WO2020129626A1 - 付着物除去方法及び成膜方法 - Google Patents

付着物除去方法及び成膜方法 Download PDF

Info

Publication number
WO2020129626A1
WO2020129626A1 PCT/JP2019/047269 JP2019047269W WO2020129626A1 WO 2020129626 A1 WO2020129626 A1 WO 2020129626A1 JP 2019047269 W JP2019047269 W JP 2019047269W WO 2020129626 A1 WO2020129626 A1 WO 2020129626A1
Authority
WO
WIPO (PCT)
Prior art keywords
gas
chamber
passivation
sulfur
hydrogen
Prior art date
Application number
PCT/JP2019/047269
Other languages
English (en)
French (fr)
Inventor
陽祐 谷本
師門 長田
Original Assignee
昭和電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 昭和電工株式会社 filed Critical 昭和電工株式会社
Priority to CN201980083535.0A priority Critical patent/CN113228235B/zh
Priority to KR1020217018145A priority patent/KR20210088710A/ko
Priority to EP19899762.9A priority patent/EP3901989A4/en
Priority to JP2020561274A priority patent/JP7359159B2/ja
Priority to US17/414,376 priority patent/US20220064777A1/en
Priority to SG11202106420QA priority patent/SG11202106420QA/en
Publication of WO2020129626A1 publication Critical patent/WO2020129626A1/ja
Priority to IL283954A priority patent/IL283954A/en

Abstract

チャンバーの内面又はチャンバーに接続された配管の内面に付着している、硫黄を含有する付着物を、チャンバーを解体することなく除去することが可能な付着物除去方法及び成膜方法を提供する。チャンバー（１０）の内面及びチャンバー（１０）に接続された排気用配管（１５）の内面の少なくとも一方に付着している、硫黄を含有する付着物を、水素含有化合物ガスを含有するクリーニングガスと反応させることにより除去する。

Description

付着物除去方法及び成膜方法
　本発明は付着物除去方法及び成膜方法に関する。
　近年、半導体分野において、シリコン（Ｓｉ）以外の元素を含有する半導体材料が注目されている。シリコン以外の元素を含有する半導体材料としては、例えば、ゲルマニウム（Ｇｅ）、インジウムガリウム砒素（ＩｎＧａＡｓ）等のＩＩＩ－Ｖ族元素を含有する半導体材料や、金属カルコゲナイドを含有する半導体材料が挙げられる。
　これらの半導体材料は、シリコン材料と比較してモビリティ（移動度）が高いというメリットを有しているものの、成膜が困難である場合や、材料間の界面の欠陥密度が高くなる場合があった。
　そこで、材料間の界面の欠陥密度を低くするために、ゲルマニウム、モリブデン等の基板の上に硫化水素（Ｈ2Ｓ）ガスを用いてパッシベーション膜を形成する方法が提案されている（例えば特許文献１を参照）。また、金属カルコゲナイドの成膜方法として、モリブデン酸化物層、タングステン酸化物層を硫化水素ガスで処理して硫化モリブデン層、硫化タングステン層を形成する方法が提案されている（例えば特許文献２を参照）。
日本国特許公開公報　２０１６年第２０７７８９号 日本国特許公開公報　２０１７年第６１７４３号 日本国特許公開公報　２０１１年第１８９３３８号
　材料間の界面の欠陥密度を低くする上記方法においては、高温下で反応が行われるため、該反応が行われるチャンバーの内面や、チャンバーの下流側に配された配管の内面に、硫化水素の分解によって生成した硫黄を含有する付着物が付着する場合があった。
　チャンバーの内面やチャンバーの下流側に配された配管の内面に硫黄を含有する付着物が付着した状態で、ウエハ等の基板をチャンバー内に導入すると、チャンバー内を真空にして不活性ガスで置換した際に硫黄のパーティクルがウエハ等の基板に付着するおそれがあった。そして、硫黄のパーティクルが基板に付着すると、製造された半導体構造の性能が低下するおそれがあった。
　例えば特許文献３には、プラズマ洗浄装置を用いて基板を洗浄する技術が開示されている。この技術においては、基板の洗浄に使用した六フッ化硫黄ガスに由来する硫黄が基板に付着するので、この付着した硫黄をアルゴンによるスパッタリングで除去している。
　しかしながら、特許文献３に開示の技術では、硫黄を物理的に除去しているため、除去された硫黄がプラズマ洗浄装置内の別の場所に再付着したり、プラズマ洗浄装置の下流側に配された配管に再付着したりするという問題があった。
　したがって、チャンバーの内面やチャンバーの下流側に配された配管の内面に、硫黄を含有する付着物が付着した場合には、チャンバーを解体して洗浄を行う必要があった。
　本発明は、チャンバーの内面又はチャンバーに接続された配管の内面に付着している、硫黄を含有する付着物を、チャンバーを解体することなく除去することが可能な付着物除去方法及び成膜方法を提供することを課題とする。
　前記課題を解決するため、本発明の一態様は以下の［１］～［６］の通りである。
［１］　チャンバーの内面及び前記チャンバーに接続された配管の内面の少なくとも一方に付着している、硫黄を含有する付着物を、水素含有化合物ガスを含有するクリーニングガスと反応させることにより除去する付着物除去方法。
［２］　温度２０℃以上８００℃以下、圧力２０Ｐａ以上１０１ｋＰａ以下の条件下で、前記クリーニングガスを前記付着物に接触させる［１］に記載の付着物除去方法。
［３］　前記水素含有化合物ガスが、水素ガス、炭化水素ガス、及びアンモニアガスからなる群より選ばれる少なくとも１種である［１］又は［２］に記載の付着物除去方法。
［４］　前記水素含有化合物ガスが水素ガスである［１］又は［２］に記載の付着物除去方法。
［５］　硫黄含有化合物ガスを含有するパッシベーションガスを、基板が収容されたチャンバーに供給し、前記基板と前記パッシベーションガスとを反応させて、前記基板の表面にパッシベーション膜を成膜するパッシベーション工程と、
　前記パッシベーション工程を行った後に、前記チャンバーの内面及び前記チャンバーに接続された配管の内面の少なくとも一方に付着している、硫黄を含有する付着物を除去する付着物除去工程と、
を備え、
　前記付着物除去工程を、［１］～［４］のいずれか一項に記載の付着物除去方法によって行う成膜方法。
［６］　前記硫黄含有化合物ガスが硫化水素ガスである［５］に記載の成膜方法。
　本発明によれば、チャンバーの内面又はチャンバーに接続された配管の内面に付着している、硫黄を含有する付着物を、チャンバーを解体することなく除去することが可能である。
本発明に係る成膜方法の一実施形態を説明する成膜装置の概略図である。 シリコン基板に付着したパーティクルの個数を測定した結果を示すグラフである。
　本発明の一実施形態について以下に説明する。なお、本実施形態は本発明の一例を示したものであって、本発明は本実施形態に限定されるものではない。また、本実施形態には種々の変更又は改良を加えることが可能であり、その様な変更又は改良を加えた形態も本発明に含まれ得る。
〔第一実施形態〕
　本発明の第一実施形態は、付着物除去方法の実施形態であり、チャンバーの内面及びチャンバーに接続された配管の内面の少なくとも一方に付着している、硫黄を含有する付着物（以下、単に「付着物」と記すこともある）を、水素含有化合物ガスを含有するクリーニングガスと反応させることにより除去する方法である。なお、水素含有化合物ガスとクリーニングガスは硫黄原子を含有しない。
　硫黄を使用する反応をチャンバー中で行った場合などにおいては、チャンバーの内面や、チャンバーに接続された配管（例えば、チャンバーの上流側に接続されたクリーニングガスの給気用配管や、チャンバーの下流側に接続された排気用配管）の内面に、硫黄を含有する付着物が付着する場合がある。付着物が付着したまま次の反応を行うと、反応に悪影響が及ぶおそれがあるので、付着物を除去した後に次の反応を行うことが好ましい。
　第一実施形態に係る付着物除去方法は、付着物にクリーニングガスを接触させ、付着物中の硫黄とクリーニングガス中の水素含有化合物ガスとを反応させて硫化水素ガスを生成することによって付着物を除去するので、チャンバーの内面やチャンバーに接続された配管の内面に付着している付着物を、チャンバーを解体することなく除去することが可能である。よって、付着物の除去を容易に行うことができる。
　クリーニングガスと付着物との接触は、温度２０℃以上８００℃以下の条件下で行うことが好ましく、温度４０℃以上６００℃以下の条件下で行うことがより好ましい。８００℃以下の温度であれば、クリーニングガス中の水素含有化合物ガスや生成した硫化水素ガスがチャンバーや配管を形成するステンレス鋼等の金属材料を腐食させにくいことに加えて、付着物中の硫黄とクリーニングガス中の水素含有化合物ガスとの反応によって生成した硫化水素ガスが硫黄へ戻る逆反応が起こりにくい。一方、２０℃以上の温度であれば、付着物中の硫黄とクリーニングガス中の水素含有化合物ガスとの反応が進行しやすい。
　また、クリーニングガスと付着物との接触は、絶対圧力で圧力２０Ｐａ以上１０１ｋＰａ以下の条件下で行うことが好ましく、圧力６０Ｐａ以上９０ｋＰａ以下の条件下で行うことがより好ましい。１０１ｋＰａ以下の圧力であれば、チャンバーや配管に不具合が生じにくい。例えば、チャンバーが、基板とパッシベーションガスとを反応させて基板の表面にパッシベーション膜を成膜する成膜装置の反応容器である場合には、減圧環境下での使用が前提となるので、圧力条件は１０１ｋＰａ以下であることが好ましい。一方、２０Ｐａ以上の圧力であれば、付着物中の硫黄とクリーニングガス中の水素含有化合物ガスとの反応が進行しやすい。
　水素含有化合物ガスは、水素原子を有する化合物のガスであって、さらには硫黄原子及びハロゲン原子を有しないガスであり、例えば、水素ガス（Ｈ2）、炭化水素ガス、及びアンモニアガス（ＮＨ3）を挙げることができる。これらの中では、水素ガス（Ｈ2）、メタンガス（ＣＨ4）、エタンガス（Ｃ2Ｈ6）、プロパンガス（Ｃ3Ｈ8）、ブタンガス（Ｃ4Ｈ10）、及びアンモニアガス（ＮＨ3）からなる群より選ばれる少なくとも一種のガスが好ましく、水素ガス及びメタンガスの少なくとも一方がより好ましい。
　水素ガスは１０１ｋＰａの圧力下では３００℃以上の温度で硫黄と反応するため、クリーニングガス中に水素ガスを含有する場合は、３００℃以上８００℃以下の温度でクリーニングガスと硫黄（付着物）を接触させることが好ましい。なお、クリーニングガス中に水素ガスを含有する場合は、付着物を効率的に除去するために、チャンバーの内部や配管を加熱しながら付着物の除去を行うことが好ましい。メタンガスは１０１ｋＰａの圧力下では１４０℃以上の温度で硫黄と反応するため、クリーニングガス中にメタンガスを含有する場合は、１４０℃以上８００℃以下の温度でクリーニングガスと硫黄（付着物）を接触させることが好ましい。
　クリーニングガスにおける水素含有化合物ガスの含有比率は、硫黄（付着物）を除去するのに十分な量であれば特に限定されるものではないが、５体積％以上であることが好ましく、２０体積％以上であることがより好ましく、９０体積％以上であることがさらに好ましく、１００体積％であることが特に好ましい。クリーニングガスに含有される水素含有化合物ガス以外の成分は、硫黄原子を有しない化合物のガスであれば特に限定されるものではないが、例えば、窒素ガス、アルゴンガス等の不活性ガスを挙げることができる。
　チャンバーは、硫化水素に対する耐性を有する素材で形成されていれば特に限定されるものではないが、所定の圧力に減圧可能な構造を有することが好ましく、素材としては例えば表面がアルマイト処理されたアルミニウムなどを挙げることができる。また、チャンバーに接続された配管についても、硫化水素に対する耐性を有する素材で形成されていれば特に限定されるものではないが、所定の圧力に耐える構造を有することが好ましい。例えば、半導体の成膜装置に反応容器として備えられるチャンバー、及び、該チャンバーに接続された配管に対して、第一実施形態に係る付着物除去方法を好適に適用することができる。
〔第二実施形態〕
　本発明の第二実施形態は、成膜方法の実施形態であり、硫黄含有化合物ガスを含有するパッシベーションガスを、基板が収容されたチャンバーに供給し、基板とパッシベーションガスとを反応させて、基板の表面にパッシベーション膜を成膜するパッシベーション工程と、パッシベーション工程を行った後に、チャンバーの内面及びチャンバーに接続された配管の内面の少なくとも一方に付着している、硫黄を含有する付着物を除去する付着物除去工程と、を備える方法である。そして、この付着物除去工程は、第一実施形態の付着物除去方法によって行われるものである。
　パッシベーションガスを用いて基板の表面にパッシベーション膜を成膜するパッシベーション工程においては、チャンバーの内面や、チャンバーに接続された配管（例えば、チャンバーの上流側に接続されたパッシベーションガス又はクリーニングガスの給気用配管や、チャンバーの下流側に接続された排気用配管）の内面に、硫黄を含有する付着物が付着する場合がある。
　チャンバーの内面や配管の内面に付着物が付着した状態で基板をチャンバー内に導入すると、チャンバー内を真空にして不活性ガスで置換した際に硫黄のパーティクルが基板に付着するおそれがある。そして、硫黄のパーティクルが基板に付着すると、製造された半導体構造の性能が低下するおそれがある。また、硫黄のパーティクルが基板に付着したまま次のパッシベーション工程を行うと、パッシベーション膜の成膜速度や膜質の低下などの不具合が生じるおそれがある。よって、付着物を除去した後に次のパッシベーション工程を行うことが好ましい。
　第二実施形態に係る成膜方法は、付着物にクリーニングガスを接触させ、付着物中の硫黄とクリーニングガス中の水素含有化合物ガスとを反応させて硫化水素ガスを生成することによって付着物を除去するので、チャンバーの内面やチャンバーに接続された配管の内面に付着している付着物を、チャンバーを解体することなく除去することが可能である。よって、付着物の除去を容易に行うことができる。また、第二実施形態に係る成膜方法であれば、付着物の除去によって硫黄のパーティクルが基板に付着することを抑制することができるので、優れた性能を有する半導体構造を製造することができる。
　なお、第二実施形態に係る成膜方法においては、パッシベーション工程を行うごとに毎回必ず付着物除去工程を行わなければならないわけではなく、パッシベーション工程を複数回行うごとに付着物除去工程を行ってもよい。パッシベーション工程を行う回数に対して付着物除去工程を行う回数を少なくすれば、成膜装置の利用効率を向上させることができる。
　硫黄含有化合物ガスを含有するパッシベーションガスの種類は、硫黄を有する化合物のガスであれば特に限定されるものではないが、パッシベーション性能が良好であることから硫化水素ガスが好ましい。
　パッシベーションガスにおける硫黄含有化合物ガスの含有比率は、パッシベーション膜の成膜に十分な量であれば特に限定されるものではないが、１体積％以上であることが好ましく、２体積％以上であることがより好ましく、１０体積％以上であることがさらに好ましく、１００体積％であることが特に好ましい。パッシベーションガスに含有される硫黄含有化合物ガス以外の成分は、特に限定されるものではないが、例えば、窒素ガス、アルゴンガス等の不活性ガスを挙げることができる。
　基板を形成する材料の種類は、半導体材料であれば特に限定されるものではないが、例えば、シリコン、ゲルマニウム、ＩＩＩ－Ｖ族化合物、モリブデン、タングステン等の元素を含有する材料が挙げられる。シリコンとしては、半導体素子の形成に使用されるシリコンが好適であり、例えば、アモルファスシリコン、ポリシリコン、単結晶シリコンなどが挙げられる。ゲルマニウム、ＩＩＩ－Ｖ族化合物、モリブデン、タングステンについても、半導体素子の形成に使用されるものが好適である。
　パッシベーション工程においてパッシベーション膜を成膜する際のチャンバー内の圧力は、特に限定されるものではないが、１Ｐａ以上１０１ｋＰａ以下であることが好ましく、１０Ｐａ以上９０ｋＰａ以下であることがより好ましく、１００Ｐａ以上８０ｋＰａ以下であることがさらに好ましい。
　パッシベーション工程において基板とパッシベーションガスとを反応させる際の基板の温度は、特に限定されるものではないが、基板の表面のパッシベーションガスによる処理の高い面内均一性を得るためには、２０℃以上１５００℃以下であることが好ましく、５０℃以上１２００℃以下であることがより好ましく、１００℃以上１０００℃以下であることがさらに好ましい。
　パッシベーション工程においてパッシベーション時間の長さは特に限定されるものではないが、半導体素子製造プロセスの効率を考慮すると、１２０分以内であることが好ましい。なお、パッシベーション時間とは、基板が収容されたチャンバーにパッシベーションガスを供給してから、パッシベーションガスによる基板の表面の処理を終えるためにチャンバー内のパッシベーションガスを真空ポンプ等により排気するまでの時間を指す。
　第二実施形態に係る成膜方法は、基板の表面にパッシベーション膜を成膜する半導体の成膜装置に対して好適に適用することができる。この成膜装置の構造は特に限定されるものではなく、反応容器であるチャンバー内に収容された基板と、チャンバーに接続された配管との位置関係も特に限定されない。
　以下に実施例及び比較例を示して、本発明をより詳細に説明する。
（実施例１）
　図１に示す成膜装置１を用いて、基板の表面にパッシベーション膜を成膜するパッシベーション工程と、硫黄を含有する付着物を除去する付着物除去工程とを繰り返し行った。成膜装置１は、パッシベーション工程や付着物除去工程を行うチャンバー１０と、チャンバー１０の内部の温度を調整する温度調整装置（図示せず）と、を有する。チャンバー１０の内部には、試料２０を支持するステージ１１が備えられている。試料２０としては、シリコン基板上に厚さ１５０ｎｍのシリコン酸化膜が形成され、さらにその上に厚さ８０ｎｍのゲルマニウム膜が形成されたものを使用した。
　チャンバー１０には、その上流側に、硫黄含有化合物ガスを含有するパッシベーションガスをチャンバー１０に供給するパッシベーションガス給気用配管１２と、水素含有化合物ガスを含有するクリーニングガスをチャンバー１０に供給するクリーニングガス給気用配管１３と、不活性ガスをチャンバー１０に供給する不活性ガス給気用配管１４とが、それぞれバルブ３２、３３、３４を介して接続されている。
　また、チャンバー１０には、その下流側に、チャンバー１０内のガスを外部に排出する排気用配管１５が接続されており、排気用配管１５の下流側にはバルブ３５を介して真空ポンプ３８が接続されている。チャンバー１０の内部の圧力は、バルブ３５を制御する圧力コントローラ３７により制御される。
　このような成膜装置１を使用して、まずパッシベーション工程を行った。ステージ１１上に試料２０を設置し、チャンバー１０内の圧力を１０Ｐａ未満まで減圧した後に、チャンバー１０内の温度を８００℃に昇温した。その後、バルブ３２を開状態とし、パッシベーションガス給気用配管１２からチャンバー１０内にパッシベーションガスとして硫化水素ガスを１０１ｋＰａの圧力で供給した。このときのパッシベーションガスの流量は１００ｓｃｃｍとし、試料２０の表面にパッシベーション膜を成膜する際のチャンバー１０内の圧力は６７ｋＰａとした。なお、ｓｃｃｍは、０℃、１０１．３ｋＰａにおける流量（ｍＬ／ｍｉｎ）を表す。
　パッシベーションガスの導入を３０分間行って、温度８００℃、圧力６７ｋＰａの条件下で試料２０の表面を硫化しパッシベーション膜を成膜したら、パッシベーションガスの導入を停止した。そして、チャンバー１０の内部を真空ポンプ３８で真空にし、不活性ガス給気用配管１４からチャンバー１０内に不活性ガスを供給してチャンバー１０の内部を不活性ガスで置換した。その後、チャンバー１０内の温度を室温に下げて、パッシベーション膜を成膜した試料２０をチャンバー１０から取り出した。
　次に、成膜装置１を使用して付着物除去工程を行った。試料２０を取り出したチャンバー１０内の圧力を１０Ｐａ未満まで減圧した後に、チャンバー１０内の温度を５００℃に昇温した。その後、バルブ３３を開状態とし、クリーニングガス給気用配管１３からチャンバー１０の内部及び排気用配管１５にクリーニングガスとして水素ガスを供給した。このときのクリーニングガスの流量は１００ｓｃｃｍとし、付着物を除去する際のチャンバー１０内の圧力は６７ｋＰａとした。
　クリーニングガスの導入を５分間行って、温度５００℃、圧力６７ｋＰａの条件下で付着物と水素ガスとを反応させて付着物の除去を行ったら、クリーニングガスの導入を停止した。そして、チャンバー１０の内部を真空ポンプ３８で真空にし、不活性ガス給気用配管１４からチャンバー１０内に不活性ガスを供給してチャンバー１０の内部を不活性ガスで置換した。
　付着物除去工程が終了したら、上記と同様にしてパッシベーション工程を行い、新たな試料２０にパッシベーション膜を成膜した。そして、上記と同様にして付着物除去工程を行った。このような操作を繰り返して、パッシベーション膜を成膜した試料２０を合計で１００枚製造した。
（実施例２）
　付着物除去工程におけるチャンバー１０内の温度を３５０℃、圧力を１００Ｐａとした点以外は、実施例１と同様にして、パッシベーション膜を成膜した試料２０を１００枚製造した。
（実施例３）
　付着物除去工程におけるチャンバー１０内の温度を２０℃とした点以外は、実施例１と同様にして、パッシベーション膜を成膜した試料２０を１００枚製造した。
（実施例４）
　付着物除去工程におけるチャンバー１０内の温度を８００℃とした点以外は、実施例１と同様にして、パッシベーション膜を成膜した試料２０を１００枚製造した。
（実施例５）
　付着物除去工程におけるチャンバー１０内の圧力を２０Ｐａとした点以外は、実施例１と同様にして、パッシベーション膜を成膜した試料２０を１００枚製造した。
（実施例６）
　付着物除去工程におけるチャンバー１０内の圧力を１０１ｋＰａとした点以外は、実施例１と同様にして、パッシベーション膜を成膜した試料２０を１００枚製造した。
（実施例７）
　付着物除去工程におけるクリーニングガス給気用配管１３から供給するクリーニングガスをメタンガスとした点以外は、実施例１と同様にして、パッシベーション膜を成膜した試料２０を１００枚製造した。
（実施例８）
　付着物除去工程におけるクリーニングガス給気用配管１３から供給するクリーニングガスをアンモニアガスとした点以外は、実施例１と同様にして、パッシベーション膜を成膜した試料２０を１００枚製造した。
（比較例１）
　付着物除去工程を行わずパッシベーション工程のみを繰り返し行う点以外は、実施例１と同様にして、パッシベーション膜を成膜した試料２０を１００枚製造した。
　実施例１～８及び比較例１の試料２０について、１枚目から１００枚目の各試料２０のパッシベーション工程が終了するたびに、試料２０の表面に付着している硫黄のパーティクルの個数を測定した。パーティクルの個数の測定は、ＫＬＡテンコール社製のウエハ検査装置サーフスキャン（登録商標）６２４０を用いて行った。測定結果を表１と図２のグラフに示す。
Figure JPOXMLDOC01-appb-T000001
　表１と図２のグラフから分かるように、付着物除去工程を行わずパッシベーション工程のみを繰り返し行う比較例１では、行ったパッシベーション工程の回数が多くなるに連れて、すなわちパッシベーション膜を成膜した試料２０の製造枚数が多くなるに連れて、試料２０に付着したパーティクルの個数が多くなり、３０回目では１０００個／ｍ2以上、１００回目では６０００個／ｍ2以上であった。
　これに対して、パッシベーション工程の後に付着物除去工程を行った実施例１～８では、試料２０に付着したパーティクルの個数は少なく、パッシベーション工程の回数が１００回目でも実施例１では１００個／ｍ2以下であり、実施例２では３００個／ｍ2以下であり、他の実施例でも１０００個／ｍ2以下であった。
　このように、付着物除去工程を行うことにより、チャンバーを解体洗浄することなく、付着するパーティクルの個数を低く保ったままパッシベーション工程を繰り返し行うことができることが示された。
　　　１・・・成膜装置
　　１０・・・チャンバー
　　１１・・・ステージ
　　１２・・・パッシベーションガス給気用配管
　　１３・・・クリーニングガス給気用配管
　　１４・・・不活性ガス給気用配管
　　１５・・・排気用配管
　　２０・・・試料

Claims (6)

  1. 　チャンバーの内面及び前記チャンバーに接続された配管の内面の少なくとも一方に付着している、硫黄を含有する付着物を、水素含有化合物ガスを含有するクリーニングガスと反応させることにより除去する付着物除去方法。
  2. 　温度２０℃以上８００℃以下、圧力２０Ｐａ以上１０１ｋＰａ以下の条件下で、前記クリーニングガスを前記付着物に接触させる請求項１に記載の付着物除去方法。
  3. 　前記水素含有化合物ガスが、水素ガス、炭化水素ガス、及びアンモニアガスからなる群より選ばれる少なくとも１種である請求項１又は請求項２に記載の付着物除去方法。
  4. 　前記水素含有化合物ガスが水素ガスである請求項１又は請求項２に記載の付着物除去方法。
  5. 　硫黄含有化合物ガスを含有するパッシベーションガスを、基板が収容されたチャンバーに供給し、前記基板と前記パッシベーションガスとを反応させて、前記基板の表面にパッシベーション膜を成膜するパッシベーション工程と、
    　前記パッシベーション工程を行った後に、前記チャンバーの内面及び前記チャンバーに接続された配管の内面の少なくとも一方に付着している、硫黄を含有する付着物を除去する付着物除去工程と、
    を備え、
    　前記付着物除去工程を、請求項１～４のいずれか一項に記載の付着物除去方法によって行う成膜方法。
  6. 　前記硫黄含有化合物ガスが硫化水素ガスである請求項５に記載の成膜方法。
PCT/JP2019/047269 2018-12-18 2019-12-03 付着物除去方法及び成膜方法 WO2020129626A1 (ja)