WO2021047700A1 - Moyen insecticide pour la protection du bois - Google Patents
Moyen insecticide pour la protection du bois Download PDFInfo
- Publication number
- WO2021047700A1 WO2021047700A1 PCT/CZ2020/050068 CZ2020050068W WO2021047700A1 WO 2021047700 A1 WO2021047700 A1 WO 2021047700A1 CZ 2020050068 W CZ2020050068 W CZ 2020050068W WO 2021047700 A1 WO2021047700 A1 WO 2021047700A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- means according
- fiber
- insecticide
- carrier
- textile
- Prior art date
Abstract
L'invention concerne un moyen insecticide qui se présente sous la forme d'au moins un support de fibres solide qui comprend des nanofibres contenant au moins un polymère synthétique choisi dans le groupe contenant le polyamide, le polyuréhane, le polyfluorure de vinylidène, le difluorure de polyvinylidène, l'acétate de cellulose, le polylactide, le polycaprolactone, le polyvinylbutyral, l'acide polylactique ou des mélanges de ceux-ci et au moins un agent actif ou un mélange de ceux-ci; le support de fibres étant fixé à au moins un côté du support textile par stratification.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CZPV2019-573 | 2019-09-11 | ||
CZ2019-573A CZ309702B6 (cs) | 2019-09-11 | 2019-09-11 | Insekticidní prostředek na ochranu dřeva proti škůdcům |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2021047700A1 true WO2021047700A1 (fr) | 2021-03-18 |
Family
ID=73029777
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CZ2020/050068 WO2021047700A1 (fr) | 2019-09-11 | 2020-09-11 | Moyen insecticide pour la protection du bois |
Country Status (2)
Country | Link |
---|---|
CZ (1) | CZ309702B6 (fr) |
WO (1) | WO2021047700A1 (fr) |
Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2008032844A2 (fr) * | 2006-09-11 | 2008-03-20 | Sumitomo Chemical Company, Limited | Fibre anti-insectes |
WO2008118955A1 (fr) * | 2007-03-27 | 2008-10-02 | Danaldson Company, Inc. | Tissu composite de haute durabilité |
WO2010012671A2 (fr) * | 2008-07-30 | 2010-02-04 | Basf Se | Filets imprégnés d'insecticides et leur utilisation pour la protection contre les parasites |
US20120270942A1 (en) * | 2009-10-21 | 2012-10-25 | Justus-Liebig-Universitat Giessen | Spreading Active Agricultural Agents |
WO2013171118A2 (fr) * | 2012-05-16 | 2013-11-21 | Intelligent Insect Control | Moustiquaire avec insecticide puissant |
CZ2017402A3 (cs) * | 2017-07-12 | 2019-01-23 | Nano Medical s.r.o. | Způsob výroby textilního materiálu obsahujícího nanovlákennou vrstvu |
Family Cites Families (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH0624907A (ja) * | 1992-04-01 | 1994-02-01 | Kanebo Ltd | 防虫用被覆材及びその製造方法並びに殺虫剤固着液 |
WO2011046657A2 (fr) * | 2009-07-22 | 2011-04-21 | Massachusetts Institute Of Technology | Membranes multifonctionnelles traitées électriquement |
-
2019
- 2019-09-11 CZ CZ2019-573A patent/CZ309702B6/cs unknown
-
2020
- 2020-09-11 WO PCT/CZ2020/050068 patent/WO2021047700A1/fr active Application Filing
Patent Citations (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2008032844A2 (fr) * | 2006-09-11 | 2008-03-20 | Sumitomo Chemical Company, Limited | Fibre anti-insectes |
WO2008118955A1 (fr) * | 2007-03-27 | 2008-10-02 | Danaldson Company, Inc. | Tissu composite de haute durabilité |
WO2010012671A2 (fr) * | 2008-07-30 | 2010-02-04 | Basf Se | Filets imprégnés d'insecticides et leur utilisation pour la protection contre les parasites |
US20120270942A1 (en) * | 2009-10-21 | 2012-10-25 | Justus-Liebig-Universitat Giessen | Spreading Active Agricultural Agents |
WO2013171118A2 (fr) * | 2012-05-16 | 2013-11-21 | Intelligent Insect Control | Moustiquaire avec insecticide puissant |
CZ2017402A3 (cs) * | 2017-07-12 | 2019-01-23 | Nano Medical s.r.o. | Způsob výroby textilního materiálu obsahujícího nanovlákennou vrstvu |
Non-Patent Citations (3)
Title |
---|
BEHNAD ROSHANI ET AL: "Controlled release of thiram pesticide from poly (L-lactic acid) nanofibers", THE JOURNAL OF THE TEXTILE INSTITUTE, vol. 108, no. 9, 21 November 2016 (2016-11-21), GB, pages 1504 - 1509, XP055620141, ISSN: 0040-5000, DOI: 10.1080/00405000.2016.1258950 * |
CHUNHUI XIANG ET AL: "Structure and Properties of Polyamide Fabrics with Insect-Repellent Functionality by Electrospinning and Oxygen Plasma-Treated Surface Coating", POLYMERS, vol. 12, no. 10, 1 October 2020 (2020-10-01), CH, pages 2196, XP055761464, ISSN: 2073-4360, DOI: 10.3390/polym12102196 * |
SENEM AVAZ SEVEN ET AL: "Abstract", BIORXIV, 31 July 2018 (2018-07-31), XP055621707, Retrieved from the Internet <URL:https://www.biorxiv.org/content/biorxiv/early/2018/07/31/381426.full.pdf> DOI: 10.1101/381426 * |
Also Published As
Publication number | Publication date |
---|---|
CZ309702B6 (cs) | 2023-08-09 |
CZ2019573A3 (cs) | 2021-03-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN102149860B (zh) | 灭除昆虫的纺织品 | |
US8215051B2 (en) | Pest control materials | |
TWI411717B (zh) | 殺蟲紡織品、製造方法及使用方法 | |
JP4387798B2 (ja) | 積層殺虫剤ディスペンサー | |
TW200916021A (en) | Insecticidal barrier partly with synergist | |
KR20100038402A (ko) | 내구성 하부가 있는 살충 장막 | |
US20090326064A1 (en) | Pesticidal composition | |
WO2010015256A2 (fr) | Matrice polymère insecticide comprenant du hdpe et du ldpe | |
CN1291075A (zh) | 防止木材害虫进入木质结构的阻挡层 | |
WO2013171118A2 (fr) | Moustiquaire avec insecticide puissant | |
JP2000189032A (ja) | 薬剤蒸散剤 | |
KR20110042186A (ko) | 피비오 및 디엠을 포함하는 살충성 중합체 매트릭스 | |
US20060198857A1 (en) | Insect control system | |
WO2021047700A1 (fr) | Moyen insecticide pour la protection du bois | |
MX2015006235A (es) | Uso de un compuesto que comprende un resto de polifluorobencilo contra plagas resistentes a insecticidas. | |
CZ33382U1 (cs) | Insekticidní prostředek na ochranu dřeva proti škůdcům | |
JP2002003313A (ja) | 飛翔害虫防除方法 | |
JP2005320279A (ja) | 薬剤保持体 | |
KR200331589Y1 (ko) | 해충 방제용 수목 보호대 | |
CZ36974U1 (cs) | Insekticidní prostředek se zlepšenou prodyšností na ochranu dřeva proti škůdcům | |
JP6827237B2 (ja) | 害虫駆除シート | |
JP4441017B2 (ja) | 携帯型飛翔害虫防除装置 | |
JP3831010B2 (ja) | ドウガネブイブイの誘引剤 | |
JP2006141399A (ja) | 薬剤蒸散装置 | |
JP2005145919A (ja) | 犬小屋の防虫方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 20797659 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 20797659 Country of ref document: EP Kind code of ref document: A1 |