WO2023149253A1 - Procédé de production d'une plaque de polarisation composite - Google Patents

Procédé de production d'une plaque de polarisation composite Download PDF

Info

Publication number
WO2023149253A1
WO2023149253A1 PCT/JP2023/001860 JP2023001860W WO2023149253A1 WO 2023149253 A1 WO2023149253 A1 WO 2023149253A1 JP 2023001860 W JP2023001860 W JP 2023001860W WO 2023149253 A1 WO2023149253 A1 WO 2023149253A1
Authority
WO
WIPO (PCT)
Prior art keywords
polarizing plate
film
layer
adhesive layer
sensitive adhesive
Prior art date
Application number
PCT/JP2023/001860
Other languages
English (en)
Japanese (ja)
Inventor
範充 江端
慎也 萩原
裕史 太田
成志 中里
辰徳 荒木
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Publication of WO2023149253A1 publication Critical patent/WO2023149253A1/fr

Abstract

L'invention concerne un procédé de production d'une plaque de polarisation composite capable de supprimer les bulles d'air de devenir piégées entre une plaque de polarisation et/ou un film traité en surface et une couche adhésive.　Dans la plaque de polarisation composite, le film traité en surface et la plaque de polarisation sont stratifiés. Le film traité en surface a un film de substrat et une couche traitée en surface formée sur la surface du film de substrat. La plaque de polarisation comprend au moins un élément polarisant. Le procédé de production d'une plaque de polarisation composite comprend : l'étape (a) pour obtenir un stratifié par liaison d'un film traité en surface et d'une plaque de polarisation à travers une couche adhésive ayant une contrainte d'au plus 0,8 N/mm2 à 800 % d'allongement et l'étape (b) pour effectuer un ajustement de telle sorte que dans le stratifié, la contrainte de la couche adhésive à un allongement de 800 % à une température de 23 °C devient d'au moins 0,9 N/mm2.
PCT/JP2023/001860 2022-02-04 2023-01-23 Procédé de production d'une plaque de polarisation composite WO2023149253A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2022016187A JP2023114075A (ja) 2022-02-04 2022-02-04 複合偏光板の製造方法
JP2022-016187 2022-02-04

Publications (1)

Publication Number Publication Date
WO2023149253A1 true WO2023149253A1 (fr) 2023-08-10

Family

ID=87552120

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2023/001860 WO2023149253A1 (fr) 2022-02-04 2023-01-23 Procédé de production d'une plaque de polarisation composite

Country Status (3)

Country Link
JP (1) JP2023114075A (fr)
TW (1) TW202346984A (fr)
WO (1) WO2023149253A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010024103A1 (fr) * 2008-09-01 2010-03-04 日本カーバイド工業株式会社 Composition d’adhésif autocollant, adhésif autocollant et film optique
JP2014164052A (ja) * 2013-02-22 2014-09-08 Dainippon Printing Co Ltd 粘着層付き位相差フィルム及びこれを用いた光学部材
US20210271011A1 (en) * 2020-02-29 2021-09-02 Gary Sharp Innovations, Llc Preserving In-Plane Function of Polarization Laminates in a Forming Process

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010024103A1 (fr) * 2008-09-01 2010-03-04 日本カーバイド工業株式会社 Composition d’adhésif autocollant, adhésif autocollant et film optique
JP2014164052A (ja) * 2013-02-22 2014-09-08 Dainippon Printing Co Ltd 粘着層付き位相差フィルム及びこれを用いた光学部材
US20210271011A1 (en) * 2020-02-29 2021-09-02 Gary Sharp Innovations, Llc Preserving In-Plane Function of Polarization Laminates in a Forming Process

Also Published As

Publication number Publication date
JP2023114075A (ja) 2023-08-17
TW202346984A (zh) 2023-12-01

Similar Documents

Publication Publication Date Title
JP5429777B2 (ja) 偏光板
JP5382843B2 (ja) 偏光板の製造方法
KR101668159B1 (ko) (메트)아크릴계 수지 조성물 및 그것을 이용한 (메트)아크릴계 수지 필름
WO2013047884A1 (fr) Plaque de polarisation et procédé de fabrication de cette dernière
WO2017204161A1 (fr) Film multicouche et dispositif d'affichage d'image
KR101855959B1 (ko) 편광 필름, 점착제층이 부착된 편광 필름 및 화상 표시 장치
JP6043315B2 (ja) 偏光子保護フィルム、その製造方法、偏光板、光学フィルムおよび画像表示装置
TW201640160A (zh) 附黏合劑層的偏光薄膜組、液晶面板及液晶顯示裝置
JP6420274B2 (ja) 硬化性接着剤組成物及びそれを用いた偏光板
JP6343057B1 (ja) プロテクトフィルム付偏光板及び光学積層体
KR102593816B1 (ko) 광학 적층체 및 그 광학 적층체를 사용한 화상 표시 장치
WO2023149253A1 (fr) Procédé de production d'une plaque de polarisation composite
WO2020213494A1 (fr) Stratifié optique et dispositif d'affichage d'image
JP7420700B2 (ja) 光学積層体及び表示装置
JP2017090894A (ja) 偏光板及び液晶表示装置
WO2023238668A1 (fr) Procédé de fabrication de plaque de polarisation composite et plaque de polarisation composite
JP2001188103A (ja) 反射防止膜
JP2022179511A (ja) 光学積層体及び表示装置
KR20190010446A (ko) 광학 시트
WO2023013275A1 (fr) Plaque de polarisation équipée d'une couche de retard et dispositif d'affichage d'image l'utilisant
CN112654685B (zh) 自由基系粘接剂组合物、粘接剂层、偏振片和影像显示装置
JP2022146427A (ja) 光学積層体及び表示装置
WO2022191033A1 (fr) Plaque de polarisation
CN115989434A (zh) 图像显示面板
JP2022077996A (ja) 偏光板及びこれを含む画像表示装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application