WO2021193999A1 - 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 및 이의 제조방법 - Google Patents

천연 무기분체 유래의 탄성을 가지는 화장용 파우더 및 이의 제조방법 Download PDF

Info

Publication number
WO2021193999A1
WO2021193999A1 PCT/KR2020/004695 KR2020004695W WO2021193999A1 WO 2021193999 A1 WO2021193999 A1 WO 2021193999A1 KR 2020004695 W KR2020004695 W KR 2020004695W WO 2021193999 A1 WO2021193999 A1 WO 2021193999A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder
natural
inorganic powder
room temperature
solid
Prior art date
Application number
PCT/KR2020/004695
Other languages
English (en)
French (fr)
Inventor
이성호
김영기
최부건
Original Assignee
선진뷰티사이언스(주)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 선진뷰티사이언스(주) filed Critical 선진뷰티사이언스(주)
Priority to CN202080100327.XA priority Critical patent/CN115515547B/zh
Priority to US17/914,941 priority patent/US20230143367A1/en
Publication of WO2021193999A1 publication Critical patent/WO2021193999A1/ko

Abstract

본 발명은 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 및 이의 제조방법에 관한 것으로, 구체적으로 내부에 천연 유래의 무기분체; 상기 무기분체 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층;을 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더 및 이의 제조방법에 관한 것이다. 본 발명의 탄성을 가지는 천연물질 화장용 파우더는 화장료에 적용시 천연유래의 물질을 사용하여 피부안정성이 우수하며, 인체에 안전하며, 분산성이 우수하며, 화장료의 사용감을 현저히 개선할 수 있다.

Description

천연 무기분체 유래의 탄성을 가지는 화장용 파우더 및 이의 제조방법
본 발명은 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 및 이의 제조방법에 관한 것으로, 구체적으로 화장료에 적용시 천연유래의 물질을 사용하여 피부안정성이 우수하며, 인체에 안전하며, 분산성이 우수하며, 화장료의 사용감을 현저히 개선할 수 있는 천연 무기분체 유래의 탄성을 가지는 화장용 파우더에 관한 것이다.
이하에 기술되는 내용은 단순히 본 발명과 관련되는 배경 정보만을 제공할 뿐 종래기술을 구성하는 것이 아니다.
화장법에 기술이 발달함에 따라 다양한 종류의 화장품이 사용되고 있으며, 천연 유래의 화장재료뿐만 아니라 여러 합성물질이 화장품에 적용되고 있다.
종래 화장품의 사용감 등을 개선하기 위하여 화장용 파우더가 화장품에 사용되었으며, 더욱 우수한 사용감을 가지도록 탄성 파우더가 사용되었다.
일예로 대한민국 특허공개 10-2014-0026818호에서는 탄성을 가지는 구상의 파우더로 PMMA, 나일론 파우더, 실리콘 엘라스토머 및 폴리우레탄 등의 탄성 파우더가 화장료에 적용됨이 개시되어 있다.
그러나 최근 합성물질 파우더로 인한 인체의 유해성, 환경오염 등의 문제가 크게 대두되면서 각국에서 종래 화장료에 적용되었던 합성물질 파우더의 사용을 제한하는 추세에 있으며, 특히 탄성을 가지는 화장용 파우더의 경우 합성물질이 아닌 파우더에 대한 개발이 미흡한 실절이며, 이에 따라 천연유래의 파우더에 요구가 절실히 요구되고 있다.
본 발명이 이루고자 하는 기술적 과제는 화장료에 적용시 천연유래의 물질을 사용하여 피부안정성이 우수하며, 인체에 안전하며, 분산성이 우수하며, 화장료의 사용감을 현저히 개선할 수 있는 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 및 이의 제조방법을 제공하는 것을 목적으로 한다.
또한 본 발명은 높은 생산성으로 천연유래의 물질을 사용하여 피부안정성이 우수하며, 개선된 물성을 가지는 천연 무기분체 유래의 탄성을 가지는 화장용 파우더를 제조할 수 있는 제조방법을 제공하는 것을 목적으로 한다.
이러한 기술적 과제를 이루기 위한 본 발명은
화장용 파우더로서,
내부에 천연 유래의 무기분체(110);
상기 무기분체(110) 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층(120);을 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더(100)를 제공한다.
바람직하기로 상기 탄성을 가지는 천연물질 화장용 파우더(100)는 상기 무기분체(110) 100 중량부에 대하여 상기 탄성 코팅층(120) 3 내지 20 중량부를 가진다.
상기 탄성 코팅층(120)은 식물성 오일을 더욱 포함할 수 있다.
바람직하기로 상기 무기분체(110) 100 중량부에 대하여 상기 오일은 1 내지 20 중량부를 가진다.
바람직하기로 상기 탄성을 가지는 천연물질 화장용 파우더(100)는 점탄성측정기로 측정시 50 내지 900 g force/um2를 가진다.
또한 본 발명은
화장용 파우더로서,
내부에 천연 유래의 무기분체(110);
상기 무기분체(110) 표면에 코팅된 오일 코팅층(130);
상기 식물성 오일 코팅층(130) 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층(120);을 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더(100)를 제공한다.
또한 본 발명은
화장용 파우더로서,
내부에 천연 유래의 무기분체(110);
상기 무기분체 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층(120);
상기 탄성 코팅층 표면에 코팅된 오일 코팅층(130);
을 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더(100)를 제공한다.
또한 본 발명은
S1) 천연 무기분체(110)를 준비하는 단계;
S2) 상기 무기분체(110) 표면에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하는 단계;
를 포함하는 탄성을 가지는 천연물질 화장용 파우더(100)의 제조방법을 제공한다.
바람직하기로 상기 무기분체(110) 100 중량부에 대하여 상기 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체; 3 내지 20 중량부를 가진다.
상기 S2) 건식코팅하는 단계에서 오일을 더욱 혼합하여 건식코팅할 수 있다.
또한 본 발명은
S11) 천연 무기분체(110)를 준비하는 단계;
S12) 상기 무기분체(110) 표면에 오일을 코팅하는 단계;
S13) 상기 식물성 오일이 코팅된 무기분체에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하는 단계;를 포함하는 탄성을 가지는 천연물질 화장용 파우더의 제조방법을 제공한다.
또한 본 발명은
S21) 천연 무기분체를 준비하는 단계;
S22) 상기 무기분체 표면에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하는 단계;
S23) 상기 건식코팅된 무기분체의 표면에 오일을 코팅하는 단계;를 포함하는 탄성을 가지는 천연물질 화장용 파우더의 제조방법을 제공한다.
또한 본 발명은 상기 천연물질 화장용 파우더를 포함하는 화장료를 제공한다.
본 발명에 따르면 화장료에 적용시 천연유래의 물질을 사용하여 피부안정성이 우수하며, 인체에 안전하며, 분산성이 우수하며, 화장료의 사용감을 현저히 개선할 수 있는 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 및 이의 제조방법을 제공할 수 있다.
또한 본 발명은 높은 생산성으로 천연유래의 물질을 사용하여 피부안정성이 우수하며, 개선된 물성을 가지는 천연 무기분체 유래의 탄성을 가지는 화장용 파우더를 제조할 수 있는 제조방법을 제공할 수 있다.
도 1은 본 발명의 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더의 모식도를 나타낸 것이다.
도 2는 본 발명의 다른 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더의 모식도를 나타낸 것이다.
도 3은 본 발명의 또 다른 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더의 모식도를 나타낸 것이다.
도 4는 본 발명의 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 제조방법의 모식도를 나타낸 것이다.
도 5는 본 발명의 다른 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 제조방법의 모식도를 나타낸 것이다.
도 6은 본 발명의 또 다른 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 제조방법의 모식도를 나타낸 것이다.
아래에서는 첨부한 도면을 참고로 하여 본 발명의 실시예에 대하여 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 그리고 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 유사한 부분에 대해서는 유사한 도면 부호를 붙였다.
명세서 전체에서, 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다.
도 1은 본 발명의 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더의 모식도를 나타낸 것이고, 도 2는 본 발명의 다른 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더의 모식도를 나타낸 것이고, 도 3은 본 발명의 또 다른 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더의 모식도를 나타낸 것이고, 도 4는 본 발명의 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 제조방법의 모식도를 나타낸 것이고, 도 5는 본 발명의 다른 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 제조방법의 모식도를 나타낸 것이고, 도 6은 본 발명의 또 다른 일실시예에 따른 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 제조방법의 모식도를 나타낸 것이다.
본 발명의 탄성을 가지는 천연물질 화장용 파우더(100)는
화장용 파우더로서,
내부에 천연 유래의 무기분체(110);
상기 무기분체(110) 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층(120);을 가지는 것을 특징으로 한다.
상기 탄성을 가지는 천연물질 화장용 파우더(100)는
S1) 천연 무기분체(110)를 준비하는 단계;
S2) 상기 무기분체(110) 표면에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하는 단계;를 포함하는 탄성을 가지는 천연물질 화장용 파우더(100)의 제조방법을 통하여 제조될 수 있다.
본 발명에서 상기 천연 무기분체(110)는 천연 유래의 무기 분체로서 화장품에 사용될 수 있는 공지의 무기분체가 사용될 수 있으며, 구체적인 예로 실리카, 탈크, 세리사이트, 색소, 이산화티탄, 산화아연 또는 마이카를 단독 또는 2종 이상 혼합하여 사용할 수 있다. 바람직하기로 상기 천연 무기 분체는 실리카이며, 상기 실리카는 기공이 있는 것이나, 기공이 없는 것 모두 사용할 수 있다.
상기 무기분체(110)의 입자크기는 당업자가 적절하게 선택하여 사용할 수 있다. 일예로 상기 무기분체(110)의 입자크기는 0.1 내지 100 um일 수 있으나 이에 한정되는 것은 아니다.
본 발명에서 상기 무기분체(110) 표면에 건식코팅되는 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;는 공지의 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;가 사용될 수 있으며, 바람직하게는 천연유래인 것이 좋으며, 시판되는 것을 사용할 수도 있다. 구체적으로 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터로는 트리히드록시스테아린일 수 있으며, (b) 상온에서 고체인 글리세릴지방산에스테르로는 글리세릴 베헤네이트(glyceryl behenate)를 사용할 수 있다.
본 발명에서 상기 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;는 상기 무기분체(110) 100 중량부에 대하여 3 내지 20 중량부를 가지도록 하는 것이 좋으며, 바람직하기로는 6 내지 10 중량부인 것이 좋다. 이 경우 제조되는 탄성을 가지는 파우더(100)가 화장품에 적합한 탄성을 가지며, 동시에 화장료에서 안정성이 우수한 물성을 가진다.
본 발명에서 건식코팅은 화장품의 제조에서 통상적으로 적용되는 건식코팅방법이 적용될 수 있으며, 구체적인 예로 2000 내지 4500 rpm으로 교반하면서 무기분체(110)에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하여 탄성 코팅층(120)을 형성한다.
필요에 따라 상기 탄성을 가지는 천연물질 화장용 파우더(100)의 제조방법은 상기 S2) 단계 이후에 건식코팅된 무기분체를 건조하는 건조단계; 건식코팅된 무기분체를 파쇄하는 파쇄단계; 건식코팅된 무기분체를 분급하는 분급단계를 각각 독립적으로 실시할 수 있다. 상기 건조단계, 파쇄단계 및 분급단계는 단독으로 실시될 수도 있으며, 2종 이상의 단계를 혼합하여 실시될 수도 있다. 일예로 건식코팅된 무기분체는 건조, 파쇄 또는 분급을 통하여 탄성을 가지는 화장품용 파우더(100)가 된다.
본 발명에 따른 상기 탄성을 가지는 화장용 파우더(100)는 도 1과 같이 내부에 천연 유래의 무기분체(110)가 위치하며, 상기 무기분체(110)의 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층(120);을 가지며, 상기 탄성 코팅층(120)은 균일한 두께를 가지는 코팅층일 수도 있으며, 탄성 코팅층의 두께가 불균일할 수도 있다.
본 발명에 따른 상기 탄성을 가지는 화장용 파우더(100)는 오일을 더욱 포함할 수 있다.
상기 오일은 화장품에 사용되는 공지의 오일이 사용될 수 있으며, 구체적으로는 식물유 또는 식물 유래의 오일이 사용될 수 있다. 더욱 구체적으로 식물유로는 Macadamia nut oil, Meadowfoam seed oil, Sunflower oil이 단독 또는 2종 이상 혼합하여 사용할 수 있으며, 식물유래 오일로는 Caprylic capric triglyceride 또는 Dicapryl carbonate가 단독 또는 혼합하여 사용할 수 있다. 상기 식물유 또는 식물유래 오일은 혼합하여 사용할 수도 있다.
바람직하기로 상기 오일은 상기 무기분체(110) 100 중량부에 대하여 1 내지 20 중량부를 가지도록 하는 것이 좋으며, 바람직하기로는 3 내지 10 중량부인 것이 좋다. 이 경우 제조되는 탄성을 가지는 파우더(100)가 화장품에 적합한 탄성을 가지며, 동시에 화장료에서 안정성이 우수한 물성을 가진다.
본 발명에서 탄성을 가지는 화장용 파우더(100)가 오일을 포함할 경우 상기 오일을 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;와 함께 혼합하여 건식코팅을 하여 탄성코팅층(120)을 형성할 수 있다,
또한 본 발명에서 탄성을 가지는 화장용 파우더(100)는 별도의 오일 코팅층을 가지는 화장용 파우더로서,
내부에 천연 유래의 무기분체(110);
상기 무기분체(110) 표면에 코팅된 오일 코팅층(130);
상기 오일 코팅층(130) 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층(120);을 가지는 것일 수 있다.
상기 탄성을 가지는 천연물질 화장용 파우더(100)는
S11) 천연 무기분체(110)를 준비하는 단계;
S12) 상기 무기분체(110) 표면에 오일을 코팅하는 단계;
S13) 상기 실리콘오일이 코팅된 무기분체에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하는 단계;를 통하여 제조될 수 있다.
상기 S12) 오일을 코팅하는 단계에서 코팅하는 방법은 공지의 오일 코팅방법이 적용될 수 있으며, 구체적인 예로 건식코팅일 수 있다.
또한 필요에 따라 상기 탄성을 가지는 천연물질 화장용 파우더(100)의 제조방법은 상기 S13) 단계 이후에 건식코팅된 무기분체를 건조하는 건조단계; 건식코팅된 무기분체를 파쇄하는 파쇄단계; 건식코팅된 무기분체를 분급하는 분급단계를 각각 독립적으로 실시할 수 있다. 상기 건조단계, 파쇄단계 및 분급단계는 단독으로 실시될 수도 있으며, 2종 이상의 단계를 혼합하여 실시될 수도 있다. 일예로 건식코팅된 무기분체는 건조, 파쇄 또는 분급을 통하여 탄성을 가지는 화장품용 파우더(100)가 된다.
또한 본 발명에서 탄성을 가지는 화장용 파우더(100)는 별도의 오일 코팅층을 가지는 화장용 파우더로서,
내부에 천연 유래의 무기분체(110);
상기 무기분체 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층(120);
상기 탄성 코팅층(120) 표면에 코팅된 오일 코팅층(130);
을 가지는 것을 가지는 것일 수 있다.
상기 탄성을 가지는 천연물질 화장용 파우더(100)는
S21) 천연 무기분체를 준비하는 단계;
S22) 상기 무기분체 표면에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하는 단계;
S23) 상기 건식코팅된 무기분체의 표면에 오일을 코팅하는 단계;를 포함하여 제조될 수 있다.
필요에 따라 상기 탄성을 가지는 천연물질 화장용 파우더(100)의 제조방법은 상기 S23) 단계 이후에 건식코팅된 무기분체를 건조하는 건조단계; 건식코팅된 무기분체를 파쇄하는 파쇄단계; 건식코팅된 무기분체를 분급하는 분급단계를 각각 독립적으로 실시할 수 있다. 상기 건조단계, 파쇄단계 및 분급단계는 단독으로 실시될 수도 있으며, 2종 이상의 단계를 혼합하여 실시될 수도 있다. 일예로 건식코팅된 무기분체는 건조, 파쇄 또는 분급을 통하여 탄성을 가지는 화장품용 파우더(100)가 된다.
본 발명에 따른 탄성을 가지는 화장품용 파우더(100)는 점탄성측정기(제품명: MCT-W500-E, 제조사: shimadzu)로 측정시 50 내지 900 g force/um2를 가져 화장료에 적용시 우수한 사용감을 가지게 할 수 있다.
또한 본 발명은 상기 탄성을 가지는 화장품용 파우더(100)를 포함하는 것을 특징으로 하는 화장료를 제공한다. 화장료의 제형은 한정되지 않으며, W/S 제형, W/O 제형, 파우더 제형, 무수제형, O/W 제형 등 모든 종류의 화장료에 적용될 수 있으며, 파운데이션, 립스틱, 스킨케어, 메이트업, 또는 썬케어 등 다양한 용도에 제한 없이 적용할 수 있다.
본 발명의 화장료에 있어서 상기 탄성을 가지는 화장품용 파우더(100)의 함량은 임의로 조절할 수 있으며, 구체적으로 화장료 내에서 상기 탄성을 가지는 화장품용 파우더(100)의 함량은 0.1 내지 30 중량%일 있다.
이하, 본 발명을 구체적으로 설명하기 위해 실시예를 들어 상세하게 설명하기로 한다. 그러나 본 발명에 따른 실시예는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 상술하는 실시예에 한정되는 것으로 해석되어서는 안 된다. 본 발명의 실시예는 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해서 제공되는 것이다.
[실시예 1]
천연 유래의 무기분체로서 실리카 100 중량부를 준비하였다. 상기 실리카 100 중량부를 건식코팅기에 넣고, 트리히드록시스테아린 6 중량부를 2000 내지 4500 rpm으로 교반하면서 건식 코팅하여 실리카에 트리히드록시스테아린 탄성 코팅층을 가지는 화장품용 파우더를 제조하였다. 상기 화장품용 파우더는 점탄성측정기(제품명: MCT-W500-E, 제조사: shimadzu)로 측정시 50 내지 900 g force/um2를 가져 화장료에 적용시 우수한 사용감을 가지게 할 수 있었다.
[실시예 2]
상기 실시예 1에서 트리히드록시스테아린 대신에 글리세릴 베헤네이트를 사용한 것을 제외하고는 대등한 방법으로 건식코팅을 진행하여 실리카에 글리세릴 베헤네이트 탄성 코팅층을 가지는 화장품용 파우더를 제조하였다. 상기 화장품용 파우더는 점탄성측정기(제품명: MCT-W500-E, 제조사: shimadzu)로 측정시 50 내지 900 g force/um2를 가져 화장료에 적용시 우수한 사용감을 가지게 할 수 있었다.
[실시예 3]
상기 실시예 1에서 트리히드록시스테아린 함량을 10 중량부 사용한 것을 제외하고는 대등한 방법으로 건식코팅을 진행하여 탄성 코팅층을 가지는 화장품용 파우더를 제조하였다. 상기 화장품용 파우더는 점탄성측정기(제품명: MCT-W500-E, 제조사: shimadzu)로 측정시 50 내지 900 g force/um2를 가져 화장료에 적용시 우수한 사용감을 가지게 할 수 있었다.
[실시예 4]
상기 실시예 1에서 오일로서 식물유 5 중량부를 더욱 혼합하여 건식코팅한 것을 제외하고는 사용한 것을 제외하고는 대등한 방법으로 건식코팅을 진행하여 탄성 코팅층을 가지는 화장품용 파우더를 제조하였다. 상기 화장품용 파우더는 점탄성측정기(제품명: MCT-W500-E, 제조사: shimadzu)로 측정시 50 내지 900 g force/um2를 가져 화장료에 적용시 우수한 사용감을 가지게 할 수 있었다.
[실시예 5]
상기 실시예 1에서 오일로서 식물유 5 중량부를 먼저 무기분체에 코팅하고, 이후에 트리히드록시스테아린를 건식코팅한 것을 제외하고는 사용한 것을 제외하고는 대등한 방법으로 건식코팅을 진행하여 무기분체층 - 오일층 - 탄성 코팅층을 가지는 화장품용 파우더를 제조하였다. 상기 화장품용 파우더는 점탄성측정기(제품명: MCT-W500-E, 제조사: shimadzu)로 측정시 50 내지 900 g force/um2를 가져 화장료에 적용시 우수한 사용감을 가지게 할 수 있었다.
[실시예 6]
상기 실시예 1에서 트리히드록시스테아린를 건식코팅한 후 오일로서 식물유 5 중량부를 건식코팅을 진행하여 무기분체층 - 탄성 코팅층 - 오일층을 가지는 화장품용 파우더를 제조하였다. 상기 화장품용 파우더는 점탄성측정기(제품명: MCT-W500-E, 제조사: shimadzu)로 측정시 50 내지 900 g force/um2를 가져 화장료에 적용시 우수한 사용감을 가지게 할 수 있었다.
[참조예 1]
상기 실시예 1에서 트리히드록시스테아린 함량을 1 중량부 사용한 것을 제외하고는 대등한 방법으로 건식코팅을 진행하여 탄성 코팅층을 가지는 화장품용 파우더를 제조하였다. 상기 화장품용 파우더는 점탄성측정기(제품명: MCT-W500-E, 제조사: shimadzu)로 측정시 50 g force/um2 미만을 가져 화장료에 적용시 탄성이 적음을 확인할 수 있었다.
[참조예 2]
상기 실시예 1에서 트리히드록시스테아린 함량을 30 중량부 사용한 것을 제외하고는 대등한 방법으로 건식코팅을 진행하여 탄성 코팅층을 가지는 화장품용 파우더를 제조하였다. 상기 화장품용 파우더는 파우더들끼리 뭉치는 현상이 발생하였으며, 화장료에 적용시 안정성이 떨어짐을 확인할 수 있었다.
이상에서 본 발명의 실시예에 대하여 상세하게 설명하였지만 본 발명의 권리범위는 이에 한정되는 것은 아니고 다음의 청구범위에서 정의하고 있는 본 발명의 기본 개념을 이용한 당업자의 여러 변형 및 개량 형태 또한 본 발명의 권리범위에 속하는 것이다.
본 발명에 따르면 화장료에 적용시 천연유래의 물질을 사용하여 피부안정성이 우수하며, 인체에 안전하며, 분산성이 우수하며, 화장료의 사용감을 현저히 개선할 수 있는 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 및 이의 제조방법을 제공할 수 있다.
또한 본 발명은 높은 생산성으로 천연유래의 물질을 사용하여 피부안정성이 우수하며, 개선된 물성을 가지는 천연 무기분체 유래의 탄성을 가지는 화장용 파우더를 제조할 수 있는 제조방법을 제공할 수 있다.

Claims (11)

  1. 화장용 파우더로서,
    내부에 천연 유래의 무기분체;
    상기 무기분체 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층;을 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더.
  2. 제1항에 있어서,
    상기 무기분체 100 중량부에 대하여 상기 탄성 코팅층 3 내지 20 중량부를 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더.
  3. 제1항에 있어서,
    상기 탄성코팅층은 오일을 더욱 포함하는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더.
  4. 제3항에 있어서,
    상기 무기분체 100 중량부에 대하여 상기 오일 1 내지 20 중량부를 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더.
  5. 화장용 파우더로서,
    내부에 천연 유래의 무기분체;
    상기 무기분체 표면에 코팅된 오일 코팅층;
    상기 오일 코팅층 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층을 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더.
  6. 화장용 파우더로서,
    내부에 천연 유래의 무기분체;
    상기 무기분체 표면에 건식코팅된 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;의 탄성 코팅층;
    상기 탄성 코팅층 표면에 코팅된 오일 코팅층;
    을 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더.
  7. S1) 천연 무기분체를 준비하는 단계;
    S2) 상기 무기분체 표면에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하는 단계;
    를 포함하는 탄성을 가지는 천연물질 화장용 파우더의 제조방법.
  8. 제7항에 있어서,
    상기 무기분체 100 중량부에 대하여 상기 탄성 코팅층은 3 내지 20 중량부를 가지는 것을 특징으로 하는 탄성을 가지는 천연물질 화장용 파우더의 제조방법.
  9. S11) 천연 무기분체를 준비하는 단계;
    S12) 상기 무기분체 표면에 오일을 코팅하는 단계;
    S13) 상기 오일이 코팅된 무기분체에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하는 단계;
    를 포함하는 탄성을 가지는 천연물질 화장용 파우더의 제조방법.
  10. S21) 천연 무기분체를 준비하는 단계;
    S22) 상기 무기분체 표면에 (a) 상온에서 고체인 글리세린과 히드록시지방산과의 트리에스터 및 그 유도체; 또는 (b) 상온에서 고체인 글리세릴지방산에스테르 및 그 유도체;를 건식코팅하는 단계;
    S23) 상기 건식코팅된 무기분체의 표면에 오일을 코팅하는 단계;
    를 포함하는 탄성을 가지는 천연물질 화장용 파우더의 제조방법.
  11. 제1항 내지 제6항 중 어느 한 항 기재의 천연물질 화장용 파우더를 포함하는 화장료.
PCT/KR2020/004695 2020-03-27 2020-04-07 천연 무기분체 유래의 탄성을 가지는 화장용 파우더 및 이의 제조방법 WO2021193999A1 (ko)