Classifications

• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M145/00—Lubricating compositions characterised by the additive being a macromolecular compound containing oxygen
  • C10M145/02—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
  • C10M145/10—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing monomers having an unsaturated radical bound to a carboxyl radical, e.g. acrylate
  • C10M145/12—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing monomers having an unsaturated radical bound to a carboxyl radical, e.g. acrylate monocarboxylic
  • C10M145/14—Acrylate; Methacrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F236/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds
  • C08F236/02—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds
  • C08F236/04—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds conjugated
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F2/00—Processes of polymerisation
  • C08F2/04—Polymerisation in solution
  • C08F2/06—Organic solvent
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F136/00—Homopolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds
  • C08F136/02—Homopolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds
  • C08F136/04—Homopolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds conjugated
  • C08F136/06—Butadiene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/14—Methyl esters, e.g. methyl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/16—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms
  • C08F220/18—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms with acrylic or methacrylic acids
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/16—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms
  • C08F220/18—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms with acrylic or methacrylic acids
  • C08F220/1804—C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/16—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms
  • C08F220/18—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms with acrylic or methacrylic acids
  • C08F220/1812—C12-(meth)acrylate, e.g. lauryl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F236/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds
  • C08F236/02—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds
  • C08F236/04—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds conjugated
  • C08F236/06—Butadiene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F236/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds
  • C08F236/02—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds
  • C08F236/04—Copolymers of compounds having one or more unsaturated aliphatic radicals, at least one having two or more carbon-to-carbon double bonds the radical having only two carbon-to-carbon double bonds conjugated
  • C08F236/08—Isoprene
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
  • C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
  • C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
  • C08F4/70—Iron group metals, platinum group metals or compounds thereof
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F8/00—Chemical modification by after-treatment
  • C08F8/04—Reduction, e.g. hydrogenation
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/04—Oxygen-containing compounds
  • C08K5/14—Peroxides
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/16—Nitrogen-containing compounds
  • C08K5/22—Compounds containing nitrogen bound to another nitrogen atom
  • C08K5/23—Azo-compounds
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M143/00—Lubricating compositions characterised by the additive being a macromolecular hydrocarbon or such hydrocarbon modified by oxidation
  • C10M143/12—Lubricating compositions characterised by the additive being a macromolecular hydrocarbon or such hydrocarbon modified by oxidation containing conjugated diene
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2205/00—Organic macromolecular hydrocarbon compounds or fractions, whether or not modified by oxidation as ingredients in lubricant compositions
  • C10M2205/06—Organic macromolecular hydrocarbon compounds or fractions, whether or not modified by oxidation as ingredients in lubricant compositions containing conjugated dienes
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10M—LUBRICATING COMPOSITIONS; USE OF CHEMICAL SUBSTANCES EITHER ALONE OR AS LUBRICATING INGREDIENTS IN A LUBRICATING COMPOSITION
  • C10M2209/00—Organic macromolecular compounds containing oxygen as ingredients in lubricant compositions
  • C10M2209/02—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
  • C10M2209/08—Macromolecular compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds containing monomers having an unsaturated radical bound to a carboxyl radical, e.g. acrylate type
  • C10M2209/084—Acrylate; Methacrylate
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
  • C10N2020/00—Specified physical or chemical properties or characteristics, i.e. function, of component of lubricating compositions
  • C10N2020/01—Physico-chemical properties
  • C10N2020/019—Shear stability
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
  • C10N2020/00—Specified physical or chemical properties or characteristics, i.e. function, of component of lubricating compositions
  • C10N2020/01—Physico-chemical properties
  • C10N2020/04—Molecular weight; Molecular weight distribution
• • C—CHEMISTRY; METALLURGY
  • C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
  • C10N—INDEXING SCHEME ASSOCIATED WITH SUBCLASS C10M RELATING TO LUBRICATING COMPOSITIONS
  • C10N2030/00—Specified physical or chemical properties which is improved by the additive characterising the lubricating composition, e.g. multifunctional additives
  • C10N2030/02—Pour-point; Viscosity index

Definitions

• the invention relates to a process for preparing random copolymers comprising monomers derived from conjugated dienes and alkyl (meth)acrylates.
• Lubricants are compositions that reduce friction between surfaces. In addition to allowing freedom of motion between two surfaces and reducing mechanical wear of the surfaces, a lubricant may also inhibit corrosion of the surfaces and/or may inhibit damage to the surfaces due to heat or oxidation. Examples of lubricant compositions include, but are not limited to, engine oils, transmission fluids, gear oils, industrial lubricating oils, greases and metalworking oils.
• a typical lubricant composition includes a base fluid (also referred to as base oils) and optionally one or more additives.
• base fluids are naturally occurring hydrocarbons, such as mineral oils, or synthetic compositions, such as poly-alpha-olefins, polyalkyl methacrylates, and ethylene- propylene copolymers.
• a wide variety of additives may be combined with the base fluid, depending on the intended use of the lubricant.
• lubricant additives include, but are not limited to, oxidation inhibitors, corrosion inhibitors, dispersing agents, high pressure additives, anti-foaming agents and metal deactivators.
• oxidation inhibitors include, but are not limited to, corrosion inhibitors, dispersing agents, high pressure additives, anti-foaming agents and metal deactivators.
• VII viscosity index improvers
• thickeners may be used for improvement of viscometric properties. These viscosity modifiers are usually of polymeric type.
• Typical polymeric additives are based on polymers of alkyl (meth)acrylates.
• patent applications EP 0 566 048 A1 and EP 0 471 266 A1 disclose random copolymers of alkyl (meth)acrylates and 1-alkenes having a weight-average molecular weight M w of 1 ,000 up to 100,000 g/mol and their use as components of lubricant oil compositions.
• US patent No. 6,350,723 discloses block copolymers comprising at least one block of alkyl methacrylates including C12-30 alkyl methacrylates and a block of a polymerized conjugated diene having a number-average molecular weight M n of 15,000 up to 5,000,000 g/mol.
• the monomers derived from the dienes are selectively hydrogenated.
• the block copolymers are used as viscosity index improvers.
• Japanese patent application JP 2015/143346 discloses a process for the preparation of the copolymerized product of butadiene and (meth)acrylic acid and/or (meth)acrylic acid derivatives.
• a separately produced catalyst solution is engaged consisting of a mixed solution of 0.1 part of dimethylaluminum (p-dimethyl)bis(2-phenylindenyl)neodymium), 0.1 part of triphenylcarbonium tetrakis(pentafluorophenyl)borate and 30 parts of toluene).
• the yield of butadiene-methacrylic acid copolymerization is 50%.
• the catalyst system is complex and expensive. Generally, a simpler process is preferred such as free radical copolymerization.
• US 2001/0025078 discloses a process for the preparation of dispersed copolymers comprising the copolymerized product of a conjugated diolefin and a (meth)acrylate by means of emulsion copolymerization.
• disclosed emulsion copolymerization process requires rigorous control of surface tension and pH value.
• GB 1 , 1 12,749 discloses the polymerization of lauryl methacrylate and butadiene in emulsion activated by AIBN and hydrogenation in the presence of a nickel catalyst.
• the reaction is done at low temperature (-5°C) and the work-up is carried out with large volume of solvent with respect to the starting material, which is more difficult to achieve on industrial scale.
• British patent No. 1 ,165,286 discloses a process for the production of oligomers comprising heating butadiene and/or isoprene with methyl methacrylate in the presence of a ruthenium catalyst and, as solvent, an aliphatic alcohol containing from one to six carbon atoms.
• ruthenium catalyst as catalyst
• methanol as solvent
• the present invention aims at providing a process for the preparation of copolymers that can be used as viscosity modifying additives in lubricant compositions.
• the process should have a high monomer conversion and should result in low cross-linking of the copolymers.
• the invention relates to a process for preparing a random copolymer, the process comprising the steps of
• step (ii) providing a reaction mixture including the monomer composition prepared in step (i) and initiating radical polymerization in the reaction mixture to obtain a random copolymer, wherein radical polymerization is performed as solution polymerization and the amount of the monomer composition relative to the total weight of the reaction mixture in step (ii) is at least 20 % by weight, and wherein the weight-average molecular weight of the random copolymer is in the range of 7,000 to 30,000 g/mol.
• the process according to the invention has the additional advantage of yielding random copolymers having a relatively low molecular weight.
• the process is used to prepare random copolymers having a weight-average molecular weight of 7,000 to 30,000 g/mol, preferably 8,000 to 20,000 g/mol. Polymers having this weight-average molecular weight have a particularly high shear resistance and offer good improvements of the viscosimetric properties of a lubricant compositions at low amounts of the copolymer.
• the process of the invention has the further advantage of yielding random copolymers with a very low degree of cross-linking and a narrow molecular weight distribution, which further contribute to the shear-resistance of the copolymers. This is reflected in a low polydispersity index of the random copolymers.
• the polydispersity index (PDI) of the copolymers is in the range of 1.5 to 6.0, more preferably 2.0 to 4.0, most preferably 2.2 to 3.2.
• a polydispersity index in the range of 2.2 to 3.2 is considered optimal for most industrial applications with regard to the shear resistance of the copolymers.
• the polydispersity index is defined as the ratio of weight-average molecular weight to number-average molecular weight (M w /M n ).
• the weight-average and number-average molecular weights are determined by gel permeation chromatography using commercially available polybutadiene calibration standards. The determination is preferably performed according to DIN 55672-1 by gel permeation chromatography with THF as eluent.
• the monomer composition comprises 5 to 55 mol-% of monomers derived from one or more conjugated dienes having 6 carbon atoms or less per molecule as component (a), based on the total amount of monomers in the monomer composition.
• dienes are butadiene, c/ ' s- and trans- -methyl-1 , 3-butadiene (piperylene), 2,3- dimethyl-1 , 3-butadiene and 2-methyl-1 , 3-butadiene (isoprene).
• component (a) comprises butadiene or isoprene. Butadiene is most preferred.
• the monomer composition comprises 15 to 55 mol-%, of one or more conjugated dienes having 6 carbon atoms or less per molecule, based on the total amount of monomers in the monomer composition.
• AlkvKmetfOacrylates (components (b) and (c))
• the monomer composition comprises a mixture of monomers derived from C1-C6 alkyl(meth)acrylates as component (b) and C7-C24 alkyl(meth)acrylates as component (c).
• (meth)acrylic acid refers to acrylic acid, methacrylic acid and mixtures of acrylic acid and methacrylic acid; methacrylic acid being preferred.
• (meth)acrylate refers to esters of acrylic acid, esters of methacrylic acid or mixtures of esters of acrylic acid and methacrylic acid; esters of methacrylic acid being preferred.
• C1-6 alkyl(meth)acrylates refers to esters of (meth)acrylic acid and straight chain or branched alcohols having 1 to 6 carbon atoms. The term encompasses individual (meth)acrylic esters with an alcohol of a particular length, and likewise mixtures of (meth)acrylic esters with alcohols of different lengths. Similarly, the term “C7-24 alkyl(meth)acrylates” refers to esters of (meth)acrylic acid and straight chain or branched alcohols having 7 to 24 carbon atoms.
• Suitable C1-6 alkyl (meth)acrylates for component (b) include, for example, methyl (meth)acrylate, ethyl (meth)acrylate, n-propyl (meth)acrylate), / ' so-propyl (meth)acrylate, n-butyl (meth)acrylate, iso- butyl (meth)acrylate and tert- butyl (meth)acrylate.
• Particularly preferred C1-4 alkyl (meth)acrylates are methyl (meth)acrylate and butyl (meth)acrylate.
• component (b) comprises a mixture of methyl (meth)acrylate and butyl (meth)acrylate. More preferably, the butyl (meth)acrylate is n-butyl (meth)acrylate.
• Suitable C7-24 alkyl (meth)acrylates for component (c) include, for example, 2-butyloctyl (meth)acrylate, 2-hexyloctyl (meth)acrylate, decyl (meth)acrylate, 2-butyldecyl (meth)acrylate, 2- hexyldecyl (meth)acrylate, 2-octyldecyl (meth)acrylate, undecyl (meth)acrylate, 5-methylundecyl (meth)acrylate, dodecyl (meth)acrylate, 2-methyldodecyl (meth)acrylate, 2-hexyldodecyl (meth)acrylate, 2-octyldodecyl (meth)acrylate, tridecyl (meth)acrylate, 5-methyltridecyl (meth)acrylate, tetradecyl (meth)acrylate, 2-decyltetradecyl (
• C7-24 alkyl (meth)acrylates are n-octyl (meth)acrylate, n-decyl (meth)acrylate, n- dodecyl (meth)acrylate, n-tetradecyl (meth)acrylate, n-pentadecyl (meth)acrylate, n-hexadecyl (meth)acrylate, n-octadecyl (meth)acrylate, n-eicosyl (meth)acrylate, n-docosyl (meth)acrylate and n-tetracosyl (meth)acrylate.
• component (c) comprises one or more C10-C16 alkyl(meth)acrylates, which refers to esters of (meth)acrylic acid and straight chain or branched alcohols having 10 to 15 carbon atoms.
• component (c) comprises n-dodecyl (meth)acrylate.
• the monomer composition comprises 5 to 45 mol-%, preferably 10 to 40 mol-%, of one or more C1-C6 alkyl(meth)acrylates as component (b), based on the total amount of monomers in the monomer composition.
• the monomer composition comprises 10 to 40 mol-% of a mixture of methyl (meth)acrylate and butyl (meth)acrylate as component (b), based on the total amount of monomers in the monomer composition.
• the monomer composition comprises 10 to 70 mol-%, preferably 15 to 55 mol-%, of one or more C7-C24 alkyl(meth)acrylates as component (c), based on the total amount of monomers in the monomer composition, preferably being the one or more C7-C24 alkyl(meth)acrylates lauryl (meth)acrylate (C12-C15 alkyl (meth)acrylate).
• the monomer composition comprises as part of component (b) 10 to 40 mol-% of a mixture of methyl(meth)acrylate and butyl(meth)acrylate and as part of component (c) 15 to 55 mol% of lauryl methacrylate.
• the sum of all components (a) to (c) adds up to at least 90 mol-%, more preferably at least 95 mol-%, most preferably to 100 mol-%, based on the total amount of monomers in the monomer composition.
• esters of (meth)acrylic acid and a hydroxylated hydrogenated polybutadiene (component (d))
• the monomer composition may optionally comprise monomers derived from esters of (meth)acrylic acid and one or more hydroxylated hydrogenated polybutadienes as component (d). Because of their high molecular weight, the hydroxylated hydrogenated polybutadienes can also be referred to as macroalcohols in the context of this invention. The resulting esters can also be referred to as macromonomers in the context of this invention.
• the monomer composition comprises 0 to 10 mol-%, preferably 0 to 5 mol-%, more preferably 0.1 to 5 mol-% of one or more macromonomers as component (d), based on the total amount of monomers in the monomer composition.
• the sum of all components (a) to (d) adds up to at least 90 mol-%, more preferably at least 95 mol-%, most preferably to 100 mol-%, based on the total amount of monomers in the monomer composition.
• Component (d) may comprise a single type of macromonomer or may comprise a mixture of different macromonomers based on different macroalcohols.
• the hydroxylated hydrogenated polybutadienes of component (d) preferably have a number-average molecular weight M n of 500 g/mol to 10,000 g/mol, preferably 700 to 80,000 g/mol, most preferably 2,000 to 5,000 g/mol.
• component (d) is one macromonomer prepared using one macroalcohol having a number average molecular weight of 1 ,500 to 3,000 g/mol, preferably 1 ,800 to 2, 100 g/mol.
• the number-average molecular weight M n is determined by gel permeation chromatography using commercially available polybutadiene standards. The determination is performed according to DIN 55672-1 by gel permeation chromatography with THF as eluent.
• one or more hydroxylated hydrogenated polybutadienes have a hydrogenation level of at least 99%.
• the selectivity of the hydrogenation can be probed by, for example, quantitative 1 H nuclear magnetic resonance ( 1 H NMR) spectroscopy or infrared (IR) spectroscopy.
• the selectivity of the hydrogenation reaction according to the present invention is measured by 1 H NMR spectroscopy in deuterated chloroform solution relative to the non-hydrogenated starting material by comparing the signal integrals of the respective protons before and after selective hydrogenation reaction. The chemical shifts are calibrated using the solvent signal.
• Preferred hydroxylated hydrogenated polybutadienes can be obtained according to GB 2270317.
• hydroxylated hydrogenated polybutadiene refers to a hydrogenated polybutadiene that comprises at least one hydroxyl group.
• the hydroxylated hydrogenated polybutadiene may further comprise additional structural units, such as polyether groups derived from the addition of alkylene oxides to a polybutadiene or a maleic anhydride group derived from the addition of maleic anhydride to a polybutadiene. These additional structural units may be introduced into the polybutadiene when the polybutadiene is functionalized with hydroxyl groups.
• the hydroxylated hydrogenated polybutadiene is a hydroxyethyl- or hydroxypropyl-terminated hydrogenated polybutadiene. Particular preference is given to hydroxypropyl-terminated polybutadienes.
• These monohydroxylated hydrogenated polybutadienes can be prepared by first converting butadiene monomers by anionic polymerization to polybutadiene. Subsequently, by reaction of the polybutadiene monomers with an alkylene oxide, such as ethylene oxide or propylene oxide, a hydroxy-functionalized polybutadiene can be prepared. The polybutadiene may also be reacted with more than one alkylene oxide units, resulting in a polyether-polybutadiene block copolymer having a terminal hydroxyl group. The hydroxylated polybutadiene can be hydrogenated in the presence of a suitable transition metal catalyst.
• These monohydroxylated hydrogenated polybutadienes can also be selected from products obtained by hydroboration of (co)polymers of having a terminal double bond (e.g. as described in US Patent No. 4,316,973); maleic anhydride-ene-amino alcohol adducts obtained by an ene reaction between a (co)polymer having a terminal double bond and maleic anhydride with an amino alcohol; and products obtained by hydroformylation of a (co)polymer having a terminal double bond, followed by hydrogenation (e.g. as described in JP Publication No. S63-175096).
• the macromonomers for use in accordance with the invention can be prepared by transesterification of alkyl (meth)acrylates. Reaction of the alkyl (meth)acrylate with the hydroxylated hydrogenated polybutadiene forms the ester of the invention. Preference is given to using methyl (meth)acrylate or ethyl (meth)acrylate as reactant.
• This transesterification is widely known.
• a heterogeneous catalyst system such as lithium hydroxide/calcium oxide mixture (LiOH/CaO), pure lithium hydroxide (LiOH), lithium methoxide (LiOMe) or sodium methoxide (NaOMe) or a homogeneous catalyst system such as isopropyl titanate (Ti(OiPr) 4 ) or dioctyltin oxide (Sn(OCt) 2 0).
• the reaction is an equilibrium reaction. Therefore, the low molecular weight alcohol released is typically removed, for example by distillation.
• the macromonomers can be obtained by a direct esterification proceeding, for example, from (meth)acrylic acid or (meth)acrylic anhydride, preferably under acidic catalysis by p- toluenesulfonic acid or methanesulfonic acid, or from free methacrylic acid by the DCC method (dicyclohexylcarbodiimide).
• the present hydroxylated hydrogenated polybutadiene can be converted to an ester by reaction with an acid chloride such as (meth)acryloyl chloride.
• polymerization inhibitors are used, for example the 4-hydroxy-2,2,6,6-tetramethylpiperidinooxyl radical and/or hydroquinone monomethyl ether.
• the monomer composition may optionally comprise monomers derived from 1-alkenes having 6 to 16 carbon atoms as component (e).
• the 1-alkenes may be branched or linear and may comprise more than one unsaturated bond.
• the monomer units derived from these 1-alkenes are preferably also hydrogenated as described above for the conjugated dienes.
• Suitable 1-alkenes are, for example, 1-hexene, 1-octene, 1-decene and 1-docadecene.
• component (e) comprises 1-decene.
• the monomer composition comprises 0 to 10 mol-%, preferably 0 to 5 mol-%, more preferably 0.1 to 5 mol-% of one or more 1-alkenes having 6 to 16 carbon atoms as component (e), based on the total amount of monomers in the monomer composition.
• the sum of all components (a) to (e) adds up to at least 90 mol-%, more preferably at least 95 mol-%, most preferably to 100 mol-% based on the total amount of monomers in the monomer composition.
• the monomer composition may also comprise further monomers (f) in addition to the components (a) to (e) described above.
• Additional monomers which can be used in accordance with the invention can selected, for example, from the group consisting of styrene monomers having from 8 to 17 carbon atoms, vinyl esters having from 1 to 1 1 carbon atoms in the acyl group, vinyl ethers having from 1 to 10 carbon atoms in the alcohol group, dispersing oxygen- and/or nitrogen-functionalized monomers, heterocyclic (meth)acrylates, heterocyclic vinyl compounds, monomers containing a covalently bonded phosphorous atom, monomers containing epoxy groups and monomers containing halogens.
• Suitable styrene monomers having from 8 to 17 carbon atoms are selected from the group consisting of styrene, substituted styrenes having an alkyl substituent in the side chain, for example alphamethylstyrene and alpha-ethylstyrene, substituted styrenes having an alkyl substituent on the ring, such as vinyltoluene and para-methylstyrene, halogenated styrenes, for example monochlorostyrenes, dichlorostyrenes, tribromostyrenes and tetrabromostyrenes, nitrostyrene; styrene being preferred.
• Suitable vinyl esters having from 1 to 1 1 carbon atoms in the acyl group are selected from the group consisting of vinyl formate, vinyl acetate, vinyl propionate, vinyl butyrate; preferably vinyl esters including from 2 to 9, more preferably from 2 to 5 carbon atoms in the acyl group, wherein the acyl group may be linear or branched.
• Suitable vinyl ethers having from 1 to 10 carbon atoms in the alcohol group are selected from the group consisting of vinyl methyl ether, vinyl ethyl ether, vinyl propyl ether, vinyl butyl ether; preferably vinyl ethers including from 1 to 8, more preferably from 1 to 4 carbon atoms in the alcohol group, wherein the alcohol group may be linear or branched.
• Suitable dispersing oxygen- and/or nitrogen-functionalized monomers are selected from the group consisting of aminoalkyl (meth)acrylates, such as N,N-dimethylaminoethyl (meth)acrylate, N,N- dimethylaminopropyl (meth)acrylate, N,N-diethylaminopentyl (meth)acrylate, N,N- dibutylaminohexadecyl (meth)acrylate; aminoalkyl(meth)acrylamides, such as N,N- dimethylaminopropyl(meth)acrylamide; hydroxyalkyl (meth)acrylates, such as 3-hydroxypropyl (meth)acrylate, 3,4-dihydroxybutyl (meth)acrylate, 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 2,5-dimethyl-1 ,6-hexanediol (meth)acrylate, 1 , 10-decane
• Suitable heterocyclic (meth)acrylates are selected form the group consisting of 2-(1-imidazolyl)ethyl (meth)acrylate, 2-(4-morpholinyl)ethyl (meth)acrylate, 1-(2-methacryloyloxyethyl)-2-pyrrolidone, N- methacryloylmorpholine, N-methacryloyl-2-pyrrolidinone, N-(2-methacryloyloxyethyl)-2- pyrrolidinone, N-(3-methacryloyloxypropyl)-2-pyrrolidinone.
• Suitable heterocyclic vinyl compounds are selected from the group consisting of 2-vinylpyridine, 4- vinylpyridine, 2-methyl-5-vinylpyridine, 3-ethyl-4-vinylpyridine, 2,3-dimethyl-5-vinylpyridine, vinylpyrimidine, vinylpiperidine, 9-vinylcarbazole, 3-vinylcarbazole, 4-vinylcarbazole, 1- vinylimidazole, 2-methyl-1-vinylimidazole, N-vinylpyrrolidone, N-vinylpyrrolidine, 3-vinylpyrrolidine, N-vinyl-caprolactam, N-vinylbutyrolactam, vinyloxolane, vinylfuran, vinyloxazoles and hydrogenated vinyloxazoles.
• Monomers containing a covalently bonded phosphorous atom are selected from the group consisting of 2-(dimethylphosphato)propyl (meth)acrylate, 2-(ethylenephosphito)propyl (meth)acrylate, dimethylphosphinomethyl (meth)acrylate, dimethylphosphonoethyl (meth)acrylate, diethyl(meth)acryloyl phosphonate, dipropyl(meth)acryloyl phosphate, 2 (dibutylphosphono)ethyl (meth)acrylate, diethylphosphatoethyl (meth)acrylate, 2-(dimethylphosphato)-3-hydroxypropyl (meth)acrylate, 2-(ethylenephosphito)-3-hydroxypropyl (meth)acrylate, 3-(meth)acryloyloxy-2- hydroxypropyl diethyl phosphonate, 3-(meth)acryloyloxy-2- hydroxypropyl dipropyl phosphon
• Suitable monomers containing epoxy groups are, for example, glycidyl (meth)acrylate and glycidyl (meth)allyl ether and the like.
• Monomers containing halogens are, for examples, such as vinyl chloride, vinyl bromide, vinylidene chloride, (meth)allyl chloride and halogenated styrene (dichlorostyrene etc) and the like.
• the most preferred additional monomers (f) are selected from styrene monomers having from 8 to 17 carbon atoms, hydroxyethyl(meth)acrylate, N,N-dimethylaminoethyl (meth)acrylate, N,N- dimethylaminopropyl (meth)acrylate or a mixture thereof.
• the amount of additional monomers (f) is limited to 0 to 10 mol-%, more preferably 0 to 8 mol-%, most preferably 0 to 6 mol-%, based on the total amount of monomers in the monomer composition.
• the sum of all components (a) to (f) adds up to 100 mol-% based on the total amount of monomers in the monomer composition.
• the monomer composition comprises
• the monomer composition comprises
• the monomer composition comprises
• the amounts of components (a) to (e) add up to at least 90 mol-%, more preferably at least 95 mol-%, most preferably to 100 mol-%, based on the total amount of monomers in the monomer composition.
• the monomer composition comprises
• (f) 0 to 6 mol-% of one or more additional monomers (f) as listed above, preferably styrene monomers having from 8 to 17 carbon atoms, hydroxyethyl(meth)acrylate, N,N-dimethylaminoethyl (meth)acrylate, N,N-dimethylaminopropyl (meth)acrylate or a mixture thereof,
• the sum of all components (a) to (f) adds up to 100 mol-% based on the total amount of monomers in the monomer composition.
• the copolymers prepared according to the claimed process are of random architecture.
• the random architecture of the copolymers can be probed by measuring the glass transition temperature T g using differential scanning calorimetry (DSC).
• DSC differential scanning calorimetry
• the random copolymers - in contrast to block copolymers or gradient copolymers - typically possess a single conjunct glass transition temperature T g .
• a free radical random copolymerization process is used.
• Anionic polymerization is disfavored on industrial scale because of severe requirements on the purity of the raw materials.
• Block copolymerization is also disfavored as the block type polymeric architectures produced can lead to disfavored solubility and higher undesired crystallization tendency in comparison to the random type polymeric architecture observed during free radical random copolymerization.
• the free radical polymerization process according to the invention allows for the synthesis of random copolymers in a simple and inexpensive manner with the use of commercially available components.
• the radical polymerization is performed by solution polymerization.
• the reaction mixture during step (ii) preferably is a single-phase composition and in the case of solution polymerization, then the monomers and/or the resulting random copolymer are soluble in the solubilizing carrier medium used for the solution polymerization.
• Solution polymerization is the preferred method for carrying out the process of the invention, because it allows adjusting the concentration of the monomer composition in the reaction mixture by adding more or less solubilizing carrier medium. By selecting the correct concentration of the monomer composition in the reaction mixture, the molecular weight and the polydispersity index of the resulting copolymer can be controlled.
• the reaction mixture during step (ii) preferably consists of the monomer composition, a solubilizing carrier medium as described below, and one or more radical initiators.
• one or more chain transfer agents may be used during polymerization.
• the total amount of monomer composition in the reaction mixture is at least 20 % by weight, based on the total weight of the reaction mixture.
• the total amount of monomer composition in the reaction mixture is 20 to 70 % by weight, more preferably 20 to 45 % by weight, and even more preferably 30 to 45 % by weight, based on the total weight of the reaction mixture.
• a concentration of the monomer composition in the range of 20 to 45 % by weight, preferably 30 to 45 % by weight, based on the total weight of the reaction mixture, is considered optimal, because it yields random copolymers having a low weight-average molecular weight in the range of 8,000 to 20,000 g/mol and a low polydispersity index in the range of 2.2 to 3.2.
• the polymerization step (ii) is preferably performed at a temperature of 20°C to 200°C, more preferably 50°C to 150°C.
• the reaction pressure is preferably 1 bar to 30 bar, more preferably 10 bar to 28 bar.
• the total reaction time of the radical polymerization is 1 to 10 hours.
• the polymerization step (ii) is carried out in the presence of toluene and a radical initiator at a temperature of 90°C to 130°C, preferably 1 10 to 130°C, a pressure of 12 bar to 25 bar, preferably 15 bar to 23 bar and a total reaction time of 2 to 9 hours, preferably 3 to 7 hours.
• the product is preferably filtered to remove any impurities present in the reaction mixture, followed by the evaporation of any volatile solvents. In this step, there is no need to add any additional solvent at the end of the reaction.
• the reaction mixture in step (ii) comprises a solubilizing carrier medium.
• the solubilizing carrier medium is selected from the group consisting of mineral oils, synthetic oils, ketones, ester solvents, aromatic hydrocarbons, cycloaliphatic hydrocarbons and aliphatic hydrocarbons or mixtures thereof.
• mineral oils are paraffinic oils, naphthenic oils, solvent-refined oils, isoparaffin- containing high VI oils and hydrocracked high VI oils.
• synthetic oils are organic esters, for example diesters and polyesters, like carboxylic esters and phosphate esters; organic ethers like silicone oils, perfluoro-alkyl ethers and polyalkylene glycol; and synthetic hydrocarbons, especially polyolefins and Gas to Liquids oils (GTL).
• ketones are butanone and methyl ethyl ketone.
• ester solvents are fatty oils, and synthetic ester lubricants (for example, di-C4- 12 alkyl C4-12 dicarboxylates, such as dioctyl sebacate and dioctyl adipate, polyol poly-C4-12 alkanoates, such as pentaerythritol tetra-caproate; and tri-04-12 hydrocarbyl phosphates, such as tri-2-ethylhexyl phosphate, dibutyl phenyl phosphate, di-2-ethylhexyl phenyl phosphate, 2-ethylhexyl diphenyl phosphate and tricresyl phosphate).
• di-C4- 12 alkyl C4-12 dicarboxylates such as dioctyl sebacate and dioctyl adipate
• polyol poly-C4-12 alkanoates such as pentaerythritol te
• Examples for aromatic hydrocarbons are benzene, toluene, xylene, ethylbenzene, trimethyl benzene, ethyl toluene and mixtures of them.
• Examples for cycloaliphatic hydrocarbons are cyclohexane, methyl cyclohexane and cycloaliphatic terpenes.
• Examples for aliphatic hydrocarbons are n-pentane, n-hexane, n-heptane, 1-decene and aliphatic terpenes.
• the solubilizing carrier medium is a cycloaliphatic or aliphatic or aromatic hydrocarbon, preferably cyclohexane, 1-decene or toluene, even more preferably cyclohexane or toluene.
• Step (ii) comprises the addition of a radical initiator.
• the radical initiator is preferably added to the reaction mixture in step (ii) once the reaction mixture has been heated to the desired reaction temperature.
• the radical initiator is added to the reaction mixture during step (ii) at a reaction temperature of 90 to 130°C, more preferably 1 10 to 130°C and most preferably 120°C.
• Suitable radical initiators are, for example, azo initiators, such as azobis-isobutyronitrile (AIBN), 2,2'- azobis(2-methylbutyronitrile) (AMBN) and 1 , 1-azobiscyclohexanecarbonitrile, and peroxy compounds such as methyl ethyl ketone peroxide, acetylacetone peroxide, dilauryl peroxide, ketone peroxide, tert- butyl peroctoate, methyl isobutyl ketone peroxide, cyclohexanone peroxide, dibenzoyl peroxide, tert- butyl peroxybenzoate, tert- butyl peroxyisopropylcarbonate, 2,5-bis(2- ethylhexanoylperoxy)-2,5-dimethylhexane, tert- butyl peroxy-3,5,5-trimethylhexanoate, dicumyl peroxide, 1
• the radical initiator is selected from the group consisting of peroxide initiators and azo initiators or mixtures thereof.
• the radical initiator is selected from the group consisting of 2,2'-azobis(2- methylbutyronitrile), 2,2-bis(tert-butylperoxy)butane, 1 , 1-di-ferf-butylperoxy-3,3,5- trimethylcyclohexane, tert- butyl peroxybenzoate and ferf-butylperoxy-3,5,5-trimethylhexanoate.
• the radical initiator is 2,2-bis(tert-butylperoxy)butane.
• the total amount of radical initiator relative to the total weight of the monomer composition is 0.01 to 5 % by weight, more preferably 0.02 to 1 % by weight, most preferably 0.05 to 0.5 % by weight.
• the total amount of radical initiator may be added in a single step or the radical initiator may be added in several steps over the course of the polymerization reaction.
• the radical initiator is added in several steps.
• the radical initiator is added in two steps.
• a part of the radical initiator may be added to initiate radical polymerization and a second part of the radical initiator may be added 0.5 to 3.5 hours after the initial dosage.
• the first portion of radical initiator consists of 50 to 90 % by weight, preferably 60 to 90 % by weight, more preferably 70 to 90 % by weight, even more preferably 80wt% of the total amount of radical initiator.
• the second portion then contains the remaining amount of radical initiator.
• Step (ii) optionally comprises the addition of a chain transfer agent.
• chain transfer agents are used to control the molecular weight and/or the molecular weight distribution. This technology is well-known and practiced in the polymer industry and is described in Odian, Principles of Polymerization, 1991.
• chain transfer agents are sulfur containing compounds such as thiols, e.g. n- and t-dodecanethiol; 2-mercaptoethanol, and mercapto carboxylic acid esters, e.g. methyl-3-mercaptopropionate; terpenes, e.g. 1-methyl-4-(propan-2-ylidene)cyclohex-1-ene; or longer chain alkenes.
• Preferred chain transfer agents are alkenes having up to 20 carbon atoms, especially up to 15 carbon atoms and more preferably up to 12 carbon atoms. Particularly preferred is the addition of 1-decene.
• the process according to the invention may further comprise as optional step (iii) the hydrogenation of the random copolymer obtained in step (ii).
• Hydrogenation is preferably selective and only affects the monomer units derived from the conjugated dienes (a). Preferably, the hydrogenation does not affect the other monomer units (b) to
• the selectivity of the hydrogenation can be probed as described above by quantitative 1 H nuclear magnetic resonance ( 1 H NMR) spectroscopy or infrared (IR) spectroscopy.
• An alternative measure to determine the hydrogenation level of the copolymer is the iodine number.
• the iodine number refers to the number of grams of iodine which can be added onto 100 g of polymer.
• the hydroxylated hydrogenated polybutadienes have an iodine number of not more than 5 g of iodine per 100 g of polymer.
• the iodine number is determined by the Wijs method according to DIN 53241- 1 : 1995-05.
• the hydrogenation degree in relation to the polymerized units derived from conjugated dienes, is >95%.
• the hydrogenation degree is defined as the molar degree of saturation of carbon- carbon bonds of the polymerized units derived from conjugated dienes through addition of hydrogen relative to the non-hydrogenated starting material.
• the degree of hydrogenation of the random copolymer obtained by the process of the present invention is measured by 1 H NMR spectroscopy in deuterated chloroform solution using dimethyl terephthalate as standard. The chemical shifts are calibrated using the solvent signal.
• the respective signal integrals of the standard are put into relation with the signal integrals of the olefinic protons. It is necessary for each sample to repeat the measurement and determination using a non-hydrogenated reference sample in order to define 0% degree of hydrogenation.
• Hydrogenation preferably performed in the presence of hydrogen gas or other hydrogen sources in the presence of a heterogeneous insoluble, supported metal or metal complex catalyst or in the presence of a homogenous soluble, organometallic catalyst.
• Heterogeneous catalysts are preferred and are, for example, described in US 3,541 ,064 (A) and GB 1 ,030,306.
• Typical catalytically active metals for heterogeneously catalyzing the selective hydrogenation according to the invention include, but are not limited to, Ru, Rh, Pd, Ir, Pt, Mn, Cr, Fe, Co, Ni, U, Cu, Nd, In, Sn, Zn, Ag, Cr and alloys of one or more of these metals. Catalysts containing Pd are particularly preferred.
• Typical catalyst supports include, but are not limited to oxides (AI203, Ti02, Si02 or others), carbon, kieselguhr or other carriers.
• the selective hydrogenation process according to the present invention is preferably performed using a heterogeneous carbon-supported Pd catalyst.
• the heterogeneous catalysts can be used, for example, in the form of pellets or powders. Powders are particularly preferred.
• the amount of catalytically active metal loaded on the support preferably is 0.1 to 10 % by weight, more preferably 1 to 10 % by weight, based on the total weight of the supported catalyst.
• the copolymer subjected to hydrogenation is provided in a composition further including a solubilizing carrier medium.
• the solubilizing carrier medium is selected from the group consisting of mineral oils, synthetic oils, ketones, ester solvents, aromatic hydrocarbons, cycloaliphatic hydrocarbons and aliphatic hydrocarbons or mixtures thereof.
• mineral oils are paraffinic oils, naphthenic oils, solvent-refined oils, isoparaffin- containing high VI oils and hydrocracked high VI oils.
• synthetic oils are organic esters, for example diesters and polyesters, like carboxylic esters and phosphate esters; organic ethers like silicone oils, perfluoro-alkyl ethers and polyalkylene glycol; and synthetic hydrocarbons, especially polyolefins and Gas to Liquids oils (GTL).
• ketones are butanone and methyl ethyl ketone.
• ester solvents are fatty oils, and synthetic ester lubricants (for example, di-C4- 12 alkyl C4-12 dicarboxylates, such as dioctyl sebacate and dioctyl adipate, polyol poly-C4-12 alkanoates, such as pentaerythritol tetra-caproate; and tri-04-12 hydrocarbyl phosphates, such as tri-2-ethylhexyl phosphate, dibutyl phenyl phosphate, di-2-ethylhexyl phenyl phosphate, 2-ethylhexyl diphenyl phosphate and tricresyl phosphate).
• di-C4- 12 alkyl C4-12 dicarboxylates such as dioctyl sebacate and dioctyl adipate
• polyol poly-C4-12 alkanoates such as pentaerythritol te
• Examples for aromatic hydrocarbons are benzene, toluene, xylene, ethylbenzene, trimethyl benzene, ethyl toluene and mixtures of them.
• Examples for cycloaliphatic hydrocarbons are cyclohexane, methyl cyclohexane and cycloaliphatic terpenes.
• Examples for aliphatic hydrocarbons are n-pentane, n-hexane, n-heptane, 1-decene and aliphatic terpenes.
• hydrogenation is carried out in the presence of a cycloaliphatic or aliphatic hydrocarbon, preferably cyclohexane.
• the reaction pressure preferably is between 5 and 1500 bar, either as constant or gradient pressure. More preferably, the reaction pressure is 5 to 500 bar, even more preferably 10 to 300 bar, and most preferably 15 to 250 bar.
• the reaction temperature preferably is 20 to 200°C, more preferably 20 to 150°C, even more preferably 20 to 130°C and most preferably 20 to 120°C.
• hydrogenation is carried out in the presence of cyclohexane and a carbon-supported Pd catalyst at a temperature of 60 to 130°C, preferably 80 to 120°C, and a pressure of 70 to 120 bar, preferably 80 to 100 bar.
• THF tetrahydrofuran
• the conversion rate corresponds to the weight of monomers incorporated into the copolymer relative to the total weight of the initial monomer mixture.
• the conversion rate was determined by gravimetric analysis, wherein the total weight of the dried polymer is calculated against the total feed amount of the monomer.
• the monomers indicated in Table 1 were mixed with toluene at a temperature of 20 °C and a pressure of 10 bar in a 5 L autoclave so that the concentration of the monomers relative to the total weight of the mixture is 40% by weight.
• the temperature was increased to 120 °C using a heat rate of 5.5 °C/min, before the initiator, 2,2-bis(tert-butylperoxy)butane (50% by weight in liquid paraffin) was added.
• Free radical copolymerization was performed at a reaction temperature of 120 °C, a reaction pressure of 20 bar and a reaction time of 4 h. The discharge was filtered and volatile solvents were evaporated.
• the amount of initiator is calculated based on the total amount of monomers in the reaction mixture.
• Example 1 was prepared according to the general procedure except that the initiator was added in two steps. Firstly, 80% of the initiator was added, followed by a second addition of 20% initiator after a reaction time of 2 hours. The work-up was also carried out in the presence of BHT (2,6-di-tert-butyl- 4-methylphenol).
• Examples 2 and 6 were prepared according to the general procedure except that the initiator was added in two steps. Firstly, 80% of the initiator was added, followed by a second addition of 20% initiator after a reaction time of 2 hours. Furthermore, after 4 hours the reaction temperature was increased to 130 °C for 30 minutes.
• Example 3 was prepared according to the general procedure except that the initiator was added in two steps and the monomer composition comprises additionally a macromonomer d). Firstly, 80% of the initiator was added, followed by a second addition of 20% initiator after a reaction time of 2 hours. Furthermore, after 4 hours the reaction temperature was increased to 130 °C for 30 minutes.
• Example 4 was prepared according to the general procedure except that butadiene was replaced by isoprene and the initiator was added in two steps. Firstly, 80% of the initiator was added, followed by a second addition of 20% initiator after a reaction time of 2 hours. Furthermore, after 4 hours the reaction temperature was increased to 130 °C for 30 minutes.
• Examples 5 and 7 were prepared according to the general procedure except that the initiator was added in two steps. Firstly, 80% of the initiator was added, followed by a second addition of 20% initiator after a reaction time of 2 hours. Furthermore, after 4 hours the reaction temperature was increased to 130 °C for 30 minutes. The reaction was carried out in 1-decene.
• Example 8 was prepared according to the general procedure except that the initiator was added in two steps. Firstly, 80% of the initiator was added, followed by a second addition of 20% initiator after a reaction time of 2 hours. Furthermore, after 4 hours the reaction temperature was increased to 130 °C for 30 minutes. The reaction was carried out in cyclohexane.
• Example 9 was prepared according to the general procedure except the reaction was carried out at a higher monomer concentration of 50%. Firstly, 80% of the initiator was added, followed by a second addition of 20% initiator after a reaction time of 2 hours. Furthermore, after 4 hours the reaction temperature was increased to 130 °C for 30 minutes.
• Comparative example 10 was prepared according to the general procedure except that the initiator was added in two steps. Firstly, 80% of the initiator was added, followed by a second addition of 20% initiator after a reaction time of 2 hours. Furthermore, after 4 hours the reaction temperature was increased to 130 °C for 30 minutes. The reaction was carried out at 10% monomer concentration.
• Comparative example 1 1 was prepared according to the general procedure except that the initiator was added in one step. Furthermore, the reaction was carried out for 1 hour.
• the monomer composition of this example did not include any C7-C24 alkyl(meth)acrylate.
• Comparative example 12 was prepared according to the general procedure except that the initiator was added in two steps. Firstly, 80% of the initiator was added, followed by a second addition of 20% initiator after a reaction time of 2 hours. Furthermore, after 4 hours the reaction temperature was increased to 130 °C for 30 minutes.
• the monomer composition comprises only butadiene. Table 1 : Preparation of copolymers
• a macromonomer is a (meth)acrylic acid ester of a hydroxylated hydrogenated polybutadiene with a hydrogenation degree of 99%. b relative to the total amount of monomers.
• Examples 1 to 8 further demonstrate that by restricting the monomer concentration to the preferred range of 20 to 45 % by weight, copolymers with a weight-average molecular weight of 8,000 to 20,000 g/mol and a low polydispersity index in the range of 2.2 to 3.2 can be obtained.

Landscapes

• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• General Chemical & Material Sciences (AREA)
• Oil, Petroleum & Natural Gas (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)

Priority Applications (7)

Applications Claiming Priority (2)

Publications (1)

Family

ID=64308614

Family Applications (1)

Country Status (8)

Families Citing this family (4)

Citations (15)

Family Cites Families (8)

• 2019
  • 2019-10-23 CA CA3118955A patent/CA3118955C/en active Active
  • 2019-10-23 ES ES19787319T patent/ES2925268T3/es active Active
  • 2019-10-23 KR KR1020217017923A patent/KR20210092765A/ko not_active Withdrawn
  • 2019-10-23 CN CN201980074776.9A patent/CN113015780B/zh active Active
  • 2019-10-23 JP JP2021525849A patent/JP2022507337A/ja not_active Withdrawn
  • 2019-10-23 EP EP19787319.3A patent/EP3880774B1/en active Active
  • 2019-10-23 WO PCT/EP2019/078865 patent/WO2020099079A1/en not_active Ceased
  • 2019-10-23 US US17/292,452 patent/US20220017654A1/en not_active Abandoned

Patent Citations (15)

Non-Patent Citations (5)

Also Published As

Similar Documents

Legal Events