WO2023008280A1 - Corps fluorescent - Google Patents

Corps fluorescent Download PDF

Info

Publication number
WO2023008280A1
WO2023008280A1 PCT/JP2022/028200 JP2022028200W WO2023008280A1 WO 2023008280 A1 WO2023008280 A1 WO 2023008280A1 JP 2022028200 W JP2022028200 W JP 2022028200W WO 2023008280 A1 WO2023008280 A1 WO 2023008280A1
Authority
WO
WIPO (PCT)
Prior art keywords
phosphor
light
meth
acrylate
manufactured
Prior art date
Application number
PCT/JP2022/028200
Other languages
English (en)
Japanese (ja)
Inventor
翔太 内藤
正樹 神波
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Publication of WO2023008280A1 publication Critical patent/WO2023008280A1/fr

Abstract

L'invention concerne un corps fluorescent qui possède une composition chimique représentée par la formule de composition Ｓｒ(２－ｃ)Ｍ４ｃＭｇ(１－ｘ－ａ)Ｍ１ｘＭ２ａＡｌ(２２－ｂ)Ｍ３ｂＯ３６　（１） [Dans la formule (1), M1 représente un élément métallique tel qu'un manganèse, ou similaire, M2 représente un élément métallique dans lequel un Mg est substitué, M3 représente un élément métallique dans lequel un Al est substitué, M4 représente un élément métallique dans lequel un Sr est substitué, et a à c représentent la proportion de substitution de chaque élément métallique.].
PCT/JP2022/028200 2021-07-27 2022-07-20 Corps fluorescent WO2023008280A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021122262A JP2023018266A (ja) 2021-07-27 2021-07-27 蛍光体
JP2021-122262 2021-07-27

Publications (1)

Publication Number Publication Date
WO2023008280A1 true WO2023008280A1 (fr) 2023-02-02

Family

ID=85086787

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/028200 WO2023008280A1 (fr) 2021-07-27 2022-07-20 Corps fluorescent

Country Status (3)

Country Link
JP (1) JP2023018266A (fr)
TW (1) TW202321419A (fr)
WO (1) WO2023008280A1 (fr)

Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2006098032A1 (fr) * 2005-03-17 2006-09-21 Hitachi Plasma Patent Licensing Co., Ltd. Dispositif d’affichage et substance fluorescente verte
JP2006344645A (ja) * 2005-06-07 2006-12-21 Super Nova Optoelectronics Corp 白色発光装置
CN101372616A (zh) * 2007-08-24 2009-02-25 北京有色金属研究总院 真空紫外线激发的高色域覆盖率的绿色荧光粉及制造方法
CN105713288A (zh) * 2016-03-30 2016-06-29 华南农业大学 一种转光功能农膜及其制备方法与应用
CN108949168A (zh) * 2018-07-27 2018-12-07 中国地质大学（武汉） 一种紫外-蓝光激发的铝酸盐基窄带绿色荧光粉及其制备方法
WO2022102407A1 (fr) * 2020-11-13 2022-05-19 住友化学株式会社 Corps luminophore
WO2022102408A1 (fr) * 2020-11-13 2022-05-19 住友化学株式会社 Corps luminophore
WO2022102409A1 (fr) * 2020-11-13 2022-05-19 住友化学株式会社 Corps luminophore

Patent Citations (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2006098032A1 (fr) * 2005-03-17 2006-09-21 Hitachi Plasma Patent Licensing Co., Ltd. Dispositif d’affichage et substance fluorescente verte
JP2006344645A (ja) * 2005-06-07 2006-12-21 Super Nova Optoelectronics Corp 白色発光装置
CN101372616A (zh) * 2007-08-24 2009-02-25 北京有色金属研究总院 真空紫外线激发的高色域覆盖率的绿色荧光粉及制造方法
CN105713288A (zh) * 2016-03-30 2016-06-29 华南农业大学 一种转光功能农膜及其制备方法与应用
CN108949168A (zh) * 2018-07-27 2018-12-07 中国地质大学（武汉） 一种紫外-蓝光激发的铝酸盐基窄带绿色荧光粉及其制备方法
WO2022102407A1 (fr) * 2020-11-13 2022-05-19 住友化学株式会社 Corps luminophore
WO2022102408A1 (fr) * 2020-11-13 2022-05-19 住友化学株式会社 Corps luminophore
WO2022102409A1 (fr) * 2020-11-13 2022-05-19 住友化学株式会社 Corps luminophore

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
WANG QIANG, ZHONGFEI MU, SHAOAN ZHANG, XING FENG, QINGTIAN ZHANG, DAOYUN ZHU, QINGPING DU, FUGEN WU: "Adjusting the structure and luminescence properties of Sr2-xBaxMgAl22O36:Eu2+ phosphors by Sr:Ba ratio", THE JOURNAL OF BIOLOGICAL AND CHEMICAL LUMINESCENCE, vol. 33, no. 8, 9 October 2018 (2018-10-09), pages 1371 - 1376, XP093029737, DOI: 10.1002/bio.3555 *
ZHU YINGLI, LIANG YUJUN, LIU SHIQI, LI HAORAN, CHEN JIAHUI: "Narrow‐Band Green‐Emitting Sr 2 MgAl 22 O 36 :Mn 2+ Phosphors with Superior Thermal Stability and Wide Color Gamut for Backlighting Display Applications", ADVANCED OPTICAL MATERIALS, WILEY, DE, vol. 7, no. 6, 1 March 2019 (2019-03-01), DE , pages 1 - 9, XP055930468, ISSN: 2195-1071, DOI: 10.1002/adom.201801419 *

Also Published As

Publication number Publication date
TW202321419A (zh) 2023-06-01
JP2023018266A (ja) 2023-02-08

Similar Documents

Publication Publication Date Title
KR101717241B1 (ko) 질화물 적색 발광재료, 그것을 포함한 발광체 및 발광소자
JP2019508549A (ja) ナノ結晶エポキシチオール（メタ）アクリレート複合材料およびナノ結晶エポキシチオール（メタクリレート）複合フィルム
WO2022102409A1 (fr) Corps luminophore
WO2022102407A1 (fr) Corps luminophore
WO2022102408A1 (fr) Corps luminophore
KR20200091887A (ko) 반도체 발광 나노입자를 포함하는 조성물
WO2023008280A1 (fr) Corps fluorescent
WO2022220171A1 (fr) Luminophore
WO2022168705A1 (fr) Luminophore et procédé de production de luminophore
WO2022168704A1 (fr) Méthode de production de luminophore et luminophore
WO2022014521A1 (fr) Substance fluorescente
WO2022014522A1 (fr) Substance fluorescente
JP2022019600A (ja) 蛍光体
JP2022019599A (ja) 蛍光体
WO2023008281A1 (fr) Composition de résine contenant un corps fluorescent
KR20160121743A (ko) 광학시트용 수지 조성물, 이를 포함하는 광학시트 및 이의 제조방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22849342

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE