WO2023276543A1 - 錯体化合物および該錯体化合物の製造方法 - Google Patents
錯体化合物および該錯体化合物の製造方法 Download PDFInfo
- Publication number
- WO2023276543A1 WO2023276543A1 PCT/JP2022/022418 JP2022022418W WO2023276543A1 WO 2023276543 A1 WO2023276543 A1 WO 2023276543A1 JP 2022022418 W JP2022022418 W JP 2022022418W WO 2023276543 A1 WO2023276543 A1 WO 2023276543A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mass
- parts
- complex compound
- compound
- meth
- Prior art date
Abstract
本発明が解決しようとする課題は、非石化原料である黒色の着色材料として、赤外領域に透過性があり、可視領域の吸収性が高い化合物を利用することで、トナー、インキ、印刷物、塗料、塗装、プラスチック、繊維、フィルム、ブラックマトリックス用レジスト、フォトスペーサー用レジスト、及び、その硬化物を提供することにある。 ベンゼン骨格の3つの隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体と三価の鉄金属から構成される錯体化合物が、従来の黒色色材であるカーボンブラックと比較すると近赤外領域の吸収が少なく、漆黒性が高い黒色系の色材であることを見出し、上記の課題を解決できたものである。
Description
本発明は錯体化合物および該錯体化合物の製造方法に関する。
近年、海洋廃棄プラスチックが生態系への影響などの観点から問題視されており、プラスチックのリサイクルに関連した研究が盛んに行われている。通常のプラスチックのリサイクル工程では赤外線を照射し、得られる赤外スペクトルからプラスチックの種類を判定し自動選別している。また、黒色プラスチックはデザインへの汎用性が高いため、家庭用品や食品容器・トレーなど幅広い製品群に使用されており、世界のプラスチック生産量の約半分を占めるといわれ、大きなボリュームを有する。しかしながら、現行黒色プラスチックのほとんどに用いられているカーボンブラックが紫外~可視域~赤外まで幅広く顕著に吸収をもつため、プラスチックの種類を判定できず、そのほとんどが埋立やサーマルリサイクル(焼却)されている。そのため、近赤外領域、特に1200―2500nmの領域において、吸収の少ない黒色材が望まれている。
さらに、リサイクルされたプラスチックの着色残存も問題視されており、実際に少しでも色材残存を抑えた低着色の再生プラスチックに向けた改善要望が上がっている。これらの色残存問題は着色や物性低下によりリサイクル品の用途先を限定してしまい(ダウンサイクル)、再生品の価値低下を引き起こしている。つまり、上記の赤外吸収レスだけでは十分ではなく、リサイクル工程において消色や可溶化により脱墨可能な性能を兼備している黒色材が求められている。しかし現状、これらを兼備している黒色材はない(特許文献1)。
一方、持続可能な社会の実現に向け、脱石油や温室効果ガス低減を可能とする技術開発が全世界で活発化している。その中でもバイオ由来を中心とする非石化原料の活用は特に大きなトピックとして注目を浴びている。この流れは色材においても同様であり、非石化原料の活用が求められているが、現行のほとんどの黒色材には石化由来のカーボンブラックが使用されている(特許文献1)。
ヨーロッパでは中世から古典インクあるいは没食子インクと呼ばれる黒色インクが使用されてきた。これはタンニン酸あるいは没食子酸,硫酸鉄(II),アラビアゴムなどを混合させたもので、鉄の空気酸化によって黒色に呈すると言われている。これまで同様の分散体は万年筆インクや染毛剤に用いられてきたが、タンニン酸の不純物によるインキ詰まりや黒色度不足、さらには遊離した硫酸による金属腐食などの問題から要求品質を満たしておらず、現代ではほとんど使用されていない(特許文献2,3)。
本発明が解決しようとする課題は、非石化原料であり、さらに脱墨可能である黒色の着色材料として、赤外領域に透過性があり、可視領域の吸収性が高い化合物を利用することで、トナー、インキ、印刷物、塗料、塗装、プラスチック、繊維、フィルム、ブラックマトリックス用レジスト、フォトスペーサー用レジスト、及び、その硬化物を提供することにある。
発明者らは課題を解決すべく鋭意研究した結果、ベンゼン骨格の隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体および三価の鉄金属から構成される金属錯体化合物が、従来の黒色色材であるカーボンブラックと比較すると近赤外領域の吸収が少なく、反射OD値が高く、漆黒性(黒色度)が高い黒色系の色材であることを見出し、課題を解決できたものである。
すなわち本発明は、
1.ベンゼン骨格の隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体と三価の鉄金属から構成される錯体化合物。
2.元素分析から算出されるモル比で、
前記ベンゼントリオール誘導体:三価の鉄金属=1.00:0.20~1.50
である1記載の錯体化合物。
(前記元素分析から算出されるモル比とは、元素分析により計測された炭素および鉄の質量パーセント濃度を、それぞれ構成元素のモル比に換算した後、さらに炭素の値は前記ベンゼントリオール誘導体分子を構成する炭素数で割ることで得られる比。)
3.水酸化鉄の含有率が1%以下である1~2のいずれか1記載の錯体化合物。
4.前記ベンゼントリオール誘導体が、少なくとも没食子酸またはピロガロールから選ばれる一つである1~3のいずれか1記載の錯体化合物。
5.前記錯体化合物が12.5質量%含まれるインキ塗膜において、可視光域400~800nmにおいて透過率が15%未満であり、近赤外領域1200~2500nmにおいて透過率が60%を超えることを特徴とする請求項1~4のいずれか1記載の錯体化合物。
6.1~5のいずれか1記載の錯体化合物を含有することを特徴とするトナー、インキ、印刷物、塗料、塗装、プラスチック、繊維、フィルム、ブラックマトリックス用レジスト、フォトスペーサー用レジスト、及び、その硬化物。
を提供するものである。
1.ベンゼン骨格の隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体と三価の鉄金属から構成される錯体化合物。
2.元素分析から算出されるモル比で、
前記ベンゼントリオール誘導体:三価の鉄金属=1.00:0.20~1.50
である1記載の錯体化合物。
(前記元素分析から算出されるモル比とは、元素分析により計測された炭素および鉄の質量パーセント濃度を、それぞれ構成元素のモル比に換算した後、さらに炭素の値は前記ベンゼントリオール誘導体分子を構成する炭素数で割ることで得られる比。)
3.水酸化鉄の含有率が1%以下である1~2のいずれか1記載の錯体化合物。
4.前記ベンゼントリオール誘導体が、少なくとも没食子酸またはピロガロールから選ばれる一つである1~3のいずれか1記載の錯体化合物。
5.前記錯体化合物が12.5質量%含まれるインキ塗膜において、可視光域400~800nmにおいて透過率が15%未満であり、近赤外領域1200~2500nmにおいて透過率が60%を超えることを特徴とする請求項1~4のいずれか1記載の錯体化合物。
6.1~5のいずれか1記載の錯体化合物を含有することを特徴とするトナー、インキ、印刷物、塗料、塗装、プラスチック、繊維、フィルム、ブラックマトリックス用レジスト、フォトスペーサー用レジスト、及び、その硬化物。
を提供するものである。
本発明の金属錯体化合物化合物は、従来の黒色色材であるカーボンブラックと比較すると近赤外領域の吸収が無く、反射OD値が高く、漆黒性(黒色度)が高い黒色系の色材であるため、トナー、インキ、印刷物、塗料、塗装、プラスチック、繊維、フィルム、ブラックマトリックス用レジスト、フォトスペーサー用レジスト、及び、その硬化物等の幅広い産業分野に使用することができるものである。
以下に示す本発明の実施形態は本発明の一部の実施形態を表すにすぎず、要旨を大幅に逸脱しない限りにおいて記載内容のみには限定されない。
[ベンゼン骨格の隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体]
本発明のベンゼン骨格の隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体としては、没食子酸、ピロガロール、5-メチルピロガロール、2,3,4-トリヒドロキシベンズアルデヒド、3,4,5-トリヒドロキシベンズアルデヒド、2’,3’,4’-トリヒドロキシベンゼンアセトフェノン、2,3,4-トリヒドロキシ安息香酸、没食子酸メチル、没食子酸エチル、没食子酸プロピル、没食子酸ブチル、没食子酸ドデシル、2,3,4-トリヒドロキシベンゾフェノン、2,3,4,4’-テトラヒドロキシベンゾフェノン等が挙げられ、没食子酸、ピロガロールが好ましい。
本発明のベンゼン骨格の隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体としては、没食子酸、ピロガロール、5-メチルピロガロール、2,3,4-トリヒドロキシベンズアルデヒド、3,4,5-トリヒドロキシベンズアルデヒド、2’,3’,4’-トリヒドロキシベンゼンアセトフェノン、2,3,4-トリヒドロキシ安息香酸、没食子酸メチル、没食子酸エチル、没食子酸プロピル、没食子酸ブチル、没食子酸ドデシル、2,3,4-トリヒドロキシベンゾフェノン、2,3,4,4’-テトラヒドロキシベンゾフェノン等が挙げられ、没食子酸、ピロガロールが好ましい。
[鉄金属イオン]
本発明の金属錯体に使用される金属としては三価の鉄金属イオンが好ましく、三価の鉄金属イオンの原料としては、塩化鉄(III)、硝酸鉄(III)あげられ、好ましくは、塩化鉄(III)である。
原料としては二価の鉄金属イオンも使用できる(空気酸化で三価に変化)。二価の鉄金属イオンの原料としては、硫酸鉄(II)、硫化鉄(II)があげられる。
本発明の金属錯体に使用される金属としては三価の鉄金属イオンが好ましく、三価の鉄金属イオンの原料としては、塩化鉄(III)、硝酸鉄(III)あげられ、好ましくは、塩化鉄(III)である。
原料としては二価の鉄金属イオンも使用できる(空気酸化で三価に変化)。二価の鉄金属イオンの原料としては、硫酸鉄(II)、硫化鉄(II)があげられる。
本発明の金属錯体は、元素分析から算出されるモル比で、ベンゼントリオール誘導体:三価の鉄金属=1.00:0.20~1.50が好ましく、黒色材の着色力という理由で1.00:0.20~1.20がより好ましく、合成の簡便性という理由で1.00:0.50~1.20がさらに好ましい。なお、元素分析はJIS M 8819に準拠する湿式酸分解/ICP-AES法によって測定した。
[金属錯体の製造方法]
本発明のベンゼン骨格の隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体と三価の鉄金属から構成される金属錯体化合物は、前記ベンゼントリオール誘導体を塩基存在下、溶媒中に溶解させた溶液に、鉄金属水溶液を滴下し、徐々に金属錯体を形成する。室温で撹拌後、高温下で撹拌させた。次に形成された金属錯体を水または有機溶媒で洗浄、乾燥し粉体の金属錯体を得た。
本発明のベンゼン骨格の隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体と三価の鉄金属から構成される金属錯体化合物は、前記ベンゼントリオール誘導体を塩基存在下、溶媒中に溶解させた溶液に、鉄金属水溶液を滴下し、徐々に金属錯体を形成する。室温で撹拌後、高温下で撹拌させた。次に形成された金属錯体を水または有機溶媒で洗浄、乾燥し粉体の金属錯体を得た。
下記に本発明の金属錯体の製造方法を詳述する。
前記ベンゼントリオール誘導体を溶解する工程で用いる塩基としては、水酸化ナトリウム、水酸化カリウム、炭酸ナトリウム、炭酸カリウム、水素化ナトリウム、t - ブトキシカリウム、酢酸ナトリム、酢酸カリウム等が使用できるが、好ましくは水酸化ナトリウムである。
塩基の使用量は、前記ベンゼントリオール誘導体の使用量の1.5倍等モル量程度が好ましい。
溶媒としては、水、アルコールが用いられる。好ましくは水である。
溶媒の使用量は、前記ベンゼントリオール誘導体に対して5~50倍重量、好ましくは10~30倍重量である。
溶解温度としては、20~50℃であり、好ましくは20~30℃ である。
鉄イオン水溶液は、前記ベンゼントリオール誘導体溶液に滴下等徐々に添加することが好ましく、金属錯体の錯体形成を均一にすることが特に重要である。
錯体が形成された溶液を熟成させるため、加熱処理を行い60~100℃で、1~10時間、撹拌を行う。
熟成後、吸引ろ過等で金属錯体のウェットケーキを得た後、得られた黒色材がそれぞれ各種溶媒に不溶な場合、水,温水、エタノール等で洗浄するのが好ましく、その後熱風乾燥機等で80~120℃で5~20時間、乾燥を行った。洗浄効果を上げるために50℃以上の温水が好ましい。
乾燥後、黒色の本発明の金属錯体を得た。また、乾燥させずにろ過した状態の含水又は含有機溶媒のウェットケーキの形態で所望のアプリケーション等に用いることもできる。
本発明の金属錯体が、水、有機溶媒に不溶である場合、必要に応じて粒子のサイズ、凝集状態をアプリケーションに適した形に制御する顔料化という操作を行うこともある。顔料化を行う場合は、公知慣用の方法をいずれも用いることができる。具体的には本発明の金属錯体を水溶性無機塩と水溶性有機溶剤と共に混錬磨砕する方法(ソルベントソルトミリング法)、本発明の金属錯体と前記金属錯体が不溶の溶剤中で加熱する方法(ソルベント法)、顔料磨砕機又は顔料分散機を用いて微細化する方法、等が挙げられる。
ソルベントソルトミリング法としては、例えば、本発明の金属錯体を、塩化ナトリウムや硫酸ナトリウムの様な水溶性無機塩と、ジエチレングリコール、トリエチレングリコールの様な水溶性有機溶媒と共に、加熱しながら混練摩砕し水洗する方法が挙げられる。
ソルベント法を行う場合の液媒体は、本発明の金属錯体を溶解しないものを選択して用いる。この液媒体としては、本発明の金属錯体の結晶制御をより安定的に行うために、水可溶性有機溶媒を必須成分として含む液媒体を用いるのが好ましい。
微細化する方法を行う場合は、例えば、ボールミル、ハンマーミル、サンドミル、アトライター、横型連続媒体分散機、ニーダー、連続式一軸混練機、連続式二軸混練機、三本ロール、及びオープンロール連続混練機等の顔料磨砕機や顔料分散機を用いることができる。また、前記顔料磨砕機や顔料分散機は、ソルベントソルトミリング法でも用いることができる。
ソルベントソルトミリング法としては、例えば、本発明の金属錯体を、塩化ナトリウムや硫酸ナトリウムの様な水溶性無機塩と、ジエチレングリコール、トリエチレングリコールの様な水溶性有機溶媒と共に、加熱しながら混練摩砕し水洗する方法が挙げられる。
ソルベント法を行う場合の液媒体は、本発明の金属錯体を溶解しないものを選択して用いる。この液媒体としては、本発明の金属錯体の結晶制御をより安定的に行うために、水可溶性有機溶媒を必須成分として含む液媒体を用いるのが好ましい。
微細化する方法を行う場合は、例えば、ボールミル、ハンマーミル、サンドミル、アトライター、横型連続媒体分散機、ニーダー、連続式一軸混練機、連続式二軸混練機、三本ロール、及びオープンロール連続混練機等の顔料磨砕機や顔料分散機を用いることができる。また、前記顔料磨砕機や顔料分散機は、ソルベントソルトミリング法でも用いることができる。
本発明の金属錯体を利用することで、カラーフィルタ用ブラックマトリックスレジスト、LCDのフォトスペーサー、医療包装用のPTP印刷インキ、食品パッケージ用印刷インキ、各種プラスチック製品、赤外線センサーカバー用フィルム、自動車塗装用塗料、建築、舗装用上塗り塗料等を提供することができる。下記詳述する用途は一例であり、本発明の金属錯体を波長制御剤としていかなる用途へも使用することができる。
(水性インキ用途)
水性インキは樹脂、溶剤、着色剤、および、助剤からなり、一般的な配合比率は次のようになっている。樹脂 15~50質量%、溶剤 40~70質量%、着色剤 1~50質量%、助剤 1~5質量%。これらを分散機にて分散する。
水性インキは樹脂、溶剤、着色剤、および、助剤からなり、一般的な配合比率は次のようになっている。樹脂 15~50質量%、溶剤 40~70質量%、着色剤 1~50質量%、助剤 1~5質量%。これらを分散機にて分散する。
分散機としては、ディスパー、ホモミキサー、ペイントコンディショナー、スキャンデックス、ビーズミル、アトライター、ボールミル、二本ロール、三本ロール、加圧ニーダー等の公知の分散機が挙げられるが、これらに限定されるものではない。
また、分散方法としては、例えば以下(1)~(3)を示すことができる。
(1)化合物分散剤及び水を含有する水性媒体に、化合物を添加した後、撹拌・分散装置を用いて化合物を該水性媒体中に分散させることにより、化合物ペーストを調製する方法。
(2)化合物、及び化合物分散剤を2本ロール、ミキサー等の混練機を用いて混練し、得られた混練物を、水を含む水性媒体中に添加し、撹拌・分散装置を用いて化合物ペーストを調製する方法。
(3)メチルエチルケトン、テトラヒドロフラン等のような水と相溶性を有する有機溶剤中に化合物分散剤を溶解して得られた溶液に化合物を添加した後、撹拌・分散装置を用いて化合物を有機溶液中に分散させ、次いで水性媒体を用いて転相乳化させた後、前記有機溶剤を留去し化合物ペーストを調製する方法。
(1)化合物分散剤及び水を含有する水性媒体に、化合物を添加した後、撹拌・分散装置を用いて化合物を該水性媒体中に分散させることにより、化合物ペーストを調製する方法。
(2)化合物、及び化合物分散剤を2本ロール、ミキサー等の混練機を用いて混練し、得られた混練物を、水を含む水性媒体中に添加し、撹拌・分散装置を用いて化合物ペーストを調製する方法。
(3)メチルエチルケトン、テトラヒドロフラン等のような水と相溶性を有する有機溶剤中に化合物分散剤を溶解して得られた溶液に化合物を添加した後、撹拌・分散装置を用いて化合物を有機溶液中に分散させ、次いで水性媒体を用いて転相乳化させた後、前記有機溶剤を留去し化合物ペーストを調製する方法。
混練機としては、特に限定されることなく、例えば、ヘンシェルミキサー、加圧ニーダー、バンバリーミキサー、プラネタリミキサー、トリミックスなどがあげられる。また、撹拌・分散装置としても特に限定されることなく、例えば、超音波ホモジナイザー、高圧ホモジナイザー、ペイントシェーカー、ボールミル、ロールミル、サンドミル、サンドグラインダー、ダイノーミル、ディスパーマット、SCミル、ナノマイザー等を挙げられる。これらのうちの1つを単独で用いてもよく、2種類以上装置を組み合わせて用いてもよい。
分散工程の後に、イオン交換処理や限外処理による不純物除去工程を経て、その後に後処理を行っても良い。イオン交換処理によって、カチオン、アニオンといったイオン性物質(2価の金属イオン等)を除去することができ、限外処理によって、不純物溶解物質(化合物合成時の残留物質、分散液組成中の過剰成分、有機化合物に吸着していない樹脂、混入異物等)を除去することができる。イオン交換処理は、公知のイオン交換樹脂を用いる。限外処理は、公知の限外ろ過膜を用い、通常タイプ又は2倍能力アップタイプのいずれでもよい。
水性インキに用いられる樹脂としてはポリビニルアルコール類、ポリビニルピロリドン類、アニオン性基やカチオン性基を有するウレタン樹脂、アニオン性基やカチオン性基を有するラジカル系共重合体樹脂等が挙げられる。アニオン性基やカチオン性基を有するラジカル系共重合体樹脂としては例えば、アクリル酸-アクリル酸エステル共重合体などのアクリル系樹脂、スチレン-アクリル酸共重合体、スチレン-メタクリル酸共重合体、スチレン-メタクリル酸-アクリル酸エステル共重合体、スチレン-α-メチルスチレン-アクリル酸共重合体、スチレン-α-メチルスチレン-アクリル酸-アクリル酸エステル共重合体などのスチレン-アクリル樹脂、スチレン-マレイン酸共重合体、スチレン-無水マレイン酸共重合体、ビニルナフタレン-アクリル酸共重合体、及び該水性樹脂の塩が挙げられる。
前記共重合体の塩を形成するための化合物としては、水酸化ナトリウム、水酸化カリウム、水酸化リチウムなどの水酸化アルカリ金属類、およびジエチルアミン、アンモニア、エチルアミン、トリエチルアミン、プロピルアミン、イソプロピルアミン、ジプロピルアミン、ブチルアミン、イソブチルアミン、トリエタノールアミン、ジエタノールアミン、アミノメチルプロパノール、モルホリンなどが挙げられる。これらの塩を形成するための化合物の使用量は、前記共重合体の中和当量以上であることが好ましい。
また市販品を使用することも勿論可能である。市販品としては、味の素ファインテクノ(株)製品のアジスパーPBシリーズ、ビックケミー・ジャパン(株)のDisperbykシリーズ、BYK-シリーズ、BASFジャパン株式会社製のJoncrylシリーズ、EFKAシリーズ等を使用できる。
溶剤としては、水や水溶性有機溶剤等が挙げられる。水溶性有機溶剤としては、例えば、アセトン、メチルエチルケトン、メチルブチルケトン、メチルイソブチルケトン、等のケトン類;メタノール、エタノール、イソプロピルアルコール、1-プロパノール、2-プロパノール、1-ブタノール、2-ブタノール、ブチルアルコール、ペンチルアルコール、およびこれらと同族のアルコールなどのアルコール類;テトラヒドロフラン、1,4-ジオキサン、1,2-ジメトキシエタン、等のエーテル類;ジメチルホルムアミド、N-メチルピロリドン、等のアミド類が挙げられる。
助剤としては、物理的、化学的な安定性や、印刷適性を向上させるための添加剤である。可塑剤、紫外線防止剤、酸化防止剤、帯電防止剤などがある。必要に応じて、例えば硫酸バリウム、炭酸バリウム、炭酸カルシウム、石膏、アルミナ白、クレー、シリカ、シリカ白、タルク、ケイ酸カルシウム、沈降性炭酸マグネシウム等の体質顔料を適宜配合しても良い。
(塗料用途)
本発明の化合物を着色剤として塗料とする場合、塗料として使用される樹脂としては、アクリル樹脂、メラミン樹脂、エポキシ樹脂、ポリエステル樹脂、ポリウレタン樹脂、ポリアミド樹脂、フェノール樹脂など様々である。
本発明の化合物を着色剤として塗料とする場合、塗料として使用される樹脂としては、アクリル樹脂、メラミン樹脂、エポキシ樹脂、ポリエステル樹脂、ポリウレタン樹脂、ポリアミド樹脂、フェノール樹脂など様々である。
塗料に使用される溶媒としては、トルエンやキシレン、メトキシベンゼン等の芳香族系溶剤、酢酸エチルや酢酸ブチル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート等の酢酸エステル系溶剤、エトキシエチルプロピオネート等のプロピオネート系溶剤、メタノール、エタノール、プロパノールn-ブタノール、イソブタノール等のアルコール系溶剤、ブチルセロソルブ、プロピレングリコールモノメチルエーテル、ジエチレングリコールエチルエーテル、ジエチレングリコールジメチルエーテル等のエーテル系溶剤、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系溶剤、ヘキサン等の脂肪族炭化水素系溶剤、N,N-ジメチルホルムアミド、γ-ブチロラクタムn-メチル-2-ピロリドン、アニリン、ピリジン等の窒素化合物系溶剤、γ-ブチロラクトン等のラクトン系溶剤、カルバミン酸メチルとカルバミン酸エチルの48:52の混合物のようなカルバミン酸エステル、水等がある。溶媒としては、特にプロピオネート系、アルコール系、エーテル系、ケトン系、窒素化合物系、ラクトン系、水等の極性溶媒で水可溶のものが適している。
また、化合物添加剤及び/又は化合物を、液状樹脂中で分散し又は混合し、塗料用樹脂組成物とする場合に、通常の添加剤類、例えば、分散剤類、充填剤類、塗料補助剤類、乾燥剤類、可塑剤類及び/又は補助化合物を用いることができる。これは、それぞれの成分を、単独又は幾つかを一緒にして、全ての成分を集め、又はそれらの全部を一度に加えることによって、分散又は混合して達成される。
上記のように用途にあわせて調製された本発明の化合物を含む組成物を分散する分散機としては、ディスパー、ホモミキサー、ペイントコンディショナー、スキャンデックス、ビーズミル、アトライター、ボールミル、二本ロール、三本ロール、加圧ニーダー等の公知の分散機が挙げられるが、これらに限定されるものではない。化合物の分散は、これらの分散機にて分散が可能な粘度になるよう、樹脂、溶剤が添加され分散される。分散後の高濃度塗料ベースは固形分5~20%であり、これにさらに樹脂、溶剤を混合し塗料として使用に供される。
(インクジェットインキ用途)
本発明の化合物は、インクジェット用インクに好適に使用することができ、特に化合物分散剤などを用いて分散させた水性化合物分散液として、水性インクジェット用インクに好適に使用することができる。前記水性化合物分散液は、本発明の縮合多環系有機化合物の高濃度水分散液(化合物ペースト)を作成し、それを水溶性溶媒及び/または水で希釈し、必要に応じてその他の添加剤を添加して調製することができる。
本発明の化合物は、インクジェット用インクに好適に使用することができ、特に化合物分散剤などを用いて分散させた水性化合物分散液として、水性インクジェット用インクに好適に使用することができる。前記水性化合物分散液は、本発明の縮合多環系有機化合物の高濃度水分散液(化合物ペースト)を作成し、それを水溶性溶媒及び/または水で希釈し、必要に応じてその他の添加剤を添加して調製することができる。
本発明の化合物を前記水溶性溶媒及び/または水に分散させて化合物ペーストを得る方法は特に限定はなく、公知の分散方法を使用することが好ましい。この時使用する分散剤も、公知の化合物分散剤を使用して水に分散してもよいし、界面活性剤を使用してもよい。前記化合物分散剤としては水性樹脂がよく、好ましい例としては、ポリビニルアルコール類、ポリビニルピロリドン類、アニオン性基やカチオン性基を有するウレタン樹脂、アニオン性基やカチオン性基を有するラジカル系共重合体樹脂等が挙げられる。アニオン性基やカチオン性基を有するラジカル系共重合体樹脂としては例えば、アクリル酸-アクリル酸エステル共重合体などのアクリル系樹脂、スチレン-アクリル酸共重合体、スチレン-メタクリル酸共重合体、スチレン-メタクリル酸-アクリル酸エステル共重合体、スチレン-α-メチルスチレン-アクリル酸共重合体、スチレン-α-メチルスチレン-アクリル酸-アクリル酸エステル共重合体などのスチレン-アクリル樹脂、スチレン-マレイン酸共重合体、スチレン-無水マレイン酸共重合体、ビニルナフタレン-アクリル酸共重合体、及び該水性樹脂の塩が挙げられる。
前記共重合体の塩を形成するための化合物としては、水酸化ナトリウム、水酸化カリウム、水酸化リチウムなどの水酸化アルカリ金属類、およびジエチルアミン、アンモニア、エチルアミン、トリエチルアミン、プロピルアミン、イソプロピルアミン、ジプロピルアミン、ブチルアミン、イソブチルアミン、トリエタノールアミン、ジエタノールアミン、アミノメチルプロパノール、モルホリンなどが挙げられる。これらの塩を形成するための化合物の使用量は、前記共重合体の中和当量以上であることが好ましい。
また市販品を使用することも勿論可能である。市販品としては、味の素ファインテクノ(株)製品のアジスパーPBシリーズ、ビックケミー・ジャパン(株)のDisperbykシリーズ、BYK-シリーズ、BASFジャパン株式会社製のEFKAシリーズ等を使用できる。
また、分散方法としては、例えば以下(1)~(3)を示すことができる。
(1)化合物分散剤及び水を含有する水性媒体に、化合物を添加した後、撹拌・分散装置を用いて化合物を該水性媒体中に分散させることにより、化合物ペーストを調製する方法。
(2)化合物、及び化合物分散剤を2本ロール、ミキサー等の混練機を用いて混練し、得られた混練物を、水を含む水性媒体中に添加し、撹拌・分散装置を用いて化合物ペーストを調製する方法。
(3)メチルエチルケトン、テトラヒドロフラン等のような水と相溶性を有する有機溶剤中に化合物分散剤を溶解して得られた溶液に化合物を添加した後、撹拌・分散装置を用いて化合物を有機溶液中に分散させ、次いで水性媒体を用いて転相乳化させた後、前記有機溶剤を留去し化合物ペーストを調製する方法。
(1)化合物分散剤及び水を含有する水性媒体に、化合物を添加した後、撹拌・分散装置を用いて化合物を該水性媒体中に分散させることにより、化合物ペーストを調製する方法。
(2)化合物、及び化合物分散剤を2本ロール、ミキサー等の混練機を用いて混練し、得られた混練物を、水を含む水性媒体中に添加し、撹拌・分散装置を用いて化合物ペーストを調製する方法。
(3)メチルエチルケトン、テトラヒドロフラン等のような水と相溶性を有する有機溶剤中に化合物分散剤を溶解して得られた溶液に化合物を添加した後、撹拌・分散装置を用いて化合物を有機溶液中に分散させ、次いで水性媒体を用いて転相乳化させた後、前記有機溶剤を留去し化合物ペーストを調製する方法。
混練機としては、特に限定されることなく、例えば、ヘンシェルミキサー、加圧ニーダー、バンバリーミキサー、プラネタリミキサー、トリミックスなどがあげられる。また、撹拌・分散装置としても特に限定されることなく、例えば、超音波ホモジナイザー、高圧ホモジナイザー、ペイントシェーカー、ボールミル、ロールミル、サンドミル、サンドグラインダー、ダイノーミル、ディスパーマット、SCミル、ナノマイザー等を挙げられる。これらのうちの1つを単独で用いてもよく、2種類以上装置を組み合わせて用いてもよい。
前記化合物ペーストに占める縮合多環系有機化合物の量は5~60質量%であることが好ましく、10~50質量%であることがより好ましい。化合物量が5質量%より少ない場合は、前記化合物ペーストから調製した水性インクの着色が不充分であり、充分な画像濃度が得られない傾向にある。また、逆に60質量%よりも多い場合は、化合物ペーストにおいて化合物の分散安定性が低下する傾向がある。
また、粗大粒子が、ノズル詰まり、その他の画像特性を劣化させる原因になるため、インク調製前後に、遠心分離、あるいは濾過処理等により粗大粒子を除去することが好ましい。
前記化合物ペーストに占める縮合多環系有機化合物の量は5~60質量%であることが好ましく、10~50質量%であることがより好ましい。化合物量が5質量%より少ない場合は、前記化合物ペーストから調製した水性インクの着色が不充分であり、充分な画像濃度が得られない傾向にある。また、逆に60質量%よりも多い場合は、化合物ペーストにおいて化合物の分散安定性が低下する傾向がある。
また、粗大粒子が、ノズル詰まり、その他の画像特性を劣化させる原因になるため、インク調製前後に、遠心分離、あるいは濾過処理等により粗大粒子を除去することが好ましい。
分散工程の後に、イオン交換処理や限外処理による不純物除去工程を経て、その後に後処理を行っても良い。イオン交換処理によって、カチオン、アニオンといったイオン性物質(2価の金属イオン等)を除去することができ、限外処理によって、不純物溶解物質(化合物合成時の残留物質、分散液組成中の過剰成分、有機化合物に吸着していない樹脂、混入異物等)を除去することができる。イオン交換処理は、公知のイオン交換樹脂を用いる。限外処理は、公知の限外ろ過膜を用い、通常タイプ又は2倍能力アップタイプのいずれでもよい。
前記化合物ペーストを作成した後、適宜希釈し必要に応じた添加剤を添加して、目的に応じた水性化合物分散液を得る。前記水性化合物分散液をインクジェット記録用インクに適用する場合は、更に水溶性溶媒及び/または水、バインダー目的のアニオン性基含有有機高分子化合物等を加え、所望の物性に必要に応じて湿潤剤(乾燥抑止剤)、浸透剤、あるいはその他の添加剤を添加して調製する。インクの調整後に、遠心分離あるいは濾過処理工程を加えてもよい。
インクの物理特性については特に限定はされないが、インクジェットインクとしての吐出性に考慮して、粘度は1~10(mPa・s)が好ましく、表面張力は20~50(mN/m)が好ましく、化合物濃度は1~10質量%であることが好ましい。
前記湿潤剤は、インクの乾燥防止を目的として添加する。乾燥防止を目的とする湿潤剤のインク中の含有量は3~50質量%であることが好ましい。本発明で使用する湿潤剤としては特に限定はないが、水との混和性がありインクジェットプリンターのヘッドの目詰まり防止効果が得られるものが好ましい。例えば、グリセリン、エチレングリコール、ジエチレングリコール、トリエチレングリコール、分子量2000以下のポリエチレングリコール、プロピレングリコール、ジプロピレングリコール、トリプロピレングリコール、1,3-プロピレングリコール、イソプロピレングリコール、イソブチレングリコール、1,4-ブタンジオール、1,3-ブタンジオール、1,5-ペンタンジオール、1,6-ヘキサンジオール、メソエリスリトール、ペンタエリスリトール、等が挙げられる。中でも、プロピレングリコール、1,3-ブチルグリコールを含むことが安全性を有し、かつインク乾燥性、吐出性能に優れた効果が見られる。
前記浸透剤は、被記録媒体への浸透性改良や記録媒体上でのドット径調整を目的として添加する。浸透剤としては、例えばエタノール、イソプロピルアルコール等の低級アルコール、エチレングリコールヘキシルエーテルやジエチレングリコールブチルエーテル等のアルキルアルコールのエチレンオキシド付加物やプロピレングリコールプロピルエーテル等のアルキルアルコールのプロピレンオキシド付加物等が挙げられる。
前記界面活性剤は、表面張力等のインク特性を調整するために添加する。このために添加することのできる界面活性剤は特に限定されるものではなく、各種のアニオン性界面活性剤、ノニオン性界面活性剤、カチオン性界面活性剤、両性界面活性剤などが挙げられ、これらの中では、アニオン性界面活性剤、ノニオン性界面活性剤が好ましい。
前記界面活性剤は、表面張力等のインク特性を調整するために添加する。このために添加することのできる界面活性剤は特に限定されるものではなく、各種のアニオン性界面活性剤、ノニオン性界面活性剤、カチオン性界面活性剤、両性界面活性剤などが挙げられ、これらの中では、アニオン性界面活性剤、ノニオン性界面活性剤が好ましい。
アニオン性界面活性剤としては、例えば、アルキルベンゼンスルホン酸塩、アルキルフェニルスルホン酸塩、アルキルナフタレンスルホン酸塩、高級脂肪酸塩、高級脂肪酸エステルの硫酸エステル塩、高級脂肪酸エステルのスルホン酸塩、高級アルコールエーテルの硫酸エステル塩及びスルホン酸塩、高級アルキルスルホコハク酸塩、ポリオキシエチレンアルキルエーテルカルボン酸塩、ポリオキシエチレンアルキルエーテル硫酸塩、アルキルリン酸塩、ポリオキシエチレンアルキルエーテルリン酸塩等が挙げられ、これらの具体例として、ドデシルベンゼンスルホン酸塩、イソプロピルナフタレンスルホン酸塩、モノブチルフェニルフェノールモノスルホン酸塩、モノブチルビフェニルスルホン酸塩、ジブチルフェニルフェノールジスルホン酸塩などを挙げることができる。
ノニオン性界面活性剤としては、例えば、ポリオキシエチレンアルキルエーテル、ポリオキシエチレンアルキルフェニルエーテル、ポリオキシエチレン脂肪酸エステル、ソルビタン脂肪酸エステル、ポリオキシエチレンソルビタン脂肪酸エステル、ポリオキシエチレンソルビトール脂肪酸エステル、グリセリン脂肪酸エステル、ポリオキシエチレングリセリン脂肪酸エステル、ポリグリセリン脂肪酸エステル、ショ糖脂肪酸エステル、ポリオキシエチレンアルキルアミン、ポリオキシエチレン脂肪酸アミド、脂肪酸アルキロールアミド、アルキルアルカノールアミド、アセチレングリコール、アセチレングリコールのオキシエチレン付加物、ポリエチレングリコールポリプロピレングリコールブロックコポリマー、等を挙げることができ、これらの中では、ポリオキシエチレンノニルフェニルエーテル、ポリオキシエチレンオクチルフェニルエーテル、ポリオキシエチレンドデシルフェニルエーテル、ポリオキシエチレンアルキルエーテル、ポリオキシエチレン脂肪酸エステル、ソルビタン脂肪酸エステル、ポリオキシエチレンソルビタン脂肪酸エステル、脂肪酸アルキロールアミド、アセチレングリコール、アセチレングリコールのオキシエチレン付加物、ポリエチレングリコールポリプロピレングリコールブロックコポリマーが好ましい。
その他の界面活性剤として、ポリシロキサンオキシエチレン付加物のようなシリコーン系界面活性剤;パーフルオロアルキルカルボン酸塩、パーフルオロアルキルスルホン酸塩、オキシエチレンパーフルオロアルキルエーテルのようなフッ素系界面活性剤;スピクリスポール酸、ラムノリピド、リゾレシチンのようなバイオサーファクタント等も使用することができる。
これらの界面活性剤は、単独で用いることもでき、又2種類以上を混合して用いることもできる。界面活性剤を添加する場合は、その添加量はインクの全質量に対し、0.001~2質量%の範囲が好ましく、0.001~1.5質量%であることがより好ましく、0.01~1質量%の範囲であることがさらに好ましい。界面活性剤の添加量が0.001質量%未満の場合は、界面活性剤添加の効果が得られない傾向にあり、2質量%を超えて用いると、画像が滲むなどの問題を生じやすくなる。
また、必要に応じて防腐剤、粘度調整剤、pH調整剤、キレート化剤、可塑剤、酸化防止剤、紫外線吸収剤等を添加することができる。
(UVインキ用途)
本発明の化合物は、UVインキに好適に使用することができ、特に分散剤などを用いて分散させた水性化合物分散液として、UVインキに好適に使用することができる。反応性紫外線吸収剤を0.1~50質量%含有し、好ましくは0.5~30質量%、さらに好ましくは1~20質量%含有する。反応性紫外線吸収剤の含有量が0.1質量%未満であると、形成される塗膜の紫外線吸収能が低くなってしまう。一方、反応性紫外線吸収剤の含有量が50質量%超であると、反応しきれなかった反応性紫外線吸収剤が形成される塗膜に残りやすくなり、塗膜が脆くなる場合がある。
本発明の化合物は、UVインキに好適に使用することができ、特に分散剤などを用いて分散させた水性化合物分散液として、UVインキに好適に使用することができる。反応性紫外線吸収剤を0.1~50質量%含有し、好ましくは0.5~30質量%、さらに好ましくは1~20質量%含有する。反応性紫外線吸収剤の含有量が0.1質量%未満であると、形成される塗膜の紫外線吸収能が低くなってしまう。一方、反応性紫外線吸収剤の含有量が50質量%超であると、反応しきれなかった反応性紫外線吸収剤が形成される塗膜に残りやすくなり、塗膜が脆くなる場合がある。
UVインキには、その他の成分として、従来公知の材料をさらに含有させることができる。その他の成分としては、単官能モノマー、多官能モノマー、光硬化性オリゴマー、光硬化性ポリマー等の硬化成分の他、これらの硬化成分を光硬化させるための光重合開始剤、増感剤、UVインクの粘性や塗布性を調整するための有機溶剤等、インクの保存安定性を高めるための重合禁止剤等を挙げることができる。
単官能モノマーとしては、メチル(メタ)アクリレート、エチル(メタ)アクリレート、ブチル(メタ)アクリレート、n-ブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、t-ブチル(メタ)アクリレート、ヘキシル(メタ)アクリレート、シクロヘキシル(メタ)アクリレート、トリメチルシクロヘキシル(メタ)アクリレート、t-ブチルシクロヘキシル(メタ)アクリレート、2-エチルヘキシル(メタ)アクリレート、イソデシル(メタ)アクリレート、ラウリル(メタ)アクリレート、ステアリル(メタ)アクリレート、イソボルニル(メタ)アクリレート、ジシクロペンテニル(メタ)アクリレート、アダマンチル(メタ)アクリレート、アダマンチルメチル(メタ)アクリレート、2-ヒドロキシエチル(メタ)アクリレート、2-ヒドロキシプロピル(メタ)アクリレート、4-ヒドロキシブチル(メタ)アクリレート、グリシジル(メタ)アクリレート、ジメチルアミノエチル(メタ)アクリレート、ジエチルアミノエチル(メタ)アクリレート、ポリエチレングリコールモノ(メタ)アクリレート、ポリエチレングリコールモノメチルエーテル(メタ)アクリレート、2-エトキシエチル(メタ)アクリレート、テトラヒドロフルフリル(メタ)アクリレート、アリル(メタ)アクリレート、ビニロキシエトキシエチル(メタ)アクリレート、ベンジル(メタ)アクリレート、フェノキシエチル(メタ)アクリレート、無水フタル酸と2-ヒドロキシエチル(メタ)アクリレートとの付加物、アクリロイルモルホリン等のラジカル重合性モノマー等を挙げることができる。
多官能モノマー及び光硬化性オリゴマーとしては、ネオペンチルグリコールジ(メタ)アクリレート、エチレングリコールジ(メタ)アクリレート、ポリ(n=2以上)エチレングリコールジ(メタ)アクリレート、ポリプロピレングリコール(n=2以上)ジ(メタ)アクリレート、ポリブチレングリコール(n=2以上)ジ(メタ)アクリレート、2,2-ビス(4-(メタ)アクリロキシエトキシフェニル)プロパン、2,2-ビス(4-(メタ)アクリロキシジエトキシフェニル)プロパン、トリメチロールプロパンジアクリレート、ビス(2-(メタ)アクリロキシエチル)-ヒドロキシエチル-イソシアヌレート、トリメチロールプロパントリ(メタ)アクリレート、トリス(2-(メタ)アクリロキシエチル)イソシアヌレート、ペンタエリスリトールトリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、ビスフェノールA型ジエポキシと(メタ)アクリル酸とを反応させたエポキシジ(メタ)アクリレート等のエポキシポリ(メタ)アクリレート、1,6-ヘキサメチレンジイソシアネートの3量体に2-ヒドロキシエチル(メタ)アクリレートを反応させたウレタントリ(メタ)アクリレート、イソホロンジイソシアネートと2-ヒドロキシプロピル(メタ)アクリレートとを反応させたウレタンジ(メタ)アクリレート、イソホロンジイソシアネートとペンタエリスリトールトリ(メタ)アクリレートとを反応させたウレタンヘキサ(メタ)アクリレート、ジシクロヘキシルジイソシアネートと2-ヒドロキシエチル(メタ)アクリレートとを反応させたウレタンジ(メタ)アクリレート、ジシクロヘキシルジイソシアネートとポリ(n=6~15)テトラメチレングリコールとのウレタン化反応物に2-ヒドロキシエチル(メタ)アクリレートとを反応させたウレタンジ(メタ)アクリレート等のウレタンポリ(メタ)アクリレート、トリメチロールエタンとコハク酸及び(メタ)アクリル酸とを反応させたポリエステル(メタ)アクリレート、トリメチロールプロパンとコハク酸、エチレングリコール、及び(メタ)アクリル酸を反応させたポリエステル(メタ)アクリレート等のポリエステルポリ(メタ)アクリレート等を挙げることができる。
光硬化性ポリマーとしては、ポリ(メタ)アクリレート、ポリウレタン、ポリエステル、ポリアミド、ポリイミド、ポリエポキシ樹脂等のポリマーの末端や側鎖に、ラジカル重合性を示す複数の(メタ)アクリロイルオキシ基が導入されたポリマー等を挙げることができる。さらに、カルボキシ基等を有する、アルカリ現像性の光硬化性ポリマーを用いることもできる。
光重合開始剤としては、ベンゾイン、ベンゾインモノメチルエーテル、ベンゾインイソプロピルエーテル、アセトイン、ベンジル、ベンゾフェノン、p-メトキシベンゾフェノン、ジエトキシアセトフェノン、ベンジルジメチルケタール、2,2-ジエトキシアセトフェノン、1-ヒドロキシシクロヘキシルフェニルケトン、メチルフェニルグリオキシレート、2-ヒドロキシ-2-メチル-1-フェニルプロパン-1-オン等のカルボニル化合物;テトラメチルチウラムモノスルフィド、テトラメチルチウラムジスルフィド等の硫黄化合物;2,4,6-トリメチルベンゾイルジフェニルフォスフィンオキサイド、2,4,6-トリメチルベンゾイルフェニルエトキシフォスフィンオキサイド、ビス(2,4,6-トリメチルベンゾイル)-フェニルフォスフィンオキサイド、ビス(2,6-ジメトキシベンゾイル)-2,4,4-トリメチル-ペンチルフォスフィンオキサイド等のリン酸化合物;2-ベンジル-2-ジメチルアミノ-1-(4-モルフォリノフェニル)ブタノン-1やカンファーキノン等を挙げることができる。
増感剤としては、トリメチルアミン、メチルジメタノールアミン、トリエタノールアミン、p-ジエチルアミノアセトフェノン、p-ジメチルアミノ安息香酸エチル、p-ジメチルアミノ安息香酸イソアミル、N,N-ジメチルベンジルアミンおよび4,4’-ビス(ジエチルアミノ)ベンゾフェノン等の、前述重合性成分と付加反応を起こさないアミン類を併用することができる。
有機溶剤としては、炭化水素系溶剤、アルコール系溶剤、エステル系溶剤、ケトン系溶剤、グリコール系溶剤、グリコールエステル系溶剤、アミド系溶剤、カーボネート系溶剤、スルホキシド系溶剤、イオン液体等を挙げることができる。
重合禁止剤としては、ハイドロキノン、メトキノン、ジ-t-ブチルハイドロキノン、P-メトキシフェノール、ブチルヒドロキシトルエン、ニトロソアミン塩等を上げることができる。
(プラスチック用途)
本発明の化合物はプラスチック着色用途にも使用できる。着色プラスチック成形品を得る場合には、たとえばポリエチレン、ポリプロピレン等のポリオレフィンやポリ塩化ビニル樹脂等の、射出成形やプレス成形等の熱成形用の熱可塑性樹脂(プラスチック)が用いられるが、本発明の化合物はこれらの樹脂に従来公知の方法で練り込んで使用することができる。
本発明の化合物はプラスチック着色用途にも使用できる。着色プラスチック成形品を得る場合には、たとえばポリエチレン、ポリプロピレン等のポリオレフィンやポリ塩化ビニル樹脂等の、射出成形やプレス成形等の熱成形用の熱可塑性樹脂(プラスチック)が用いられるが、本発明の化合物はこれらの樹脂に従来公知の方法で練り込んで使用することができる。
(トナー用途)
本発明の化合物はトナー着色用途にも使用できる。
静電荷像現像用トナーを得る場合には、たとえばポリエステル樹脂、ポリアミド樹脂、スチレン樹脂、アクリル樹脂等の常温で固形の皮膜形成性の熱可塑性樹脂が分散用樹脂として使用される。
本発明の化合物はトナー着色用途にも使用できる。
静電荷像現像用トナーを得る場合には、たとえばポリエステル樹脂、ポリアミド樹脂、スチレン樹脂、アクリル樹脂等の常温で固形の皮膜形成性の熱可塑性樹脂が分散用樹脂として使用される。
本発明の化合物を構成成分として製造される静電荷像現像用トナーは、トナー中に磁性体を含有する1成分色磁性トナー(磁性一成分現像用カラートナー)、磁性体を含有しない非磁性1成分色カラートナー(非磁性一成分現像用カラートナー)、又は、キャリアーを混合した2成分色現像剤用カラートナー(二成分現像用カラートナー)として用いることができる。
1成分色磁性トナーは、通常使用されているものと同様に、例えば着色剤、結着樹脂、磁性粉、電荷制御剤(CCA)や離型剤に代表されるその他添加剤等から構成出来る。
静電荷像現像用トナー中に占める本発明の化合物の使用量は特に限定されないが、結着樹脂100質量部に対し0.5~25質量部の割合で使用することが好ましく、着色剤自身の有する帯電性能を一層顕著ならしめる点から結着樹脂100質量部に対し4~10質量部であることが更に好ましい。
静電荷像現像用トナーに用いられる結着樹脂としては、前記熱可塑性樹脂として例示した公知慣用のものがいずれも使用できるが、熱又は圧力の適用下で接着性を示す合成樹脂、天然樹脂、天然ゴム、合成ゴム、合成ワックス等がいずれも使用できる。
(ブラックマトリックス・フォトスペーサー用途)
本発明の化合物は、公知の方法でカラーフィルタのブラックマトリックス部のパターンの形成やLCD用のフォトスペーサーに用いることが出来る。典型的には、本発明の化合物と、感光性樹脂とを必須成分して含むパターン形成用感光性組成物を得ることが出来る。
本発明の化合物は、公知の方法でカラーフィルタのブラックマトリックス部のパターンの形成やLCD用のフォトスペーサーに用いることが出来る。典型的には、本発明の化合物と、感光性樹脂とを必須成分して含むパターン形成用感光性組成物を得ることが出来る。
前記パターン形成用感光性組成物を調製するには、例えば、本発明の化合物と、感光性樹脂と、光重合開始剤と、前記樹脂を溶解する有機溶剤とを必須成分として混合する。その製造方法としては、本発明の化合物と有機溶剤と必要に応じて分散剤を用いて分散液を調製してから、そこに感光性樹脂等を加えて調製する方法が一般的である。
前記パターン形成用感光性組成物に使用される本発明の化合物には必要に応じて黄色化合物を用いることができる。必要に応じて用いる分散剤としては、例えばビックケミー社のディスパービック(DISPERBYK 登録商標)130、同161、同162、同163、同170、同LPN-6919、同LPN-21116等が挙げられる。また、レベリング剤、カップリング剤、カチオン系の界面活性剤なども併せて使用可能である。
有機溶剤としては、例えばトルエンやキシレン、メトキシベンゼン等の芳香族系溶剤、酢酸エチルや酢酸ブチル、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート等の酢酸エステル系溶剤、エトキシエチルプロピオネート等のプロピオネート系溶剤、メタノール、エタノール等のアルコール系溶剤、ブチルセロソルブ、プロピレングリコールモノメチルエーテル、ジエチレングリコールエチルエーテル、ジエチレングリコールジメチルエーテル等のエーテル系溶剤、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系溶剤、ヘキサン等の脂肪族炭化水素系溶剤、N,N-ジメチルホルムアミド、γ-ブチロラクタムn-メチル-2-ピロリドン、アニリン、ピリジン等の窒素化合物系溶剤、γ-ブチロラクトン等のラクトン系溶剤、カルバミン酸メチルとカルバミン酸エチルの48:52の混合物のようなカルバミン酸エステル、水等がある。有機溶剤としては、特にプロピオネート系、アルコール系、エーテル系、ケトン系、窒素化合物系、ラクトン系、水等の極性溶媒で水可溶のものが適している。
使用可能な感光性樹脂としては、例えばウレタン系樹脂、アクリル系樹脂、ポリアミド酸系樹脂、ポリイミド系樹脂、スチレンマレイン酸系樹脂、スチレン無水マレイン酸系樹脂等の熱可塑性樹脂や、例えば1,6-ヘキサンジオールジアクリレート、エチレングリコールジアクリレート、ネオペンチルグリコールジアクリレート、トリエチレングリコールジアクリレート、ビス(アクリロキシエトキシ)ビスフェノールA、3-メチルペンタンジオールジアクリレート等のような2官能モノマー、トリメチロールプロパントリアクリレート、ペンタエリスリトールトリアクリレート、トリス(2-ヒドロキシエチル)イソシアネート、ジペンタエリスリトールヘキサアクリレート、ジペンタエリスリトールペンタアクリレート等のような多官能モノマー等の光重合性モノマーが挙げられる。
光重合開始剤としては、例えばアセトフェノン、ベンゾフェノン、ベンジルジメチルケタール、ベンゾイルパーオキサイド、2-クロロチオキサントン、1,3-ビス(4'-アジドベンザル)-2-プロパン、1,3-ビス(4'-アジドベンザル)-2-プロパン-2'-スルホン酸、4,4'-ジアジドスチルベン-2,2'-ジスルホン酸等がある。
こうして調製されたブラックマトリックス用感光性組成物は、フォトマスクを介して紫外線によるパターン露光を行った後、未露光部分を有機溶剤やアルカリ水等で洗浄することによりブラックマトリックスやスペーサーとなすことができる。
光重合開始剤としては、例えばアセトフェノン、ベンゾフェノン、ベンジルジメチルケタール、ベンゾイルパーオキサイド、2-クロロチオキサントン、1,3-ビス(4'-アジドベンザル)-2-プロパン、1,3-ビス(4'-アジドベンザル)-2-プロパン-2'-スルホン酸、4,4'-ジアジドスチルベン-2,2'-ジスルホン酸等がある。
こうして調製されたブラックマトリックス用感光性組成物は、フォトマスクを介して紫外線によるパターン露光を行った後、未露光部分を有機溶剤やアルカリ水等で洗浄することによりブラックマトリックスやスペーサーとなすことができる。
その他、本発明の化合物から成る着色剤組成物は、様々な物品に使用することができる。例えば、グラビアインキ、オフセットインキ、UVインクジェットインクなどとして用いることができる。
以下、実施例を挙げて本発明を更に詳述するが、本発明はこれらの実施例に限定されるものではない。また、以下の実施例の組成物における「%」は『質量%』を意味する。
(実施例1)
没食子酸・一水和物170質量部を2.50%希苛性2180質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液419質量部を15分で滴下した。室温で30分撹拌させた後、8%希苛性溶液でpH1.00に調整し、90℃まで1℃/minで昇温後、6時間撹拌した。放冷後、濾過で回収した。続いて、60℃の温水10000質量部、エタノール3000質量部およびイオン交換水10000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(1)を250質量部得た。
元素分析値:C,34.2;H,2.6;Fe,19.1。
よって、元素分析値から算出される没食子酸:三価の鉄金属のモル比は、1.00:0.840
FT-IR分析値(ピーク波数):1067,1196,1320,1364,1565,1658cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
没食子酸・一水和物170質量部を2.50%希苛性2180質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液419質量部を15分で滴下した。室温で30分撹拌させた後、8%希苛性溶液でpH1.00に調整し、90℃まで1℃/minで昇温後、6時間撹拌した。放冷後、濾過で回収した。続いて、60℃の温水10000質量部、エタノール3000質量部およびイオン交換水10000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(1)を250質量部得た。
元素分析値:C,34.2;H,2.6;Fe,19.1。
よって、元素分析値から算出される没食子酸:三価の鉄金属のモル比は、1.00:0.840
FT-IR分析値(ピーク波数):1067,1196,1320,1364,1565,1658cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
(実施例2)
没食子酸・一水和物170質量部を2.50%希苛性2180質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液838質量部を15分で滴下した。室温で30分撹拌させた後、8%希苛性溶液でpH1.00に調整し、90℃まで1℃/minで昇温後、6時間撹拌した。放冷後、濾過で回収した。続いて、60℃の温水10000質量部、エタノール3000質量部およびイオン交換水10000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(2)を365質量部得た。
元素分析値:C,25.3;H,2.1;Fe,24.4。
よって、元素分析値から算出される没食子酸:三価の鉄金属のモル比は、1.00:1.45
FT-IR分析値(ピーク波数):1061,1206,1311,1362,1558,1681cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
没食子酸・一水和物170質量部を2.50%希苛性2180質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液838質量部を15分で滴下した。室温で30分撹拌させた後、8%希苛性溶液でpH1.00に調整し、90℃まで1℃/minで昇温後、6時間撹拌した。放冷後、濾過で回収した。続いて、60℃の温水10000質量部、エタノール3000質量部およびイオン交換水10000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(2)を365質量部得た。
元素分析値:C,25.3;H,2.1;Fe,24.4。
よって、元素分析値から算出される没食子酸:三価の鉄金属のモル比は、1.00:1.45
FT-IR分析値(ピーク波数):1061,1206,1311,1362,1558,1681cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
(実施例3)
没食子酸・一水和物50質量部を2.50%希苛性435質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液61.6質量部を10分で滴下した。室温で30分撹拌させた後、pH1.00に調整し、90℃まで1℃/minで昇温後、3時間撹拌した。放冷後、濾過で回収した。続いて、エタノール880質量部およびイオン交換水3000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(3)を21質量部得た。
元素分析値:C,38.4;H,2.6;Fe,6.0。
よって、元素分析値から算出される没食子酸:三価の鉄金属のモル比は、1.00:0.235
FT-IR分析値(ピーク波数):1057,1176,1310,1323,1589,1662cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
没食子酸・一水和物50質量部を2.50%希苛性435質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液61.6質量部を10分で滴下した。室温で30分撹拌させた後、pH1.00に調整し、90℃まで1℃/minで昇温後、3時間撹拌した。放冷後、濾過で回収した。続いて、エタノール880質量部およびイオン交換水3000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(3)を21質量部得た。
元素分析値:C,38.4;H,2.6;Fe,6.0。
よって、元素分析値から算出される没食子酸:三価の鉄金属のモル比は、1.00:0.235
FT-IR分析値(ピーク波数):1057,1176,1310,1323,1589,1662cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
(実施例4)
ピロガロール114質量部を2.50%希苛性2180質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液419質量部を15分で滴下した。室温で30分撹拌させた後、8%希苛性溶液でpH1.00に調整し、90℃まで1℃/minで昇温後、6時間撹拌した。放冷後、濾過で回収した。続いて、60℃の温水10000質量部、エタノール3000質量部およびイオン交換水10000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(4)を215質量部得た。
元素分析値:C,33.8;H,2.5;Fe,18.6。
よって、元素分析値から算出されるピロガロール:三価の鉄金属のモル比は、1.00:0.710
FT-IR分析値(ピーク波数):1055,1191,1310,1354,1560cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
ピロガロール114質量部を2.50%希苛性2180質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液419質量部を15分で滴下した。室温で30分撹拌させた後、8%希苛性溶液でpH1.00に調整し、90℃まで1℃/minで昇温後、6時間撹拌した。放冷後、濾過で回収した。続いて、60℃の温水10000質量部、エタノール3000質量部およびイオン交換水10000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(4)を215質量部得た。
元素分析値:C,33.8;H,2.5;Fe,18.6。
よって、元素分析値から算出されるピロガロール:三価の鉄金属のモル比は、1.00:0.710
FT-IR分析値(ピーク波数):1055,1191,1310,1354,1560cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
(実施例5)
5-メチルピロガロール127質量部を2.50%希苛性2180質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液315質量部を15分で滴下した。室温で30分撹拌させた後、pH1.00に調整し、90℃まで1℃/minで昇温後、6時間撹拌した。放冷後、濾過で回収した。続いて、エタノール3000質量部およびイオン交換水10000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(5)を130質量部得た。
元素分析値:C,36.4;H,2.5;Fe,11.1。
よって、元素分析値から算出される5-メチルピロガロール:三価の鉄金属のモル比は、1.00:0.459
FT-IR分析値(ピーク波数):1051,1188,1302,1350,1566cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
5-メチルピロガロール127質量部を2.50%希苛性2180質量部中に加え撹拌した。全溶するのを確認後、35%塩化鉄(III)水溶液315質量部を15分で滴下した。室温で30分撹拌させた後、pH1.00に調整し、90℃まで1℃/minで昇温後、6時間撹拌した。放冷後、濾過で回収した。続いて、エタノール3000質量部およびイオン交換水10000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(5)を130質量部得た。
元素分析値:C,36.4;H,2.5;Fe,11.1。
よって、元素分析値から算出される5-メチルピロガロール:三価の鉄金属のモル比は、1.00:0.459
FT-IR分析値(ピーク波数):1051,1188,1302,1350,1566cm-1(FT-IRから水酸化鉄由来のピークは検出されなかった)
(比較例1)
タンニン酸190質量部を1.50%希苛性958質量部中に加え撹拌した。全て溶解するのを確認後、13.5%硫酸鉄(II)水溶液231質量部を5分で滴下した。室温で1時間撹拌させた後、濾過で回収した。続いて、60℃の温水3000質量部、エタノール3000質量部およびイオン交換水1000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(6)を150質量部得た。
タンニン酸190質量部を1.50%希苛性958質量部中に加え撹拌した。全て溶解するのを確認後、13.5%硫酸鉄(II)水溶液231質量部を5分で滴下した。室温で1時間撹拌させた後、濾過で回収した。続いて、60℃の温水3000質量部、エタノール3000質量部およびイオン交換水1000質量部で洗浄した。得られたウェットケーキを90℃で10時間熱風乾燥機で乾燥することで、黒色材(6)を150質量部得た。
[顔料化1]
実施例1で得た黒色材(1)0.50質量部を塩化ナトリウム1.50質量部、ジエチレングリコール0.70質量部とともにフーバーマーラーで磨砕した。その後、この混合物を1500質量部の60℃の温水に投じ、40℃で2時間攪拌した。水不溶分をろ過分離して60℃の温水200質量部で洗浄した後、90℃で10時間熱風乾燥機で乾燥して黒色材(7)を得た。
実施例1で得た黒色材(1)0.50質量部を塩化ナトリウム1.50質量部、ジエチレングリコール0.70質量部とともにフーバーマーラーで磨砕した。その後、この混合物を1500質量部の60℃の温水に投じ、40℃で2時間攪拌した。水不溶分をろ過分離して60℃の温水200質量部で洗浄した後、90℃で10時間熱風乾燥機で乾燥して黒色材(7)を得た。
[インキ1]
実施例1で得た黒色材(1)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ1を作製した。
実施例1で得た黒色材(1)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ1を作製した。
[インキ2]
実施例2で得た黒色材(2)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ2を作製した。
実施例2で得た黒色材(2)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ2を作製した。
[インキ3]
実施例3で得た黒色材(3)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ3を作製した。
実施例3で得た黒色材(3)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ3を作製した。
[インキ4]
実施例4で得た黒色材(4)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ4を作製した。
実施例4で得た黒色材(4)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ4を作製した。
[インキ5]
実施例5で得た黒色材(5)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ5を作製した。
実施例5で得た黒色材(5)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA(イソプロピルアルコール)2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ5を作製した。
[インキ6]
顔料化1で得た黒色材(7)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ6を作製した。
顔料化1で得た黒色材(7)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、インキ6を作製した。
[比較インキ1]
カーボンブラック(三菱ケミカル株式会社製)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA 2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、比較インキ1を作製した。
カーボンブラック(三菱ケミカル株式会社製)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA 2.92質量部、3.0mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、比較インキ1を作製した。
[比較インキ2]
比較例1で得た黒色材(6)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA 2.92質量部、3.0 mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、比較インキ2を作製した。
比較例1で得た黒色材(6)6.65質量部をポリ瓶に入れ、Joncryl-63J(BASF株式会社製)17.5質量部、イオン交換水17.5質量部、IPA 2.92質量部、3.0 mmガラスビーズ160質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で1時間分散し、顔料分散体を得た。さらに、それらの顔料分散体にJoncryl PDX-7341(BASF株式会社製)17.5質量部を加え、ペイントコンディショナーで10分間分散することで、比較インキ2を作製した。
[インキ色評価]
作製したインキを4milsのアプリケータでPETフィルム上に製膜した。1時間風乾後、90℃で1時間乾燥させインキ塗膜を得た。
次に分光測色計(SDG株式会社社製SpectroEye)にて反射ODを測定した。また、分光測色計(X-rite株式会社製eXact)にてK値を測定した。
作製したインキを4milsのアプリケータでPETフィルム上に製膜した。1時間風乾後、90℃で1時間乾燥させインキ塗膜を得た。
次に分光測色計(SDG株式会社社製SpectroEye)にて反射ODを測定した。また、分光測色計(X-rite株式会社製eXact)にてK値を測定した。
実施例1―5及び顔料化1(没食子酸鉄(III)錯体,ピロガロール鉄(III)錯体,5-メチルピロガロール鉄(III)錯体)を使用したインキ1-6では、比較インキ1(カーボンブラック)および2(古典インク処方品)に比べ、より高いOD値やK値を示した。
[インキ膜透過率評価]
上記で得られたインキ塗膜を分光光度計(日本分光株式会社製V-670)にて透過スペクトルを測定し、インキ1,6および比較インキ1を用いて作製した塗膜のスペクトルを図1に示し比較した。
上記で得られたインキ塗膜を分光光度計(日本分光株式会社製V-670)にて透過スペクトルを測定し、インキ1,6および比較インキ1を用いて作製した塗膜のスペクトルを図1に示し比較した。
実施例1及び顔料化1(没食子酸鉄(III)錯体)を使用したインキ1および6では、比較インキ1(カーボンブラック)に比べ、近赤外領域(800-2480nm)において、より高い透過率を示した。さらに、インキ6を用いた塗膜では近赤外領域(1200-2480nm)の領域において、60%を超える透過率を示した。また、可視域(400-800nm)の領域において、15%未満の透過率を示した。
[塗料1]
実施例1で得た黒色材(1)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料1を作製した。
実施例1で得た黒色材(1)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料1を作製した。
[塗料2]
実施例2で得た黒色材(2)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料2を作製した。
実施例2で得た黒色材(2)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料2を作製した。
[塗料3]
実施例3で得た黒色材(3)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料3を作製した。
実施例3で得た黒色材(3)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料3を作製した。
[塗料4]
実施例4で得た黒色材(4)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料4を作製した。
実施例4で得た黒色材(4)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料4を作製した。
[塗料5]
実施例5で得た黒色材(5)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料5を作製した。
実施例5で得た黒色材(5)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料5を作製した。
[塗料6]
顔料化1で得た黒色材(7)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料6を作製した。
顔料化1で得た黒色材(7)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、塗料6を作製した。
[比較塗料1]
カーボンブラック(三菱ケミカル株式会社製)2.00質量部をポリ瓶に入れ、アミラック 1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナー No.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、比較塗料1を作製した。
カーボンブラック(三菱ケミカル株式会社製)2.00質量部をポリ瓶に入れ、アミラック 1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナー No.3(関西ペイント株式会社製)24.0質量部、3.0mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、比較塗料1を作製した。
[比較塗料2]
比較例1で得た黒色材(6)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0 mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、比較塗料2を作製した。
比較例1で得た黒色材(6)2.00質量部をポリ瓶に入れ、アミラック1026クリヤー(関西ペイント株式会社製)14.0質量部、カンペ焼付シンナーNo.3(関西ペイント株式会社製)24.0質量部、3.0 mmガラスビーズ42.5質量部を加え、ペイントコンディショナー(東洋精機株式会社製)で70分間分散し、比較塗料2を作製した。
[塗料塗膜色評価]
分光測色計(SDG株式会社社製SpectroEye)にて反射ODを測定した。また、分光測色計(X-rite株式会社製eXact)にてK値を測定した。
分光測色計(SDG株式会社社製SpectroEye)にて反射ODを測定した。また、分光測色計(X-rite株式会社製eXact)にてK値を測定した。
実施例1-5及び顔料化1(没食子酸鉄(III)錯体,ピロガロール鉄(III)錯体,5-メチルピロガロール鉄(III)錯体)を使用した塗料1-6では、比較塗料1(カーボンブラック)および2(古典インク処方品)に比べ、より高いOD値やK値を示した。
Claims (6)
- ベンゼン骨格の隣接部位にそれぞれヒドロキシル基を有するベンゼントリオール誘導体と三価の鉄金属から構成される錯体化合物。
- 元素分析から算出されるモル比で、
前記ベンゼントリオール誘導体:三価の鉄金属=1.00:0.20~1.50
である請求項1記載の錯体化合物。
(前記元素分析から算出されるモル比とは、元素分析により計測された炭素および鉄の質量パーセント濃度を、それぞれ構成元素のモル比に換算した後、さらに炭素の値は前記ベンゼントリオール誘導体分子を構成する炭素数で割ることで得られる比) - 水酸化鉄の含有率が1%以下である請求項1または2に記載の錯体化合物。
- 前記ベンゼントリオール誘導体が、少なくとも没食子酸またはピロガロールから選ばれる一つである請求項1または2に記載の錯体化合物。
- 前記錯体化合物が12.5質量%含まれるインキ塗膜において、可視光域400~800nmにおいて透過率が15%未満であり、近赤外領域1200~2500nmにおいて透過率が60%を超えることを特徴とする請求項1または2に記載の錯体化合物。
- 請求項1または2に記載の錯体化合物を含有することを特徴とするトナー、インキ、印刷物、塗料、塗装、プラスチック、繊維、フィルム、ブラックマトリックス用レジスト、フォトスペーサー用レジスト、及び、その硬化物。