WO2023112443A1 - 熱硬化性組成物、接着シート、プリント配線板および電子機器 - Google Patents
熱硬化性組成物、接着シート、プリント配線板および電子機器 Download PDFInfo
- Publication number
- WO2023112443A1 WO2023112443A1 PCT/JP2022/037675 JP2022037675W WO2023112443A1 WO 2023112443 A1 WO2023112443 A1 WO 2023112443A1 JP 2022037675 W JP2022037675 W JP 2022037675W WO 2023112443 A1 WO2023112443 A1 WO 2023112443A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- phenolic hydroxyl
- polyimide resin
- hydroxyl group
- acid
- Prior art date
Abstract
熱硬化性組成物は、一般式(1): の繰り返し単位を有し、フェノール性水酸基を有し、貯蔵弾性率G'が1.0×107Paとなる温度が0~90℃のいずれかにあり、X2の少なくとも一部はダイマージアミン等に由来する残基X2dを有するポリイミド樹脂(A)と、2以上の官能基を有する架橋剤(B)とを有する。架橋剤(B)は、エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)等からなる群から選択される一種以上を含み、これらをポリイミド樹脂(A)100質量部に対して0.5~10質量部含有する。
Description
本発明は、ポリイミド樹脂を含む熱硬化性組成物に関する。また、熱硬化性組成物からなる接着シート、並びにこの接着シートを用いて形成されるプリント配線板および電子機器に関する。
ポリイミド樹脂は耐熱性および耐薬品性に優れるので、電気絶縁分野、電子分野をはじめとする幅広い分野で多用されている。例えば、特許文献1には、特定の構造を有するアミド酸を含有する熱硬化性インク組成物をインクジェット塗布により塗膜とし、これを硬化処理してポリイミド膜を得る方法が開示されている。また、特許文献2には、末端変性ポリイミドと、架橋剤と、有機溶剤とを含むポリイミド系接着剤が開示されている。この末端変性ポリイミドには、芳香族テトラカルボン酸無水物およびダイマージアミンを含むモノマー群の反応物である酸無水物基末端ポリイミドと、一級モノアミンとの反応物が用いられている。
特許文献3には、芳香族テトラカルボン酸類およびダイマージアミンを特定量含むジアミン類を反応させてなるポリイミド樹脂、熱硬化性樹脂、難燃剤、並びに有機溶剤を含むポリイミド系接着剤組成物が開示されている。また、このポリイミド樹脂に更にダイマージアミンを特定量含むジアミン類で鎖伸長してなるポリイミド樹脂を用いたポリイミド系接着剤組成物が開示されている。特許文献4では、テトラカルボン酸無水物成分と、ダイマー構造を有するジアミン成分とを反応させて得られたポリイミドを含有する、特定の誘電特性を示す樹脂フィルムが開示されている。特許文献5には、脂肪族、脂環族および/又は芳香族テトラカルボン酸残基と、ダイマージアミンを含むジアミン残基とを含むポリイミド樹脂、エポキシ樹脂およびエポキシ基を硬化することのできる硬化剤を含む樹脂組成物が開示されている。特許文献6には、アミノフェノール化合物、脂肪族ジアミノ化合物、四塩基酸二無水物および芳香族ジアミノ化合物の反応物であるポリアミック酸樹脂であって、両末端にアミノ基を有するポリアミック酸樹脂のイミド化物であるポリイミド樹脂が開示されている。また、このポリイミド樹脂を用いて得られる末端変性ポリイミド樹脂を含有する樹脂組成物が開示されている。特許文献7には、硬化性樹脂と、硬化剤(イミドオリゴマーを含む)とを含有する硬化性樹脂組成物が開示されている。この硬化性樹脂組成物のTgは0℃以上25℃未満であることが好ましく、硬化後は100℃以上250℃未満であることが好ましい旨が記載されている。
電子部品の製造時のめっきプロセスなどでアルカリ水溶液や酸溶液に曝された場合に、部材間に浮きや剥離が起こりやすいという問題がある。例えば、特許文献1に開示されているアミド酸含有熱硬化性インク組成物では、ポリイミド前駆体であるポリアミド酸を用いているため保存安定性が低いという課題がある。また、当該インク組成物はで高酸価のポリアミド酸を用いていることから、めっき液耐性が不足するといった課題がある。また、特許文献2や特許文献3に開示されているポリイミド系接着剤では、アルカリ耐性が充分ではなく、アルカリ水溶液曝露時に接着剤層の剥離が生じやすいという問題がある。
一方、近年のスマートフォンやタブレット端末などの電子機器の普及に伴い、幅広い温度範囲での信頼性が求められる。特に極端な温度変化に対して高い絶縁信頼性を発現することが求められている(以下、ヒートサイクル試験後の絶縁信頼性)。例えば、特許文献2に開示されているポリイミド系接着剤では、ヒートサイクル試験後の電圧印加でイオンマイグレーションが生じやすく、短絡が生じやすく、絶縁信頼性に問題がある。特許文献4に開示されているポリイミド含有樹脂フィルムや、特許文献5に開示の樹脂組成物においても、ヒートサイクル試験後の絶縁信頼性について課題がある。
更に、近年の無線通信の高速・大容量化の進展に伴い、低誘電特性を有する液晶ポリマー(LCP)基材が注目されており、LCP基材との相性のよい材料が市場で求められている。しかし、LCP基材は熱硬化性シートと仮貼するラミネート工程において、仮貼不良が生じやすいという問題がある。例えば、特許文献6に開示されているポリイミド樹脂組成物においては、LCP基材に対するラミネート性が不足する課題がある。また、スマートフォンやタブレット端末などの電子機器の薄型化に伴い、優れた屈曲性が求められている。
本発明は上記背景に鑑みてなされたものであり、LCP基材へのラミネート性に優れ、本組成物の硬化により、めっき液耐性(耐アルカリ性および酸耐性)に優れ、屈曲性にも優れ、且つヒートサイクル試験後の絶縁信頼性に優れる硬化物が得られる熱硬化性組成物、接着シートおよびこの接着シートを用いて形成されたプリント配線板並びに電子機器を提供することを目的とする。
本発明者らが鋭意検討を重ねたところ、以下の態様において、本発明の課題を解決し得ることを見出し、本発明を完成するに至った。
[1]: ポリイミド樹脂(A)、および官能基を2以上有する架橋剤(B)を含む熱硬化性組成物であって、
ポリイミド樹脂(A)は、一般式(1):
(X1は繰り返し単位毎にそれぞれ独立に4価のテトラカルボン酸残基であり、X2は繰り返し単位毎にそれぞれ独立に2価の有機基であり、前記X1とイミド結合が互いに結合して2つのイミド環を形成する。)
で表される構造の繰り返し単位を有し、且つフェノール性水酸基を有しており、
前記X2の少なくとも一部は、ダイマージアミンおよび/又はダイマージイソシアネートに由来する残基X2dであり、
ポリイミド樹脂(A)は、貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにあり、
架橋剤(B)は、エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)、イソシアネート基含有化合物(b3)、金属キレート化合物(b4)、カルボジイミド基含有化合物(b5)およびマレイミド基含有化合物(b6)からなる群から選択される一種以上を含み、
エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)、イソシアネート基含有化合物(b3)、金属キレート化合物(b4)、カルボジイミド基含有化合物(b5)およびマレイミド基含有化合物(b6)の合計含有量が、ポリイミド樹脂(A)100質量部に対して0.5~10質量部である熱硬化性組成物。
[2]: 180℃、60分の条件で熱硬化させた後のガラス転移温度が0~70℃であることを特徴とする[1]記載の熱硬化性組成物。
[3]: 前記フェノール性水酸基として、以下の(i)~(iv)の少なくともいずれかを満たすフェノール性水酸基を含む[1]または[2]記載の熱硬化性組成物。
(i)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環のメタ位またはオルト位に、モノアミン由来のイミド環を形成する窒素原子が結合する。
(ii)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、モノアミン由来のイミド環を形成する窒素原子が結合する。
(iii)前記X2の一部が、フェノール性水酸基を有するジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に、ジアミン由来のイミド環を形成する窒素原子が結合する。
(iv)前記X2の一部が、フェノール性水酸基を有するジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、ジアミン由来のイミド環を形成する窒素原子が結合する。
[4]: ポリイミド樹脂(A)中の前記X1の少なくとも一部は、脂肪族基を有するX1aであり、当該X1100モル%に対し、前記X1aを60~100モル%有することを特徴とする[1]~[3]いずれか記載の熱硬化性組成物。
[5]: 不揮発分100質量%に対し、紫外線吸収剤(C)を0.1~10質量%含むことを特徴とする[1]~[4]いずれか記載の熱硬化性組成物。
[6]: 不揮発分100質量%に対し、フィラー(D)を3~60質量%含むことを特徴とする[1]~[5]いずれか記載の熱硬化性組成物。
[7]: [1]~[6]のいずれか記載の熱硬化性組成物からなる接着シート。
[8]: [7]記載の接着シートを用いて形成されるプリント配線板。
[9]: [8]記載のプリント配線板を有する電子機器。
[1]: ポリイミド樹脂(A)、および官能基を2以上有する架橋剤(B)を含む熱硬化性組成物であって、
ポリイミド樹脂(A)は、一般式(1):
で表される構造の繰り返し単位を有し、且つフェノール性水酸基を有しており、
前記X2の少なくとも一部は、ダイマージアミンおよび/又はダイマージイソシアネートに由来する残基X2dであり、
ポリイミド樹脂(A)は、貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにあり、
架橋剤(B)は、エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)、イソシアネート基含有化合物(b3)、金属キレート化合物(b4)、カルボジイミド基含有化合物(b5)およびマレイミド基含有化合物(b6)からなる群から選択される一種以上を含み、
エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)、イソシアネート基含有化合物(b3)、金属キレート化合物(b4)、カルボジイミド基含有化合物(b5)およびマレイミド基含有化合物(b6)の合計含有量が、ポリイミド樹脂(A)100質量部に対して0.5~10質量部である熱硬化性組成物。
[2]: 180℃、60分の条件で熱硬化させた後のガラス転移温度が0~70℃であることを特徴とする[1]記載の熱硬化性組成物。
[3]: 前記フェノール性水酸基として、以下の(i)~(iv)の少なくともいずれかを満たすフェノール性水酸基を含む[1]または[2]記載の熱硬化性組成物。
(i)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環のメタ位またはオルト位に、モノアミン由来のイミド環を形成する窒素原子が結合する。
(ii)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、モノアミン由来のイミド環を形成する窒素原子が結合する。
(iii)前記X2の一部が、フェノール性水酸基を有するジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に、ジアミン由来のイミド環を形成する窒素原子が結合する。
(iv)前記X2の一部が、フェノール性水酸基を有するジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、ジアミン由来のイミド環を形成する窒素原子が結合する。
[4]: ポリイミド樹脂(A)中の前記X1の少なくとも一部は、脂肪族基を有するX1aであり、当該X1100モル%に対し、前記X1aを60~100モル%有することを特徴とする[1]~[3]いずれか記載の熱硬化性組成物。
[5]: 不揮発分100質量%に対し、紫外線吸収剤(C)を0.1~10質量%含むことを特徴とする[1]~[4]いずれか記載の熱硬化性組成物。
[6]: 不揮発分100質量%に対し、フィラー(D)を3~60質量%含むことを特徴とする[1]~[5]いずれか記載の熱硬化性組成物。
[7]: [1]~[6]のいずれか記載の熱硬化性組成物からなる接着シート。
[8]: [7]記載の接着シートを用いて形成されるプリント配線板。
[9]: [8]記載のプリント配線板を有する電子機器。
本発明によれば、LCP基材へのラミネート性に優れ、本組成物の硬化により、めっき液耐性(耐アルカリ性および酸耐性)に優れ、且つヒートサイクル試験後の絶縁信頼性に優れる硬化物が得られる熱硬化性組成物、接着シートおよび、この接着シートを用いて形成されたプリント配線板並びに電子機器を提供できるという優れた効果を奏する。
以下、本発明について詳細に説明する。なお、本発明の趣旨に合致する限り、他の実施形態も本発明の範疇に含まれることは言うまでもない。また、本明細書において「~」を用いて特定される数値範囲は、「~」の前後に記載される数値を下限値および上限値の範囲として含むものとする。また、本明細書において「フィルム」や「シート」は同義であり、厚みによって区別されないものとする。また、本明細書中に出てくる各種成分は特に注釈しない限り、それぞれ独立に一種単独でも二種以上を併用してもよい。本明細書に記載する数値は、後述する[実施例]に記載の方法にて得られる値をいう。
1.熱硬化性組成物
本実施形態に係る熱硬化性組成物(以下、本組成物ともいう)は、ポリイミド樹脂(A)、および官能基を2以上有する架橋剤(B)を含有する。
ポリイミド樹脂(A)は、下記一般式(1)で表される構造の繰り返し単位を有し、且つフェノール性水酸基を有する。
式(1)中のX1は繰り返し単位毎にそれぞれ独立に4価のテトラカルボン酸残基であり、X2は繰り返し単位毎にそれぞれ独立に2価の有機基を表す。X1とイミド結合は互いに結合して2つのイミド環を形成する。前記X2の少なくとも一部は、ダイマージアミンおよび/又はダイマージイソシアネートに由来する残基X2d(以下、ダイマー構造ともいう)である。
本実施形態に係る熱硬化性組成物(以下、本組成物ともいう)は、ポリイミド樹脂(A)、および官能基を2以上有する架橋剤(B)を含有する。
ポリイミド樹脂(A)は、下記一般式(1)で表される構造の繰り返し単位を有し、且つフェノール性水酸基を有する。
本明細書において、「テトラカルボン酸残基」とは、テトラカルボン酸、並びにテトラカルボン酸二無水物およびテトラカルボン酸ジエステル等のテトラカルボン酸誘導体(以下、これらを「テトラカルボン酸類」という)に由来する基をいい、上記式(1)において「有機基」とはテトラカルボン酸類と反応する官能基を有する有機化合物に由来する基をいう。テトラカルボン酸類と前記有機化合物の反応によりイミド結合が得られる。前記有機化合物の好適例として、ジアミン、ジイソシアネートが例示できる。
「イミド結合」とは、1つの窒素原子と2つのカルボニル結合(C=O)からなるものとし、イミド結合と式(1)中のX1の一部が互いに結合してイミド環を形成する。「イミド環」は、イミド結合を有する環であり、1つの環を形成する元素数が4以上、7以下である。好適には5又は6である。イミド環は他の環と縮合していてもよい。また、「酸無水物基」とは、-C(=O)-O-C(=O)-で表される基を意味し、「酸無水物環」は、酸無水物基と炭素元素が結合して形成された環をいう。
架橋剤(B)は、エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)、イソシアネート基含有化合物(b3)、金属キレート化合物(b4)、カルボジイミド基含有化合物(b5)およびマレイミド基含有化合物(b6)(以下、(b1)~(b6)ともいう)からなる群から選択される一種以上を含む。(b1)~(b6)の合計含有量は、ポリイミド樹脂(A)100質量部に対して0.5~10質量部とする。ここで、熱硬化性組成物とは、熱硬化性樹脂を含み、加熱硬化処理により樹脂の三次元架橋構造を形成して硬化する組成物をいう。なお、本明細書において硬化物とは、更に加熱しても実質的に硬化反応が進行しない程度に硬化された状態をいう。熱硬化性組成物をシート等の所望の形状に成形する際に、その一部が硬化反応し得るが、更に加熱すれば硬化し得る状態は、ここでいう硬化物には含まない。熱硬化性組成物の段階で、成分の一部が半硬化したBステージの状態であってもよい。
従来、LCP基材は仮貼不良が生じやすく、低温・短時間でのラミネートが可能な組成物が求められていた。本組成物は上記構成を有しているので、LCP基材へのラミネート性に優れる。これは、貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにある柔軟性の高い樹脂を用いる効果と、フェノール性水酸基によるLCP基材への親和性効果と、ダイマー構造による濡れ性の高さによる相乗効果によると考えられる。本組成物より形成した熱硬化性シートはLCP基材に対して、例えば、90~100℃程度の低温×60~120秒程度の加温時間でも優れたラミネート性を有する熱硬化性組成物を提供できる。
また、本組成物は上記構成を有しているので、耐アルカリ性および酸耐性(以下、纏めてめっき液耐性ともいう)に優れる硬化物が得られる。なお、本明細書における耐アルカリ性および耐酸性は、後述する実施例において記載した評価に対する耐性をいう。特に、ダイマー構造を有し、且つ貯蔵弾性率G’が1.0×107Paとなる温度が前記特定範囲にあり、フェノール性水酸基を導入したポリイミド樹脂(A)により、硬化物のめっき液耐性を顕著に高めることができる。これは、(b1)~(b6)のいずれかを架橋剤(B)として含むことにより、ポリイミド樹脂(A)のフェノール性水酸基と架橋剤(B)との間に架橋構造を形成でき、当該架橋近傍におけるフェノール性水酸基の芳香環とポリイミド樹脂(A)のイミド環とが相互作用することによる効果であると考えられる。また、ポリイミド樹脂(A)のフェノール性水酸基と架橋剤(B)とを架橋させることによって強固な架橋構造が構築されることによる効果であると考えられる。
なお、熱硬化によりポリイミド樹脂(A)中の反応性官能基が架橋剤(B)と架橋されるが、その一部は架橋せずに反応性官能基のまま残存する場合がある。残存する官能基がフェノール性水酸基の場合、例えば、酸無水物基、カルボキシ基および/又はアミノ基が残存する場合に比べて耐酸性および耐アルカリ性を向上させることができる。また、フェノール性水酸基と共に酸無水物基、カルボキシ基および/又はアミノ基を併用する場合においても、カルボキシ基等の残存量をより低減できるので、耐酸性および耐アルカリ性向上効果が期待できる。
なお、熱硬化によりポリイミド樹脂(A)中の反応性官能基が架橋剤(B)と架橋されるが、その一部は架橋せずに反応性官能基のまま残存する場合がある。残存する官能基がフェノール性水酸基の場合、例えば、酸無水物基、カルボキシ基および/又はアミノ基が残存する場合に比べて耐酸性および耐アルカリ性を向上させることができる。また、フェノール性水酸基と共に酸無水物基、カルボキシ基および/又はアミノ基を併用する場合においても、カルボキシ基等の残存量をより低減できるので、耐酸性および耐アルカリ性向上効果が期待できる。
更に、本組成物は上記構成を有しているので、ヒートサイクル試験後も絶縁信頼性に優れる硬化物が得られる。前記貯蔵弾性率G’の条件を満たし、更に、炭化水素鎖や環構造を有している、分子鎖間の相互作用が少ないダイマー構造を有するポリイミド樹脂(A)を用いることによって、平面性の高いイミド環周辺のパッキング性を適度に阻害させ、イミド環の均一な分散と柔軟性の両立を実現できる。このようなポリイミド樹脂(A)に、比較的少量の上記特定の架橋剤(B)を配合させることにより、本組成物の硬化物において、ヒートサイクル時に急激な温度変化により生じる応力を緩和してクラックの発生などを抑制できる。その結果、ヒートサイクル試験後でも優れた絶縁信頼性が実現できると考えられる。
本組成物は、例えば、熱硬化性の接着シート、熱硬化性のカバーシートをはじめとする各種シートやフィルムとして好適である。これらは、他の基材や層と本組成物により形成された層を積層して用いられる。積層方法は公知の方法を制限無く適用できる。例えば塗工する方法、ラミネートする方法がある。ラミネート法は簡便性の点で優れている。以下、本組成物の各成分および製造方法について説明する。
1-1.ポリイミド樹脂(A)
ポリイミド樹脂(A)は、前述したように、上記一般式(1)で表される構造の繰り返し単位を有し、且つフェノール性水酸基を有する。ポリイミド樹脂(A)のフェノール性水酸基の位置は特に限定されない。ポリイミド樹脂(A)は、貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにある。貯蔵弾性率G’が前記条件を満たす樹脂は、低温で軟化して流動性を向上させることができるので基材への濡れ性を高められる一方で、従来よりめっき液耐性が悪化しやすいという課題があった。本発明者らが検討を重ねた結果、前記条件の貯蔵弾性率に、フェノール性水酸基を有するポリイミド樹脂(A)を用いる本組成物によれば、前述のめっき液耐性の問題を解決できることがわかった。ポリイミド樹脂(A)は、一種単独もしくは二種以上を混合して用いることができる。
ポリイミド樹脂(A)は、前述したように、上記一般式(1)で表される構造の繰り返し単位を有し、且つフェノール性水酸基を有する。ポリイミド樹脂(A)のフェノール性水酸基の位置は特に限定されない。ポリイミド樹脂(A)は、貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにある。貯蔵弾性率G’が前記条件を満たす樹脂は、低温で軟化して流動性を向上させることができるので基材への濡れ性を高められる一方で、従来よりめっき液耐性が悪化しやすいという課題があった。本発明者らが検討を重ねた結果、前記条件の貯蔵弾性率に、フェノール性水酸基を有するポリイミド樹脂(A)を用いる本組成物によれば、前述のめっき液耐性の問題を解決できることがわかった。ポリイミド樹脂(A)は、一種単独もしくは二種以上を混合して用いることができる。
1-1-a.一般式(1)中のX1
一般式(1)中のX1は、前述したように、繰り返し単位毎にそれぞれ独立の構造を有していてよい4価のテトラカルボン酸残基である。X1を得るための重合に用いるテトラカルボン酸類は特に限定されない。テトラカルボン酸類として、芳香族基を含む芳香族テトラカルボン酸類、脂肪族基を含む脂肪族テトラカルボン酸類、および芳香族基と脂肪族基を含むテトラカルボン酸類が好適に用いられる。X1中には、窒素、酸素、硫黄、セレン、フッ素、塩素、臭素などのヘテロ原子が含まれていてもよい。テトラカルボン酸類は単独で用いても二種以上を併用してもよい。また、上記単量体の例は、適宜、置換基を有していてもよい。置換基としては、アルキル基、ハロゲン原子、ニトロ基、シアノ基等が例示できる。
一般式(1)中のX1は、前述したように、繰り返し単位毎にそれぞれ独立の構造を有していてよい4価のテトラカルボン酸残基である。X1を得るための重合に用いるテトラカルボン酸類は特に限定されない。テトラカルボン酸類として、芳香族基を含む芳香族テトラカルボン酸類、脂肪族基を含む脂肪族テトラカルボン酸類、および芳香族基と脂肪族基を含むテトラカルボン酸類が好適に用いられる。X1中には、窒素、酸素、硫黄、セレン、フッ素、塩素、臭素などのヘテロ原子が含まれていてもよい。テトラカルボン酸類は単独で用いても二種以上を併用してもよい。また、上記単量体の例は、適宜、置換基を有していてもよい。置換基としては、アルキル基、ハロゲン原子、ニトロ基、シアノ基等が例示できる。
芳香族テトラカルボン酸類としては、例えば、ピロメリット酸二無水物、1,2,3,4-ベンゼンテトラカルボン酸二無水物、2,3',3,4'-ビフェニルテトラカルボン酸二無水物、3,3’,4,4’-ビフェニルテトラカルボン酸二無水物、1,4,5,8-ナフタレンテトラカルボン酸二無水物、2,3,6,7-ナフタレンテトラカルボン酸二無水物、以下の一般式(2)で表されるジフタル酸二無水物が例示できる。
式中のX5は、2価の置換基を有していてもよい有機基(例えば炭素数1~10の炭化水素基)、-O-、-CO-、-SO2-、-S-、-SO2-、-CONH-、-COO-、又は-OCO-、-C(CF3)2-、-COO-Z-OCO-、-O-Ph-C(CH3)2-Ph-O-等の連結基を示す。前記Zは例えば-C6H4-、-(CH2)n-、-CH2-CH(-O-C(=O)-CH3)-CH2-が例示できる。これらは、置換基を含んでいてもよい。前記置換基としては、アルキル基、ハロゲン、カルボニル基等が例示できる。後述するテトラカルボン酸においても同様である。具体例としては、3,3’,4,4’-ベンゾフェノンテトラカルボン酸二無水物、3,3’,4,4’-ビフェニルテトラカルボン酸二無水物、3,3’,4,4’-ジフェニルスルホンテトラカルボン酸二無水物、4,4’-オキシジフタル酸無水物、4,4’-(ヘキサフルオロイソプロピリデン)ジフタル酸無水物、2,2-ビス〔4-(3,4-ジカルボキシフェノキシ)フェニル〕プロパン二無水物、p-フェニレンビス(トリメリット酸モノエステル酸無水物)、エチレングリコールビスアンヒドロトリメリテートが例示できる。
低温でのLCP基材へのラミネート性の効果的な向上と、ヒートサイクル後の絶縁信頼性をより向上させる観点からは、一般式(1)中のX1の少なくとも一部は脂肪族基を有するX1aとすることが好ましい。なお、X1aは脂肪族基を有していればよく、芳香族基が含まれていてもよい。
脂肪族基を有するテトラカルボン酸類としては、芳香族基を含んでいてもよい、鎖状炭化水素構造および/又は脂環式炭化水素構造がある。「鎖状炭化水素構造」は、不飽和結合を有していてもよい、直鎖状炭化水素構造および/又は分岐状炭化水素構造である。また、「脂環式炭化水素構造」は、不飽和結合を有していてもよい、脂環式炭化水素であり、単環であっても多環であってもよい。これらは、置換基を含んでいてもよい。
脂肪族基を有するテトラカルボン酸類の具体例として、1,2,3,4-ブタンテトラカルボン酸、1,2,3,4-ペンタンテトラカルボン酸、1,2,4,5-ペンタンテトラカルボン酸、1,2,3,4-ヘキサンテトラカルボン酸、1,2,5,6-ヘキサンテトラカルボン酸等の鎖状炭化水素構造を有するテトラカルボン酸二無水物が例示できる。
また、シクロブタン-1,2,3,4-テトラカルボン酸、シクロペンタン-1,2,3,4-テトラカルボン酸、シクロヘキサン-1,2,3,4-テトラカルボン酸、シクロヘキサン-1,2,4,5-テトラカルボン酸、1-カルボキシメチル-2,3,5-シクロペンタントリカルボン酸、3-カルボキシメチル-1,2,4-シクロペンタントリカルボン酸、rel-ジシクロヘキシル-3,3’,4,4’-テトラカルボン酸、トリシクロ[4.2.2.02,5]デカ-9-エン-3,4,7,8-テトラカルボン酸、5-カルボキシメチルビシクロ[2.2.1]ヘプタン-2,3,6-トリカルボン酸、ビシクロ[2.2.1]ヘプタン-2,3,5,6-テトラカルボン酸、ビシクロ[2.2.2]オクタ-7-エン-2,3,6,7-テトラカルボン酸、ビシクロ[3.3.0]オクタン-2,4,6,7-テトラカルボン酸、7,8-ジフェニルビシクロ[2.2.2]オクタ-7-エン-2,3,5,6-テトラカルボン酸、4,8-ジフェニル-1,5-ジアザビシクロオクタン-2,3,6,7-テトラカルボン酸、9-オキサトリシクロ[4.2.1.02,5]ノナン-3,4,7,8-テトラカルボン酸、9,14-ジオキソペンタシクロ[8.2.11,11.14,7.02,10.03,8]テトラデカン-5,6,12,13-テトラカルボン酸等のシクロ、ビシクロ、トリシクロテトラカルボン酸;2,8-ジオキサスピロ[4.5]デカン-1,3,7,9-テロトン等のスピロ環含有テトラカルボン酸;5-(2,5-ジオキソテトラヒドロフリル)-3-メチル-3-シクロヘキセン-1,2-ジカルボン酸無水物、1,3,3a,4,5,9b-ヘキサヒドロ-5(テトラヒドロ-2,5-ジオキソ-3-フラニル)ナフト[1,2-c]フラン-1,3-ジオン、4-(2,5-ジオキソテトラヒドロフラン-3-イル)-1,2,3,4-テトラヒドロナフタレン-1,2-ジカルボン酸無水物)等の脂環式炭化水素構造を有するテトラカルボン酸二無水物が例示できる。
また、シクロブタン-1,2,3,4-テトラカルボン酸、シクロペンタン-1,2,3,4-テトラカルボン酸、シクロヘキサン-1,2,3,4-テトラカルボン酸、シクロヘキサン-1,2,4,5-テトラカルボン酸、1-カルボキシメチル-2,3,5-シクロペンタントリカルボン酸、3-カルボキシメチル-1,2,4-シクロペンタントリカルボン酸、rel-ジシクロヘキシル-3,3’,4,4’-テトラカルボン酸、トリシクロ[4.2.2.02,5]デカ-9-エン-3,4,7,8-テトラカルボン酸、5-カルボキシメチルビシクロ[2.2.1]ヘプタン-2,3,6-トリカルボン酸、ビシクロ[2.2.1]ヘプタン-2,3,5,6-テトラカルボン酸、ビシクロ[2.2.2]オクタ-7-エン-2,3,6,7-テトラカルボン酸、ビシクロ[3.3.0]オクタン-2,4,6,7-テトラカルボン酸、7,8-ジフェニルビシクロ[2.2.2]オクタ-7-エン-2,3,5,6-テトラカルボン酸、4,8-ジフェニル-1,5-ジアザビシクロオクタン-2,3,6,7-テトラカルボン酸、9-オキサトリシクロ[4.2.1.02,5]ノナン-3,4,7,8-テトラカルボン酸、9,14-ジオキソペンタシクロ[8.2.11,11.14,7.02,10.03,8]テトラデカン-5,6,12,13-テトラカルボン酸等のシクロ、ビシクロ、トリシクロテトラカルボン酸;2,8-ジオキサスピロ[4.5]デカン-1,3,7,9-テロトン等のスピロ環含有テトラカルボン酸;5-(2,5-ジオキソテトラヒドロフリル)-3-メチル-3-シクロヘキセン-1,2-ジカルボン酸無水物、1,3,3a,4,5,9b-ヘキサヒドロ-5(テトラヒドロ-2,5-ジオキソ-3-フラニル)ナフト[1,2-c]フラン-1,3-ジオン、4-(2,5-ジオキソテトラヒドロフラン-3-イル)-1,2,3,4-テトラヒドロナフタレン-1,2-ジカルボン酸無水物)等の脂環式炭化水素構造を有するテトラカルボン酸二無水物が例示できる。
低温でのLCP基材へのラミネート性をより効果的に向上させる観点からは、脂肪族基を有するX1aが以下の(I)および(II)の少なくとも一方を満たす構造Sを有することが好ましい。
(I)一般式(1)中のイミド環を構成するX1であるX1a中の炭素の少なくとも一つが、他方のイミド環を構成するX1a中の炭素の少なくとも一つと互いに直結する。
(II)一般式(1)中の2つのイミド環それぞれを構成する、X1であるX1a中の炭素の少なくとも一つが、それぞれ独立に、鎖状炭化水素構造または脂環式炭化水素構造と直結する、および脂環式炭化水素構造の構成元素の一つであるのいずれかを満たす。
上記(I)を満たす具体例として、化学式(I-a)~(I-d)が例示できる。なお、化学式(I-b)~(I-d)は上記(II)を満たす化合物でもある。式中の*は、イミド基との結合部位を示す。
(I)一般式(1)中のイミド環を構成するX1であるX1a中の炭素の少なくとも一つが、他方のイミド環を構成するX1a中の炭素の少なくとも一つと互いに直結する。
(II)一般式(1)中の2つのイミド環それぞれを構成する、X1であるX1a中の炭素の少なくとも一つが、それぞれ独立に、鎖状炭化水素構造または脂環式炭化水素構造と直結する、および脂環式炭化水素構造の構成元素の一つであるのいずれかを満たす。
上記(I)を満たす具体例として、化学式(I-a)~(I-d)が例示できる。なお、化学式(I-b)~(I-d)は上記(II)を満たす化合物でもある。式中の*は、イミド基との結合部位を示す。
上記(II)を満たす具体例として、化学式(II-a)~(II-v)が例示できる。
イミド環を形成するX1a中の炭素が鎖状炭化水素構造に直結する、構造Sを有するX1aの例として化学式(II-a)で表される化合物が例示できる。イミド環を形成するX1中の炭素が、脂環式炭化水素構造の構成元素の一つとなる、構造Sを有するX1aの例として化学式(II-b)で表される化合物が例示できる。また、一方のイミド環を形成するX1aの炭素が、脂環式炭化水素構造に直結し、他方のイミド環を形成するX1a中の炭素が、脂環式炭化水素構造の構成元素の一つとなる、構造Sを有するX1aの例として、化学式(II-c)が例示できる。なお、2つのイミド環がそれぞれ独立に、上記(I)および(II)の少なくともいずれかを満たしていればよく、化学式(II-d)に示すように芳香環が含まれていてもよい。
脂肪族基を有するX1aの割合は、ポリイミド樹脂(A)を構成するX1100モル%に対して、60~100モル%が好適であり、より好ましい範囲は75~100モル%、更に好ましい範囲は85~100モル%である。脂肪族基を有するX1aを60~100モル%用いることにより、LCPへのラミネート性がより優れたものとなる。脂肪族基を有するX1aの割合は、ポリイミド樹脂(A)を合成する際に使用する原料モノマーのうち、X1残基となる全単量体100モル%中に対する、脂肪族基を有するX1aが残基となる単量体の含有率(モル%)より求めることができる。通常、合成時に用いる単量体の比率が、樹脂中の構成比率と同等になる。
1-1-b.一般式(1)中のX2
一般式(1)中のX2は、前述したように、繰り返し単位毎にそれぞれ独立の構造を有していてよい2価の有機基である。X2を得るための重合に用いる有機化合物の好適例として、前述したようにジアミン、ジイソシアネートが例示できる。X2の少なくとも一部は、ダイマージアミンおよび/又はダイマージイソシアネートに由来する残基X2dである。
一般式(1)中のX2は、前述したように、繰り返し単位毎にそれぞれ独立の構造を有していてよい2価の有機基である。X2を得るための重合に用いる有機化合物の好適例として、前述したようにジアミン、ジイソシアネートが例示できる。X2の少なくとも一部は、ダイマージアミンおよび/又はダイマージイソシアネートに由来する残基X2dである。
ダイマージアミンは、例えば、ダイマー酸のカルボキシ基をアミノ基に転化することにより得られる。また、ダイマージイソシアネートは、例えば、ダイマー酸のカルボキシ基をイソシアネート基に転化することにより得られる。ここでダイマー酸とは、不飽和脂肪族カルボン酸の二量体またはその水添物をいう。例えば、大豆油脂肪酸、トール油脂肪酸、菜種油脂肪酸等の天然の脂肪酸およびこれらを精製したリノレン酸、リノール酸、オレイン酸、エルカ酸等の不飽和脂肪酸を二量化してダイマー酸を得ることができる。不飽和結合を必要に応じて水添し、不飽和度を低下させてもよい。不飽和度を下げたダイマージアミンおよびダイマージイソシアネートは、耐酸化性(特に高温域における着色)や合成時のゲル化抑制の点で好適である。
ダイマー酸は、炭素数20~60の化合物が好ましく、炭素数24~56の化合物がより好ましく、炭素数28~48の化合物が更に好ましく、炭素数36~44の化合物が特に好ましい。脂肪酸をディールス-アルダー反応させた分岐構造を有するジカルボン酸化合物が好ましい。前記分岐構造は、脂肪鎖および環構造が好ましく、環構造がより好ましい。前記環構造は、1または2以上の芳香環や脂環構造が好ましく、脂環構造がより好ましい。環構造が2つの場合、2つの環が独立していても、連続していてもよい。ダイマージアミンおよびダイマージイソシアネートは一種または複数種の化合物を用いることができる。脂環構造は、環内に二重結合を1つまたは複数有する場合、二重結合を有さない場合などがある。ダイマー酸のカルボキシ基をアミノ基に転化する方法は、例えば、カルボン酸をアミド化させ、ホフマン転位によりアミン化させ、更に蒸留・精製を行う方法が挙げられる。また、ダイマー酸のカルボキシ基をジイソシアネート基に転化する方法は、例えば、カルボン酸からクルチウス転移によりイソシアネート化させる方法が挙げられる。
ダイマージアミン中のアミノ基、あるいはダイマージイソシアネート中のイソシアネート基は、環構造に直接結合していてもよいが、溶解性向上、柔軟性向上の観点から、当該アミノ基は脂肪族鎖を介して環構造と結合していることが好ましい。アミノ基あるいはイソシアネート基と環構造との間の炭素数は2~25であることが好ましい。脂肪族鎖の好適例として、アルキレン基等の鎖状炭化水素基が例示できる。好適な例として、当該2つのアミノ基あるいはイソシアネート基が、それぞれアルキレン基を介して環構造と結合している化合物が例示できる。
なお、ダイマージアミンあるいはダイマージイソシアネートを得るためのダイマー酸(多塩基酸)の具体例として、下記化学式(d1)~化学式(d4)が挙げられる。これらは一例であり、ダイマー酸は下記構造に限定されない。
ダイマージアミンおよびダイマージイソシアネートは、炭素数20~60の化合物が好ましく、炭素数24~56の化合物がより好ましく、炭素数28~48の化合物が更に好ましく、炭素数36~44の化合物が更に好ましい。かかる炭素数は、入手し易さの観点で好ましい。
ダイマージアミンの市販品は、例えば、クローダジャパン社製の「プリアミン1071」、「プリアミン1073」、「プリアミン1074」、「プリアミン1075」や、BASFジャパン社製の「バーサミン551」等が挙げられる。
ダイマー構造である残基X2dを得る単量体の割合は、X2残基を得る単量体100質量%あたり、80~100質量%が好ましい。80質量%以上とすることにより、低温でのLCP基材へのラミネート性がより優れたものとなる。前記のより好ましい範囲は83~100質量%であり、更に好ましい範囲は85~100質量%である。ダイマー構造を有するX2dの割合は、ポリイミド樹脂(A)を合成する際に使用する原料モノマーのうち、X2残基となる全単量体100質量%中に対する、ダイマー構造を有するX2dが残基となる単量体の含有率(質量%)より求めることができる。通常、合成時に用いる単量体の比率が、樹脂中の構成比率と同等になる。
一般式(1)中のX2として、後述するフェノール性水酸基を有するジアミンが例示できる。また、残基X2dを形成する単量体およびフェノール性水酸基を有するジアミン以外のジアミンを適宜用いることができる。例えば、置換基を有していてもよい、脂肪族基(不飽和結合が含まれていてもよい、鎖状炭化水素構造および/又は脂環式炭化水素構造)、芳香環およびこれらを任意に組み合わせたジアミン化合物が例示できる。
その他のジアミンは、例えば、1,4-ジアミノベンゼン、1,3-ジアミノベンゼン、1,2-ジアミノベンゼン、1,5-ジアミノナフタレン、1,8-ジアミノナフタレン、2,3-ジアミノナフタレン、2,6-ジアミノトルエン、2,4-ジアミノトルエン、3,4-ジアミノトルエン、4,4’-ジアミノジフェニルメタン、3,4’-ジアミノジフェニルエーテル、4,4’-ジアミノジフェニルエーテル、4,4’-ジアミノ-1,2-ジフェニルエタン、3,3’-ジアミノジフェニルメタン、3,4’-ジアミノジフェニルメタン、4,4’-ジアミノベンゾフェノン、4,4’-ジアミノジフェニルスルホン、3,3’-ジアミノベンゾフェノン、3,3’-ジアミノジフェニルスルホン等の芳香族ジアミン;エチレンジアミン、1,3-プロパンジアミン、1,4-ブタンジアミン、1,6-ヘキサンジアミン、1,7-ヘプタンジアミン、1,9-ノナンジアミン、1,12-ドデカメチレンジアミン、メタキシレンジアミン等の脂肪族ジアミン;イソホロンジアミン、ノルボルナンジアミン、1,2-シクロヘキサンジアミン、1,3-シクロヘキサンジアミン、1,4-シクロヘキサンジアミン、4,4’―ジアミノジシクロヘキシルメタン、ピペラジン等の脂環族ジアミン等が挙げられる。
1-1-c.フェノール性水酸基
ポリイミド樹脂(A)は、前述したように、フェノール性水酸基を有する。フェノール性水酸基とは、芳香環に直接結合している水酸基をいう。芳香環の好適例として、ベンゼン環、ナフタレン環、ピリジン環が例示できる。フェノール性水酸基は、ポリイミド樹脂(A)の分子鎖末端に導入したり、主鎖骨格の側鎖、側基に導入したりすることができる。フェノール性水酸基は、分子鎖末端、側基、側鎖のいずれかに導入する他、任意に組み合わせることができる。なお、分子鎖末端とは、ポリイミド樹脂(A)の分子鎖を構成する繰り返し構造単位のうち末端にあるもの、或いはその末端に連結された非繰り返し構造をいう。
ポリイミド樹脂(A)は、前述したように、フェノール性水酸基を有する。フェノール性水酸基とは、芳香環に直接結合している水酸基をいう。芳香環の好適例として、ベンゼン環、ナフタレン環、ピリジン環が例示できる。フェノール性水酸基は、ポリイミド樹脂(A)の分子鎖末端に導入したり、主鎖骨格の側鎖、側基に導入したりすることができる。フェノール性水酸基は、分子鎖末端、側基、側鎖のいずれかに導入する他、任意に組み合わせることができる。なお、分子鎖末端とは、ポリイミド樹脂(A)の分子鎖を構成する繰り返し構造単位のうち末端にあるもの、或いはその末端に連結された非繰り返し構造をいう。
ポリイミド樹脂(A)のフェノール性水酸基価は、1~30mgKOH/gが好適である。この範囲とすることにより、架橋密度を適切なものとし、めっき液耐性(耐アルカリ性および耐酸性)をより効果的に高めることができる。また、前記フェノール性水酸基価とすることにより、架橋密度を適切にして応力緩和効果を引き出し、ヒートサイクル試験後の絶縁信頼性をより効果的に高めることができる。フェノール性水酸基価は3~20mgKOH/gであることがより好ましく、5~15mgKOH/gであることが更に好ましい。フェノール性水酸基価は、フェノール性水酸基を有するモノマーの仕込み量、分子鎖末端へのフェノール性水酸基の導入率、および/又は側鎖へのフェノール性水酸基の導入率により調整できる。
ポリイミド樹脂(A)の好適例として、分子鎖末端の官能基の全てまたは一部がフェノール性水酸基であり、側基/側鎖にフェノール性水酸基を有しないポリイミド樹脂(A);分子鎖末端の官能基の全てまたは一部がフェノール性水酸基であり、側基/側鎖にもフェノール性水酸基を有するポリイミド樹脂(A);分子鎖末端を末端封鎖し、側基または側鎖にフェノール性水酸基を有するポリイミド樹脂(A);分子鎖末端を酸無水物基等の他の官能基とし、側基または側鎖にフェノール性水酸基を有するポリイミド樹脂(A)が挙げられる。これらの中でも、めっき液耐性の観点から、分子鎖末端の官能基を実質的に全てフェノール性水酸基であるポリイミド樹脂(A)、分子鎖末端が、フェノール性水酸基末端と、官能基を有しない分子鎖末端からなるポリイミド樹脂(A)が特に好ましい。ポリイミド樹脂(A)は、本発明の趣旨を逸脱しない範囲において、分子鎖末端、側基および/または側鎖に、酸無水物基、アミノ基、カルボキシ基等の他の官能基を有していてもよい。酸無水物基を含む場合には、酸無水物基価はめっき液耐性の観点から15mgKOH/g以下であることが好ましく、10mgKOH/g以下であることがより好ましく、5mgKOH/g以下であることが更に好ましい。アミノ基を含む場合には、アミン価はめっき液耐性の観点から15mgKOH/g以下であることが好ましく、10mgKOH/g以下であることがより好ましく、5mgKOH/g以下であることが更に好ましい。
1-1-c1.分子鎖末端
ポリイミド樹脂(A)の分子鎖末端にフェノール性水酸基を導入するには、酸無水物末端ポリイミド樹脂を合成した後、一般式(3)で表されるフェノール性水酸基を有するアミン化合物を更に反応させる方法が例示できる。酸無水物末端ポリイミド樹脂をカルボン酸末端ポリイミド樹脂に代えて、同様の方法によりフェノール性水酸基を導入してもよい。
一般式(3)中のArは、置換基を有していてもよい芳香族基である。置換基としては、炭素数1~10のアルキル基やフルオロアルキル基、ハロゲン原子が例示できる。一般式(3)中のアミノ基が、芳香族基に直結している化合物の他、脂肪族基を介して芳香族基に結合している化合物も好適である。後述する一般式(4)、(5)のArおよび置換基についても同様である。
ポリイミド樹脂(A)の分子鎖末端にフェノール性水酸基を導入するには、酸無水物末端ポリイミド樹脂を合成した後、一般式(3)で表されるフェノール性水酸基を有するアミン化合物を更に反応させる方法が例示できる。酸無水物末端ポリイミド樹脂をカルボン酸末端ポリイミド樹脂に代えて、同様の方法によりフェノール性水酸基を導入してもよい。
また、アミノ基末端ポリイミド樹脂を合成した後、一般式(4)で表されるフェノール性水酸基を有する酸無水物化合物、または一般式(5)で表されるフェノール性水酸基を有するカルボン酸化合物を更に反応させ、末端にフェノール性水酸基を導入する方法が例示できる。
一般式(3)の具体例として、3-アミノフェノール、4-アミノフェノール、4-アミノ-o-クレゾール、5-アミノ-o-クレゾール、4-アミノ-2,3-キシレノール、4-アミノ-2,5-キシレノール、4-アミノ-2,6-キシレノール、4-アミノ-1-ナフトール、5-アミノ-2-ナフトール、6-アミノ-1-ナフトール、4-アミノ-2,6-ジフェニルフェノールが例示できる。一般式(4)の具体例として、3-ヒドロキシフタル酸無水物、4-ヒドロキシフタル酸無水物等が挙げられる。また、一般式(5)の具体例として、サリチル酸、オキシ安息香酸が例示できる。一般式(3)~(4)では水酸基が1つの例を挙げたが、Arに水酸基が2つ以上結合している化合物を用いてもよい。
硬化物のヒートサイクル試験後の絶縁信頼性をより効果的に向上させる観点からは、以下の(i)および(ii)の少なくとも一方を満たすフェノール性水酸基を有するポリイミド樹脂(A)が好適である。
(i)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環のメタ位またはオルト位に、モノアミン由来のイミド環を形成する窒素原子が結合する。
(ii)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、モノアミン由来のイミド環を形成する窒素原子が結合する。
上記(i)および(ii)の少なくとも一方を満たすフェノール性水酸基を有することにより、本組成物の硬化物のヒートサイクル試験後の絶縁信頼性をより効果的に高めることができる。本発明者らが鋭意検討を重ねたところ、分子鎖末端のフェノール性水酸基の周辺構造は、架橋点周辺の構造となるため、応力緩和への影響が大きいことがわかった。水酸基とアミノ基の位置がオルト位またはメタ位にある(i)の構造を有することにより、イミド環と別のイミド環との相互作用が低減されて、応力緩和性が向上すると考えられる。また、アミノ基が、芳香環に直結せずに脂肪族基を介して結合する(ii)の構造を有することにより、イミド環と別のイミド環との相互作用が低減されて、応力緩和性が向上すると考えられる。
(i)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環のメタ位またはオルト位に、モノアミン由来のイミド環を形成する窒素原子が結合する。
(ii)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、モノアミン由来のイミド環を形成する窒素原子が結合する。
上記(i)および(ii)の少なくとも一方を満たすフェノール性水酸基を有することにより、本組成物の硬化物のヒートサイクル試験後の絶縁信頼性をより効果的に高めることができる。本発明者らが鋭意検討を重ねたところ、分子鎖末端のフェノール性水酸基の周辺構造は、架橋点周辺の構造となるため、応力緩和への影響が大きいことがわかった。水酸基とアミノ基の位置がオルト位またはメタ位にある(i)の構造を有することにより、イミド環と別のイミド環との相互作用が低減されて、応力緩和性が向上すると考えられる。また、アミノ基が、芳香環に直結せずに脂肪族基を介して結合する(ii)の構造を有することにより、イミド環と別のイミド環との相互作用が低減されて、応力緩和性が向上すると考えられる。
上記(i)および(ii)を満たす分子鎖末端を得るために、酸無水物基末端ポリイミド樹脂またはカルボキシ基末端ポリイミド樹脂の末端封止に用いるフェノール性水酸基を有するモノアミン化合物として、m-アミノフェノール、o-アミノフェノール、2-アミノ-5-エチルフェノール、2-(1-アミノエチル)フェノール、3-(2-アミノエチル)フェノール、4-(2-アミノエチル)フェノール、2-(2-アミノエチル)フェノール、2-(2-アミノメチル)フェノール、3-(2-アミノメチル)フェノール、2-(2-アミノメチル)フェノール、3-(2-アミノメチル)フェノール、4-(2-アミノプロピル)フェノールが例示できる。
ポリイミド樹脂(A)の分子鎖末端の官能基を実質的に全てフェノール性水酸基とすることができる。また、フェノール性水酸基末端の他、官能基を有しない分子鎖末端を含んでいてもよい。また、フェノール性水酸基末端の他、他の官能基(酸無水物基等)を有する分子鎖末端を有していてもよい。
官能基を有しない分子鎖末端とフェノール性水酸基末端を有するポリイミド樹脂(A)は、例えば、酸無水物末端ポリイミドに対し、一般式(3)のアミン化合物と、フェノール性水酸基を有しないモノアミン化合物を特定比率で混合して、末端封止反応を行うことにより得られる。また、アミン末端ポリイミドに対し、一般式(4)および/又は(5)の化合物と、フェノール性水酸基を有しない酸無水物化合物および/又はカルボン酸化合物を特定比率で混合して末端封止反応を行うことにより得てもよい。これらの方法によれば、ポリイミド樹脂(A)の分子鎖末端のフェノール性水酸基の量を容易に調整することができる。
フェノール性水酸基を有しないモノアミン化合物としては、例えば、メチルアミン、エチルアミン、プロピルアミン、ブチルアミン、ヘキシルアミン、オクチルアミン、デシルアミン、ステアリルアミン、ジメチルアミン、ジエチルアミン、ジプロピルアミンおよびジブチルアミン等の脂肪族アミン;シクロヘキシルアミンおよびジシクロヘキシルアミン等の脂環族アミン;アニリン、トルイジン、ジフェニルアミンおよびナフチルアミン等の芳香族アミン、並びにこれらの任意の混合物が例示できる。
フェノール性水酸基を有しない酸無水物としては、無水フタル酸、2,2’-ビフェニルジカルボン酸無水物、1,2-ナフタレンジカルボン酸無水物、2,3-ナフタレンジカルボン酸無水物、1.8-ナフタレンジカルボン酸無水物、1,2-アントラセンジカルボン酸無水物、2,3-アントラセンジカルボン酸無水物、L9-アントラセンジカルボン酸無水物等が挙げられる。フェノール性水酸基を有しないカルボン酸としては、上記フェノール性水酸基を有するカルボン酸からフェノール性水酸基を除いた構造を有するカルボン酸が挙げられる。
フェノール性水酸基末端と他の官能基末端を有するポリイミド樹脂(A)は、例えば、酸無水物末端ポリイミドに対し、一般式(3)のアミン化合物と、他の官能基を有するモノアミン化合物を特定比率で混合して、末端封止反応を行うことにより得られる。アミン末端ポリイミドにおいても同様に、一般式(4)および/又は(5)の化合物と、他の官能基を有する酸無水物化合物および/又はカルボン酸化合物を特定比率で混合して末端封止反応を行うことにより得られる。この方法によれば、ポリイミド樹脂(A)の分子鎖末端のフェノール性水酸基および他の官能基の量を調整することができる。他の官能基は特に限定されない。例えば、ニトロ基、シアノ基が例示できる。
他の官能基が酸無水物基の場合には、酸無水物末端ポリイミドを合成後、末端の一部にフェノール性水酸基を有するアミン化合物を反応させ、酸無水物末端の一部をフェノール性水酸基に変換してもよい。同様に、他の官能基がアミノ基の場合には、アミノ基末端ポリイミドを合成後、末端の一部にフェノール性水酸基を有する酸無水物基を一つ有する化合物を反応させる方法により合成してもよい。
上記においては、ポリイミド樹脂を合成し、次いで分子鎖末端とする化合物を反応させる例を挙げたが、ポリイミド樹脂を合成する単量体と共に分子鎖末端に導入する化合物を混合し、重合することによりポリイミド樹脂(A)を合成してもよい。この方法によれば合成工程の簡略化を図ることができる。
ヒートサイクル試験後の絶縁信頼性、およびめっき液耐性(耐アルカリ、耐酸性)をより優れたものとする観点から、ポリイミド樹脂(A)の分子鎖末端の官能基100モル%に対し、フェノール性水酸基を有する分子鎖末端は50~100モル%が好ましく、70~100モル%であることがより好ましい。ポリイミド樹脂(A)の分子鎖末端にフェノール性水酸基を導入することにより、架橋剤(B)との架橋密度を適切なものとし応力緩和効果を効果的に引き出すことができる。その結果、ヒートサイクル試験後の絶縁信頼性を良好に保つことができると考えられる。
1-1-c2.側鎖・側基
ポリイミド樹脂(A)の側鎖および/又は側基にフェノール性水酸基を導入するには、フェノール性水酸基を有するジアミン、ジイソシアネートなどの有機化合物および/又はフェノール性水酸基を有するテトラカルボン酸類を用いる方法が好適である。また、ポリイミド樹脂を合成後、フェノール性水酸基を有する化合物を側鎖に導入してもよい。側鎖にフェノール性水酸基を導入する場合には、側鎖のフェノール性水酸基価は適宜設計可能であるが、めっき液耐性およびヒートサイクル後の絶縁信頼性をより効果的に発揮させる観点からは1~5mgKOH/gが好適である。
ポリイミド樹脂(A)の側鎖および/又は側基にフェノール性水酸基を導入するには、フェノール性水酸基を有するジアミン、ジイソシアネートなどの有機化合物および/又はフェノール性水酸基を有するテトラカルボン酸類を用いる方法が好適である。また、ポリイミド樹脂を合成後、フェノール性水酸基を有する化合物を側鎖に導入してもよい。側鎖にフェノール性水酸基を導入する場合には、側鎖のフェノール性水酸基価は適宜設計可能であるが、めっき液耐性およびヒートサイクル後の絶縁信頼性をより効果的に発揮させる観点からは1~5mgKOH/gが好適である。
フェノール性水酸基を有するジアミンの好適例として、ビス(3-アミノ-4-ヒドロキシフェニル)ヘキサフルオロプロパン、ビス(3-アミノ-4-ヒドロキシフェニル)スルホン、ビス(3-アミノ-4-ヒドロキシフェニル)プロパン、ビス(3-アミノ-4-ヒドロキシフェニル)メチレン、ビス(3-アミノ-4-ヒドロキシフェニル)エーテル、ビス(3-アミノ-4-ヒドロキシ)ビフェニル、2,2’-ジトリフルオロメチル-5,5’-ジヒドロキシル-4,4’-ジアミノビフェニル、ビス(3-アミノ-4-ヒドロキシフェニル)フルオレン、2,2’-ビス(トリフルオロメチル)-5,5’-ジヒドロキシベンジジンなどの芳香族ジアミンが挙げられる。また、これらの化合物の任意の位置に置換基が導入されていてもよい。
式中R1は、直接結合、または炭素、水素、酸素、窒素、硫黄、またはハロゲンを含む基を示す。前記基は、例えば、炭素数1~30の2価の炭化水素基またはハロゲン原子によって水素の一部若しくは全部が置換されている炭素数1~30の2価の炭化水素基、-(C=O)-、―SO2-、-O-、-S-、―NH-(C=O)-、―(C=O)-O-、下記一般式(7)で表される基および下記一般式(8)で示す基が挙げられる。式中、rおよびsはそれぞれ独立に1~20の整数を示し、R2は水素原子またはメチル基を示す。
一般式(6)で示すジアミンは、例えば2,2-ビス(3-アミノ-4-ヒドロキシフェニル)プロパン、9,9-ビス(3-アミノ-4-ヒドロキシフェニル)フルオレン、2,2-ビス(3-アミノ-4-ヒドロキシフェニル)ヘキサフルオロプロパン、4,4’-ジアミノ-3,3’-ジヒドロキシビスフェニル等が挙げられる。
フェノール性水酸基を有するテトラカルボン酸類の好適例として、後述する芳香族系のテトラカルボン酸類の芳香族基の置換基に水酸基を有する化合物が例示できる。
これらの中でも、めっき液耐性をより効果的に向上させる観点からは、以下の(iii)および(iv)の少なくともいずれかを満たすフェノール性水酸基を含むジアミンが好適である。
(iii)一般式(1)中のX2の一部が、フェノール性水酸基を含むジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に、前記イミド環を形成するジアミン由来の窒素原子が結合する。
(iv)一般式(1)中のX2の一部が、フェノール性水酸基を有するジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、前記イミド環を形成するジアミン由来の窒素原子が結合する。
上記(iii)又は(iv)の少なくとも一方を満たすフェノール性水酸基を有することにより、本組成物の硬化物のめっき液耐性およびヒートサイクル後の絶縁信頼性をより効果的に高めることができる。架橋剤(B)との架橋点をポリイミド樹脂(A)の側基とすることにより、効果的に架橋構造を形成できる。
(iii)一般式(1)中のX2の一部が、フェノール性水酸基を含むジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に、前記イミド環を形成するジアミン由来の窒素原子が結合する。
(iv)一般式(1)中のX2の一部が、フェノール性水酸基を有するジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、前記イミド環を形成するジアミン由来の窒素原子が結合する。
上記(iii)又は(iv)の少なくとも一方を満たすフェノール性水酸基を有することにより、本組成物の硬化物のめっき液耐性およびヒートサイクル後の絶縁信頼性をより効果的に高めることができる。架橋剤(B)との架橋点をポリイミド樹脂(A)の側基とすることにより、効果的に架橋構造を形成できる。
1-1-d.その他の単量体
ポリイミド樹脂(A)には、本発明の趣旨を逸脱しない範囲において、X1残基、X2残基以外の単量体に由来する残基が含まれていてもよい。例えば、アミノ基を3以上有するポリアミン化合物を用いてもよい。アミノ基を3つ以上有するポリアミン化合物としては、例えば、1,2,4-トリアミノベンゼン、3,4,4’-トリアミノジフェニルエーテルが挙げられる。
ポリイミド樹脂(A)には、本発明の趣旨を逸脱しない範囲において、X1残基、X2残基以外の単量体に由来する残基が含まれていてもよい。例えば、アミノ基を3以上有するポリアミン化合物を用いてもよい。アミノ基を3つ以上有するポリアミン化合物としては、例えば、1,2,4-トリアミノベンゼン、3,4,4’-トリアミノジフェニルエーテルが挙げられる。
1-1-e.ポリイミド樹脂(A)の製造方法
ポリイミド樹脂(A)は、各種公知の方法により製造できる。具体例として、ポリイミド前駆体であるポリアミド酸樹脂、またはポリアミド酸エステル樹脂を加熱により環化してイミド基に変換する方法が挙げられる。ポリアミド酸樹脂の合成法は、例えば、テトラカルボン酸二無水物とジアミンを反応させる方法がある。より具体的には、テトラカルボン酸二無水物とジアミンを含む単量体を溶媒に溶解させて例えば60~120℃の温度で0.1~2時間撹拌して、重合させることでポリイミド前駆体であるポリアミド酸樹脂を製造できる。テトラカルボン酸類とジアミン等との当量比(モル比)は例えば0.7~1.3であり、好ましくは0.8~1.2である。また、テトラカルボン酸二無水物とジイソシアネートを反応させてポリイミド前駆体を得、続いてポリイミド樹脂を得る方法も好適である。
ポリイミド樹脂(A)は、各種公知の方法により製造できる。具体例として、ポリイミド前駆体であるポリアミド酸樹脂、またはポリアミド酸エステル樹脂を加熱により環化してイミド基に変換する方法が挙げられる。ポリアミド酸樹脂の合成法は、例えば、テトラカルボン酸二無水物とジアミンを反応させる方法がある。より具体的には、テトラカルボン酸二無水物とジアミンを含む単量体を溶媒に溶解させて例えば60~120℃の温度で0.1~2時間撹拌して、重合させることでポリイミド前駆体であるポリアミド酸樹脂を製造できる。テトラカルボン酸類とジアミン等との当量比(モル比)は例えば0.7~1.3であり、好ましくは0.8~1.2である。また、テトラカルボン酸二無水物とジイソシアネートを反応させてポリイミド前駆体を得、続いてポリイミド樹脂を得る方法も好適である。
分子鎖末端にフェノール性水酸基を導入する場合、ポリアミド酸樹脂を合成する段階で導入しても、ポリイミド樹脂を得てから導入してもよい。後述するポリアミド酸エステル樹脂を経由する場合も同様である。側鎖または側基にフェノール性水酸基を導入する場合、ポリイミド樹脂(A)を重合するための単量体にフェノール性水酸基を有する化合物を用いる方法、ポリイミド樹脂前駆体またはポリイミド樹脂を合成した後に、側鎖または側基にフェノール性水酸基を導入する方法がある。
ポリアミド酸エステル樹脂の合成法は、テトラカルボン酸二無水物とアルコールとによりジエステルを得、次いで縮合剤の存在下でジアミンと反応させる方法や、テトラカルボン酸二無水物とアルコールとによりジエステルを得、次いで、残りのジカルボン酸を酸クロリド化し、ジアミンと反応させる方法が例示できる。
重合に用いる有機溶媒としては、例えば、N-メチル-2-ピロリドン(NMP)、2-ブタノン、ジメチルスルホキシド(DMSO)、N,N-ジメチルホルムアミド(DMF)、N,N-ジメチルアセトアミド(DMAc)、N,N-ジエチルアセトアミド、ヘキサメチルホスホルアミド、N-メチルカプロラクタム、硫酸ジメチル、シクロヘキサノン、ジオキサン、テトラヒドロフラン、ジグライム、トリグライム、クレゾールが例示できる。溶媒は単独若しくは二種以上を併用して用いられる。キシレン、トルエンのような芳香族炭化水素の併用も可能である。
ポリイミド前駆体をイミド化させてポリイミド樹脂を得る方法は、特に制限されないが、溶媒中で、例えば、80~400℃の温度で0.5~50時間加熱する方法が例示できる。このとき、必要に応じて触媒および/又は脱水剤を用いてもよい。反応触媒として、トリエチルアミン等の脂肪族第3級アミン類、ジメチルアニリン等の芳香族第3級アミン類、ピリジン、ピコリン、イソキノリン等の複素環式第3級アミン類等が例示できる。また、脱水剤としては、例えば無水酢酸等の脂肪族酸無水物や無水安息香酸等の芳香族酸無水物が例示できる。
イミド化率(イミド環の形成率)は限定されないが、めっき液耐性(耐アルカリ性および耐酸性)を効果的に発揮させる観点からは80%以上であることが好ましく、90%以上であることがより好ましく、95~100%であることが更に好ましい。NMRやIR分析等によりイミド化率を決定できる。
1-1-f.ポリイミド樹脂(A)の特性
ポリイミド樹脂(A)は、その貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにある。めっき液耐性をより優れたものとする観点からは、貯蔵弾性率G’が1.0×107Paとなる温度が30~80℃のいずれかにあることがより好ましく、30~70℃にあることが更に好ましい。また、屈曲性をより優れたものとする観点からは、貯蔵弾性率G’が1.0×107Paとなる温度が0℃以上、30℃未満のいずれかにあることが好ましく、10℃以上、25℃以下のいずれかにあることが更に好ましい。ポリイミド樹脂(A)の配合量は任意であるが、LCP基材へのラミネート性をより優れたものとするために、本組成物の固形分(不揮発分)100質量%に対し50~98質量%含まれていることが好ましい。
ポリイミド樹脂(A)は、その貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにある。めっき液耐性をより優れたものとする観点からは、貯蔵弾性率G’が1.0×107Paとなる温度が30~80℃のいずれかにあることがより好ましく、30~70℃にあることが更に好ましい。また、屈曲性をより優れたものとする観点からは、貯蔵弾性率G’が1.0×107Paとなる温度が0℃以上、30℃未満のいずれかにあることが好ましく、10℃以上、25℃以下のいずれかにあることが更に好ましい。ポリイミド樹脂(A)の配合量は任意であるが、LCP基材へのラミネート性をより優れたものとするために、本組成物の固形分(不揮発分)100質量%に対し50~98質量%含まれていることが好ましい。
貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにあるポリイミド樹脂(A)は、繰り返し構造単位となる単量体の種類、およびMwにより調整できる。具体的には、単量体としてダイマー構造などの柔軟性を有する単量体と、脂肪族(脂環式骨格含む)を有する構造を組み合わせることにより貯蔵弾性率G’が低下する傾向にあり、逆に平面性の高い芳香族骨格にイミド構造が直接結合した構造を組み合わせると貯蔵弾性率G’が大きくなる傾向にある。また、Mwを低下させることにより、貯蔵弾性率G’が低下する傾向にある。前記に加え、テトラカルボン酸類の酸無水物基当量を80~300程度とする方法と、ジアミン成分中のダイマージアミンの割合を60~100モル%とする方法とを組み合わせることも有効である。なお、テトラカルボン酸類は、水分で酸無水物基が開環することがあるため、酸無水物基当量を測定時は、適宜、サンプルを乾燥させてから測定するものとする。剛直なポリイミド樹脂、例えば、ピロメリット酸とジアミノビフェニルよりなるポリイミド樹脂の90℃の貯蔵弾性率G’は凡そ1.0×109であり、柔軟なポリイミド樹脂、例えば、ダイマージアミンと1,2,4,5-シクロヘキサンテトラカルボン酸二無水物よりなるポリイミド樹脂の90℃の貯蔵弾性率G’は凡そ1.0×105である。
ポリイミド樹脂(A)の重量平均分子量(Mw)は特に限定されないが、硬化物のヒートサイクル試験後の絶縁信頼性向上の観点から1.5万以上であることが好ましく2万以上で有ることがより好ましい。Mwの上限値は特に限定されないが、溶液粘度の扱いやすさの観点から100万であることが好ましく、10万であることがより好ましく、8万であることが更に好ましい。
1-2.架橋剤(B)
架橋剤(B)は、熱硬化処理により架橋構造を形成する化合物であり、架橋性の官能基を2以上有する。架橋剤(B)は、エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)、イソシアネート基含有化合物(b3)、金属キレート化合物(b4)、カルボジイミド基含有化合物(b5)およびマレイミド基含有化合物(b6)からなる群から選択される一種以上を含む。(b1)~(b6)は一種を単独で用いても二種以上を併用して用いてもよい。上記(b1)~(b6)を含んでいればよく、本発明の趣旨を逸脱しない範囲で他の架橋剤を併用してもよい。(b1)~(b6)のいずれかを架橋剤(B)として含むことにより、ポリイミド樹脂(A)のフェノール性水酸基と架橋剤(B)との間に架橋構造を形成できる。硬化物には、架橋剤(B)同士の架橋構造が含まれていてもよい。
架橋剤(B)は、熱硬化処理により架橋構造を形成する化合物であり、架橋性の官能基を2以上有する。架橋剤(B)は、エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)、イソシアネート基含有化合物(b3)、金属キレート化合物(b4)、カルボジイミド基含有化合物(b5)およびマレイミド基含有化合物(b6)からなる群から選択される一種以上を含む。(b1)~(b6)は一種を単独で用いても二種以上を併用して用いてもよい。上記(b1)~(b6)を含んでいればよく、本発明の趣旨を逸脱しない範囲で他の架橋剤を併用してもよい。(b1)~(b6)のいずれかを架橋剤(B)として含むことにより、ポリイミド樹脂(A)のフェノール性水酸基と架橋剤(B)との間に架橋構造を形成できる。硬化物には、架橋剤(B)同士の架橋構造が含まれていてもよい。
架橋剤(B)の(b1)~(b6)の合計含有量は、ポリイミド樹脂(A)100質量部に対して0.5~10質量部とする。架橋剤(B)の(b1)~(b6)の合計含有量は1~8質量部がより好ましく、2~6質量部が更に好ましく、3~5質量部が特に好ましい。架橋剤(B)は、低分子化合物であっても高分子化合物であってもよい。なお、後述する金属キレート化合物(b4)は、配位結合し得る個数を官能基数とする。例えば、Al、Ti、Zrを含む金属キレート化合物の場合、3官能成分となる。また、架橋剤(B)の平均官能基数は、同一骨格の架橋剤(B)毎に平均官能基数を算出するものとする。
架橋剤(B)100質量%中に、(b1)~(b6)を合計で30~100質量%含んでいることが好ましく、50~100質量%含んでいることがより好ましい。
LCP基材とのラミネート性、めっき液耐性、ヒートサイクル試験後の絶縁信頼性向上および硬化後のレーザー加工性をバランスよく向上させる観点からは、エポキシ基含有化合物(b1)単独、或いはエポキシ基含有化合物(b1)と、(b2)~(b6)のいずれか一種以上との併用系が好適である。また、組み合わせる架橋剤(B)同士で架橋反応が進行する組合せも好適である。
1-2-a.エポキシ基含有化合物(b1)
エポキシ基含有化合物(b1)は、エポキシ基を分子内に2以上有する化合物であればよく、特に限定されない。エポキシ基含有化合物(b1)の中でも、平均官能基数が3以上のエポキシ基を有する化合物が好適である。エポキシ基含有化合物(b1)としては、例えば、グリジシルエーテル型エポキシ樹脂、グリジシルアミン型エポキシ樹脂、グリシジルエステル型エポキシ樹脂、又は環状脂肪族(脂環型)エポキシ樹脂などのエポキシ樹脂を用いることができる。
エポキシ基含有化合物(b1)は、エポキシ基を分子内に2以上有する化合物であればよく、特に限定されない。エポキシ基含有化合物(b1)の中でも、平均官能基数が3以上のエポキシ基を有する化合物が好適である。エポキシ基含有化合物(b1)としては、例えば、グリジシルエーテル型エポキシ樹脂、グリジシルアミン型エポキシ樹脂、グリシジルエステル型エポキシ樹脂、又は環状脂肪族(脂環型)エポキシ樹脂などのエポキシ樹脂を用いることができる。
2官能のエポキシ基含有化合物(b1)としては、例えば、ジグリシジルフタレート、ジグリシジルヘキサヒドロフタレート、又はジグリシジルテトラヒドロフタレート等のグリシジルエステル型エポキシ樹脂;エポキシシクロヘキシルメチル-エポキシシクロヘキサンカルボキシレート、又はビス(エポキシシクロヘキシル)アジペートなどの環状脂肪族(脂環型)エポキシ樹脂;が挙げられる。また、ビスフェノールA型エポキシ樹脂、ビスフェノールF型エポキシ樹脂、ビスフェノールS型エポキシ樹脂、ビスフェノールAD型エポキシ樹脂が例示できる。
平均官能基数が3以上のエポキシ基含有化合物(b1)としては、トリス(グリシジルオキシフェニル)メタン、テトラキス(グリシジルオキシフェニル)エタン、グリシジルアミン型エポキシ樹脂としては、例えば、テトラグリシジルジアミノジフェニルメタン、トリグリシジルパラアミノフェノール、トリグリシジルメタアミノフェノール、又はテトラグリシジルメタキシリレンジアミン、ソルビトールポリグリシジルエーテル等が挙げられる。
また、クレゾールノボラック型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、α-ナフトールノボラック型エポキシ樹脂、ビスフェノールA型ノボラック型エポキシ樹脂、ジシクロペンタジエン型エポキシ樹脂、テトラブロムビスフェノールA型エポキシ樹脂、臭素化フェノールノボラック型エポキシ樹脂等のエポキシ基含有化合物(b1)が例示できる。
エポキシ基含有化合物(b1)としては、前記化合物を一種単独で若しくは二種以上を組み合わせて用いることができる。高接着性の観点から、ビスフェノールA型エポキシ樹脂、クレゾールノボラック型エポキシ樹脂、フェノールノボラック型エポキシ樹脂、トリス(グリシジルオキシフェニル)メタン、テトラキス(グリシジルオキシフェニル)エタン、又はテトラグリシジルメタキシリレンジアミンを用いることが好ましい。
1-2-b.シアネートエステル化合物(b2)
シアネートエステル化合物(b2)は、シアネート基を2以上有する化合物をいう。具体例としては、2,2-ビス(4-シアネートフェニル)プロパン(ビスフェノールA型シアネート樹脂)、ビス(3,5-ジメチル-4-シアネートフェニル)メタン、2,2-ビス(4-シアネートフェニル)エタン等またはこれらの誘導体等の芳香族系シアネートエステル化合物が挙げられる。これらは単独で用いても、二種以上を組み合わせてもよい。
シアネートエステル化合物(b2)は、シアネート基を2以上有する化合物をいう。具体例としては、2,2-ビス(4-シアネートフェニル)プロパン(ビスフェノールA型シアネート樹脂)、ビス(3,5-ジメチル-4-シアネートフェニル)メタン、2,2-ビス(4-シアネートフェニル)エタン等またはこれらの誘導体等の芳香族系シアネートエステル化合物が挙げられる。これらは単独で用いても、二種以上を組み合わせてもよい。
1-2-c.イソシアネート基含有化合物(b3)
イソシアネート基含有化合物(b3)は、イソシアネート基を分子内に2以上有する化合物であればよく、特に限定されるものではない。
イソシアネート基含有化合物(b3)は、イソシアネート基を分子内に2以上有する化合物であればよく、特に限定されるものではない。
1分子中にイソシアネート基を2個有するイソシアネート基含有化合物としては、具体的には、1,3-フェニレンジイソシアネート、4,4’-ジフェニルジイソシアネート、1,4-フェニレンジイソシアネート、4,4’-ジフェニルメタンジイソシアネート、2,4-トリレンジイソシアネート、2,6-トリレンジイソシアネート、4,4’-トルイジンジイソシアネート、2,4,6-トリイソシアネートトルエン、1,3,5-トリイソシアネートベンゼン、ジアニシジンジイソシアネート、4,4’-ジフェニルエーテルジイソシアネート、4,4’,4”-トリフェニルメタントリイソシアネート等の芳香族ジイソシアネート、トリメチレンジイソシアネート、テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、ペンタメチレンジイソシアネート、1,2-プロピレンジイソシアネート、2,3-ブチレンジイソシアネート、1,3-ブチレンジイソシアネート、ドデカメチレンジイソシアネート、2,4,4-トリメチルヘキサメチレンジイソシアネート等の脂肪族ジイソシアネート、ω,ω’-ジイソシアネート-1,3-ジメチルベンゼン、ω,ω’-ジイソシアネート-1,4-ジメチルベンゼン、ω,ω’-ジイソシアネート-1,4-ジエチルベンゼン、1,4-テトラメチルキシリレンジイソシアネート、1,3-テトラメチルキシリレンジイソシアネート等の芳香脂肪族ジイソシアネート、3-イソシアネートメチル-3,5,5-トリメチルシクロヘキシルイソシアネート[別名:イソホロンジイソシアネート]、1,3-シクロペンタンジイソシアネート、1,3-シクロヘキサンジイソシアネート、1,4-シクロヘキサンジイソシアネート、メチル-2,4-シクロヘキサンジイソシアネート、メチル-2,6-シクロヘキサンジイソシアネート、4,4’-メチレンビス(シクロヘキシルイソシアネート)、1,3-ビス(イソシアネートメチル)シクロヘキサン、1,4-ビス(イソシアネートメチル)シクロヘキサン等の脂環族ジイソシアネートが挙げられる。
また、1分子中にイソシアネート基を3個有するイソシアネート基含有化合物としては、芳香族ポリイソシアネート、リジントリイソシアネートなどの脂肪族ポリイソシアネート、芳香脂肪族ポリイソシアネート、脂環族ポリイソシアネート等が挙げられ、前記で説明したジイソシアネートのトリメチロールプロパンアダクト体、水と反応したビュウレット体、イソシアヌレート環を有する3量体が挙げられる。
イソシアネート基含有化合物としては、例示した種々のイソシアネート基含有化合物中のイソシアネート基がε-カプロラクタムやMEKオキシム等で保護されたブロック化イソシアネート基含有化合物を用いてもよい。具体的には、前記イソシアネート基含有化合物のイソシアネート基を、ε-カプロラクタム、メチルエチルケトン(以下、MEKという)オキシム、シクロヘキサノンオキシム、ピラゾール、フェノール等でブロックしたものなどが挙げられる。特に、イソシアヌレート環を有し、MEKオキシムやピラゾールでブロックされたヘキサメチレンジイソシアネート三量体を本発明に使用した場合、ポリイミドや銅に対する接着強度や耐熱性に優れるため、非常に好ましい。また耐熱性の観点から3以上のイソシアネート基を有していることが好ましい。
1-2-d.金属キレート化合物(b4)
金属キレート化合物(b4)は、金属と有機物からなる有機金属化合物であり、ポリイミド樹脂(A)の反応性官能基または架橋剤(B)の架橋性の官能基と反応して架橋を形成するものである。有機金属化合物の種類は特に限定されないが、有機アルミニウム化合物、有機チタン化合物、有機ジルコニウム化合物などが挙げられる。また、金属と有機物の結合は金属-酸素結合でもよく、金属-炭素結合に限定されるものではない。更に、官能基数(配位結合し得る個数)が3以上であることが耐熱性の観点から好ましい。
金属キレート化合物(b4)は、金属と有機物からなる有機金属化合物であり、ポリイミド樹脂(A)の反応性官能基または架橋剤(B)の架橋性の官能基と反応して架橋を形成するものである。有機金属化合物の種類は特に限定されないが、有機アルミニウム化合物、有機チタン化合物、有機ジルコニウム化合物などが挙げられる。また、金属と有機物の結合は金属-酸素結合でもよく、金属-炭素結合に限定されるものではない。更に、官能基数(配位結合し得る個数)が3以上であることが耐熱性の観点から好ましい。
前記有機アルミニウム化合物はアルミニウム金属キレート化合物が好ましい。アルミニウム金属キレート化合物は、例えば、エチルアセトアセテートアルミニウムジイソプロピレート、アルミニウムトリス(エチルアセトアセテート)、アルキルアセトアセテートアルミニウムジイソプロピレート、アルミニウムモノアセチルアセトネートビス(エチルアセトアセテート)、アルミニウムトリス(アセチルアセテート)、アルミニウムモノアセチルアセテートビス(エチルアセトアセテート)、アルミニウムジ-n-ブトキシドモノメチルアセトアセテート、アルミニウムジイソブトキシドモノメチルアセトアセテート、アルミニウムジ-sec-ブトキシドモノメチルアセトアセテート、アルミニウムイソプロピレート、モノsec-ブトキシアルミニウムジイソプロピレート、アルミニウム-sec-ブチレート、アルミニウムエチレート等が挙げられる。
前記有機チタン化合物はチタン金属キレート化合物が好ましい。チタン金属キレート化合物は、例えば、チタンアセチルアセトネート、チタンテトラアセチルアセトネート、チタンエチルアセトアセテート、チタンオクチレングリコレート、チタンエチルアセトアセテート、チタン-1.3-プロパンジオキシビス(エチルアセトアセテート)、ポリチタンアセチルアセチルアセトナート、テトライソプロピルチタネート、テトラノルマルブチルチタネート、ブチルチタネートダイマー、テトラオクチルチタネート、ダーシャリーアミルチタネート、テトラターシャリーブチルチタネート、テトラステアリルチタネート、チタンイソステアレート、トリ-n-ブトキシチタンモノステアレート、ジ-i-プロポキシチタンジステアレート、チタニウムステアレート、ジ-i-プロポキシチタンジイソステアレート、(2-n-ブトキシカルボニルベンゾイルオキシ)トリブトキシチタン等が挙げられる。
有機ジルコニウム化合物はジルコニウム金属キレート化合物が好ましい。ジルコニウム金属キレート化合物は、例えば、ジルコニウムテトラアセチルアセトネート、ジルコニウムトリブトキシアセチルアセトネート、ジルコニウムモノブトキシアセチルアセトネートビス(エチルアセトアセテート)、ジルコニウムジブトキシビス(エチルアセトアセテート)、ジルコニウムテトラアセチルアセトネート、ノルマルプロピルジルコネート、ノルマルブチルジルコネート、ステアリン酸ジルコニウム、オクチル酸ジルコニウム等が挙げられる。これらの中でも有機チタン化合物、有機ジルコニウム化合物が熱硬化反応性の点から好ましい。
有機ジルコニウム化合物はジルコニウム金属キレート化合物が好ましい。ジルコニウム金属キレート化合物は、例えば、ジルコニウムテトラアセチルアセトネート、ジルコニウムトリブトキシアセチルアセトネート、ジルコニウムモノブトキシアセチルアセトネートビス(エチルアセトアセテート)、ジルコニウムジブトキシビス(エチルアセトアセテート)、ジルコニウムテトラアセチルアセトネート、ノルマルプロピルジルコネート、ノルマルブチルジルコネート、ステアリン酸ジルコニウム、オクチル酸ジルコニウム等が挙げられる。これらの中でも有機チタン化合物、有機ジルコニウム化合物が熱硬化反応性の点から好ましい。
1-2-e.カルボジイミド基含有化合物(b5)
カルボジイミド基含有化合物(b5)は、分子内にカルボジイミド基を2以上有するものであれば、特に限定されない。カルボジイミド基含有化合物としては、例えば、カルボジライトV-01、V-03、V-05、V-07、V-09(日清紡ケミカル株式会社)、環状カルボジイミド(帝人株式会社)などが挙げられる。耐熱性の観点から1分子中に平均官能基数が3以上のカルボジイミド基を有するものが好ましい。
カルボジイミド基含有化合物(b5)は、分子内にカルボジイミド基を2以上有するものであれば、特に限定されない。カルボジイミド基含有化合物としては、例えば、カルボジライトV-01、V-03、V-05、V-07、V-09(日清紡ケミカル株式会社)、環状カルボジイミド(帝人株式会社)などが挙げられる。耐熱性の観点から1分子中に平均官能基数が3以上のカルボジイミド基を有するものが好ましい。
1-2-f.マレイミド基含有化合物(b6)
マレイミド基含有化合物(b6)は、マレイミド基を分子内に2以上有する化合物であればよく、特に限定されるものではないが、平均官能基数が3以上であることがより好ましい。
具体例としては、o-フェニレンビスマレイミド、m-フェニレンビスマレイミド、p-フェニレンビスマレイミド、4-メチル-1,3-フェニレンビスマレイミド、N,N’-(トルエン-2,6-ジイル)ビスマレイミド)、4,4’-ジフェニルメタンビスマレイミド、ビスフェノールAジフェニルエーテルビスマレイミド、3,3’-ジメチル-5,5’-ジエチル-4,4’-ジフェニルメタンビスマレイミド、4,4’-ジフェニルエーテルビスマレイミド、4,4’-ジフェニルスルフォンビスマレイミド、1,3-ビス(3-マレイミドフェノキシ)ベンゼン、1,3-ビス(4-マレイミドフェノキシ)ベンゼン、ポリフェニルメタンマレイミド(CASNO:67784-74-1、ホルムアルデヒドとアニリンからなるポリマーと無水マレイン酸の反応物)、N,N’-エチレンビスマレイミド、N,N’-トリメチレンビスマレイミド、N,N’-プロピレンビスマレイミド、N,N’-テトラメチレンビスマレイミド、N,N’-ペンタメチレンビスマレイミド、N,N’-(1,3-ペンタンジイル)ビス(マレインイミド)、N,N’-ヘキサメチレンビスマレイミド、N,N’-(1,7-ヘプタンジイル)ビスマレイミド、N,N’-(1,8-オクタンジイル)ビスマレイミド、N,N’-(1,9-ノタンジイル)ビスマレイミド、N,N’-(1,10-デカンジイル)ビスマレイミド、N,N’-(1,11-ウンデカンジイル)ビスマレイミド、N,N’-(1,12-ドデカンジイル)ビスマレイミド、N,N’-[(1,4-フェニレン)ビスメチレン]ビスマレイミド、N,N’-[(1,2-フェニレン)ビスメチレン]ビスマレイミド、N,N’-[(1,3-フェニレン)ビスメチレン]ビスマレイミド、1,6’-ビスマレイミド-(2,2,4-トリメチル)ヘキサン、N,N′‐[(メチルイミノ)ビス(4,1‐フェニレン)]ビスマレイミド、N,N′‐(2‐ヒドロキシプロパン‐1,3‐ジイルビスイミノビスカルボニルビスエチレン)ビスマレイミド、N,N′‐(ジチオビスエチレン)ビスマレイミド、N,N′‐[ヘキサメチレンビス(イミノカルボニルメチレン)]ビスマレイミド、N,N′‐カルボニルビス(1,4‐フェニレン)ビスマレイミド、N,N′,N′′‐[ニトリロトリス(エチレン)]トリスマレイミド、N,N’,N’’-[ニトリロトリス(4,1-フェニレン)]トリスマレイミド、N,N′‐[p‐フェニレンビス(オキシ-p-フェニレン)]ビスマレイミド、N,N′‐[メチレンビス(オキシ)ビス(2-メチル-1,4-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(オキシ-p-フェニレン)]ビス(マレインイミド)N,N′‐[ジメチルシリレンビス[(4,1-フェニレン)(1,3,4,-オキサジアゾール-5,2-ジイル)(4,1-フェニレン)]]ビスマレイミド、N,N’-[(1,3-フェニレン)ビスオキシビス(3,1-フェニレン)]ビスマレイミド、1,1’-[3’-オキソスピロ[9H-キサンテン-9,1’(3’H)-イソベンゾフラン]-3,6-ジイル]ビス(1H-ピロール-2,5-ジオン)、N,N’-(3,3’-ジクロロビフェニル-4,4’-ジイル)ビスマレイミド、N,N’-(3,3’-ジメチルビフェニル-4,4’-ジイル)ビスマレイミド、N,N’-(3,3’-ジメトキシビフェニル-4,4’-ジイル)ビスマレイミド、N,N’-[メチレンビス(2-エチル-4,1-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(2,6-ジエチル-4,1-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(2-ブロモ-6-エチル-4,1-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(2-メチル-4,1-フェニレン)]ビスマレイミド、N,N’-[エチレンビス(オキシエチレン)]ビスマレイミド、N,N’-[スルホニルビス(4,1-フェニレン)ビス(オキシ)ビス(4,1-フェニレン)]ビスマレイミド、N,N’-[ナフタレン-2,7-ジイルビス(オキシ)ビス(4,1-フェニレン)]ビスマレイミド、N,N’-[p-フェニレンビス(オキシ-p-フェニレン)]ビスマレイミド、N,N’-[(1,3-フェニレン)ビスオキシビス(3,1-フェニレン)]ビスマレイミド、N,N’-(3,6,9-トリオキサウンデカン-1,11-ジイル)ビスマレイミド、N,N’-[イソプロピリデンビス[p-フェニレンオキシカルボニル(m-フェニレン)]]ビスマレイミド、N,N’-[イソプロピリデンビス[p-フェニレンオキシカルボニル(p-フェニレン)]]ビスマレイミド、N,N’-[イソプロピリデンビス[(2,6-ジクロロベンゼン-4,1-ジイル)オキシカルボニル(p-フェニレン)]]ビスマレイミド、N,N’-[(フェニルイミノ)ビス(4,1-フェニレン)]ビスマレイミド、N,N’-[アゾビス(4,1-フェニレン)]ビスマレイミド、N,N’-[1,3,4-オキサジアゾール-2,5-ジイルビス(4,1-フェニレン)]ビスマレイミド、2,6-ビス[4-(マレインイミド-N-イル)フェノキシ]ベンゾニトリル、N,N’-[1,3,4-オキサジアゾール-2,5-ジイルビス(3,1-フェニレン)]ビスマレイミド、N,N’-[ビス[9-オキソ-9H-9-ホスファ(V)-10-オキサフェナントレン-9-イル]メチレンビス(p-フェニレン)]ビスマレイミド、N,N’-[ヘキサフルオロイソプロピリデンビス[p-フェニレンオキシカルボニル(m-フェニレン)]]ビスマレイミド、N,N’-[カルボニルビス[(4,1-フェニレン)チオ(4,1-フェニレン)]]ビスマレイミド、N,N’-カルボニルビス(p-フェニレンオキシp-フェニレン)ビスマレイミド、N,N’-[5-tert-ブチル-1,3-フェニレンビス[(1,3,4-オキサジアゾール-5,2-ジイル)(4,1-フェニレン)]]ビスマレイミド、N,N’-[シクロヘキシリデンビス(4,1-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(オキシ)ビス(2-メチル-1,4-フェニレン)]ビスマレイミド、N,N’-[5-[2-[5-(ジメチルアミノ)-1-ナフチルスルホニルアミノ]エチルカルバモイル]-1,3-フェニレン]ビスマレイミド、N,N’-(オキシビスエチレン)ビスマレイミド、N,N’-[ジチオビス(m-フェニレン)]ビスマレイミド、N,N’-(3,6,9-トリオキサウンデカン-1,11-ジイル)ビスマレイミド、N,N’-(エチレンビス-p-フェニレン)ビスマレイミド、DesignerMolecules社製のBMI-689、BMI-1500、BMI-1700、BMI-3000、BMI-5000、BMI-9000、JFEケミカル社製のODA-BMI、BAFBMIなどの多官能マレイミドを挙げることができる。
マレイミド基含有化合物(b6)は、マレイミド基を分子内に2以上有する化合物であればよく、特に限定されるものではないが、平均官能基数が3以上であることがより好ましい。
具体例としては、o-フェニレンビスマレイミド、m-フェニレンビスマレイミド、p-フェニレンビスマレイミド、4-メチル-1,3-フェニレンビスマレイミド、N,N’-(トルエン-2,6-ジイル)ビスマレイミド)、4,4’-ジフェニルメタンビスマレイミド、ビスフェノールAジフェニルエーテルビスマレイミド、3,3’-ジメチル-5,5’-ジエチル-4,4’-ジフェニルメタンビスマレイミド、4,4’-ジフェニルエーテルビスマレイミド、4,4’-ジフェニルスルフォンビスマレイミド、1,3-ビス(3-マレイミドフェノキシ)ベンゼン、1,3-ビス(4-マレイミドフェノキシ)ベンゼン、ポリフェニルメタンマレイミド(CASNO:67784-74-1、ホルムアルデヒドとアニリンからなるポリマーと無水マレイン酸の反応物)、N,N’-エチレンビスマレイミド、N,N’-トリメチレンビスマレイミド、N,N’-プロピレンビスマレイミド、N,N’-テトラメチレンビスマレイミド、N,N’-ペンタメチレンビスマレイミド、N,N’-(1,3-ペンタンジイル)ビス(マレインイミド)、N,N’-ヘキサメチレンビスマレイミド、N,N’-(1,7-ヘプタンジイル)ビスマレイミド、N,N’-(1,8-オクタンジイル)ビスマレイミド、N,N’-(1,9-ノタンジイル)ビスマレイミド、N,N’-(1,10-デカンジイル)ビスマレイミド、N,N’-(1,11-ウンデカンジイル)ビスマレイミド、N,N’-(1,12-ドデカンジイル)ビスマレイミド、N,N’-[(1,4-フェニレン)ビスメチレン]ビスマレイミド、N,N’-[(1,2-フェニレン)ビスメチレン]ビスマレイミド、N,N’-[(1,3-フェニレン)ビスメチレン]ビスマレイミド、1,6’-ビスマレイミド-(2,2,4-トリメチル)ヘキサン、N,N′‐[(メチルイミノ)ビス(4,1‐フェニレン)]ビスマレイミド、N,N′‐(2‐ヒドロキシプロパン‐1,3‐ジイルビスイミノビスカルボニルビスエチレン)ビスマレイミド、N,N′‐(ジチオビスエチレン)ビスマレイミド、N,N′‐[ヘキサメチレンビス(イミノカルボニルメチレン)]ビスマレイミド、N,N′‐カルボニルビス(1,4‐フェニレン)ビスマレイミド、N,N′,N′′‐[ニトリロトリス(エチレン)]トリスマレイミド、N,N’,N’’-[ニトリロトリス(4,1-フェニレン)]トリスマレイミド、N,N′‐[p‐フェニレンビス(オキシ-p-フェニレン)]ビスマレイミド、N,N′‐[メチレンビス(オキシ)ビス(2-メチル-1,4-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(オキシ-p-フェニレン)]ビス(マレインイミド)N,N′‐[ジメチルシリレンビス[(4,1-フェニレン)(1,3,4,-オキサジアゾール-5,2-ジイル)(4,1-フェニレン)]]ビスマレイミド、N,N’-[(1,3-フェニレン)ビスオキシビス(3,1-フェニレン)]ビスマレイミド、1,1’-[3’-オキソスピロ[9H-キサンテン-9,1’(3’H)-イソベンゾフラン]-3,6-ジイル]ビス(1H-ピロール-2,5-ジオン)、N,N’-(3,3’-ジクロロビフェニル-4,4’-ジイル)ビスマレイミド、N,N’-(3,3’-ジメチルビフェニル-4,4’-ジイル)ビスマレイミド、N,N’-(3,3’-ジメトキシビフェニル-4,4’-ジイル)ビスマレイミド、N,N’-[メチレンビス(2-エチル-4,1-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(2,6-ジエチル-4,1-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(2-ブロモ-6-エチル-4,1-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(2-メチル-4,1-フェニレン)]ビスマレイミド、N,N’-[エチレンビス(オキシエチレン)]ビスマレイミド、N,N’-[スルホニルビス(4,1-フェニレン)ビス(オキシ)ビス(4,1-フェニレン)]ビスマレイミド、N,N’-[ナフタレン-2,7-ジイルビス(オキシ)ビス(4,1-フェニレン)]ビスマレイミド、N,N’-[p-フェニレンビス(オキシ-p-フェニレン)]ビスマレイミド、N,N’-[(1,3-フェニレン)ビスオキシビス(3,1-フェニレン)]ビスマレイミド、N,N’-(3,6,9-トリオキサウンデカン-1,11-ジイル)ビスマレイミド、N,N’-[イソプロピリデンビス[p-フェニレンオキシカルボニル(m-フェニレン)]]ビスマレイミド、N,N’-[イソプロピリデンビス[p-フェニレンオキシカルボニル(p-フェニレン)]]ビスマレイミド、N,N’-[イソプロピリデンビス[(2,6-ジクロロベンゼン-4,1-ジイル)オキシカルボニル(p-フェニレン)]]ビスマレイミド、N,N’-[(フェニルイミノ)ビス(4,1-フェニレン)]ビスマレイミド、N,N’-[アゾビス(4,1-フェニレン)]ビスマレイミド、N,N’-[1,3,4-オキサジアゾール-2,5-ジイルビス(4,1-フェニレン)]ビスマレイミド、2,6-ビス[4-(マレインイミド-N-イル)フェノキシ]ベンゾニトリル、N,N’-[1,3,4-オキサジアゾール-2,5-ジイルビス(3,1-フェニレン)]ビスマレイミド、N,N’-[ビス[9-オキソ-9H-9-ホスファ(V)-10-オキサフェナントレン-9-イル]メチレンビス(p-フェニレン)]ビスマレイミド、N,N’-[ヘキサフルオロイソプロピリデンビス[p-フェニレンオキシカルボニル(m-フェニレン)]]ビスマレイミド、N,N’-[カルボニルビス[(4,1-フェニレン)チオ(4,1-フェニレン)]]ビスマレイミド、N,N’-カルボニルビス(p-フェニレンオキシp-フェニレン)ビスマレイミド、N,N’-[5-tert-ブチル-1,3-フェニレンビス[(1,3,4-オキサジアゾール-5,2-ジイル)(4,1-フェニレン)]]ビスマレイミド、N,N’-[シクロヘキシリデンビス(4,1-フェニレン)]ビスマレイミド、N,N’-[メチレンビス(オキシ)ビス(2-メチル-1,4-フェニレン)]ビスマレイミド、N,N’-[5-[2-[5-(ジメチルアミノ)-1-ナフチルスルホニルアミノ]エチルカルバモイル]-1,3-フェニレン]ビスマレイミド、N,N’-(オキシビスエチレン)ビスマレイミド、N,N’-[ジチオビス(m-フェニレン)]ビスマレイミド、N,N’-(3,6,9-トリオキサウンデカン-1,11-ジイル)ビスマレイミド、N,N’-(エチレンビス-p-フェニレン)ビスマレイミド、DesignerMolecules社製のBMI-689、BMI-1500、BMI-1700、BMI-3000、BMI-5000、BMI-9000、JFEケミカル社製のODA-BMI、BAFBMIなどの多官能マレイミドを挙げることができる。
また、多官能アミンと無水マレイン酸を反応させて得られる多官能マレイミドを挙げることができる。多官能アミンとしては、イソホロンジアミン、ジシクロヘキシルメタン-4,4′-ジアミン、ハンツマン・コーポレーション社製の、末端アミノ化ポリプロピレングリコール骨格を有するジェファーミンD-230、HK-511、D-400、XTJ-582、D-2000、XTJ-578、XTJ-509、XTJ-510、T-403、T-5000、末端アミノ化エチレングリコール骨格を有するXTJ-500、XTJ-501、XTJ-502、XTJ-504、XTJ-511、XTJ-512、XTJ-590末端アミノ化ポリテトラメチレングリコール骨格を有するXTJ-542、XTJ-533、XTJ-536、XTJ-548、XTJ-559などが挙げられる。
マレイミド基含有化合物(b6)をラジカルにより架橋させる場合には、ラジカル重合開始剤を添加することができる。具体的にはアゾ系化合物、有機過酸化物が例示できる。重合開始剤は一種もしくは二種以上を組み合わせて用いられる。
アゾ系化合物としては、2,2’-アゾビスイソブチロニトリル、2,2’-アゾビス(2-メチルブチロニトリル)、1,1’-アゾビス(シクロヘキサン1-カルボニトリル)、2,2’-アゾビス(2,4-ジメチルバレロニトリル)、2,2’-アゾビス(2,4-ジメチル-4-メトキシバレロニトリル)、ジメチル2,2’-アゾビス(2-メチルプロピオネート)、4,4’-アゾビス(4-シアノバレリック酸)、2,2’-アゾビス(2-ヒドロキシメチルプロピオニトリル)、2,2’-アゾビス[2-(2-イミダゾリン-2-イル)プロパン]が例示できる。
有機過酸化物としては、過酸化ベンゾイル、t-ブチルパーベンゾエイト、クメンヒドロパーオキシド、ジイソプロピルパーオキシジカーボネート、ジ-n-プロピルパーオキシジカーボネート、ジ(2-エトキシエチル)パーオキシジカーボネート、t-ブチルパーオキシ2-エチルヘキサノエート、t-ブチルパーオキシネオデカノエート、t-ブチルパーオキシビバレート、(3,5,5-トリメチルヘキサノイル)パーオキシド、ジプロピオニルパーオキシド、ジアセチルパーオキシドが例示できる。
アゾ系化合物としては、2,2’-アゾビスイソブチロニトリル、2,2’-アゾビス(2-メチルブチロニトリル)、1,1’-アゾビス(シクロヘキサン1-カルボニトリル)、2,2’-アゾビス(2,4-ジメチルバレロニトリル)、2,2’-アゾビス(2,4-ジメチル-4-メトキシバレロニトリル)、ジメチル2,2’-アゾビス(2-メチルプロピオネート)、4,4’-アゾビス(4-シアノバレリック酸)、2,2’-アゾビス(2-ヒドロキシメチルプロピオニトリル)、2,2’-アゾビス[2-(2-イミダゾリン-2-イル)プロパン]が例示できる。
有機過酸化物としては、過酸化ベンゾイル、t-ブチルパーベンゾエイト、クメンヒドロパーオキシド、ジイソプロピルパーオキシジカーボネート、ジ-n-プロピルパーオキシジカーボネート、ジ(2-エトキシエチル)パーオキシジカーボネート、t-ブチルパーオキシ2-エチルヘキサノエート、t-ブチルパーオキシネオデカノエート、t-ブチルパーオキシビバレート、(3,5,5-トリメチルヘキサノイル)パーオキシド、ジプロピオニルパーオキシド、ジアセチルパーオキシドが例示できる。
架橋剤(B)は、エポキシ基含有化合物(b1)と、(b2)~(b7)の少なくともいずれかとの併用が好ましい。特に、めっき液耐性、および耐熱性をより優れた物とする観点からは、エポキシ基含有化合物(b1)とイソシアネート基含有化合物(b3)の併用、エポキシ基含有化合物(b1)とカルボジイミド基含有化合物(b5)の併用、エポキシ基含有化合物(b1)とマレイミド基含有化合物(b6)の併用が好ましい。また、めっき液耐性とヒートサイクル後マイグレーション性をより優れたものとする観点からは、エポキシ基含有化合物(b1)とシアネートエステル化合物(b2)の併用、エポキシ基含有化合物(b1)と金属キレート化合物(b4)の併用が好ましい。
1-3.紫外線吸収剤(C)
本組成物には、任意成分として紫外線吸収剤(C)を含有させてもよい。紫外線吸収剤は、紫外線を吸収し、紫外線の光エネルギーを熱エネルギーに変換する役割を担う。本組成物より形成した接着シートなどの熱硬化性シートを硬化せしめた硬化層のビア形成時にUVレーザー光を用いる場合、紫外線吸収剤を添加することにより、接着シートや硬化物層に加わるエネルギー量を調整することができる。その結果、レーザー加工性を向上させることができる。紫外線吸収剤(C)は、本組成物100質量%中、0.1~10質量%含むことが好ましく、0.1~5質量%含むことがより好ましい。なお、接着シートや硬化物層へのレーザー光照射は用途に応じて種々の波長(紫外光、赤外光等)を選定できる。また、必要に応じて複数のレーザー光を照射してもよい。
本組成物には、任意成分として紫外線吸収剤(C)を含有させてもよい。紫外線吸収剤は、紫外線を吸収し、紫外線の光エネルギーを熱エネルギーに変換する役割を担う。本組成物より形成した接着シートなどの熱硬化性シートを硬化せしめた硬化層のビア形成時にUVレーザー光を用いる場合、紫外線吸収剤を添加することにより、接着シートや硬化物層に加わるエネルギー量を調整することができる。その結果、レーザー加工性を向上させることができる。紫外線吸収剤(C)は、本組成物100質量%中、0.1~10質量%含むことが好ましく、0.1~5質量%含むことがより好ましい。なお、接着シートや硬化物層へのレーザー光照射は用途に応じて種々の波長(紫外光、赤外光等)を選定できる。また、必要に応じて複数のレーザー光を照射してもよい。
紫外線吸収剤(C)の種類は、ベンゾフェノン系、ベンゾトリアゾール系、トリアジン系、サリチル酸エステル系、シアノアクリレート系などが挙げられる。また、酸化亜鉛を用いてもよい。紫外線吸収剤(C)は、表面処理の有無に関わらず使用できる。
具体的には、2-ヒドロキシ-4-メトキシベンゾフェノン、2-ヒドロキシ-4-メトキシ-2’-カルボキシベンゾフェノン、2-ヒドロキシ-4-オクトキシベンゾフェノン、2-ヒドロキシ-4-n-ドデシルオキシベンゾフェノン、2-ヒドロキシ-4-n-オクタデシルオキシベンゾフェノン、2-ヒドロキシ-4-ベンジルオキシベンゾフェノン、2-ヒドロキシ-4-メトキシ-5-スルホベンゾフェノン、2-ヒドロキシ-5-クロロベンゾフェノン、2,4-ジヒドロキシベンゾフェノン、2,2’-ジヒドロキシ-4-メトキシベンゾフェノン、2,2’-ジヒドロキシ-4,4’-ジメトキシベンゾフェノン、2,2’,4,4’-テトラヒドロキシベンゾフェノン、ポリ-4-(2-アクリロキシエトキシ)-2-ヒドロキシベンゾフェノン、2-(2-ヒドロキシ-5-メチルフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-5-t-ブチルフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-3,5-ジメチルフェニル)ベンゾトリアゾール、2-(2-メチル-4-ヒドロキシフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-3-メチル-5-t-ブチルフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-3,5-ジ-t-ブチルフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-3、5-ジメチルフェニル)-5-メトキシベンゾトリアゾール、2-(2-ヒドロキシ-3-t-ブチル-5-メチルフェニル)-5-クロロベンゾトリアゾール、2-(2-ヒドロキシ-5-t-ブチルフェニル)-5-クロロベンゾトリアゾール、2-[4,6-ビス(2,4-ジメチルフェニル)-1,3,5-トリアジン-2-イル]-5-(オクチルオキシ)フェノール、2-(4,6-ジフェニル-1,3,5-トリアジン-2-イル)-5-(ヘキシルオキシ)フェノール、フェニルサリチレート、p-オクチルフェニルサリチレート、2-シアノ-3,3-ジフェニルアクリル酸エチル 、2-シアノ-3,3-ジフェニルアクリル酸2-エチルヘキシル、2,2-ビス{[2-シアノ-3,3-ジフェニルアクリロイルオキシ]メチル}プロパン-1,3-ジイル-ビス(2-シアノ-3,3-ジフェニルアクリラート)などが挙げられる。
具体的には、2-ヒドロキシ-4-メトキシベンゾフェノン、2-ヒドロキシ-4-メトキシ-2’-カルボキシベンゾフェノン、2-ヒドロキシ-4-オクトキシベンゾフェノン、2-ヒドロキシ-4-n-ドデシルオキシベンゾフェノン、2-ヒドロキシ-4-n-オクタデシルオキシベンゾフェノン、2-ヒドロキシ-4-ベンジルオキシベンゾフェノン、2-ヒドロキシ-4-メトキシ-5-スルホベンゾフェノン、2-ヒドロキシ-5-クロロベンゾフェノン、2,4-ジヒドロキシベンゾフェノン、2,2’-ジヒドロキシ-4-メトキシベンゾフェノン、2,2’-ジヒドロキシ-4,4’-ジメトキシベンゾフェノン、2,2’,4,4’-テトラヒドロキシベンゾフェノン、ポリ-4-(2-アクリロキシエトキシ)-2-ヒドロキシベンゾフェノン、2-(2-ヒドロキシ-5-メチルフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-5-t-ブチルフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-3,5-ジメチルフェニル)ベンゾトリアゾール、2-(2-メチル-4-ヒドロキシフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-3-メチル-5-t-ブチルフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-3,5-ジ-t-ブチルフェニル)ベンゾトリアゾール、2-(2-ヒドロキシ-3、5-ジメチルフェニル)-5-メトキシベンゾトリアゾール、2-(2-ヒドロキシ-3-t-ブチル-5-メチルフェニル)-5-クロロベンゾトリアゾール、2-(2-ヒドロキシ-5-t-ブチルフェニル)-5-クロロベンゾトリアゾール、2-[4,6-ビス(2,4-ジメチルフェニル)-1,3,5-トリアジン-2-イル]-5-(オクチルオキシ)フェノール、2-(4,6-ジフェニル-1,3,5-トリアジン-2-イル)-5-(ヘキシルオキシ)フェノール、フェニルサリチレート、p-オクチルフェニルサリチレート、2-シアノ-3,3-ジフェニルアクリル酸エチル 、2-シアノ-3,3-ジフェニルアクリル酸2-エチルヘキシル、2,2-ビス{[2-シアノ-3,3-ジフェニルアクリロイルオキシ]メチル}プロパン-1,3-ジイル-ビス(2-シアノ-3,3-ジフェニルアクリラート)などが挙げられる。
1-4.フィラー(D)
本組成物には、任意成分としてフィラー(D)を含有させてもよい。本組成物のめっき液耐性およびヒートサイクル試験後の絶縁信頼性、LCPへのラミネート性を向上させる観点からは、本組成物100質量%中、フィラー(D)を3~60質量%含むことが好ましく、5~40質量%含むことがより好ましい。フィラー(D)量を3質量%以上にすることで、ヒートサイクル試験時の急激な温度変化による応力に対し、クラックや剥離などの発生を効果的に抑制でき、また、めっき液の浸食を受けにくい成分を特定以上の量含むことによりめっき液耐性を向上することができる。加えて、ヒートサイクル試験時の急激な温度変化による応力に対し、クラックや剥離などの発生を効果的に抑制することでクラックや剥離部分への水分等の侵入を防ぐことで絶縁信頼性を向上することができる。一方、フィラー(D)量を60質量%以下にすることで、被着体への接着に寄与する樹脂成分の比率が高くなり、LCP基材へのラミネート性がより優れたものとなる。
本組成物には、任意成分としてフィラー(D)を含有させてもよい。本組成物のめっき液耐性およびヒートサイクル試験後の絶縁信頼性、LCPへのラミネート性を向上させる観点からは、本組成物100質量%中、フィラー(D)を3~60質量%含むことが好ましく、5~40質量%含むことがより好ましい。フィラー(D)量を3質量%以上にすることで、ヒートサイクル試験時の急激な温度変化による応力に対し、クラックや剥離などの発生を効果的に抑制でき、また、めっき液の浸食を受けにくい成分を特定以上の量含むことによりめっき液耐性を向上することができる。加えて、ヒートサイクル試験時の急激な温度変化による応力に対し、クラックや剥離などの発生を効果的に抑制することでクラックや剥離部分への水分等の侵入を防ぐことで絶縁信頼性を向上することができる。一方、フィラー(D)量を60質量%以下にすることで、被着体への接着に寄与する樹脂成分の比率が高くなり、LCP基材へのラミネート性がより優れたものとなる。
フィラー(D)形状は特に限定されない。例えば、球状、粉状、繊維状、針状、鱗片状等が挙げられる。フィラー(D)の具体例としては、フッ素フィラー:ポリテトラフルオロエチレン粉末やその変性物、テトラフルオロエチレン-パーフルオロアルキルビニルエーテル粉末、テトラフルオロエチレン-エチレン粉末、テトラフルオロエチレン-ヘキサフルオロプロピレン粉末、テトラフルオロエチレン-フッ化ビニリデン粉末、テトラフルオロエチレン-ヘキサフルオロプロピレン-パーフルオロアルキルビニルエーテル粉末、ポリクロロトリフルオロエチレン粉末、クロロトリフルオロエチレン-エチレン粉末、クロロトリフルオロエチレン-フッ化ビニリデン粉末、ポリフッ化ビニリデン粉末、ポリフッ化ビニル粉末が挙げられる。また、ポリエチレン粉末、ポリアクリル酸エステル粉末、エポキシ樹脂粉末、ポリアミド粉末、ポリイミド粉末、ポリウレタン粉末、液晶ポリマービーズ、ポリシロキサン粉末等の他、シリコーン、アクリル、スチレンブタジエンゴム、ブタジエンゴム等を用いた多層構造のコアシェル等の高分子フィラー;リン酸メラミン、ポリリン酸メラミン、リン酸グアニジン、ポリリン酸グアニジン、リン酸アンモニウム、ポリリン酸アンモニウム、リン酸アミドアンモニウム、ポリリン酸アミドアンモニウム、リン酸カルバメート、ポリリン酸カルバメート等の(ポリ)リン酸塩系化合物、有機リン酸エステル化合物、ホスファゼン化合物、ホスホン酸化合物、ジエチルホスフィン酸アルミニウム、メチルエチルホスフィン酸アルミニウム、ジフェニルホスフィン酸アルミニウム、エチルブチルホスフィン酸アルミニウム、メチルブチルホスフィン酸アルミニウム、ポリエチレンホスフィン酸アルミニウム等のホスフィン酸化合物、ホスフィンオキシド化合物、ホスホラン化合物、ホスホルアミド化合物等のリン系フィラー;ベンゾグアナミン、メラミン、メラム、メレム、メロン、メラミンシアヌレート、シアヌル酸化合物、イソシアヌル酸化合物、トリアゾール系化合物、テトラゾール化合物、ジアゾ化合物、尿素等の窒素系フィラー;結晶性シリカ、非晶性シリカ、中空シリカ、多孔質シリカ、マイカ、タルク、カオリン、クレー、ハイドロタルサイト、ウォラストナイト、ゾノトライト、窒化ケイ素、窒化ホウ素、窒化アルミニウム、リン酸水素カルシウム、リン酸カルシウム、ガラスフレーク、水和ガラス、チタン酸カルシウム、セピオライト、硫酸マグネシウム、水酸化アルミニウム、水酸化マグネシウム、水酸化ジルコニウム、水酸化バリウム、水酸化カルシウム、酸化チタン、酸化スズ、酸化アルミニウム、酸化マグネシウム、酸化ジルコニウム、酸化亜鉛、酸化モリブデン、酸化アンチモン、酸化ニッケル、炭酸亜鉛、炭酸マグネシウム、炭酸カルシウム、炭酸バリウム、ホウ酸亜鉛、ホウ酸アルミニウム等の無機フィラー等が挙げられる。
本組成物から形成した硬化層を大容量高速基板の絶縁層に適用する場合には、液晶ポリマー、フッ素樹脂、変性ポリフェニレンエーテル、ガラス中空体であるガラスバルーン、石炭灰中空体、シラスバルーン、炭酸カルシウム、タルク、これらの混合物が例示できる。
衝撃吸収性の観点からは、フッ素フィラー、窒化ホウ素、液晶ポリマーおよびシリカを使用することが好ましい。フィラー(D)は、単独または複数を併用して用いられる。
フィラー(D)の添加方法は特に制限されるものではなく、従来公知の方法を用いることができる。好適例として、ポリイミド樹脂(A)の重合前または途中に重合反応液に添加する方法、3本ロールなどを用いてポリイミド樹脂(A)にフィラーを混錬する方法、フィラーを含む分散液を用意しこれをポリイミド樹脂(A)に混合する方法などが挙げられる。また、フィラーを良好に分散させ、また分散状態を安定化させるために分散剤、増粘剤等を熱硬化性樹脂組成物の物性に影響を及ぼさない範囲で用いることもできる。
1-5.その他の任意成分
本組成物は、本発明の趣旨を逸脱しない範囲で種々の添加剤を含むことができる。例えば、ポリイミド樹脂(A)に該当しないポリイミド樹脂を用いてもよい。また、任意の熱可塑性樹脂を用いることができる。また、ポリイミド樹脂(A)中のフェノール性水酸基と架橋剤(B)との架橋促進するために、任意成分として触媒を含有することができる。触媒の好適例として、イミダゾール系、アミン系、リン系が例示できる。更に、染料、顔料(例えば、カーボンブラック)、難燃剤、酸化防止剤、重合禁止剤、消泡剤、レベリング剤、イオン捕集剤、保湿剤、粘度調整剤、防腐剤、抗菌剤、帯電防止剤、アンチブロッキング剤、紫外線吸収剤、赤外線吸収剤、電磁波シールド剤等が挙げられる。
本組成物は、本発明の趣旨を逸脱しない範囲で種々の添加剤を含むことができる。例えば、ポリイミド樹脂(A)に該当しないポリイミド樹脂を用いてもよい。また、任意の熱可塑性樹脂を用いることができる。また、ポリイミド樹脂(A)中のフェノール性水酸基と架橋剤(B)との架橋促進するために、任意成分として触媒を含有することができる。触媒の好適例として、イミダゾール系、アミン系、リン系が例示できる。更に、染料、顔料(例えば、カーボンブラック)、難燃剤、酸化防止剤、重合禁止剤、消泡剤、レベリング剤、イオン捕集剤、保湿剤、粘度調整剤、防腐剤、抗菌剤、帯電防止剤、アンチブロッキング剤、紫外線吸収剤、赤外線吸収剤、電磁波シールド剤等が挙げられる。
1-6.熱硬化性組成物の特性
本組成物は、ヒートサイクル試験後の絶縁信頼性の観点からは、180℃、60分の条件で熱硬化した後のガラス転移温度が0~70℃の範囲にあることが好ましい。より好ましくは10~60℃である。前記ガラス転移温度が0℃以上であることで、極端な環境温度のサイクル変化に対しても組成物中の架橋構造が大きく崩れることがなく、短絡現象の原因となる電極から発生する金属イオンの流動を抑制することができ絶縁信頼特性が優れたものとなる。一方、前記ガラス転移温度が70℃以下であることで、本組成物に一定の柔軟性を付与することができ、極端な環境温度のサイクル変化における被着体の膨張収縮に対して応力緩和することで剥離を抑制し、剥離によって生じる間隙から流入する水分などを原因とする短絡を抑制することができる。なお、前記硬化条件は本組成物の硬化処理時のTgを見積もるための硬化条件であって、本組成物から形成される硬化物の硬化条件を何ら限定するものではない。
本組成物は、ヒートサイクル試験後の絶縁信頼性の観点からは、180℃、60分の条件で熱硬化した後のガラス転移温度が0~70℃の範囲にあることが好ましい。より好ましくは10~60℃である。前記ガラス転移温度が0℃以上であることで、極端な環境温度のサイクル変化に対しても組成物中の架橋構造が大きく崩れることがなく、短絡現象の原因となる電極から発生する金属イオンの流動を抑制することができ絶縁信頼特性が優れたものとなる。一方、前記ガラス転移温度が70℃以下であることで、本組成物に一定の柔軟性を付与することができ、極端な環境温度のサイクル変化における被着体の膨張収縮に対して応力緩和することで剥離を抑制し、剥離によって生じる間隙から流入する水分などを原因とする短絡を抑制することができる。なお、前記硬化条件は本組成物の硬化処理時のTgを見積もるための硬化条件であって、本組成物から形成される硬化物の硬化条件を何ら限定するものではない。
2.熱硬化性組成物の製造方法
本組成物は、各配合成分を配合することにより得られる。ポリイミド前駆体ではなく、イミド化したポリイミド樹脂(A)を配合成分として用いる。配合に際して、適宜、溶媒を用いることができる。固形分濃度は、例えば20~60質量%とすることができる。本実施形態のポリイミド樹脂(A)によれば、ダイマー構造を有しているので、各種有機溶剤に容易に溶解させることができる。
本組成物は、各配合成分を配合することにより得られる。ポリイミド前駆体ではなく、イミド化したポリイミド樹脂(A)を配合成分として用いる。配合に際して、適宜、溶媒を用いることができる。固形分濃度は、例えば20~60質量%とすることができる。本実施形態のポリイミド樹脂(A)によれば、ダイマー構造を有しているので、各種有機溶剤に容易に溶解させることができる。
本組成物は、例えば粉末状、フィルム状、シート状、板状、ペレット状、ペースト状または液状とすることができる。液状またはペースト状の熱硬化性組成物は、溶剤を用いて粘度を調整することにより容易に得ることができる。また、フィルム状、シート状、板状の熱硬化性組成物は、例えば、液状またはペースト状の熱硬化性組成物を塗工して乾燥することにより形成できる。また、粉末状、ペレット状の熱硬化性組成物は、例えば、前記フィルム状等の熱硬化性組成物を所望のサイズに粉砕または分断することにより得られる。
接着シートは、溶剤を含む本組成物の塗布液を、例えば剥離フィルムの片面に塗布し、有機溶剤等の液状媒体を例えば40~150℃で除去・乾燥することにより得られる。得られた接着シートの表面に別の剥離フィルムを積層することにより、両面剥離フィルム付き接着シートを得ることができる。両面を剥離フィルムで積層することにより、接着シートの表面汚染を予防することができる。剥離フィルムを剥がすことによって、接着シートを単離することができる。2つの剥離フィルムは、同種または異種のいずれも用いることができる。剥離性の異なる剥離フィルムを用いることによって、剥離力に強弱をつけることができるので順番に剥がしやすくなる。また、基材に塗布液を直接塗工して接着シートを形成してもよい。
基材は、ポリイミドフィルム、ポリエチレンフィルム、ポリカーボネート、ポリエチレン、液晶ポリマー、フェノール樹脂、アラミド樹脂などの樹脂材料:銅、アルミニウム、ステンレス等の金属材料;ITO、ガラス、シリコン、シリコンカーバイト等の無機材料およびこれらを任意に組み合わせた複合材料が例示できる。本組成物によれば、貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにある軟らかいポリイミド樹脂(A)により各種基材への密着性に優れるのみならず、成形加工性に優れる。
塗布方法としては、例えば、コンマコート、ナイフコート、ダイコート、リップコート、ロールコート、カーテンコート、バーコート、グラビア印刷、フレキソ印刷、スクリーン印刷、ディップコート、スプレーコート、スピンコート等、公知の方法を選択することができる。
接着シートの乾燥後の厚みは十分な接着性を発揮させる為、また取り扱い易さの点から、5~500μmであることが好ましく、10~100μmであることが更に好ましい。
3.硬化物の製造方法
本組成物を熱硬化処理することにより硬化物が得られる。例えば、熱硬化性組成物をシート等の所望の形状に成形し、熱硬化処理する方法が例示できる。溶剤を含む熱硬化性組成物を塗布、乾燥することにより簡便に熱硬化性組成物のシートなどの成形体を得ることができる。そして、成形体を熱硬化することにより硬化物を形成する。成形体と硬化のタイミングは同時であってもよい。なお、硬化物のうちシート状のものを硬化層ともいう。
本組成物を熱硬化処理することにより硬化物が得られる。例えば、熱硬化性組成物をシート等の所望の形状に成形し、熱硬化処理する方法が例示できる。溶剤を含む熱硬化性組成物を塗布、乾燥することにより簡便に熱硬化性組成物のシートなどの成形体を得ることができる。そして、成形体を熱硬化することにより硬化物を形成する。成形体と硬化のタイミングは同時であってもよい。なお、硬化物のうちシート状のものを硬化層ともいう。
熱硬化温度は、架橋剤(B)の種類に応じて適宜選定すればよい。例えば、150~230℃の温度で、30~180分加熱処理する方法が例示できる。熱硬化時に、必要に応じて圧をかけて熱圧着(例えば、5MPa)することができる。熱硬化処理により、本組成物に架橋構造が形成され、3次元架橋した硬化物が得られる。
4.熱硬化性組成物および硬化物の用途等
本組成物は、LCP基材とのラミネート性に優れるので、低誘電特性が求められるフレキシブルプリント配線板用途の接着シートとして好適である。硬化後に優れた接着性を示すので、各種材料(樹脂層、金属層、ITO等の無機層、複合層など)を接合するための接着シート、接合材料として好適である。例えば、銅張積層体の接着シート、電子回路基板と電子部品等との部品同士の接合材料に好適である。銅張積層板(CCL:Copper Clad Laminate)では、銅箔面に電解銅めっきを行い、レジスト層を除去した後にアルカリ性等のめっき液でエッチングする工程があるが、本硬化物によれば、めっき液耐性に優れるので銅張積層板の接着シートとして好適である。更に、本硬化物はレーザー加工性に優れるので、ビア、パターン等の開口部を形成する用途に好適である。また、TBAテープやCOFテープのキャリアテープの接着層としても利用できる。
本組成物は、LCP基材とのラミネート性に優れるので、低誘電特性が求められるフレキシブルプリント配線板用途の接着シートとして好適である。硬化後に優れた接着性を示すので、各種材料(樹脂層、金属層、ITO等の無機層、複合層など)を接合するための接着シート、接合材料として好適である。例えば、銅張積層体の接着シート、電子回路基板と電子部品等との部品同士の接合材料に好適である。銅張積層板(CCL:Copper Clad Laminate)では、銅箔面に電解銅めっきを行い、レジスト層を除去した後にアルカリ性等のめっき液でエッチングする工程があるが、本硬化物によれば、めっき液耐性に優れるので銅張積層板の接着シートとして好適である。更に、本硬化物はレーザー加工性に優れるので、ビア、パターン等の開口部を形成する用途に好適である。また、TBAテープやCOFテープのキャリアテープの接着層としても利用できる。
また、本組成物のポリイミド樹脂(A)は電気絶縁性に優れるので、絶縁性に優れた硬化物を提供できる。例えば、回路基板上の絶縁層形成材料(プリント配線板のカバーレイ層、ビルトアップ基板等の層間絶縁層、ボンディングシート等を含む)等として好適に用いられる。また、電子部品の絶縁性部材に好適に適用できる。電子部品は、例えば、パワー半導体装置、LED、インバーター装置等のパワーモジュールであり、基板、半導体チップパッケージの絶縁層、アンダーフィル材、接着材等に好適に用いられる。また、銅張積層板用の熱硬化性組成物、配線板形成用ボンディングシート、フレキシブル基板のカバーコート、プリプレグ等に使用できる。
フィラー(D)として導電性フィラーを配合することにより、導電性接着シートとして利用してもよい。更に、フィラー(D)として熱伝導性フィラーを用いることにより、放熱性が求められる用途全般に適用できる。例えば、樹脂組成物の成形性を利用して、所望の形状の放熱部品として好適に利用できる。特に、軽薄短小化のために、ファンやヒートシンクを設置できない電子機器(スマートフォン、ダブレット端末等)、電池用外装材の放熱性接着材や放熱性シートとして有用である。また、本組成物の硬化物は、発熱体とヒートシンクとの接着層あるいはヒートスプレッダーとして好適である。また、基板上に搭載された一種または複数の電子部品を被覆する放熱層として適用できる。
5.プリント配線板
本組成物からなる接着シートは、上記特性を有しているのでプリント配線板の製造に好適に用いることができる。接着シートは、熱硬化により接着性を示す硬化層として機能する。また、本組成物から形成した熱硬化性シートの硬化物である硬化層は絶縁性に優れるので、プリント配線板において、保護膜や層間絶縁層として好適に利用できる。本組成物からなる熱硬化性シートは、柔軟性の高いポリイミド樹脂(A)を用いているので、低温・短時間でのラミネートが可能となる。このため、低誘電特性に優れる液晶ポリマー(LCP)基材との接合に好適である。
本組成物からなる接着シートは、上記特性を有しているのでプリント配線板の製造に好適に用いることができる。接着シートは、熱硬化により接着性を示す硬化層として機能する。また、本組成物から形成した熱硬化性シートの硬化物である硬化層は絶縁性に優れるので、プリント配線板において、保護膜や層間絶縁層として好適に利用できる。本組成物からなる熱硬化性シートは、柔軟性の高いポリイミド樹脂(A)を用いているので、低温・短時間でのラミネートが可能となる。このため、低誘電特性に優れる液晶ポリマー(LCP)基材との接合に好適である。
プリント配線板は、例えば、銅張積層板における銅箔をエッチング等によって加工し、信号回路等を形成して得た基板とカバーフィルムとを接着シートを介して貼り合わせ、熱硬化により接合する工程等を経て製造できる。また、例えば、絶縁性のフレキシブルフィルム上に導体パターンを形成し、その上に本接着シートを介して保護膜を形成し、熱圧着する工程等を経てフレキシブルプリント配線板を製造できる。前記フレキシブルフィルムとしては、ポリエステル、ポリイミド、液晶ポリマー、PTFEフィルムが例示できる。導体パターンは、プリント技術により形成する方法、スパッタリングやめっきによる方法が例示できる。
プリント配線板の片面または両面に形成された本組成物の硬化層に対し、ドリル加工やレーザー加工などにより開口部を設け、導電剤を充填してビアを形成してもよい。また、本組成物の硬化物である層間絶縁層上に回路層を形成してもよい。本組成物の硬化物はめっき耐性に優れるので多層プリント配線板の製造に好適である。更に、フェノール性水酸基を介して、柔軟性の高いポリイミド樹脂(A)と架橋剤(B)との架橋構造を有することにより残留応力を低く抑え、ヒートサイクル試験後の絶縁信頼性を優れたものとすることができる。本組成物を用いて形成されたプリント配線板は、幅広い温度範囲での絶縁信頼性に優れるので、スマートフォンやタブレット端末等の各種電子機器に好適である。
以下、本発明を実施例によりさらに具体的に説明する。本発明は、その趣旨を越えない限り以下の実施例に限定されない。特に断りのない限り、「%」および「部」は質量基準とする。
(i)重量平均分子量(Mw)の測定
Mwの測定は、昭和電工社製GPC(ゲルパーミエーションクロマトグラフィー)「GPC-101」を用いた。溶媒はTHF(テトラヒドロフラン)とし、カラムとして「KF-805L」(昭和電工社製:GPCカラム:8mmID×300mmサイズ)を直列に2本接続したものを用いた。試料濃度1質量%、流量1.0mL/min、圧力3.8MPa、カラム温度40℃の条件で行い、Mwの決定はポリスチレン換算で行った。データ解析はメーカー内蔵ソフトを使用して検量線および分子量、ピーク面積を算出し、保持時間17.9~30.0分の範囲を分析対象としてMwを求めた。
Mwの測定は、昭和電工社製GPC(ゲルパーミエーションクロマトグラフィー)「GPC-101」を用いた。溶媒はTHF(テトラヒドロフラン)とし、カラムとして「KF-805L」(昭和電工社製:GPCカラム:8mmID×300mmサイズ)を直列に2本接続したものを用いた。試料濃度1質量%、流量1.0mL/min、圧力3.8MPa、カラム温度40℃の条件で行い、Mwの決定はポリスチレン換算で行った。データ解析はメーカー内蔵ソフトを使用して検量線および分子量、ピーク面積を算出し、保持時間17.9~30.0分の範囲を分析対象としてMwを求めた。
(ii)酸価の測定
酸価はJIS K0070に準じて測定した。具体的には、共栓三角フラスコ中に試料(ポリイミド樹脂(A))約1gを精密に量り採り、シクロヘキサノン溶媒100mLを加えて溶解する。これに、フェノールフタレイン試液を指示薬として加え、0.1Nアルコール性水酸化カリウム溶液で滴定し、指示薬が淡紅色を30秒間保持した時を終点とした。酸価は次式により求めた。
酸価(mgKOH/g)=(5.611×a×F)/S
ただし、
S:試料の採取量(g)
a:0.1Nアルコール性水酸化カリウム溶液の消費量(mL)
F:0.1Nアルコール性水酸化カリウム溶液の力価
酸価はJIS K0070に準じて測定した。具体的には、共栓三角フラスコ中に試料(ポリイミド樹脂(A))約1gを精密に量り採り、シクロヘキサノン溶媒100mLを加えて溶解する。これに、フェノールフタレイン試液を指示薬として加え、0.1Nアルコール性水酸化カリウム溶液で滴定し、指示薬が淡紅色を30秒間保持した時を終点とした。酸価は次式により求めた。
酸価(mgKOH/g)=(5.611×a×F)/S
ただし、
S:試料の採取量(g)
a:0.1Nアルコール性水酸化カリウム溶液の消費量(mL)
F:0.1Nアルコール性水酸化カリウム溶液の力価
(iii)フェノール性水酸基価の測定
フェノール性水酸基価は、JIS K0070に準じて測定した。フェノール性水酸基価は、ポリイミド樹脂(A)1g中に含まれるフェノール性水酸基をアセチル化させたときに、フェノール性水酸基と結合した酢酸を中和するために必要な水酸化カリウムの量(mg)で表したものである。ポリイミド樹脂(A)のフェノール性水酸基価を算出する場合には、下記式に示す通り、酸価を考慮して計算した。具体的には、共栓三角フラスコ中に試料(ポリイミド樹脂(A))約1gを精密に量り採り、シクロヘキサノン溶媒100mLを加えて溶解する。更にアセチル化剤(無水酢酸25gをピリジンで溶解し、容量100mLとした溶液)を正確に5mL加え、約1時間攪拌した。これに、フェノールフタレイン試液を指示薬として加え、30秒間持続する。その後、溶液が淡紅色を呈するまで0.5Nアルコール性水酸化カリウム溶液で滴定する。フェノール性水酸基価は次式により求めた。
フェノール性水酸基価(mgKOH/g)=[{(b-a)×F×28.05}/S]+D
ただし、
S:試料の採取量(g)
a:0.5Nアルコール性水酸化カリウム溶液の消費量(mL)
b:空実験の0.5Nアルコール性水酸化カリウム溶液の消費量(mL)
F:0.5Nアルコール性水酸化カリウム溶液の力価
D:酸価(mgKOH/g)
側鎖フェノール性水酸基価は、得られたフェノール性水酸基価に対して、ポリイミド樹脂(A)の合成に用いた単量体の仕込み率から算出した。また、末端フェノール性水酸基価は、実験で得られたフェノール性水酸基価から側鎖フェノール性水酸基価を差し引いた値とした。なお、bの値は、アセチル化剤(無水酢酸25gをピリジンで溶解し、容量100mLとした溶液)5mLを0.5Nアルコール性水酸化カリウム溶液で滴定することで求められる。
フェノール性水酸基価は、JIS K0070に準じて測定した。フェノール性水酸基価は、ポリイミド樹脂(A)1g中に含まれるフェノール性水酸基をアセチル化させたときに、フェノール性水酸基と結合した酢酸を中和するために必要な水酸化カリウムの量(mg)で表したものである。ポリイミド樹脂(A)のフェノール性水酸基価を算出する場合には、下記式に示す通り、酸価を考慮して計算した。具体的には、共栓三角フラスコ中に試料(ポリイミド樹脂(A))約1gを精密に量り採り、シクロヘキサノン溶媒100mLを加えて溶解する。更にアセチル化剤(無水酢酸25gをピリジンで溶解し、容量100mLとした溶液)を正確に5mL加え、約1時間攪拌した。これに、フェノールフタレイン試液を指示薬として加え、30秒間持続する。その後、溶液が淡紅色を呈するまで0.5Nアルコール性水酸化カリウム溶液で滴定する。フェノール性水酸基価は次式により求めた。
フェノール性水酸基価(mgKOH/g)=[{(b-a)×F×28.05}/S]+D
ただし、
S:試料の採取量(g)
a:0.5Nアルコール性水酸化カリウム溶液の消費量(mL)
b:空実験の0.5Nアルコール性水酸化カリウム溶液の消費量(mL)
F:0.5Nアルコール性水酸化カリウム溶液の力価
D:酸価(mgKOH/g)
側鎖フェノール性水酸基価は、得られたフェノール性水酸基価に対して、ポリイミド樹脂(A)の合成に用いた単量体の仕込み率から算出した。また、末端フェノール性水酸基価は、実験で得られたフェノール性水酸基価から側鎖フェノール性水酸基価を差し引いた値とした。なお、bの値は、アセチル化剤(無水酢酸25gをピリジンで溶解し、容量100mLとした溶液)5mLを0.5Nアルコール性水酸化カリウム溶液で滴定することで求められる。
(iv)アミン価の測定
共栓三角フラスコ中に試料(ポリイミド樹脂(A))約1gを精密に量り採り、シクロヘキサノン溶媒100mLを加えて溶解する。これに、別途0.20gのMethyl Orangeを蒸溜水50mLに溶解した液と、0.28gのXylene Cyanol FFをメタノール50mLに溶解した液とを混合して調製した指示薬を2、3滴加え、30秒間保持する。その後、溶液が青灰色を呈するまで0.1Nアルコール性塩酸溶液で滴定する。アミン価は次式により求めた。
アミン価(mgKOH/g)=(5.611×a×F)/S
但し、
S:試料の採取量(g)
a:0.1Nアルコール性塩酸溶液の消費量(mL)
F:0.1Nアルコール性塩酸溶液の力価
共栓三角フラスコ中に試料(ポリイミド樹脂(A))約1gを精密に量り採り、シクロヘキサノン溶媒100mLを加えて溶解する。これに、別途0.20gのMethyl Orangeを蒸溜水50mLに溶解した液と、0.28gのXylene Cyanol FFをメタノール50mLに溶解した液とを混合して調製した指示薬を2、3滴加え、30秒間保持する。その後、溶液が青灰色を呈するまで0.1Nアルコール性塩酸溶液で滴定する。アミン価は次式により求めた。
アミン価(mgKOH/g)=(5.611×a×F)/S
但し、
S:試料の採取量(g)
a:0.1Nアルコール性塩酸溶液の消費量(mL)
F:0.1Nアルコール性塩酸溶液の力価
(v)酸無水物基価の測定
共栓三角フラスコ中に試料(ポリイミド樹脂(A))約1gを精密に量り採り、1,4-ジオキサン溶媒100mLを加えて溶解した。試料中の酸無水物基の量よりも多いオクチルアミン、1,4-ジオキサン、水の混合溶液(質量の混合比は1.49/800/80)を10mL加えて15分攪拌し、酸無水物基と反応させた。その後、過剰のオクチルアミンを0.02M過塩素酸、1,4-ジオキサンの混合溶液で滴定した。また、試料を加えていない、オクチルアミン、1,4-ジオキサン、水の混合溶液(質量の混合比は1.49/800/80)10mLもブランクとして測定を実施した。酸無水物価は次式により求めた(単位:mgKOH/g)
酸無水物価(mgKOH/g)=0.02×(B-A)×F×56.11/S
B:ブランクの滴定量(mL)
A:試料の滴定量(mL)
S:試料の採取量(g)
F:0.02mol/L過塩素酸の力価
共栓三角フラスコ中に試料(ポリイミド樹脂(A))約1gを精密に量り採り、1,4-ジオキサン溶媒100mLを加えて溶解した。試料中の酸無水物基の量よりも多いオクチルアミン、1,4-ジオキサン、水の混合溶液(質量の混合比は1.49/800/80)を10mL加えて15分攪拌し、酸無水物基と反応させた。その後、過剰のオクチルアミンを0.02M過塩素酸、1,4-ジオキサンの混合溶液で滴定した。また、試料を加えていない、オクチルアミン、1,4-ジオキサン、水の混合溶液(質量の混合比は1.49/800/80)10mLもブランクとして測定を実施した。酸無水物価は次式により求めた(単位:mgKOH/g)
酸無水物価(mgKOH/g)=0.02×(B-A)×F×56.11/S
B:ブランクの滴定量(mL)
A:試料の滴定量(mL)
S:試料の採取量(g)
F:0.02mol/L過塩素酸の力価
(vi)ポリイミド樹脂(A)の貯蔵弾性率G’およびTgの測定
各合成例に係るポリイミド樹脂(A)を不揮発分35%になるようにシクロヘキサノンに溶解させ、ポリイミド樹脂ワニスを作製した。耐熱性の離形フィルム上に10milのギャップを持ったドクターブレードを用いて、前記ワニスを塗工し、130℃で10min乾燥させることにより、厚さ25μmの樹脂シートを得た。得られた樹脂シートを重剥離フィルムから剥離し、樹脂シートの貯蔵弾性率およびTgを動的粘弾性測定装置「DVA200」(アイティー計測制御社製)により測定した。
貯蔵弾性率は、樹脂シートを0℃まで冷却後、昇温速度10℃/分で300℃まで昇温させ、振動周波数10Hz、つかみ間長:10mmで粘弾性を測定し、貯蔵弾性率G’が1.0×107Paとなる温度を測定した。また、tanδプロットのピーク温度をTgとした。
昇温速度:10℃/min
測定周波数:10Hz
つかみ間長:10mm
幅:5mm
各合成例に係るポリイミド樹脂(A)を不揮発分35%になるようにシクロヘキサノンに溶解させ、ポリイミド樹脂ワニスを作製した。耐熱性の離形フィルム上に10milのギャップを持ったドクターブレードを用いて、前記ワニスを塗工し、130℃で10min乾燥させることにより、厚さ25μmの樹脂シートを得た。得られた樹脂シートを重剥離フィルムから剥離し、樹脂シートの貯蔵弾性率およびTgを動的粘弾性測定装置「DVA200」(アイティー計測制御社製)により測定した。
貯蔵弾性率は、樹脂シートを0℃まで冷却後、昇温速度10℃/分で300℃まで昇温させ、振動周波数10Hz、つかみ間長:10mmで粘弾性を測定し、貯蔵弾性率G’が1.0×107Paとなる温度を測定した。また、tanδプロットのピーク温度をTgとした。
昇温速度:10℃/min
測定周波数:10Hz
つかみ間長:10mm
幅:5mm
(vii)熱硬化性組成物を180℃で60分熱処理したときのTgの測定
後述する各実施例、比較例の塗布液(熱硬化性組成物)に対し、上記(vi)と同様の方法によりポリイミド樹脂シートを得た。次いで、ポリイミド樹脂シートを180℃で60分加熱処理を行い、硬化シートを得た。得られた硬化シートに対し、(vi)と同様の動的粘弾性測定装置を用い、昇温速度、測定周波数、つかみ間長、幅を同一の条件として、-50~200℃の温度範囲で損失正接(tanδ)の測定をおこない、上記と同様の方法によりTgを測定した。
後述する各実施例、比較例の塗布液(熱硬化性組成物)に対し、上記(vi)と同様の方法によりポリイミド樹脂シートを得た。次いで、ポリイミド樹脂シートを180℃で60分加熱処理を行い、硬化シートを得た。得られた硬化シートに対し、(vi)と同様の動的粘弾性測定装置を用い、昇温速度、測定周波数、つかみ間長、幅を同一の条件として、-50~200℃の温度範囲で損失正接(tanδ)の測定をおこない、上記と同様の方法によりTgを測定した。
<ポリイミド樹脂の合成>
[合成例1] ポリイミド樹脂(P1)
オイルバスを備えた撹拌棒付き1Lセパラブルフラスコに、窒素ガスを導入しながら、シクロヘキサノン200gを加え、ジアミンとしてダイマージアミン(PRIAMINE1075)149.8g、モノアミン化合物として、m-アミノフェノール4.7gを撹拌しながら加え、続いてテトラカルボン酸二無水物として1,2,4,5-シクロヘキサンテトラカルボン酸二無水物67.3gを加えて室温で30分撹拌した。これを100℃に昇温し、3時間撹拌した後、オイルバスを外して室温に戻し、ワニス状のポリイミド前駆体を得た。その後、ディーンスタークトラップを用いて留出する水を系外に除去しながら、170℃で10時間加熱を行い、イミド化してポリイミド樹脂(P1)を得た。得られたポリイミド樹脂のMw、Tgおよび官能基価をそれぞれ表1に示す。
[合成例1] ポリイミド樹脂(P1)
オイルバスを備えた撹拌棒付き1Lセパラブルフラスコに、窒素ガスを導入しながら、シクロヘキサノン200gを加え、ジアミンとしてダイマージアミン(PRIAMINE1075)149.8g、モノアミン化合物として、m-アミノフェノール4.7gを撹拌しながら加え、続いてテトラカルボン酸二無水物として1,2,4,5-シクロヘキサンテトラカルボン酸二無水物67.3gを加えて室温で30分撹拌した。これを100℃に昇温し、3時間撹拌した後、オイルバスを外して室温に戻し、ワニス状のポリイミド前駆体を得た。その後、ディーンスタークトラップを用いて留出する水を系外に除去しながら、170℃で10時間加熱を行い、イミド化してポリイミド樹脂(P1)を得た。得られたポリイミド樹脂のMw、Tgおよび官能基価をそれぞれ表1に示す。
[合成例2~25、比較合成例1~5]ポリイミド樹脂(P2)~(P30)
表1~3に記載の単量体を用いた以外は、合成例1と同様の方法によりポリイミド樹脂P2~P30を得た。
表1等の略称の内容を以下に示す。
TA1:1,2,4,5-シクロヘキサンテトラカルボン酸二無水物、酸無水物基当量112.1g/eq.
TA2:1,2,3,4-ブタンテトラカルボン酸二無水物、酸無水物基当量99.1g/eq.
TA3:4,4’-(4,4’-イソプロピリデンジフェノキシ)ジフタル酸無水物、酸無水物基当量260.2g/eq.
TA4:4-(2,5-ジオキソテトラヒドロフラン-3-イル)-1,2,3,4-テトラヒドロナフタレン-1,2-ジカルボン酸無水物、酸無水物基当量150.1g/eq.
DA1:プリアミン1075(ダイマージアミン)
DA2:4,4’-(ヘキサフルオロイソプロピリデン)ビス(2-アミノフェノール)
DA3:1,12-ドデカンジアミン
DA4:D-2000(ハンツマン社製ポリエーテルジアミン、分子量2000)
MA1:m-アミノフェノール
MA2:o-アミノフェノール
MA3:p-アミノフェノール
MA4:4-ヒドロキシフェネチルアミン(チラミン)
表1~3に記載の単量体を用いた以外は、合成例1と同様の方法によりポリイミド樹脂P2~P30を得た。
表1等の略称の内容を以下に示す。
TA1:1,2,4,5-シクロヘキサンテトラカルボン酸二無水物、酸無水物基当量112.1g/eq.
TA2:1,2,3,4-ブタンテトラカルボン酸二無水物、酸無水物基当量99.1g/eq.
TA3:4,4’-(4,4’-イソプロピリデンジフェノキシ)ジフタル酸無水物、酸無水物基当量260.2g/eq.
TA4:4-(2,5-ジオキソテトラヒドロフラン-3-イル)-1,2,3,4-テトラヒドロナフタレン-1,2-ジカルボン酸無水物、酸無水物基当量150.1g/eq.
DA1:プリアミン1075(ダイマージアミン)
DA2:4,4’-(ヘキサフルオロイソプロピリデン)ビス(2-アミノフェノール)
DA3:1,12-ドデカンジアミン
DA4:D-2000(ハンツマン社製ポリエーテルジアミン、分子量2000)
MA1:m-アミノフェノール
MA2:o-アミノフェノール
MA3:p-アミノフェノール
MA4:4-ヒドロキシフェネチルアミン(チラミン)
表1,2に、各合成例のポリイミド樹脂の配合量(質量部)、得られたポリイミド樹脂の酸無水物基価、フェノール性水酸基(以下、PhOHともいう)価(側鎖PhOH価、末端PhOH価)、アミン価、Mw、PhOH価/全官能基価等を示す。また、X1残基100モル%に対するX1a残基のモル%、X2残基を得るための単量体(仕込み量)100質量%に対するX2dを得るための単量体(仕込み量)の質量%を示す。なお、本明細書において全官能基価とは、アミノ基価+酸無水物基価+フェノール性水酸基価の合計官能基価のことをいうものとする。
実施例および比較例で使用した材料の詳細を下記に示す。
(架橋剤(B))
(B)-1:エポキシ基含有化合物(b1)、デナコールEX-614B(ナガセケムテックス社製、ソルビトールポリグリシジルエーテル、4官能、官能基当量173g/eq.)
(B)-2:エポキシ基含有化合物(b1ー2)、jER828(三菱ケミカル社製、ビスフェノール A型エポキシ、2官能、官能基当量188g/eq.)
(B)-3:シアネートエステル化合物(b2)、BAD(三菱ガス化学社製、ビスフェノール A型シアン酸エステル、2官能、官能基当量 139)
(B)-4:イソシアネート基含有化合物(b3)、デュラネートTKA-100(旭化成社製、イソシアヌレート型イソシアネート化合物、3官能、官能基当量:180g/eq.)
(B)-5:金属キレート化合物(b4)、オルガチックスZC-150(マツモトファインケミカル社製、有機ジルコニア化合物、4官能、官能基当量122g/eq.)
(B)-6:カルボジイミド基含有化合物(b5)、カルボジライトV―05(日清紡ケミカル社製、カルボジイミド基含有化合物、3官能以上、官能基当量:262g/eq.)
(B)-7:マレイミド基含有化合物(b6):BMI‐3000(大和化成工業社製、ビスフェノール A ジフェニルエーテルビスマレイミド、2官能、官能基当量285.3g/eq.)
(B)-8:(b7):N-12(ドデカン二酸ジヒドラジド)
(架橋剤(B))
(B)-1:エポキシ基含有化合物(b1)、デナコールEX-614B(ナガセケムテックス社製、ソルビトールポリグリシジルエーテル、4官能、官能基当量173g/eq.)
(B)-2:エポキシ基含有化合物(b1ー2)、jER828(三菱ケミカル社製、ビスフェノール A型エポキシ、2官能、官能基当量188g/eq.)
(B)-3:シアネートエステル化合物(b2)、BAD(三菱ガス化学社製、ビスフェノール A型シアン酸エステル、2官能、官能基当量 139)
(B)-4:イソシアネート基含有化合物(b3)、デュラネートTKA-100(旭化成社製、イソシアヌレート型イソシアネート化合物、3官能、官能基当量:180g/eq.)
(B)-5:金属キレート化合物(b4)、オルガチックスZC-150(マツモトファインケミカル社製、有機ジルコニア化合物、4官能、官能基当量122g/eq.)
(B)-6:カルボジイミド基含有化合物(b5)、カルボジライトV―05(日清紡ケミカル社製、カルボジイミド基含有化合物、3官能以上、官能基当量:262g/eq.)
(B)-7:マレイミド基含有化合物(b6):BMI‐3000(大和化成工業社製、ビスフェノール A ジフェニルエーテルビスマレイミド、2官能、官能基当量285.3g/eq.)
(B)-8:(b7):N-12(ドデカン二酸ジヒドラジド)
(紫外線吸収剤(C))
(C)-1:Tinuvin326(BASFジャパン社製、ベンゾトリアゾール含有化合物)
(フィラー(D))
(D)-1:SC2050-MB(アドマテックス社製、シリカ、平均粒子径D50;0.5μm)
(D)-2:SP-2(デンカ社製、窒化ホウ素、平均粒子径D50;4.0μm)
(D)-3:エクソリットOP935(クラリアント社製、ホスフィン酸アルミニウム塩、平均粒子径D50;2.5μm)
(D)-4:KT-300(喜多村社製、フッ素系フィラー、平均粒子径D50;10.0μm)
(D)-5:E101―S(住友化学社製、液晶ポリマー、平均粒子径D50;17.5μm)
(C)-1:Tinuvin326(BASFジャパン社製、ベンゾトリアゾール含有化合物)
(フィラー(D))
(D)-1:SC2050-MB(アドマテックス社製、シリカ、平均粒子径D50;0.5μm)
(D)-2:SP-2(デンカ社製、窒化ホウ素、平均粒子径D50;4.0μm)
(D)-3:エクソリットOP935(クラリアント社製、ホスフィン酸アルミニウム塩、平均粒子径D50;2.5μm)
(D)-4:KT-300(喜多村社製、フッ素系フィラー、平均粒子径D50;10.0μm)
(D)-5:E101―S(住友化学社製、液晶ポリマー、平均粒子径D50;17.5μm)
[実施例1]
<<塗布液の製造>>
固形分換算で合成例1のポリイミド樹脂(P1)を100部、架橋剤((B)-1)を5部、紫外線吸収剤(C)-1を7.0部(不揮発分に対して5.0質量%)、フィラー(D)-1を28.0部(不揮発分に対して20.0質量%)容器に仕込み、不揮発分濃度が30%になるように混合溶剤(トルエン:MEK=9:1(質量比))を加え、ディスパーで10分攪拌して塗布液を得た。
<<塗布液の製造>>
固形分換算で合成例1のポリイミド樹脂(P1)を100部、架橋剤((B)-1)を5部、紫外線吸収剤(C)-1を7.0部(不揮発分に対して5.0質量%)、フィラー(D)-1を28.0部(不揮発分に対して20.0質量%)容器に仕込み、不揮発分濃度が30%になるように混合溶剤(トルエン:MEK=9:1(質量比))を加え、ディスパーで10分攪拌して塗布液を得た。
<<接着シートの製造>>
得られた塗布液を、ドクターブレードを使用して乾燥後の厚さが25μmとなるように、厚さ50μmの重剥離フィルム(重離型剤がコーティングされたポリエチレンテレフタレート(PET)フィルム)上に均一塗工して100℃で2分乾燥させた。その後、室温まで冷却し、片面剥離フィルム付き接着シートを得た。次いで、得られた片面剥離フィルム付き接着性樹脂シートの接着シート面を厚さ50μmの軽剥離フィルム(軽離型剤がコーティングされたポリエチレンテレフタレート(PET)フィルム)に重ね合わせ、重剥離フィルム/接着シート/軽剥離フィルムからなる両面剥離フィルム付き接着シートを得た。そして、後述する評価を行った。結果を表3に示す。
得られた塗布液を、ドクターブレードを使用して乾燥後の厚さが25μmとなるように、厚さ50μmの重剥離フィルム(重離型剤がコーティングされたポリエチレンテレフタレート(PET)フィルム)上に均一塗工して100℃で2分乾燥させた。その後、室温まで冷却し、片面剥離フィルム付き接着シートを得た。次いで、得られた片面剥離フィルム付き接着性樹脂シートの接着シート面を厚さ50μmの軽剥離フィルム(軽離型剤がコーティングされたポリエチレンテレフタレート(PET)フィルム)に重ね合わせ、重剥離フィルム/接着シート/軽剥離フィルムからなる両面剥離フィルム付き接着シートを得た。そして、後述する評価を行った。結果を表3に示す。
[実施例2~59、比較例1~9]
表4~8に記載の配合成分および配合量に変更する以外は実施例1と同様の方法により、実施例2~59、比較例1~9に係る塗布液を調製し、両面剥離フィルム付き接着シートを得た。各評価結果も合わせて表4~8に示す。なお、表中の空欄は添加していないことを意味する。
表4~8に記載の配合成分および配合量に変更する以外は実施例1と同様の方法により、実施例2~59、比較例1~9に係る塗布液を調製し、両面剥離フィルム付き接着シートを得た。各評価結果も合わせて表4~8に示す。なお、表中の空欄は添加していないことを意味する。
α.LCP基材とのラミネート性
両面剥離フィルム付き接着シートから軽剥離フィルムを剥がし、露出した接着シート面を、50μmのLCPフィルムと12μmの銅箔とが積層されてなる片面銅張積層板(クラレ社製、ベクスター(登録商標)FCCL Fxx‐05012)のLCP側に真空ラミネーター(ニッコー・マテリアルズ社製 小型加圧式真空ラミネーターV-130)で接着した。なお、真空ラミネート条件は加熱温度90℃、真空時間60秒、真空到達圧2hPa、圧力0.4MPa、加圧時間60秒とした。
次いで、重剥離フィルムを剥がし、露出した接着シート面に、2枚目の片面銅張積層板の銅箔側を同様に真空ラミネーターにて接着し、銅箔/LCPフィルム/接着シート/LCPフィルム/銅箔という積層構成の評価用サンプルαを作製した。
両面剥離フィルム付き接着シートから軽剥離フィルムを剥がし、露出した接着シート面を、50μmのLCPフィルムと12μmの銅箔とが積層されてなる片面銅張積層板(クラレ社製、ベクスター(登録商標)FCCL Fxx‐05012)のLCP側に真空ラミネーター(ニッコー・マテリアルズ社製 小型加圧式真空ラミネーターV-130)で接着した。なお、真空ラミネート条件は加熱温度90℃、真空時間60秒、真空到達圧2hPa、圧力0.4MPa、加圧時間60秒とした。
次いで、重剥離フィルムを剥がし、露出した接着シート面に、2枚目の片面銅張積層板の銅箔側を同様に真空ラミネーターにて接着し、銅箔/LCPフィルム/接着シート/LCPフィルム/銅箔という積層構成の評価用サンプルαを作製した。
評価用サンプルαから幅100mm、長さ100mmの試験片を切り出し、23℃相対湿度50%の雰囲気下で24時間以上保管した。そして、23℃相対湿度50%の雰囲気下で、引っ張り速度50mm/minで90°ピール剥離試験を行い、接着強度(N/cm)を測定した。
A:2N/cm以上。極めて良好な結果である。
B:1N/cm以上、2N/cm未満。良好な結果である。
C:0.5N/cm以上、1N/cm未満。実用範囲内である。
D:0.5N/cm未満。実用不可。
A:2N/cm以上。極めて良好な結果である。
B:1N/cm以上、2N/cm未満。良好な結果である。
C:0.5N/cm以上、1N/cm未満。実用範囲内である。
D:0.5N/cm未満。実用不可。
β.硬化物のめっき液耐性
硬化物のめっき液耐性は、各試験片に対し、後述するIおよびIIのめっき試験を行った後の外観により評価した。
[I.酸性めっき試験]
前記両面剥離フィルム付き接着シートを65mm×65mmの大きさにカットし、軽剥離フィルムを剥離した。そして、剥離により露出した接着シート面を、新日鉄住金化学社製の2層のCCL[エスパネックスMC18-25-00FRM]銅面と合わせて90℃でラミネートし、続いて180℃、2.0MPaの条件で60分圧着処理を行った。最後に重剥離フィルムを剥離し、評価用試験片を作製した。この試験片に対して、上記両面剥離フィルム付き接着シートから軽剥離フィルムを剥がし、露出した接着シート面に対し、下記a~gの手順及び条件に従って無電解ニッケル処理を行った。
a.酸性脱脂工程:40℃のICPクリーンS-135K(奥野製薬工業社製)に4分間浸漬。
b.ソフトエッチング工程:30℃の過硫酸ナトリウムに1分間浸漬。
c.デスマット工程:25℃の硫酸に1分間浸漬。
d.プリディップ工程:25℃の塩酸に30秒間浸漬。
e.活性化工程:30℃のICPアクセラ(奥野製薬工業社製)に1分間浸漬。
f.ポストディップ工程:25℃の硫酸に1分間浸漬。
g.無電解ニッケルめっき工程:85℃のIPニコロンFPF(奥野製薬工業社製)に20分間浸漬。
[II.アルカリ性めっき試験]
酸めっき試験と同様の方法にて、評価用試験片を作製し、この試験片に対して、下記s~wの手順及び条件に従って、無電解ニッケル処理を行った。
s.アルカリ性脱脂工程:50℃のアルカリ性脱脂剤(奥野製薬工業社製エースクリーンA-220(商標名)50g/L水溶液)に5分間浸漬。
t.エッチング処理工程:無水クロム酸400g/L及び98%硫酸400g/Lを含む水溶液中に67℃で10分間浸漬。
u.活性化工程:98%硫酸を20mL/L含有する水溶液中に25℃で2分間浸漬。
v.触媒活性付与:25℃の触媒活性化液(奥野製薬工業(株)製TSPアクチベーターコンク(商標名)10mL/Lを含有する水溶液)に2分間浸漬。
w.無電解ニッケルめっき工程:アンモニアアルカリタイプの自己触媒型無電解ニッケルめっき液(奥野製薬工業(株)製化学ニッケルA(商標名)160mL/L、化学ニッケルB(商標名)160mL/Lを含有するpH9の水溶液)中に40℃で5分間浸漬。
硬化物のめっき液耐性は、各試験片に対し、後述するIおよびIIのめっき試験を行った後の外観により評価した。
[I.酸性めっき試験]
前記両面剥離フィルム付き接着シートを65mm×65mmの大きさにカットし、軽剥離フィルムを剥離した。そして、剥離により露出した接着シート面を、新日鉄住金化学社製の2層のCCL[エスパネックスMC18-25-00FRM]銅面と合わせて90℃でラミネートし、続いて180℃、2.0MPaの条件で60分圧着処理を行った。最後に重剥離フィルムを剥離し、評価用試験片を作製した。この試験片に対して、上記両面剥離フィルム付き接着シートから軽剥離フィルムを剥がし、露出した接着シート面に対し、下記a~gの手順及び条件に従って無電解ニッケル処理を行った。
a.酸性脱脂工程:40℃のICPクリーンS-135K(奥野製薬工業社製)に4分間浸漬。
b.ソフトエッチング工程:30℃の過硫酸ナトリウムに1分間浸漬。
c.デスマット工程:25℃の硫酸に1分間浸漬。
d.プリディップ工程:25℃の塩酸に30秒間浸漬。
e.活性化工程:30℃のICPアクセラ(奥野製薬工業社製)に1分間浸漬。
f.ポストディップ工程:25℃の硫酸に1分間浸漬。
g.無電解ニッケルめっき工程:85℃のIPニコロンFPF(奥野製薬工業社製)に20分間浸漬。
[II.アルカリ性めっき試験]
酸めっき試験と同様の方法にて、評価用試験片を作製し、この試験片に対して、下記s~wの手順及び条件に従って、無電解ニッケル処理を行った。
s.アルカリ性脱脂工程:50℃のアルカリ性脱脂剤(奥野製薬工業社製エースクリーンA-220(商標名)50g/L水溶液)に5分間浸漬。
t.エッチング処理工程:無水クロム酸400g/L及び98%硫酸400g/Lを含む水溶液中に67℃で10分間浸漬。
u.活性化工程:98%硫酸を20mL/L含有する水溶液中に25℃で2分間浸漬。
v.触媒活性付与:25℃の触媒活性化液(奥野製薬工業(株)製TSPアクチベーターコンク(商標名)10mL/Lを含有する水溶液)に2分間浸漬。
w.無電解ニッケルめっき工程:アンモニアアルカリタイプの自己触媒型無電解ニッケルめっき液(奥野製薬工業(株)製化学ニッケルA(商標名)160mL/L、化学ニッケルB(商標名)160mL/Lを含有するpH9の水溶液)中に40℃で5分間浸漬。
Iの処理を行った評価用試験片の外観を目視で観察し、硬化後接着層の膨れ、剥がれ等の異常の有無を確認した。そして、異常の無いものは、更にIの工程を3回繰り返した。IIの評価用試験片も同様に試験を行った。
この試験はめっき液に対する硬化層の耐性を外観で評価するものであり、a~gの繰り返し回数で耐性を評価した。
A:I,IIいずれの試験片においても、3回目の浸漬後も外観不良なし。極めて良好。
B:I,IIいずれの試験片においても、2回目の浸漬までは外観不良が無いが、3回目の浸漬後にはいずれかの試験片において外観不良が発生。良好。
C:I,IIいずれの試験片においても、1回目の浸漬までは外観不良が無いが、2回目の浸漬後にはいずれかの試験片において外観不良発生。実用上問題ない。
D:I,IIいずれかの試験片において1回目の浸漬で外観不良発生。実用不可。
この試験はめっき液に対する硬化層の耐性を外観で評価するものであり、a~gの繰り返し回数で耐性を評価した。
A:I,IIいずれの試験片においても、3回目の浸漬後も外観不良なし。極めて良好。
B:I,IIいずれの試験片においても、2回目の浸漬までは外観不良が無いが、3回目の浸漬後にはいずれかの試験片において外観不良が発生。良好。
C:I,IIいずれの試験片においても、1回目の浸漬までは外観不良が無いが、2回目の浸漬後にはいずれかの試験片において外観不良発生。実用上問題ない。
D:I,IIいずれかの試験片において1回目の浸漬で外観不良発生。実用不可。
γ.硬化物のヒートサイクル試験後の絶縁信頼性
図1~図4を参照して評価方法を説明する。厚さ12μmの銅箔と厚さ25μmポリイミドフィルムの積層体をエッチング処理し、ポリイミドフィルム1上にカソード電極接続点2’を備えたカソード電極用櫛型信号配線2と、アノード電極接続点3’を備えたアノード電極用櫛型信号配線3とをそれぞれ形成した(図1参照)。ライン/スペースは0.05mm/0.05mmとした。
次いで、カソード電極用櫛型信号配線2およびアノード電極用櫛型信号配線3が形成された面上に、両面剥離フィルム付き接着シートの軽剥離フィルムを剥がして接着シート面を貼付した。このとき、カソード電極接続点2’付近およびアノード電極接続点3’付近が露出するようにした。そして、真空ラミネーターにて接着した。その後、重剥離フィルムを剥離し、接着シート4を露出させた(図2参照)。この接着シート4上に、絶縁層5b、銅層5aの2層構造の片面銅張積層板(MC18-25-00FRM)5の絶縁層5bが接着シート4と接するようにして、真空ラミネーターで接着した。そして、熱プレスにて180℃、1時間、2MPaで熱硬化させて、接着シート4の硬化層4’とし、評価用積層板γを得た(図3,図4参照)。
図1~図4を参照して評価方法を説明する。厚さ12μmの銅箔と厚さ25μmポリイミドフィルムの積層体をエッチング処理し、ポリイミドフィルム1上にカソード電極接続点2’を備えたカソード電極用櫛型信号配線2と、アノード電極接続点3’を備えたアノード電極用櫛型信号配線3とをそれぞれ形成した(図1参照)。ライン/スペースは0.05mm/0.05mmとした。
次いで、カソード電極用櫛型信号配線2およびアノード電極用櫛型信号配線3が形成された面上に、両面剥離フィルム付き接着シートの軽剥離フィルムを剥がして接着シート面を貼付した。このとき、カソード電極接続点2’付近およびアノード電極接続点3’付近が露出するようにした。そして、真空ラミネーターにて接着した。その後、重剥離フィルムを剥離し、接着シート4を露出させた(図2参照)。この接着シート4上に、絶縁層5b、銅層5aの2層構造の片面銅張積層板(MC18-25-00FRM)5の絶縁層5bが接着シート4と接するようにして、真空ラミネーターで接着した。そして、熱プレスにて180℃、1時間、2MPaで熱硬化させて、接着シート4の硬化層4’とし、評価用積層板γを得た(図3,図4参照)。
次いで、評価用積層板γに、ヒートサイクル処理を行った。評価用積層板γを冷熱衝撃装置(「TSE‐11‐A」、エスペック社製)に投入し、高温さらし:125℃、15分、低温さらし:-50℃、15分の曝露条件にて交互曝露を200回実施した。
その後、取り出した評価用積層板γを85℃-85%RH(相対湿度)の雰囲気下で、アノード電極接続点3’にアノード電極を接続し、カソード電極接続点2’にカソード電極を接続した上で、電圧50Vの印加を1000時間継続した。そして1000時間経過するまでの抵抗値の変化を継続して測定した。なお「リークタッチ」とは、短絡による絶縁破壊があり、瞬間的に抵抗が低下し電流が流れることをいう。リークタッチがない場合は絶縁性が低下しない。評価基準は以下の通りである。
A:1000時間経過後の抵抗値が1×1010Ω以上、且つリークタッチ無し。極めて良好。
B:1000時間経過後の抵抗値が1×108Ω以上、1×1010Ω未満、且つリークタッチ無し。良好。
C:A、Bに該当せず、1000時間経過後の抵抗値が1×107Ω以上、且つリークタッチ1回以下。実用上問題ない。
D:A~Cに該当しない。実用不可。
A:1000時間経過後の抵抗値が1×1010Ω以上、且つリークタッチ無し。極めて良好。
B:1000時間経過後の抵抗値が1×108Ω以上、1×1010Ω未満、且つリークタッチ無し。良好。
C:A、Bに該当せず、1000時間経過後の抵抗値が1×107Ω以上、且つリークタッチ1回以下。実用上問題ない。
D:A~Cに該当しない。実用不可。
δ.硬化層のレーザー加工性
図5を参照して接着シートの硬化層のレーザー加工性の評価方法を説明する。両面剥離フィルム付き接着シートから軽剥離フィルムを剥がし、露出した接着シート4面を、50μmのポリイミドフィルム12の両面に12μmの銅箔11が積層されてなる両面銅張積層板10の一方の面の銅箔11に接着した。次いで、重剥離フィルムを剥がし、露出した接着シート4面に、50μmのポリイミドフィルム22と12μmの銅箔21とが積層されてなる片面銅張積層板20のポリイミドフィルム22側を同様に真空ラミネーターにて接着した。その後、熱プレスにて180℃、1時間、2MPaで熱硬化させ、銅箔11/ポリイミドフィルム12/銅箔11/接着シートの硬化層4’/ポリイミドフィルム22/銅箔21の積層構成を有する評価サンプルδを得た。
図5を参照して接着シートの硬化層のレーザー加工性の評価方法を説明する。両面剥離フィルム付き接着シートから軽剥離フィルムを剥がし、露出した接着シート4面を、50μmのポリイミドフィルム12の両面に12μmの銅箔11が積層されてなる両面銅張積層板10の一方の面の銅箔11に接着した。次いで、重剥離フィルムを剥がし、露出した接着シート4面に、50μmのポリイミドフィルム22と12μmの銅箔21とが積層されてなる片面銅張積層板20のポリイミドフィルム22側を同様に真空ラミネーターにて接着した。その後、熱プレスにて180℃、1時間、2MPaで熱硬化させ、銅箔11/ポリイミドフィルム12/銅箔11/接着シートの硬化層4’/ポリイミドフィルム22/銅箔21の積層構成を有する評価サンプルδを得た。
評価サンプルδに対し、UV-YAGレーザー(Model5330、ESI社製)を用いて、片面銅張積層板20の銅箔21側よりレーザーを照射し、接着シートの硬化層4’と両面銅張積層板10との境界まで直径150μmのブラインドビア加工を行った(図5参照)。次いで、ブラインドビア部30の断面をレーザー顕微鏡(キーエンス社製VK-X100)にて倍率20~500倍程度で観察し、熱硬化性接着シートの硬化層4’に生じたサイドエッチング31(設計した開口径以上に水平方向が削られること)の最大長を測定した。評価基準は以下の通りとした。
A:5μm以下。極めて良好な結果である。
B:5μmより大きく7μm以下。良好な結果である。
C:7μmより大きく10μm以下。実用範囲内である。
D:10μmより大きい。実用不可。
A:5μm以下。極めて良好な結果である。
B:5μmより大きく7μm以下。良好な結果である。
C:7μmより大きく10μm以下。実用範囲内である。
D:10μmより大きい。実用不可。
ω.硬化層の屈曲性
各実施例・比較例の両面剥離フィルム付き接着シートを65mm×65mmの大きさにカットし、軽剥離フィルムを剥離した。そして、剥離により露出した接着シート面を、プリント配線板(ポリイミド上に銅回路が形成された櫛型パターン(導体パターン幅/スペース幅=50μm/50μm、導体の厚み12μm、ポリイミドの厚み25μm))に90℃でラミネートし、更に接着シートの反対側の面の重剥離フィルムを剥離し、厚さが25μmのポリイミドフィルム[東レ・デュポン(株)製「カプトン100H」]に90℃でラミネートすることで、ポリイミドフィルム/樹脂シート/プリント配線板(ポリイミド上に銅回路が形成された櫛型パターン)の3層構成のフィルムを作製した。続いて160℃、1.0MPaの条件で30分圧着処理を行った。さらに、この試験片を160℃で2時間熱硬化させ、評価用試験片を作製した。
この評価用試験片を、ポリイミドフィルム面が外側になるよう180度折り曲げて(試験片の一辺と対向する他辺がギャップをもって対向するように折り曲げて)、上側に配置されたポリイミドフィルム上に1kgの荷重を10秒載せ、その後、評価用試験片を元の平面状態に戻した。これを折り曲げ回数1回とした。接着シートの折り曲げ部位のひび割れの有無を(株)キーエンス製マイクロスコープ「VHX-900」で観察し、クラックが発生するまでの回数を次の基準で評価した。
A:20回屈曲させてもクラック(ひび割れ)が見られない。極めて良好な結果である。
B:10回屈曲させてもクラックが見られない。20回までにクラック発生。良好な結果である。
C:5回屈曲させてもクラックが見られない。10回までにクラック発生。実用範囲内である。
D:5回屈曲させるまでにクラック発生。実用不可。
各実施例・比較例の両面剥離フィルム付き接着シートを65mm×65mmの大きさにカットし、軽剥離フィルムを剥離した。そして、剥離により露出した接着シート面を、プリント配線板(ポリイミド上に銅回路が形成された櫛型パターン(導体パターン幅/スペース幅=50μm/50μm、導体の厚み12μm、ポリイミドの厚み25μm))に90℃でラミネートし、更に接着シートの反対側の面の重剥離フィルムを剥離し、厚さが25μmのポリイミドフィルム[東レ・デュポン(株)製「カプトン100H」]に90℃でラミネートすることで、ポリイミドフィルム/樹脂シート/プリント配線板(ポリイミド上に銅回路が形成された櫛型パターン)の3層構成のフィルムを作製した。続いて160℃、1.0MPaの条件で30分圧着処理を行った。さらに、この試験片を160℃で2時間熱硬化させ、評価用試験片を作製した。
この評価用試験片を、ポリイミドフィルム面が外側になるよう180度折り曲げて(試験片の一辺と対向する他辺がギャップをもって対向するように折り曲げて)、上側に配置されたポリイミドフィルム上に1kgの荷重を10秒載せ、その後、評価用試験片を元の平面状態に戻した。これを折り曲げ回数1回とした。接着シートの折り曲げ部位のひび割れの有無を(株)キーエンス製マイクロスコープ「VHX-900」で観察し、クラックが発生するまでの回数を次の基準で評価した。
A:20回屈曲させてもクラック(ひび割れ)が見られない。極めて良好な結果である。
B:10回屈曲させてもクラックが見られない。20回までにクラック発生。良好な結果である。
C:5回屈曲させてもクラックが見られない。10回までにクラック発生。実用範囲内である。
D:5回屈曲させるまでにクラック発生。実用不可。
フェノール性水酸基を有しないポリイミド樹脂を用いた組成物は、比較例1,2に示すように、めっき液耐性が劣っていた。また、ダイマージアミンおよび/又はダイマージイソシアネートに由来する残基X2dを有しないポリイミド樹脂を用いた比較例3は、LCP基材へのラミネート性に劣っていた。更に、貯蔵弾性率G’が1.0×107Paとなる温度が90℃を超えるポリイミド樹脂を用いた比較例4もLCP基材へのラミネート性に劣っていた。また、架橋剤(B)の量が、ポリイミド樹脂(A)100質量部あたり、0.5~30質量部の範囲外の比較例5~8は、ヒートサイクル試験後のマイグレーション耐性等において劣っていた。一方、本発明に係る実施例1~実施例59は、低温・短時間においてもLCP基材にラミネート性に優れていることを確認できた。また、硬化物において耐アルカリ性および耐酸性に優れ、更にヒートサイクル試験後の絶縁信頼性に優れることが確認できた。
この出願は、2021年12月13日に出願された日本出願特願2021-201930を基礎とする優先権を主張し、その開示の全てをここに取り込む。
本発明の熱硬化性組成物は、接着シートとして好適である。また、この接着シートは、プリント配線板をはじめとする各種部材間の接合に用いる接着シートとして好適である。更に、本発明の熱硬化性組成物の硬化物は、発熱体とヒートシンクとの接着層あるいはヒートスプレッダーとして好適である。また、基板上に搭載された一種または複数の電子部品を被覆する放熱層としても好適である。
1 ポリイミドフィルム
2 カソード電極用櫛型信号配線
2’ カソード電極接続点
3 アノード電極用櫛型信号配線
3’ アノード電極接続点
4 接着シート
4’ 硬化層
5 片面銅張積層板
5a 銅層
5b 絶縁層
10 両面銅張積層板
11 銅箔
12 ポリイミドフィルム
20 片面銅張積層板
21 銅箔
22 ポリイミドフィルム
30 ブラインドビア部
31 サイドエッチング
2 カソード電極用櫛型信号配線
2’ カソード電極接続点
3 アノード電極用櫛型信号配線
3’ アノード電極接続点
4 接着シート
4’ 硬化層
5 片面銅張積層板
5a 銅層
5b 絶縁層
10 両面銅張積層板
11 銅箔
12 ポリイミドフィルム
20 片面銅張積層板
21 銅箔
22 ポリイミドフィルム
30 ブラインドビア部
31 サイドエッチング
Claims (9)
- ポリイミド樹脂(A)、および官能基を2以上有する架橋剤(B)を含む熱硬化性組成物であって、
ポリイミド樹脂(A)は、一般式(1):
で表される構造の繰り返し単位を有し、且つフェノール性水酸基を有しており、
前記X2の少なくとも一部は、ダイマージアミンおよび/又はダイマージイソシアネートに由来する残基X2dであり、
ポリイミド樹脂(A)は、貯蔵弾性率G’が1.0×107Paとなる温度が0~90℃のいずれかにあり、
架橋剤(B)は、エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)、イソシアネート基含有化合物(b3)、金属キレート化合物(b4)、カルボジイミド基含有化合物(b5)およびマレイミド基含有化合物(b6)からなる群から選択される一種以上を含み、
エポキシ基含有化合物(b1)、シアネートエステル化合物(b2)、イソシアネート基含有化合物(b3)、金属キレート化合物(b4)、カルボジイミド基含有化合物(b5)およびマレイミド基含有化合物(b6)の合計含有量が、ポリイミド樹脂(A)100質量部に対して0.5~10質量部である熱硬化性組成物。 - 180℃、60分の条件で熱硬化させた後のガラス転移温度が0~70℃であることを特徴とする請求項1記載の熱硬化性組成物。
- 前記フェノール性水酸基として、以下の(i)~(iv)の少なくともいずれかを満たすフェノール性水酸基を含む請求項1または2記載の熱硬化性組成物。
(i)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環のメタ位またはオルト位に、モノアミン由来のイミド環を形成する窒素原子が結合する。
(ii)分子鎖末端にフェノール性水酸基を有し、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、モノアミン由来のイミド環を形成する窒素原子が結合する。
(iii)前記X2の一部が、フェノール性水酸基を有するジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に、ジアミン由来のイミド環を形成する窒素原子が結合する。
(iv)前記X2の一部が、フェノール性水酸基を有するジアミン残基X2fであり、当該フェノール性水酸基を有する芳香環に直結する脂肪族基を有し、当該脂肪族基に、ジアミン由来のイミド環を形成する窒素原子が結合する。 - ポリイミド樹脂(A)中の前記X1の少なくとも一部は、脂肪族基を有するX1aであり、当該X1100モル%に対し、前記X1aを60~100モル%有することを特徴とする請求項1または2記載の熱硬化性組成物。
- 不揮発分100質量%に対し、紫外線吸収剤(C)を0.1~10質量%含むことを特徴とする請求項1または2記載の熱硬化性組成物。
- 不揮発分100質量%に対し、フィラー(D)を3~60質量%含むことを特徴とする請求項1または2記載の熱硬化性組成物。
- 請求項1~6のいずれか記載の熱硬化性組成物からなる接着シート。
- 請求項7記載の接着シートを用いて形成されるプリント配線板。
- 請求項8記載のプリント配線板を有する電子機器。