WO2024092998A1 - Processus de construction par compactage vibrant à l'eau saturée pour des pierres concassées calibrées - Google Patents

Processus de construction par compactage vibrant à l'eau saturée pour des pierres concassées calibrées Download PDF

Info

Publication number
WO2024092998A1
WO2024092998A1 PCT/CN2022/142583 CN2022142583W WO2024092998A1 WO 2024092998 A1 WO2024092998 A1 WO 2024092998A1 CN 2022142583 W CN2022142583 W CN 2022142583W WO 2024092998 A1 WO2024092998 A1 WO 2024092998A1
Authority
WO
WIPO (PCT)
Prior art keywords
crushed stone
graded
paving
raw materials
compaction
Prior art date
Application number
PCT/CN2022/142583
Other languages
English (en)
Chinese (zh)
Inventor
白银战
Original Assignee
中国港湾工程有限责任公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 中国港湾工程有限责任公司 filed Critical 中国港湾工程有限责任公司
Publication of WO2024092998A1 publication Critical patent/WO2024092998A1/fr

Abstract

La présente invention concerne un processus de construction par compactage vibrant à l'eau saturée pour des pierres concassées calibrées, consistant à : réaliser la vérification ainsi que l'acceptation et la finition sur une couche de base ; effectuer la conception et les essais de proportion de mélange sur des pierres concassées calibrées afin de déterminer une proportion de mélange, le coefficient de pose en vrac et une méthode de pose ; effectuer le relevé et la mise en place sur la couche de base qui a été qualifiée lors de la vérification et de l'acceptation ; préparer des matières premières de pierres concassées selon la proportion de mélange déterminée par les essais, ajouter les matières premières de pierres concassées dans une machine de mélange et les mélanger afin d'obtenir un mélange ; et poser le mélange sur la surface de la couche de base selon le coefficient de pose en vrac et la méthode de pose qui sont déterminés par les essais, et le compacter, une méthode de compactage consistant à effectuer d'abord un compactage statique, à réparer et à niveler, puis à effectuer un roulage par vibration, à arroser complètement le mélange roulé d'eau jusqu'à saturation et à le rouler à plusieurs reprises jusqu'à ce que l'eau s'écoule des interstices et que ladite couche de pierres concassées calibrées satisfasse les exigences du degré de compactage. Par conséquent, le processus peut permettre d'appliquer des pierres concassées calibrées aux couches de roulement des routes d'aéroport, le degré de compactage atteignant 100 %, et les couches de roulement des routes d'aéroport ayant des surfaces planes et compactes et étant exemptes d'ameublissement et de ségrégation.
PCT/CN2022/142583 2022-11-01 2022-12-28 Processus de construction par compactage vibrant à l'eau saturée pour des pierres concassées calibrées WO2024092998A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN202211354290.0A CN115787386A (zh) 2022-11-01 2022-11-01 级配碎石饱和水密振实施工工艺
CN202211354290.0 2022-11-01

Publications (1)

Publication Number Publication Date
WO2024092998A1 true WO2024092998A1 (fr) 2024-05-10

Family

ID=85434762

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2022/142583 WO2024092998A1 (fr) 2022-11-01 2022-12-28 Processus de construction par compactage vibrant à l'eau saturée pour des pierres concassées calibrées

Country Status (2)

Country Link
CN (1) CN115787386A (fr)
WO (1) WO2024092998A1 (fr)

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102477710A (zh) * 2010-11-22 2012-05-30 中国十七冶集团有限公司 一种天然级配卵石路面底基层的施工方法
CN103161109A (zh) * 2011-12-13 2013-06-19 中国二十冶集团有限公司 采用海砂对泥炭土地基进行路基填筑的方法
CN105714653A (zh) * 2016-02-02 2016-06-29 上海建工集团股份有限公司 级配碎石基层施工组合碾压工艺
CN107604785A (zh) * 2017-07-19 2018-01-19 甘肃路桥建设集团养护科技有限责任公司 振动拌和宽幅全厚半刚性基层施工工艺
CN113718604A (zh) * 2021-07-15 2021-11-30 兰州交通大学 一种沙漠腹地高速公路风积沙填料填筑方法
CN114381981A (zh) * 2022-01-28 2022-04-22 中电建路桥集团有限公司 导行路双层联铺试验段施工方法
US20220205188A1 (en) * 2020-12-30 2022-06-30 Shandong Provincial Communications Planning And Design Institute Group Co., Ltd Full-depth ultra-thin long-life pavement structure and construction method thereof

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6781669B2 (ja) * 2017-06-14 2020-11-04 鹿島建設株式会社 締固め方法、及び、締固め管理システム
CN108004864A (zh) * 2017-12-01 2018-05-08 江苏中路工程技术研究院有限公司 运用改良湿陷性黄土作为路基填料的施工方法
CN112982058A (zh) * 2019-12-14 2021-06-18 浙江建腾建设有限公司 一种水泥稳定碎石振动拌和施工工法
CN111893827A (zh) * 2020-08-05 2020-11-06 中交上海航道局有限公司 一种城市主干道路的施工工艺

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102477710A (zh) * 2010-11-22 2012-05-30 中国十七冶集团有限公司 一种天然级配卵石路面底基层的施工方法
CN103161109A (zh) * 2011-12-13 2013-06-19 中国二十冶集团有限公司 采用海砂对泥炭土地基进行路基填筑的方法
CN105714653A (zh) * 2016-02-02 2016-06-29 上海建工集团股份有限公司 级配碎石基层施工组合碾压工艺
CN107604785A (zh) * 2017-07-19 2018-01-19 甘肃路桥建设集团养护科技有限责任公司 振动拌和宽幅全厚半刚性基层施工工艺
US20220205188A1 (en) * 2020-12-30 2022-06-30 Shandong Provincial Communications Planning And Design Institute Group Co., Ltd Full-depth ultra-thin long-life pavement structure and construction method thereof
CN113718604A (zh) * 2021-07-15 2021-11-30 兰州交通大学 一种沙漠腹地高速公路风积沙填料填筑方法
CN114381981A (zh) * 2022-01-28 2022-04-22 中电建路桥集团有限公司 导行路双层联铺试验段施工方法

Also Published As

Publication number Publication date
CN115787386A (zh) 2023-03-14

Similar Documents

Publication Publication Date Title
CN107338686A (zh) 一种高速铁路路基填料施工方法
CN108978389A (zh) 一种沥青路面的施工方法
CN111021174A (zh) 一种城市道路的施工方法
CN114381981A (zh) 导行路双层联铺试验段施工方法
CN106522073A (zh) 一种高掺量水稳铣刨旧料基层施工方法
CN114232649B (zh) 无砟轨道路基土方填筑的施工方法
CN211472012U (zh) 一种信号灯路口灌入式复合路面
CN113929378A (zh) 一种油页岩半焦及其改性材料的应用
CN111827033A (zh) 一种高速公路互通匝道路基加宽填筑固化土施工方法
CN112982058A (zh) 一种水泥稳定碎石振动拌和施工工法
WO2024092998A1 (fr) Processus de construction par compactage vibrant à l'eau saturée pour des pierres concassées calibrées
CN111719371A (zh) 一种道路基层组分以及道路铺设方法
CN113152200A (zh) 垦区公路水稳砂砾基层裂缝防治方法
Pittman Construction of roller-compacted concrete pavements
Sharp Concrete in Highway Engineering: International Series of Monographs in Civil Engineering
CN111979865A (zh) 一种复合式沥青路面施工方法
CN113529575A (zh) 高等级公路桥涵台背回填建筑废弃物施工工艺
Mallick et al. Construction of Asphalt Pavements
CN111576125B (zh) 一种横向自动给料基层施工方法
Li et al. Control Points of the Compaction Technology for Subgrades and Pavements in Municipal Road Engineering
CN113584981A (zh) 一种装配式水泥混凝土路面板及施工方法
CN113174793A (zh) 一种通过改良填筑材料固化土加宽路基的施工方法
Wu et al. Louisiana Transportation Research Center
CN112176815A (zh) 公路水稳结构分段阶梯式连铺施工工艺
CN116356797A (zh) 一种弃土资源化利用改良土的填筑施工方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22964292

Country of ref document: EP

Kind code of ref document: A1