WO2020048852A1 - Procédé de préparation d'aldéhydes alpha, bêta insaturés par oxydation d'alcools en présence d'une phase liquide - Google Patents

Procédé de préparation d'aldéhydes alpha, bêta insaturés par oxydation d'alcools en présence d'une phase liquide Download PDF

Info

Publication number
WO2020048852A1
WO2020048852A1 PCT/EP2019/073033 EP2019073033W WO2020048852A1 WO 2020048852 A1 WO2020048852 A1 WO 2020048852A1 EP 2019073033 W EP2019073033 W EP 2019073033W WO 2020048852 A1 WO2020048852 A1 WO 2020048852A1
Authority
WO
WIPO (PCT)
Prior art keywords
catalyst
liquid phase
weight
support
process according
Prior art date
Application number
PCT/EP2019/073033
Other languages
English (en)
Inventor
Michaela FENYN
Joseph John ZAKZESKI
Nicolas VAUTRAVERS
Joaquim Henrique Teles
Original Assignee
Basf Se
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se filed Critical Basf Se
Publication of WO2020048852A1 publication Critical patent/WO2020048852A1/fr

Abstract

L'invention concerne un procédé de préparation d'aldéhydes alpha, bêta insaturés par oxydation d'alcools en présence d'une phase liquide
PCT/EP2019/073033 2018-09-07 2019-08-29 Procédé de préparation d'aldéhydes alpha, bêta insaturés par oxydation d'alcools en présence d'une phase liquide WO2020048852A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
EP18193182.5 2018-09-07
EP18193182 2018-09-07
EP18210452.1 2018-12-05
EP18210452 2018-12-05

Publications (1)

Publication Number Publication Date
WO2020048852A1 true WO2020048852A1 (fr) 2020-03-12

Family

ID=67766179

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2019/073033 WO2020048852A1 (fr) 2018-09-07 2019-08-29 Procédé de préparation d'aldéhydes alpha, bêta insaturés par oxydation d'alcools en présence d'une phase liquide

Country Status (1)

Country Link
WO (1) WO2020048852A1 (fr)

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0881206A1 (fr) 1997-05-28 1998-12-02 Basf Aktiengesellschaft Procédé pour la préparation technique d'aldéhydes aliphatiques insaturés dans un réacteur à faisceau tubulaire
WO1999018058A1 (fr) 1997-10-02 1999-04-15 RWE-DEA Aktiengesellschaft für Mineraloel und Chemie Procede pour la preparation d'aldehydes et d'acides carboxyliques par oxydation d'alcools primaires
WO2008037693A1 (fr) 2006-09-26 2008-04-03 Basf Se Procédé de production de citral en continu
JP2010202555A (ja) 2009-03-02 2010-09-16 Nagoya Industrial Science Research Inst カルボニル化合物の製造方法
WO2014170604A1 (fr) * 2013-04-17 2014-10-23 Centre National De La Recherche Scientifique Procede de production de nitriles mettant en œuvre un catalyseur a base d'antimoine et de fer
WO2016167726A1 (fr) * 2015-04-15 2016-10-20 Agency For Science, Technology And Research Procédé de synthèse d'un acide alcénoïque
WO2018002040A1 (fr) * 2016-06-29 2018-01-04 Basf Se Procédé de préparation d'aldéhydes alpha,bêta-insaturés par oxydation d'alcools en présence d'une phase liquide
WO2018073367A1 (fr) 2016-10-20 2018-04-26 Basf Se Procédé de production d'un catalyseur comprenant un composé intermétallique et catalyseur produit par le procédé
WO2018172110A1 (fr) * 2017-03-20 2018-09-27 Basf Se Procédé de préparation d'aldéhydes alpha,bêta-insaturés par oxydation d'alcools en présence d'une phase liquide
WO2019121012A1 (fr) * 2017-12-21 2019-06-27 Basf Se Procédé de préparation d'aldéhydes alpha,bêta-insaturés par oxydation d'alcools en présence d'une phase liquide

Patent Citations (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0881206A1 (fr) 1997-05-28 1998-12-02 Basf Aktiengesellschaft Procédé pour la préparation technique d'aldéhydes aliphatiques insaturés dans un réacteur à faisceau tubulaire
WO1999018058A1 (fr) 1997-10-02 1999-04-15 RWE-DEA Aktiengesellschaft für Mineraloel und Chemie Procede pour la preparation d'aldehydes et d'acides carboxyliques par oxydation d'alcools primaires
US6476260B1 (en) * 1997-10-02 2002-11-05 Rwe-Dea Aktiengesellschraft Fur Mineraloel Und Chemie Method of producing aldehydes and carboxylic acids by oxidizing primary alcohols
WO2008037693A1 (fr) 2006-09-26 2008-04-03 Basf Se Procédé de production de citral en continu
JP2010202555A (ja) 2009-03-02 2010-09-16 Nagoya Industrial Science Research Inst カルボニル化合物の製造方法
WO2014170604A1 (fr) * 2013-04-17 2014-10-23 Centre National De La Recherche Scientifique Procede de production de nitriles mettant en œuvre un catalyseur a base d'antimoine et de fer
WO2016167726A1 (fr) * 2015-04-15 2016-10-20 Agency For Science, Technology And Research Procédé de synthèse d'un acide alcénoïque
WO2018002040A1 (fr) * 2016-06-29 2018-01-04 Basf Se Procédé de préparation d'aldéhydes alpha,bêta-insaturés par oxydation d'alcools en présence d'une phase liquide
WO2018073367A1 (fr) 2016-10-20 2018-04-26 Basf Se Procédé de production d'un catalyseur comprenant un composé intermétallique et catalyseur produit par le procédé
WO2018172110A1 (fr) * 2017-03-20 2018-09-27 Basf Se Procédé de préparation d'aldéhydes alpha,bêta-insaturés par oxydation d'alcools en présence d'une phase liquide
WO2019121012A1 (fr) * 2017-12-21 2019-06-27 Basf Se Procédé de préparation d'aldéhydes alpha,bêta-insaturés par oxydation d'alcools en présence d'une phase liquide

Non-Patent Citations (20)

* Cited by examiner, † Cited by third party
Title
"Handbook of Heterogeneous Catalysis", 1997, WILEY-VCH
ADAM F. LEE ET AL: "Aspects of allylic alcohol oxidation - a bimetallic heterogeneous selective oxidation catalyst", GREEN CHEMISTRY, vol. 2, no. 6, 14 November 2000 (2000-11-14), GB, pages 279 - 282, XP055401485, ISSN: 1463-9262, DOI: 10.1039/b006528p *
ADV. SYNTH. CATAL., vol. 345, 2003, pages 517 - 523
ANDERSON ET AL: "Selective oxidation of alcohols to carbonyl compounds and carboxylic acids with platinum group metal catalysts", ADVANCED SYNTHESIS & CATALYSIS, WILEY-VCH VERLAG GMBH, DE, vol. 345, January 2003 (2003-01-01), pages 517 - 523, XP002380135, ISSN: 1615-4150, DOI: 10.1002/ADSC.200390060 *
BIMAL K. BANIK ET AL: "Sodium Bismuthate Mediated Oxidation of Allylic and Benzylic Alcohols", SYNTHETIC COMMUNICATIONS, vol. 30, no. 15, August 2000 (2000-08-01), PHILADELPHIA, PA; US, pages 2701 - 2705, XP055623319, ISSN: 0039-7911, DOI: 10.1080/00397910008086894 *
CATALYSIS TODAY, vol. 121, 2007, pages 13 - 21
CATALYSIS TODAY, vol. 57, 2000, pages 127 - 141
CHEM. COMMUN., 2007, pages 4399 - 4400
CHEM. COMMUN., 2008, pages 3181 - 3183
CHEN ET AL., J. AM. CHEM. SOC., vol. 134, 2012, pages 18453 - 18459
CUI ET AL., J. AM. CHEM. SOC., vol. 136, 2014, pages 10206 - 10209
CUI ET AL., JAM. CHEM. SOC., vol. 136, 2014, pages 10206 - 10209
FURUKAWA ET AL., RSC ADV., vol. 3, 2013, pages 23269 - 23277
GREEN CHEMISTRY, vol. 2, 2000, pages 279 - 282
M. CHEO. CLAUSECH. MARCILLY, IMPREGNATION AND ION EXCHANGE, pages 315 - 340
TETRAHEDRON, vol. 9, 1960, pages 67 - 75
YU SHI ET AL: "Au Pd nanoparticles on layered double hydroxide: Highly active catalyst for aerobic oxidation of alcohols in aqueous phase", CATALYSIS COMMUNICATIONS, ELSEVIER, AMSTERDAM, NL, vol. 18, 10 December 2011 (2011-12-10), pages 142 - 146, XP028442940, ISSN: 1566-7367, [retrieved on 20111210], DOI: 10.1016/J.CATCOM.2011.12.003 *
ZHANG ET AL., J. AM. CHEM. SOC., vol. 137, 2015, pages 6263 - 6269
ZHANG ET AL.: "Characterization of Pt-Bi intermetallic NPs", J. AM. CHEM. SOC., vol. 137, 2015, pages 6264
ZHANG, ELECTROCHEMISTRY COMMUNICATIONS, vol. 25, 2012, pages 105 - 108

Similar Documents

Publication Publication Date Title
US10875821B2 (en) Process for the preparation of alpha, beta unsaturated aldehydes by oxidation of alcohols in the presence of a liquid phase
EP2671861B1 (fr) Oxydation sélective d'hydrocarbures à l'aide de catalyseurs hétérogènes
US20110152546A1 (en) Process for producing olefin oxide
CN109803921B (zh) 低聚硅烷的制造方法
US11111197B2 (en) Process for the preparation of alpha, beta unsaturated aldehydes by oxidation of alcohols in the presence of a liquid phase
CN115400763B (zh) 用于co2加氢制备高级醇的催化剂及其催化剂的制备方法和应用
EP3478651B1 (fr) Procédé de préparation d'aldéhydes alpha,bêta-insaturés par oxydation d'alcools en présence d'une phase liquide
US11046632B2 (en) Process for the preparation of 3-methyl-2-buten-1-al
WO2020048855A1 (fr) Procédé de préparation d'aldéhydes alpha,bêta-insaturés par oxydation d'alcools en présence d'une phase liquide
WO2020048852A1 (fr) Procédé de préparation d'aldéhydes alpha, bêta insaturés par oxydation d'alcools en présence d'une phase liquide
CN112221508B (zh) 一种苯乙酮加氢制苯乙醇的催化剂及其制备和应用方法
US7230141B2 (en) Method for producing toluol derivatives
JP5468324B2 (ja) Ｎ−アルキル−ｔｅｒｔ−ブチルアミンの製造方法
EP4115974A1 (fr) Catalyseur de cobalt à support d'oxyde favorisant l'amination réductive
BR112019018099B1 (pt) Processo para a preparação de aldeídos alfa, beta insaturados
CN113304753B (zh) 一种用于催化羟基醛加氢制备多元醇的催化剂及其制备和应用方法
CN117181214A (zh) 一种催化剂、制备方法及其在乙醇脱氢氨化制乙腈中的应用
JPS5925340A (ja) 含酸素化合物の製造法
JPH11315049A (ja) ３−アシロキシシクロヘキセンの製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19758986

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19758986

Country of ref document: EP

Kind code of ref document: A1