AT207057B - Optisches Glas - Google Patents

Optisches Glas

Info

Publication number
AT207057B
AT207057B AT236958A AT236958A AT207057B AT 207057 B AT207057 B AT 207057B AT 236958 A AT236958 A AT 236958A AT 236958 A AT236958 A AT 236958A AT 207057 B AT207057 B AT 207057B
Authority
AT
Austria
Prior art keywords
sep
optical glass
weight
glasses
oxide
Prior art date
Application number
AT236958A
Other languages
English (en)
Inventor
Heinz Dipl Chem Broemer
Norbert Meinert
Original Assignee
Leitz Ernst Gmbh
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Leitz Ernst Gmbh filed Critical Leitz Ernst Gmbh
Priority to AT236958A priority Critical patent/AT207057B/de
Application granted granted Critical
Publication of AT207057B publication Critical patent/AT207057B/de

Description


   <Desc/Clms Page number 1> 
 



  Optisches Glas 
Die Erfindung'betrifft optische Gläser mit Borsäure als Glasbildner, Aluminiumoxyd, sowie bis zu etwa 50 Gew.-% Lanthanoxyd, die allenfalls ausserdem noch beträchtliche Mengen an Oxy- den anderer seltener Erden enthalten können, wie etwa Thoriumoxyd ; derartige Gläser weisen neben einem hohen Brechungsindex ne > 1,65 eine geringe'Dispersion auf. 



   Diese Gläser eignen sich besonders für Zwecke der rechnenden Optik, weil sich bei gleichen Brechungskräften längere Krümmungsradien ergeben als bei niedrig brechenden Gläsern und dadurch die Gesamt-Fehlerkorrektur wesentlich erleichtert wird. Thoriumhaltige Gläser können allerdings wegen ihrer Radioaktivität nur unter bestimmten   Vorsichtsmassnahmen   bearbeitet werden und sind zum Teil auch nur sehr beschränkt verwendbar. 



   Alle diese Gläser weisen jedoch verhältnismä- ssig geringe Haltbarkeit und Widerstandsfähigkeit   gegen Witterungseinflüsse   auf, was sich besonders bei Bearbeitung der Gläser äusserst unangenehm auswirkt. 



   Es wurde daher bereits vorgeschlagen, derartigen Gläsern zur Erhöhung ihrer Haltbarkeit Kieselsäure bis zu 12% zuzusetzen, womit jedoch kein wesentlicher Fortschritt erzielt wurde. 



   Nach der Erfindung werden nun bei optischen Gläsern der eingangs beschriebenen Zusammensetzung die oben aufgezeigten Nachteile im wesentlichen dadurch behoben, dass das Glas 16- 32 Gew.-% Borsäure sowie über 10   Gew.-"/o-   vorzugsweise bis 23 Gew.-% - Aluminiumoxyd enthält, wobei der Gesamt-Anteil dieser beiden Glasbildner 29-50   Gew.-"/o   beträgt.
Nach einem weitem Merkmal der Erfindung enthält das Glas zusätzlich noch 8-50   Gew.-'/o   an Oxyden zweiwertiger Elemente und ausserdem vorzugsweise bis zu je 10   Gew.-/o Zirkon-   oxyd oder/und Tantaloxyd. 



   Als besonders hochwertig-d. h. gegen äussere Einflüsse unempfindlich-haben sich erfindungsgemässe optische Gläser mit einer   Zusammenset-   zung aus folgenden Bestandteilen in   Gew.-"/e   erwiesen : 
 EMI1.1 
 mente und vorzugsweise bis je 10% ZrO2 oder/ und   TaO"wobei   der Gesamt-Anteil von B2O3 und   Alp,   zusammen zwischen 29 und 50   Gew.-/o   liegen. 



   In der folgenden Tabelle sind eine Anzahl vorteilhafter   Ausführungsbeispiele   von nach der Vorschrift der Erfindung zusammengesetzten Gläsern angegeben, die z. B. bei Behandlung mit Salpetersäure um mindestens zwei Grössenordnungen höhere Beständigkeit aufweisen als die bisher bekannten Gläser der eingangs beschriebenen Zusammensetzung ; die hier angegebenen Gläser lassen sich aus den angegebenen Gemengen in Platintiegeln bei Temperaturen von etwa   1200.   bis   13000 C niederschme\zen   und bis etwa 10000 C herunter rühren. 
 EMI1.2 
 
<tb> 
<tb> 



  Tabelle <SEP> in <SEP> Gew.-*/ & 
<tb> Schmelz-Nr. <SEP> B2O, <SEP> Al2O3 <SEP> La2O3 <SEP> CaO <SEP> MgO <SEP> BaO <SEP> ZrO2 <SEP> CdO <SEP> Ta2O5 <SEP> ne <SEP> v <SEP> # <SEP> # <SEP> v
<tb> EL <SEP> 15 <SEP> 25,2 <SEP> 21,0 <SEP> 40,3 <SEP> 13,5 <SEP> - <SEP> - <SEP> - <SEP> - <SEP> - <SEP> 1,6837 <SEP> 53,2 <SEP> 547 <SEP> - <SEP> 4,0
<tb> EL/T <SEP> 1 <SEP> 26,4 <SEP> 21,9 <SEP> 37,6 <SEP> 14,1 <SEP> - <SEP> - <SEP> - <SEP> - <SEP> - <SEP> 1,6742 <SEP> 53,6 <SEP> 548 <SEP> - <SEP> 3,0
<tb> EL <SEP> 16 <SEP> 25,4 <SEP> 21,2 <SEP> 33,8 <SEP> 13,6 <SEP> - <SEP> - <SEP> 6,0 <SEP> - <SEP> - <SEP> 1,6875 <SEP> 52,0 <SEP> 547 <SEP> - <SEP> 5,2
<tb> EL <SEP> 26 <SEP> 29,7 <SEP> 15,1 <SEP> 37,3 <SEP> 12,7 <SEP> - <SEP> - <SEP> 5,2 <SEP> - <SEP> - <SEP> 1,6964 <SEP> 52,7 <SEP> 544 <SEP> - <SEP> 6,2
<tb> Vers.

   <SEP> Ca <SEP> 29,8 <SEP> 15,2 <SEP> 37,5 <SEP> 12,8 <SEP> - <SEP> - <SEP> 4,7 <SEP> - <SEP> - <SEP> 1,7012 <SEP> 52,2 <SEP> - <SEP> - <SEP> EL <SEP> 17 <SEP> 25,1 <SEP> 21,0 <SEP> 33,6 <SEP> 13,4 <SEP> - <SEP> - <SEP> - <SEP> - <SEP> 6,9 <SEP> 1,6855 <SEP> 51,7 <SEP> 550 <SEP> - <SEP> 3,8
<tb> EL <SEP> 12 <SEP> 22,9 <SEP> 16,3 <SEP> 10,7 <SEP> - <SEP> - <SEP> 50,1 <SEP> - <SEP> - <SEP> - <SEP> 1,6530 <SEP> 53,2 <SEP> - <SEP> - <SEP> EL <SEP> 9 <SEP> 17,0 <SEP> 12,4 <SEP> 39,6 <SEP> - <SEP> - <SEP> - <SEP> - <SEP> 31,0 <SEP> 1,7690 <SEP> 44,2 <SEP> 560 <SEP> - <SEP> 5,4
<tb> EL <SEP> 27 <SEP> 30,8 <SEP> 15,7 <SEP> 38,6 <SEP> - <SEP> 9,5 <SEP> - <SEP> 5,4 <SEP> - <SEP> - <SEP> 1,6842 <SEP> 53,5 <SEP> 543 <SEP> - <SEP> 6,0
<tb> EL <SEP> 28 <SEP> 26, <SEP> 0 <SEP> 13, <SEP> 2 <SEP> 48, <SEP> 2-8, <SEP> 1-43--1, <SEP> 7084 <SEP> 52, <SEP> 2 <SEP> 546-5,

   <SEP> 5 <SEP> 
<tb> EL <SEP> 29 <SEP> 29,8 <SEP> 15,3 <SEP> 37,4 <SEP> 3,1 <SEP> 9,2 <SEP> - <SEP> 5,2 <SEP> - <SEP> - <SEP> 1,6842 <SEP> 53,5 <SEP> 543 <SEP> - <SEP> 6,0
<tb> EL <SEP> 30 <SEP> 29,1 <SEP> 10,5 <SEP> 44,5 <SEP> 3,4 <SEP> 8,2 <SEP> - <SEP> 4,4 <SEP> - <SEP> - <SEP> 1,6886 <SEP> 53,2 <SEP> 544 <SEP> - <SEP> 5,7
<tb> EL <SEP> 31 <SEP> 29,8 <SEP> 10,4 <SEP> 45,6 <SEP> 3,5 <SEP> 8,5 <SEP> - <SEP> 2,2 <SEP> - <SEP> - <SEP> 1,7007 <SEP> 43,8 <SEP> 545 <SEP> - <SEP> 4,5
<tb> EL <SEP> 32 <SEP> 30, <SEP> 5 <SEP> 10. <SEP> 7 <SEP> 46, <SEP> 6 <SEP> 3, <SEP> 6 <SEP> 8, <SEP> 6----1, <SEP> 6944 <SEP> 54, <SEP> 2 <SEP> 543-5, <SEP> 2 <SEP> 
<tb> 


Claims (1)

  1. PATENTANSPRÜCHE : 1. Optisches Glas mit Borsäure als Glasbildner, Aluminiumoxyd, sowie bis zu etwa 50 Gew.-/o Lanthanoxyd, dadurch gekennzeichnet, dass es 16-32 Gew.-% Borsäure sowie über 10 Gew.-% - vorzugsweise bis 23 Gew.-% - Aluminiumoxyd enthält, wo'bei der Gesamt-Anteil dieser beiden Glasbildner 29-50 Gew.-% beträgt.
    2. Optisches Glas nach Anspruch 1, dadurch gekennzeichnet, dass es 8-50 Gew.-"/o Oxyde zweiwertiger Elemente enthält.
    3. Optisches Glas nach Anspruch 2, dadurch gekennzeichnet, dass es bis je 10 Gew.-% Zirkonoxyd oder/und Tantaloxyd enthält.
    4. Optisches Glas nach einem der Anspruche EMI2.1 teile in Gew.-"/G : 16-32%B2O3 :über10-23%Al2O3;25-50% La2O3; sowie 8-50% Oxyde zweiwertiger Elemente und vorzugsweise bis je 10% ZrO2 oder/ und Ta2O5, wobei der Gesamt-Anteil von B20a und Al2O3 zusammen zwischen 29 und 50 Gewei liegt.
AT236958A 1958-04-01 1958-04-01 Optisches Glas AT207057B (de)