WO2022008506A1 - Cellule au lithium solide, batterie comprenant lesdites cellules et procédé de fabrication pour fabriquer ladite batterie - Google Patents
Cellule au lithium solide, batterie comprenant lesdites cellules et procédé de fabrication pour fabriquer ladite batterie Download PDFInfo
- Publication number
- WO2022008506A1 WO2022008506A1 PCT/EP2021/068652 EP2021068652W WO2022008506A1 WO 2022008506 A1 WO2022008506 A1 WO 2022008506A1 EP 2021068652 W EP2021068652 W EP 2021068652W WO 2022008506 A1 WO2022008506 A1 WO 2022008506A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- electrolyte
- graphite
- solid lithium
- cell
- Prior art date
Abstract
Description
Claims