WO2020045378A1 - Élément semi-conducteur - Google Patents

Élément semi-conducteur Download PDF

Info

Publication number
WO2020045378A1
WO2020045378A1 PCT/JP2019/033407 JP2019033407W WO2020045378A1 WO 2020045378 A1 WO2020045378 A1 WO 2020045378A1 JP 2019033407 W JP2019033407 W JP 2019033407W WO 2020045378 A1 WO2020045378 A1 WO 2020045378A1
Authority
WO
WIPO (PCT)
Prior art keywords
thermoelectric
element layer
semiconductor
dmax
thermoelectric element
Prior art date
Application number
PCT/JP2019/033407
Other languages
English (en)
Japanese (ja)
Inventor
亘 森田
邦久 加藤
豪志 武藤
祐馬 勝田
Original Assignee
リンテック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by リンテック株式会社 filed Critical リンテック株式会社
Priority to JP2020539461A priority Critical patent/JP7348192B2/ja
Publication of WO2020045378A1 publication Critical patent/WO2020045378A1/fr

Abstract

L'invention concerne un élément semi-conducteur contenant une couche d'élément semi-conducteur formée à partir d'une composition semi-conductrice contenant un matériau semi-conducteur sur un substrat; lorsque l'élément semi-conducteur est utilisé comme élément de conversion thermoélectrique, l'élément semi-conducteur fournit un élément de conversion thermoélectrique pourvu d'une couche d'élément thermoélectrique qui a une excellente performance thermoélectrique et dont la forme de section a été réglée. En définissant S(μm2) comme étant la zone de la section verticale comprenant la partie centrale de la couche d'élément semi-conducteur, Dmax(μm) comme étant la valeur maximale de l'épaisseur dans le sens de l'épaisseur de la section verticale et Xmax (μm) comme étant la valeur maximale de la longueur dans le sens de la largeur de la section verticale, la section verticale de la couche d'élément semi-conducteur satisfait les conditions (A) et (B). <sp />(A) 0,75 ≤ S / (Dmax×Xmax) ≤ 1,00 (B) Dmax ≥ 10 μm, ou (Dmax/Xmax) ≥ 0,03<u /> <u />
PCT/JP2019/033407 2018-08-28 2019-08-27 Élément semi-conducteur WO2020045378A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2020539461A JP7348192B2 (ja) 2018-08-28 2019-08-27 半導体素子

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018-159290 2018-08-28
JP2018159290 2018-08-28

Publications (1)

Publication Number Publication Date
WO2020045378A1 true WO2020045378A1 (fr) 2020-03-05

Family

ID=69644547

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/033407 WO2020045378A1 (fr) 2018-08-28 2019-08-27 Élément semi-conducteur

Country Status (3)

Country Link
JP (1) JP7348192B2 (fr)
TW (1) TW202023073A (fr)
WO (1) WO2020045378A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022071043A1 (fr) * 2020-09-30 2022-04-07 リンテック株式会社 Couche de matériau de conversion thermoélectrique

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015050426A (ja) * 2013-09-04 2015-03-16 富士フイルム株式会社 熱電変換素子
WO2016147809A1 (fr) * 2015-03-18 2016-09-22 リンテック株式会社 Feuille de récupération de chaleur
WO2018139475A1 (fr) * 2017-01-27 2018-08-02 リンテック株式会社 Élément de conversion thermoélectrique flexible, et procédé de fabrication de celui-ci

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015050426A (ja) * 2013-09-04 2015-03-16 富士フイルム株式会社 熱電変換素子
WO2016147809A1 (fr) * 2015-03-18 2016-09-22 リンテック株式会社 Feuille de récupération de chaleur
WO2018139475A1 (fr) * 2017-01-27 2018-08-02 リンテック株式会社 Élément de conversion thermoélectrique flexible, et procédé de fabrication de celui-ci

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2022071043A1 (fr) * 2020-09-30 2022-04-07 リンテック株式会社 Couche de matériau de conversion thermoélectrique

Also Published As

Publication number Publication date
JPWO2020045378A1 (ja) 2021-09-24
TW202023073A (zh) 2020-06-16
JP7348192B2 (ja) 2023-09-20

Similar Documents

Publication Publication Date Title
JP6683132B2 (ja) ペルチェ冷却素子及びその製造方法
JP7406756B2 (ja) 熱電変換モジュール及びその製造方法
JP7486949B2 (ja) 熱電変換モジュール用電極材料及びそれを用いた熱電変換モジュール
WO2020045377A1 (fr) Procédé de fabrication d&#39;élément de conversion thermoélectrique
WO2019188862A1 (fr) Module de conversion thermoélectrique
WO2020045378A1 (fr) Élément semi-conducteur
JP7346427B2 (ja) 熱電変換材料のチップの製造方法及びその製造方法により得られたチップを用いた熱電変換モジュールの製造方法
WO2020071424A1 (fr) Puce constituée de matériau de conversion thermoélectrique
US20230200240A1 (en) Thermoelectric conversion module and manufacturing method therefor
WO2020203612A1 (fr) Couche de matériau thermoélectrique et son procédé de production
JP7458375B2 (ja) 熱電変換材料のチップの製造方法
WO2021193357A1 (fr) Module de conversion thermoélectrique
WO2020203611A1 (fr) Procédé de formation d&#39;une couche de réception de brasure sur une puce de matériau de conversion thermoélectrique
JP7401361B2 (ja) 熱電変換モジュール
WO2021193358A1 (fr) Module de conversion thermoélectrique
WO2023013590A1 (fr) Couche de matériau de conversion thermoélectrique et module de conversion thermoélectrique
JP2020035818A (ja) 熱電変換素子及びその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19855113

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020539461

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19855113

Country of ref document: EP

Kind code of ref document: A1