WO2020130097A1 - Composition d'étanchéité et dispositif à semi-conducteur - Google Patents

Composition d'étanchéité et dispositif à semi-conducteur Download PDF

Info

Publication number
WO2020130097A1
WO2020130097A1 PCT/JP2019/049923 JP2019049923W WO2020130097A1 WO 2020130097 A1 WO2020130097 A1 WO 2020130097A1 JP 2019049923 W JP2019049923 W JP 2019049923W WO 2020130097 A1 WO2020130097 A1 WO 2020130097A1
Authority
WO
WIPO (PCT)
Prior art keywords
epoxy resin
mass
group
epoxy
sealing composition
Prior art date
Application number
PCT/JP2019/049923
Other languages
English (en)
Japanese (ja)
Inventor
実佳 田中
健太 石橋
拓也 児玉
慧地 堀
Original Assignee
日立化成株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日立化成株式会社 filed Critical 日立化成株式会社
Priority to CN201980083406.1A priority Critical patent/CN113242873B/zh
Priority to JP2020561521A priority patent/JP7392659B2/ja
Publication of WO2020130097A1 publication Critical patent/WO2020130097A1/fr

Abstract

Cette composition d'étanchéité contient : une première résine époxy ayant un équivalent de groupe époxy de 300 g/éq ou plus et une température de transition vitreuse de 40 °C ou moins lorsqu'elle est durcie à l'aide d'un agent de durcissement de résine phénolique polyfonctionnelle et d'un promoteur de durcissement au phosphore; un agent de durcissement; et une charge minérale.
PCT/JP2019/049923 2018-12-21 2019-12-19 Composition d'étanchéité et dispositif à semi-conducteur WO2020130097A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201980083406.1A CN113242873B (zh) 2018-12-21 2019-12-19 密封组合物及半导体装置
JP2020561521A JP7392659B2 (ja) 2018-12-21 2019-12-19 封止組成物及び半導体装置

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018239253 2018-12-21
JP2018-239253 2018-12-21

Publications (1)

Publication Number Publication Date
WO2020130097A1 true WO2020130097A1 (fr) 2020-06-25

Family

ID=71102873

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/049923 WO2020130097A1 (fr) 2018-12-21 2019-12-19 Composition d'étanchéité et dispositif à semi-conducteur

Country Status (4)

Country Link
JP (1) JP7392659B2 (fr)
CN (1) CN113242873B (fr)
TW (1) TW202033726A (fr)
WO (1) WO2020130097A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11282194B2 (en) 2015-12-23 2022-03-22 Gauss Surgical, Inc. Method for estimating blood component quantities in surgical textiles

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007194405A (ja) * 2006-01-19 2007-08-02 Nitto Shinko Kk 熱伝導用エポキシ樹脂組成物
WO2012091000A1 (fr) * 2010-12-27 2012-07-05 東レ・ダウコーニング株式会社 Composition de résine époxy durcissable
JP2013071950A (ja) * 2011-09-27 2013-04-22 Nippon Kayaku Co Ltd 硬化性樹脂組成物およびその硬化物
JP2016219619A (ja) * 2015-05-21 2016-12-22 日東電工株式会社 接着シート、ダイシングテープ一体型接着シート、フィルム、半導体装置の製造方法および半導体装置
JP2019001841A (ja) * 2017-06-12 2019-01-10 信越化学工業株式会社 エポキシ樹脂組成物及び該組成物の硬化物を備える半導体装置

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007194405A (ja) * 2006-01-19 2007-08-02 Nitto Shinko Kk 熱伝導用エポキシ樹脂組成物
WO2012091000A1 (fr) * 2010-12-27 2012-07-05 東レ・ダウコーニング株式会社 Composition de résine époxy durcissable
JP2013071950A (ja) * 2011-09-27 2013-04-22 Nippon Kayaku Co Ltd 硬化性樹脂組成物およびその硬化物
JP2016219619A (ja) * 2015-05-21 2016-12-22 日東電工株式会社 接着シート、ダイシングテープ一体型接着シート、フィルム、半導体装置の製造方法および半導体装置
JP2019001841A (ja) * 2017-06-12 2019-01-10 信越化学工業株式会社 エポキシ樹脂組成物及び該組成物の硬化物を備える半導体装置

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11282194B2 (en) 2015-12-23 2022-03-22 Gauss Surgical, Inc. Method for estimating blood component quantities in surgical textiles
US11790637B2 (en) 2015-12-23 2023-10-17 Gauss Surgical Inc. Method for estimating blood component quantities in surgical textiles

Also Published As

Publication number Publication date
JP7392659B2 (ja) 2023-12-06
CN113242873B (zh) 2024-04-19
TW202033726A (zh) 2020-09-16
CN113242873A (zh) 2021-08-10
JPWO2020130097A1 (ja) 2021-11-04

Similar Documents

Publication Publication Date Title
JP2024026589A (ja) 封止用樹脂組成物、電子部品装置及び電子部品装置の製造方法
EP4261254A1 (fr) Composition de résine pour moulage, et dispositif de composant électronique
JP2023083365A (ja) 封止用樹脂組成物、封止用樹脂組成物の製造方法、半導体装置及び半導体装置の製造方法
JP2004307650A (ja) 封止用エポキシ樹脂成形材料及び半導体装置
JP2018172545A (ja) 圧縮成形用固形封止材、半導体装置の製造方法及び半導体装置
JP7392659B2 (ja) 封止組成物及び半導体装置
JP7388160B2 (ja) 封止用樹脂組成物、電子部品装置及び電子部品装置の製造方法
TW202120580A (zh) 環氧樹脂組成物、電子零件裝置、及電子零件裝置的製造方法
JP2020139042A (ja) 封止組成物及び半導体装置
JP2019001841A (ja) エポキシ樹脂組成物及び該組成物の硬化物を備える半導体装置
JP7415950B2 (ja) 封止組成物及び半導体装置
JP2022093030A (ja) 樹脂組成物及び高周波デバイス
TWI835960B (zh) 密封組成物及半導體裝置
JPWO2020175669A1 (ja) 封止組成物及び半導体装置
JP2020122071A (ja) 封止用樹脂組成物、電子部品装置及び電子部品装置の製造方法
WO2019035430A1 (fr) Composition de résine pour scellement, et dispositif à semi-conducteurs ainsi que procédé de fabrication de celui-ci
WO2024111461A1 (fr) Composition de résine pour moulage, et dispositif de composant électronique
JP7452287B2 (ja) 封止用樹脂組成物の製造方法、封止用樹脂組成物、電子部品装置の製造方法、及び電子部品装置
KR102668756B1 (ko) 밀봉 조성물 및 그의 제조 방법 그리고 반도체 장치
JP7487596B2 (ja) 封止用樹脂組成物、電子部品装置及び電子部品装置の製造方法
JP2024055627A (ja) 成形用樹脂組成物及び電子部品装置
WO2024111575A1 (fr) Composition de résine pour moulage, et dispositif de composant électronique
WO2021149727A1 (fr) Composition de résine d'étanchéité, dispositif à composants électroniques et procédé de fabrication de dispositif à composants électroniques
KR20200103683A (ko) 밀봉 조성물 및 그의 제조 방법 그리고 반도체 장치
JPWO2019131670A1 (ja) 封止組成物及び半導体装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19897757

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020561521

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

32PN Ep: public notification in the ep bulletin as address of the adressee cannot be established

Free format text: NOTING OF LOSS OF RIGHTS PURSUANT TO RULE 112(1) EPC (EPO FORM 1205 DATED 04.10.21)

122 Ep: pct application non-entry in european phase

Ref document number: 19897757

Country of ref document: EP

Kind code of ref document: A1