WO2021194091A1 - 감압 점착제 조성물, 이를 포함하는 점착제, 상기 점착제를 포함하는 인조네일 및 네일용 스티커 - Google Patents

감압 점착제 조성물, 이를 포함하는 점착제, 상기 점착제를 포함하는 인조네일 및 네일용 스티커 Download PDF

Info

Publication number
WO2021194091A1
WO2021194091A1 PCT/KR2021/001932 KR2021001932W WO2021194091A1 WO 2021194091 A1 WO2021194091 A1 WO 2021194091A1 KR 2021001932 W KR2021001932 W KR 2021001932W WO 2021194091 A1 WO2021194091 A1 WO 2021194091A1
Authority
WO
WIPO (PCT)
Prior art keywords
pressure
sensitive adhesive
adhesive composition
acid
adhesive
Prior art date
Application number
PCT/KR2021/001932
Other languages
English (en)
French (fr)
Inventor
박수정
배준호
박현지
우진
Original Assignee
제이씨코리아 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 제이씨코리아 주식회사 filed Critical 제이씨코리아 주식회사
Publication of WO2021194091A1 publication Critical patent/WO2021194091A1/ko

Abstract

본 발명은 감압 점착제 조성물, 이를 포함하는 점착제, 상기 점착제를 포함하는 인조네일 및 네일용 스티커에 관한 것으로, 본 발명의 감압 점착제 조성물은 점착 물성 조절제를 포함하여 감압 점착제 조성물의 생산, 보관 중에 안정하며, 조절된 점착력에 의해 인조 네일 또는 네일용 스티커에 적용되어 우수한 부착 지속력을 가짐과 동시에 고온, 다습, 고압의 가혹 조건에서도 점착력이 일정하게 유지되어 손톱 또는 발톱의 손상을 완화할 수 있는 효과가 있다.

Description

감압 점착제 조성물, 이를 포함하는 점착제, 상기 점착제를 포함하는 인조네일 및 네일용 스티커
본 발명은 감압 점착제 조성물, 이를 포함하는 점착제, 상기 점착제를 포함하는 인조네일 및 네일용 스티커에 관한 것이다.
네일 미용은 패션의 한 부분으로 자리매김하여 화장 또는 미용을 목적으로 고분자 중합체를 포함하고 있는 네일 폴리쉬, 젤네일 등과 같은 제품을 손톱, 발톱에 사용되어왔다.
상기 젤네일은 일반 매니큐어와는 달리 시술 후 따로 드라이가 필요 없으며 부딪히거나 찍혀도 흠이 나지 않아, 바로 일상생활 하는데 무리가 없고, 한 번의 시술로 색깔과 광택이 3-4주간 지속되는 장점이 있는 것으로 알려져 있으나, 젤 네일 시술 후 손톱에 도포되어 있는 매니큐어를 제거하기가 어렵고, 매니큐어가 손톱에 장시간 동안 도포되어 있는 경우, 손톱이 얇아지거나 손톱이 갈라지는 현상, 손톱이 물러져서 뜨는 현상 등의 문제점이 있다.
이러한 제품은 인체에 유해한 유기용매를 포함하고 있기 때문에 시술 및 제거 시, 시술자 및 피시술자의 건강에 안 좋은 영향을 미칠 수 있고, 휘발성이 강하여 폭발 위험성을 가지고 있다는 특성으로 인하여, 제조 및 보관 시 각별한 주의가 요구되었다.
이에 한국등록특허 제10-1226696호(원터치 장착식 인조네일), 제10-1388254호(네일용 스티커), 제10-1164554호(인조네일용 양면테이프) 등에서는 완제품 상태에서 유기용매가 완전히 제거된 압력 민감형 점착 테이프(pressure sensitive adhesive)를 이용하여 용이한 탈부착이 가능한 인조 네일 또는 네일용 스티커를 개시하고 있다.
상기 제품은 시술자가 특별한 기술이나 도구 없이도 간편하고 신속하게 탈부착 할 수 있으나, 과도한 점착력 또는 시간 경과에 따른 점착력의 변화 등에 의하여 탈착 과정에서 손톱 또는 발톱의 표면 손상이 수반되며, 부착 후 외부와 밀폐된 환경, 특히 발톱에 부착한 상태에서 신발을 장기간 착용할 경우, 점착력이 증가하여 손상을 악화시키거나, 외부 환경 노출 등에 의하여 장시간 부착하지 못하는 문제가 있다.
[선행기술문헌]
[특허문헌]
한국등록특허 제10-1226696호
한국등록특허 제10-1388254호
한국등록특허 제10-1164554호
따라서, 본 발명이 해결하고자 하는 기술적 과제는 점착 물성 조절제를 포함하여 손톱 또는 발톱의 손상을 완화할 수 있는 감압 점착제 조성물, 이를 포함하는 점착제, 상기 점착제를 포함하는 인조 네일 또는 네일용 스티커를 제공하는 것이다.
상기한 기술적 과제를 해결하기 위한 본 발명의 일 측면은 감압 점착성 고분자(PSA: Pressure-sensitive adhesive) 및 점착 물성 조절제를 포함하고, 상기 점착 물성 조절제는 천연추출물, 항균방부소재 및 케라틴 용해제로 이루어진 군에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 감압 점착성 조성물.
본 발명의 다른 측면은 상기 감압 점착제 조성물을 포함하는 점착제를 제공한다.
본 발명의 또 다른 측면은 상기 점착제를 포함하는 점착제층; 및 상기 점착제 층의 일면에 부착된 인조손톱본체;를 포함하는 인조 네일을 제공한다.
본 발명의 또 다른 측면은 상기 점착제를 포함하는 점착제층; 및 상기 점착제 층의 일면에 부착된 필름;을 포함하는 네일용 스티커를 제공한다.
본 발명의 감압 점착제 조성물은 점착 물성 조절제를 포함하여 감압 점착제 조성물의 생산, 보관 중에 안정하며, 조절된 점착력에 의해 인조 네일 또는 네일용 스티커에 적용되어 우수한 부착 지속력을 가짐과 동시에 고온, 다습, 고압의 가혹 조건에서도 점착력이 일정하게 유지되어 손톱 또는 발톱의 손상을 완화할 수 있는 효과가 있다.
도 1a는 본 발명의 일 실시예에 따른 감압 점착제 조성물 용액, 도 1b는 본 발명의 일 비교예에 따른 감압 점착제 조성물 용액을 60 ℃에서 12주 동안 보관한 후 외관을 촬영한 사진이다.
도 2a는 가혹 보관 조건에서 점착력 변화를 측정하기 위하여 제작한 시료의 단면도이고, 도 2b는 상기 시료의 상층을 촬영한 사진이다.
도 3은 본 발명의 실시예 2-2 및 비교예 3의 양면테이프를 이용하여 제조한 네일용 스티커 부착하기 전 및 탈착 후, 손톱 외관을 촬영한 폴리스코프 카메라 이미지이다.
도 4는 본 발명의 실시예 2-2 및 비교예 3의 양면테이프를 이용하여 제조한 네일용 스티커 부착 전 및 탈착 후, PRIMOS CR 촬영 이미지이다.
이하에서, 본 발명의 여러 측면 및 다양한 구현예에 대해 더욱 구체적으로 설명한다.
본 발명의 일 측면은 감압 점착성 고분자(PSA: Pressure-sensitive adhesive) 및 점착 물성 조절제를 포함하고, 상기 점착 물성 조절제는 천연추출물, 항균방부소재 및 케라틴 용해제 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 감압 점착제 조성물을 제공한다.
본 발명의 감압 점착제 조성물은 감압 점착성 고분자에 점착 물성 조절제를 첨가하여 점착력을 적절하게 조절함으로써, 이후 상기 감압 점착제 조성물을 포함하여 제조되는 인조 네일 또는 네일용 스티커의 과도한 점착력에 의해 탈착 과정에서 발생하는 손톱 또는 발톱의 손상을 완화하고, 용이한 탈부착이 가능하다.
또한 기존의 인조 네일 또는 네일용 스티커는 부착 후, 일정 수준의 점착력이 유지되는 것이 장시간의 부착이 지속될 수 있으며, 손·발톱의 손상도 예방할 수 있으나, 외부와 밀폐된 환경, 특히 발톱에 부착한 상태에서 신발을 장시간 착용할 경우, 점착력이 증가하여 발톱 손상을 악화시키거나, 외부 환경 노출 등에 의하여 장시간 부착하지 못하는 문제가 있다. 하지만, 본 발명의 감압 점착제 조성물은 점착 물성 조절제를 포함함으로써, 이와 유사한 가혹 조건에서 급격한 점착력 상승이 발생하지 않아, 장시간 부착이 가능하고 손상도 완화시킬 수 있다.
게다가 본 발명의 점착 물성 조절제는 인체에 유해한 유기 용매 등의 물질을 포함하지 않고, 의약품, 화장품, 식품 등에 사용하는 인체에 안전한 물질을 포함하므로 사용자의 건강에 유해한 영향을 미치지 않는다.
상기 감압 점착성 고분자란, 압력 민감성 고분자로서 점착면에 접착시키기 위한 압력이 가해질 때 점착성이 발휘되는 고분자를 의미한다. 상기 감압 점착성 고분자는 탄소수 1 내지 18의 알킬기가 부가된 아크릴계 모노머, 아크릴산, 메타크릴산 및 하이드록시기가 부가된 아크릴계 모노머 중 선택되는 어느 하나 또는 둘 이상의 혼합물이 중합된 아크릴레이트 중합체일 수 있다.
구체적으로 상기 아크릴레이트 중합체는 폴리메틸메타크릴레이트(PMMA: Poly methyl methacrylate), 폴리-2-하이드록시에틸메타크릴레이트(P2HEMA: Poly-2-hydroxy ethyl methacrylate), 폴리스테아릴메타아크릴레이트(PSMA: poly stearylmethacrylate), 폴리-2-하이드록시프로필메타크릴레이트(P2HPMA: Poly-2-hydroxy propyl methacrylate), 폴리부틸메타크릴레이트(PBMA: Poly n-butyl methacrylate), 폴리에틸아크릴레이트(PEA: Poly ethyl acrylate), 폴리부틸아크릴레이트(PBA: Poly butyl acrylate) 및 폴리-2-에틸헥실아크릴레이트(P2EHA: Poly-2-ethyl hexylacrylate) 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 것이 가능하다.
상기 천연 추출물은 올레아놀산(oleanolic acid), 올레산(oleic acid), 로즈마린산(rosmarinic acid), 프테로스틸벤(pterostilbene) 및 크시메닌산(ximenynic acid) 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있으며, 바람직하게는 올레아놀산 또는 올레산일 수 있다. 상기 천연 추출물은 의약품 및 화장품 원료로 사용되는 인체에 무해한 불포화 지방산 소재로, 산화질소 생성 억제를 통한 상처 치유 효과 및 인체 면역 반응을 조절을 통한 항염증 효과를 가진다. 상기 천연 추출물은 상기 감압 점착제 조성물을 적용한 인조 네일 및 네일용 스티커 등의 제품은 피시술자의 손·발톱 표면 손상을 완화하는 본연의 효능을 지닌다.
상기 항균방부소재는 에틸헥실글리세린(ethylhexylglycerin), 히드록시아세토페논(hydroxyacetophenone), 옥탄디올(1,2-octanediol), 헥산디올(1,2-hexanediol), 페녹시에탄올(phenoxyethanol), 클로르페네신(chlorphenesin) 및 벤질알콜(benzyl alcohol) 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있으며, 바람직하게는 에틸헥실글리세린, 옥탄디올, 헥산디올 또는 페녹시에탄올일 수 있다. 상기 항균방부소재는 상기 감암 접착제 조성물의 물성의 변화를 방지하고 상기 감압 점착제 조성물을 적용한 인조 네일 및 네일용 스티커 등의 제품이 피시술자의 손·발톱 표면에 존재하는 유해한 세균의 성장을 억제하여 건강한 손·발톱 상태를 유지할 수 있도록 하는 소재 본연의 효능을 지닌다.
상기 케라틴 용해제는 우레아(urea), 젖산(lactic acid), 글리콜산(glycolic acid) 및 살리실산(salicylic acid) 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있으며, 바람직하게는 살리실산일 수 있다. 각질(케라틴)은 상피구조의 기본을 형성하는 단백질로서, 글루탐산, 아르기닌 등 여러 아미노산으로 이루어져 있으며 그 중 시스테인의 함량이 많고, 대표적인 조직으로는 손·발톱이 있다. 각질성 증식, 상피비후와 이들 증세가 수반되는 피부병 등에 의하여 각질이 불필요하게 또는 이상적으로 증식하는 경우가 있는데, 상기 케라틴 용해제는 상기 감압 점착제 조성물이 인조 네일, 네일용 스티커 등의 제품에 적용되어 피시술자의 손·발톱 표면의 각질을 용해하거나 연화시켜 상기 질병을 예방 또는 완화하는 효과가 있다.
상기 천연 추출물, 항균방부소재 및 케라틴 용해제는 상술한 본래 가지고 있는 효능/효과 외, 점착 물성 조절제로 사용되여 함량에 따라 감압 점착제 조성물의 점착 물성을 적절한 범위로 조절하는 것이 가능하다는 사실을 확인하였으며, 아울러 의약품 또는 식품 등에 사용하는 인체에 안전한 물질을 사용하기 때문에, 시술자 및 피시술자의 건강에 안 좋은 영향을 미치거나, 휘발성이 강하여 폭발 위험성을 갖는 등의 문제가 없어 제조 및 보관이 용이하다.
바람직한 구현예에 따르면, 상기 점착 물성 조절제는 올레아놀산, 올레산, 에틸헥실글리세린, 옥탄디올, 헥산디올, 페녹시에탄올 및 살리실산 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물일 수 있다.
본 발명의 감압 점착제 조성물은 첨가되는 점착 물성 조절제의 함량이 증가할수록 감압 점착제 조성물의 점착력이 감소하는 경향이 있으며, 특히 고온, 다습, 고압 조건에서 점착력이 과도하게 증가되어 손톱 또는 발톱 손상을 증가시킬 수 있고, 활동적인 운동 및 급격한 외부 환경 변화에 의하여 부착 지속력이 감소하는 경향이 있다. 또한, 일반적으로 감압 점착제 조성물은 용액으로 보관되는데, 여타 점착 물성 조절제의 함량이 증가할수록 점착제 조성물의 색상 또는 점도가 시간 경과에 따라 변화하는 등 용액 안정성이 저하되어 제조 및 보관 과정에서 문제가 있을 수 있다.
하지만 상술한 올레아놀산, 올레산, 에틸헥실글리세린, 옥탄디올, 헥산디올, 페녹시에탄올 및 살리실산은 특정 함량 범위에서 소재 본래의 효능/효과도 나타내면서, 감압 점착제 조성물의 안정성에 영향이 없음을 확인하였고, 고온, 다습, 고압 조건 또는 활동적인 운동, 급격한 외부 환경 변화에 노출되어도 점착력이 큰 변화 없이 유지되어 부착 지속력이 유지되면서 손·발톱 손상도 완화시킬 수 있음을 확인하였다.
후술하는 실시예에서 확인할 수 있는 바와 같이, 감압 점착제 조성물의 안정성에 영향을 주지 않으면서 장기간의 부착 지속력, 손·발톱 손상을 완화시킬 수 있는 점착력을 갖도록 하는 점착 물성 조절제의 함량 범위는 종류에 따라 상이하였다.
따라서, 상기 점착 물성 조절제들의 점착제 조성물 용액에 대한 용해도를 중량%로 측정하고, 해당 용해도를 상한 값으로 설정하고, 점착력 변화가 없는 중량%를 하한 값으로 설정하여 실험을 진행했다. 상술한 각 점착 물성 조절제의 종류에 따른 함량 범위는 다음과 같다.
- 올레아놀산: 감압 점착제 조성물의 중량 대비 0.05 내지 0.2 중량%.
- 올레산: 감압 점착제 조성물의 중량 대비 0.1 내지 3.0 중량%.
- 에틸헥실글리세린: 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량%.
- 옥탄디올: 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량%.
- 헥산디올: 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량%.
- 페녹시에탄올: 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량%.
- 살리실산: 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량%.
상기 점착 물성 조절제의 조성을 갖는 감압 점착제 조성물은 전술한 바와 같이, 감압 점착제 조성물의 안정성, 점착력 및 부착 지속력 등이 바람직한 수준으로 유지됨을 확인하였으며, 각각의 소재 본연의 효과(천연추출물: 손발톱 표면 손상 완화 효과, 항균방부소재: 항균 효과, 케라틴용해제: 손·발톱 표면 각질 용해 효과)를 발현할 수 있었다. 상기 점착 물성 조절제의 종류에 따른 함량 범위 미만의 경우 소재 본연의 효과를 기대하기 어려웠으며, 점착력이 시간 경과에 따라 비교적 큰 폭으로 변화하여 부착 지속력이 저하되고 손·발톱 손상을 유발하는 등의 문제가 있었으며, 상기 함량 범위 초과 시, 요구되는 부착 지속력을 확보할 수 없는 수준의 점착력 저하 및 보관 중 점착 물성 조절제의 석출되거나 색상 또는 점도가 변화하여 안정성이 확보되지 못하여 감압 점착제 조성물 제조 및 사용이 불가능하였다.
상기 감압 점착제 조성물은 상기 감압 점착제 조성물을 도포한 테이프를 ASTM D903에 따라 측정한 180°박리 강도가 500 내지 1200 gf/10 mm일 수 있다. 상기 감압 점착제 조성물을 도포한 테이프는 당업계에 알려진 테이프를 제조하기 위하여 사용되는 필름이라면 제한 없이 사용되어 제조될 수 있으며, 예를 들어 SH34(SKC), CD901(코오롱인더스트리), RX600((주)HS화인텍) 필름에 감압 점착제 조성물을 도포하여 이용할 수 있다. 상기 범위의 180° 박리 강도를 가질 경우, 손톱 또는 발톱에 부착되어 손톱 또는 발톱의 손상을 완화시킬 수 있음과 동시에 장시간 사용 가능한 부착 유지력을 확보할 수 있다는 것을 확인하였다. 상기 180° 박리 강도가 500 gf/10 mm 미만의 경우 점착력이 부족하여 제조되는 인조 네일 또는 네일용 스티커가 쉽게 탈착될 수 있으며, 1200 gf/10 mm를 초과할 경우, 과도한 점착력으로 탈착과정에서 손톱 또는 발톱의 손상을 유발할 수 있다는 문제가 있다. 부착일수를 더욱 늘릴 수 있다는 점에서 바람직하게는 상기 180°박리 강도가 500 내지 1000 gf/10 mm, 보다 바람직하게는 600 내지 800 gf/10 mm 일 수 있다.
가장 바람직한 구현예에 따르면, 상기 점착 물성 조절제는 올레산이고, 상기 올레산을 상기 감압 점착제 조성물의 중량 대비 0.1 내지 1.0 중량% 포함될 수 있다. 상기 조건의 감압 점착제 조성물은 이를 도포한 테이프를 ASTM D903에 따라 측정한 180° 박리 강도가 가장 바람직한 범위인 600 내지 800 gf/10 mm을 보였고, 고온, 고압, 다습의 가혹 조건에서의 점착력 변화가 최소화되었으며, 이에 따라 정상적인 부착일수가 10일을 초과하였다. 특히, 상기 조건에 따른 감압 점착제 조성물은 동일 또는 유사한 점착력을 갖는 다른 감압 점착제 조성물(다른 종류의 점착 물성 조절제 및 함량 범위)과 비교하여도 부착 지속력이 유의미하게 향상되었으며, 손·발톱의 손상이 완화됨을 확인하였다. 게다가, 상기 조건에서는 다른 종류의 점착 물성 조절제 및 함량 범위와는 달리 감압 점착제 조성물의 함량이 증가할수록 점착력이 증가하는 경향을 보였는데, 이러한 특성을 바탕으로 상기 감압 점착제 조성물을 포함하는 네일용 스티커의 부착되는 손톱 또는 발톱의 종류에 따라 점착력을 조절하여 적용할 수 있는 장점을 가진다.
본 발명의 다른 측면은 상기 감압 점착제 조성물을 포함하는 점착제를 제공한다.
본 발명의 또 다른 측면은 상기 점착제를 포함하는 점착제층; 및 상기 점착제 층의 일면에 부착된 인조손톱본체;를 포함하는 인조 네일을 제공한다.
본 발명의 또 다른 측면은 상기 점착제를 포함하는 점착제층; 및 상기 점착제 층의 일면에 부착된 필름;을 포함하는 네일용 스티커를 제공한다.
실시예. 감압 점착제 조성물을 포함하는 양면테이프의 제조
실시예 1-1
에틸아세테이트 및 아크릴레이트 점착제 용액(BA-2290)에 점착 물성 조절제로 올레아놀산(oleanolic acid)을 0.05 중량% 포함되도록 혼합하고 교반하여 완전히 용해시킨 후 감압 점착제 조성물을 제조하였다. 상기 감압 점착제 조성물을 코팅 장비를 이용하여 이면지에 도포한 후 열 경화 또는 UV 경화 공정을 거쳐 양면테이프를 제조하였다.
실시예 1-2
올레아놀산(oleanolic acid)을 0.1 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 1-3
올레아놀산(oleanolic acid)을 0.2 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 2-1
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 올레산(oleic acid)을 0.1 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 2-2
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 올레산(oleic acid)을 0.5 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 2-3
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 올레산(oleic acid)을 1 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 2-4
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 올레산(oleic acid)을 2 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 2-5
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 올레산(oleic acid)을 3 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 3-1
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 에틸헥실글리세린(ethylhexylglycerin)을 5 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 3-2
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 옥탄디올(1,2-octanediol)을 5 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 3-3
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 헥산디올(1,2-hexanediol)을 5 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 3-4
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 페녹시에탄올(phenoxyethanol)을 5 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
실시예 4
점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 살리실산(salicylic acid)을 5 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
비교예 1
점착 물성 조절제가 포함되어 있는 감압 점착제 조성물 용액의 안정성을 비교/확인하고자 점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 비타민 유도체인 판테놀(panthenol)을 각각 0.1 내지 1 내지 2 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
비교예 2
점착 물성 조절제가 포함되어 있는 감압 점착제 조성물 용액의 안정성을 비교/확인하고자 점착 물성 조절제로 올레아놀산(oleanolic acid)을 대신하여 아미노산인 아세칠메치오닌(N-acetyl methionine)을 0.1 중량% 포함되도록 혼합한 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하였다.
비교예 3
점착 물성 조절제를 투입하지 않은 것을 제외하고는 상기 실시예 1-1과 동일하게 실시하여 양면테이프를 제조하였다.
실험예 1. 안정성 테스트
상기 실시예 및 비교예에 명시된 양면테이프 제조 전, 제조 액에서의 점착 물성 조절제의 안정성을 확인하고자 점착 물성 조절제가 포함되어 있는 각각의 감압 점착제 조성물 용액을 60 ℃에서 12주 보관, 색상의 경시 변화 및 점도를 측정하였고, 그 결과는 하기 표 1에 나타내었다.
대표적인 비교 사진은 도 1a(3.0 중량%-올레산 용액) 및 1b(0.1/1.0/2.0 중량%-판테놀 용액)와 같다.
구분 점착 물성
조절제		 함량(중량%) 색상 변화 점도
실시예 1-1 올레아놀산 0.05 - -
실시예 1-2 올레아놀산 0.1 - -
실시예 1-3 올레아놀산 0.2 - -
실시예 2-1 올레산 0.1 - -
실시예 2-2 올레산 0.5 - -
실시예 2-3 올레산 1.0 - -
실시예 2-4 올레산 2.0 - -
실시예 2-5 올레산 3.0 - -
실시예 3-1 에틸헥실글리세린 5.0 - -
실시예 3-2 옥탄디올 5.0 - -
실시예 3-3 헥산디올 5.0 - -
실시예 3-4 페녹시에탄올 5.0 - -
실시예 4 살리실산 5.0 - -
비교예 1 판테놀 0.1/1.0/2.0 함량 증가에 따라 갈변 -
비교예 2 아세칠메치오닌 0.1 - 겔화 수준의 점도 상승
상기 표 1 및 도 1에서 확인할 수 있는 바와 같이, 점착 물성 조절제를 첨가한 실시예의 경우, 비교예 1에 비하여 색상 변화가 없는 것을 확인할 수 있었으며, 비교예 2에 비하여 점도 변화가 없는 것을 확인할 수 있었다.
실험예 2. 점착력 테스트 및 부착 지속력 측정 테스트
상기 실시예 및 비교예에서 제조한 양면테이프의 점착력을 측정하기 위하여, ASTM (American Society for Testing Materials, 미국시험재료협회)에서 규정한 D903 시험법에 따라 SUS를 이용하여 180°박리 강도 (peel strength)를 측정하였고, 상기 실시예 및 비교예에서 제조한 양면 테이프를 적용한 네일용 스티커를 인체 손톱에 부착한 후 부착 일수를 측정하였다. 그 결과를 하기 표 2에 나타내었다.
구분 점착 물성
조절제		 함량(중량%) 제조 직후, 점착력 (gf/10mm) 부착일수 (일)
실시예 1-1 올레아놀산 0.05 775 8
실시예 1-2 올레아놀산 0.1 742 9
실시예 1-3 올레아놀산 0.2 752 7
실시예 2-1 올레산 0.1 645 11
실시예 2-2 올레산 0.5 685 14
실시예 2-3 올레산 1.0 688 13
실시예 2-4 올레산 2.0 435 6
실시예 2-5 올레산 3.0 350 5
실시예 3-1 에틸헥실글리세린 5.0 470 6
실시예 3-2 옥탄디올 5.0 607 10
실시예 3-3 헥산디올 5.0 725 11
실시예 3-4 페녹시에탄올 5.0 762 9
실시예 4 살리실산 5.0 820 12
비교예 3 - - 1380 10
상기 표 2에서 확인할 수 있는 바와 같이, 점착 물성 조절제 함량이 증가할수록 점착력이 감소하고, 부착 지속력이 감소하지만, 이는 모든 실시예에 해당하는 것은 아님을 알 수 있다. 이는 점착 물성 조절제가 단순히 점착력만 조절하는 것은 아니며, 이 외 복합적인 요인이 작용하고 있다는 것을 확인할 수 있었다.
실험예 3. 가혹 조건에서 점착력 변화 테스트
상기 실시예 2-2 및 비교예 3에서 제조한 양면테이프의 점착력 변화를 측정하기 위하여, 실시예 2-2 및 비교예 3에 따라 제조한 양면테이프(PSA)를 180° 박리 강도(peel strength) 측정에 사용하는 SUS 사이에 한 면은 부착한 상태로 한 면은 PET 필름을 덧댄 상태로 고무줄로 강하게 압박하여 묶은 후 (도 2), 아래 조건에서 보관하였다. 점착제 안정화 시간을 확보하기 위하여, 보관 3일 후 점착력을 측정하였고, 최종 점착력은 보관 4주 후에 측정하였다. 그 결과는 표 3에 나타내었다.
- 싸이클링 보관 조건 : 1사이클 (8시간-37 ℃/75% RH+16 시간-32 ℃/40% RH)/일 * 4주
점착력(gf/10 mm)
3 일 후 4 주 후 점착력 증가량
비교예 3 880 1,110 26%
실시예 2-2 870 990 14%
상기 표 3에서 확인할 수 있는 바와 같이, 점착 물성 조절제를 첨가하지 않은 실시예 3의 경우, 실시예 2-2 보다 점착력이 약 2배 증가한 것을 확인할 수 있었으며, 이러한 점착력의 증가는 부착 지속력의 증가로 이어져 손톱 또는 발톱 손상을 악화시킬 수 있을 것으로 예상된다.
실험예 4. 네일용 스티커에 대한 손상도 테스트
상기 실험예 1 내지 3에서 우수한 안정성, 부착지속력, 가혹 조건에서의 점착력 변화가 적었던 실시예 2-2에 대한 손톱 손상도를 측정하였다. 상기 실시예 2-2 및 비교예 3을 적용한 네일용 스티커를 제조하고, 손톱에 부착 후, 14일 경과 후 탈착하고, 부착 전후의 손톱 표면에 대한 손상도를 평가하였다. 손상도는 폴리스코프 카메라 (130만 화소 Full HD)로 촬영한 이미지를 정성적으로 육안 평가하였고, PRIMOS CR (Optical 3D skin measuring system)을 이용하여 손톱 표면 평균 거칠기 (Ra) 및 손톱 표면 최대 거칠기 (Rmax) 값을 정량적으로 측정하였다.
도 3은 상기 실시예 2-2 및 비교예 3의 양면테이프를 이용하여 제조한 네일용 스티커 부착하기 전 및 탈착 후, 손톱 외관을 촬영한 폴리스코프 카메라 이미지이다. 도 4는 상기 실시예 2-2 및 비교예 3의 양면테이프를 이용하여 제조한 네일용 스티커 부착 전 및 탈착 후, PRIMOS CR 촬영 이미지이다. 또한 상세한 결과는 하기 표 4와 같다.
손톱 표면 평균 거칠기
(Ra)		 손톱 표면 최대 거칠기 (Rmax)
부착전 (%) 탈착 후 (%) 부착전 (%) 탈착 후 (%)
비교예 3 100.0 120.0 100.0 121.9
실시예 2-2 100.0 111.3 100.0 104.4
손상도 차이 * -8.7% 개선 -17.5% 개선
* 부착전 손상도 100% 기준, 탈착 수 증가한 손톱 표면 거칠기 차이값
상기 표 4, 도 3 및 도 4에서 확인할 수 있는 바와 같이, 비교예 3 대비 실시예 2-2에 대한 손상도가 수치적으로 낮은 것을 알 수 있다. 즉, 실시예 2-2를 부착한 실험군에서 손톱 표면 손상이 덜 생겼다는 것을 알 수 있었고, 폴리스코프 촬영 이미지를 통한 정성적 분석에서도 실시예 2-2를 부착한 실험군에서 비교예 3 대비, 손톱 표면 손상이 덜 발생하는 것을 추가로 확인할 수 있었다.
따라서 본 발명의 감압 점착제 조성물은 점착 물성 조절제를 포함하여 감압 점착제 조성물의 생산, 보관 중에 안정하며, 조절된 점착력에 의해 인조 네일 또는 네일용 스티커에 적용되어 우수한 부착 지속력을 가짐과 동시에 고온, 다습, 고압의 가혹 조건에서도 점착력이 일정하게 유지되어 손톱 또는 발톱의 손상을 완화할 수 있는 효과가 있다.
전술한 실시예 및 비교예는 본 발명을 설명하기 위한 예시로서, 본 발명이 이에 한정되는 것은 아니다. 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 이로부터 다양하게 변형하여 본 발명을 실시하는 것이 가능할 것이므로, 본 발명의 기술적 보호범위는 첨부된 특허청구범위에 의해 정해져야 할 것이다.

Claims (17)

  1. 감압 점착성 고분자(PSA: Pressure-sensitive adhesive) 및 점착 물성 조절제를 포함하고,
    상기 점착 물성 조절제는 천연추출물, 항균방부소재 및 케라틴 용해제 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 감압 점착제 조성물.
  2. 제1항에 있어서,
    상기 감압 점착성 고분자는 탄소수 1 내지 18의 알킬기가 부가된 아크릴계 모노머, 탄소수 1 내지 18의 알킬기가 부가된 아크릴산, 탄소수 1 내지 18의 알킬기가 부가된 메타크릴산 및 하이드록시기가 부가된 아크릴계 모노머 중 선택되는 어느 하나 또는 둘 이상의 혼합물이 중합된 아크릴레이트 중합체인 감압 점착제 조성물.
  3. 제1항에 있어서,
    상기 천연 추출물은 올레아놀산(oleanolic acid), 올레산(oleic acid), 로즈마린산(rosmarinic acid), 프테로스틸벤(pterostilbene) 및 크시메닌산(ximenynic acid) 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 감압 점착제 조성물.
  4. 제1항에 있어서,
    상기 항균방부소재는 에틸헥실글리세린(ethylhexylglycerin), 히드록시아세토페논(hydroxyacetophenone), 옥탄디올(1,2-octanediol), 헥산디올(1,2-hexanediol), 페녹시에탄올(phenoxyethanol), 클로르페네신(chlorphenesin) 및 벤질알콜(benzyl alcohol) 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 감압 점착제 조성물.
  5. 제1항에 있어서,
    상기 케라틴 용해제는 우레아(urea), 젖산(lactic acid), 글리콜산(glycolic acid) 및 살리실산(salicylic acid) 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 감압 점착제 조성물.
  6. 제1항에 있어서,
    상기 점착 물성 조절제는 올레아놀산, 올레산, 에틸헥실글리세린, 옥탄디올, 헥산디올, 페녹시에탄올 및 살리실산 중에서 선택되는 어느 하나 또는 둘 이상의 혼합물인 감압 점착제 조성물.
  7. 제1항에 있어서,
    상기 점착 물성 조절제는 올레아놀산이고,
    상기 올레아놀산은 상기 감압 점착제 조성물의 중량 대비 0.05 내지 0.2 중량% 포함되는 감압 점착제 조성물.
  8. 제1항에 있어서,
    상기 점착 물성 조절제는 올레산이고,
    상기 올레산은 상기 감압 점착제 조성물의 중량 대비 0.1 내지 3.0 중량% 포함되는 감압 점착제 조성물.
  9. 제1항에 있어서,
    상기 점착 물성 조절제는 에틸헥실글리세린이고,
    상기 에틸헥실글리세린은 상기 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량% 포함되는 감압 점착제 조성물.
  10. 제1항에 있어서,
    상기 점착 물성 조절제는 옥탄디올이고,
    상기 옥탄디올은 상기 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량% 포함되는 감압 점착제 조성물.
  11. 제1항에 있어서,
    상기 점착 물성 조절제는 헥산디올이고,
    상기 헥산디올은 상기 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량% 포함되는 감압 점착제 조성물.
  12. 제1항에 있어서,
    상기 점착 물성 조절제는 페녹시에탄올이고,
    상기 페녹시에탄올은 상기 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량% 포함되는 감압 점착제 조성물.
  13. 제1항에 있어서,
    상기 점착 물성 조절제는 살리실산이고,
    상기 살리실산은 상기 감압 점착제 조성물의 중량 대비 1.0 내지 5.0 중량% 포함되는 감압 점착제 조성물.
  14. 제1항에 있어서,
    상기 감압 점착제 조성물은 상기 감압 점착제 조성물을 도포한 테이프를 ASTM D903에 따라 측정한 180° 박리 강도가 500 내지 1200 gf/10 mm인 감압 점착제 조성물.
  15. 제1항 내지 제14항 중 어느 한 항에 따른 감압 점착제 조성물을 포함하는 점착제.
  16. 제15항의 점착제를 포함하는 점착제층; 및
    상기 점착제 층의 일면에 부착된 인조손톱본체;를 포함하는 인조 네일.
  17. 제15항의 점착제를 포함하는 점착제층; 및
    상기 점착제 층의 일면에 부착된 필름;을 포함하는 네일용 스티커.
PCT/KR2021/001932 2020-03-23 2021-02-16 감압 점착제 조성물, 이를 포함하는 점착제, 상기 점착제를 포함하는 인조네일 및 네일용 스티커 WO2021194091A1 (ko)