WO2021122323A1 - Formation d'acide formique à l'aide d'une électrode catalytique contenant de l'indium - Google Patents

Formation d'acide formique à l'aide d'une électrode catalytique contenant de l'indium Download PDF

Info

Publication number
WO2021122323A1
WO2021122323A1 PCT/EP2020/085585 EP2020085585W WO2021122323A1 WO 2021122323 A1 WO2021122323 A1 WO 2021122323A1 EP 2020085585 W EP2020085585 W EP 2020085585W WO 2021122323 A1 WO2021122323 A1 WO 2021122323A1
Authority
WO
WIPO (PCT)
Prior art keywords
electrode
air
electrochemical
indium
catalytic electrode
Prior art date
Application number
PCT/EP2020/085585
Other languages
English (en)
Inventor
Davide ANSOVINI
Matthew Francis PHILIPS
Julia. KRASOVIC
Marta Catarina Costa FIGUEIREDO
Klaas Jan Pieter SCHOUTEN
Original Assignee
Avantium Knowledge Centre B.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Avantium Knowledge Centre B.V. filed Critical Avantium Knowledge Centre B.V.
Priority to US17/781,600 priority Critical patent/US20220411942A1/en
Priority to EP20824218.0A priority patent/EP4077766A1/fr
Publication of WO2021122323A1 publication Critical patent/WO2021122323A1/fr

Abstract

L'invention concerne la conversion électrochimique du CO2 en acide formique ou en un sel de celui-ci, à l'aide d'une électrode catalytique contenant de l'indium, consistant à (a) convertir électrochimiquement du CO2 en acide formique ou en un sel de celui-ci par application d'une tension à une cellule électrochimique comprenant l'électrode catalytique en tant que cathode et une anode, la cellule électrochimique étant alimentée par un électrolyte comprenant du CO2 ; et (b) régénérer l'électrode catalytique en abaissant la tension, puis en lavant l'électrode catalytique avec un liquide aqueux et en exposant l'électrode catalytique à l'air sans appliquer de tension ; et (c) répéter éventuellement les étapes (a) et (b).
PCT/EP2020/085585 2019-12-20 2020-12-10 Formation d'acide formique à l'aide d'une électrode catalytique contenant de l'indium WO2021122323A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
US17/781,600 US20220411942A1 (en) 2019-12-20 2020-12-10 Formation of formic acid with the help of indium-containing catalytic electrode
EP20824218.0A EP4077766A1 (fr) 2019-12-20 2020-12-10 Formation d'acide formique à l'aide d'une électrode catalytique contenant de l'indium

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP19218627 2019-12-20
EP19218627.8 2019-12-20

Publications (1)

Publication Number Publication Date
WO2021122323A1 true WO2021122323A1 (fr) 2021-06-24

Family

ID=69061068

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2020/085585 WO2021122323A1 (fr) 2019-12-20 2020-12-10 Formation d'acide formique à l'aide d'une électrode catalytique contenant de l'indium

Country Status (3)

Country Link
US (1) US20220411942A1 (fr)
EP (1) EP4077766A1 (fr)
WO (1) WO2021122323A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20230057465A1 (en) * 2020-01-30 2023-02-23 Avantium Knowledge Centre B.V. Electrochemical production of formate

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130105304A1 (en) 2012-07-26 2013-05-02 Liquid Light, Inc. System and High Surface Area Electrodes for the Electrochemical Reduction of Carbon Dioxide
WO2014032000A1 (fr) 2012-08-23 2014-02-27 Liquid Light, Inc. Réduction du dioxyde de carbone en produits à l'aide d'une électrode en oxyde d'indium
WO2014042781A2 (fr) 2012-09-14 2014-03-20 Liquid Light, Inc. Processus et électrodes à surface élevée pour réduction électrochimique de dioxyde de carbone
US20140227634A1 (en) 2011-09-15 2014-08-14 Industrie De Nora S.P.A. Gas-diffusion electrode
US20190085477A1 (en) 2017-09-20 2019-03-21 Kabushiki Kaisha Toshiba Carbon dioxide electrolytic device and method of electrolyzing carbon dioxide
WO2019141827A1 (fr) 2018-01-18 2019-07-25 Avantium Knowledge Centre B.V. Système catalytique pour réactions électrochimiques catalysées et leur préparation, leurs applications et leurs utilisations

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20140227634A1 (en) 2011-09-15 2014-08-14 Industrie De Nora S.P.A. Gas-diffusion electrode
US20130105304A1 (en) 2012-07-26 2013-05-02 Liquid Light, Inc. System and High Surface Area Electrodes for the Electrochemical Reduction of Carbon Dioxide
WO2014032000A1 (fr) 2012-08-23 2014-02-27 Liquid Light, Inc. Réduction du dioxyde de carbone en produits à l'aide d'une électrode en oxyde d'indium
US20150218716A1 (en) 2012-08-23 2015-08-06 The Trustees Of Princeton University Reducing Carbon Dioxide to Products with an Indium Oxide Electrode
WO2014042781A2 (fr) 2012-09-14 2014-03-20 Liquid Light, Inc. Processus et électrodes à surface élevée pour réduction électrochimique de dioxyde de carbone
US20190085477A1 (en) 2017-09-20 2019-03-21 Kabushiki Kaisha Toshiba Carbon dioxide electrolytic device and method of electrolyzing carbon dioxide
WO2019141827A1 (fr) 2018-01-18 2019-07-25 Avantium Knowledge Centre B.V. Système catalytique pour réactions électrochimiques catalysées et leur préparation, leurs applications et leurs utilisations

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20230057465A1 (en) * 2020-01-30 2023-02-23 Avantium Knowledge Centre B.V. Electrochemical production of formate
US11814738B2 (en) * 2020-01-30 2023-11-14 Avantium Knowledge Centre B.V. Electrochemical production of formate

Also Published As

Publication number Publication date
EP4077766A1 (fr) 2022-10-26
US20220411942A1 (en) 2022-12-29

Similar Documents

Publication Publication Date Title
Jitaru et al. Electrochemical reduction of carbon dioxide on flat metallic cathodes
WO2016134952A1 (fr) Dépôt d'un électrocatalyseur contenant du cuivre et dégageant des hydrocarbures sur des substrats sans cuivre
JPH09503956A (ja) 金属カチオンの錯体及び塩の電気透析による転化
WO2021122323A1 (fr) Formation d'acide formique à l'aide d'une électrode catalytique contenant de l'indium
JP7295882B2 (ja) 光起電力－電気化学（ｐｖ－ｅｃ）システム
JP2005501177A (ja) 電気化学的反応電極、製造方法、及びその適用機器。
EP0139382B1 (fr) Production d'une cathode pour l'utilisation dans une cellule électrolytique
WO1981002169A1 (fr) Extraction electrolytique aqueuse de metaux
US11814738B2 (en) Electrochemical production of formate
JP2012500335A (ja) 電極材料、電極および塩化水素電気分解法
US20240271294A1 (en) System for electrocatalytic conversion of carbon oxides to multicarbon products using a stationary catholyte layer and related process
EP0136794B1 (fr) Traitement des cathodes pour leur utilisation dans les cellules electrolytiques
KR102040338B1 (ko) 인 시츄 억제를 갖는 전기도금에 의해 금속 입자들을 성장시키기 위한 프로세스
JP2012077381A (ja) 輸送および貯蔵安定性酸素消費電極の製造方法
JP6438744B2 (ja) 電解用陰極の活性化方法
JP2011222438A (ja) 固体高分子電解質膜・触媒金属複合電極及びその製造方法
US20150017554A1 (en) Process for producing transport and storage-stable oxygen-consuming electrode
EP4446465A1 (fr) Electrolyse de l'eau enrichie en fer
EP0823495A1 (fr) Réactivation d'une cathode
RU2709305C1 (ru) Регенерация солянокислого медно-хлоридного раствора травления меди методом мембранного электролиза
KR20180060253A (ko) 환원 전극의 재생방법
JP3420790B2 (ja) 塩化アルカリ電解用電解槽及び電解方法
KR100837423B1 (ko) 염수 전기분해용 전해조에서 비활성화된 전극의 재생 방법
JP6926782B2 (ja) 水素発生用電極及びその製造方法並びに水素発生用電極を用いた電気分解方法
JP3344801B2 (ja) ガス電極構造体

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20824218

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2020824218

Country of ref document: EP

Effective date: 20220720