WO2022129201A1 - Agent de matité lamellaire pour peinture en poudre et peintures en poudre - Google Patents
Agent de matité lamellaire pour peinture en poudre et peintures en poudre Download PDFInfo
- Publication number
- WO2022129201A1 WO2022129201A1 PCT/EP2021/085944 EP2021085944W WO2022129201A1 WO 2022129201 A1 WO2022129201 A1 WO 2022129201A1 EP 2021085944 W EP2021085944 W EP 2021085944W WO 2022129201 A1 WO2022129201 A1 WO 2022129201A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- additive
- substrate
- formula
- atoms
- butyl
- Prior art date
Abstract
La présente invention concerne un additif pouvant être utilisé en tant qu'agent de matité pour des peintures en poudre, comprenant un substrat lamellaire transparent qui est au moins partiellement appliqué sur la surface du substrat à l'aide d'un agent de modification de surface constitué d'une polysilicone spéciale. L'invention porte en outre sur des compositions de peinture en poudre contenant cet agent de matité.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP20215508 | 2020-12-18 | ||
EP20215508.1 | 2020-12-18 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022129201A1 true WO2022129201A1 (fr) | 2022-06-23 |
Family
ID=73855819
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2021/085944 WO2022129201A1 (fr) | 2020-12-18 | 2021-12-15 | Agent de matité lamellaire pour peinture en poudre et peintures en poudre |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2022129201A1 (fr) |
Citations (14)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1993008237A1 (fr) | 1991-10-18 | 1993-04-29 | Merck Patent Gmbh | Pigments en plaquettes enrobes et colores |
WO1999036481A1 (fr) | 1998-01-16 | 1999-07-22 | Cabot Corporation | Composition de revetement en poudre |
EP0955344A2 (fr) | 1998-04-28 | 1999-11-10 | Degussa-Hüls Aktiengesellschaft | Charges traitées en surface, procédé pour leur préparation et leur utilisation |
JP2004010735A (ja) | 2002-06-06 | 2004-01-15 | Maruo Calcium Co Ltd | 粉体塗料用充填剤及びそれを配合してなる粉体塗料組成物 |
EP1690884A1 (fr) | 2005-02-14 | 2006-08-16 | Byk-Chemie GmbH | Polysiloxanes modifiés par de l'organosilane et leur utilisation pour la modification de surfaces |
US20060204528A1 (en) * | 2005-02-14 | 2006-09-14 | Ulrich Nolte | Surface-modified nanoparticles, their preparation and use |
DE102009023158A1 (de) | 2009-05-29 | 2010-12-02 | Merck Patent Gmbh | Beschichtete Partikel und deren Verwendung |
US20130310464A1 (en) * | 2010-11-17 | 2013-11-21 | BYK-Dhemie GmbH | Copolymers which can be obtained from urethane-based, polysiloxane-containing macromonomers, processes for the preparation thereof and their use |
EP2698403A1 (fr) | 2012-08-17 | 2014-02-19 | Eckart GmbH | Pigments nacrés modifiés en surface et leur utilisation dans les laques en poudre |
EP2318463B1 (fr) | 2008-07-08 | 2014-10-01 | Eckart GmbH | Pigments métalliques, procédé de fabrication ainsi qu'utilisation de ces pigments et peinture en poudre |
WO2014202495A1 (fr) | 2013-06-19 | 2014-12-24 | Akzo Nobel Coatings International B.V. | Composition pour une peinture en poudre résistante aux hautes températures, son procédé de préparation et son utilisation |
WO2015057895A1 (fr) | 2013-10-15 | 2015-04-23 | S&B Industrial Minerals S.A. | Verre d'aluminosilicate d'origine volcanique traité en surface, micronisé et expansé utilisable en tant que charge fonctionnelle lamellaire pour plastiques et revêtements spéciaux |
CN106675152A (zh) | 2016-12-22 | 2017-05-17 | 重庆市锦艺硅材料开发有限公司苏州分公司 | 粉末涂料用消光改性剂及其应用、以及含有其的消光粉末涂料 |
CN111378298A (zh) | 2018-12-27 | 2020-07-07 | 苏州锦艺新材料科技有限公司 | 一种粉体材料、其制备方法及粉末涂料 |
-
2021
- 2021-12-15 WO PCT/EP2021/085944 patent/WO2022129201A1/fr active Application Filing
Patent Citations (17)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO1993008237A1 (fr) | 1991-10-18 | 1993-04-29 | Merck Patent Gmbh | Pigments en plaquettes enrobes et colores |
WO1999036481A1 (fr) | 1998-01-16 | 1999-07-22 | Cabot Corporation | Composition de revetement en poudre |
EP0955344A2 (fr) | 1998-04-28 | 1999-11-10 | Degussa-Hüls Aktiengesellschaft | Charges traitées en surface, procédé pour leur préparation et leur utilisation |
US6239194B1 (en) * | 1998-04-28 | 2001-05-29 | Huels Aktiengesellschaft | Surface-modified fillers, process for their preparation and their use |
JP2004010735A (ja) | 2002-06-06 | 2004-01-15 | Maruo Calcium Co Ltd | 粉体塗料用充填剤及びそれを配合してなる粉体塗料組成物 |
EP1690902B1 (fr) | 2005-02-14 | 2012-08-15 | BYK-Chemie GmbH | particules nanométriques à surfaces modifiées, procédé de fabrication et utilisation |
US20060204528A1 (en) * | 2005-02-14 | 2006-09-14 | Ulrich Nolte | Surface-modified nanoparticles, their preparation and use |
EP1690884A1 (fr) | 2005-02-14 | 2006-08-16 | Byk-Chemie GmbH | Polysiloxanes modifiés par de l'organosilane et leur utilisation pour la modification de surfaces |
EP2318463B1 (fr) | 2008-07-08 | 2014-10-01 | Eckart GmbH | Pigments métalliques, procédé de fabrication ainsi qu'utilisation de ces pigments et peinture en poudre |
DE102009023158A1 (de) | 2009-05-29 | 2010-12-02 | Merck Patent Gmbh | Beschichtete Partikel und deren Verwendung |
US20130310464A1 (en) * | 2010-11-17 | 2013-11-21 | BYK-Dhemie GmbH | Copolymers which can be obtained from urethane-based, polysiloxane-containing macromonomers, processes for the preparation thereof and their use |
EP2698403A1 (fr) | 2012-08-17 | 2014-02-19 | Eckart GmbH | Pigments nacrés modifiés en surface et leur utilisation dans les laques en poudre |
EP2698403B1 (fr) | 2012-08-17 | 2018-01-03 | Eckart GmbH | Pigments nacrés modifiés en surface et leur utilisation dans les laques en poudre |
WO2014202495A1 (fr) | 2013-06-19 | 2014-12-24 | Akzo Nobel Coatings International B.V. | Composition pour une peinture en poudre résistante aux hautes températures, son procédé de préparation et son utilisation |
WO2015057895A1 (fr) | 2013-10-15 | 2015-04-23 | S&B Industrial Minerals S.A. | Verre d'aluminosilicate d'origine volcanique traité en surface, micronisé et expansé utilisable en tant que charge fonctionnelle lamellaire pour plastiques et revêtements spéciaux |
CN106675152A (zh) | 2016-12-22 | 2017-05-17 | 重庆市锦艺硅材料开发有限公司苏州分公司 | 粉末涂料用消光改性剂及其应用、以及含有其的消光粉末涂料 |
CN111378298A (zh) | 2018-12-27 | 2020-07-07 | 苏州锦艺新材料科技有限公司 | 一种粉体材料、其制备方法及粉末涂料 |
Non-Patent Citations (1)
Title |
---|
"Chemie und Technologie der Silikone", 1984, WILEY/VCH |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US8304077B2 (en) | Metal effect pigments, method for the production and the use thereof and powder coating | |
EP1980594B1 (fr) | Pigments à effet comprenant un substrat de type paillettes | |
KR101321623B1 (ko) | 혼합된 무기/유기 층을 포함하는 금속 효과 안료, 상기금속 효과 안료의 제조 방법, 및 그 용도 | |
US9790368B2 (en) | Pearlescent pigments coated with mixed inorganic/organic layers and method for the production thereof | |
CA2281801C (fr) | Materiaux hybrides organiques-inorganiques | |
US20100269733A1 (en) | Metallic pigments, method for the production thereof and use thereof and coating powder | |
JP2009527605A (ja) | 薄いガラスの微小板をベースとする耐候安定性真珠光沢顔料およびそれを調製するためのプロセス | |
CA2270005A1 (fr) | Charges minerales a surface modifiee et procede de preparation et d'utilisation de celles-ci | |
EP2361953A1 (fr) | Pigments métalliques de couleur or qui incluent des couches de nanoparticules d'oxyde de manganèse | |
KR101478150B1 (ko) | 관능화된 입자 및 이들의 용도 | |
JP2007525572A (ja) | 官能性多層構造を有する粒子 | |
KR20140011347A (ko) | 내후성 진주광택 안료, 그 제조 방법 및 용도 | |
KR20020035449A (ko) | 소수성 커플링제를 갖는 진주 광택 안료의 후피복물 | |
WO2001019928A1 (fr) | Pigment au dioxyde de titane, procede de production et composition a base de resine le contenant | |
KR102573560B1 (ko) | 표면 광택 개질제를 포함하는 실리콘 코팅 조성물 | |
WO2008011616A2 (fr) | Pigments perlés à base de mica synthétique contenant des ferrites | |
KR20150039808A (ko) | 효과 안료 | |
KR102541874B1 (ko) | 보호 캡슐화를 가진 판상 pvd 알루미늄 안료 및 보호 캡슐화를 가진 판상 pvd 알루미늄 안료를 제조하는 방법 | |
WO2022129201A1 (fr) | Agent de matité lamellaire pour peinture en poudre et peintures en poudre | |
WO2003076524A1 (fr) | Procede de production de pigment de dioxyde de titane et compositions de resine contenant ce pigment | |
US20080053336A1 (en) | Aqueous coating compositions with improved tint strength and gloss properties, comprising pigments surface-treated with certain organosilicon compounds | |
KR101941460B1 (ko) | 멜라민 관능기가 도입된 에폭시실릴 인산에스테르 유무기 복합 하이브리드 수지 및 이를 이용한 불연 도료 조성물 | |
WO2024132896A1 (fr) | Mélanges transparents aux ondes radar de pigments à effet métallique avec des pigments à effet semi-conducteur ou avec des pigments nacrés absorbants argentés et formulations de revêtement de ceux-ci | |
Henglein et al. | SiO 2 coated pearlescent pigments |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 21836180 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 21836180 Country of ref document: EP Kind code of ref document: A1 |