WO2021153402A1 - Polymère à photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de fabrication de stratifié optique, et dispositif d'affichage d'image - Google Patents

Polymère à photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de fabrication de stratifié optique, et dispositif d'affichage d'image Download PDF

Info

Publication number
WO2021153402A1
WO2021153402A1 PCT/JP2021/001972 JP2021001972W WO2021153402A1 WO 2021153402 A1 WO2021153402 A1 WO 2021153402A1 JP 2021001972 W JP2021001972 W JP 2021001972W WO 2021153402 A1 WO2021153402 A1 WO 2021153402A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
formula
repeating unit
photo
preferable
Prior art date
Application number
PCT/JP2021/001972
Other languages
English (en)
Japanese (ja)
Inventor
壮一郎 渡邉
寛 野副
隆史 飯泉
一茂 中川
匡広 渥美
西川　秀幸
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to JP2021574686A priority Critical patent/JP7303334B2/ja
Priority to KR1020227017089A priority patent/KR20220088746A/ko
Publication of WO2021153402A1 publication Critical patent/WO2021153402A1/fr

Abstract

La présente invention aborde le problème concernant la production d'un polymère à photo-alignement au moyen duquel des propriétés de revêtement de couche supérieure et des propriétés d'alignement de cristaux liquides peuvent être améliorées, même lorsqu'une couche inférieure et une couche supérieure sont formées dans une large plage de conditions de production ; une composition de liant ; une couche de liant ; un stratifié optique ; un procédé de fabrication d'un stratifié optique ; et un dispositif d'affichage d'image. Le polymère à photo-alignement de la présente invention comprend un motif de répétition contenant un groupe de photo-alignement et un motif de répétition représenté par la formule (1).
PCT/JP2021/001972 2020-01-30 2021-01-21 Polymère à photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de fabrication de stratifié optique, et dispositif d'affichage d'image WO2021153402A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2021574686A JP7303334B2 (ja) 2020-01-30 2021-01-21 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法、画像表示装置
KR1020227017089A KR20220088746A (ko) 2020-01-30 2021-01-21 광배향성 폴리머, 바인더 조성물, 바인더층, 광학 적층체, 광학 적층체의 제조 방법, 화상 표시 장치

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-013190 2020-01-30
JP2020013190 2020-01-30

Publications (1)

Publication Number Publication Date
WO2021153402A1 true WO2021153402A1 (fr) 2021-08-05

Family

ID=77078538

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/001972 WO2021153402A1 (fr) 2020-01-30 2021-01-21 Polymère à photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de fabrication de stratifié optique, et dispositif d'affichage d'image

Country Status (3)

Country Link
JP (1) JP7303334B2 (fr)
KR (1) KR20220088746A (fr)
WO (1) WO2021153402A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018216812A1 (fr) * 2017-05-26 2018-11-29 富士フイルム株式会社 Polymère de photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de production de stratifié optique, et dispositif d'affichage d'image
WO2019117082A1 (fr) * 2017-12-15 2019-06-20 富士フイルム株式会社 Copolymère à photo-alignement, film photo-aligné et produit stratifié optique
WO2019225632A1 (fr) * 2018-05-25 2019-11-28 富士フイルム株式会社 Copolymère photo-alignable, film de photo-alignement et stratifié optique

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2018216812A1 (fr) * 2017-05-26 2018-11-29 富士フイルム株式会社 Polymère de photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de production de stratifié optique, et dispositif d'affichage d'image
WO2019117082A1 (fr) * 2017-12-15 2019-06-20 富士フイルム株式会社 Copolymère à photo-alignement, film photo-aligné et produit stratifié optique
WO2019225632A1 (fr) * 2018-05-25 2019-11-28 富士フイルム株式会社 Copolymère photo-alignable, film de photo-alignement et stratifié optique

Also Published As

Publication number Publication date
KR20220088746A (ko) 2022-06-28
JPWO2021153402A1 (fr) 2021-08-05
JP7303334B2 (ja) 2023-07-04

Similar Documents

Publication Publication Date Title
JP7232754B2 (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法および画像表示装置
JP7228049B2 (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法、画像表示装置
WO2018216806A1 (fr) Composition polymérisable à cristaux liquides, couche optiquement anisotrope, stratifié optique, procédé de production de stratifié optique et dispositif d'affichage d'image
WO2021167075A1 (fr) Corps stratifié optique, plaque de polarisation et dispositif d'affichage d'image
JP7212136B2 (ja) 光配向膜用組成物、光配向膜、積層体
US11180661B2 (en) Binder composition, binder layer, optical laminate, and image display device
JP7189232B2 (ja) 光配向性共重合体、バインダー組成物、バインダー層、光学積層体および画像表示装置
WO2021153402A1 (fr) Polymère à photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de fabrication de stratifié optique, et dispositif d'affichage d'image
JP7138721B2 (ja) 光学積層フィルムロールの製造方法、および、光学積層フィルムロール
WO2021241450A1 (fr) Polymère de photo-alignement, composition de liant, couche de liant, stratifié optique, procédé de fabrication de stratifié optique et dispositif d'affichage d'image
US11827727B2 (en) Photo-alignment polymer, binder composition, binder layer, optical laminate, optical laminate manufacturing method, and image display device
JP7355928B2 (ja) 組成物、組成物層、光学積層体および画像表示装置
JP7104804B2 (ja) 光学積層体の製造方法
JP7385729B2 (ja) 光学積層体、偏光板および画像表示装置
JP2023080006A (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法、画像表示装置
WO2020110819A1 (fr) Rouleau de film optique stratifié, et procédé de fabrication de celui-ci
WO2022024683A1 (fr) Composition de liant, composé, couche de liant, stratifié optique, procédé de fabrication pour stratifié optique et dispositif d'affichage d'image
JP2023104473A (ja) 光配向性ポリマー、バインダー組成物、バインダー層、光学積層体、光学積層体の製造方法、画像表示装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21747519

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20227017089

Country of ref document: KR

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2021574686

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21747519

Country of ref document: EP

Kind code of ref document: A1