ZA200905998B - Steel for tool-less hot forming or quenching with improved ductility - Google Patents

Steel for tool-less hot forming or quenching with improved ductility

Info

Publication number
ZA200905998B
ZA200905998B ZA200905998A ZA200905998A ZA200905998B ZA 200905998 B ZA200905998 B ZA 200905998B ZA 200905998 A ZA200905998 A ZA 200905998A ZA 200905998 A ZA200905998 A ZA 200905998A ZA 200905998 B ZA200905998 B ZA 200905998B
Authority
ZA
South Africa
Prior art keywords
quenching
tool
steel
hot forming
less hot
Prior art date
Application number
ZA200905998A
Other languages
English (en)
Inventor
Jean-Pierre Laurent
Thierry Malot
Original Assignee
Arcelormittal France
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal France filed Critical Arcelormittal France
Publication of ZA200905998B publication Critical patent/ZA200905998B/xx

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D7/00—Modifying the physical properties of iron or steel by deformation
    • C21D7/13—Modifying the physical properties of iron or steel by deformation by hot working
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0405—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0478—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing involving a particular surface treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C21D9/48—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals deep-drawing sheets
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/42—Ferrous alloys, e.g. steel alloys containing chromium with nickel with copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/44—Ferrous alloys, e.g. steel alloys containing chromium with nickel with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/48—Ferrous alloys, e.g. steel alloys containing chromium with nickel with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/68—Temporary coatings or embedding materials applied before or during heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12736—Al-base component
    • Y10T428/1275—Next to Group VIII or IB metal-base component
    • Y10T428/12757—Fe
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12861—Group VIII or IB metal-base component
    • Y10T428/12951—Fe-base component
    • Y10T428/12972—Containing 0.01-1.7% carbon [i.e., steel]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
ZA200905998A 2007-03-14 2009-08-27 Steel for tool-less hot forming or quenching with improved ductility ZA200905998B (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/FR2007/000441 WO2008110670A1 (fr) 2007-03-14 2007-03-14 Acier pour formage a chaud ou trempe sous outil a ductilite amelioree

Publications (1)

Publication Number Publication Date
ZA200905998B true ZA200905998B (en) 2010-04-28

Family

ID=38799374

Family Applications (1)

Application Number Title Priority Date Filing Date
ZA200905998A ZA200905998B (en) 2007-03-14 2009-08-27 Steel for tool-less hot forming or quenching with improved ductility

Country Status (17)

Country Link
US (2) US8722203B2 (uk)
EP (1) EP2137327B1 (uk)
JP (1) JP5726419B2 (uk)
KR (5) KR20150048913A (uk)
CN (1) CN101631880B (uk)
AR (1) AR065764A1 (uk)
AT (1) ATE556152T1 (uk)
BR (1) BRPI0809006B1 (uk)
CA (1) CA2680623C (uk)
ES (1) ES2387229T3 (uk)
MA (1) MA31235B1 (uk)
MX (1) MX2009009769A (uk)
PL (1) PL2137327T3 (uk)
RU (1) RU2423532C1 (uk)
UA (1) UA99127C2 (uk)
WO (2) WO2008110670A1 (uk)
ZA (1) ZA200905998B (uk)

Families Citing this family (54)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1767659A1 (fr) * 2005-09-21 2007-03-28 ARCELOR France Procédé de fabrication d'une pièce en acier de microstructure multi-phasée
DE102010004081C5 (de) * 2010-01-06 2016-11-03 Benteler Automobiltechnik Gmbh Verfahren zum Warmformen und Härten einer Platine
CN102251177A (zh) * 2011-07-12 2011-11-23 内蒙古包钢钢联股份有限公司 一种含稀土高强度钢板及其轧制方法
CN102230129A (zh) * 2011-07-12 2011-11-02 内蒙古包钢钢联股份有限公司 一种含稀土高强度钢板及其热处理工艺
WO2013014481A1 (fr) 2011-07-26 2013-01-31 Arcelormittal Investigación Y Desarrollo Sl Pièce d'acier soudée préalablement mise en forme à chaud à très haute résistance mécanique et procédé de fabrication
KR101575832B1 (ko) * 2011-08-09 2015-12-08 신닛테츠스미킨 카부시키카이샤 저온에서의 충격 에너지 흡수 특성과 haz 내연화 특성이 우수한 고항복비 열연 강판 및 그 제조 방법
UA109963C2 (uk) * 2011-09-06 2015-10-26 Катана сталь, яка затвердіває внаслідок виділення часток після гарячого формування і/або загартовування в інструменті, яка має високу міцність і пластичність, та спосіб її виробництва
CN102367554A (zh) * 2011-10-28 2012-03-07 内蒙古包钢钢联股份有限公司 一种工程机械用高性能调质钢板及其生产工艺
MX2014008430A (es) 2012-01-13 2014-10-06 Nippon Steel & Sumitomo Metal Corp Articulo moldeado estampado en caliente y metodo para la produccion de articulo moldeado estampado en caliente.
MX2014008428A (es) * 2012-01-13 2014-10-06 Nippon Steel & Sumitomo Metal Corp Lamina de acero laminada en frio y metodo para producir lamina de acero laminada en frio.
KR101636639B1 (ko) * 2012-03-28 2016-07-05 신닛테츠스미킨 카부시키카이샤 핫 스탬프용 테일러드 블랭크 및 핫 스탬프 부재 및 그들의 제조 방법
DE102012006941B4 (de) * 2012-03-30 2013-10-17 Salzgitter Flachstahl Gmbh Verfahren zur Herstellung eines Bauteils aus Stahl durch Warmumformen
EP2664682A1 (de) 2012-05-16 2013-11-20 ThyssenKrupp Steel Europe AG Stahl für die Herstellung eines Stahlbauteils, daraus bestehendes Stahlflachprodukt, daraus hergestelltes Bauteil und Verfahren zu dessen Herstellung
CN102747295B (zh) * 2012-07-27 2014-06-18 武汉钢铁(集团)公司 一种利用控轧控冷方法生产的贝氏体薄钢板及其制备方法
KR101448473B1 (ko) 2012-12-03 2014-10-10 현대하이스코 주식회사 테일러 웰디드 블랭크, 그 제조방법 및 이를 이용한 핫스탬핑 부품
CN103114292B (zh) * 2013-02-18 2015-01-07 梅河口市弘业无缝钢管有限公司 激光熔敷多元共渗复合处理的油井管、生产工艺及装置
PL2982772T3 (pl) 2013-04-02 2019-03-29 Nippon Steel & Sumitomo Metal Corporation Wyrób formowany przez wytłaczanie na gorąco, blacha stalowa cienka walcowana na zimno i sposób wytwarzania wyrobu formowanego przez wytłaczanie na gorąco
CZ2013281A3 (cs) * 2013-04-22 2015-05-27 Západočeská Univerzita V Plzni Způsob výroby ocelových dílů
DE202013011800U1 (de) 2013-07-24 2014-10-27 GM Global Technology Operations LLC (n. d. Gesetzen des Staates Delaware) Linienverstärktes Kraftfahrzeugblech, insbesondere Karosserieblech
US20170029914A1 (en) * 2013-11-29 2017-02-02 Nippon Steel & Sumitomo Metal Corporation Hot formed steel sheet component and method for producing the same as well as steel sheet for hot forming
CA2933435C (en) 2013-12-20 2020-03-24 Nippon Steel & Sumitomo Metal Corporation Hot-pressed steel sheet member, method of manufacturing the same, and steel sheet for hot pressing
JP6229736B2 (ja) 2014-01-06 2017-11-15 新日鐵住金株式会社 熱間成形部材およびその製造方法
DE102014010661A1 (de) * 2014-07-18 2016-01-21 GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) Blech und Verfahren zu dessen Behandlung
WO2016016676A1 (fr) 2014-07-30 2016-02-04 ArcelorMittal Investigación y Desarrollo, S.L. Procédé de fabrication de tôles d'acier, pour durcissement sous presse, et pièces obtenues par ce procédé
KR20160078807A (ko) 2014-12-24 2016-07-05 주식회사 포스코 연신율 및 충격 인성이 우수한 열간 프레스 부재 및 그 제조방법
WO2016132165A1 (fr) * 2015-02-19 2016-08-25 Arcelormittal Procede de fabrication d'une piece phosphatable a partir d'une tole revetue d'un revetement a base d'aluminium et d'un revetement de zinc
JP6515356B2 (ja) * 2015-03-31 2019-05-22 日本製鉄株式会社 ホットスタンプ用鋼板およびその製造方法、並びにホットスタンプ成形体
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
WO2017017483A1 (en) 2015-07-30 2017-02-02 Arcelormittal Steel sheet coated with a metallic coating based on aluminum
WO2017017485A1 (en) 2015-07-30 2017-02-02 Arcelormittal A method for the manufacture of a phosphatable part starting from a steel sheet coated with a metallic coating based on aluminium
WO2017017484A1 (en) * 2015-07-30 2017-02-02 Arcelormittal Method for the manufacture of a hardened part which does not have lme issues
DE102015014490A1 (de) 2015-11-10 2017-05-11 GM Global Technology Operations LLC (n. d. Ges. d. Staates Delaware) Verfahren zur Verarbeitung eines Blechwerkstücks
WO2017187215A1 (en) * 2016-04-29 2017-11-02 Arcelormittal Carbon steel sheet coated with a barrier coating
KR101726139B1 (ko) 2016-09-21 2017-04-12 주식회사 포스코 연신율 및 충격 인성이 우수한 열간 프레스 부재 및 그 제조방법
JP6424195B2 (ja) * 2016-11-14 2018-11-14 株式会社豊田中央研究所 熱間プレス成形方法
WO2018096387A1 (en) * 2016-11-24 2018-05-31 Arcelormittal Hot-rolled and coated steel sheet for hot-stamping, hot-stamped coated steel part and methods for manufacturing the same
CN107190203B (zh) * 2017-05-31 2019-07-23 武汉钢铁有限公司 用薄板坯直接轧制的屈服强度≥800MPa热轧薄板及生产方法
WO2018220430A1 (en) 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
CA3077793A1 (en) 2017-10-02 2019-04-11 Nippon Steel Corporation Hot stamped product, steel sheet for hot stamp, and manufacturing method thereof
US20190126401A1 (en) * 2017-11-02 2019-05-02 Ak Steel Properties, Inc. Press hardened steel with tailored properties after novel thermal treatment
WO2019102255A1 (en) 2017-11-24 2019-05-31 Arcelormittal Method of producing a welded steel blank with the provision of a filler wire having a defined carbon content, associated welded blank, method of producing a welded part with hot press-formed and cooled steel part and associated part
DE102017131247A1 (de) 2017-12-22 2019-06-27 Voestalpine Stahl Gmbh Verfahren zum Erzeugen metallischer Bauteile mit angepassten Bauteileigenschaften
DE102017131253A1 (de) 2017-12-22 2019-06-27 Voestalpine Stahl Gmbh Verfahren zum Erzeugen metallischer Bauteile mit angepassten Bauteileigenschaften
WO2019166852A1 (en) 2018-02-27 2019-09-06 Arcelormittal Method for producing a press-hardened laser welded steel part and press-hardened laser welded steel part
DE102018133143A1 (de) * 2018-11-06 2020-05-07 Salzgitter Flachstahl Gmbh Innenhochdruck umgeformtes Bauteil aus Stahl und Verwendung eines Stahls für Vorprodukte zur Herstellung eines innenhochdruckumgeformten Bauteiles sowie Vorprodukt hierfür
CN109821951B (zh) * 2018-12-06 2020-07-21 苏州普热斯勒先进成型技术有限公司 一种耐腐蚀热冲压零件的制备方法及装置
KR102603637B1 (ko) 2019-04-01 2023-11-21 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형품 및 핫 스탬프용 강판, 그리고 그것들의 제조 방법
KR102633542B1 (ko) 2019-04-01 2024-02-06 닛폰세이테츠 가부시키가이샤 핫 스탬프 성형품 및 그 제조 방법
KR102213974B1 (ko) * 2019-04-30 2021-02-08 현대제철 주식회사 핫 스탬핑 부품 및 그 제조방법
JP7235621B2 (ja) 2019-08-27 2023-03-08 株式会社神戸製鋼所 低強度ホットスタンプ用鋼板、ホットスタンプ部品およびホットスタンプ部品の製造方法
CN113924373B (zh) * 2019-12-20 2023-09-01 现代制铁株式会社 热冲压部件及其制造方法
US20220403492A1 (en) 2020-01-16 2022-12-22 Nippon Steel Corporation Hot stamped body
CN112301276B (zh) * 2020-10-12 2021-10-22 马鞍山钢铁股份有限公司 一种高强、高耐候冷轧双相耐候钢的制作方法
CN112962021B (zh) * 2021-01-25 2022-06-10 唐山钢铁集团有限责任公司 激光拼焊后用于整体热冲压成形的强塑钢板及生产方法

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2787735B1 (fr) * 1998-12-24 2001-02-02 Lorraine Laminage Procede de realisation d'une piece a partir d'une bande de tole d'acier laminee et notamment laminee a chaud
JP3698046B2 (ja) * 1999-10-22 2005-09-21 Ｊｆｅスチール株式会社 加工性およびめっき性に優れた高強度溶融亜鉛めっき鋼板ならびにその製造方法
AU773014B2 (en) * 1999-10-22 2004-05-13 Jfe Steel Corporation Hot-dip galvanized steel sheet having high strength and also being excellent in formability and galvanizing property
DE60127879T2 (de) * 2000-02-29 2007-09-06 Jfe Steel Corp. Hochfestes warmgewalztes Stahlblech mit ausgezeichneten Reckalterungseigenschaften
FR2807447B1 (fr) 2000-04-07 2002-10-11 Usinor Procede de realisation d'une piece a tres hautes caracteristiques mecaniques, mise en forme par emboutissage, a partir d'une bande de tole d'acier laminee et notamment laminee a chaud et revetue
CN1147609C (zh) 2000-04-07 2004-04-28 川崎制铁株式会社 具有优良应变时效硬化特性的钢板及其制造方法
JP4333940B2 (ja) * 2001-08-31 2009-09-16 新日本製鐵株式会社 アルミ系めっき鋼板を用いた高強度自動車部材の熱間プレス方法
DE60236447D1 (de) * 2001-10-23 2010-07-01 Sumitomo Metal Ind Verfahren zur heisspressbearbeitung von einem plattierten stahlprodukt
KR100467487B1 (ko) * 2001-10-26 2005-01-24 현대자동차주식회사 자동차용 강판의 강성강화 방법 및 그 성형품
FR2833504A1 (fr) * 2001-12-14 2003-06-20 Usinor Procede de mise en forme a chaud et notamment l'obtention de tout ou partie d'une roue de vehicule automobile
JP4400079B2 (ja) * 2002-03-29 2010-01-20 Ｊｆｅスチール株式会社 超微細粒組織を有する冷延鋼板の製造方法
JP4168750B2 (ja) 2002-12-27 2008-10-22 Ｊｆｅスチール株式会社 超微細粒組織を有し疲労特性に優れる溶融亜鉛めっき冷延鋼板の製造方法
JP4506434B2 (ja) * 2004-11-29 2010-07-21 Ｊｆｅスチール株式会社 剛性に優れた高強度鋼板およびその製造方法
FR2883007B1 (fr) * 2005-03-11 2007-04-20 Usinor Sa Procede de fabrication d'une piece d'acier revetu presentant une tres haute resistance apres traitement thermique
KR100676935B1 (ko) * 2005-06-25 2007-02-02 신닛뽄세이테쯔 카부시키카이샤 가공성이 우수한 고강도 합금화 용융 아연 도금 강판 및 그제조 방법
CN102242308B (zh) * 2005-08-03 2013-03-27 住友金属工业株式会社 热轧钢板及冷轧钢板及它们的制造方法

Also Published As

Publication number Publication date
US9611517B2 (en) 2017-04-04
CN101631880B (zh) 2012-07-04
CN101631880A (zh) 2010-01-20
US20100221572A1 (en) 2010-09-02
US20140216612A1 (en) 2014-08-07
KR102008641B1 (ko) 2019-08-07
BRPI0809006A2 (pt) 2014-09-16
WO2008132303A1 (fr) 2008-11-06
KR20150048913A (ko) 2015-05-07
JP5726419B2 (ja) 2015-06-03
KR20090128414A (ko) 2009-12-15
EP2137327B1 (fr) 2012-05-02
WO2008110670A1 (fr) 2008-09-18
UA99127C2 (uk) 2012-07-25
KR20190091571A (ko) 2019-08-06
RU2423532C1 (ru) 2011-07-10
KR101952525B1 (ko) 2019-02-26
RU2009137930A (ru) 2011-04-20
ATE556152T1 (de) 2012-05-15
PL2137327T3 (pl) 2012-10-31
KR20180122489A (ko) 2018-11-12
CA2680623C (fr) 2013-02-05
MA31235B1 (fr) 2010-03-01
US8722203B2 (en) 2014-05-13
BRPI0809006B1 (pt) 2017-11-21
EP2137327A1 (fr) 2009-12-30
KR20170038119A (ko) 2017-04-05
JP2010521584A (ja) 2010-06-24
CA2680623A1 (fr) 2008-11-06
AR065764A1 (es) 2009-07-01
ES2387229T3 (es) 2012-09-18
MX2009009769A (es) 2009-10-07

Similar Documents

Publication Publication Date Title
ZA200905998B (en) Steel for tool-less hot forming or quenching with improved ductility
EP2128295A4 (en) HOT GALVANIZED STEEL SHEET, HIGH RESISTANCE, HAVING EXCELLENT MOLDING CAPABILITY, AND PROCESS FOR PRODUCING THE SAME
EP2177640A4 (en) ULTRA-HIGH STEEL PLATE
EP2233597A4 (en) HOT DIP GALVANIZED STEEL PLATE WITH HIGH STRENGTH HAVING EXCELLENT MOLDING CAPABILITY AND METHOD FOR PRODUCTION THEREOF
EP2003223A4 (en) HEAT-TREATED STEEL FOR A HIGH-STRENGTH SPRING
EP2216422A4 (en) COLD LAMINATED STEEL SHEET OF HIGH STRENGTH
EP2105514A4 (en) HIGH STRENGTH STEEL PLATE
EP2251448A4 (en) COLD-ROLLED STEEL PLATE
EP2003222A4 (en) HEAT-TREATED STEEL FOR A HIGH-STRENGTH SPRING
GB0723970D0 (en) Hot cold straightening iron
EP2138600A4 (en) HOT GALVANIZED STEEL SHEET HIGH RESISTANCE
GB0812614D0 (en) Metal forming
EP2186925A4 (en) GALVANIZED STEEL
EP2418303A4 (en) ZINC-COATED STEEL PLATE
EP1988182A4 (en) FERRITIC HEAT-RESISTANT STEEL
EP2520684A4 (en) AUSTENITIC STEEL MATERIAL WITH SUPERIOR DUCTILITY
ZA201001584B (en) Quenching vessel
PL2762593T3 (pl) Stal kuta
EP2405026A4 (en) COLD-ROLLED STEEL PLATE WITH EXCEPTIONAL BENDING TOLERANCE, METHOD FOR THE PRODUCTION THEREOF AND THEREOF APPLICABLE TO THE ELEMENT
EP2157202A4 (en) HEAT-RESISTANT FERRITE STEEL
ZA201006646B (en) Steel with high properties for solid parts
EP2204464A4 (en) EQUIPMENT FOR MANUFACTURING HOT GALVANIZED STEEL SHEET
ZA201204354B (en) Steel with high temper resistance
EP2312017A4 (en) STAINLESS STEEL PLATE AND METHOD FOR PRODUCING THE SAME
TWI365916B (en) Cold-working steel