WO2023182126A1 - 表面被覆切削工具 - Google Patents

表面被覆切削工具 Download PDF

Info

Publication number
WO2023182126A1
WO2023182126A1 PCT/JP2023/010248 JP2023010248W WO2023182126A1 WO 2023182126 A1 WO2023182126 A1 WO 2023182126A1 JP 2023010248 W JP2023010248 W JP 2023010248W WO 2023182126 A1 WO2023182126 A1 WO 2023182126A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
avg
lower layer
layers
average thickness
Prior art date
Application number
PCT/JP2023/010248
Other languages
English (en)
French (fr)
Inventor
新 高山
英利 淺沼
Original Assignee
三菱マテリアル株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱マテリアル株式会社 filed Critical 三菱マテリアル株式会社
Publication of WO2023182126A1 publication Critical patent/WO2023182126A1/ja

Abstract

下部層Ａの平均厚さＡｔは０．３～６．０μｍ、上部層Ｂの平均厚さＢｔは０．１～３．０μｍであって、２．０≦Ａt／Ｂｔ≦５．０であり、 下部層Ａは平均厚さαｔのＡ１α層と平均厚さβｔのＡ１β層の交互積層で、 ０．５ｎｍ≦αｔ≦４．０ｎｍ、０．５ｎｍ≦βｔ≦４．０ｎｍ、０．７≦βｔ／αｔ≦１．３であり、 Ａ１α層の組成は、ＡｌｘＴｉ１－ｘＮ（ｘの平均値のｘａｖｇが、０．３５≦ｘａｖｇ≦０．５５）、 Ａ１β層の組成は、ＡｌｙＴｉ１－ｙＮ（ｙの平均値のｙａｖｇが０．６０≦ｙａｖｇ≦０．８０）であって、 １．２≦ｙａｖｇ／ｘａｖｇであり、 上部層Ｂの組成はＡｌａＴｉ１－ａ－ｂＳｉｂＮ（ａの平均値のａａｖｇ、ｂの平均値のｂａｖｇが、０．３５≦ａａｖｇ≦０．６０、０．００＜ｂａｖｇ≦０．１５）である被覆工具

Description

表面被覆切削工具
　本発明は、表面被覆切削工具（以下、被覆工具ということがある）に関する。本出願は、２０２２年３月２２日に出願した日本特許出願である特願２０２２－４５６３３号に基づく優先権を主張する。当該日本特許出願に記載された全ての記載内容は、参照によって本明細書に援用される。
　従来から、被覆工具としては、炭化タングステン（以下、ＷＣで表す）基超硬合金等の基体に被覆層を形成したものが知られている。
　そして、この被覆層の組成、層構造を調整することによって、切削性能がより一層向上した被覆工具を得る提案がなされている
　例えば、特許文献１には、ＴｉｘＡｌ１－ｘＮとＴｉｙＡｌ１－ｙＮ（０≦ｘ＜０．５、０．５＜ｙ≦１）の２種の層を、交互に繰り返して積層体とし、該積層体の全体組成を化学量論的にアルミニウムリッチとした被覆層を有する被覆工具が記載され、該被覆工具は優れた耐摩耗性、耐欠損性を有しているとされている。
　また、例えば、特許文献２には、被覆層が交互層を含み、該交互層は、それぞれの厚さが２ｎｍ以上１００ｎｍ以下であって、１層以上の第１層と第２層とを含み、前記第１層の組成は、ＴｉaＡｌbＳｉcＮ（０．２５≦ａ≦０．４５、０．５５≦ｂ≦０．７５、０≦ｃ≦０．１、ａ＋ｂ＋ｃ＝１）であり、前記第２層の組成は、ＴｉdＡｌeＳｉfＮ（０．３５≦ｄ≦０．５５、０．４５≦ｅ≦０．６５、０≦ｆ≦０．１、ｄ＋ｅ＋ｆ＝１）であって、０．０５≦ｄ－ａ≦０．２かつ０．０５≦ｂ－ｅ≦０．２である被覆工具が記載され、該被覆工具は工具寿命が向上しているとされている。
　さらに、例えば、特許文献３には、ナノビーム回折パターンがＷＣの結晶構造に指数付けされ、ＷとＴｉを含有する炭化物からなるａ層と、前記ａ層の上に配置される相互積層とを有し、前記ａ層は、膜厚が１ｎｍ以上１０ｎｍ以下であり、前記相互積層は、金属元素の総量に対し、Ａｌの含有比率（原子％）が５０％以上７０％以下のＡｌとＴｉの窒化物または炭窒化物からなるｂ層と、前記金属元素の総量に対し、Ａｌの含有比率（原子％）が７０％以上のＡｌとＴｉの窒化物または炭窒化物からなるｃ層とが交互に形成されたものであり、前記ｂ層と前記ｃ層のＡｌの含有比率（原子％）の差が１０％以上３０％以下である被覆層を有する被覆工具が記載され、該被覆工具は、ステンレス鋼の切削においても優れた耐久性を有するとされている。
　加えて、例えば、特許文献４には、被覆層の最外層が、金属成分のみの原子％でＡｌが６０％以上８０％以下、およびＳｉが５％以上１０％以下で残りＴｉよりなる六方晶の窒化物または炭窒化物で構成された被膜である被覆工具が記載され、該被覆工具は耐久性を有するとされている。
特開平７－９７６７９号公報 特開２０１７－１９３００４号公報 特開２０１５－１１０２５９号公報 特開２０１７－１８５５１号公報
　本発明は、前記事情や前記提案を鑑みてなされたものであって、鋼や鋳鉄だけでなく、ステンレス鋼等の高速切削加工に供しても優れた耐摩耗性を有する切削工具を提供することを目的とする。
　ここで、高速切削加工とは、通常の切削加工に比して、切削加工速度が３０％以上速い切削加工をいう。
　本発明の実施形態に係る表面被覆切削工具は、
　基体と該基体に設けられた被覆層を有し、
　前記被覆層は、下部層Ａと該下部層Ａ上の上部層Ｂを有し、
　前記下部層Ａの平均厚さＡｔは０．３μｍ以上、６．０μｍ以下であり、前記上部層Ｂの平均厚さＢｔは０．１μｍ以上、３．０μｍ以下であって、２．０≦Ａt／Ｂｔ≦５．０であり、
前記下部層Ａは、平均厚さαｔのＡ１α層と平均厚さβｔのＡ１β層の交互積層を有し、
０．５ｎｍ≦αｔ≦４．０ｎｍ、０．５ｎｍ≦βｔ≦４．０ｎｍ、０．７≦βｔ／αｔ≦１．３であり、
前記Ａ１α層の組成は、ＡｌｘＴｉ１－ｘＮ（ｘの平均値であるｘａｖｇが、０．３５≦ｘａｖｇ≦０．５５）、
前記Ａ１β層の組成は、ＡｌｙＴｉ１－ｙＮ（ｙの平均値であるｙａｖｇが、０．６０≦ｙａｖｇ≦０．８０）であって、
１．２≦ｙａｖｇ／ｘａｖｇを満足し、
前記上部層Ｂの組成は、ＡｌａＴｉ１－ａ－ｂＳｉｂＮ（ａの平均値であるａａｖｇ、ｂの平均値であるｂａｖｇが、ぞれぞれ、０．３５≦ａａｖｇ≦０．６０、０．００＜ｂａｖｇ≦０．１５）である。
　前記実施形態に係る表面被覆切削工具は、次の事項を満足していてもよい。
　前記下部層Ａは前記基体の側の下部層Ａ１と前記上部層Ｂの側の下部層Ａ２であり、
前記下部層Ａ１の平均厚さＡ１ｔと前記下部層Ａ２の平均厚さＡ２ｔは、０．１μｍ≦Ａ１ｔ≦４．５μｍ、０．２μｍ≦Ａ２ｔ≦４．０μｍ、０．５≦Ａ１t／Ａ２ｔ≦３．０であり、
前記下部層Ａ１は、前記Ａ１α層と前記Ａ１β層の前記交互積層であり、
前記下部層Ａ２は、平均厚さγｔのＡ２γ層と平均厚さδｔのＡ２δ層の交互積層であり、
１．５ｎｍ≦γｔ≦８．０ｎｍ、１．５ｎｍ≦δｔ≦８．０ｎｍ、０．７≦δｔ／γｔ≦１．３であって、
１．０＜（γｔ＋δｔ）／（αｔ＋βｔ）≦６．０であり、
前記Ａ２γ層の組成は、ＡｌｚＴｉ１－ｚＮ（ｚの平均値であるｚａｖｇが、０．３０≦ｚａｖｇ≦０．５０）、
前記Ａ２δ層の組成は、ＡｌｗＴｉ１－ｗＮ（ｗの平均値であるｗａｖｇが、０．５５≦ｗａｖｇ≦０．７５）であって、
１．２≦ｗａｖｇ／ｚａｖｇを満足し、
かつ、０．０２≦（ｘａｖｇ－ｚａｖｇ）≦０．３０、０．０２≦（ｙａｖｇ－ｗａｖｇ）≦０．３０であること。
　前記表面被覆切削工具は、鋼や鋳鉄だけでなくステンレス鋼の高速切削に供しても、優れた耐摩耗性を発揮する。
本発明の一実施形態に係る表面被覆切削工具における被覆層の縦断面の模式図の一例である。 本発明の他の実施形態に係る表面被覆切削工具における被覆層の縦断面の模式図の一例である。
　本発明者は、鋼や鋳鉄切削加工での性能を担保しつつステンレス鋼等の高速切削加工に供しても優れた耐摩耗性を有する切削工具を得るために被覆層について鋭意検討を行った。その結果、以下の（１）～（３）の知見を得た。
（１）被覆層として、それぞれ平均厚さが０．５～４．０ｎｍのＡｌ含有量の多いＡｌＴｉＮ層とＡｌ含有量の少ないＡｌＴｉＮ層とを積層した層を用いると、切削加工中にＡｌＴｉＮの分解（ＡｌＴｉＮがＴｉＮとＡｌＮに分解すると推定している）を生じることより硬さが上昇し、鋼や鋳鉄の切削に対して耐摩耗性が優れる被覆工具を得ることができる。しかし、この被覆層に酸化摩耗が生じる場合、十分にその性能を発揮できないときがある。すなわち、Ａｌ含有量の異なるＡｌＴｉＮ積層のみでは酸化損傷により耐摩耗性が低下することがある。
（２）そこで、このＡｌＴｉＮ積層の上部に、被覆層に前述の酸化摩耗を抑えるべくＴｉＳｉＮ層を設けることを検討した。しかし、このＴｉＳｉＮ層は耐酸化性が低いため、例えばステンレス鋼の切削加工において境界損傷による損傷が発達してしまう。さらに、ＴｉＳｉＮ層はＡｌＴｉＮ層との格子定数差が大きく、両層の界面において整合性が悪い。
（３）一方、前記ＡｌＴｉＮ積層に代えて、Ｓｉの含有量が異なるＴｉＡｌＳｉＮ積層としても、ＴｉＡｌＳｉＮ積層ではＴｉＡｌＳｉＮの分解（ＴｉＡｌＳｉＮがＴｉＮとＡｌＮ、Ｓｉ３Ｎ４に分解すると推定している）が生じ難く耐摩耗性の向上が小さいため耐摩耗性が低下する。
　そこで、本発明者は更に検討をした結果、それぞれ平均厚さが０．５～４．０ｎｍの２種のＡｌ含有量であるＡｌＴｉＮ層を交互積層した層と、その上部にＳｉを含むＡｌＴｉＮ層、すなわち、ＡｌＴｉＳｉＮ層を設けると、前記目的が達成できることを見出した。
　また、下部層を基体側の下部層Ａ１とその上側の下部層Ａ２とし、下部層Ａ１は前述の平均厚さの２種のＡｌ含有量であるＡｌＴｉＮ層を交互積層した層とし、下部層Ａ２は平均厚さが１．５～８．０ｎｍのそれぞれ２種のＡｌ含有量であるＡｌＴｉＮ層を交互積層した層とし、かつ、下部層Ａ１の２種のＡｌＴｉＮ層のＡｌ含有量は、下部層Ａ２の２種のＡｌＴｉＮ層のＡｌ含有量よりも多くすると、より確実に、前記目的が達成できることも見出した。
　以下では、本発明の実施形態に係る被覆工具について、より詳細に説明する。なお、本明細書、特許請求の範囲の記載において、数値範囲を「Ｌ～Ｍ」を用いて表現する場合、「Ｌ以上、Ｍ以下」と同義であって、その範囲は上限値（Ｍ）および下限値（Ｌ）の数値を含むものである。また、上限値（Ｍ）のみに単位が記載されているとき、上限値（Ｍ）および下限値（Ｌ）は同じ単位である。
Ｉ．第１の実施形態
　以下、第１の実施形態に係る被覆工具について説明する。
１．被覆層
　本発明の第１の実施形態に係る被覆工具の被覆層の層構造はその一例を図１に模式的に示すとおりであり、被覆層（２）は、基体（１）上に下部層Ａ（３）を有し、この下部層Ａ（３）の上部に上部層Ｂ（４）を有している。図１おいて、下部層Ａ（３）は、それぞれ０．５～４．０ｎｍの平均厚さを有する薄い層の積層、すなわち、Ａ１α層（７）とＡ１β層（８）交互積層であることが好ましい。なお、図１において、下部層Ａ（３）の白地の部分にも、Ａ１α層（７）とＡ１β層（８）が交互積層されている。
　なお、被覆層はこれらの層に加えて、後述するその他の層を有していてもよい。
（１）下部層Ａの平均厚さと上部層Ｂの平均厚さの和
　本実施形態における、下部層Ａの平均厚さと上部層Ｂの平均厚さの和は、０．４μｍ以上、９．０μｍ以下であることが好ましい。その理由は、０．４μｍ未満であると、長期の使用にわたって優れた耐摩耗性を発揮することができず、一方、９．０μｍを超えると、結晶粒が粗大化しやすくなり、耐チッピング性の向上が得られなくなるからである。この平均厚さは、０．８μｍ以上、６．０μｍ以下がより好ましい。
（２）下部層Ａと上部層Ｂのそれぞれの平均厚さ
　下部層Ａの平均厚さＡｔは０．３μｍ以上、６．０μｍ以下、上部層Ｂの平均厚さＢｔは０．１μｍ以上、３．０μｍ以下であり、かつ、２．０≦Ａｔ／Ｂｔ≦５．０であることが好ましい。その理由は、下部層Ａの平均厚さＡｔと上部層Ｂの平均厚さＢｔがこの範囲にあると、切削時の被覆層の酸化損傷を抑制し、下部層ＡにおいてＴｉＡｌＮがＴｉＮとＡｌＮに分解することによる耐摩耗性向上が可能となるためである。
　下部層Ａの平均厚さＡｔは０．６μｍ以上、４．０μｍ以下、上部層Ｂの平均厚さＢｔは０．２μｍ以上、２．０μｍ以下がより好ましい。また、２．３≦Ａｔ／Ｂｔ≦３．５であることがより好ましい。
　また、下部層Ａの平均厚さＡｔよりも上部層Ｂの平均厚さＢｔを薄くすることにより、下部層Ａが切削加工中にＡｌＴｉＮの分解（ＡｌＴｉＮがＴｉＮとＡｌＮに分解する）を生じて硬さが上昇し、被覆層の耐摩耗性が向上する。
（３）下部層Ａの構成
　下部層Ａは、Ａ１α層とＡ１β層との交互積層である。そして、Ａ１α層とＡ１β層のそれぞれの平均厚さであるαｔ、βｔは、以下の関係、すなわち、
０．５ｎｍ≦αｔ≦４．０ｎｍ、０．５ｎｍ≦βｔ≦４．０ｎｍ、０．７≦βｔ／αｔ≦１．３
を満足することが好ましい。また、０．８ｎｍ≦αｔ≦３．５ｎｍ、０．８ｎｍ≦βｔ≦３．５ｎｍ、０．８≦βｔ／αｔ≦１．２を満足することがより好ましい。
　その理由は、これらの平均厚さの関係を満足すると、前記目的が達成できるためである。
（３－１）Ａ１α層、Ａ１β層の積層数
　Ａ１α層の積層数をｍとＡ１β層の積層数をｎとすると、｜ｍ－ｎ｜≦１であり、ｍ＋ｎは特に制約はないが、５０～２００１が好ましい。その理由は、５０未満では切削加工時に発生するクラック進展を十分に防止することができないために耐欠損性が低下することがあり、２００１を超えると繰返し数が増えることより、下部層Ａの結晶粒が微粒化し耐摩耗性が低下してしまうことがあるためである。ｍ＋ｎは、１００～１００１がより好ましい。
　また、Ａ１α層とＡ１β層は、それぞれ、交互に積層されていればよく、基体側、工具表面側の層は、それぞれ、いずれであってもよい。
（３－２）Ａ１α層とＡ２α層の組成
　下部層を構成するＡ１α層とＡ２α層の組成は、
Ａ１α層が、ＡｌｘＴｉ１－ｘＮ（ｘの平均値であるｘａｖｇが、０．３５≦ｘａｖｇ≦０．５５）であり、
Ａ１β層が、ＡｌｙＴｉ１－ｙＮ（ｙの平均値であるｙａｖｇが０．６０≦ｙａｖｇ≦０．８０）であって、
１．２≦ｙａｖｇ／ｘａｖｇを満足することが好ましい。
　Ａ１α層、Ａ２α層の組成この範囲にあると、耐摩耗性が向上する。その理由は、切削加工中にＡｌＴｉＮがＴｉＮとＡｌＮに分解するためと推定される。
　なお、下部層を構成するＡｌＴｉＮについて、後述する製造法の一例に従えば、（ＡｌＴｉ）とＮとの比は、１：１となるように製造されるが、不可避的に（意図せずに）１：１とならないものが存在することがある。このことは、以下で述べる他の窒化物についても同様である。
（４）上部層Ｂの組成
　上部層Ｂは、ＡｌａＴｉ１－ａ－ｂＳｉｂＮ（ａの平均値であるａａｖｇ、ｂの平均値であるｂａｖｇが、ぞれぞれ、０．３５≦ａａｖｇ≦０．６０、０．００＜ｂａｖｇ≦０．１５）であることが好ましい。
　上部層Ｂの組成が前記範囲であれば、耐酸化性、耐摩耗性を向上させることができるが、この範囲外になると耐酸化性、耐摩耗性が低下してしまう。その理由は、六方晶構造のＡｌＮ相が析出するためと推定される。
（５）その他の層
（５－１）意図的に成膜してもよい層
　意図的に成膜してもよい層として、以下に述べる最外層と下地層をあげることができる。
（５－１－１）最外層
　上部層Ｂの上に最外層を選択的に設けてもよい。
　最外層としては、例えば、ＴｉＮ層（ＴｉＮ層のＴｉとＮの原子比は化学量論的なものに限定されない）を設けてもよい。このＴｉＮ層を設けた場合には、ＴｉＮ層自体が黄金色の色調を有することから、例えば、被覆工具が未使用であるか使用したものであるかを色調変化によって、判別する識別層として活用することができる。なお、この識別層としてのＴｉＮ層の平均層厚は、例えば、０．１～１．０μｍでよい。
（５－１－２）下地層
　下部層Ａと基体との間に下地層を選択的に設けてもよい。
　下地層としては、ＴｉＣ層、ＴｉＮ層、ＴｉＣＮ層、ＴｉＣＮＯ層のＴｉ化合物層およびＡｌＴｉＮ層が例示でき、その平均厚さは、０．１～２．０μｍが例示できる。平均厚さがこの範囲にあると、下部層Ａと基体との密着性がより一層向上する場合がある。
（５－２）意図せずに成膜されてしまう層（不可避的に生じる可能性のある層）
　本実施形態では、下地層、下部層Ａ（Ａ１α層とＡ１β層）、上部層Ｂ、および、最外層以外の層は存在しないように、すなわち、これらの層は接するように成膜される。しかし、成膜すべき層の種類を変更する際に、成膜装置内の圧力や温度の変化が意図せずに発生し、これらの層とは異なる意図しない層が形成されることがある。
３．基体
（１）材質
　本実施形態に使用する基体は、従来公知の基体の材質であれば、前述の目的を達成することを阻害するものでない限り、いずれのものも使用可能である。一例をあげるならば、ＷＣ基超硬合金（ＷＣの他、Ｃｏを含み、さらに、Ｔｉ、Ｔａ、Ｎｂ等の炭化物または炭窒化物を添加したものも含むもの）、サーメット（ＴｉＣ、ＴｉＮ、ＴｉＣＮ等を主成分とするもの）、セラミックス（炭化チタン、炭化珪素、窒化珪素、窒化アルミニウム、酸化アルミニウム）、ｃＢＮ焼結体、またはダイヤモンド焼結体のいずれかであることが好ましい。
（２）形状
　基体の形状は、切削工具として用いられる形状であれば特段の制約はなく、インサートの形状、ドリルの形状が例示できる。
ＩＩ．第２の実施形態
　第２の実施形態について説明する。第１の実施形態の説明と重複する個所の記載は省略する。
１．被覆層
　第２の実施形態に係る被覆工具の被覆層の層構造はその一例を図２に模式的に示すとおりであり、被覆層（２）は、基体（１）上に下部層Ａ（３）を有し、この下部層Ａ（３）の上部に上部層Ｂ（４）を有している。下部層Ａ（３）では、下部層Ａ１（５）と下部層Ａ２（６）が積層されている。図２おいて、下部層Ａ１（５）は第１の実施形態と同じであり、下部層Ａ２（６）はそれぞれ、１．５～８．０ｎｍの平均厚さを有する薄い層の交互積層、すなわち、それぞれ、下部層Ａ１（５）はＡ１α層（７）とＡ１β層（８）、下部層Ａ２（６）はＡ２γ層（９）とＡ２δ層（１０）との交互積層であることが好ましい。なお、図２において、下部層Ａ１（５）および下部層Ａ２（６）の白地の部分にも、それぞれ、Ａ１α層（７）とＡ１β層（８）、Ａ２γ層（９）とＡ２δ層（１０）がそれぞれ交互積層されている。
　なお、第１の実施形態と同様に被覆層はこれらの層に加えて、後述するその他の層を有していてもよい。
（１）下部層Ａの平均厚さと上部層Ｂの平均厚さの和
　第２の実施形態においても、下部層Ａの平均厚さと上部層Ｂの平均厚さの和は、第１の実施形態と同じ厚さ範囲が好ましい（より好ましい厚さ範囲も同じである）。
（２）下部層Ａと上部層Ｂのそれそれの平均厚さ
　第２の実施形態においても、下部層Ａと上部層Ｂのそれぞれの平均厚さは第１の実施形態と同じ厚さ範囲が好ましい（より好ましい厚さ範囲も同じである）。
（３）下部層Ａの構成
　第２の実施形態では、下部層Ａは下部層Ａ１と下部層Ａ２である。下部層Ａ１の平均厚さＡ１ｔと下部層Ａ２の平均厚さＡ２ｔは、０．１μｍ≦Ａ１ｔ≦４．５μｍ、０．２μｍ≦Ａ２ｔ≦４．０μｍであって、０．５≦Ａ１t／Ａ２ｔ≦３．０であることが好ましい。この関係を満たすとき、前述の目的が達成される。
　以下、下部層Ａ１と下部層Ａ２について詳細に説明する。
（３－１）下部層Ａ１
　下部層Ａ１は、第１の実施形態の下部層Ａと同じＡ１α層とＡ２α層との交互積層であり、第１の実施形態の説明で述べた平均厚さ、平均厚さの関係式、さらには、組成、組成の関係式を満足することが好ましい。
（３－２）下部層Ａ２
　下部層Ａ２は、Ａ２γ層とＡ２δ層との交互積層である。Ａ２γ層とＡ２δ層のそれぞれの平均厚さであるγｔ、δｔは、以下の関係、すなわち、
１．５ｎｍ≦γｔ≦８．０ｎｍ、１．５ｎｍ≦δｔ≦８．０ｎｍ、０．７≦δｔ／γｔ≦１．３
を満足し、かつ、下部層Ａ１を構成するＡ１α層とＡ２α層のそれぞれの平均厚さに対して、
１．０＜（γｔ＋δｔ）／（αｔ＋βｔ）≦６．０
を満足することが好ましい。
　その理由は、この関係式を満足すると、前述の目的が達成されるためである。（γｔ＋δｔ）／（αｔ＋βｔ）は、１．２≦（γｔ＋δｔ）／（αｔ＋βｔ）≦３．０であることがより好ましい。
（３－２）Ａ２γ層とＡ２δ層の組成
　Ａ２γ層の組成は、ＡｌｚＴｉ１－ｚＮ（ｚの平均値であるｚａｖｇが、０．３０≦ｚａｖｇ≦０．５０）であり、
前記Ａ２δ層の組成は、ＡｌｗＴｉ１－ｗＮ（ｗの平均値であるｗａｖｇが、０．５５≦ｗａｖｇ≦０．７５）であって、
１．２≦ｗａｖｇ／ｚａｖｇを満足することが好ましい。
　また、Ａ１α層とＡ２α層の組成およびＡ２γ層とＡ２δ層の組成は、
０．０２≦（ｘａｖｇ－ｚａｖｇ）≦０．３０、０．０２≦（ｙａｖｇ－ｗａｖｇ）≦０．３０
を満足することが好ましい。
　Ａ１α層、Ａ２α層の組成、および、Ａ２γ層、Ａ２δ層の組成が、この範囲にあると、耐摩耗性が向上する。その理由は、これらの層の組成がこの範囲にあると、より高いＡｌ含有量の下部層Ａを形成することができ、切削加工中にＡｌＴｉＮがＴｉＮとＡｌＮに分解すると推定されるが、この範囲を外れるときは、下部層Α１と下部層Ａ２のＡｌ含有量差が小さくなって、この分解が不十分となり下部層Α１によるひずみ低減が十分ではなく六方晶構造のＡｌＮ相が析出し、被覆層の耐摩耗性が低下してしまうためと推定される。
（４）Ａ１α層、Ａ１β層、Ａ２γ層、および、Ａ２δ層の平均厚さと積層数
　下部層Ａ１と下部層Ａ２をそれぞれ構成するＡ１α層およびＡ１β層の平均厚さは０．５～４．０ｎｍ、Ａ２γ層およびＡ２δ層の平均厚さは１．５～８．０ｎｍが好ましい。下部層Ａ１におけるＡ１α層の積層数ｐとＡ１β層の積層数ｑ、下部層Ａ２におけるＡ２γ層の積層数ｒとＡ２δ層の積層数ｓは、｜ｐ－ｑ｜≦１、｜ｒ－ｓ｜≦１であって、ｐ＋ｑおよびｒ＋ｓは特に制約はないが、、ｐ＋ｑは５０～９０１、ｒ＋ｓは２０～５５１が好ましい。その理由は、ｐ＋ｑが５０およびｒ＋ｓが２０未満では切削加工時に発生するクラック進展を十分に防止することができないために耐欠損性が低下することがあり、一方、ｐ＋ｑが９０１およびｒ＋ｓが５５１を超えると繰返し数が増えることより、下部層Ａの結晶粒が微粒化し耐摩耗性が低下してしまうことがあるためである。ｐ＋ｑは１００～４５１、ｒ＋ｓは５０～１８０がより好ましい。
　また、Ａ１α層とＡ１β層、Ａ２γ層とＡ２δ層は、それぞれ、交互に積層されていればよく、基体側、工具表面側の層は、それぞれ、いずれであってもよい。
３．上部層
　上部層については、第１の実施形態の説明と同じである。
４．その他の層
　最外層および下地層については、第１の実施形態の説明と同じである。
　意図せずに成膜されてしまう層（不可避的に生じる可能性のある層）については、下部層Ａ（Ａ１α層とＡ１β層）を下部層Ａ１（Ａ１α層とＡ１β層）、下部層Ａ２（Ａ２γ層とＡ２δ層）と読み替えたものと同じである。
５．基体
　基体の材質、形状は、第１の実施形態と同じでよい。
ＩＩＩ．測定方法
１．下部層Ａ、上部層Ｂ、および、その他の層の平均組成および平均厚さ
　被覆層を構成する下部層Ａ、下部層Ａ１、下部層Ａ２、上部層Ｂ、および、その他の層の平均厚さについては、走査型電子顕微鏡（Ｓｃａｎｎｉｎｇ　Ｅｌｅｃｔｒｏｎ　Ｍｉｃｒｏｓｃｏｐｅ：ＳＥＭ）、透過型電子顕微鏡（Ｔｒａｎｓｍｉｓｓｉｏｎ　Ｅｌｅｃｔｒｏｎ　Ｍｉｃｒｏｓｃｏｐｅ：ＴＥＭ）に付属するエネルギー分散型Ｘ線分光器（Ｅｎｅｒｇｙ　Ｄｉｓｐｅｒｓｉｖｅ　Ｘ－ｒａｙ　Ｓｐｅｃｔｒｏｍｅｔｅｒ：ＥＤＳ）を用いた縦断面（インサートのとき、基体表面の微少な凹凸を無視し平坦な面として扱ったとき、この面に垂直な断面。ドリルのような軸物工具のときは軸に垂直な断面）の観察により各層を鑑別してその平均厚さを求めることができる。各層の各成分平均含有割合については、厚さ方向に５本 のＴＥＭ－ＥＤＳ線分析を行って求めた。
　ここで、基体の表面は、この縦断面を観察して、基体と下部層Ａ（または下部層Ａ１）との界面を、元素マッピングにより定め、こうして得られた界面の粗さ曲線について、平均直線を算術的に求め、これを基体の表面とする。
２．Ａ１α層、Ａ１β層、Ａ２γ層、および、Ａ２δ層の平均厚さ
　被覆層の厚さ方向に、これら層が少なくとも１０層、好ましくは５０層以上含まれる長さのラインスキャンを行い、隣り合うＴｉのＥＤＳスペクトルの強度の極大値と極小値の平均値をそれぞれ算出する。算出した隣り合う強度の極大値と極小値の平均値を与えるラインスキャンを行った線分上の位置を求める。そして、一つの極大値を含み隣り合う平均値を与える位置間の距離および一つの極小値を含み隣り合う平均値を与える位置間の距離が各層の厚みとなり、これを平均して平均厚さを得ることができる。
ＩＶ．製造方法
　第１および第２の実施形態の被覆工具の被覆層は、例えば、ＡＩＰ装置（アークイオンプレーティング装置）を用いて製造することができる。また、そのターゲットとして、下部層Ａ、下部層Ａ１および下部層Ａ２の組成にそれぞれ対応した組成のＡｉＴｉターゲットを、上部層Ｂの成膜用ターゲットとして、上部層Ｂの組成に対応した組成のＡｌＴｉＳｉターゲットを、それぞれ用いることにより成膜することができる。
　以上の説明は、以下に付記する特徴を含む。
（付記１）
　基体と該基体に設けられた被覆層を有する表面被覆切削工具であって、
　前記被覆層は、下部層Ａと該下部層Ａ上の上部層Ｂを有し、
　前記下部層Ａの平均厚さＡｔは０．３μｍ以上、６．０μｍ以下であり、前記上部層Ｂの平均厚さＢｔは０．１μｍ以上、３．０μｍ以下であって、２．０≦Ａt／Ｂｔ≦５．０であり、
　前記下部層Ａは、平均厚さαｔのＡ１α層と平均厚さβｔのＡ１β層の交互積層を有し、
０．５ｎｍ≦αｔ≦４．０ｎｍ、０．５ｎｍ≦βｔ≦４．０ｎｍ、０．７≦βｔ／αｔ≦１．３であり、
　前記Ａ１α層の組成は、ＡｌｘＴｉ１－ｘＮ（ｘの平均値であるｘａｖｇが、０．３５≦ｘａｖｇ≦０．５５）、
前記Ａ１β層の組成は、ＡｌｙＴｉ１－ｙＮ（ｙの平均値であるｙａｖｇが、０．６０≦ｙａｖｇ≦０．８０）であって、
１．２≦ｙａｖｇ／ｘａｖｇを満足し、
　前記上部層Ｂの組成は、ＡｌａＴｉ１－ａ－ｂＳｉｂＮ（ａの平均値であるａａｖｇ、ｂの平均値であるｂａｖｇが、ぞれぞれ、０．３５≦ａａｖｇ≦０．６０、０．００＜ｂａｖｇ≦０．１５）である
ことを特徴とする表面被覆切削工具。
（付記２）
　前記下部層Ａは前記基体の側の下部層Ａ１と前記上部層Ｂの側の下部層Ａ２であり、
　前記下部層Ａ１の平均厚さＡ１ｔと前記下部層Ａ２の平均厚さＡ２ｔは、０．１μｍ≦Ａ１ｔ≦４．５μｍ、０．２μｍ≦Ａ２ｔ≦４．０μｍ、０．５≦Ａ１t／Ａ２ｔ≦３．０であり、
　前記下部層Ａ１は、前記Ａ１α層と前記Ａ１β層の前記交互積層であり、
　前記下部層Ａ２は、平均厚さγｔのＡ２γ層と平均厚さδｔのＡ２δ層の交互積層であり、
１．５ｎｍ≦γｔ≦８．０ｎｍ、１．５ｎｍ≦δｔ≦８．０ｎｍ、０．７≦δｔ／γｔ≦１．３であって、
１．０＜（γｔ＋δｔ）／（αｔ＋βｔ）≦６．０であり、
　前記Ａ２γ層の組成は、ＡｌｚＴｉ１－ｚＮ（ｚの平均値であるｚａｖｇが、０．３０≦ｚａｖｇ≦０．５０）、
前記Ａ２δ層の組成は、ＡｌｗＴｉ１－ｗＮ（ｗの平均値であるｗａｖｇが、０．５５≦ｗａｖｇ≦０．７５）であって、
１．２≦ｗａｖｇ／ｚａｖｇを満足し、
かつ、０．０２≦（ｘａｖｇ－ｚａｖｇ）≦０．３０、０．０２≦（ｙａｖｇ－ｗａｖｇ）≦０．３０である
ことを特徴とする付記１に記載の表面被覆切削工具。
（付記３）
　前記上部層Ｂの上に最外層を有することを特徴とする付記１または２記載の表面被覆切削工具。
（付記４）
　前記下部層Ａと前記基体との間に下地層を有することを特徴とする付記１～３のいずれかに記載の表面被覆切削工具。
　次に、実施例について説明する。
　ここでは、本発明の被覆工具の実施例として、基体がＷＣ基超硬合金であってインサート形状の被覆工具について述べるが、基体は前述の材質のものがいずれも使用でき、また、前述のとおり形状としてドリル、エンドミル等であっても同様である。
　まず、原料粉末として、Ｃｏ粉末、ＴｉＣ粉末、ＶＣ粉末、ＴａＣ粉末、ＮｂＣ粉末、Ｃｒ３Ｃ２粉末、ＷＣ粉末を用意し、これら原料粉末を、表１に示される配合割合に配合し、さらにワックスを加えてボールミルで７２時間湿式混合し、減圧乾燥した後、１００ＭＰａの圧力でプレス成形した。これらの圧粉成形体を６Ｐａの真空雰囲気下、１４００℃で１時間保持して焼結し、所定寸法となるように加工して、ＡＮＳＩ規格・ＳＥＥＮ４２ＡＦＴＮ１のインサート形状をもったＷＣ基超硬合金製の基体１～３を作製した。
　次に、基体１～３をアセトン中で超音波洗浄し乾燥させた。そして、ＡＩＰ装置を用いて被覆層を形成すべく、該装置内の回転テーブル上の中心軸から半径方向に所定距離離れた位置に外周部に沿って基体１～３を装着した。また、カソード電極（蒸発源）として所定組成のターゲットを配置した。
　続いて、ＡＩＰ装置内を排気して０．１Ｐａ以下の真空に保持しながら、ヒーターで装置内を６００℃に加熱した後、回転テーブル上で自転する基体に－１０００Ｖの直流バイアス電圧を印加し、カソード電極とアノード電極との間に１００Ａの電流を流して基体表面をボンバード処理した。
＜第１の実施形態に対応する実施例＞
　ＡＩＰ装置内に反応ガスとして、表２に示す分圧が２．６～７．５Ｐａの窒素雰囲気とし、同じく表２に示す炉内温度に維持した。そして、前記回転テーブル上で自転する基体に、表２に示す－４０～－１２５Ｖの直流電圧を印加し、下部層Ａ（Ａ１α層、Ａ１β層）形成用のＡｌＴｉ合金電極とアノード電極との間に１２５～２１０Ａの電流を流してアーク放電を発生させて所定厚さのＡ１α層、Ａ１β層を形成した。
　そして、Ａ１α層とＡ１β層の成膜をそれぞれ所定回数繰り返すことにより、所定の下部層Ａの積層数とした。
　次に、表２に示す分圧が０．４～０．６Ｐａの窒素雰囲気で、基体に、表２に示す－４０～－１２０Ｖの直流電圧を印加し、上部層Ｂ形成用のＡｉＴｉＳｉ合金とアノード電極との間に１２０～２２０Ａの電流を流してアーク放電を発生させて所定厚さの上部層Ｂを成膜し、実施例の被覆工具（以下、実施例という）１～９を得た。
＜第２の実施形態に対応する実施例＞
　ＡＩＰ装置内に反応ガスとして、表４に示す分圧が１．０～８．２Ｐａの窒素雰囲気とし、同じく表４に示す炉内温度に維持した。そして、前記回転テーブル上で自転する基体に、表２に示す－３０～－１２０Ｖの直流電圧を印加し、下部層Ａ１（Ａ１α層、Ａ１β層）形成用のＡｌＴｉ合金電極とアノード電極との間に１００～２３０Ａの電流を流してアーク放電を発生させて所定厚さのＡ１α層、Ａ１β層を形成した。
　そして、Ａ１α層とＡ１β層の成膜をそれぞれ所定回数繰り返すことにより、所定の下部層Ａ１の積層数とした。
　続いて、表４に示す分圧が３．２～７．５Ｐａの窒素雰囲気で、－６０～－１３５Ｖの直流電圧を印加し、下部層Ａ２（Ａ２γ層、Ａ２δ層）形成用のＡｌＴｉ合金電極とアノード電極との間に１１５～２５０Ａの電流を流してアーク放電を発生させて所定厚さのＡ２γ層、Ａ２δ層を形成した。
　そして、Ａ２γ層とＡ２δ層の成膜をそれぞれ所定回数繰り返すことにより、所定の下部層Ａ２の積層数とした。
　次に、表４に示す分圧が２．５～７．７Ｐａの窒素雰囲気で、基体に、表２に示す－４５～－１８０Ｖの直流電圧を印加し、上部層Ｂ形成用のＡｉＴｉＳｉ合金とアノード電極との間に１２５～２００Ａの電流を流してアーク放電を発生させて所定厚さの上部層Ｂを成膜し、実施例１１～１９を得た。
　さらに、第１の実施形態および第２の実施形態に対応するいくつかの実施例ではＡＩＰ装置内に反応ガスとして、分圧が０．５～９．０Ｐａの窒素雰囲気とし、炉内温度を３００～６００℃に維持した。そして、前記回転テーブル上で自転する基体に、－２０～－５００Ｖの直流電圧を印加し、最外層形成用のＴｉ電極とアノード電極との間に５０～２５０Ａの電流を流してアーク放電を発生させて所定厚さの最外層であるＴｉＮ層を成膜した（最外層の成膜条件は表６に示す）。これらの実施例を表７、８に示す。
　一方、比較のため、前記基体１～３に対して、前記と同じ成膜装置を用いて、第１の実施形態に対応する比較例は表３に示す条件により、第２の実施形態に対応する比較例は表５に示す条件により被覆層を蒸着形成し、表７、８に示す比較例の被覆工具（以下、「比較例」という）１～９、１１～１９を作製した。
　なお、第１の実施形態および第２の実施形態に対応するいくつかの比較例では、実施例と同様に最外層であるＴｉＮ層を成膜した。
　被覆層の平均厚さ、被覆層の平均組成は、前記で作製した実施例１～９、１１～１９および比較例１～９、１１～１９の基体の表面に垂直な被覆層の縦断面について、基体の表面に平行な方向の幅が１０μｍであり、被覆層の厚み領域が全て含まれるよう設定された視野について、走査型電子顕微鏡（ＳＥＭ）、透過型電子顕微鏡（ＴＥＭ）、エネルギー分散型Ｘ線分光器（ＥＤＳ）を用いた断面観察により求めた。
　具体的には、下部層Ａと上部層Ｂの平均厚さは観察断面である縦断面を５０００倍に拡大して、５点の膜厚を求めて平均厚さを算出した。また下部層Ａと上部層Ｂの平均厚さが１μｍ以下の場合は観察断面である縦断面を１００００倍拡大して、５点の膜厚を求めて平均厚さを算出した。また、交互積層を構成する各層の平均厚さ、各層の各成分平均含有量は、前述の方法により測定した。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
　表３において、「－」は該当するものがないことを示している。
Figure JPOXMLDOC01-appb-T000004
Figure JPOXMLDOC01-appb-T000005
Figure JPOXMLDOC01-appb-T000006
Figure JPOXMLDOC01-appb-T000007
　表７において、「－」は該当するものがないことを示している。
Figure JPOXMLDOC01-appb-T000008
　表８において、「－」は該当するものがないことを示している。
　次いで、実施例１～９、１１～１９および比較例１～９、１１～１９について、次の切削条件で切削試験１～３を行った。
切削試験１
切削条件：
　被削材：幅６０ｍｍ×長さ２００ｍｍのブロック材（ＳＵＳ３０４製）
　切削速度：　　１６０　ｍ／ｍｉｎ．
　切り込み：　１．５　ｍｍ
　送り：　　０．１０　ｍｍ／ｔｏｏｔｈ．
切削長２．０ｍまで切削し、逃げ面摩耗幅を測定し、刃先の損耗状態を観察した。逃げ面摩耗幅には酸化損傷、境界損傷による摩耗幅も含むため、酸化損傷、境界損傷が抑制されたかも評価できる
　切削試験の結果を表９、１０に示す。
切削試験２
切削条件：
被削材：幅６０ｍｍ×長さ２００ｍｍのブロック材（ＦＣ■４５０製）
　切削速度：　　１８０　ｍ／ｍｉｎ．
　切り込み：　１．２　ｍｍ
　送り：　　０．１０　ｍｍ／ｔｏｏｔｈ．
切削長１０．０ｍまで切削し、逃げ面摩耗幅を測定し、刃先の損耗状態を観察した。
　切削試験の結果を表１１、１２に示す。
切削試験３
切削条件：
被削材：幅６０ｍｍ×長さ２００ｍｍのブロック材（ＳＮＣＭ４３５製）
　切削速度：　　２００　ｍ／ｍｉｎ．
　切り込み：　１．２　ｍｍ
　送り：　　０．１０　ｍｍ／ｔｏｏｔｈ．
切削長１０．０ｍまで切削し、逃げ面摩耗幅を測定し、刃先の損耗状態を観察した。
　切削試験の結果を表１３、１４に示す。
Figure JPOXMLDOC01-appb-T000009
　表９において、「※」は、最大切削長に達する前に使用寿命に至ったため、使用寿命に至る時間（秒）を示している。
Figure JPOXMLDOC01-appb-T000010
Figure JPOXMLDOC01-appb-T000011
Figure JPOXMLDOC01-appb-T000012
Figure JPOXMLDOC01-appb-T000013
Figure JPOXMLDOC01-appb-T000014
　表９～１４の結果によれば、実施例１～９、１１～１９は、いずれも、チッピング、剥離等の異常損傷の発生はなく、耐摩耗性、耐チッピング性のいずれにも優れていることがわかる。
　これに対して、比較例１～９、１１～１９、チッピングの発生、あるいは、逃げ面摩耗の進行により、短時間で寿命に至っていることは明らかである。
　前記開示した実施の形態はすべての点で例示にすぎず、制限的なものではない。本発明の範囲は前記した実施の形態ではなく請求の範囲によって示され、請求の範囲と均等の意味、および範囲内でのすべての変更が含まれることが意図される。
１　基体
２　被覆層
３　下部層Ａ
４　上部層Ｂ
５　下部層Ａ１
６　下部層Ａ２
７　Ａ１α層
８　Ａ１β層
９　Ａ２γ層
１０　Ａ２δ層
 

Claims (2)

  1. 　基体と該基体に設けられた被覆層を有する表面被覆切削工具であって、
    　前記被覆層は、下部層Ａと該下部層Ａ上の上部層Ｂを有し、
    　前記下部層Ａの平均厚さＡｔは０．３μｍ以上、６．０μｍ以下であり、前記上部層Ｂの平均厚さＢｔは０．１μｍ以上、３．０μｍ以下であって、２．０≦Ａt／Ｂｔ≦５．０であり、
    　前記下部層Ａは、平均厚さαｔのＡ１α層と平均厚さβｔのＡ１β層の交互積層を有し、
    ０．５ｎｍ≦αｔ≦４．０ｎｍ、０．５ｎｍ≦βｔ≦４．０ｎｍ、０．７≦βｔ／αｔ≦１．３であり、
    　前記Ａ１α層の組成は、ＡｌｘＴｉ１－ｘＮ（ｘの平均値であるｘａｖｇが、０．３５≦ｘａｖｇ≦０．５５）、
    前記Ａ１β層の組成は、ＡｌｙＴｉ１－ｙＮ（ｙの平均値であるｙａｖｇが、０．６０≦ｙａｖｇ≦０．８０）であって、
    １．２≦ｙａｖｇ／ｘａｖｇを満足し、
    　前記上部層Ｂの組成は、ＡｌａＴｉ１－ａ－ｂＳｉｂＮ（ａの平均値であるａａｖｇ、ｂの平均値であるｂａｖｇが、ぞれぞれ、０．３５≦ａａｖｇ≦０．６０、０．００＜ｂａｖｇ≦０．１５）である
    ことを特徴とする表面被覆切削工具。
  2. 　前記下部層Ａは前記基体の側の下部層Ａ１と前記上部層Ｂの側の下部層Ａ２であり、
    　前記下部層Ａ１の平均厚さＡ１ｔと前記下部層Ａ２の平均厚さＡ２ｔは、０．１μｍ≦Ａ１ｔ≦４．５μｍ、０．２μｍ≦Ａ２ｔ≦４．０μｍ、０．５≦Ａ１t／Ａ２ｔ≦３．０であり、
    　前記下部層Ａ１は、前記Ａ１α層と前記Ａ１β層の前記交互積層であり、
    　前記下部層Ａ２は、平均厚さγｔのＡ２γ層と平均厚さδｔのＡ２δ層の交互積層であり、
    １．５ｎｍ≦γｔ≦８．０ｎｍ、１．５ｎｍ≦δｔ≦８．０ｎｍ、０．７≦δｔ／γｔ≦１．３であって、
    １．０＜（γｔ＋δｔ）／（αｔ＋βｔ）≦６．０であり、
    　前記Ａ２γ層の組成は、ＡｌｚＴｉ１－ｚＮ（ｚの平均値であるｚａｖｇが、０．３０≦ｚａｖｇ≦０．５０）、
    前記Ａ２δ層の組成は、ＡｌｗＴｉ１－ｗＮ（ｗの平均値であるｗａｖｇが、０．５５≦ｗａｖｇ≦０．７５）であって、
    １．２≦ｗａｖｇ／ｚａｖｇを満足し、
    かつ、０．０２≦（ｘａｖｇ－ｚａｖｇ）≦０．３０、０．０２≦（ｙａｖｇ－ｗａｖｇ）≦０．３０である
    ことを特徴とする請求項１に記載の表面被覆切削工具。
     
PCT/JP2023/010248 2022-03-22 2023-03-16 表面被覆切削工具 WO2023182126A1 (ja)