WO2021140965A1 - Composition de peinture et son procédé de production - Google Patents

Composition de peinture et son procédé de production Download PDF

Info

Publication number
WO2021140965A1
WO2021140965A1 PCT/JP2020/048776 JP2020048776W WO2021140965A1 WO 2021140965 A1 WO2021140965 A1 WO 2021140965A1 JP 2020048776 W JP2020048776 W JP 2020048776W WO 2021140965 A1 WO2021140965 A1 WO 2021140965A1
Authority
WO
WIPO (PCT)
Prior art keywords
activated carbon
coating composition
mass
less
submicron
Prior art date
Application number
PCT/JP2020/048776
Other languages
English (en)
Japanese (ja)
Inventor
修治 川崎
Original Assignee
株式会社クラレ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社クラレ filed Critical 株式会社クラレ
Priority to JP2021570025A priority Critical patent/JPWO2021140965A1/ja
Publication of WO2021140965A1 publication Critical patent/WO2021140965A1/fr

Abstract

La présente invention concerne une composition de peinture comprenant du charbon actif et un milieu de dispersion liquide, le charbon actif ayant un diamètre de particule central D50 d'au plus 1 000 nm, et la teneur du charbon actif étant de 1 à 10 % en masse par rapport à la masse totale de la composition de peinture.
PCT/JP2020/048776 2020-01-06 2020-12-25 Composition de peinture et son procédé de production WO2021140965A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2021570025A JPWO2021140965A1 (fr) 2020-01-06 2020-12-25

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-000369 2020-01-06
JP2020000369 2020-01-06

Publications (1)

Publication Number Publication Date
WO2021140965A1 true WO2021140965A1 (fr) 2021-07-15

Family

ID=76787501

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/048776 WO2021140965A1 (fr) 2020-01-06 2020-12-25 Composition de peinture et son procédé de production

Country Status (3)

Country Link
JP (1) JPWO2021140965A1 (fr)
TW (1) TW202134355A (fr)
WO (1) WO2021140965A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023085237A1 (fr) * 2021-11-12 2023-05-19 日本ペイント株式会社 Composition de revêtement aqueuse antivirale et article

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62188021A (ja) * 1986-02-13 1987-08-17 Matsushita Electric Ind Co Ltd 磁気記録媒体
JP2003284435A (ja) * 2002-03-29 2003-10-07 Dainichiseika Color & Chem Mfg Co Ltd 黒色紙マルチ用塗工液、黒色紙マルチの製造方法および黒色紙マルチ
JP2006083363A (ja) * 2004-04-26 2006-03-30 Showa Denko Kk コーティング材とその用途
JP2008530311A (ja) * 2005-02-16 2008-08-07 ミードウエストベコ・コーポレーション 吸着性塗料処方
JP2009209327A (ja) * 2008-03-06 2009-09-17 Hinomaru Carbo Techno Co Ltd 炭粉含有コーティング剤とその用途
JP2019167497A (ja) * 2018-03-26 2019-10-03 大建工業株式会社 水性塗料組成物
JP2019537643A (ja) * 2016-11-28 2019-12-26 Cqv株式会社Cqv Co., Ltd. 天然炭を用いた黒色系の真珠光沢顔料及びその製造方法

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS62188021A (ja) * 1986-02-13 1987-08-17 Matsushita Electric Ind Co Ltd 磁気記録媒体
JP2003284435A (ja) * 2002-03-29 2003-10-07 Dainichiseika Color & Chem Mfg Co Ltd 黒色紙マルチ用塗工液、黒色紙マルチの製造方法および黒色紙マルチ
JP2006083363A (ja) * 2004-04-26 2006-03-30 Showa Denko Kk コーティング材とその用途
JP2008530311A (ja) * 2005-02-16 2008-08-07 ミードウエストベコ・コーポレーション 吸着性塗料処方
JP2009209327A (ja) * 2008-03-06 2009-09-17 Hinomaru Carbo Techno Co Ltd 炭粉含有コーティング剤とその用途
JP2019537643A (ja) * 2016-11-28 2019-12-26 Cqv株式会社Cqv Co., Ltd. 天然炭を用いた黒色系の真珠光沢顔料及びその製造方法
JP2019167497A (ja) * 2018-03-26 2019-10-03 大建工業株式会社 水性塗料組成物

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023085237A1 (fr) * 2021-11-12 2023-05-19 日本ペイント株式会社 Composition de revêtement aqueuse antivirale et article

Also Published As

Publication number Publication date
TW202134355A (zh) 2021-09-16
JPWO2021140965A1 (fr) 2021-07-15

Similar Documents

Publication Publication Date Title
JP3963941B2 (ja) 徐放性熱可塑性ポリマー組成物およびそれからなる製品
Chew et al. Effect of amino acids on the dispersion of disodium cromoglycate powders
WO2021140965A1 (fr) Composition de peinture et son procédé de production
CN101985536B (zh) 氟碳涂料及其制备方法
JP5291293B2 (ja) 疎水性コーティング膜形成組成物、疎水性コーティング膜、その形成方法及びそれを備えた機能性材料
JP4942222B2 (ja) 塗膜除去剤及びそれを用いた塗膜除去方法
JP2017088509A (ja) 抗菌性部材
JP3846369B2 (ja) ペースト状消臭剤および該消臭剤を用いて製造した消臭製品
JP2010285592A5 (fr)
JP4879523B2 (ja) 粉体塗料組成物、塗膜形成方法および塗装物
JP2007320977A (ja) キトサンパウダーおよび水性コーティング剤
CN107151941A (zh) 光触媒悬浮液、抗粘连自清洁人造板装饰纸及其制备方法
JP6706222B2 (ja) 抗菌抗カビ用塗料、及び該塗料を用いる抗菌抗カビ性部材の製造方法
JP5441255B2 (ja) 繊維表面への光触媒粒子の固着方法
CN101641398B (zh) 包覆吸水性聚合物颗粒的方法
JP2011183318A (ja) 放出ピン部材及びそれを用いた静電霧化装置
US20190262490A1 (en) Composite particles, dispersion liquid, film, deodorizing material, wet wiper, and spray
JP5130206B2 (ja) 可視光応答型酸化チタン系光触媒分散組成物およびその製造方法
TWI376408B (en) Composition for forming antifogging coating and fabric textile applying the same and method of forming the antifogging coating
WO2017057148A1 (fr) Électret et filtre à électret
JP6389335B2 (ja) 環境ホルモン分解組成物、これを用いたコーティング鋼板、及びその製造方法
JP7404163B2 (ja) 光触媒スプレーおよび消臭方法
JP5347169B2 (ja) 速乾性エアコンフィン用スプレー製品及びエアコンフィンの洗浄方法
JP2002194296A (ja) 塗料組成物
TWM651660U (zh) 驅蟲噴液裝置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20912161

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2021570025

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20912161

Country of ref document: EP

Kind code of ref document: A1