WO2020255377A1 - 糸、織物およびその糸の製造方法 - Google Patents

糸、織物およびその糸の製造方法 Download PDF

Info

Publication number
WO2020255377A1
WO2020255377A1 PCT/JP2019/024728 JP2019024728W WO2020255377A1 WO 2020255377 A1 WO2020255377 A1 WO 2020255377A1 JP 2019024728 W JP2019024728 W JP 2019024728W WO 2020255377 A1 WO2020255377 A1 WO 2020255377A1
Authority
WO
WIPO (PCT)
Prior art keywords
sheet
yarn
carbon
japanese paper
strip
Prior art date
Application number
PCT/JP2019/024728
Other languages
English (en)
French (fr)
Inventor
大木　武彦
大木　達彦
Original Assignee
株式会社大木工藝
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社大木工藝 filed Critical 株式会社大木工藝
Priority to PCT/JP2019/024728 priority Critical patent/WO2020255377A1/ja
Publication of WO2020255377A1 publication Critical patent/WO2020255377A1/ja

Abstract

本発明に係る糸１５、１６、は、炭素材料（炭素シート１１）と和紙材料（和紙シート１２）とを備えて形成されている。

Description

糸、織物およびその糸の製造方法
　本発明は、炭素材料と和紙材料とを備えた糸、織物布地および糸の製造方法に関する。
　和紙は、伸縮性や通気性、強靭性などのすぐれた特性を有することから、衣料の材料としても用いられている。例えば特許文献１には、和紙シートをシート基材とした引箔用シート、引箔糸が提案されている。引箔糸は例えば帯などの織物の緯糸として用いられる。
　一方、炭素材料を含んだ糸（撚糸）についても多く提案されている。この種の糸は、例えば空気清浄用フィルター、人工透析用フィルターなどの工業製品などに用いられる。また、炭素材料は遠赤外線を放射することが一般に知られており、遠赤外線の放射による血流促進効果などの人体への健康増進作用があることも知られている。
特許第４０１３０６６号公報
　上記のような和紙材料、炭素材料のそれぞれの利点を生かすべく、それらを組み合わせた材料は、健康増進作用を有するとともに衣料としてもすぐれたものとなり得るが、そのような材料はいまだ開発されていない。
　本発明は、このような事情を考慮して提案されたもので、和紙材料と炭素材料の特性を生かした糸、それを用いた織物および糸の製造方法を提供することにある。
　上記目的を達成するために、本発明の糸は、炭素材料と和紙材料とを備えたことを特徴とする。
　また、本発明の糸の製造方法は、炭素材料と和紙材料とを備えた糸の製造方法であって、炭素シートと和紙シートとを貼り合わせてシート材を成形する貼着工程と、シート材を糸状に裁断する裁断工程とを備えたことを特徴とする。
　本発明の糸は上述した構成とされているため、炭素材料による健康増進効果を有した衣料などの生活用品に利用することができる。また、和紙材料を含んでいるため、その種々の特性を生かすことができる。また、金や銀などを付加すれば、織物の引箔としても利用できる。
　本発明の糸の製造方法は上述した手順とされているため、炭素材料と和紙材料の両方を含んだ糸を簡単に製造することができる。
本発明の一実施形態に係る糸の説明図である。（ａ）は糸の材料とされるシート材の製造方法を示す概略部分断面図、（ｂ）はシート材をもとにした糸（帯状材）の生成方法を示す模式的斜視図、（ｃ）はシート材の他例を示す概略部分断面図である。 （ａ）（ｂ）は、糸（撚糸）の加工方法の２例を示す図である。（ｃ）は、撚糸の部分拡大図である。 撚糸を用いて形成した織物の模式説明図である。 （ａ）（ｂ）は、他の層構成のシート材（帯状材）の２例を示す概略部分断面図である。 シート材（帯状材）に用いられる活性炭（球状微粒子活性炭）の拡大断面図である。
　以下に、本発明の実施の形態について、添付図面をもとに説明する。
　本実施形態に係る糸１５、１６は、炭素材料と和紙材料とを備えている。まず、この糸１５、１６について、その製造方法とともに記述する。なお、本実施形態に係る糸１５、１６として、帯状材１５および撚糸１６が含まれる。
　図１および図２は、本糸の製造方法の手順を示す図である。
　まず、糸１５、１６の材料とされるシート材１０を、基材である和紙シート１２（和紙材料）と、炭素シート１１（炭素材料）との貼り合わせにて作製する（貼着工程）。
　炭素シート１１としては、結晶化された炭素材料を膨張させて生成した、炭素比率が９９％の膨張黒鉛を圧延して３０μｍ～７０μｍの厚さにしたものを好適に用いられる。４００度以上の熱圧延にて炭素シート１１を作製することが望ましい。
　和紙シート１２については種々のものを用いることができるが、水に強いものを用いることが望ましい。また、和紙シート１２は、種々の色にあらかじめ染色したものであってもよい。
　貼り合わせ用の粘着剤（不図示）としては、アクリル系、ゴム系、シリコーン系、ウレタン系など種々の公知のものを用いることができる。具体的には、アクリル溶剤系粘着剤（アクリル酸エステル共重合体）は、強粘着性があり、耐候性に優れ、好適である。また、シリコーン系粘着剤は２００℃以上の熱に耐え得る。粘着剤としては、ホットメルト粘着剤を用いることができる。
　貼り合わせ手順としては、図１（ａ）に示すように、基材である和紙シート１２の一方の面に粘着剤を塗布し、その粘着面１２ａに炭素シート１１を貼り合わせればよい。塗布の方法としては、貼着面１２ａの一面に塗布してもよいが、網目状に塗布してもよい。また、貼着面１２ａに粘着剤を噴霧してもよい。
　また、例えば、和紙シート１２／炭素シート１１／和紙シート１２の層構成（図１（ｃ）参照）や、炭素シート１１／和紙シート１２／炭素シート１１の層構成よりなる３層のシート材１０や、さらに多層のシート材１０を形成してもよい。シート材１０には、少なくとも炭素シート１１と和紙シート１２の両方が含まれればよい。
　図１（ｃ）に示した、和紙シート１２／炭素シート１１／和紙シート１２の３層構成のシート材１０によれば、濃色系の炭素シート１１を和紙シート１２で挟むため、シート材１０の両面を白などの淡色系や染色した色とすることができる。なお、和紙シート１２の染色は、炭素シート１１と貼り合わせする前、後のいずれであってもよい。
　ついで、このように作製したシート材１０を裁断して帯状材１５を形成する（裁断工程）。
　帯状材１５の幅寸法を０．１ｍｍ～５ｍｍ程度として裁断することが望ましいが、これには限らない。帯状材１５としては、幅寸法が小さい繊維状のものであってもよいし、幅広のものであってもよい。
　シート材１０が炭素シート１１と和紙シート１２との層状材であるから、裁断して得た帯状材１５もそれらの材料を含んでいる。また、和紙シート１２や、和紙シート１２と炭素シート１１の間に抗菌剤３３（図５参照）を含ませてもよい。抗菌剤３３としては、銀系の無機抗菌剤を用いることができる。なお、抗菌剤３３はそれぞれのシートの内部や、シート間に配してもよいし、活性炭とともにシート間に配してもよい。活性炭に抗菌剤３３を含ませた例の詳細については、図５の説明とともに後述する。
　裁断して得た帯状材１５は、強度を得るために、この帯状材１５をもとに撚糸１６に加工すること（加工工程）が望ましい。加工工程としては、例えば図２（ａ）（ｂ）に示した２種の方法が想定される。
　図２（ａ）に示した方法は、１本の帯状材１５をもとに撚り装置１にて撚糸１６に加工する方法であり、図２（ｂ）に示した方法は複数本の帯状材１５をもとに、上記撚り装置１とは異なる撚り装置２にて撚糸１６に加工する方法である。
　帯状材１５の幅寸法が微細である場合には、図２（ｂ）に示した方法にて、帯状材１５を束ねるようにして撚ることが望ましいが、幅寸法が大きい帯状材１５に関しては、１本の帯状材１５を長手方向に延ばしながら撚ればよい。
　撚糸１６の例として部分拡大図を図２（ｃ）に示したが、撚り方としては、このような撚り方に限らず、種々のものがある。例えば、片撚り（右撚り、左撚り）、右撚りした糸と左撚りした糸との撚り、片撚りと撚りがかかっていない糸との撚り、など種々の撚り方が挙げられる。また、撚りの強度としても、５００Ｔ／ｍ（１メートル当たりの回転数）以下、５００～１０００Ｔ／ｍ、１０００～２５００Ｔ／ｍ、２５００Ｔ／ｍ以上など種々のものが想定される。
　このように、帯状材１５を撚糸１６に加工することで、繊維状の帯状材１５を用いた場合であっても強度を上げることができる。また、帯状材１５を撚って長手方向につなぎ合わせることもできるため、長尺状の撚糸１６を形成することもできる。
　本撚糸１６の原材料である炭素シート１１および和紙シート１２は可撓性を有しているため、従来公知の糸と同様に、布地（例えば織物２０）の材料としても利用することができる。
　また、帯状材１５は炭素シート１１、和紙シート１２を含んで強靭でかつ伸縮性も低いものであるから、帯状材１５から撚糸１６を形成することなく、帯状材１５をそのまま糸として用いてもよい。帯状材１５を撚糸１６に加工することなく、帯状材１５を例えば織物２０の材料として用いることもできる。
　帯状材１５または撚糸１６を用いて織物２０を形成する場合には、例えば、経糸２１、緯糸２２の一方に帯状材１５または撚糸１６を用い、他方に他の糸（撚糸）を用いればよい。他の糸の材料としては、絹糸、木綿糸、麻糸、合成繊維糸などが想定されるが、経糸２１、緯糸２２の両方に帯状材１５、撚糸１６を用いてもよい。
　また、図１（ｃ）に示した、和紙シート１２／炭素シート１１／和紙シート１２の３層構成のシート材１０をもとに形成した帯状材１５を経糸２１または緯糸２２に用いれば、帯状材１５は和紙を２層にしているためより強靭であり、織物２０の材料として有効に利用することができる。このような帯状材１５を用いれば、炭素材料１１による濃色系の色が織物２０の表面に出ず、和紙材料１２の淡色系の色や染色した色を表出させることができる。例えば、和紙材料１２を金色に染めた帯状材１０をもとに西陣織のような織物２０を生成することもできる。
　上記のように、帯状材１５および撚糸１６は炭素シート１１を原材料としているため伸縮性はあまりない。そのため、経糸２１、緯糸２２の一方に伸縮性のある糸を採用することで、伸縮性が必要とされる衣料用の織物２０を形成することもできる。
　このような織物２０には和紙材料１２と炭素材料１１とが含まれているため、織物２０やその他布地をもとにして、強靭で遠赤外線放射性を有した衣料、カーテンなどの生活用品の布地を形成することができる。ようするに、和紙材料１２と炭素材料１１の両方の特性を有した、丈夫で健康増進効果を期待できる布地を形成することができる。また、抗菌剤３３（図５参照）を含むシート材１０を用いれば、織物２０に抗菌作用を付加することができ、衣料などの生活用品に好適に使用することができる。織物２０は和紙が用いてあるため、夏の衣料にも利用できる。
　ここで、結晶化された炭素材料がもたらす遠赤外線効果のメカニズムについて述べる。
　人体は、身体組成の６０％は水分、２５％は炭素であり、３６．５℃の平均体温で常に１０ミクロンの遠赤外線を放射している。一方、上述のように高温焼成により結晶化させた炭素材料は導電性が高いため、熱伝導性も高く、熱吸収がよい。したがって、人体の皮膚に上述の炭素材料１１が触れたり近づいたりすると、人体が遠赤外線を吸収して加温される。すなわち、これら炭素材と人体との間で同じ波長の遠赤外線を放射し合い、炭素材は約３６．５℃を維持する一方で身体の中では水分子が激しく衝突して、この振動が運動エネルギーとなって、熱に変換され身体が加温される。
　その結果、遠赤外線が皮下組織や血管などに作用して血流が改善され、本発明者によれば、抹消、中枢の血流に１５％の上昇効果があることが確認されている。また、これらの炭素材は、α波を発生して、身体を癒して疲労を軽減し、健康増進に寄与すると考えられる。
　帯状材１５および撚糸１６に用いられる炭素シート１１は、面方向に結晶が並んでなり、そのため面方向の熱伝導率が高い（２５０～５００Ｗ／（ｍ・Ｋ））。そのため、帯状材１５や撚糸１６を枕カバーや夏用のシーツに用いれば放熱効果を期待できる。また、下着やサポーターなどの身体に密着する衣料に用いれば、それらの衣料に身体の熱を吸収させることができ、清涼感が得られる。
　また、帯状材１５または撚糸１６の材料である和紙材料（和紙シート１２）は水に強いため、それらの糸１５、１６を用いた衣料の洗濯も問題なく行うことができる。
　ついで、他の構成のシート材１０、帯状材１５について、図４を参照しながら説明する。
　図４（ａ）（ｂ）に示したシート材１０（帯状材１５）は、図１に示したシート材１０（帯状材１５）の一方の面に装飾層１３を配したものである。
　装飾層１３としては、種々の材料、例えば金箔、銀箔などを薄膜状に加工した薄膜が用いられる。また、塗料や染料を塗布して装飾層１３を形成してもよい。塗料としては、着色塗料、透明塗料を挙げられる。また、染料としては、天然染料、合成染料を挙げられる。
　装飾層１３としては、上記の薄膜、塗料、染料に加えて、あるいは代えて、種々の変色粉末による変色層を使用することもできる。変色粉末としては、アルミニウム粉、金粉、銀粉、雲母粉、貝殻粉などを挙げることができる。
　このように表面に装飾層１３を有したシート材１０を裁断して得た帯状材１５によれば、その帯状材１５をそのままあるいは撚糸１６に加工したのち、経糸２１、緯糸２２のすくなくとも一方に用いることで、装飾性の豊かな織物２０（図３参照）を形成することができる。
　図４（ａ）に示した、炭素シート１１を和紙シート１２と装飾層１３とで挟んだ帯状材１５を用いて織物２０を形成してもよい。例えば、金色に染色した和紙シート１２と、金粉などを付加した装飾層１３とを用いた帯状材１５を用いれば、両面に装飾性豊かな色を表出させた織物２０を製造することができる。
　以上に示した種々の実施形態において、帯状材１５（シート材１０）の炭素シート１１、和紙シート１２間などの構成層間に活性炭を配してもよい。活性炭としては、粒径を例えば球径が１５０μｍ～６００μｍの球状微粒子活性炭３０が挙げられる。
　例えば、アイオノマー樹脂溶液（不図示）に浸した状態の球状微粒子活性炭３０を、２枚のシート間に挟み込んで、保持させるようにすればよい。より具体的には、多数の球状微粒子活性炭３０を浸した上記溶液を炭素シート１１などの一方の面に塗り、その上に他方のシートを貼りつければよい。なお、他の接着剤を用いて球状微粒子活性炭３０を挟み込むこともできる。
　図５は、球状微粒子活性炭３０の拡大断面図である。この図に示すように、球状微粒子活性炭３０は略真球形状をなしている。
　図５に示すように、球状微粒子活性炭３０の内部には、球体表面に開口する複数の孔部３１が形成されている。これら孔部３１は、球内部に向かって形成される複数のマクロ孔３１ａを有しており、各マクロ孔３１ａには、そのマクロ孔３１ａを幹としてここから枝分かれするように複数のミクロ孔３１ｂが形成されている。ミクロ孔３１ｂの孔径寸法は、マクロ孔３１ａよりも小さい。このような構成の孔部３１が複数設けられていることにより、球状微粒子活性炭３０は、超多孔質とされている。
　球状微粒子活性炭３０は、炭素材であるため遠赤外線を放射する。球状微粒子活性炭３０としては、炭素純度が９０％以上のものを用いればよく、望ましくは９９．９％以上のものを用いればよい。また、球径が１５０μｍ～６００μｍのものを用いることが望ましく、大きさにばらつきがないように１８０μｍ～５００μｍのものを用いることがさらに望ましい。
　また、細孔容積が０．９ｃｍ３／ｇ～２．０ｃｍ３／ｇ、細孔ピーク直径が０．５ｎｍ～２．０ｎｍのものを用いればよい。ここで、細孔容積とは、球状微粒子活性炭３０内に形成された全てのマクロ孔３１ａおよびミクロ孔３１ｂの孔内の容積の和であり、また、細孔ピーク直径とは、孔部３１における球状微粒子活性炭３０表面の開口径のうち最大のものを指す。
　本実施形態では、球状微粒子活性炭３０は、炭化させたフェノール樹脂から構成されており、比表面積が１，０００ｍ２／ｇ以上とされている。ここで、比表面積とは、球状微粒子活性炭３０の球表面の面積、およびすべての孔部３１のマクロ孔３１ａおよびミクロ孔３１ｂを構成する面の面積の合計である。
　球状微粒子活性炭３０は、例えば以下のようにして製造すればよい。
　まず、原料となるフェノール樹脂などを粉砕し、粉砕片を加工して複数の球体を得る。この球体を高温下（例えば７００℃～８００℃程度）で炭化させた後、その処理物を高温下（例えば９００℃～１０００℃程度）で水蒸気と反応させる（水蒸気賦活）。この水蒸気賦活により多孔質の構造が形成される（この場合、比表面積が１，０００ｍ２／ｇ～２，０００ｍ２／ｇ程度になる）。その後、精製し不純物を取り除き、ふるい分けを行い、所望の粒径、および所望のマクロ孔３１ａおよびミクロ孔３１ｂの孔径を有した多数の孔部３１が形成された球状微粒子活性炭３０が得られる。
　また、球状微粒子活性炭３０に代えて、ペットボトルの再利用による活性炭を用いる場合には、その活性炭は、ペットボトルをフレーク状にして炭化させた後、賦活することで得ることができる。この場合も、比表面積が１，０００ｍ２／ｇ～２，０００ｍ２／ｇのものが得られる。
　なお、上記の賦活としては、水蒸気賦活に限られず、二酸化炭素や空気などを用いて行なってもよい。また、ＫＯＨなどを用いたアルカリ賦活を行なってもよい。また、球状微粒子活性炭３０の原料としては、フェノール樹脂に限られず、ヤシ殻炭や石灰などとしてもよい。ペットボトルを原材料とした場合には、２，５００ｍ２／ｇ～３，６００ｍ２／ｇのものが得られる。
　球状微粒子活性炭３０としては、例えば、Ｂ’ｓ　Ｗｉｐｅｒ（登録商標）や、特許第４２６６７１１号公報および特許第４３０８７４０号公報に開示された製法で製造されたものを好適に使用することができる。この種の球状微粒子活性炭３０を用いれば、帯状材１５（シート材１０）より抜け出た場合でも、周辺が汚れるおそれはない。
　また、球状微粒子活性炭３０としては、強い圧力や衝撃が加えられても割れて粉々にならず、色素などが皮膚などに付着するおそれがないものを利用することが望ましい。さらにｐＨ値が７前後（中性）のものとすることが望ましい。
　また、図５に示すように、球状微粒子活性炭３０には機能性物質として消臭分解酵素３２が収蔵されている。消臭分解酵素３２としては、臭い成分を活性酸素で酸化して別の物質に変化させてその臭い成分を分解する作用を有する人工酵素を用いればよい。
　このような消臭分解酵素３２として、ＤＥＯＲＡＳＥ（登録商標）がある。このＤＥＯＲＡＳＥ（登録商標）は、アルカリ条件での中心金属の脱離による消臭効果の低下が見られず、生体内の酵素に似たサイクル反応をもたらすため、他の化学反応を用いた消臭剤と比べて、格段に消臭効果が持続する。また、一般的に、上記サイクル反応の反応性は、吸湿による水分により低下することが知られているが、ＤＥＯＲＡＳＥ（登録商標）では、逆に吸湿により反応性が向上することがわかっている。
　なお、消臭分解酵素３２としては、これ以外に、例えば、人工酵素である鉄系フタロシアニンなどを用いたものを採用してもよい。
　また、球状微粒子活性炭３０には、他の機能性物質として抗菌剤３３が収蔵されている。抗菌剤３３としては、無機系の抗菌剤３３を用いることができ、抗菌作用を有する金属や金属イオンを無機系担体に担持させて構成したものを用いればよい。このような無機系の抗菌剤３３としては、例えば、粉体である銀系の無機抗菌剤（例えば、ノバロン（登録商標））を用いてもよい。無機系の抗菌剤３３は、溶液に溶解又は分散させて、球状微粒子活性炭３０の孔部３１内に含侵させるようにしてもよい。これにより、球状微粒子活性炭３０を含むシート材１０（帯状材１５）を、雑菌が繁殖しにくいなどの抗菌効果を有するものにすることができ、シート材１０の劣化を防ぐことができる。
　衣服に人体の皮膚が接触した場合、皮膚の汗や皮脂などが衣服の内部に吸い取られて、皮膚表面に存在する雑菌によってこれらが分解され、いわゆる分解臭である悪臭が生じるが、上記のような抗菌剤３３を球状微粒子活性炭３０内に含ませれば、雑菌がこれにより死ぬので、雑菌による汗や皮脂などの分解が抑えられ、悪臭の発生が抑制される。
　これら機能性物質は、図５に示すように、球状微粒子活性炭３０の孔部３１内に収蔵されている。図例では、機能性物質が孔部３１のマクロ孔３１ａ内に収蔵されている例を示しているが、ミクロ孔３１ｂ内に収蔵されていてもよい。球状微粒子活性炭３０は複数の孔部３１を有した超多孔質であるので、多数の機能性物質を孔部３１内に効率よく含ませることができる。なお、球状微粒子活性炭３０に機能性物質として芳香剤を含ませてもよい。
　さらに、球状微粒子活性炭３０には抗菌剤３３も含まれているため、抗菌作用も奏せられ、消臭分解酵素３２による消臭作用とあいまって、帯状材１５を用いた衣服を清浄な状態に維持することができる。
　１０　　　　　シート材
　１１　　　　　炭素シート（炭素材料）
　１２　　　　　和紙シート（和紙材料）
　１２ａ　　　　粘着面
　１３　　　　　装飾層
　１５　　　　　帯状材（糸）
　１６　　　　　撚糸（糸）
　２０　　　　　織物
　２１　　　　　経糸
　２２　　　　　緯糸
　１、２　　　　撚り装置
　３０　　　　　球状微粒子活性炭
　３１　　　　　孔部
　３１ａ　　　　マクロ孔
　３１ｂ　　　　ミクロ孔
　３２　　　　　消臭分解酵素
　３３　　　　　抗菌剤
 

 

Claims (8)

  1. 　炭素材料と和紙材料とを備えたことを特徴とする糸。
  2. 　請求項１において、
    　前記炭素材料と前記和紙材料とは層状に固着されていることを特徴とする糸。
  3. 　請求項１または２において、
    　前記炭素材料は原材料が膨張黒鉛とされることを特徴とする糸。
  4. 　請求項１～３のいずれかに記載の糸を用いた織物。
  5. 　炭素材料と和紙材料とを備えた糸の製造方法であって、
    　炭素シートと和紙シートとを貼り合わせてシート材を成形する貼着工程と、
    　前記シート材を帯状に裁断する裁断工程とを備えたことを特徴とする、糸の製造方法。
  6. 　請求項５において、
    　前記裁断工程で得た糸をもとにして撚糸に加工する加工工程をさらに備えたことを特徴とする糸の製造方法。
  7. 　請求項５において、
    　前記裁断工程で得た複数の糸をもとに撚糸に加工する加工工程をさらに備えたことを特徴とする糸の製造方法。
  8. 　請求項５～７のいずれか１項において、
    　前記炭素シートは、膨張黒鉛を厚さ３０～７０μｍに圧延して形成されていることを特徴とする糸の製造方法。

     
PCT/JP2019/024728 2019-06-21 2019-06-21 糸、織物およびその糸の製造方法 WO2020255377A1 (ja)