WO2024029668A1 - Ruban adhésif comprenant une composition pour former une couche adhésive soluble dans l'eau - Google Patents
Ruban adhésif comprenant une composition pour former une couche adhésive soluble dans l'eau Download PDFInfo
- Publication number
- WO2024029668A1 WO2024029668A1 PCT/KR2022/021050 KR2022021050W WO2024029668A1 WO 2024029668 A1 WO2024029668 A1 WO 2024029668A1 KR 2022021050 W KR2022021050 W KR 2022021050W WO 2024029668 A1 WO2024029668 A1 WO 2024029668A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- water
- parts
- adhesive layer
- soluble
- Prior art date
Abstract
La présente invention concerne une composition comprenant une résine polymère acrylique pour former une couche adhésive soluble dans l'eau. La composition pour former une couche adhésive soluble dans l'eau selon l'invention, qui est un agent adhésif soluble dans l'eau à partir duquel ni le formaldéhyde ni les composés organiques volatils nocifs pour le corps humain ne sont détectés et auxquels des matériaux naturels inoffensifs sont appliqués, a une faible toxicité et est respectueuse de l'environnement car elle se dissout dans l'eau sans laisser de résidu. De plus, la composition présente une excellente adhérence et un temps de rétention d'adhésif durable.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR10-2022-0098195 | 2022-08-05 | ||
KR1020220098195A KR102459161B1 (ko) | 2022-08-05 | 2022-08-05 | 수용성 점착층 형성용 조성물을 포함하는 점착 테이프 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2024029668A1 true WO2024029668A1 (fr) | 2024-02-08 |
Family
ID=83810467
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2022/021050 WO2024029668A1 (fr) | 2022-08-05 | 2022-12-22 | Ruban adhésif comprenant une composition pour former une couche adhésive soluble dans l'eau |
Country Status (2)
Country | Link |
---|---|
KR (5) | KR102459161B1 (fr) |
WO (1) | WO2024029668A1 (fr) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR102459161B1 (ko) * | 2022-08-05 | 2022-10-27 | (주)재성글로벌 | 수용성 점착층 형성용 조성물을 포함하는 점착 테이프 |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2009227759A (ja) * | 2008-03-21 | 2009-10-08 | Nbl Kk | 接着剤組成物 |
JP2012236996A (ja) * | 2011-05-12 | 2012-12-06 | Yun Yeol Kim | 生花飾り用水溶性点接着剤及び生花飾り用水溶性点接着剤を用いた生花飾り方法 |
KR20130089605A (ko) * | 2012-02-02 | 2013-08-12 | 가부시키가이샤 지로 코포레토 프란 | 편광자 보호 필름, 편광판 및 액정 표시 소자 |
KR102247297B1 (ko) * | 2019-10-30 | 2021-05-03 | (주)화인테크놀리지 | 수해리성 점착 테이프 |
KR102459161B1 (ko) * | 2022-08-05 | 2022-10-27 | (주)재성글로벌 | 수용성 점착층 형성용 조성물을 포함하는 점착 테이프 |
Family Cites Families (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
KR101370389B1 (ko) | 2013-03-29 | 2014-03-06 | 주식회사 연우 | 수성 접착 조성물 및 이의 제조방법 |
-
2022
- 2022-08-05 KR KR1020220098195A patent/KR102459161B1/ko active IP Right Grant
- 2022-10-14 KR KR1020220132654A patent/KR102469271B1/ko active IP Right Grant
- 2022-10-14 KR KR1020220132675A patent/KR102473226B1/ko active IP Right Grant
- 2022-10-14 KR KR1020220132661A patent/KR102473215B1/ko active IP Right Grant
- 2022-10-14 KR KR1020220132644A patent/KR102469265B1/ko active IP Right Grant
- 2022-12-22 WO PCT/KR2022/021050 patent/WO2024029668A1/fr unknown
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2009227759A (ja) * | 2008-03-21 | 2009-10-08 | Nbl Kk | 接着剤組成物 |
JP2012236996A (ja) * | 2011-05-12 | 2012-12-06 | Yun Yeol Kim | 生花飾り用水溶性点接着剤及び生花飾り用水溶性点接着剤を用いた生花飾り方法 |
KR20130089605A (ko) * | 2012-02-02 | 2013-08-12 | 가부시키가이샤 지로 코포레토 프란 | 편광자 보호 필름, 편광판 및 액정 표시 소자 |
KR102247297B1 (ko) * | 2019-10-30 | 2021-05-03 | (주)화인테크놀리지 | 수해리성 점착 테이프 |
KR102459161B1 (ko) * | 2022-08-05 | 2022-10-27 | (주)재성글로벌 | 수용성 점착층 형성용 조성물을 포함하는 점착 테이프 |
Also Published As
Publication number | Publication date |
---|---|
KR102459161B1 (ko) | 2022-10-27 |
KR102469271B1 (ko) | 2022-11-23 |
KR102469265B1 (ko) | 2022-11-23 |
KR102473215B1 (ko) | 2022-12-02 |
KR102473226B1 (ko) | 2022-12-02 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2024029668A1 (fr) | Ruban adhésif comprenant une composition pour former une couche adhésive soluble dans l'eau | |
WO2014073840A1 (fr) | Composition adhésive d'émulsion hybride à base d'acryl-silicium, et son procédé de préparation | |
WO2012070807A2 (fr) | Composition adhésive pour écran tactile, film adhésif, et écran tactile | |
WO2016024729A1 (fr) | Adhésif en émulsion acrylique présentant une excellente force d'adhérence à basse température et une excellente force de rétention, et son procédé de fabrication | |
CA2106462A1 (fr) | Rubans auto-adhesifs a encollage acrylate/silicone reticulable par rayonnement, adherant a des supports peintures | |
WO2013069907A1 (fr) | Composition adhésive pour film de protection antistatique, et son procédé de production | |
EP2231807A2 (fr) | Composition d'adhésif sensible à la pression, film protecteur, polariseur et dispositif d'affichage à cristaux liquides la comprenant | |
CN104099046B (zh) | 用于改进胶粘带在亲水表面上、尤其是在玻璃表面上的粘合性的硅烷底胶 | |
CN110878190B (zh) | 一种泡棉双面胶带及其制造方法 | |
WO2015041403A1 (fr) | Adhésif acrylique en émulsion et son procédé de fabrication | |
WO2020040426A1 (fr) | Ruban double face résistant au choc pour dispositif d'affichage | |
WO2009134043A2 (fr) | Feuille adhésive, procédé de fabrication de celle-ci, filtre optique et panneau afficheur plasma | |
KR20020050733A (ko) | 내충격성이 우수한 양면 점착 시트 | |
TWI786159B (zh) | 雙面黏著片材 | |
KR20160090802A (ko) | 표면 보호용 점착 시트 및 표면 보호용 점착 시트의 사용 방법 | |
KR102462480B1 (ko) | 피착제 종류와 상관없이 점착할 수 있는 아크릴계 점착 테이프 및 이의 제조방법 | |
CN112852325B (zh) | 一种pet复合聚酯保护膜及其制备方法 | |
WO2009104936A2 (fr) | Composition de résine hybride de polyuréthane/copolymère acrylique hydrodispersible redispersible et procédé de préparation | |
KR102099539B1 (ko) | 응집력이 우수한 점착 테이프 | |
JP2001323227A (ja) | 耐衝撃性に優れる遮光性粘着テープ | |
CN109153239A (zh) | 脱模膜 | |
WO2013180374A1 (fr) | Appareil électroluminescent organique et film adhésif pour une charge d'appareil électroluminescent organique | |
CN116875215B (zh) | 低voc释放的硅树脂-丙烯酸杂化双面胶带的制备方法 | |
WO2013162230A1 (fr) | Composition de substrat pour ruban mousse à dispersion de bulles, ruban mousse l'utilisant, et son procédé de préparation | |
WO2013051876A2 (fr) | Composition adhésive aqueuse variant peu avec le temps |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22954123 Country of ref document: EP Kind code of ref document: A1 |