WO2022244850A1 - ポリウレタン樹脂組成物、硬化物、人工皮革、合成皮革、および皮革用表面処理剤 - Google Patents
ポリウレタン樹脂組成物、硬化物、人工皮革、合成皮革、および皮革用表面処理剤 Download PDFInfo
- Publication number
- WO2022244850A1 WO2022244850A1 PCT/JP2022/020865 JP2022020865W WO2022244850A1 WO 2022244850 A1 WO2022244850 A1 WO 2022244850A1 JP 2022020865 W JP2022020865 W JP 2022020865W WO 2022244850 A1 WO2022244850 A1 WO 2022244850A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyurethane resin
- resin composition
- mmol
- isocyanate group
- charged
- Prior art date
Abstract
Description
(1) イソシアネート基末端ウレタンプレポリマー(E)と、鎖延長剤(G)と、の反応生成物と、
中和剤(F)と、を含むポリウレタン樹脂組成物であって、
前記イソシアネート基末端ウレタンプレポリマー(E)が、
平均水酸基官能基数が2を超えるポリカーボネートポリオール(B)を含むポリオール(A)と、
有機酸(C)と、
ポリイソシアネート(D)と、の反応生成物を含み、
前記ポリウレタン樹脂組成物中、ウレア基の全含有量が、前記イソシアネート基末端ウレタンプレポリマー(E)の質量と、前記鎖延長剤(G)の質量と、の総和に対して、0.01~0.80mmol/gであり、
前記ポリカーボネートポリオール(B)のみなし平均官能基数が2.0~3.90である、ポリウレタン樹脂組成物。
(2) 前記鎖延長剤(G)が、
1個以上の一級または二級アミノ基を有するアミン化合物、および、
水、からなる群より選択される1種以上である、(1)に記載のポリウレタン樹脂組成物。
(3) 前記鎖延長剤(G)が、1個以上の一級または二級アミノ基を有するアミン化合物を含み、
前記ポリウレタン樹脂組成物中、前記アミン化合物由来のウレア基の含有量が、前記イソシアネート基末端ウレタンプレポリマー(E)の質量と、前記鎖延長剤(G)の質量と、の総和に対して0mmol/g超0.480mmol/g以下である、(1)または(2)に記載のポリウレタン樹脂組成物。
(4) 前記鎖延長剤(G)が、1個以上の一級または二級アミノ基を有するアミン化合物を含み、
前記ポリウレタン樹脂組成物中、前記アミン化合物由来のウレア基の含有量が、前記ウレア基の全含有量に対して、0mol%超95mol%以下である、(1)~(3)のいずれかに記載のポリウレタン樹脂組成物。
(5) 前記鎖延長剤(G)が、水を含み、
前記ポリウレタン樹脂組成物中、前記水由来のウレア基の含有量が、前記イソシアネート基末端ウレタンプレポリマー(E)の質量と、前記鎖延長剤(G)の質量と、の総和に対して、0mmol/g超0.80mmol/g以下である、(1)~(4)のいずれかに記載のポリウレタン樹脂組成物。
(6) 前記ポリカーボネートポリオール(B)の含有量が、前記ポリオール(A)の含有量の総和に対して、5.0質量%以上である、(1)~(5)のいずれかに記載のポリウレタン樹脂組成物。
(7) 前記ポリオール(A)の平均水酸基価が、30~150mgKOH/gである、(1)~(6)のいずれかに記載のポリウレタン樹脂組成物。
(8) 前記ポリカーボネートポリオール(B)が、
ジオール(b-1)と、多価アルコール(b-2)と、炭酸エステル(b-3)と、のエステル交換反応物を含む、または、
ジオール(b-1)と、多価アルコール(b-2)と、ポリカーボネートポリオール(b-4)と、のエステル交換反応物を含む、(1)~(7)のいずれかに記載のポリウレタン樹脂組成物。
(9) 前記ポリカーボネートポリオール(B)の水酸基価が、40~500mgKOH/gである、(1)~(8)のいずれかに記載のポリウレタン樹脂組成物。
(10) 前記ポリカーボネートポリオール(B)の数平均分子量が、400~4,000g/molである、(1)~(9)のいずれかに記載のポリウレタン樹脂組成物。
(11) 前記有機酸(C)が、ジメチロール脂肪酸である、(1)~(10)のいずれか1項に記載のポリウレタン樹脂組成物。
(12) 前記中和剤(F)が、塩基性中和剤である、(1)~(11)のいずれかに記載のポリウレタン樹脂組成物。
(13) 前記ポリオール(A)が、ジオール(a-1)を含む、(1)~(12)のいずれかに記載のポリウレタン樹脂組成物。
(14) 一液型である、(1)~(13)のいずれかに記載のポリウレタン樹脂組成物。
(15) 硬化剤(X)をさらに含有する、(1)~(13)のいずれかに記載のポリウレタン樹脂組成物。
(16) 二液型である、(15)に記載のポリウレタン樹脂組成物。
(17) イソシアネート基末端ウレタンプレポリマー(E)と、鎖延長剤(G)と、の反応生成物を含むポリウレタン樹脂組成物の硬化物であって、
前記イソシアネート基末端ウレタンプレポリマー(E)が、
平均水酸基官能基数が2を超えるポリカーボネートポリオール(B)を含むポリオール(A)と、
有機酸(C)と、
ポリイソシアネート(D)と、の反応生成物を含み、
前記ポリウレタン樹脂組成物中、ウレア基の全含有量が、前記イソシアネート基末端ウレタンプレポリマー(E)の質量と、前記鎖延長剤(G)の質量と、の総和に対して、0.01~0.80mmol/gであり、
前記ポリカーボネートポリオール(B)のみなし平均官能基数が2.0~3.90である、硬化物。
(18) (1)~(17)のいずれかに記載のポリウレタン樹脂組成物の硬化物を含む、人工皮革、または合成皮革。
(19) (1)~(17)のいずれかに記載のポリウレタン樹脂組成物の硬化物を含む、皮革用表面処理剤。
イソシアネート基末端ウレタンプレポリマー(E)は、ポリオール(A)と、有機酸(C)と、ポリイソシアネート(D)と、の反応生成物を含む。
ポリオール(A)は、平均水酸基官能基数が2を超えるポリカーボネートポリオール(B)を含む。ポリオール(A)は、ポリカーボネートポリオール(B)と、ポリカーボネートポリオール(B)とは異なるポリオール(B’)とを含んでいてよく、ポリカーボネートポリオール(B)のみを含んでいてもよい。
ポリカーボネートポリオール(B)としては例えば、以下の(α)~(β)のポリカーボネートポリオール、およびこれらの任意の2種以上の組み合わせが挙げられる。
(α) ジオール(b-1)と、多価アルコール(b-2)と、炭酸エステル(b-3)とのエステル交換反応物であるポリカーボネートポリオール(以下、「ポリカーボネートポリオール(α)」ともいう。)
(β) ジオール(b-1)と、多価アルコール(b-2)と、ポリカーボネートポリオール(b-4)とのエステル交換反応物であるポリカーボネートポリオール(以下、「ポリカーボネートポリオール(β)」ともいう。)
ポリカーボネートポリオール(α)の作製の際には、触媒を用いることが好ましい。触媒としては公知のエステル交換触媒が挙げられる。触媒としては、例えば、リチウムメトキシド、ナトリウムメトキシド、ナトリウムエトキシド、カリウムメトキシド、カリウムエトキシド等の金属アルコキシド類、リチウムアセチルアセトナート、アルミニウムアセチルアセトナート、ジルコニウムアセチルアセトナート等の金属エノラート類、炭酸リチウム、炭酸ナトリウム、炭酸カリウム等の金属炭酸塩、水酸化リチウム、水酸化ナトリウム、水酸化カリウム等の金属水酸化物、酢酸リチウム、酢酸ナトリウム、酢酸カリウム等の金属カルボン酸塩、トリメチルアミン、トリエチルアミン、ジイソプロピルエチルアミン、トリブチルアミン等の第三級アルキルアミン、ピリジン、ピラジン、キノリン等の環状アジン、N-メチルピロリジン、N-メチルピペリジン、N,N’-ジメチルピペラジン、N-メチルモルホリン、ジアザビシクロウンデセン、1,4-ジアザビシクロ[2.2.2]オクタン、1,8-ジアザビシクロ[5.4.0]ウンデセン等の第三級環状アミン、t-ブチルイミノトリス(ジメチルアミノ)ホスホラン(P1-t-Bu)、t-ブチルイミノトリ(ピロリジノ)ホスホラン、t-オクチルイミノトリス(ジメチルアミノ)ホスホラン(P1-t-Oct)、1-t-ブチル-2,2,4,4,4-ペンタキス(ジメチルアミノ)-2λ5,4λ5-カテナジ(ホスファゼン)(P2-t-Bu)、1-エチル-2,2,4,4,4-ペンタキス(ジメチルアミノ)-2λ5、4λ5-カテナジ(ホスファゼン)、1-t-ブチル-4,4,4-トリス(ジメチルアミノ)-2,2-ビス[トリス(ジメチルアミノ)ホスホラニリデンアミノ]-2λ5,4λ5-カテナジ(ホスファゼン)(P4-t-Bu)、1-tert-オクチル-4,4,4-トリス(ジメチルアミノ)-2,2-ビス[トリス(ジメチルアミノ)ホスホラニリデンアミノ]-2λ5,4λ5-カテナジ(ホスファゼン)(P4-t-Oct)等のホスファゼン類;およびこれらの任意の2種以上の組み合わせが挙げられる。中でもポリカーボネートポリオールの収率がさらに向上することから、炭酸水素カリウム、炭酸水素ナトリウム、リチウムアセテート、リチウムアセチルアセトナート、またはP4-t-Buが好ましい。
ポリカーボネートポリオール(β)の作製の際には、触媒を用いることが好ましい。触媒としては、ポリカーボネートポリオール(α)の作製の説明で挙げたものと同じものが挙げられる。中でもポリカーボネートポリオールの収率がさらに向上することから、炭酸水素カリウム、炭酸水素ナトリウム、リチウムアセテート、リチウムアセチルアセトナート、またはP4-t-Buが好ましい。
みなし平均官能基数=(ポリカーボネートポリオール(B)の平均水酸基価(mgKOH/g)×ポリカーボネートポリオール(B)のGPC測定よりPPG検量線から算出される数平均分子量(g/mol))/(56.11(KOHg/mol)×1000)
ポリカーボネートポリオール(B)の含有量は、ポリウレタン樹脂組成物中のポリオール(A)の含有量(またはポリオール(B’)の質量とポリカーボネートポリオール(B)の質量との合計)に対して、より高い軟化温度を有する硬化物の形成が可能になることから、5.0質量%以上、7.0質量%以上、10.0質量%以上、15.0質量%以上、または20.0質量%以上であってよく、100質量%以下であり、95質量%以下、90質量%以下、85質量%以下、または80質量%以下であってよい。ポリカーボネートポリオール(B)の含有量は、ポリウレタン樹脂組成物中のポリオール(A)の含有量(またはポリオール(B’)の質量とポリカーボネートポリオール(B)の質量との合計)に対して、5.0~100質量%、8.0~95質量%、10~90質量%が好ましく、15~80質量%がより好ましく、20~70質量%がさらに好ましい。ポリカーボネートポリオール(B)の含有量が上記範囲であると、ポリウレタンフィルムとして使用された場合に、100%モジュラスと耐熱性がともにさらに良好なポリウレタンフィルムが得られやすい。また、ポリカーボネートポリオール(B)の含有量が100質量%以下であると、ハンドリング性にさらに優れたポリウレタンディスパージョンが得られやすい。さらに、ポリカーボネートポリオール(B)の含有量が100質量%以下であると、100%モジュラスにさらに優れたポリウレタンフィルムが得られやすい。
ポリカーボネートポリオール(B)とは異なるポリオール(B’)としては、例えば、ポリエステルポリオール、ポリエーテルポリオール、ポリカーボネートポリオール(但し、ポリカーボネートポリオール(B)に該当する化合物は除く。)、ポリオレフィンポリオール等、およびこれらの任意の2種以上の組み合わせが挙げられる。
ポリオール(A)の平均水酸基価は30~150mgKOHが好ましく、50~130mgKOHがより好ましく、60~120mgKOHがさらに好ましい。平均水酸基価が上記範囲であると、ポリウレタンフィルムとして使用された場合に、100%モジュラスと耐熱性がともにさらに良好なポリウレタンフィルムが得られやすい傾向がある。また、平均水酸基価が150mgKOH以下であると、100%モジュラスにさらに優れるポリウレタンフィルムが得られやすい。ポリオール(A)の平均水酸基価は、ポリオール(A)中に含まれる各成分それぞれの水酸基価から算出される。ポリオール(A)の平均水酸基価の具体的な算出方法の詳細は後述する実施例に記載されるとおりである。
イソシアネート基末端ウレタンプレポリマー(E)および鎖延長剤(G)に対する架橋密度は0.02~0.47が好ましく、0.03~0.40がより好ましく、0.05~0.35がより好ましい。架橋密度が上記範囲であると、ポリウレタンフィルムとして使用された場合に、100%モジュラスと耐熱性がともにさらに良好なポリウレタンフィルムが得られやすい傾向がある。また、架橋密度が0.47以下であると、100%モジュラスにさらに優れるポリウレタンフィルムが得られやすい。
有機酸(C)は、例えば、ポリイソシアネート(D)との反応により得られるイソシアネート基末端プレポリマー(E)に親水性を付与し、最終的に得られる樹脂組成物を水性にし得る親水性基含有モノマーであってよい。
ポリイソシアネート(D)は、イソシアネート基(-N=C=O)を2個以上有する化合物である。ポリイソシアネート(D)のイソシアネート基の数は、例えば、6以下、4以下、または3以下であってよい。ポリイソシアネート(D)のイソシアネート基の数は、例えば、2~3であってよく、2であってよい。ポリイソシアネート(D)は、例えば、複数のイソシアネート基と、複数のイソシアネート基を連結する炭化水素基と、を有する化合物であってよい。
イソシアネート基末端プレポリマー(E)の一実施形態は、例えば、ポリオール(B’)と、該ポリオール(B’)とは異なるポリオールと、有機酸(C)と、ポリイソシアネート(D)との反応生成物を含み、ポリオール(B’)とは異なるポリオールが、平均水酸基官能基数が2を超えるポリカーボネートポリオール(B)であってよい。
イソシアネート基末端プレポリマー(E)は、例えば、ポリイソシアネート(D)、ポリオール(A)および有機酸(C)を、イソシアネート基のモル数が水酸基のモル数よりも過剰となる条件で、必要に応じて希釈溶剤中で反応させることを含む方法によって製造することができる。このとき公知のウレタン化触媒を用いてもよい。反応温度は0~100℃が好ましく、特に好ましくは20~90℃である。
中和剤(F)は、塩基性中和剤が好ましい。中和剤(F)としては、例えば、アンモニア、エチルアミン、トリメチルアミン、トリエチルアミン、トリイソプロピルアミン、トリブチルアミン、トリエタノールアミン、N-メチルジエタノールアミン、N-フェニルジエタノールアミン、モノエタノールアミン、ジメチルエタノールアミン、ジエチルエタノールアミン、モルホリン、N-メチルモルホリン、2-アミノ-2-エチル-1-プロパノール、高級アルキル変性モルホリン等の有機アミン類;リチウム、カリウム、ナトリウム等のアルカリ金属;水酸化ナトリウム、水酸化カリウムの無機アルカリ類;等、およびこれらの任意の2種以上の組み合わせが挙げられる。また、塗膜の耐久性や平滑性向上の観点から、アンモニア、トリメチルアミン、トリエチルアミン等の加熱によって解離する揮発性の高い中和剤が好ましい。
活性水素基を1個以上有する1級あるいは2級アミンと、
無機酸および有機酸の中和剤、4級化剤のいずれかから選択される1種以上と、からなるものが挙げられる。
なお、イソシアネート基末端プレポリマー(E)合成時、イソシアネート基に対して不活性な有機溶剤にて、任意の固形分に希釈してもよい。この有機溶剤としては、例えば、トルエン、キシレン、スワゾール(丸善石油化学社製の芳香族系炭化水素溶剤)、ソルベッソ(エクソンモービル社製の芳香族系炭化水素溶剤)等の芳香族系溶剤;ヘキサン等の脂肪族炭化水素系溶剤;シクロヘキサン、イソホロン等の脂環族炭化水素系溶剤;アセトン、メチルエチルケトン、メチルイソブチルケトン、シクロヘキサノン等のケトン系溶剤;酢酸エチル、酢酸ブチル、酢酸イソブチル等のエステル系溶剤;エチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコール-3-メチル-3-メトキシブチルアセテート、エチレングリコールエチル-3-エトキシプロピオネート等のグリコールエーテルエステル系溶剤;エチレングリコールジメチルエーテル、ジエチレングリコールジブチルエーテル、プロピレングリコールジブチルエーテル、ジプロピレングリコールジメチルエーテル等のグリコールエーテル系溶剤;テトラヒドロフラン、ジオキサン等のエーテル系溶剤;およびこれらの任意の2種以上の組み合わせが挙げられる。
鎖延長剤は、イソシアネート基末端ウレタンプレポリマー(E)と反応してポリウレタン樹脂を形成する化合物である。鎖延長剤としては、例えば、一級アミノ基(-NH2)、二級アミノ基(-NH-)、またはヒドロキシ基(-OH)等のイソシアネート基と反応し得る官能基を有する化合物、または、水(H2O)が挙げられる。
ポリウレタン樹脂組成物は、例えば、イソシアネート基末端プレポリマー(E)を、中和剤(F)により中和し、イソシアネート基末端プレポリマー(E)の中和物を得る工程と、イソシアネート基末端プレポリマー(E)の中和物を水により乳化させ、鎖延長剤(G)と反応させることにより、ポリウレタン樹脂組成物を得る工程とを含む方法によって製造することができる。
ウレア基の全含有量の下限は、ポリウレタン樹脂組成物中、イソシアネート基末端ウレタンプレポリマー(E)の質量と鎖延長剤(G)の質量との総和に対して、0.01mmol/g以上であり、例えば、0.02mmol/g以上、0.05mmol/g以上、0.10mmol/g以上、0.13mmol/g以上、または0.15mmol/g以上であってよい。ウレア基の全含有量の上限は、ポリウレタン樹脂組成物中、イソシアネート基末端ウレタンプレポリマー(E)の質量と鎖延長剤(G)の質量との総和に対して、0.80mmol/g以下であり、例えば、0.70mmol/g以下、0.60mmol/g以下、0.55mmol/g以下、0.50mmol/g以下、または0.45mmol/g以下であってよい。ウレア基の全含有量は、イソシアネート基末端ウレタンプレポリマー(E)の質量と、鎖延長剤(G)の質量と、の総和に対して、0.01~0.80mmol/gであり、例えば、0.05mmol/g以上0.75mmol/g以下、0.07mmol/g以上0.70mmol/g以下、0.13mmol/g以上0.60mmol/g以下、又は0.15mmol/g以上0.55mmol/g以下であってよい。ウレア基の全含有量が上記範囲であると、ポリウレタンフィルムとして使用された場合に、100%モジュラスと耐熱性がともにさらに良好なポリウレタンフィルムが得られやすい。また、ウレア基の全含有量が0.80mmol/g以下であると、100%モジュラスにさらに優れるポリウレタンフィルムが得られやすい。
鎖延長剤(G)が、1個以上の一級もしくは二級アミノ基を有するアミン化合物を含んでいてもよい。このとき、ポリウレタン樹脂組成物中、アミン化合物由来のウレア基の含有量は、イソシアネート基末端ウレタンプレポリマー(E)の質量と鎖延長剤(G)の質量との総和に対して、例えば、0.01mmol/g以上、0.02mmol/g以上、0.03mmol/g以上、0.05mmol/g以上、0.10mmol/g以上、0.13mmol/g以上、または0.15mmol/g以上であってよい。アミン化合物由来のウレア基の含有量の上限は、イソシアネート基末端ウレタンプレポリマー(E)の質量と鎖延長剤(G)の質量との総和に対して、例えば、0.48mmol/g以下、0.45mmol/g以下、0.40mmol/g以下、0.34mmol/g以下、0.30mmol/g以下、0.25mmol/g以下、または0.23mmol/g以下であってよい。アミン化合物由来のウレア基の含有量は、イソシアネート基末端ウレタンプレポリマー(E)の質量と、鎖延長剤(G)の質量と、の総和に対して、例えば、0mmol/g以上0.480mmol/g以下、0.01mmol/g以上0.400mmol/g以下、0.05mmol/g以上0.340mmol/g以下、又は0.130mmol/g以上0.300mmol/g以下であってよい。アミン化合物由来のウレア基濃度が上記範囲であると、ポリウレタンフィルムとして使用された場合に、100%モジュラスと耐熱性がともにさらに良好なポリウレタンフィルムが得られやすい。また、アミン化合物由来のウレア基濃度が0.480mmol/g以下であると、100%モジュラスにさらに優れるポリウレタンフィルムが得られやすい。
鎖延長剤(G)が、水を含んでいてもよい。
水由来のウレア基の含有量の下限は、ポリウレタン樹脂組成物中、イソシアネート基末端ウレタンプレポリマー(E)の質量と鎖延長剤(G)の質量との総和に対して、例えば、0.01mmol/g以上、0.02mmol/g以上、0.03mmol/g以上、0.05mmol/g以上、0.10mmol/g以上、0.13mmol/g以上、または0.15mmol/g以上であってよい。水由来のウレア基の含有量の上限は、ポリウレタン樹脂組成物中、イソシアネート基末端ウレタンプレポリマー(E)の質量と鎖延長剤(G)の質量との総和に対して、0.80mmol/g以下であり、例えば、0.70mmol/g以下、0.60mmol/g以下、0.50mmol/g以下、0.40mmol/g以下、0.30mmol/g以下、または0.25mmol/g以下であってよい。水由来のウレア基の含有量は、イソシアネート基末端ウレタンプレポリマー(E)の質量と、鎖延長剤(G)の質量と、の総和に対して、例えば、0.01mmol/g以上0.80mmol/g以下、0.05mmol/g以上0.70mmol/g以下、0.10mmol/g以上0.60mmol/g以下、又は0.15mmol/g以上0.50mmol/g以下であってよい。水由来のウレア基濃度が上記範囲であると、ポリウレタンフィルムとして使用された場合に、100%モジュラスと耐熱性がともにさらに良好なポリウレタンフィルムが得られやすい。また、水由来のウレア基濃度が0.80mmol/g以下であると、100%モジュラスにさらに優れるポリウレタンフィルムが得られやすい。
アミン化合物由来のウレア基の含有量(アミン化合物由来のウレア基比率)の下限は、ウレア基の全含有量に対して、例えば、0mol%以上、5mol%以上、10mol%以上、15mol%以上、20mol%以上、25mol%以上、または30mol%以上であってよい。ウレア基の全含有量に対するアミン化合物由来のウレア基の含有量の上限は、例えば、95mol%以下、90mol%以下、85mol%以下、80mol%以下、75mol%以下、70mol%以下、または65mol%以下であってよい。ウレア基の全含有量に対するアミン化合物由来のウレア基の含有量は、ウレア基の全含有量に対して、例えば、0~95mol%、5~90mol%、10~85mol%、15~80mol%又は20~70mol%であってよい。ウレア基の全含有量に対するアミン化合物由来のウレア基の含有量が上記範囲であると、ポリウレタンフィルムとして使用された場合に、100%モジュラスと耐熱性がともにさらに良好なポリウレタンフィルムが得られやすい。また、アミン化合物由来のウレア基濃度が100mol%以下であると、軟化温度にさらに優れるポリウレタンフィルムが得られやすい。
ポリウレタン樹脂組成物は、硬化剤(X)をさらに含んでいてもよい。
硬化剤(X)は、イソシアネート基末端ウレタンプレポリマー(E)と、鎖延長剤(G)との反応生成物を硬化させて、ポリウレタン樹脂を形成する。ポリウレタン樹脂組成物が硬化剤(X)を含む場合、該硬化剤(X)は、二液システムの一液を構成する。ポリウレタン樹脂組成物が硬化剤(X)を含まない場合、当該ポリウレタン樹脂組成物は、一液システムとして好適である。
より物性を高め、また、各種物性を付加するために、ポリウレタン樹脂組成物は、各種添加剤を含んでいてもよい。各種添加剤としては、成膜剤、粘度調節剤、ゲル化防止剤、難燃剤、可塑剤、酸化防止剤、紫外線吸収剤、抗菌剤、充填剤、内部離型剤、補強材、艶消し剤、導電性付与剤、帯電制御剤、帯電防止剤、滑剤、染料、顔料その他の加工助剤等が挙げられる。
また、ポリウレタン樹脂組成物は、一液型であっても二液型であってもよいが、一液型であることが好ましい。
硬化物の一実施形態は、イソシアネート基末端ウレタンプレポリマー(E)と、鎖延長剤(G)と、の反応生成物を含むポリウレタン樹脂組成物の硬化物であって、
前記イソシアネート基末端ウレタンプレポリマー(E)が、
平均水酸基官能基数が2を超えるポリカーボネートポリオール(B)を含むポリオール(A)と、
有機酸(C)と、
ポリイソシアネート(D)と、の反応生成物を含み、
前記ポリウレタン樹脂組成物中、ウレア基の全含有量が、前記イソシアネート基末端ウレタンプレポリマー(E)の質量と、前記鎖延長剤(G)の質量と、の総和に対して、0.01~0.80mmol/gであり、
前記ポリカーボネートポリオール(B)のみなし平均官能基数が2.0~3.90である。
一実施形態にかかる硬化物は、上述したポリウレタン樹脂組成物が硬化してなるものであって、例えば、該組成物からは中和剤(F)の一部または全部、および水の一部または全部が除かれてなる。
人工皮革または合成皮革の一実施形態は、ポリウレタン樹脂組成物の硬化物と、基材とを含む。一実施形態に係る人工皮革または合成皮革は、例えば、基材上に、ポリウレタン樹脂組成物の硬化物を形成することを含む方法によって製造することができる。また、一実施形態に係る人工皮革または合成皮革は、基材にポリウレタン樹脂組成物を含侵させ、当該ポリウレタン樹脂組成物を硬化させることを含む方法によって製造することができる。人工皮革において、基材は、例えば、編物又は織物等の基布であってよい。合成皮革において、基材は、不織布であってよい。
皮革用表面処理剤は、皮革又はその材料の表面を処理するために用いられる剤である。皮革用表面処理剤の適用対象の皮革は、例えば、合成皮革、人工皮革、又は天然皮革であってよい。
(みなし平均官能基数)
ポリカーボネートポリオール(B)のみなし平均官能基数はGPC(Gel Permeation Chromatography)測定より得られる数平均分子量と水酸基価から算出した。本来であれば、平均官能基数は真の数平均分子量と平均水酸基価から算出されるが、ポリカーボネートポリオール(B)の真の数平均分子量の算出が難しいため、GPC測定よりPPG検量線より換算される数平均分子量を用い、みなし平均官能基数として定義する。みなし平均官能基数は下記式より定義する。
みなし平均官能基数=(ポリカーボネートポリオール(B)の平均水酸基価(mgKOH/g)×ポリカーボネートポリオール(B)のGPC測定よりPPG検量線から算出される数平均分子量(g/mol))/(56.11(KOHg/mol)×1000)
ポリウレタン樹脂組成物中のウレア基は、イソシアネート基末端プレポリマー(E)中のイソシアネート基と、鎖延長剤(G)として含まれるアミン化合物および/または水との反応によって形成される。イソシアネート基と、鎖延長剤(G)との反応速度は、イソシアネート基とポリオール成分のヒドロキシ基との反応速度と比較して、非常に高いことが知られている。従って、ウレア基の全含有量はイソシアネート基末端プレポリマー(E)の未反応のイソシアネート基の含有量と一致する。以上より、イソシアネート基末端ウレタンプレポリマー(E)の質量と、鎖延長剤(G)の質量と、の総和に対するウレア基の全含有量は、下記式で定義する。
ウレア基の全含有量(mmol/g)=水由来のウレア基の含有量(mmol/g)+アミン化合物由来のウレア基の含有量(mmol/g)
アミン化合物由来のウレア基の含有量は、アミン化合物の仕込み量から算出されるアミン量より求めた。従って、イソシアネート基末端ウレタンプレポリマー(E)の質量と鎖延長剤(G)の質量との総和に対するアミン化合物由来のウレア基の含有量は、下記式で定義する。
アミン化合物由来のウレア基の含有量(mmol/g)=アミン化合物の仕込み量(g)/アミン化合物の分子量(g/mol)×一分子当たりのアミノ基の数/(ポリオール(B’)の仕込み量(g)+ポリカーボネートポリオール(B)の仕込み量(g)+有機酸(ジメチロール脂肪酸)(C)の仕込み量(g)+ポリイソシアネート(D)の仕込み量(g)+鎖延長剤(G)の仕込み量(g))×1000
イソシアネート基末端ウレタンプレポリマー(E)の質量と鎖延長剤(G)の質量との総和に対する水由来のウレア基の含有量は、下記式で定義する。
水由来のウレア基の含有量(mmol/g)=[イソシアネート基末端プレポリマー(E)の未反応のイソシアネート基の含有量(mmol/g)×((ポリオール(B’)の仕込み量(g)+ポリカーボネートポリオール(B)の仕込み量(g)+有機酸(ジメチロール脂肪酸)(C)の仕込み量(g)+ポリイソシアネート(D)の仕込み量(g)+イソシアネート基測定前の有機溶剤の仕込み量(g))/(ポリオール(B’)の仕込み量(g)+ポリカーボネートポリオール(B)の仕込み量(g)+有機酸(ジメチロール脂肪酸)(C)の仕込み量(g)+ポリイソシアネート(D)の仕込み量(g)+鎖延長剤(G)の仕込み量(g))-アミン化合物由来のウレア基濃度(mmol/g)]/2
ウレア基の全含有量に対するアミン化合物由来のウレア基の含有量(アミン化合物由来のウレア基比率)は、アミン化合物由来のウレア基の含有量を、ウレア基の全含有量で除することにより算出した。従って、ウレア基の全含有量に対するアミン化合物由来のウレア基の含有量は、下記式で定義する。
ウレア基の全含有量に対するアミン化合物由来のウレア基の含有量(mol%)=アミン化合物由来のウレア基の含有量(mmol/g)/ウレア基の全含有量(mmol/g)×100
平均水酸基価はポリオール(B’)とポリカーボネートポリオール(B)とを混合した際の水酸基価から算出した。従って、平均水酸基価は下記式より定義する。
平均水酸基価(mgKOH/g)=(ポリオール(B’)の平均水酸基価(mgKOH/g)×ポリオール(B’)の仕込み量(g)+ポリカーボネートポリオール(B)の平均水酸基価(mgKOH/g)×ポリカーボネートポリオール(B)の仕込み量(g))/(ポリオール(B’)の仕込み量(g)+ポリカーボネートポリオール(B)の仕込み量(g))
イソシアネート基末端ウレタンプレポリマー(E)および鎖延長剤(G)に対する架橋密度はポリカーボネートポリオール(B)あるいはポリオール(B’)の3官能以上の多価アルコール由来の架橋量から算出した。従って、架橋密度は、下記式で定義する。なお、架橋を形成する成分が他にもある場合には、式中の分子の「ポリカーボネートポリオール(B)」、「多価アルコール」を当該他の成分に置き換えることで同様に算出できる。
架橋密度(mmol/g)=ポリカーボネートポリオール(B)の仕込み量(g)×ポリカーボネートポリオール(B)の平均水酸基価(mgKOH/g)/56.11/1000/ポリカーボネートポリオール(B)の官能基数×(ポリカーボネートポリオール(B)の官能基数-2)/(ポリオール(B’)の仕込み量(g)+ポリカーボネートポリオール(B)の仕込み量(g)+有機酸(ジメチロール脂肪酸)(C)の仕込み量(g)+ポリイソシアネート(D)の仕込み量(g)+鎖延長剤(G)の仕込み量(g))×1000
架橋密度(mmol/g)=多価アルコールの仕込み量(g)/多価アルコールの分子量(g/mol)×(多価アルコールの官能基数-2)/(ポリオール(B’)の仕込み量(g)+ポリカーボネートポリオール(B)の仕込み量(g)+有機酸(ジメチロール脂肪酸)(C)の仕込み量(g)+ポリイソシアネート(D)の仕込み量(g)+鎖延長剤(G)の仕込み量(g))×1000
ポリウレタン樹脂組成物中のポリカーボネートポリオール(B)の含有量はポリオール(B’)とポリカーボネートポリオール(B)とを混合した際の質量比から算出した。従って、ポリカーボネートポリオール(B)の含有量は下記式より定義する。
[イソシアネート基末端プレポリマー(E)の未反応のイソシアネート基の含有量]
イソシアネート基末端プレポリマー(E)の未反応のイソシアネート基の含有量はJIS-K6806に基づき測定した。
以下の条件で、得られた組成物のGPC分析を行い、組成物の数平均分子量を測定した。結果を表1に示す。
(1)測定器:HLC-8420(東ソー社製)
(2)カラム:TSKgel(東ソー社製)
・G3000H-XL
・G3000H-XL
・G2000H-XL
・G2000H-XL
(3)移動相:THF(テトラヒドロフラン)
(4)検出器:RI(屈折率)検出器(HLC-8420付属品)
(5)温度:40℃
(6)流速:1.000ml/min
(7)検量線:以下の商品(いずれも三洋化成工業社製の2官能のポリオキシプロピレンポリオール)を用いて、検量線を得た。
・「サンニックスPP-200」(数平均分子量=200、平均官能基数:2)
・「サンニックスPP-400」(数平均分子量=400、平均官能基数:2)
・「サンニックスPP-1000」(数平均分子量=1000、平均官能基数:2)
・「サンニックスPP-2000」(数平均分子量=2000、平均官能基数:2)
・「サンニックスPP-3000」(数平均分子量=3200、平均官能基数:2)
・「サンニックスPP-4000」(数平均分子量=4160、平均官能基数:2)
(8)検量線の近似式:3次式
(9)サンプル溶液濃度:0.5質量%THF溶液
JIS K1557-1に準拠し、アセチル化試薬を用いた方法にて得られた組成物の水酸基価を測定した。結果を表1に示す。
得られた組成物をサンプルとし、該サンプルを80℃で1時間加熱した後、25℃で3日間放置した。放置後のサンプルの状態を目視により確認し、上記温度で僅かでも流動性があれば液状とし、流動性がない場合には固体とした。
攪拌機、温度計、加熱装置、冷却器を組んだ1L二口ガラス製反応器(以下、反応器Aと称する)に、トリメチロールプロパン31.3g、1,6-ヘキサンジオール413.8g、炭酸ジエチル454.9g、およびリチウムアセチルアセトナート0.045gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-1A)。
全ての操作はポリカーボネートポリオールの合成1と同様にして、ポリカーボネートポリオールを得た(PCP-1B)。
全ての操作はポリカーボネートポリオールの合成1と同様にして、ポリカーボネートポリオールを得た(PCP-1C)。
全ての操作はポリカーボネートポリオールの合成1と同様にして、ポリカーボネートポリオールを得た(PCP-1D)。
全ての操作はポリカーボネートポリオールの合成1と同様にして、ポリカーボネートポリオールを得た(PCP-1E)。
反応器Aに、トリメチロールプロパン74.4g、1,6-ヘキサンジオール393.2g、炭酸ジエチル432.4g、およびリチウムアセチルアセトナート0.045gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-2A)。
反応器Aに、トリメチロールプロパン35.2g、1,6-ヘキサンジオール298.5g、炭酸ジエチル468.8g、およびリチウムアセチルアセトナート0.045gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-3)。
反応器Aに、トリメチロールプロパン0.82g、1,6-ヘキサンジオール199.1g、炭酸ジエチル200.1g、およびリチウムアセチルアセトナート0.020gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-4)。
反応器Aに、トリメチロールプロパン3.31g、1,6-ヘキサンジオール196.81g、炭酸ジエチル199.9g、およびリチウムアセチルアセトナート0.020gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-5)。
反応器Aに、トリメチロールプロパン8.08g、1,6-ヘキサンジオール192.2g、炭酸ジエチル199.8g、およびリチウムアセチルアセトナート0.020gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-6)。
反応器Aに、トリメチロールプロパン20.53g、1,6-ヘキサンジオール180.3g、炭酸ジエチル199.2g、およびリチウムアセチルアセトナート0.020gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-7)。
反応器Aに、トリメチロールプロパン24.82g、1,6-ヘキサンジオール176g、炭酸ジエチル199.2g、およびリチウムアセチルアセトナート0.020gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-8)。
反応器Aに、トリメチロールプロパン30.43g、1,6-ヘキサンジオール170.3g、炭酸ジエチル199.2g、およびリチウムアセチルアセトナート0.020gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-9)。
反応器Aに、トリメチロールプロパン44.63g、1,6-ヘキサンジオール156.2g、炭酸ジエチル199.2g、およびリチウムアセチルアセトナート0.020gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-10)
・1,4-ブタンジオール:富士フイルム和光純薬社製
・トリメチロールプロパン:Sigma-Aldrich社製
・炭酸ジエチル:Sigma-Aldrich社製
・リチウムアセチルアセトナート:Sigma-Aldrich社製
撹拌機、温度計、窒素シール管、および冷却器を装着した容量1Lの反応器(以下、反応器Bと称する)に、N-980N(東ソー社製:数平均分子量2000;水酸基価56.11mgKOH/g;1,6-ヘキサンジオール系ポリカーボネートジオール)77.6g、1,6-ヘキサンジオール3.04g、PCP-1Aを26.9g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.286mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン1.99gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-1)を得た。
反応器Bに、N-980N 51.8g、1,6-ヘキサンジオール1.99g、PCP-1Aを53.8g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.268mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-2)を得た。
反応器Bに、N-980N 25.9g、1,6-ヘキサンジオール0.95g、PCP-1Aを80.6g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.270mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-3)を得た。
反応器Bに、N-980N 84.1g、1,6-ヘキサンジオール4.32g、PCP-2Aを15.6g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.284mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-4)を得た。
反応器Bに、N-980N 70.4g、1,6-ヘキサンジオール2.37g、PCP-2Aを31.2g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを34.7g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.280mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-5)を得た。
反応器Bに、N-980N 56.8g、1,6-ヘキサンジオール0.41g、PCP-2Aを46.8g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを34.7g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.355mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-6)を得た。
反応器Bに、N-980N 78.9g、1,6-ヘキサンジオール3.40g、PCP-1Bを27.4g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを29.9g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.170mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン0.99gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-7)を得た。
反応器Bに、N-980N 52.5g、1,6-ヘキサンジオール2.42g、PCP-1Bを54.9g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを29.9g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.169mmol/gであった。次いで、乳化および乳化後の操作は実施例7と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-8)を得た。
反応器Bに、N-980N 75.7g、1,6-ヘキサンジオール3.26g、PCP-1Bを26.3g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを32.4g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.266mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン2.99gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-9)を得た。
反応器Bに、N-980N 50.3g、1,6-ヘキサンジオール2.32g、PCP-1Bを52.6g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを32.4g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.263mmol/gであった。次いで、乳化および乳化後の操作は実施例9と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-10)を得た。
反応器Bに、N-980N 84.6g、PCP-1Bを28.2g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを25.9g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.238mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-11)を得た。
反応器Bに、N-980N 55.5g、PCP-1Bを55.5g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを27.6g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.231mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-12)を得た。
反応器Bに、N-980N 27.4g、PCP-1Bを82.3g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを29.0g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.242mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-13)を得た。
反応器Bに、N-980N 98.2g、PCP-1Cを10.9g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを27.6g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.322mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン3.98gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-14)を得た。
反応器Bに、N-980N 76.9g、1,6-ヘキサンジオール3.70g、PCP-3を26.9g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.143mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-15)を得た。
反応器Bに、N-980N 50.6g、1,6-ヘキサンジオール3.11g、PCP-3を53.7g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.223mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-16)を得た。
反応器Bに、N-980N 54.6g、1,6-ヘキサンジオール2.45g、PCP-1Dを57.1g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、ヘキサメチレンジイソシアネートを24.5g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.192mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-17)を得た。
反応器Bに、プラクセル220(ダイセル社製:数平均分子量2000;水酸基価56.11mgKOH/g;ε-カプロラクトン開環重合系エステルポリオール;平均官能基数2) 51.3g、1,6-ヘキサンジオール2.44g、PCP-1Eを53.7g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.251mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-18)を得た。
反応器Bに、N-980N 103.4g、1,6-ヘキサンジオール4.08g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.197mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-19)を得た。
反応器Bに、N-980N 99.1g、1,6-ヘキサンジオール3.91g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを33.6g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.340mmol/gであった。次いで、乳化および乳化後の操作は実施例14と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-20)を得た。
反応器Bに、N-980N 97.0g、1,6-ヘキサンジオール3.82g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを34.8g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.263mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン4.97gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-21)を得た。
反応器Bに、N-980N 101.1g、1,6-ヘキサンジオール3.56g、トリメチロールプロパン2.15g、アセトン75g、2,2-ジメチロールプロパン酸を5.43g、イソホロンジイソシアネートを35.6g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.275mmol/gであった。次いで、乳化および乳化後の操作は比較例5と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-22)を得た。
反応器Bに、N-980N 101.9g、1,6-ヘキサンジオール0.69g、トリメチロールプロパン4.29g、アセトン75g、2,2-ジメチロールプロパン酸を5.43g、イソホロンジイソシアネートを35.6g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.328mmol/gであった。次いで、乳化および乳化後の操作は比較例5と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-23)を得た。
反応器Bに、N-980N 106.8g、1,6-ヘキサンジオール1.59g、トリメチロールプロパン2.06g、アセトン75g、2,2-ジメチロールプロパン酸を5.43g、イソホロンジイソシアネートを32.0g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.305mmol/gであった。次いで、乳化および乳化後の操作は比較例5と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-24)を得た。
反応器Bに、N-980N 50.2g、1,6-ヘキサンジオール3.52g、PCP-5を53.7g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.207mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-25)を得た。
反応器Bに、N-980N 50.6g、1,6-ヘキサンジオール3.16g、PCP-6を53.7g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.229mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-26)を得た。
反応器Bに、N-980N 52.6g、1,6-ヘキサンジオール1.18g、PCP-7を53.7g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.253mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-27)を得た。
反応器Bに、N-980N 52.4g、1,6-ヘキサンジオール1.31g、PCP-8を53.7g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.268mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-28)を得た。
反応器Bに、N-980N 53.5g、1,6-ヘキサンジオール0.24g、PCP-9を53.7g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.205mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-29)を得た。
反応器Bに、N-980N 50.0g、1,6-ヘキサンジオール3.71g、PCP-4を53.7g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.224mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-30)を得た。
反応器Bに、N-980N 56.8g、PCP-10を53.7g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを31.2g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.186mmol/gであった。次いで、乳化および乳化後の操作は実施例1と同様にして水性ポリウレタン樹脂エマルジョン組成物(PUD-31)を得た。
反応器Bに、N-980N 51.2g、PCP-1Dを53.7g、1,6-ヘキサンジオール2.6g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを27.1g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.257mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン3.68gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-32)を得た。
反応器Bに、実施例24と同様にしてイソシアネート基末端ウレタンプレポリマーを得た。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.241mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン2.67gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-33)を得た。
反応器Bに、実施例24と同様にしてイソシアネート基末端ウレタンプレポリマーを得た。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.268mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン1.99gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-34)を得た。
反応器Bに、実施例24と同様にしてイソシアネート基末端ウレタンプレポリマーを得た。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.259mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン0.97gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-35)を得た。
反応器Bに、実施例24と同様にしてイソシアネート基末端ウレタンプレポリマーを得た。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.258mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン0.49gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-36)を得た。
反応器Bに、実施例24と同様にしてイソシアネート基末端ウレタンプレポリマーを得た。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.271mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を350g仕込み、乳化させた。乳化後、KL-245を0.18g加え、アミン延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-37)を得た。
反応器Bに、N-980N 55.8g、PCP-1Dを55.8g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを27.1g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、2時間45分反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.399mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン3.20gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-38)を得た。
反応器Bに、N-980N 55.8g、PCP-1Dを55.8g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを27.1g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、4時間15分反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.345mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン2.77gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-39)を得た。
反応器Bに、N-980N 55.8g、PCP-1Dを55.8g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを27.1g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、1時間20分反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.780mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン6.25gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-40)を得た。
・1,6-ヘキサンジオール:BASF-JAPAN社製
・2,2-ジメチロールプロピオン酸:東京化成工業社製
・イソホロンジイソシアネート:エボニック社製
・ヘキサメチレンジイソシアネート:東京化成工業社製
・アセトン:KHネオケム社製
・トリエチルアミン:キシダ化学社製
・イソホロンジアミン:東京化成工業社製
・ネオスタンU-600:日東化成株式会社製
・KL-245:Evonik社製
・水:精製水
実施例1~31および比較例1~9で得られたPUD-1~PUD-40水性ポリウレタン樹脂エマルジョン組成物100部に対してジプロピレングリコールジメチルエーテルを14.0部添加し、混合して主剤を得た。その主剤を乾燥膜厚が約100μmとなるように塗布し、25℃で2日間、80℃で2時間、乾燥させることにより硬化物を作製した。この硬化物を用いて、物性の評価を行った。結果を表7~10に示す。
[引張特性]
得られた硬化物を、JIS K7321に準拠して引張特性を測定した。(100%モジュラス、破断時強度、破断時伸び)
・試験装置:テンシロンUTA-500(エー・アンド・デー社製)
・測定条件:25℃×50%RH
・ヘッドスピード:200mm/分
・ダンベル4号
得られたフィルムからダンベルを用いて試験片を得た後、試験片に2cmの標線を記し、標線中央部の厚みを測定した。試験片の一方のつかみ部に所定重量のおもりを取り付け、もう一方のつかみ部をダブルクリップで挟み込み、クリップが上側となるように乾燥機内に吊り下げた後、乾燥機内を昇温し標線間距離を観測、標線間距離が4cmとなったときの温度を軟化温度として読み取った。
・処理装置:送風定温乾燥機DRK633DA(アドバンテック社製)
・おもり重量:標線中央部厚み(μm)×0.05g
・ダンベル2号(JIS K6251準拠)
・昇温速度:5℃/分
100%モジュラス、破断時強度、破断時伸び、および軟化温度の各物性値を、A、B、CおよびD(A:非常に良好、B:良好、C:普通、D:不良)で評価した。さらに、総合評価はA、BおよびD(A:非常に良好、B:良好、D不良)とした。
A:4.0MPa未満
B:4.0MPa以上5.0MPa未満
D:5.0MPa以上
<破断時強度>
A:30MPa以上
C:30MPa未満
<破断時伸び>
A:450MPa以上
C:450MPa未満
<軟化温度>
A:120℃以上
B:120℃未満90℃以上
D:90℃未満
<総合評価>
A:各物性値の評価がAのみ
B:各物性値の評価がDを含まず、少なくとも1つのBまたはCを含む
D:各物性値の評価がDを含む
攪拌機、温度計、加熱装置、冷却器を組んだ1L二口ガラス製反応器に、トリメチロールプロパン31.3g、1,6-ヘキサンジオール413.8g、炭酸ジエチル454.9g、およびリチウムアセチルアセトナート0.045gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-1F)。
攪拌機、温度計、加熱装置、冷却器を組んだ1L二口ガラス製反応器に、トリメチロールプロパン74.4g、1,6-ヘキサンジオール393.2g、炭酸ジエチル432.4g、およびリチウムアセチルアセトナート0.045gを混合し、常圧下、低沸点成分を除去しながら100~150℃で8時間反応させた。さらに反応温度を150℃としてフラスコ内の圧力を1kPaまで減圧し、さらに8時間反応を行うことでポリカーボネートポリオールを得た(PCP-2B)。
・トリメチロールプロパン:Sigma-Aldrich社製
・炭酸ジエチル:Sigma-Aldrich社製
・リチウムアセチルアセトナート:Sigma-Aldrich社製。
撹拌機、温度計、窒素シール管、および冷却器を装着した容量1Lの反応器(以下、反応基Aと称する)に、N-980N(東ソー社製:数平均分子量2000;水酸基価56.11mgKOH/g;1,6-ヘキサンジオール系ポリカーボネートジオール)51.1g、1,6-ヘキサンジオール3.07g、PCP-1Fを51.9g、アセトン75g、2,2-ジメチロールプロパン酸を5.43g、イソホロンジイソシアネートを34.6g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.356mmol/gであった。次いで、トリエチルアミンを4.10g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン2.04g、モノエタノールアミン1.83gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-41)を得た。
反応器Aに、N-980N 26.6g、PCP-1Fを79.8g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを30.5g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.349mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン1.99g、モノエタノールアミン1.78gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-42)を得た。
反応器Aに、N-980N 81.1g、1,6-ヘキサンジオール4.33g、PCP-2Aを15.1g、アセトン75g、2,2-ジメチロールプロパン酸を5.29g、イソホロンジイソシアネートを36.5g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.371mmol/gであった。次いで、トリエチルアミンを3.99g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン1.99g、モノエタノールアミン1.43gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-43)を得た。
反応器Aに、N-980N 103.1g、トリメチロールプロパンを3.00g、アセトン75g、2,2-ジメチロールプロパン酸を5.43g、イソホロンジイソシアネートを34.6g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.361mmol/gであった。次いで、トリエチルアミンを4.10g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン2.04g、モノエタノールアミン1.83gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-44)を得た。
反応器Aに、N-980N 102.0g、1,6-ヘキサンジオール4.02g、アセトン75g、2,2-ジメチロールプロパン酸を5.43g、イソホロンジイソシアネートを34.6g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.356mmol/gであった。次いで、トリエチルアミンを4.10g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン2.04g、モノエタノールアミン1.83gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-45)を得た。
反応器Aに、N-980N 97.6g、1,6-ヘキサンジオール3.85g、アセトン75g、2,2-ジメチロールプロパン酸を5.43g、イソホロンジイソシアネートを37.1g仕込み、60℃に加温し、同温度で30分撹拌した後、U-600を0.12g加え、5時間反応させた。ウレタン化終了時の未反応のイソシアネート基含有量は、上記仕込み量に対して、0.420mmol/gであった。次いで、トリエチルアミンを4.10g仕込んでカルボキシル基を中和した後、撹拌しながら水を320g仕込み、乳化させた。乳化後、KL-245を0.18g加え、30分以内にアミン水(水30g、イソホロンジアミン4.09g、モノエタノールアミン1.83gを配合)を仕込み、アミン鎖延長反応を40℃にて12時間行った。FT-IRによりイソシアネート基の存在が確認されなくなったところで撹拌を停止した。その後、2Lのナスフラスコに反応溶液を移し、減圧蒸留することで、アセトン75g、水50gを除去し、水性ポリウレタン樹脂エマルジョン組成物(PUD-46)を得た。
・1,6-ヘキサンジオール:BASF-JAPAN社製
・2,2-ジメチロールプロピオン酸:東京化成社製
・イソホロンジイソシアネート:エボニック社製
・アセトン:KHネオケム社製
・トリエチルアミン:キシダ化学社製
・イソホロンジアミン:東京化成社製
・モノエタノールアミン:富士フイルム和光純薬社製
・ネオスタンU-600:日東化成株式会社製
・KL-245:Evonik社製
・水:市水
・ジプロピレングリコールジメチルエーテル:富士フイルム和光純薬社製
・アクアネート200:東ソー社製(ノニオン型水分散性ポリイソシアネート、NCO含有量=11.9%)
[引張特性]
得られた硬化物を、JIS K7321に準拠して引張特性を測定した。(100%モジュラス、破断時強度、破断時伸び)
・試験装置:テンシロンUTA-500(エー・アンド・デー社製)
・測定条件:25℃×50%RH
・ヘッドスピード:200mm/分
・ダンベル4号
得られたフィルムからダンベルを用いて試験片を得た後、試験片に2cmの標線を記し、標線中央部の厚みを測定した。試験片の一方のつかみ部に所定重量のおもりを取り付け、もう一方のつかみ部をダブルクリップで挟み込み、クリップが上側となるように乾燥機内に吊り下げた後、乾燥機内を昇温し標線間距離を観測、標線間距離が4cmとなったときの温度を軟化温度として読み取った。
・処理装置:送風定温乾燥機DRK633DA(アドバンテック社製)
・おもり重量:標線中央部厚み(μm)×0.05g
・ダンベル2号(JIS K6251準拠)
・昇温速度:5℃/分
100%モジュラス、破断時強度、破断時伸び、および軟化温度の各物性値を、A、B、CおよびD(A:非常に良好、B:良好、C:普通、D:不良)で評価した。さらに、総合評価はA、BおよびD(A:非常に良好、B:良好、D不良)とした。
<100%モジュラス>
A:5.0MPa未満
B:5.0MPa以上6.5MPa未満
D:6.5MPa以上
<破断時強度>
A:30MPa以上
C:30MPa未満
<破断時伸び>
A:250MPa以上
C:250MPa未満
<軟化温度>
A:230℃以上
B:230℃未満210℃以上
D:210℃未満
<総合評価>
A:各物性値の評価がAのみ
B:各物性値の評価がDを含まず、少なくとも1つのBまたはCを含む
D:各物性値の評価がDを含む
・ジプロピレングリコールジメチルエーテル:富士フイルム和光純薬社製
Claims (19)
- イソシアネート基末端ウレタンプレポリマー(E)と、鎖延長剤(G)と、の反応生成物と、
中和剤(F)と、を含むポリウレタン樹脂組成物であって、
前記イソシアネート基末端ウレタンプレポリマー(E)が、
平均水酸基官能基数が2を超えるポリカーボネートポリオール(B)を含むポリオール(A)と、
有機酸(C)と、
ポリイソシアネート(D)と、の反応生成物を含み、
前記ポリウレタン樹脂組成物中、ウレア基の全含有量が、前記イソシアネート基末端ウレタンプレポリマー(E)の質量と、前記鎖延長剤(G)の質量と、の総和に対して、0.01~0.80mmol/gであり、
前記ポリカーボネートポリオール(B)のみなし平均官能基数が2.0~3.90である、ポリウレタン樹脂組成物。 - 前記鎖延長剤(G)が、
1個以上の一級または二級アミノ基を有するアミン化合物、および、
水、からなる群より選択される1種以上である、請求項1に記載のポリウレタン樹脂組成物。 - 前記鎖延長剤(G)が、1個以上の一級または二級アミノ基を有するアミン化合物を含み、
前記ポリウレタン樹脂組成物中、前記アミン化合物由来のウレア基の含有量が、前記イソシアネート基末端ウレタンプレポリマー(E)の質量と、前記鎖延長剤(G)の質量と、の総和に対して0mmol/g超0.480mmol/g以下である、請求項1または2に記載のポリウレタン樹脂組成物。 - 前記鎖延長剤(G)が、1個以上の一級または二級アミノ基を有するアミン化合物を含み、
前記ポリウレタン樹脂組成物中、前記アミン化合物由来のウレア基の含有量が、前記ウレア基の全含有量に対して、0mol%超95mol%以下である、請求項1~3のいずれか1項に記載のポリウレタン樹脂組成物。 - 前記鎖延長剤(G)が、水を含み、
前記ポリウレタン樹脂組成物中、前記水由来のウレア基の含有量が、前記イソシアネート基末端ウレタンプレポリマー(E)の質量と、前記鎖延長剤(G)の質量と、の総和に対して、0mmol/g超0.80mmol/g以下である、請求項1~4のいずれか1項に記載のポリウレタン樹脂組成物。 - 前記ポリカーボネートポリオール(B)の含有量が、前記ポリオール(A)の含有量の総和に対して、5.0質量%以上である、請求項1~5のいずれか1項に記載のポリウレタン樹脂組成物。
- 前記ポリオール(A)の平均水酸基価が、30~150mgKOH/gである、請求項1~6のいずれか1項に記載のポリウレタン樹脂組成物。
- 前記ポリカーボネートポリオール(B)が、
ジオール(b-1)と、多価アルコール(b-2)と、炭酸エステル(b-3)と、のエステル交換反応物を含む、または、
ジオール(b-1)と、多価アルコール(b-2)と、ポリカーボネートポリオール(b-4)と、のエステル交換反応物を含む、請求項1~7のいずれか1項に記載のポリウレタン樹脂組成物。 - 前記ポリカーボネートポリオール(B)の水酸基価が、40~500mgKOH/gである、請求項1~8のいずれか1項に記載のポリウレタン樹脂組成物。
- 前記ポリカーボネートポリオール(B)の数平均分子量が、400~4,000g/molである、請求項1~9のいずれか1項に記載のポリウレタン樹脂組成物。
- 前記有機酸(C)が、ジメチロール脂肪酸である、請求項1~10のいずれか1項に記載のポリウレタン樹脂組成物。
- 前記中和剤(F)が、塩基性中和剤である、請求項1~11のいずれか1項に記載のポリウレタン樹脂組成物。
- 前記ポリオール(A)が、ジオール(a-1)を含む、請求項1~12のいずれか1項に記載のポリウレタン樹脂組成物。
- 一液型である、請求項1~13のいずれか1項に記載のポリウレタン樹脂組成物。
- 硬化剤(X)をさらに含有する、請求項1~13のいずれか一項に記載のポリウレタン樹脂組成物。
- 二液型である、請求項15に記載のポリウレタン樹脂組成物。
- イソシアネート基末端ウレタンプレポリマー(E)と、鎖延長剤(G)と、の反応生成物を含むポリウレタン樹脂組成物の硬化物であって、
前記イソシアネート基末端ウレタンプレポリマー(E)が、
平均水酸基官能基数が2を超えるポリカーボネートポリオール(B)を含むポリオール(A)と、
有機酸(C)と、
ポリイソシアネート(D)と、の反応生成物を含み、
前記ポリウレタン樹脂組成物中、ウレア基の全含有量が、前記イソシアネート基末端ウレタンプレポリマー(E)の質量と、前記鎖延長剤(G)の質量と、の総和に対して、0.01~0.80mmol/gであり、
前記ポリカーボネートポリオール(B)のみなし平均官能基数が2.0~3.90である、硬化物。 - 請求項1~17のいずれか1項に記載のポリウレタン樹脂組成物の硬化物を含む、人工皮革、または合成皮革。
- 請求項1~17のいずれか1項に記載のポリウレタン樹脂組成物の硬化物を含む、皮革用表面処理剤。