BR112013021462A2 - processo para derreter e refinar vidro sódico cálcico - Google Patents
processo para derreter e refinar vidro sódico cálcicoInfo
- Publication number
- BR112013021462A2 BR112013021462A2 BR112013021462A BR112013021462A BR112013021462A2 BR 112013021462 A2 BR112013021462 A2 BR 112013021462A2 BR 112013021462 A BR112013021462 A BR 112013021462A BR 112013021462 A BR112013021462 A BR 112013021462A BR 112013021462 A2 BR112013021462 A2 BR 112013021462A2
- Authority
- BR
- Brazil
- Prior art keywords
- sodium silicate
- glass
- calcium
- sodium
- silicate glass
- Prior art date
Abstract
processo para derreter e refinar vidro sódico cálcico a presente invenção refere-se a um processo para fazer vidro sódico cálcio que inclui calcinar carbonato de cálcio na fase sólida e em temperatura elevada para formar óxido de cálcio e liberar gases tais como dióxido de carbono. o vidro de silicato de sódio é formado separadamente na fase líquida enquanto libra os produtos de reação gasosa. o óxido de cálcio e os produtos de vidro de silicato de sódio intermediários são misturados na fase líquida para formar uma fusão de vidro sódico cálcio. a formação de vidro de silicato de sódio como um produto intermediário antes de misturá-lo com o óxido de cálcio, tem a vantagem de promover a liberação de produtos de reação gasosa no silicato de sódio devido, pelo menos em parte, à viscosidade relativamente baixa do vidro de silicato de sódio. a etapa de calcinação e/ou a etapa de formação de silicato de sódio e/ou a etapa de mixagem final podem ser realizadas sob pressão reduzida ainda para promover a liberação de gases e reduzir formação de bolhas.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US13/034,154 US9051199B2 (en) | 2011-02-24 | 2011-02-24 | Process for melting and refining soda-lime glass |
PCT/US2012/026569 WO2012116303A1 (en) | 2011-02-24 | 2012-02-24 | Process for melting and refining soda-lime glass |
Publications (1)
Publication Number | Publication Date |
---|---|
BR112013021462A2 true BR112013021462A2 (pt) | 2016-11-01 |
Family
ID=46025872
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112013021462A BR112013021462A2 (pt) | 2011-02-24 | 2012-02-24 | processo para derreter e refinar vidro sódico cálcico |
Country Status (13)
Country | Link |
---|---|
US (2) | US9051199B2 (pt) |
EP (2) | EP2678279B1 (pt) |
JP (1) | JP2014506560A (pt) |
CN (2) | CN103492326B (pt) |
AR (1) | AR085389A1 (pt) |
AU (1) | AU2012222173B2 (pt) |
BR (1) | BR112013021462A2 (pt) |
CL (1) | CL2013002426A1 (pt) |
MX (2) | MX349694B (pt) |
RU (1) | RU2013143164A (pt) |
TW (1) | TW201238928A (pt) |
WO (1) | WO2012116303A1 (pt) |
ZA (1) | ZA201306230B (pt) |
Families Citing this family (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
DE102014110483B4 (de) | 2014-07-24 | 2023-05-25 | Progress-Werk Oberkirch Ag | Verfahren zum Herstellen einer Befestigungsanordnung |
DE102014019391A1 (de) | 2014-12-30 | 2016-06-30 | Ipgr International Partners In Glass Research | Verfahren zur Erhöhung der Umsetzungsgeschwindigkeit von Flachglas- oder Behälterglasgemengen zur Glasschmelze durch Nutzbarmachung einer Alkali-Erdalkali-Carbonat Schmelze mit einem Erdalkalicarbonatgehalt zwischen 10 und 62 Massenprozent |
TW201711967A (zh) | 2015-08-26 | 2017-04-01 | 美商.康寧公司 | 用於增進的均質性之玻璃熔融系統及方法 |
DE102016205845A1 (de) | 2016-04-07 | 2017-10-12 | Tu Bergakademie Freiberg | Verfahren zur Herstellung von Glas, Steuereinrichtung, Anlage zur Herstellung von Glas |
CN106966584A (zh) * | 2017-03-28 | 2017-07-21 | 常州大学 | 一种绿色无毒玻璃用澄清剂的制备方法 |
FR3066810B1 (fr) | 2017-05-23 | 2019-06-14 | Arc France | Four combine |
FR3068347B1 (fr) * | 2017-06-30 | 2020-08-28 | Arc France | Preparation de fabrication de verre et four de verrerie |
FR3087768B1 (fr) | 2018-10-29 | 2020-10-30 | Arc France | Preparation de fabrication de verre et installation de verrerie industrielle |
CN114555675A (zh) * | 2019-10-08 | 2022-05-27 | Agc株式会社 | 带拒水拒油层的物品 |
FR3125033A1 (fr) | 2021-07-09 | 2023-01-13 | Arc France | Préparation de fabrication de verre et four de verrerie |
Family Cites Families (18)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2239880A (en) * | 1937-01-14 | 1941-04-29 | Philadelphia Quartz Co | Manufacture of silicates |
US2220750A (en) * | 1938-03-29 | 1940-11-05 | Norbert S Garbisch | Manufacture of siliceous bodies |
FR1477690A (fr) * | 1966-03-09 | 1967-04-21 | Saint Gobain | Procédé de préparation de matière première pour la fabrication du verre |
US3967934A (en) | 1969-06-13 | 1976-07-06 | Baxter Laboratories, Inc. | Prothrombin timer |
US4303487A (en) | 1978-04-19 | 1981-12-01 | Ppg Industries, Inc. | Production of alkali metal silicate having a high silica to alkali metal oxide ratio |
GB8728892D0 (en) | 1987-12-10 | 1988-01-27 | Pilkington Plc | Producing molten glass |
US4920080A (en) | 1988-08-19 | 1990-04-24 | Ppg Industries, Inc. | Method of making glass with preliminary reaction of batch materials |
US5395806A (en) | 1993-08-28 | 1995-03-07 | Chemical Products Corporation | Dense, granular alkaline earth metal carbonate and alkali metal salt composition for use in glass manufacture |
US6287378B1 (en) | 1996-09-03 | 2001-09-11 | Minerals Technologies, Inc. | Method of producing synthetic silicates and use thereof in glass production |
HU224748B1 (en) * | 1999-02-05 | 2006-01-30 | Saint Gobain | Method for preparing raw materials for glass-making |
EG25130A (en) | 1999-02-05 | 2011-09-18 | Saint Gobain Vitrage | Process and apparatus for preparing batch materials for the manufacture of glass. |
MXPA04005800A (es) * | 2001-12-27 | 2004-09-10 | Specialty Minerals Michigan | Metodo para la fabricacion de vidrio y composiciones para el mismo. |
MXNL02000026A (es) | 2002-08-30 | 2004-03-05 | Vitro Europa Ltd | Metodo para preparar cargas pre-reaccionadas de materias primas para la produccion de formulas de vidrio. |
FR2851767B1 (fr) * | 2003-02-27 | 2007-02-09 | Saint Gobain | Procede de preparation d'un verre par melange de verres fondus |
US7946131B2 (en) | 2006-03-23 | 2011-05-24 | Johns Manville | Method for producing reactive raw material for manufacture of glass suitable fiberization |
US20070220922A1 (en) | 2006-03-23 | 2007-09-27 | Bauer Jon F | Method for making glass fibers |
JP2010202413A (ja) * | 2007-06-27 | 2010-09-16 | Asahi Glass Co Ltd | ガラスの製造方法、ガラス原料の製造方法及びガラス原料 |
DE102009025905A1 (de) | 2008-06-10 | 2010-02-11 | Matthias Fraass | Hochleistungsschmelzverfahren für die Glasherstellung als High-Efficieny-Glas-Melter-Verfahren (HEGM-Verfahren) und dazugehörige Anlage zur Glasherstellung |
-
2011
- 2011-02-24 US US13/034,154 patent/US9051199B2/en not_active Expired - Fee Related
-
2012
- 2012-02-16 TW TW101105054A patent/TW201238928A/zh unknown
- 2012-02-23 AR ARP120100601A patent/AR085389A1/es not_active Application Discontinuation
- 2012-02-24 CN CN201280010445.7A patent/CN103492326B/zh not_active Expired - Fee Related
- 2012-02-24 WO PCT/US2012/026569 patent/WO2012116303A1/en active Application Filing
- 2012-02-24 RU RU2013143164/03A patent/RU2013143164A/ru not_active Application Discontinuation
- 2012-02-24 MX MX2015006157A patent/MX349694B/es unknown
- 2012-02-24 AU AU2012222173A patent/AU2012222173B2/en not_active Ceased
- 2012-02-24 EP EP12718441.4A patent/EP2678279B1/en active Active
- 2012-02-24 JP JP2013555609A patent/JP2014506560A/ja active Pending
- 2012-02-24 EP EP18151216.1A patent/EP3342758A1/en not_active Withdrawn
- 2012-02-24 MX MX2013009784A patent/MX2013009784A/es active IP Right Grant
- 2012-02-24 CN CN201611021299.4A patent/CN106517738B/zh not_active Expired - Fee Related
- 2012-02-24 BR BR112013021462A patent/BR112013021462A2/pt not_active Application Discontinuation
-
2013
- 2013-08-19 ZA ZA2013/06230A patent/ZA201306230B/en unknown
- 2013-08-22 CL CL2013002426A patent/CL2013002426A1/es unknown
-
2015
- 2015-04-13 US US14/684,923 patent/US20150299017A1/en not_active Abandoned
Also Published As
Publication number | Publication date |
---|---|
TW201238928A (en) | 2012-10-01 |
ZA201306230B (en) | 2014-11-26 |
MX2013009784A (es) | 2013-09-26 |
EP3342758A1 (en) | 2018-07-04 |
AR085389A1 (es) | 2013-09-25 |
US20150299017A1 (en) | 2015-10-22 |
AU2012222173A1 (en) | 2013-09-12 |
RU2013143164A (ru) | 2015-03-27 |
US20120216574A1 (en) | 2012-08-30 |
CN106517738A (zh) | 2017-03-22 |
WO2012116303A1 (en) | 2012-08-30 |
US9051199B2 (en) | 2015-06-09 |
EP2678279B1 (en) | 2018-04-11 |
MX349694B (es) | 2017-08-09 |
CL2013002426A1 (es) | 2014-06-20 |
CN103492326A (zh) | 2014-01-01 |
CN106517738B (zh) | 2019-04-16 |
CN103492326B (zh) | 2016-12-21 |
EP2678279A1 (en) | 2014-01-01 |
JP2014506560A (ja) | 2014-03-17 |
AU2012222173B2 (en) | 2016-01-14 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR112013021462A2 (pt) | processo para derreter e refinar vidro sódico cálcico | |
BR112015031344A2 (pt) | composição mineral com base em uma fase sólida mista de carbonatos de cálcio e magnésio e processo para a preparação de tal composição | |
WO2013023731A3 (de) | Verfahren zur herstellung von ternesit-belit-calciumsulfoaluminat-klinker | |
BR112012022583A2 (pt) | método e reator de produção em linha de carbonato de cálcio no processo de produção de uma trama fibrosa | |
BR112017005780A2 (pt) | ?uso de um carbonato de cálcio reagido na superfície como agente antiaglomerante, métodos para controlar, reduzir ou evitar aglomeração de uma composição particulada e para produzir uma composição, e, composição? | |
BR112013000618A2 (pt) | novo processo de produção de sílica precipitada | |
BR112013004588A2 (pt) | processo para preparar ácido acrílico as partir de metanol e ácido acético, ácido acrílico, e, fase líquida p. | |
BR112018002011A2 (pt) | ?processo para produzir carbonato de cálcio precipitado, carbonato de cálcio precipitado, carbonato de cálcio precipitado revestido na superfície, sistema de carbonatação para produzir um carbonato de cálcio precipitado, e, uso de um carbonato de cálcio precipitado ou de um carbonato de cálcio precipitado revestido na superfície? | |
BR112016029621A2 (pt) | método e produto para controle de odor, processo, e, uso de um carbonato de cálcio reagido na superfície. | |
BRPI0810238A8 (pt) | Processo para produção de pcc | |
BR112015014668A2 (pt) | mistura de material de molde para produzir moldes e machos de fundição, método para produção de moldes ou machos de fundição, molde ou macho, uso de uma mistura de material de molde, e, sistema multicomponente para produção de moldes ou machos | |
BR112018000778A2 (pt) | método para a fabricação de aluminatos de cálcio em um forno industrial | |
BR112013024304A2 (pt) | pino de ancoragem e processo de produção | |
BR112018012056A2 (pt) | ?processo e sistema de reação para produção de óxido de etileno, carbonato de etileno e/ou etilenoglicol a partir de etileno? | |
BR112013016578A2 (pt) | processo para preparar metilmercaptopropionaldeídeo | |
BR112016002340A2 (pt) | método para a combustão e resfriamento de rochas carbonáticas em um forno de cuba regenerativa de corrente paralela para cal com duas cubas e forno de cuba regenerativa de corrente paralela para cal para a combustão e resfriamento de rochas carbonáticas | |
BR112012018870A2 (pt) | processo de fabricação de uma composição de elastômero auto-vedante | |
BR112012012895A2 (pt) | método para produzir o carbonato de etileno e etileno glicol. | |
BR112013021063A2 (pt) | usoi de um alquil alcoxi sulfonato linear, método para a produção de espumas e composição aquosa espumável | |
BR112014018028A8 (pt) | Processo para preparação de sílicas precipitadas | |
BR112012008819A2 (pt) | asfalto modificado de borracha fragmentada com estabilidade melhorada | |
BR112016026603B8 (pt) | Processo para a preparação de um material compósito carbonáceo e processo para fabricação de um bloco de carbono | |
BR112015017802A2 (pt) | processo e dispositivo para produção de combustível para uma turbina de gás | |
BR112014007046A2 (pt) | método de bloqueio/abertura para furo de rosqueamento, método de bloqueio e aparelho de bloqueio/abertura do mesmo | |
BR112012033707A2 (pt) | processo e instalação para a produção de um produto líquido ou semilíquido sensível à oxidação. |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B06F | Objections, documents and/or translations needed after an examination request according art. 34 industrial property law | ||
B06T | Formal requirements before examination | ||
B07A | Technical examination (opinion): publication of technical examination (opinion) | ||
B09B | Decision: refusal | ||
B09B | Decision: refusal |
Free format text: MANTIDO O INDEFERIMENTO UMA VEZ QUE NAO FOI APRESENTADO RECURSO DENTRO DO PRAZO LEGAL |