pt
Inventor
Josée DRILLET
Véronique HEBERT
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of BR112016013130A2 publication Critical patent/BR112016013130A2/pt
Publication of BR112016013130B1 publication Critical patent/BR112016013130B1/pt

Links

Images

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0421—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the working steps
    • C21D8/0436—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0447—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing
    • C21D8/0447—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for drawing, e.g. for deep-drawing characterised by the heat treatment
    • C21D8/0473—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
    • C23C14/06—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the coating material
    • C23C14/14—Metallic material, boron or silicon
    • C23C14/16—Metallic material, boron or silicon on metallic substrates or on substrates of boron or silicon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Steel (AREA)
  • Coating With Molten Metal (AREA)
BR112016013130-4A 2013-12-11 2014-12-05 folha de aço e método para fabricar uma folha de aço BR112016013130B1 (pt)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
USPCT/US2013/074482 2013-12-11
PCT/US2013/074482 WO2015088523A1 (en) 2013-12-11 2013-12-11 Cold rolled and annealed steel sheet
PCT/IB2014/066647 WO2015087224A1 (fr) 2013-12-11 2014-12-05 Acier à haute résistance et procédé de fabrication

Publications (2)

Publication Number Publication Date
BR112016013130A2 BR112016013130A2 (pt) 2017-08-08
BR112016013130B1 true BR112016013130B1 (pt) 2021-03-09

Family

ID=52278684

Family Applications (1)

Application Number Title Priority Date Filing Date
BR112016013130-4A BR112016013130B1 (pt) 2013-12-11 2014-12-05 folha de aço e método para fabricar uma folha de aço

Country Status (16)

Country Link
US (1) US10597745B2 (https=)
EP (1) EP3084014B1 (https=)
JP (1) JP6599868B2 (https=)
KR (1) KR102264641B1 (https=)
CN (1) CN105874086B (https=)
BR (1) BR112016013130B1 (https=)
CA (1) CA2933542C (https=)
ES (1) ES2741304T3 (https=)
HU (1) HUE044562T2 (https=)
MA (1) MA39075B1 (https=)
MX (1) MX388381B (https=)
PL (1) PL3084014T3 (https=)
RU (1) RU2669487C2 (https=)
UA (1) UA118036C2 (https=)
WO (2) WO2015088523A1 (https=)
ZA (1) ZA201603640B (https=)

Families Citing this family (45)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
ES2777835T3 (es) 2014-07-03 2020-08-06 Arcelormittal Procedimiento para producir una lámina de acero de ultra alta resistencia no recubierta y una lámina obtenida
WO2016198906A1 (fr) 2015-06-10 2016-12-15 Arcelormittal Acier a haute résistance et procédé de fabrication
KR101736619B1 (ko) 2015-12-15 2017-05-17 주식회사 포스코 화성처리성 및 굽힘가공성이 우수한 초고강도 강판 및 이의 제조방법
WO2017109542A1 (en) * 2015-12-21 2017-06-29 Arcelormittal Method for producing a high strength steel sheet having improved ductility and formability, and obtained steel sheet
WO2017109541A1 (en) 2015-12-21 2017-06-29 Arcelormittal Method for producing a high strength coated steel sheet having improved ductility and formability, and obtained coated steel sheet
PL3397785T3 (pl) 2015-12-29 2020-08-10 Arcelormittal Sposób wytwarzania blachy stalowej ocynkowanej z przeżarzaniem o bardzo wysokiej wytrzymałości i otrzymana blacha stalowa ocynkowana z przeżarzaniem
JP6264507B2 (ja) * 2016-02-10 2018-01-24 Ｊｆｅスチール株式会社 高強度亜鉛めっき鋼板及びその製造方法
KR101822292B1 (ko) 2016-08-17 2018-01-26 현대자동차주식회사 고강도 특수강
KR101822295B1 (ko) 2016-09-09 2018-01-26 현대자동차주식회사 고강도 특수강
WO2018055425A1 (en) * 2016-09-22 2018-03-29 Arcelormittal High strength and high formability steel sheet and manufacturing method
KR101858852B1 (ko) * 2016-12-16 2018-06-28 주식회사 포스코 항복강도, 연성 및 구멍확장성이 우수한 고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법
KR101889181B1 (ko) 2016-12-19 2018-08-16 주식회사 포스코 굽힘성 및 신장플랜지성이 우수한 고장력강 및 이의 제조방법
CN110100030B (zh) * 2016-12-23 2021-04-20 Posco公司 弯曲加工性优异的超高强度热轧钢板及其制造方法
BR112019010271A2 (pt) * 2017-01-17 2019-09-10 Nippon Steel Corporation chapa de aço para estampagem a quente
US11408045B2 (en) * 2017-02-20 2022-08-09 Nippon Steel Corporation Steel sheet
DE102017112164A1 (de) * 2017-06-01 2018-12-06 Benteler Automobiltechnik Gmbh Blechumformbauteil sowie Verfahren zur Herstellung des Blechumformbauteils
WO2018220430A1 (en) * 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
US20200340124A1 (en) * 2017-10-24 2020-10-29 Arcelormittal A method for the manufacture of a coated steel sheet
US11680331B2 (en) 2017-10-24 2023-06-20 Arcelormittal Method for the manufacture of a coated steel sheet
WO2019111028A1 (en) 2017-12-05 2019-06-13 Arcelormittal Cold rolled and annealed steal sheet and method of manufacturing the same
KR102095509B1 (ko) 2017-12-22 2020-03-31 주식회사 포스코 고강도 열연 도금강판 및 그의 제조방법
US20210189517A1 (en) * 2018-05-22 2021-06-24 Thyssenkrupp Steel Europe Ag Sheet Metal Part Formed from a Steel Having a High Tensile Strength and Method for Manufacturing Said Sheet Metal Part
JP7492460B2 (ja) 2018-06-12 2024-05-29 ティッセンクルップ スチール ヨーロッパ アクチェンゲゼルシャフト 平鋼製品およびその製造方法
CN109576579A (zh) * 2018-11-29 2019-04-05 宝山钢铁股份有限公司 一种具有高扩孔率和较高延伸率的980MPa级冷轧钢板及其制造方法
KR102538733B1 (ko) 2018-12-18 2023-05-31 아르셀러미탈 내지연 파괴성이 높은 프레스 경화된 부분 및 그 제조 방법
KR102153197B1 (ko) 2018-12-18 2020-09-08 주식회사 포스코 가공성이 우수한 냉연강판, 용융아연도금강판 및 이들의 제조방법
WO2020229877A1 (en) * 2019-05-15 2020-11-19 Arcelormittal A cold rolled martensitic steel and a method for it's manufacture
WO2020250009A1 (en) * 2019-06-12 2020-12-17 Arcelormittal A cold rolled martensitic steel and a method of martensitic steel thereof
KR102290782B1 (ko) * 2019-09-26 2021-08-18 주식회사 포스코 내구성이 우수한 고강도 코팅강판의 제조방법
WO2021116741A1 (en) 2019-12-13 2021-06-17 Arcelormittal Heat treated cold rolled steel sheet and a method of manufacturing thereof
CA3164036C (en) * 2019-12-18 2024-06-18 Arcelormittal Cold-rolled and annealed steel sheet and manufacturing method
CN113025877A (zh) * 2019-12-24 2021-06-25 通用汽车环球科技运作有限责任公司 高性能压制硬化钢
US11976341B2 (en) 2020-06-30 2024-05-07 Jfe Steel Corporation Steel sheet, member, and method for producing them
CN115698365B (zh) * 2020-07-20 2024-03-26 安赛乐米塔尔公司 经热处理的冷轧钢板及其制造方法
KR102485004B1 (ko) * 2020-12-17 2023-01-04 주식회사 포스코 가공성이 우수한 고강도 강판 및 그 제조방법
CN113528947B (zh) * 2021-06-21 2022-03-25 武汉钢铁有限公司 一种用CSP生产抗拉强度为1500MPa级高塑韧性汽车结构件用钢及生产方法
CN113699337B (zh) * 2021-08-06 2023-05-05 山西太钢不锈钢股份有限公司 一种9Cr系耐热钢连铸大圆坯热处理工艺
KR102949639B1 (ko) * 2021-09-27 2026-04-08 주식회사 포스코 구멍확장성 및 연성이 우수한 고강도 후물 강판 및 이의 제조방법
KR20230069426A (ko) * 2021-11-12 2023-05-19 주식회사 포스코 굽힘성 및 신장 플랜지성이 우수한 초고강도 강판 및 이의 제조 방법
KR20230077777A (ko) * 2021-11-25 2023-06-02 주식회사 포스코 성형성이 우수한 초고강도 열연 강판 및 이의 제조 방법
EP4502218A4 (en) * 2022-05-11 2025-07-30 Jfe Steel Corp STEEL SHEET, ELEMENT AND METHOD FOR THE PRODUCTION THEREOF
WO2023218576A1 (ja) * 2022-05-11 2023-11-16 Ｊｆｅスチール株式会社 亜鉛めっき鋼板、部材およびそれらの製造方法
JP7635895B1 (ja) * 2023-03-31 2025-02-26 Ｊｆｅスチール株式会社 鋼板、部材およびそれらの製造方法
KR20250150126A (ko) * 2023-03-31 2025-10-17 제이에프이 스틸 가부시키가이샤 강판, 부재 및 그들의 제조 방법
CN116949366B (zh) 2023-08-01 2024-03-19 北京理工大学 无碳化物的回火马氏体钢及其制备方法

Family Cites Families (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1999005334A1 (en) 1997-07-28 1999-02-04 Exxonmobil Upstream Research Company Ultra-high strength, weldable, essentially boron-free steels wit h superior toughness
DZ2530A1 (fr) 1997-12-19 2003-02-01 Exxon Production Research Co Procédé de préparation d'une tôle d'acier cette tôle d'acier et procédé pour renforcer la resistanceà la propagation des fissures d'une tôle d'acier.
JP2002180182A (ja) 2000-12-08 2002-06-26 Kawasaki Steel Corp 耐孔あき性に優れる鋼材
JP4109619B2 (ja) 2003-12-16 2008-07-02 株式会社神戸製鋼所 伸び、及び伸びフランジ性に優れた高強度鋼板
DE102005008410B3 (de) * 2005-02-24 2006-02-16 Thyssenkrupp Stahl Ag Verfahren zum Beschichten von Stahlbändern und beschichtetes Stahlband
JP4772496B2 (ja) * 2005-12-27 2011-09-14 新日本製鐵株式会社 穴拡げ性に優れた高強度冷延薄鋼板及びその製造方法
EP1832667A1 (fr) 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
JP4959471B2 (ja) * 2007-08-28 2012-06-20 新日本製鐵株式会社 靭性に優れた機械構造用高強度シームレス鋼管及びその製造方法
JP5365216B2 (ja) * 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
JP5365217B2 (ja) 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
US20110168000A1 (en) 2008-03-03 2011-07-14 Langner F Richard Ballistic wall panel device and system and method therefor
JP5251208B2 (ja) * 2008-03-28 2013-07-31 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
EP2123786A1 (fr) * 2008-05-21 2009-11-25 ArcelorMittal France Procédé de fabrication de tôles d'aciers dual phase laminées à froid à trés haute résistance et tôles ainsi produites
JP5418168B2 (ja) 2008-11-28 2014-02-19 Ｊｆｅスチール株式会社 成形性に優れた高強度冷延鋼板、高強度溶融亜鉛めっき鋼板およびそれらの製造方法
EP2199425A1 (fr) 2008-12-18 2010-06-23 ArcelorMittal France Générateur de vapeur industriel pour le dépôt d'un revêtement d'alliage sur une bande métallique (II)
CN102264934A (zh) 2008-12-26 2011-11-30 杰富意钢铁株式会社 焊接热影响部及母材部的耐延性破裂发生特性优良的钢材及其制造方法
JP4924730B2 (ja) 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP5412182B2 (ja) 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5703608B2 (ja) 2009-07-30 2015-04-22 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5466552B2 (ja) * 2010-03-24 2014-04-09 株式会社神戸製鋼所 伸び、伸びフランジ性および溶接性を兼備した高強度冷延鋼板
JP5136609B2 (ja) 2010-07-29 2013-02-06 Ｊｆｅスチール株式会社 成形性および耐衝撃性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
WO2012052626A1 (fr) * 2010-10-21 2012-04-26 Arcelormittal Investigacion Y Desarrollo, S.L. Tole d'acier laminee a chaud ou a froid, don procede de fabrication et son utilisation dans l'industrie automobile
KR101220619B1 (ko) * 2010-11-09 2013-01-10 주식회사 포스코 초고강도 냉연강판, 용융아연도금강판 및 이들의 제조방법
US9745639B2 (en) 2011-06-13 2017-08-29 Kobe Steel, Ltd. High-strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof
BR112014007498B1 (pt) 2011-09-30 2019-04-30 Nippon Steel & Sumitomo Metal Corporation Chapa de aço galvanizado a quente de alta resistência e método de produção da mesma
EP2803747B1 (en) 2012-01-13 2019-03-27 Nippon Steel & Sumitomo Metal Corporation Cold-rolled steel sheet and method for producing cold-rolled steel sheet
JP6047037B2 (ja) 2012-03-29 2016-12-21 株式会社神戸製鋼所 鋼板形状に優れた高強度冷延鋼板の製造方法
CN104245971B (zh) * 2012-03-30 2017-09-12 奥钢联钢铁有限责任公司 高强度冷轧钢板和生产该钢板的方法

Also Published As

Publication number Publication date
MX388381B (es) 2025-03-19
EP3084014A1 (fr) 2016-10-26
RU2016123172A (ru) 2017-12-14
RU2669487C2 (ru) 2018-10-11
CN105874086B (zh) 2018-07-03
CA2933542A1 (fr) 2015-06-18
JP6599868B2 (ja) 2019-10-30
ES2741304T3 (es) 2020-02-10
PL3084014T3 (pl) 2019-10-31
US10597745B2 (en) 2020-03-24
BR112016013130A2 (pt) 2017-08-08
KR20160096611A (ko) 2016-08-16
HUE044562T2 (hu) 2019-11-28
KR102264641B1 (ko) 2021-06-14
JP2017507241A (ja) 2017-03-16
UA118036C2 (uk) 2018-11-12
MA39075B1 (fr) 2017-11-30
RU2016123172A3 (https=) 2018-08-21
CA2933542C (fr) 2023-02-14
ZA201603640B (en) 2017-11-29
US20160312326A1 (en) 2016-10-27
MA39075A1 (fr) 2017-01-31
MX2016007664A (es) 2016-09-13
WO2015087224A1 (fr) 2015-06-18
WO2015088523A1 (en) 2015-06-18
CN105874086A (zh) 2016-08-17
EP3084014B1 (fr) 2019-05-08

Similar Documents

Publication Publication Date Title
BR112016013130B1 (pt) folha de aço e método para fabricar uma folha de aço
KR102648441B1 (ko) 우수한 신장-플랜지 성형성을 가진 열간-압연 고강도 롤-성형 가능한 강 시트 및 그 제조방법
BR112018012538B1 (pt) Método para produzir uma folha de aço revestida, processo para produzir uma solda por pontos de resistência de pelo menos duas folhas de aço, folha de aço revestida, uso de uma folha de aço e uso de uma solda por pontos de resistência
BR112017025366B1 (pt) Chapa de aço e método para fabricação de uma chapa laminada a frio e recozida
BR112019027154A2 (pt) chapa de aço laminado a quente e método de fabricação da mesma
BR112018012422B1 (pt) Método para produzir uma folha de aço, processo para a produção de um componente, folha de aço, estrutura soldada, uso de uma folha de aço e uso de uma soldagem por pontos de resistência
BR112019003791B1 (pt) Chapa de aço laminada a frio e tratada termicamente, junta soldada por pontos de resistência, método para a fabricação de uma chapa de aço laminada a frio e tratada termicamente e processo para a produção de uma junta soldada por pontos de resistência
BR112018013375B1 (pt) Chapa de aço e método de fabricação de uma chapa de aço
BR112019010707A2 (pt) chapa de aço temperado e revestido, método de produção de chapas de aço temperado e revestido, uso de chapa de aço e veículo
BR112018011831B1 (pt) Tira de aço galvanizada por imersão a quente de alta resistência e método de produção
BR112018012133B1 (pt) Método para produzir uma chapa de aço, processo para produzir uma solda por ponto de resistência, chapa de aço, estrutura soldada, uso de uma chapa de aço e uso de uma estrutura soldada
BR112020008013B1 (pt) Chapa de aço tratada com calor e laminada a frio, método para fabricar uma chapa de aço e método para produzir uma junta soldada
KR20190064681A (ko) 성형성 및 형상 동결성이 우수한, 고강도 냉연 강판, 고강도 용융 아연도금 강판 및 고강도 합금화 용융 아연도금 강판, 및 그들의 제조 방법
BRPI0912879B1 (pt) Chapa de aço bifásico laminada a frio e recozida e processo de fabricação de uma chapa de aço bifásico laminada a frio e recozida
BR112014002026B1 (pt) Chapa de aço de alta resistência e chapa de aço galvanizado de alta resistência em fixabilidade de forma,e método de produção das mesmas.
JPWO2014185405A1 (ja) 熱延鋼板およびその製造方法
BR112020007989B1 (pt) Chapa de aço laminada a frio, método para fabricação de uma chapa de aço laminada a frio e método para produção de uma junta soldada por pontos de pelo menos duas chapas de aço
BR112019022543B1 (pt) Método para produzir uma chapa de aço revestida, processo para produzir uma solda a pontos por resistência, chapa de aço revestida, estrutura soldada, processo para produzir a estrutura soldada, uso de uma chapa de aço revestida e uso de uma solda a pontos por resistência
BR112019003122B1 (pt) Chapa de aço
BR112014019497B1 (pt) Chapa de aço laminada a frio, chapa de aço revestida, e métodos para produção das mesmas
ES2818195T3 (es) Tira de acero galvanizado por inmersión en caliente de alta resistencia
BR112022011703B1 (pt) Chapa de aço laminada a frio e recozida e método de fabricação de uma chapa de aço laminada a frio e recozida
BR112021003523A2 (pt) chapa de aço laminada a quente, processo para a fabricação de uma chapa de aço laminada a quente e uso da chapa de aço laminada a quente
BR112021003523B1 (pt) Chapa de aço laminada a quente, processo para a fabricação de uma chapa de aço laminada a quente e uso da chapa de aço laminada a quente
BR112023008842B1 (pt) Chapa de aço revestida, método para produzir uma chapa de aço revestida, peça de aço endurecida por pressão e processo para fabricar uma peça de aço endurecida por pressão

Legal Events

Date Code Title Description
B06U Preliminary requirement: requests with searches performed by other patent offices: procedure suspended [chapter 6.21 patent gazette]
B06A Patent application procedure suspended [chapter 6.1 patent gazette]
B09A Decision: intention to grant [chapter 9.1 patent gazette]
B16A Patent or certificate of addition of invention granted [chapter 16.1 patent gazette]

Free format text: PRAZO DE VALIDADE: 20 (VINTE) ANOS CONTADOS A PARTIR DE 05/12/2014, OBSERVADAS AS CONDICOES LEGAIS.