WO2020235383A1 - Composition de résine, film de revêtement dur et polyorganosilsesquioxane - Google Patents

Composition de résine, film de revêtement dur et polyorganosilsesquioxane Download PDF

Info

Publication number
WO2020235383A1
WO2020235383A1 PCT/JP2020/018872 JP2020018872W WO2020235383A1 WO 2020235383 A1 WO2020235383 A1 WO 2020235383A1 JP 2020018872 W JP2020018872 W JP 2020018872W WO 2020235383 A1 WO2020235383 A1 WO 2020235383A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
structural unit
polyorganosylsesquioxane
hydrogen bond
crosslinkable
Prior art date
Application number
PCT/JP2020/018872
Other languages
English (en)
Japanese (ja)
Inventor
裕三 永田
暢之 芥川
北村　哲
顕夫 田村
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to KR1020217034154A priority Critical patent/KR20210144791A/ko
Priority to JP2021520715A priority patent/JP7142158B2/ja
Priority to CN202080036599.8A priority patent/CN113840854B/zh
Publication of WO2020235383A1 publication Critical patent/WO2020235383A1/fr

Abstract

La présente invention concerne : une composition de résine qui contient un polyorganosilsesquioxane qui comporte un groupe contenant un atome d'hydrogène pouvant former une liaison hydrogène, le polyorganosilsesquioxane ayant un indice de liaison hydrogène supérieur ou égal à 3,0 et une longueur de chaîne latérale de 14 × 10-10 m à 19 × 10-10 m ; la composition de résine dans laquelle le polyorganosilsesquioxane présente un indice de liaison hydrogène supérieur ou égal à 3,0 et un indice de groupe réticulable de 4,5 à 6,0 ; un film de revêtement dur qui comprend une couche de revêtement dur qui est obtenue par durcissement de la composition de résine décrite ci-dessus ; et un polyorganosilsesquioxane.
PCT/JP2020/018872 2019-05-17 2020-05-11 Composition de résine, film de revêtement dur et polyorganosilsesquioxane WO2020235383A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
KR1020217034154A KR20210144791A (ko) 2019-05-17 2020-05-11 수지 조성물, 하드 코트 필름, 및 폴리오가노실세스퀴옥세인
JP2021520715A JP7142158B2 (ja) 2019-05-17 2020-05-11 樹脂組成物、ハードコートフィルム、及びポリオルガノシルセスキオキサン
CN202080036599.8A CN113840854B (zh) 2019-05-17 2020-05-11 树脂组合物、硬涂薄膜以及聚有机硅倍半氧烷

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019093792 2019-05-17
JP2019-093792 2019-05-17

Publications (1)

Publication Number Publication Date
WO2020235383A1 true WO2020235383A1 (fr) 2020-11-26

Family

ID=73458450

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/018872 WO2020235383A1 (fr) 2019-05-17 2020-05-11 Composition de résine, film de revêtement dur et polyorganosilsesquioxane

Country Status (4)

Country Link
JP (1) JP7142158B2 (fr)
KR (1) KR20210144791A (fr)
CN (1) CN113840854B (fr)
WO (1) WO2020235383A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021193478A1 (fr) * 2020-03-25 2021-09-30 富士フイルム株式会社 Composition pour formation d'une couche de revêtement dur, film de revêtement dur, article pourvu d'un film de revêtement dur, dispositif d'affichage d'image et procédé de fabrication d'un film de revêtement dur

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005104025A (ja) * 2003-09-30 2005-04-21 Fuji Photo Film Co Ltd ガスバリア性積層フィルム、及びそれを用いた画像表示素子
JP2015212353A (ja) * 2013-12-13 2015-11-26 株式会社ダイセル ポリオルガノシルセスキオキサン、ハードコートフィルム、接着シート、及び積層物
JP2017008134A (ja) * 2015-06-17 2017-01-12 東京応化工業株式会社 硬化性組成物、硬化物の製造方法、及びハードコート材
JP2018189800A (ja) * 2017-05-02 2018-11-29 株式会社ダイセル 曲面ディスプレイ用ハードコートフィルム、ハードコートフィルム付き透明基板及びディスプレイ装置
JP2018192634A (ja) * 2017-05-12 2018-12-06 株式会社ダイセル カールが抑制されたハードコートフィルム及びその製造方法

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20090269504A1 (en) 2008-04-24 2009-10-29 Momentive Performance Materials Inc. Flexible hardcoats and substrates coated therewith
WO2010067685A1 (fr) 2008-12-10 2010-06-17 関西ペイント株式会社 Composé silsesquioxane ayant un groupe fonctionnel polymérisable
MY154045A (en) * 2012-05-25 2015-04-27 Daicel Corp Curable resin composition and cured product thereof, encapsulating agent, and optical semiconductor device

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005104025A (ja) * 2003-09-30 2005-04-21 Fuji Photo Film Co Ltd ガスバリア性積層フィルム、及びそれを用いた画像表示素子
JP2015212353A (ja) * 2013-12-13 2015-11-26 株式会社ダイセル ポリオルガノシルセスキオキサン、ハードコートフィルム、接着シート、及び積層物
JP2017008134A (ja) * 2015-06-17 2017-01-12 東京応化工業株式会社 硬化性組成物、硬化物の製造方法、及びハードコート材
JP2018189800A (ja) * 2017-05-02 2018-11-29 株式会社ダイセル 曲面ディスプレイ用ハードコートフィルム、ハードコートフィルム付き透明基板及びディスプレイ装置
JP2018192634A (ja) * 2017-05-12 2018-12-06 株式会社ダイセル カールが抑制されたハードコートフィルム及びその製造方法

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2021193478A1 (fr) * 2020-03-25 2021-09-30 富士フイルム株式会社 Composition pour formation d'une couche de revêtement dur, film de revêtement dur, article pourvu d'un film de revêtement dur, dispositif d'affichage d'image et procédé de fabrication d'un film de revêtement dur

Also Published As

Publication number Publication date
KR20210144791A (ko) 2021-11-30
CN113840854A (zh) 2021-12-24
JPWO2020235383A1 (fr) 2020-11-26
CN113840854B (zh) 2024-05-14
JP7142158B2 (ja) 2022-09-26

Similar Documents

Publication Publication Date Title
JP7064650B2 (ja) 積層体、積層体を備えた物品、及び画像表示装置
JP6979517B2 (ja) ハードコートフィルム、ハードコートフィルムを備えた物品、及び画像表示装置
JP6967662B2 (ja) ハードコートフィルム、ハードコートフィルムを有する物品、画像表示装置、及びハードコートフィルムの製造方法
CN112390974B (zh) 聚酰亚胺基复合膜及其显示装置
JP7263356B2 (ja) ハードコートフィルム、ハードコートフィルムを備えた物品、及び画像表示装置
JP6999808B2 (ja) 組成物、ハードコートフィルム、ハードコートフィルムを備えた物品、及び画像表示装置
CN112004838B (zh) 改性剂、组合物、硬涂膜、具备硬涂膜的物品及图像显示装置
WO2020235383A1 (fr) Composition de résine, film de revêtement dur et polyorganosilsesquioxane
JP7280963B2 (ja) ハードコート層形成用組成物、ハードコートフィルム、ハードコートフィルムの製造方法、及びハードコートフィルムを含む物品
JP7377261B2 (ja) ハードコートフィルム、ハードコートフィルムを備えた物品、及び画像表示装置
WO2021206066A1 (fr) Film antireflet et procédé de production de film antireflet
JP7358624B2 (ja) ハードコート層形成用組成物、ハードコートフィルム、ハードコートフィルムの製造方法及びハードコートフィルムを備えた物品
WO2022209922A1 (fr) Composition durcissable, film de revêtement dur, et produit, dispositif d'affichage d'image et afficheur souple comprenant un film de revêtement dur
CN116917125A (zh) 叠层体及其制造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20809538

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20217034154

Country of ref document: KR

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2021520715

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20809538

Country of ref document: EP

Kind code of ref document: A1