WO2020246207A1 - 電子装置の製造方法 - Google Patents

電子装置の製造方法 Download PDF

Info

Publication number
WO2020246207A1
WO2020246207A1 PCT/JP2020/019120 JP2020019120W WO2020246207A1 WO 2020246207 A1 WO2020246207 A1 WO 2020246207A1 JP 2020019120 W JP2020019120 W JP 2020019120W WO 2020246207 A1 WO2020246207 A1 WO 2020246207A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive
adhesive resin
resin layer
mass
electronic device
Prior art date
Application number
PCT/JP2020/019120
Other languages
English (en)
French (fr)
Inventor
三浦　徹
宏嘉 栗原
Original Assignee
三井化学東セロ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三井化学東セロ株式会社 filed Critical 三井化学東セロ株式会社
Priority to US17/596,021 priority Critical patent/US20220319918A1/en
Priority to SG11202113246XA priority patent/SG11202113246XA/en
Priority to JP2021524726A priority patent/JP7269336B2/ja
Priority to EP20817947.3A priority patent/EP3978577A4/en
Priority to CN202080040890.2A priority patent/CN113966372A/zh
Priority to KR1020217039543A priority patent/KR102662547B1/ko
Publication of WO2020246207A1 publication Critical patent/WO2020246207A1/ja

Abstract

基材層（１０）と、基材層（１０）の第１面（１０Ａ）側に設けられた粘着性樹脂層（Ａ）と、基材層（１０）の第２面（１０Ｂ）側に設けられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、を備え、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ'が０．２×１０６Ｐａ以上４．５×１０６Ｐａ以下である粘着性フィルム（５０）と、粘着性フィルム（５０）の粘着性樹脂層（Ａ）に貼り付けられた電子部品（７０）と、粘着性フィルム（５０）の粘着性樹脂層（Ｂ）に貼り付けられた支持基板（８０）と、を備える構造体（１００）を準備する工程（１）と、封止材（６０）により電子部品（７０）を封止する工程（２）と、外部刺激を与えることにより粘着性樹脂層（Ｂ）の粘着力を低下させて構造体（１００）から支持基板（８０）を剥離する工程（３）と、電子部品（７０）から粘着性フィルム（５０）を剥離する工程（４）と、を少なくとも備える電子装置の製造方法。

Description

電子装置の製造方法
　本発明は、電子装置の製造方法に関する。
　電子装置（例えば、半導体装置）の小型化・軽量化を図ることができる技術として、ファンアウト型ＷＬＰ（ウエハレベルパッケージ）が開発されている。
　ファンアウト型ＷＬＰの作製方法のひとつであるｅＷＬＢ（Embedded Wafer Level Ball Grid Array）では、支持基板に貼り付けた粘着性フィルム上に、半導体チップ等の複数の電子部品を離間させた状態で仮固定し、封止材により複数の電子部品を一括封止する手法が取られる。ここで、粘着性フィルムは、封止工程等においては電子部品および支持基板に固着させる必要があり、封止後は支持基板とともに封止された電子部品から除去する必要がある。
　このようなファンアウト型ＷＬＰの製造方法に関する技術としては、例えば、特許文献１（特開２０１１－１３４８１１号）に記載のものが挙げられる。
　特許文献１には、基板レス半導体チップを樹脂封止する際に、貼着して使用される半導体装置製造用耐熱性粘着シートであって、上記耐熱性粘着シートは基材層と粘着剤層とを有し、該粘着剤層は貼り合わせ後の対ＳＵＳ３０４粘着力が０．５Ｎ／２０ｍｍ以上であり、樹脂封止工程完了時点に至るまでに受ける刺激により硬化して、対パッケージ剥離力が２．０Ｎ／２０ｍｍ以下になる層であることを特徴とする半導体装置製造用耐熱性粘着シートが記載されている。
特開２０１１－１３４８１１号公報
　本発明者らの検討によれば、粘着性フィルム上に電子部品を配置して封止材により電子部品を封止する際に、電子部品の位置がずれてしまう場合（以下、電子部品の位置ずれとも呼ぶ。）や、支持基板に貼り付けた粘着性フィルム上に電子部品を配置して封止材により電子部品を封止し、その後、粘着性フィルムから電子部品を剥離する際に、電子部品側に粘着性フィルムの粘着性樹脂層の一部（以下、糊とも呼ぶ。）が残ってしまう場合（以下、糊残りとも呼ぶ。）があることが明らかになった。
　本発明は上記事情に鑑みてなされたものであり、封止工程における電子部品の位置ずれを抑制できるとともに、粘着性フィルムから電子部品を剥離する際の電子部品側の糊残りを抑制することが可能な電子装置の製造方法を提供するものである。
　本発明者らは、上記課題を達成するために鋭意検討を重ねた。その結果、基材層と、上記基材層の第１面側に設けられた粘着性樹脂層（Ａ）と、上記基材層の第２面側に設けられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、を備える粘着性フィルムにおいて、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’という尺度が、電子部品の位置ずれおよび糊残りを抑制するための粘着性フィルムの設計指針として有効であることを見出して、本発明を完成させた。
　本発明によれば、以下に示す電子装置の製造方法が提供される。
［１］
　基材層と、上記基材層の第１面側に設けられた粘着性樹脂層（Ａ）と、上記基材層の第２面側に設けられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、を備え、上記粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’が０．２×１０６Ｐａ以上４．５×１０６Ｐａ以下である粘着性フィルムと、上記粘着性フィルムの上記粘着性樹脂層（Ａ）に貼り付けられた電子部品と、上記粘着性フィルムの上記粘着性樹脂層（Ｂ）に貼り付けられた支持基板と、を備える構造体を準備する工程（１）と、
　封止材により上記電子部品を封止する工程（２）と、
　外部刺激を与えることにより上記粘着性樹脂層（Ｂ）の粘着力を低下させて上記構造体から上記支持基板を剥離する工程（３）と、
　上記電子部品から上記粘着性フィルムを剥離する工程（４）と、
を少なくとも備える電子装置の製造方法。
［２］
　上記［１］に記載の電子装置の製造方法において、
　上記粘着性樹脂層（Ｂ）は１５０℃を超える温度で加熱することにより粘着力が低下する粘着性フィルムであり、工程（３）では１５０℃を超える温度に加熱する電子装置の製造方法。
［３］
　上記［１］または［２］に記載の電子装置の製造方法において、
　上記粘着性樹脂層（Ｂ）が気体発生成分および熱膨張性の微小球から選択される少なくとも一種を含む電子装置の製造方法。
［４］
　上記［１］乃至［３］のいずれか一つに記載の電子装置の製造方法において、
　上記粘着性樹脂層（Ａ）は（メタ）アクリル系粘着性樹脂を含む電子装置の製造方法。
［５］
　上記［１］乃至［４］のいずれか一つに記載の電子装置の製造方法において、
　上記封止材がエポキシ樹脂系封止材である電子装置の製造方法。
　本発明によれば、封止工程における電子部品の位置ずれを抑制できるとともに、粘着性フィルムから電子部品を剥離する際の電子部品側の糊残りを抑制することが可能な電子装置の製造方法を提供することができる。
本発明に係る実施形態の粘着性フィルムの構造の一例を模式的に示した断面図である。 本発明に係る実施形態の電子装置の製造方法の一例を模式的に示した断面図である。 本発明に係る実施形態の電子装置の製造方法の一例を模式的に示した断面図である。
　以下、本発明の実施形態について、図面を用いて説明する。なお、すべての図面において、同様な構成要素には共通の符号を付し、適宜説明を省略する。また、図は概略図であり、実際の寸法比率とは一致していない。また、数値範囲の「Ａ～Ｂ」は特に断りがなければ、Ａ以上Ｂ以下を表す。また、本実施形態において、「（メタ）アクリル」とはアクリル、メタクリルまたはアクリルおよびメタクリルの両方を意味する。
１．粘着性フィルム
　以下、本実施形態に係る粘着性フィルム５０について説明する。
　図１は、本発明に係る実施形態の粘着性フィルム５０の構造の一例を模式的に示した断面図である。
　図１に示すように、本実施形態に係る粘着性フィルム５０は、基材層１０と、基材層１０の第１面１０Ａ側に設けられた粘着性樹脂層（Ａ）と、基材層１０の第２面１０Ｂ側に設けられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、を備え、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’が０．２×１０６Ｐａ以上４．５×１０６Ｐａ以下である。
　上述したように、本発明者らの検討によれば、従来の電子装置の製造方法では、電子部品の位置ずれおよび糊残りの問題が生じる場合があることが明らかになった。
　そこで、本発明者らは、封止工程における電子部品の位置ずれを抑制できるとともに、粘着性フィルムから電子部品を剥離する際の電子部品側の糊残りを抑制することが可能な電子装置の製造方法を実現するために、鋭意検討を重ねた。その結果、基材層１０と、基材層１０の第１面１０Ａ側に設けられた粘着性樹脂層（Ａ）と、基材層１０の第２面１０Ｂ側に設けられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、を備える粘着性フィルムにおいて、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’を上記範囲内に設定することによって、封止工程における電子部品の位置ずれおよび粘着性フィルムから電子部品を剥離する際の電子部品側の糊残りを抑制することができることを初めて見出した。
　すなわち、本実施形態に係る粘着性フィルム５０は、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’を上記範囲とすることで、封止工程における電子部品の位置ずれを抑制できるとともに、粘着性フィルム５０から電子部品を剥離する際の電子部品側の糊残りを抑制することが可能となる。
　本実施形態に係る粘着性フィルム５０において、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’の下限は０．２×１０６Ｐａ以上であるが、粘着性フィルム５０から電子部品を剥離した際の電子部品側の糊残りをより一層抑制することができる点から、０．３×１０６Ｐａ以上が好ましく、０．５×１０６Ｐａ以上がより好ましく、０．６×１０６Ｐａ以上がさらに好ましい。
　また、本実施形態に係る粘着性フィルム５０において、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’の上限は４．５×１０６Ｐａ以下であるが、封止工程における電子部品の位置ずれをより一層抑制することができる点から、４．０×１０６Ｐａ以下が好ましく、３．０×１０６Ｐａ以下がより好ましく、２．５×１０６Ｐａ以下がさらに好ましい。
　粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’は、例えば、粘着性樹脂層（Ａ）を構成する各成分の種類や配合割合を制御することにより上記範囲内に制御することができる。
　本実施形態に係る粘着性フィルム５０全体の厚さは、機械的特性と取扱い性のバランスの観点から、好ましくは１０μｍ以上１０００μｍ以下であり、より好ましくは２０μｍ以上５００μｍ以下である。
　本実施形態に係る電子装置の製造方法は、特に、ファンアウト型ＷＬＰの製造工程に好適に用いることができる。
　次に、本実施形態に係る粘着性フィルム５０を構成する各層について説明する。
＜基材層＞
　基材層１０は、粘着性フィルム５０の取り扱い性や機械的特性、耐熱性等の特性をより良好にすることを目的として設けられる層である。
　基材層１０は特に限定されないが、例えば、樹脂フィルムが挙げられる。
　上記樹脂フィルムを構成する樹脂としては、公知の熱可塑性樹脂を用いることができる。例えば、ポリエチレン、ポリプロピレン、ポリ（４－メチル－１－ペンテン）、ポリ（１－ブテン）等のポリオレフィン；ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート等のポリエステル；ナイロン－６、ナイロン－６６、ポリメタキシレンアジパミド等のポリアミド；ポリアクリレート；ポリメタアクリレート；ポリ塩化ビニル；ポリ塩化ビニリデン；ポリイミド；ポリエーテルイミド；エチレン・酢酸ビニル共重合体；ポリアクリロニトリル；ポリカーボネート；ポリスチレン；アイオノマー；ポリスルホン；ポリエーテルスルホン；ポリフェニレンエーテル等から選択される一種または二種以上を挙げることができる。
　これらの中でも、透明性や機械的強度、価格等のバランスに優れる観点から、ポリプロピレン、ポリエチレンテレフタレート、ポリエチレンナフタレート、ポリアミド、ポリイミドから選択される一種または二種以上が好ましく、ポリエチレンテレフタレート、ポリエチレンナフタレートから選択される少なくとも一種がより好ましい。
　基材層１０は、単層であっても、二種以上の層であってもよい。
　また、基材層１０を形成するために使用する樹脂フィルムの形態としては、延伸フィルムであってもよいし、一軸方向または二軸方向に延伸したフィルムであってもよいが、基材層１０の機械的強度を向上させる観点から、一軸方向または二軸方向に延伸したフィルムであることが好ましい。
　基材層１０の厚さは、良好なフィルム特性を得る観点から、好ましくは１μｍ以上５００μｍ以下、より好ましくは５μｍ以上３００μｍ以下、さらに好ましくは１０μｍ以上２５０μｍ以下である。
　基材層１０は、他の層との接着性を改良するために、表面処理を行ってもよい。具体的には、コロナ処理、プラズマ処理、アンダーコート処理、プライマーコート処理等を行ってもよい。
＜粘着性樹脂層（Ａ）＞
　粘着性樹脂層（Ａ）は、基材層１０の一方の面側に設けられる層であり、電子装置の製造工程において封止材により電子部品を封止する際に、電子部品の表面に接触して電子部品を仮固定するための層である。
　粘着性樹脂層（Ａ）は、粘着性樹脂（Ａ１）を含む。
　粘着性樹脂（Ａ１）としては、例えば、（メタ）アクリル系粘着性樹脂（ａ）、シリコーン系粘着性樹脂、ウレタン系粘着性樹脂、オレフィン系粘着性樹脂、スチレン系粘着性樹脂等が挙げられる。
　これらの中でも粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’の調整が容易である点から、（メタ）アクリル系粘着性樹脂（ａ）が好ましい。
　粘着性樹脂層（Ａ）としては、放射線により粘着力を低下させる放射線架橋型粘着性樹脂層を用いることもできる。放射線架橋型粘着性樹脂層は、放射線の照射により架橋して粘着力が著しく減少するため、電子部品から粘着性フィルム５０を剥離し易くなる。放射線としては、紫外線、電子線、赤外線等が挙げられる。
　放射線架橋型粘着性樹脂層としては、紫外線架橋型粘着性樹脂層が好ましい。
　粘着性樹脂層（Ａ）に使用される（メタ）アクリル系粘着性樹脂（ａ）としては、例えば、（メタ）アクリル酸アルキルエステルモノマー単位（ａ１）および架橋剤と反応し得る官能基を有するモノマー単位（ａ２）を含む共重合体が挙げられる。
　本実施形態において、（メタ）アクリル酸アルキルエステルとは、アクリル酸アルキルエステル、メタクリル酸アルキルエステル、またはこれらの混合物を意味する。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ａ）は、例えば、（メタ）アクリル酸アルキルエステルモノマー（ａ１）および架橋剤と反応し得る官能基を有するモノマー（ａ２）を含むモノマー混合物を共重合することにより得ることができる。
　（メタ）アクリル酸アルキルエステルモノマー単位（ａ１）を形成するモノマー（ａ１）としては、炭素数１～１２程度のアルキル基を有する（メタ）アクリル酸アルキルエステルが挙げられる。好ましくは炭素数１～８のアルキル基を有する（メタ）アクリル酸アルキルエステルである。具体的には、アクリル酸メチル、メタクリル酸メチル、アクリル酸エチル、メタクリル酸エチル、アクリル酸ブチル、メタクリル酸ブチル、アクリル酸－２－エチルヘキシル、メタクリル酸－２－エチルヘキシル等が挙げられる。これらは単独で使用してもよいし、２種以上を使用してもよい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ａ）において、（メタ）アクリル酸アルキルエステルモノマー単位（ａ１）の含有量は、（メタ）アクリル系粘着性樹脂（ａ）中の全モノマー単位の合計を１００質量％としたとき、１０質量％以上９８．９質量％以下であることが好ましく、５０質量％以上９７質量％以下であることがより好ましく、８５質量％以上９５質量％以下であることがさらに好ましい。
　架橋剤と反応し得る官能基を有するモノマー（ａ２）を形成するモノマー（ａ２）としては、アクリル酸、メタクリル酸、イタコン酸、メサコン酸、シトラコン酸、フマル酸、マレイン酸、イタコン酸モノアルキルエステル、メサコン酸モノアルキルエステル、シトラコン酸モノアルキルエステル、フマル酸モノアルキルエステル、マレイン酸モノアルキルエステル、アクリル酸グリシジル、メタクリル酸グリシジル、アクリル酸－２－ヒドロキシエチル、メタクリル酸－２－ヒドロキシエチル、アクリルアミド、メタクリルアミド、ターシャル－ブチルアミノエチルアクリレート、ターシャル－ブチルアミノエチルメタクリレート等が挙げられる。好ましくは、アクリル酸、メタクリル酸、アクリル酸－２－ヒドロキシエチル、メタクリル酸－２－ヒドロキシエチル、アクリルアミド、メタクリルアミド等である。これらは単独で使用してもよいし、２種以上を使用してもよい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ａ）において、モノマー単位（ａ２）の含有量は、（メタ）アクリル系粘着性樹脂（ａ）中の全モノマー単位の合計を１００質量％としたとき、１質量％以上４０質量％以下であることが好ましく、１質量％以上２０質量％以下であることがより好ましく、１質量％以上１０質量％以下であることがさらに好ましい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ａ）は、モノマー単位（ａ１）、モノマー単位（ａ２）以外に、２官能性モノマー単位（ａ３）や界面活性剤としての性質を有する特定のコモノマー（以下、重合性界面活性剤と称する）単位をさらに含んでもよい。
　重合性界面活性剤は、モノマー（ａ１）、モノマー（ａ２）およびモノマー（ａ３）と共重合する性質を有すると共に、乳化重合する場合には乳化剤としての作用を有する。
　２官能性モノマー単位（ａ３）を形成するモノマー（ａ３）としては、メタクリル酸アリル、アクリル酸アリル、ジビニルベンゼン、メタクリル酸ビニル、アクリル酸ビニル、トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、テトラエチレングリコールジ（メタ）アクリレートや、例えば、両末端がジアクリレートまたはジメタクリレートで主鎖の構造がプロピレングリコール型（例えば、日本油脂（株）製、商品名；ＰＤＰ－２００、同ＰＤＰ－４００、同ＡＤＰ－２００、同ＡＤＰ－４００）、テトラメチレングリコール型（例えば、日本油脂（株）製、商品名；ＡＤＴ－２５０、同ＡＤＴ－８５０）およびこれらの混合型（例えば、日本油脂（株）製、商品名：ＡＤＥＴ－１８００、同ＡＤＰＴ－４０００）であるもの等が挙げられる。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ａ）において、モノマー単位（ａ３）の含有量は、（メタ）アクリル系粘着性樹脂（ａ）中の全モノマー単位の合計を１００質量％としたとき、０．１質量％以上３０質量％以下であることが好ましく、０．１質量％以上１５質量％以下であることがより好ましく、０．１質量％以上２０質量％以下であることがさらに好ましく、０．１質量％以上５質量％以下であることが特に好ましい。
　重合性界面活性剤の例としては、例えば、ポリオキシエチレンノニルフェニルエーテルのベンゼン環に重合性の１－プロペニル基を導入したもの（第一工業製薬（株）製；商品名：アクアロンＲＮ－１０、同ＲＮ－２０、同ＲＮ－３０、同ＲＮ－５０等）、ポリオキシエチレンノニルフェニルエーテルの硫酸エステルのアンモニウム塩のベンゼン環に重合性の１－プロペニル基を導入したもの（第一工業製薬（株）製；商品名：アクアロンＨＳ－１０、同ＨＳ－２０、同ＨＳ－１０２５等）、および分子内に重合性二重結合を持つ、スルホコハク酸ジエステル系（花王（株）製；商品名：ラテムルＳ－１２０Ａ、同Ｓ－１８０Ａ等）等が挙げられる。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ａ）において、重合性界面活性剤の含有量は、（メタ）アクリル系粘着性樹脂（ａ）中の全モノマー単位の合計を１００質量％としたとき、０．１質量％以上３０質量％以下であることが好ましく、０．１質量％以上１５質量％以下であることがより好ましく、０．１質量％以上２０質量％以下であることがさらに好ましく、０．１質量％以上５質量％以下であることが特に好ましい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ａ）は、さらに必要に応じて、酢酸ビニル、アクリロニトリル、スチレン等の重合性２重結合を有するモノマーにより形成されたモノマー単位をさらに含有してもよい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ａ）の重合反応機構としては、ラジカル重合、アニオン重合、カチオン重合等が挙げられる。（メタ）アクリル系粘着性樹脂（ａ）の製造コスト、モノマーの官能基の影響および電子部品表面へのイオンの影響等を考慮すればラジカル重合によって重合することが好ましい。
　ラジカル重合反応によって重合する際、ラジカル重合開始剤として、ベンゾイルパーオキサイド、ジ－ｔ－ブチルパーオキサイド、ジクミルパーオキサイド、３，３，５－トリメチルヘキサノイルパーオキサイド、ジ－２－エチルヘキシルパーオキシジカーボネート、メチルエチルケトンパーオキサイド、ｔ－ブチルパーオキシフタレート、ｔ－ブチルパーオキシベンゾエート、ジ－ｔ－ブチルパーオキシアセテート、ｔ－ブチルパーオキシイソブチレート、ｔ－ブチルパーオキシ－２－ヘキサノエート、ｔ－ブチルパーオキシ－２－エチルヘキサノエート、ｔ－ブチルパーオキシ－３，５，５－トリメチルヘキサノエート、アセチルパーオキサイド、イソブチリルパーオキサイド、オクタノイルパーオキサイド、ｔ－ブチルパーオキサイド、ジ－ｔ－アミルパーオキサイド等の有機過酸化物；過硫酸アンモニウム、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物；２，２'－アゾビスイソブチロニトリル、２，２'－アゾビス－２－メチルブチロニトリル、４，４'－アゾビス－４－シアノバレリックアシッド等のアゾ化合物が挙げられる。
　乳化重合法により重合する場合には、これらのラジカル重合開始剤の中で、水溶性の過硫酸アンモニウム、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物、同じく水溶性の４，４'－アゾビス－４－シアノバレリックアシッド等の分子内にカルボキシル基を持ったアゾ化合物が好ましい。電子部品表面へのイオンの影響を考慮すれば、過硫酸アンモニウム、４，４'－アゾビス－４－シアノバレリックアシッド等の分子内にカルボキシル基を有するアゾ化合物がさらに好ましく、４，４'－アゾビス－４－シアノバレリックアシッド等の分子内にカルボキシル基を有するアゾ化合物が特に好ましい。
　本実施形態に係る粘着性樹脂層（Ａ）は、粘着性樹脂（Ａ１）に加えて、架橋性の官能基を１分子中に２個以上有する架橋剤（Ａ２）をさらに含むことが好ましい。
　架橋性の官能基を１分子中に２個以上有する架橋剤（Ａ２）は、粘着性樹脂（Ａ１）が有する官能基と反応させ、貯蔵弾性率、粘着力および凝集力を調整するために用いる。
　このような架橋剤（Ａ２）としては、ソルビトールポリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ペンタエリスリトールポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル、グリセロールポリグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、レソルシンジグリシジルエーテル等のエポキシ系化合物；テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、トリメチロールプロパンのトルエンジイソシアネート３付加物、ポリイソシアネート、ジフェニルメタンジイソシアネート、トリレンジイソシアネート等のイソシアネート系化合物；トリメチロールプロパン－トリ－β－アジリジニルプロピオネート、テトラメチロールメタン－トリ－β－アジリジニルプロピオネート、Ｎ，Ｎ'－ジフェニルメタン－４，４'－ビス（１－アジリジンカルボキシアミド）、Ｎ，Ｎ'－ヘキサメチレン－１，６－ビス（１－アジリジンカルボキシアミド）、Ｎ，Ｎ'－トルエン－２，４－ビス（１－アジリジンカルボキシアミド）、トリメチロールプロパン－トリ－β－（２－メチルアジリジン）プロピオネート等のアジリジン系化合物；Ｎ，Ｎ，Ｎ'，Ｎ'－テトラグリシジル－ｍ－キシレンジアミン、１，３－ビス（Ｎ，Ｎ'－ジグリシジルアミノメチル）シクロヘキサン等の４官能性エポキシ系化合物；ヘキサメトキシメチロールメラミン等のメラミン系化合物等が挙げられる。これらは単独で使用してもよいし、２種以上を併用してもよい。
　これらの中でも、エポキシ系化合物、イソシアネート系化合物およびアジリジン系化合物から選択される一種または二種以上を含むことが好ましい。
　粘着性樹脂層（Ａ）中の架橋剤（Ａ２）の含有量は、１２５℃における貯蔵弾性率Ｅ’を所望の値に調整する観点から、粘着性樹脂（Ａ１）１００質量部に対し、１．０質量部以上１８．０質量部以下であることが好ましく、２．０質量部以上１６．０質量部以下であることがより好ましい。
　粘着性樹脂層（Ａ）は、その他の成分として、可塑剤、粘着付与樹脂等の添加剤を含んでもよい。粘着性樹脂層（Ａ）が放射線架橋型粘着性樹脂層の場合は放射線架橋のための各種添加剤を含んでもよい。粘着性樹脂層（Ａ）中の粘着性樹脂（Ａ１）および架橋剤（Ａ２）の含有量の合計は、粘着性樹脂層（Ａ）の全体を１００質量％としたとき、好ましくは５０質量％以上、より好ましくは７０質量％以上、さらに好ましくは９０質量％以上、特に好ましくは９５質量％以上である。これにより、電子部品から粘着性フィルムを剥離する際の電子部品側の糊残りをより一層抑制することができる。
　粘着性樹脂層（Ａ）の厚さは特に制限されないが、例えば、１μｍ以上１００μｍ以下であることが好ましく、３μｍ以上５０μｍ以下であることがより好ましい。
　粘着性樹脂層（Ａ）は、例えば、基材層１０上に粘着剤を塗布することにより形成することができる。この際の塗布液は、溶剤に溶解した塗布液や、水系エマルジョン塗布液等である。
　中でも水系エマルジョン塗布液が好ましい。水系エマルジョン塗布液としては、例えば、（メタ）アクリル系粘着性樹脂（ａ）、シリコーン系粘着性樹脂、ウレタン系粘着性樹脂、オレフィン系粘着性樹脂、スチレン系粘着性樹脂等を水に分散させた塗布液が挙げられる。
　有機溶剤に溶解した粘着剤塗布液を用いてもよい。有機溶剤は特に限定されず、溶解性や乾燥時間を鑑みて公知の中から適宜選択すればよい。有機溶剤としては、酢酸エチル、酢酸メチル等のエステル系；アセトン、ＭＥＫ等のケトン系；ベンゼン、トルエン、エチルベンゼン等の芳香族系；ヘプタン、ヘキサン、シクロヘキサン等の直鎖ないし環状脂肪族系；イソプロパノール、ブタノール等のアルコール系を例示することができる。有機溶剤として酢酸エチル、トルエンが好ましい。これらの溶剤は、１種単独で用いてもよいし、２種以上を混合して用いてもよい。
　粘着剤塗布液を塗布する方法としては、従来公知の塗布方法、例えば、ロールコーター法、リバースロールコーター法、グラビアロール法、バーコート法、コンマコーター法、ダイコーター法等が採用できる。塗布された粘着剤の乾燥条件には特に制限はないが、一般的には、８０～２００℃の温度範囲において、１０秒～１０分間乾燥することが好ましい。さらに好ましくは、８０～１７０℃において、１５秒～５分間乾燥する。架橋剤と粘着剤との架橋反応を十分に促進させるために、粘着剤塗布液の乾燥が終了した後、４０～８０℃において５～３００時間程度加熱してもよい。
　また、基材層１０と粘着性樹脂層（Ａ）とは共押出成形によって形成してもよいし、フィルム状の基材層１０とフィルム状の粘着性樹脂層（Ａ）とをラミネート（積層）して形成してもよい。
＜粘着性樹脂層（Ｂ）＞
　本実施形態に係る粘着性フィルム５０は、基材層１０の第１面１０Ａとは反対側の第２面１０Ｂ側に外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）を備える。
　これにより、外部刺激を与えることで支持基板８０から粘着性フィルム５０を容易に剥離することができる。
　ここで、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）としては、例えば、加熱により粘着力が低下する加熱剥離型の粘着性樹脂層や、放射線により粘着力が低下する放射線剥離型の粘着性樹脂層等が挙げられる。これらの中でも加熱により粘着力が低下する加熱剥離型の粘着性樹脂層が好ましい。
　加熱剥離型の粘着性樹脂層としては、例えば、気体発生成分を含む加熱膨張型粘着剤、膨張して粘着力を低減できる熱膨張性の微小球を含む加熱膨張型粘着剤、熱により接着剤成分が架橋反応することで接着力が低下する粘着剤等により構成された粘着性樹脂層が挙げられる。
　本実施形態において、粘着性樹脂層（Ｂ）に使用される加熱膨張型粘着剤は、例えば１５０℃を超える温度で加熱することで接着力が低下または喪失する粘着剤である。例えば、１５０℃以下では剥離せず、１５０℃を超える温度で剥離する材料を選択することができ、電子装置の製造工程中に粘着性フィルム５０が支持基板８０から剥離しない程度の接着力を有していることが好ましい。
　ここで、１５０℃を超える温度で加熱することで接着力が低下または喪失することは、例えば、粘着性樹脂層（Ｂ）側をステンレス板に貼り付け、１4０℃で１時間の加熱処理をおこない、次いで、１５０℃を超える温度で２分間加熱した後に測定される、ステンレス板からの剥離強度により評価することができる。１５０℃を超える温度で加熱する際の具体的な加熱温度は、気体が発生する温度や熱膨張性の微小球が熱膨張する温度よりも高い温度に設定され、発生する気体や熱膨張性の微小球の種類によって適宜設定される。本実施形態において、接着力が喪失するとは、例えば、２３℃、引張速度３００ｍｍ／分の条件で測定される１８０°剥離強度が０．５Ｎ／２５ｍｍ未満になる場合をいう。
　加熱膨張型粘着剤に使用される気体発生成分としては、例えば、アゾ化合物、アジド化合物、メルドラム酸誘導体等を用いることができる。また、炭酸アンモニウム、炭酸水素アンモニウム、炭酸水素ナトリウム、亜硝酸アンモニウム、水酸化ホウ素ナトリウム、各種アジド類等の無機系発泡剤や、水；トリクロロモノフルオロメタン、ジクロロモノフルオロメタン等の塩フッ化アルカン系化合物；アゾビスイソブチロニトリル、アゾジカルボンアミド、バリウムアゾジカルボキシレート等のアゾ系化合物；パラトルエンスルホニルヒドラジド、ジフェニルスルホン－３，３’－ジスルホニルヒドラジド、４，４’－オキシビス（ベンゼンスルホニルヒドラジド）、アリルビス（スルホニルヒドラジド）等のヒドラジン系化合物；ｐ－トルイレンスルホニルセミカルバジド、４，４’－オキシビス（ベンゼンスルホニルセミカルバジド）等のセミカルバジド系化合物；５－モルホリル－１，２，３，４－チアトリアゾール等のトリアゾール系化合物；Ｎ，Ｎ’－ジニトロソペンタメチレンテトラミン、Ｎ，Ｎ´－ジメチル－Ｎ，Ｎ’－ジニトロソテレフタルアミド等のＮ－ニトロソ系化合物等の有機系発泡剤等も用いることができる。気体発生成分は粘着性樹脂（Ｂ１）に添加されていてもよく、粘着性樹脂（Ｂ１）に直接結合されていてもよい。
　加熱膨張型粘着剤に使用される熱膨張性の微小球としては、例えば、マイクロカプセル化されている発泡剤を用いることができる。このような熱膨張性の微小球としては、例えば、イソブタン、プロパン、ペンタン等の加熱により容易にガス化して膨張する物質を、弾性を有する殻内に内包させた微小球等が挙げられる。上記殻を構成する材料として、例えば、塩化ビニリデン－アクリロニトリル共重合体、ポリビニルアルコール、ポリビニルブチラール、ポリメチルメタクリレート、ポリアクリロニトリル、ポリ塩化ビニリデン、ポリスルホン等が挙げられる。熱膨張性の微小球は、例えば、コアセルベーション法や、界面重合法等により製造することができる。
　熱膨張性の微小球は粘着性樹脂に添加することができる。
　気体発生成分および熱膨張性の微小球から選択される少なくとも一種の含有量は、加熱剥離型の粘着性樹脂層（Ｂ）の膨張倍率や接着力の低下性等に応じて適宜設定することができ、特に限定されないが、例えば、加熱剥離型の粘着性樹脂層（Ｂ）中の粘着性樹脂（Ｂ１）１００質量部に対して、例えば１質量部以上１５０質量部以下、好ましくは１０質量部以上１３０質量部以下、さらに好ましくは１２質量部以上１００質量部以下である。
　気体が発生する温度や熱膨張性の微小球が熱膨張する温度が、１５０℃を超える温度になるように設計することが好ましい。
　加熱膨張型粘着剤を構成する粘着性樹脂（Ｂ１）としては、例えば、（メタ）アクリル系樹脂（ｂ）、ウレタン系樹脂、シリコーン系樹脂、ポリオレフィン系樹脂、ポリエステル系樹脂、ポリアミド系樹脂、フッ素系樹脂、スチレン－ジエンブロック共重合体系樹脂等を挙げることができる。これらの中でも（メタ）アクリル系樹脂（ｂ）が好ましい。
　粘着性樹脂層（Ｂ）に使用される（メタ）アクリル系粘着性樹脂（ｂ）としては、例えば、（メタ）アクリル酸アルキルエステルモノマー単位（ｂ１）および架橋剤と反応し得る官能基を有するモノマー単位（ｂ２）を含む共重合体が挙げられる。
　本実施形態において、（メタ）アクリル酸アルキルエステルとは、アクリル酸アルキルエステル、メタクリル酸アルキルエステル、またはこれらの混合物を意味する。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ｂ）は、例えば、（メタ）アクリル酸アルキルエステルモノマー（ｂ１）および架橋剤と反応し得る官能基を有するモノマー（ｂ２）を含むモノマー混合物を共重合することにより得ることができる。
　（メタ）アクリル酸アルキルエステルモノマー単位（ｂ１）を形成するモノマー（ｂ１）としては、炭素数１～１２程度のアルキル基を有する（メタ）アクリル酸アルキルエステルが挙げられる。好ましくは炭素数１～８のアルキル基を有する（メタ）アクリル酸アルキルエステルである。具体的には、アクリル酸メチル、メタクリル酸メチル、アクリル酸エチル、メタクリル酸エチル、アクリル酸ブチル、メタクリル酸ブチル、アクリル酸－２－エチルヘキシル、メタクリル酸－２－エチルヘキシル等が挙げられる。これらは単独で使用してもよいし、２種以上を使用してもよい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ｂ）において、（メタ）アクリル酸アルキルエステルモノマー単位（ｂ１）の含有量は、（メタ）アクリル系粘着性樹脂（ｂ）中の全モノマー単位の合計を１００質量％としたとき、１０質量％以上９８．９質量％以下であることが好ましく、５０質量％以上９７質量％以下であることがより好ましく、８５質量％以上９５質量％以下であることがさらに好ましい。
　架橋剤と反応し得る官能基を有するモノマー（ｂ２）を形成するモノマー（ｂ２）としては、アクリル酸、メタクリル酸、イタコン酸、メサコン酸、シトラコン酸、フマル酸、マレイン酸、イタコン酸モノアルキルエステル、メサコン酸モノアルキルエステル、シトラコン酸モノアルキルエステル、フマル酸モノアルキルエステル、マレイン酸モノアルキルエステル、アクリル酸グリシジル、メタクリル酸グリシジル、アクリル酸－２－ヒドロキシエチル、メタクリル酸－２－ヒドロキシエチル、アクリルアミド、メタクリルアミド、ターシャル－ブチルアミノエチルアクリレート、ターシャル－ブチルアミノエチルメタクリレート等が挙げられる。好ましくは、アクリル酸、メタクリル酸、アクリル酸－２－ヒドロキシエチル、メタクリル酸－２－ヒドロキシエチル、アクリルアミド、メタクリルアミド等である。これらは単独で使用してもよいし、２種以上を使用してもよい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ｂ）において、モノマー単位（ｂ２）の含有量は、（メタ）アクリル系粘着性樹脂（ｂ）中の全モノマー単位の合計を１００質量％としたとき、１質量％以上４０質量％以下であることが好ましく、１質量％以上２０質量％以下であることがより好ましく、１質量％以上１０質量％以下であることがさらに好ましい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ｂ）は、モノマー単位（ｂ１）、モノマー単位（ｂ２）以外に、２官能性モノマー単位（ｂ３）や界面活性剤としての性質を有する特定のコモノマー（以下、重合性界面活性剤と称する）単位をさらに含んでもよい。
　重合性界面活性剤は、モノマー（ｂ１）、モノマー（ｂ２）およびモノマー（ｂ３）と共重合する性質を有すると共に、乳化重合する場合には乳化剤としての作用を有する。
　２官能性モノマー単位（ｂ３）を形成するモノマー（ｂ３）としては、メタクリル酸アリル、アクリル酸アリル、ジビニルベンゼン、メタクリル酸ビニル、アクリル酸ビニル、トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、テトラエチレングリコールジ（メタ）アクリレートや、例えば、両末端がジアクリレートまたはジメタクリレートで主鎖の構造がプロピレングリコール型（例えば、日本油脂（株）製；商品名：ＰＤＰ－２００、同ＰＤＰ－４００、同ＡＤＰ－２００、同ＡＤＰ－４００）、テトラメチレングリコール型（例えば、日本油脂（株）製；商品名：ＡＤＴ－２５０、同ＡＤＴ－８５０）およびこれらの混合型（例えば、日本油脂（株）製；商品名：ＡＤＥＴ－１８００、同ＡＤＰＴ－４０００）であるもの等が挙げられる。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ｂ）において、モノマー単位（ｂ３）の含有量は、（メタ）アクリル系粘着性樹脂（ｂ）中の全モノマー単位の合計を１００質量％としたとき、０．１質量％以上３０質量％以下であることが好ましく、０．１質量％以上１５質量％以下であることがより好ましく、０．１質量％以上２０質量％以下であることがさらに好ましく、０．１質量％以上５質量％以下であることが特に好ましい。
　重合性界面活性剤の例としては、例えば、ポリオキシエチレンノニルフェニルエーテルのベンゼン環に重合性の１－プロペニル基を導入したもの（第一工業製薬（株）製；商品名：アクアロンＲＮ－１０、同ＲＮ－２０、同ＲＮ－３０、同ＲＮ－５０等）、ポリオキシエチレンノニルフェニルエーテルの硫酸エステルのアンモニウム塩のベンゼン環に重合性の１－プロペニル基を導入したもの（第一工業製薬（株）製；商品名：アクアロンＨＳ－１０、同ＨＳ－２０、同ＨＳ－１０２５等）、および分子内に重合性二重結合を持つ、スルホコハク酸ジエステル系（花王（株）製；商品名：ラテムルＳ－１２０Ａ、同Ｓ－１８０Ａ等）等が挙げられる。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ｂ）において、重合性界面活性剤の含有量は、（メタ）アクリル系粘着性樹脂（ｂ）中の全モノマー単位の合計を１００質量％としたとき、０．１質量％以上３０質量％以下であることが好ましく、０．１質量％以上１５質量％以下であることがより好ましく、０．１質量％以上２０質量％以下であることがさらに好ましく、０．１質量％以上５質量％以下であることが特に好ましい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ｂ）は、さらに必要に応じて、酢酸ビニル、アクリロニトリル、スチレン等の重合性２重結合を有するモノマーにより形成されたモノマー単位をさらに含有してもよい。
　本実施形態に係る（メタ）アクリル系粘着性樹脂（ｂ）の重合反応機構としては、ラジカル重合、アニオン重合、カチオン重合等が挙げられる。（メタ）アクリル系粘着性樹脂（ｂ）の製造コスト、モノマーの官能基の影響および電子部品表面へのイオンの影響等を考慮すればラジカル重合によって重合することが好ましい。
　ラジカル重合反応によって重合する際、ラジカル重合開始剤として、ベンゾイルパーオキサイド、ジ－ｔ－ブチルパーオキサイド、ジクミルパーオキサイド、３，３，５－トリメチルヘキサノイルパーオキサイド、ジ－２－エチルヘキシルパーオキシジカーボネート、メチルエチルケトンパーオキサイド、ｔ－ブチルパーオキシフタレート、ｔ－ブチルパーオキシベンゾエート、ジ－ｔ－ブチルパーオキシアセテート、ｔ－ブチルパーオキシイソブチレート、ｔ－ブチルパーオキシ－２－ヘキサノエート、ｔ－ブチルパーオキシ－２－エチルヘキサノエート、ｔ－ブチルパーオキシ－３，５，５－トリメチルヘキサノエート、アセチルパーオキサイド、イソブチリルパーオキサイド、オクタノイルパーオキサイド、ｔ－ブチルパーオキサイド、ジ－ｔ－アミルパーオキサイド等の有機過酸化物；過硫酸アンモニウム、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物；２，２'－アゾビスイソブチロニトリル、２，２'－アゾビス－２－メチルブチロニトリル、４，４'－アゾビス－４－シアノバレリックアシッド等のアゾ化合物が挙げられる。
　乳化重合法により重合する場合には、これらのラジカル重合開始剤の中で、水溶性の過硫酸アンモニウム、過硫酸カリウム、過硫酸ナトリウム等の無機過酸化物、同じく水溶性の４，４'－アゾビス－４－シアノバレリックアシッド等の分子内にカルボキシル基を持ったアゾ化合物が好ましい。電子部品表面へのイオンの影響を考慮すれば、過硫酸アンモニウム、４，４'－アゾビス－４－シアノバレリックアシッド等の分子内にカルボキシル基を有するアゾ化合物がさらに好ましく、４，４'－アゾビス－４－シアノバレリックアシッド等の分子内にカルボキシル基を有するアゾ化合物が特に好ましい。
　本実施形態に係る粘着性樹脂層（Ｂ）は、粘着性樹脂（Ｂ１）に加えて、架橋性の官能基を１分子中に２個以上有する架橋剤（Ｂ２）をさらに含むことが好ましい。
　架橋性の官能基を１分子中に２個以上有する架橋剤（Ｂ２）は、粘着性樹脂（Ｂ１）が有する官能基と反応させ、粘着力および凝集力を調整するために用いる。
　このような架橋剤（Ｂ２）としては、ソルビトールポリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ペンタエリスリトールポリグリシジルエーテル、ジグリセロールポリグリシジルエーテル、グリセロールポリグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、レソルシンジグリシジルエーテル等のエポキシ系化合物；テトラメチレンジイソシアネート、ヘキサメチレンジイソシアネート、トリメチロールプロパンのトルエンジイソシアネート３付加物、ポリイソシアネート、ジフェニルメタンジイソシアネート、トリレンジイソシアネート等のイソシアネート系化合物；トリメチロールプロパン－トリ－β－アジリジニルプロピオネート、テトラメチロールメタン－トリ－β－アジリジニルプロピオネート、Ｎ，Ｎ'－ジフェニルメタン－４，４'－ビス（１－アジリジンカルボキシアミド）、Ｎ，Ｎ'－ヘキサメチレン－１，６－ビス（１－アジリジンカルボキシアミド）、Ｎ，Ｎ'－トルエン－２，４－ビス（１－アジリジンカルボキシアミド）、トリメチロールプロパン－トリ－β－（２－メチルアジリジン）プロピオネート等のアジリジン系化合物；Ｎ，Ｎ，Ｎ'，Ｎ'－テトラグリシジル－ｍ－キシレンジアミン、１，３－ビス（Ｎ，Ｎ'－ジグリシジルアミノメチル）シクロヘキサン等の４官能性エポキシ系化合物；ヘキサメトキシメチロールメラミン等のメラミン系化合物等が挙げられる。これらは単独で使用してもよいし、２種以上を併用してもよい。
　これらの中でも、エポキシ系化合物、イソシアネート系化合物およびアジリジン系化合物から選択される一種または二種以上を含むことが好ましい。
　架橋剤（Ｂ２）の含有量は、通常、架橋剤（Ｂ２）中の官能基数が粘着性樹脂（Ｂ１）中の官能基数よりも多くならない程度の範囲が好ましい。しかし、架橋反応で新たに官能基が生じる場合や、架橋反応が遅い場合等、必要に応じて過剰に含有してもよい。
　粘着性樹脂層（Ｂ）中の架橋剤（Ｂ２）の含有量は、粘着性樹脂（Ｂ１）１００質量部に対し、０．１質量部以上１０質量部以下であることが好ましく、０．５質量部以上５質量部以下であることがより好ましい。
　本実施形態に係る粘着性樹脂層（Ｂ）は、支持基板への密着性を向上させる観点から、粘着性樹脂（Ｂ１）に加えて、粘着付与樹脂を含むことが好ましい。粘着性樹脂層（Ｂ）に粘着付与樹脂を含有させることが、常温付近における支持基板との密着性の調整が容易となるために好ましい。粘着付与樹脂としては、その軟化点が１００℃以上であるものが好ましい。粘着付与樹脂の具体例としては、エステル化等の処理をしたロジン系誘導体等のロジン系樹脂；α－ピネン系、β－ピネン系、ジペンテン系、テルペンフェノール系等のテルペン系樹脂；ガム系、ウッド系、トール油系等の天然系ロジン；これらの天然系ロジンに水素化、不均化、重合、マレイン化、石油樹脂；クマロン－インデン樹脂等を挙げることができる。
　これらのなかでも、軟化点が１００～１６０℃の範囲内であるものがより好ましく、１２０～１５０℃の範囲であるものが特に好ましい。軟化点が上記範囲内である粘着付与樹脂を用いると、支持基板への汚染、糊残りが少ないばかりでなく、作業環境下における支持基板との密着性をさらに向上させることが可能となる。さらに、粘着付与樹脂として重合ロジンエステル系の粘着付与樹脂を用いると、支持基板への汚染、糊残りが少ないばかりか、８０～１３０℃の環境下での支持基板との粘着性が向上するとともに、熱膨張性の微小球を含む加熱膨張型粘着剤の場合には、熱膨張性微小球の膨張後は、支持基板からさらに容易に剥離可能となる。
　粘着付与樹脂の配合割合は、粘着性樹脂層（Ｂ）の弾性率を所望とする所定の数値範囲内に調整することができるように適宜選択すればよく、特に制限はない。ただし、粘着性樹脂層（Ｂ）の弾性率と初期剥離力の面から、粘着性樹脂（Ｂ１）１００質量部に対して、１～１００質量部とすることが好ましい。粘着付与樹脂の配合割合が、粘着性樹脂（Ｂ１）１００質量部に対して、上記下限値以上であると、作業時の支持基板との密着性が良好になる傾向にある。一方、上記上限値以下であると、常温における支持基板との貼り付け性が良好になる傾向にある。支持基板との密着性、及び常温における貼り付け性の面から、粘着付与樹脂の配合割合を、粘着性樹脂（Ｂ１）１００質量部に対して、２～５０質量部とすることがさらに好ましい。また、粘着付与樹脂の酸価は、３０以下であることが好ましい。粘着付与樹脂の酸価が上記上限値以下であると剥離時に支持基板に糊残りが生じ難くなる傾向にある。
　粘着性樹脂層（Ｂ）は、その他の成分として、可塑剤等の添加剤を含んでもよい。粘着性樹脂層（Ｂ）中の粘着性樹脂（Ｂ１）、架橋剤（Ｂ２）および粘着付与樹脂の含有量の合計は粘着性樹脂層（Ｂ）の全体を１００質量％としたとき、好ましくは５０質量％以上、より好ましくは７０質量％以上、さらに好ましくは９０質量％以上、特に好ましくは９５質量％以上である。さらに粘着性樹脂層（Ｂ）が加熱膨張型粘着剤により構成されている場合は、粘着性樹脂層（Ｂ）中の粘着性樹脂（Ｂ１）、架橋剤（Ｂ２）、粘着付与樹脂、気体発生成分および熱膨張性の微小球の含有量の合計は、粘着性樹脂層（Ｂ）の全体を１００質量％としたとき、好ましくは５０質量％以上、より好ましくは７０質量％以上、さらに好ましくは９０質量％以上、特に好ましくは９５質量％以上である。
　粘着性樹脂層（Ｂ）の厚さは特に制限されないが、例えば、５μｍ以上３００μｍ以下であることが好ましく、２０μｍ以上１５０μｍ以下であることがより好ましい。
　粘着性樹脂層（Ｂ）は、例えば、基材層１０上に粘着剤塗布液を塗布する方法や、セパレータ上に形成した粘着性樹脂層（Ｂ）を基材１０上に移着する方法等により形成することができる。
　粘着剤塗布液を塗布する方法としては、従来公知の塗布方法、例えば、ロールコーター法、リバースロールコーター法、グラビアロール法、バーコート法、コンマコーター法、ダイコーター法等が採用できる。塗布された粘着剤の乾燥条件には特に制限はないが、一般的には、８０～２００℃の温度範囲において、１０秒～１０分間乾燥することが好ましい。さらに好ましくは、８０～１７０℃において、１５秒～５分間乾燥する。架橋剤と粘着剤との架橋反応を十分に促進させるために、粘着剤塗布液の乾燥が終了した後、４０～８０℃において５～３００時間程度加熱してもよい。
　また、基材層１０と粘着性樹脂層（Ｂ）とは共押出成形によって形成してもよいし、フィルム状の基材層１０とフィルム状の粘着性樹脂層（Ｂ）とをラミネート（積層）して形成してもよい。
＜その他の層＞
　本実施形態に係る粘着性フィルム５０は、本実施形態の効果を損なわない範囲で、基材層１０と粘着性樹脂層（Ａ）との間あるいは基材層１０と粘着性樹脂層（Ｂ）との間に、例えば凹凸吸収層、衝撃吸収層、易接着層等がさらに設けられていてもよい。
　凹凸吸収層は、ＡＳＴＭ　Ｄ－２２４０のＤ型ショアーによるショアーＤ型硬度が、例えば５０以下、好ましくは４０以下の天然ゴムや合成ゴム、又はゴム弾性を有する合成樹脂により形成することが好ましい。凹凸吸収層の厚さは、例えば５００μｍ以下、好ましくは５～３００μｍ、より好ましくは１０～１５０μｍである。
　合成ゴム又は合成樹脂としては、例えばニトリル系やジエン系やアクリル系等の合成ゴム、ポリオレフィン系やポリエステル系等の熱可塑性エラストマー、エチレン・酢酸ビニル共重合体やポリウレタン、ポリブタジエンや軟質ポリ塩化ビニル等のゴム弾性を有する合成樹脂が挙げられる。なお、ポリ塩化ビニルのように本質的には硬質系のポリマーであっても可塑剤や柔軟剤等の配合剤との組合せでゴム弾性をもたせたものも本実施形態においては用いることができる。また上記の粘着性樹脂層（Ａ）や粘着性樹脂層（Ｂ）で例示した粘着性樹脂等も凹凸吸収層の形成に好ましく用いることができる。
２．電子装置の製造方法
　次に、本実施形態に係る電子装置の製造方法について説明する。図２および３は、本発明に係る実施形態の電子装置の製造方法の一例を模式的に示した断面図である。
　本実施形態に係る電子装置の製造方法は、以下の４つの工程を少なくとも備えている。
　（１）粘着性フィルム５０と、粘着性フィルム５０の粘着性樹脂層（Ａ）に貼り付けられた電子部品７０と、粘着性フィルム５０の粘着性樹脂層（Ｂ）に貼り付けられた支持基板８０と、を備える構造体１００を準備する工程
　（２）封止材６０により電子部品７０を封止する工程
　（３）外部刺激を与えることにより粘着性樹脂層（Ｂ）の粘着力を低下させて構造体１００から支持基板８０を剥離する工程
　（４）電子部品７０から粘着性フィルム５０を剥離する工程
　そして、本実施形態に係る電子装置の製造方法では、電子部品７０を仮固定する粘着性フィルムとして、前述した本実施形態に係る粘着性フィルム５０を使用する。
　以下、本実施形態に係る電子装置の製造方法の各工程について説明する。
（工程（１））
　はじめに、粘着性フィルム５０と、粘着性フィルム５０の粘着性樹脂層（Ａ）に貼り付けられた電子部品７０と、粘着性フィルム５０の粘着性樹脂層（Ｂ）に貼り付けられた支持基板８０と、を備える構造体１００を準備する。
　このような構造体１００は、例えば、以下の手順で作製することができる。
　まず、支持基板８０上に、粘着性フィルム５０を、粘着性樹脂層（Ｂ）が支持基板８０側となるように貼着する。粘着性樹脂層（Ｂ）上にはセパレータと称する保護フィルムが貼付けられていてもよく、当該保護フィルムを剥がし、粘着性樹脂層（Ｂ）の露出面を支持基板８０表面に貼着することができる。
　支持基板８０としては、例えば、石英基板、ガラス基板、ＳＵＳ基板等を使用することができる。
　次いで、支持基板８０上に貼着された粘着性フィルム５０の粘着性樹脂層（Ａ）上に電子部品７０を配置することにより構造体１００を得ることができる。粘着性樹脂層（Ａ）上にもセパレータと称する保護フィルムが貼付されていてもよく、この場合は当該保護フィルムを剥がしてから電子部品を配置する。
　電子部品７０としては、例えば、ＩＣ、ＬＳＩ、ディスクリート、発光ダイオード、受光素子等の半導体チップや半導体パネル、半導体パッケージ等を挙げることができる。
（工程（２））
　次いで、封止材６０により電子部品７０を封止する。
　封止材６０により電子部品７０を覆い、例えば粘着層樹脂層（Ｂ）が加熱剥離型の粘着性樹脂層の場合は、支持基板８０から剥離しない温度、例えば１５０℃以下の温度で封止材６０を硬化させて、電子部品７０を封止する。
　また、封止材６０の形態としては特に限定されないが、例えば、顆粒状、シート状または液状である。
　封止材６０としては特に限定されないが、例えば、エポキシ樹脂を用いたエポキシ樹脂系封止材を用いることができる。
　特に、粘着性フィルム５０への封止材６０の親和性がより良好になり、電子部品７０をより一層ムラなく封止することが可能となる点から、液状のエポキシ樹脂系封止材が好ましい。
　このようなエポキシ樹脂系封止材としては、例えば、ナガセケムテックス社製のＴ６９３／Ｒ４０００シリーズやＴ６９３／Ｒ１０００シリーズ、Ｔ６９３／Ｒ５０００シリーズ等を用いることができる。
　封止方法としては、例えば、トランスファー成形、射出成形、圧縮成形、注型成形等が挙げられる。封止材６０で電子部品７０を封止後、例えば１５０℃以下の温度で加熱することによって封止材６０を硬化させ、電子部品７０が封止された構造体１００が得られる。
（工程（３））
　次いで、外部刺激を与えることにより粘着性樹脂層（Ｂ）の粘着力を低下させて構造体１００から支持基板８０を剥離する。
　支持基板８０は、電子部品７０を封止した後、接着力が低下または喪失する温度、例えば１５０℃を超える温度に加熱して、粘着性樹脂層（Ｂ）の接着力を低下させることにより、粘着性フィルム５０から容易に除去することができる。
（工程（４））
　次いで、電子部品７０から粘着性フィルム５０を除去し、電子装置２００を得る。
　電子部品７０から粘着性フィルム５０を除去する方法としては、例えば、機械的に剥離する方法や、粘着性フィルム５０表面の粘着力を低下させてから剥離する方法等が挙げられる。
（工程（５））
　本実施形態に係る電子装置の製造方法において、図３に示すように、得られた電子装置２００の露出面に、配線層３１０およびバンプ３２０を形成し、電子装置３００を得る工程（５）をさらに備えてもよい。
　配線層３１０は、最外面に形成された外部接続端子であるパッド（不図示）と、露出した電子部品７０と該パッドとを電気的に接続する配線（不図示）と、を備える。配線層３１０は、従来公知の方法によって形成することができ、多層構造であってもよい。
　そして、配線層３１０のパッド上にバンプ３２０を形成し、電子装置３００を得ることができる。バンプ３２０としては、はんだバンプや金バンプ等を挙げることができる。はんだバンプは、例えば、配線層３１０の外部接続端子であるパッド上にはんだボールを配置し、加熱してはんだを溶融させる（リフローする）ことにより形成することができる。金バンプは、ボールボンディング法、めっき法、Ａｕボール転写法等の方法により形成することができる。
（工程（６））
　本実施形態に係る電子装置の製造方法において、図３に示すように、電子装置３００をダイシングし、複数の電子装置４００を得る工程（６）をさらに備えてもよい。
　電子装置３００のダイシングは、公知の方法で行うことができる。
　以上、本発明の実施形態について述べたが、これらは本発明の例示であり、上記以外の様々な構成を採用することもできる。
　なお、本発明は前述の実施形態に限定されるものではなく、本発明の目的を達成できる範囲での変形、改良等は本発明に含まれるものである。
　以下、実施例により本発明を具体的に説明するが本発明はこれに限定されるものではない。
　粘着性フィルムの作製に用いた材料の詳細は以下の通りである。
［実施例１］
（ｉ）（メタ）アクリル系粘着性樹脂を主たる構成成分とし１２５℃における貯蔵弾性率Ｅ’が２．２×１０６Ｐａで、かつ、ガラス転移温度（Ｔｇ）が－１４℃である厚さ１３μｍの粘着性樹脂層（Ａ）、厚さ３８μｍのポリエチレンテレフタレート（ＰＥＴ）フィルムからなる基材層、アクリル系樹脂からなる厚さ２２μｍの易接着層および１８５℃で剥離する特性を有する厚さ２８μｍの加熱膨張型粘着剤層（粘着性樹脂層（Ｂ））をこの順番に有する粘着性フィルムを用意した。
（ｉｉ）用意した粘着性フィルムを、粘着性樹脂層（Ｂ）側を介してコンプレッションモールド用のステンレス板（φ３１０ｍｍ、厚さ１．５ｍｍ）上に接着した。
（ｉｉｉ）次いで、粘着性フィルムの粘着性樹脂層（Ａ）上に、電子部品である５．０ｍｍ角で、かつ、厚さ２５０μｍの半導体チップを２．０ｍｍ間隔の格子状となるように、フリップチップボンダを用いて、ヘッド温度およびステージ温度を２５℃とし、押し込み圧力１０Ｎ、押し込み時間０．５ｓにてチップマウントを実施して密着させた。
（ｉｖ）モールディングマシンを用いて液状のエポキシ樹脂系封止材（ナガセケムテックス社製、製品名：Ｔ６９３／Ｒ４２１２－２Ｃ）により、圧力２８０ｋＮ、モールド温度１２５℃、モールド時間４００ｓで、粘着性樹脂層（Ａ）上の複数個の半導体チップの樹脂封止を行った。これにより、厚さ５５０μｍで、かつ、φ３００ｍｍの電子装置が粘着性フィルムを介してステンレス板上に形成された構造体を得た。
（ｖ）得られた構造体を１５０℃のオーブン内に入れ３０分間加熱しエポキシ樹脂系封止材をさらに硬化させた。
（ｖｉ）その後、構造体を１９０℃で1分間加熱プレスして粘着性樹脂層（Ｂ）を加熱膨張させ、粘着性樹脂層（Ｂ）とステンレス板との間を剥離した。
（ｖｉｉ）次いで、１５０℃で粘着性樹脂層（Ａ）と電子装置の間を剥離して粘着性フィルムを除去し、電子装置を得た。
（ｖｉｉｉ）得られた電子装置について「封止工程における電子部品の位置ずれ」および「電子部品上の糊残り」の評価をそれぞれ行った。得られた結果を表１に示す。
［実施例２～４、比較例１および２］
　粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’およびＴｇを表１に示す値に変更した以外は実施例１で用いた粘着性フィルムと同様の粘着性フィルムを用いて、実施例１と同様の方法により電子装置をそれぞれ作製した。
　得られた電子装置について実施例１と同様の評価を行った。得られた結果を表１に示す。
＜評価＞
（１）封止工程における電子部品の位置ずれ
　実施例・比較例で得られた電子装置について、下記の基準で電子部品の位置ずれを評価した。
　〇：半導体チップの位置ずれが観察されなかった
　×：半導体チップの少なくとも一部に位置ずれが観察された
（２）電子部品上の糊残り
　実施例・比較例で得られた電子装置について、粘着性フィルムの剥離後の半導体チップ表面を光学顕微鏡により２００倍と５００倍で観察し、半導体チップ表面の粘着性フィルムの糊残りを確認し、下記の基準で粘着性フィルムの糊残りを評価した。
　〇：半導体チップ側の剥離面に糊残りが観察されなかった
　×：半導体チップ側の剥離面に糊残りが観察された
＜実施例・比較例で用いた粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’の測定方法＞
　実施例・比較例で用いた粘着性樹脂層（Ａ）について、粘着性フィルムとは別に２０μｍの粘着性樹脂層をそれぞれ作製した。その後、得られた粘着性樹脂層を積層し、厚さが１ｍｍの粘弾性測定用サンプルをそれぞれ得た。
　得られた粘弾性測定用サンプルについて、固体粘弾性測定装置（ＲＳＡ－３、ＴＡインスツルメント社製）を用いて、周波数１Ｈｚ、昇温速度５℃／ｍｉｎ、ひずみ０．０５％、チャック間距離２０ｍｍ、サンプル幅１０ｍｍの条件で固体粘弾性を測定し測定結果を解析し、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’とした。あわせて測定されたｔａｎδのピーク温度をＴｇとした。
Figure JPOXMLDOC01-appb-T000001
　粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’が０．２×１０６Ｐａ以上４．５×１０６Ｐａ以下である粘着性フィルムを用いた実施例では、封止工程における電子部品の位置ずれおよび電子部品上の糊残りは観察されなかった。よって、実施例の電子装置の製造方法では、封止工程における電子部品の位置ずれを抑制できるとともに、粘着性フィルムから電子部品を剥離する際の電子部品側の糊残りを抑制することが可能できることが理解できる。
　これに対し、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’が４．５×１０６Ｐａ超過である粘着性フィルムを用いた比較例１では、封止工程における電子部品の位置ずれが観察された。また、粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’が０．２×１０６Ｐａ未満である粘着性フィルムを用いた比較例２では、電子部品上の糊残りが観察された。
　この出願は、２０１９年６月３日に出願された日本出願特願２０１９－１０３４６９号を基礎とする優先権を主張し、その開示の全てをここに取り込む。
Ａ　　　粘着性樹脂層
Ｂ　　　粘着性樹脂層
１０　　基材層
１０Ａ　第１面
１０Ｂ　第２面
５０　　粘着性フィルム
６０　　封止材
７０　　電子部品
８０　　支持基板
１００　構造体
２００　電子装置
３００　電子装置
３１０　配線層
３２０　バンプ
４００　電子装置

Claims (5)

  1. 　基材層と、前記基材層の第１面側に設けられた粘着性樹脂層（Ａ）と、前記基材層の第２面側に設けられ、かつ、外部刺激により粘着力が低下する粘着性樹脂層（Ｂ）と、を備え、前記粘着性樹脂層（Ａ）の１２５℃における貯蔵弾性率Ｅ’が０．２×１０６Ｐａ以上４．５×１０６Ｐａ以下である粘着性フィルムと、前記粘着性フィルムの前記粘着性樹脂層（Ａ）に貼り付けられた電子部品と、前記粘着性フィルムの前記粘着性樹脂層（Ｂ）に貼り付けられた支持基板と、を備える構造体を準備する工程（１）と、
    　封止材により前記電子部品を封止する工程（２）と、
    　外部刺激を与えることにより前記粘着性樹脂層（Ｂ）の粘着力を低下させて前記構造体から前記支持基板を剥離する工程（３）と、
    　前記電子部品から前記粘着性フィルムを剥離する工程（４）と、
    を少なくとも備える電子装置の製造方法。
  2. 　請求項１に記載の電子装置の製造方法において、
    　前記粘着性樹脂層（Ｂ）は１５０℃を超える温度で加熱することにより粘着力が低下する粘着性フィルムであり、工程（３）では１５０℃を超える温度に加熱する電子装置の製造方法。
  3. 　請求項１または２に記載の電子装置の製造方法において、
    　前記粘着性樹脂層（Ｂ）が気体発生成分および熱膨張性の微小球から選択される少なくとも一種を含む電子装置の製造方法。
  4. 　請求項１乃至３のいずれか一項に記載の電子装置の製造方法において、
    　前記粘着性樹脂層（Ａ）は（メタ）アクリル系粘着性樹脂を含む電子装置の製造方法。
  5. 　請求項１乃至４のいずれか一項に記載の電子装置の製造方法において、
    　前記封止材がエポキシ樹脂系封止材である電子装置の製造方法。
PCT/JP2020/019120 2019-06-03 2020-05-13 電子装置の製造方法 WO2020246207A1 (ja)