WO2021052069A1 - Dispositif et procédé d'impression 3d fondés sur une atomisation centrifuge - Google Patents

Dispositif et procédé d'impression 3d fondés sur une atomisation centrifuge Download PDF

Info

Publication number
WO2021052069A1
WO2021052069A1 PCT/CN2020/108610 CN2020108610W WO2021052069A1 WO 2021052069 A1 WO2021052069 A1 WO 2021052069A1 CN 2020108610 W CN2020108610 W CN 2020108610W WO 2021052069 A1 WO2021052069 A1 WO 2021052069A1
Authority
WO
WIPO (PCT)
Prior art keywords
molten metal
turntable
receiving unit
metal
atomized
Prior art date
Application number
PCT/CN2020/108610
Other languages
English (en)
Chinese (zh)
Inventor
魏世忠
毛丰
欧黎明
张程
陈冲
乔永枫
徐流杰
王晓东
潘昆明
李秀青
熊美
靳东亮
Original Assignee
河南科技大学
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 河南科技大学 filed Critical 河南科技大学
Priority to JP2022515922A priority Critical patent/JP7185975B2/ja
Publication of WO2021052069A1 publication Critical patent/WO2021052069A1/fr

Abstract

Selon l'invention, sont décrits un dispositif et un procédé d'impression 3D fondés sur une atomisation centrifuge, le dispositif comprenant un système de fusion, une armoire (3) comportant une cavité scellée, un plateau tournant (20), un manchon de guidage (18) et une plateforme à mouvement tridimensionnel comportant une unité de réception de métal fondu (7), et une unité de commande pour commander la plateforme à mouvement tridimensionnel. Des matières premières métalliques entrent dans la cavité scellée après avoir été fondues, et sont atomisées et projetées dans la direction circonférentielle sous l'effet de la rotation du plateau tournant ; le métal fondu atomisé passant à travers des espaces de pulvérisation (24) dans le manchon de guidage adhère à l'unité de réception de la plateforme à mouvement tridimensionnel ; et l'unité de commande commande le mouvement de la plateforme à mouvement tridimensionnel pour changer la position dans laquelle l'unité de réception reçoit le métal fondu, afin de former des pièces de formes différentes. Selon le procédé d'impression 3D fondé sur l'atomisation centrifuge, pendant la totalité du processus d'impression, les matières premières métalliques sont directement fondues et atomisées, puis empilées et solidifiées, et par la seule régulation de la vitesse de solidification des matières premières métalliques, la structure interne des pièces de sortie peut être plus dense et uniforme, ce qui améliore l'efficacité de production.
PCT/CN2020/108610 2019-09-18 2020-08-12 Dispositif et procédé d'impression 3d fondés sur une atomisation centrifuge WO2021052069A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2022515922A JP7185975B2 (ja) 2019-09-18 2020-08-12 遠心霧化による３ｄ印刷装置及び方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201910882557.5A CN110605402B (zh) 2019-09-18 2019-09-18 一种基于离心雾化的3d打印装置及方法
CN201910882557.5 2019-09-18

Publications (1)

Publication Number Publication Date
WO2021052069A1 true WO2021052069A1 (fr) 2021-03-25

Family

ID=68892930

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2020/108610 WO2021052069A1 (fr) 2019-09-18 2020-08-12 Dispositif et procédé d'impression 3d fondés sur une atomisation centrifuge

Country Status (3)

Country Link
JP (1) JP7185975B2 (fr)
CN (1) CN110605402B (fr)
WO (1) WO2021052069A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113458422A (zh) * 2021-07-01 2021-10-01 上海交通大学 一种金属液喷射成型控制装置及方法
CN116372178A (zh) * 2023-04-06 2023-07-04 扬州众力金属制造有限公司 一种发动机粉末冶金成型的制粉装置
CN116673478A (zh) * 2023-04-23 2023-09-01 安徽旭晶粉体新材料科技有限公司 一种金属铜粉雾化加工装置

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN110605402B (zh) * 2019-09-18 2021-04-30 河南科技大学 一种基于离心雾化的3d打印装置及方法
CN111112624B (zh) * 2020-02-27 2021-04-20 西安交通大学 一种金属液滴离心式增材制造装置及制造方法
CN112059199A (zh) * 2020-09-15 2020-12-11 湖南天际智慧材料科技有限公司 一种旋转盘造粒结构及其造粒方法
CN112045197A (zh) * 2020-09-15 2020-12-08 湖南天际智慧材料科技有限公司 一种旋转盘造粒设备及其生产工艺
CN112317760B (zh) * 2020-11-16 2024-03-19 华南理工大学 3dp打印件烧结方法及烧结装置
CN113579241B (zh) * 2021-08-03 2023-04-28 昆山轩塔电子科技有限公司 金属液化雾化装置
CN113618074B (zh) * 2021-08-16 2023-04-18 辽宁科技大学 一种制备铁合金颗粒的装置和方法

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998045107A1 (fr) * 1997-04-09 1998-10-15 Massachusetts Institute Of Technology Fabrication de produits tridimensionnels a l'aide de masques
CN1300871A (zh) * 1999-12-17 2001-06-27 哈尔滨工业大学 离心雾化喷射沉积复合方法及装置
CN105127415A (zh) * 2015-10-19 2015-12-09 北京化工大学 一种金属3d打印快速成型设备
CN106735275A (zh) * 2016-12-07 2017-05-31 深圳微纳增材技术有限公司 一种适用于3d打印的金属粉末制备方法及装置
CN108274013A (zh) * 2018-04-23 2018-07-13 安徽哈特三维科技有限公司 一种气雾化法制备3d打印钛合金球形粉体的专用雾化器
CN108943712A (zh) * 2018-08-29 2018-12-07 北京化工大学 一种可连续工作的3d打印系统
CN109014226A (zh) * 2018-09-25 2018-12-18 大连理工大学 一种制备3d打印用球形金属粉末的装置及方法
CN109877299A (zh) * 2019-04-16 2019-06-14 河南科技大学 一种甩铸装置及甩铸离心盘
CN110605402A (zh) * 2019-09-18 2019-12-24 河南科技大学 一种基于离心雾化的3d打印装置及方法

Family Cites Families (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1982003809A1 (fr) * 1981-05-08 1982-11-11 Rickinson Bernard Alan Dispositif de pulverisation d'un metal ou d'un autre materiau
JPS63230807A (ja) * 1987-03-19 1988-09-27 Agency Of Ind Science & Technol 遠心噴霧用の回転デイスク
CN1025660C (zh) * 1991-11-30 1994-08-17 中南工业大学 制造微细金属粉末的方法和装置
CN202336581U (zh) * 2011-10-21 2012-07-18 北华航天工业学院 金属细粉末雾化器
CN102528035B (zh) * 2011-12-31 2014-06-11 西北工业大学 一种两级雾化喷射成形圆盘类零件的系统及成型方法
CN203096086U (zh) * 2013-03-06 2013-07-31 圣火科技(河南)有限责任公司 一种干熄渣装置熔渣离心粒化旋转转杯
KR20170075446A (ko) * 2015-12-23 2017-07-03 주식회사 포스코 입체 형상물 조형 장치
CN106391370A (zh) * 2016-12-01 2017-02-15 广东工业大学 一种锥形内腔表面涂层加工装置及其加工方法
CN206392867U (zh) * 2016-12-07 2017-08-11 深圳微纳增材技术有限公司 一种制备金属粉末的离心装置
CN106735224A (zh) * 2016-12-17 2017-05-31 许昌学院 一种多孔金属结构件热熔滴打印沉积制造方法及装置
CN106862578B (zh) * 2017-02-13 2018-11-09 连云港倍特超微粉有限公司 一种组合雾化式制备球形金属合金微粉的装置和方法
CN109093128A (zh) * 2018-09-25 2018-12-28 大连理工大学 一种逐液滴雾化法制备超细低熔点球形金属粉末的装置及方法
JP2020111801A (ja) * 2019-01-15 2020-07-27 セイコーエプソン株式会社 三次元造形物の製造方法及び三次元造形物の製造装置

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998045107A1 (fr) * 1997-04-09 1998-10-15 Massachusetts Institute Of Technology Fabrication de produits tridimensionnels a l'aide de masques
CN1300871A (zh) * 1999-12-17 2001-06-27 哈尔滨工业大学 离心雾化喷射沉积复合方法及装置
CN105127415A (zh) * 2015-10-19 2015-12-09 北京化工大学 一种金属3d打印快速成型设备
CN106735275A (zh) * 2016-12-07 2017-05-31 深圳微纳增材技术有限公司 一种适用于3d打印的金属粉末制备方法及装置
CN108274013A (zh) * 2018-04-23 2018-07-13 安徽哈特三维科技有限公司 一种气雾化法制备3d打印钛合金球形粉体的专用雾化器
CN108943712A (zh) * 2018-08-29 2018-12-07 北京化工大学 一种可连续工作的3d打印系统
CN109014226A (zh) * 2018-09-25 2018-12-18 大连理工大学 一种制备3d打印用球形金属粉末的装置及方法
CN109877299A (zh) * 2019-04-16 2019-06-14 河南科技大学 一种甩铸装置及甩铸离心盘
CN110605402A (zh) * 2019-09-18 2019-12-24 河南科技大学 一种基于离心雾化的3d打印装置及方法

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN113458422A (zh) * 2021-07-01 2021-10-01 上海交通大学 一种金属液喷射成型控制装置及方法
CN113458422B (zh) * 2021-07-01 2024-01-19 上海交通大学 一种金属液喷射成型控制方法
CN116372178A (zh) * 2023-04-06 2023-07-04 扬州众力金属制造有限公司 一种发动机粉末冶金成型的制粉装置
CN116372178B (zh) * 2023-04-06 2023-10-03 扬州众力金属制造有限公司 一种发动机粉末冶金成型的制粉装置
CN116673478A (zh) * 2023-04-23 2023-09-01 安徽旭晶粉体新材料科技有限公司 一种金属铜粉雾化加工装置

Also Published As

Publication number Publication date
CN110605402B (zh) 2021-04-30
CN110605402A (zh) 2019-12-24
JP2022548571A (ja) 2022-11-21
JP7185975B2 (ja) 2022-12-08

Similar Documents

Publication Publication Date Title
WO2021052069A1 (fr) Dispositif et procédé d'impression 3d fondés sur une atomisation centrifuge
WO2021073107A1 (fr) Procédé d'impression tridimensionnelle et dispositif d'impression tridimensionnelle
CN104084596B (zh) 非晶态粉末的制备方法及装置
EP1795282B1 (fr) Élément pulvérisateur à atomisation centrifuge et guidage d'air
CN101637823B (zh) 一种制备金属粉末的方法及其装置
CN113059169A (zh) 一种采用转盘离心雾化法生产高温金属粉末的装置
CN109877299B (zh) 一种甩铸装置及甩铸离心盘
US4218410A (en) Method for the production of high-purity metal powder by means of electron beam heating
CN106956008A (zh) 一种3D打印用Hastelloy X合金粉末的制备方法
CN211614316U (zh) 真空紧耦合气雾化制粉用的预热系统及真空紧耦合气雾化制粉系统
CN110280763A (zh) 同轴送粉激光烧结装置
CN110961739A (zh) 一种带同轴视觉系统的锡球焊接装置
CN114192790A (zh) 球形钛及钛合金粉末制备装置和方法
CN215392473U (zh) 一种射频等离子旋转雾化制粉设备
CA1139065A (fr) Refroidissement par projection de gouttelettes de metal en fusion
CN202317021U (zh) 一种喷射成形制备合金及金属基零部件的装置
CN113737176A (zh) 一种风电滑动轴承的制造方法
CN113305392A (zh) 一种锡球焊接设备
EP3659731B1 (fr) Appareil de production de poudre métallique
CN216680211U (zh) 一种雾化室温度调节装置
CN109806988B (zh) 一种防止结瘤堵嘴的金属熔体喷射沉积雾化器
CN114700573B (zh) 一种激光锡球焊装置
US4217082A (en) Spin cup means for the production of metal powder
CN211939058U (zh) 一种快速凝固金属粉末的生产设备
CN209791800U (zh) 一种防止结瘤堵嘴的金属熔体喷射沉积雾化器

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20865985

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022515922

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20865985

Country of ref document: EP

Kind code of ref document: A1